NL8502162A - COLORED SODA LIMEGLAS. - Google Patents
COLORED SODA LIMEGLAS. Download PDFInfo
- Publication number
- NL8502162A NL8502162A NL8502162A NL8502162A NL8502162A NL 8502162 A NL8502162 A NL 8502162A NL 8502162 A NL8502162 A NL 8502162A NL 8502162 A NL8502162 A NL 8502162A NL 8502162 A NL8502162 A NL 8502162A
- Authority
- NL
- Netherlands
- Prior art keywords
- glass
- amount
- present
- weight
- color
- Prior art date
Description
? I 4 * NL 32859-Kp/cs? I 4 * NL 32859-Kp / cs
Gekleurd soda-limeglas.Colored soda lime glass.
De uitvinding heeft betrekking op gekleurd soda-lime-glas met een basismengsel van de belangrijkste glasvormende bestanddelen samen met kleurstoffen.The invention relates to colored soda-lime glass with a basic mixture of the main glass-forming constituents together with dyes.
De uitdrukking "soda-limeglas" wordt hier in ruime 5 zin gebruikt en betekent elk glas, dat de volgende glasvormende bestanddelen in gewichtsprocenten bevatThe term "soda lime glass" is used in a broad sense here and means any glass containing the following glass-forming components in percent by weight
Si02 60% tot 75%Si02 60% to 75%
Na20 10% tot 20%Na20 10% to 20%
CaO 0% tot 16% 10 K20 0% tot 10%CaO 0% to 16% 10 K20 0% to 10%
MgO 0% tot 10% A1203 0% tot 5%MgO 0% to 10% A1203 0% to 5%
BaO 0% tot 2%BaO 0% to 2%
BaO + CaO + MgO 10% tot 20% 15 K20 + Na20 10% tot 20%BaO + CaO + MgO 10% to 20% 15 K20 + Na20 10% to 20%
Bij het bespreken van de optische eigenschappen van een glasplaat is het gewoonlijk noodzakelijk deze eigenschappen te relateren aan een standaardlichtbron. Voor de doeleinden van de onderhavige beschrijving is als standaardlicht-20 bron Illuminant C, vastgesteld door de Internationale Commissie voor Belichting (CIE) gebruikt. Illuminant C is zo goed als een gemiddelde daglichtbron met een kleurtemperatuur van 6700K. De Internationale Commisie voor Belichting heeft ook gepubliceerd "Colorimetry, Official Recommendations of the 25 International Commission on Illumination" (mei 1970), waarin de theorie van colorimetrie is uiteengezet, volgens welke de kleurcoördinaten voor licht van elke golflengte binnen het zichtbare spectrum zodanig zijn gedefinieerd, dat zij grafisch kunnen worden weergegeven op een grafiek met orthogonale X-en 30 Y-assen onder vorming van wat bekend staat als CIE-kleurdia-gram. Dit kleurdiagram is weergegeven als fig. 1 in deze beschrijving. Fig. 1 toont de locus voor licht van elke golflengte (uitgedrukt in nanometers) binnen het zichtbare spectrum. Dit is bekend als de spectrumlocus, en licht, waarvan 35 de kleurcoördinaten voorkomen in de spectrumlocus hebben 100% zuiverheid van excitatie van de geschikte golflengte. De spec- 85021S2 i ï - 2 - trumlocus wordt gesloten door een lijn bekend als de’ purper-lijn, die de coördinaatposities op de spectrumlocus voor golflengten van 380 nm (violet) en 780 nm (rood) verbindt. Het oppervlak, ingesloten door de spectrumlocus en de purperlijn, 5 is het gebied dat beschikbaar is voor mogelijke kleurcoördi-naten van elk zichtbaar licht. De kleurcoördinaten van het licht, geëmitteerd door Illuminant C zijn eveneens in fig. 1 bij punt C uitgezet. Punt C (0,3101; 0,3163) is genomen om wit licht voor te stellen en heeft dienovereenkomstig een zero 10 zuiverheid van excitatie van kleur van elke golflengte. Het spreekt voor zich, dat vanuit punt C naar de spectrumlocus bij elke gewenste golflengte lijnen kunnen worden getrokken en dat elk punt, dat op een dergelijke lijn ligt, gedefinieerd kan worden niet alleen in termen van zijn X;Y-coördinaten, 15 doch ook in termen van de golflengtelijn, waarop het licht en zijn afstand van punt C ten opzichte van de totale lengte van die golflengtelijn. Dus het licht, dat is geëmitteerd door een gekleurde glasplaat, kan worden beschreven in termen van deze dominante golflengte en zijn zuiverheid van excitatie 20 uitgedrukt in procenten.When discussing the optical properties of a glass plate, it is usually necessary to relate these properties to a standard light source. For the purposes of the present specification, Illuminant C, determined by the International Lighting Commission (CIE), was used as the standard light source. Illuminant C is as good as an average daylight source with a color temperature of 6700K. The International Lighting Commission has also published "Colorimetry, Official Recommendations of the 25 International Commission on Illumination" (May 1970), which sets forth the theory of colorimetry, according to which the color coordinates for light of any wavelength within the visible spectrum are defined that they can be plotted on a graph with orthogonal X and 30 Y axes to form what is known as CIE color chart. This color chart is shown as Fig. 1 in this description. Fig. 1 shows the locus for light of any wavelength (expressed in nanometers) within the visible spectrum. This is known as the spectrum locus, and light, the color coordinates of which occur in the spectrum locus, have 100% purity of excitation of the appropriate wavelength. The spec 85021S2 i - 2 - drum locus is closed by a line known as the purple line, which connects the coordinate positions on the spectral locus for wavelengths of 380 nm (violet) and 780 nm (red). The area enclosed by the spectrum locus and the purple line 5 is the area available for possible color coordinates of any visible light. The color coordinates of the light emitted by Illuminant C are also plotted at point C in Fig. 1. Point C (0.3101; 0.3163) is taken to represent white light and accordingly has a zero purity of excitation of color of any wavelength. It goes without saying that lines can be drawn from point C to the spectrum locus at any desired wavelength and that each point lying on such a line can be defined not only in terms of its X; Y coordinates, but also in terms of the wavelength line, on which the light and its distance from point C to the total length of that wavelength line. Thus, the light emitted from a colored glass plate can be described in terms of this dominant wavelength and its excitation purity expressed in percent.
In feite hangen de CIE-coördinaten van het door een gekleurde glasplaat doorgelaten licht niet alleen van de samenstelling van het glas af, doch ook van de dikte van de plaat.In fact, the CIE coordinates of the light transmitted through a colored glass plate depend not only on the composition of the glass, but also on the thickness of the plate.
In de beschrijving en conclusies hebben de gegeven waarden 25 voor de kleurcoördinaten (X;Y) de zuiverheid van excitatie Ρε% en de dominerende golflengte van het doorgelaten licht, alsmede de zichtbare lichttransmissiefactor van het glas (LT) berekend van de specifieke interne transmissie (SIT) van een glasplaat met een dikte van 5 mm. De specifieke interne trans-30 missie van een glasplaat wordt enkel beheerst door de absorptie van het glas en kan worden uitgedrukt volgens de wet van Beer-Lambert voor een plaat met een dikte van 5 mm als SIT = e ' , waarin a de absorptiecoëfficiënt van het glas (cm”') is. Als eerste benadering kan SIT worden voorgesteld door de 35 formule (I3 + R2) / (I1 - R1) , waarin: 1^ de intensiteit van het zichtbare licht, dat valt op het eerste vlak van de glasplaat voorstelt; R^ de intensiteit van het zichtbare licht, dat wordt teruggekaatst door 350 2 1 62 - 3 - * .In the description and claims, the given values for the color coordinates (X; Y) have calculated the purity of excitation Ρε% and the dominant wavelength of the transmitted light, as well as the visible light transmission factor of the glass (LT) of the specific internal transmission ( SIT) of a glass plate with a thickness of 5 mm. The specific internal transmission of a glass plate is governed only by the absorption of the glass and can be expressed according to Beer-Lambert's law for a plate with a thickness of 5 mm as SIT = e ', where a is the absorption coefficient of the glass is (cm ”'). As a first approximation, SIT can be represented by the formula (I3 + R2) / (I1 - R1), in which: 1 ^ represents the intensity of the visible light falling on the first plane of the glass plate; R ^ the intensity of the visible light reflected by 350 2 1 62 - 3 - *.
dat vlak, voorstelt; de intensiteit van het zichtbare licht, dat wordt doorgelaten door het tweede vlak van de glasplaat is; terwijl R2 de intensiteit van zichtbaar licht, dat door dat tweede vlak inwendig wordt teruggekaatst, voorstelt.' 5 De onderhavige uitvinding heeft betrekking in het bijzonder op de samenstelling van de zogenaamde bronsglazen.that plane, represents; the intensity of the visible light transmitted through the second face of the glass plate; while R2 represents the intensity of visible light reflected internally by that second plane. " The present invention relates in particular to the composition of the so-called bronze glasses.
Veel samenstellingen zijn bekend voor de bereiding van bronsglazen met een dominante golflengte λβ ergens tussen 570 nm en 590 nm.Many compositions are known for the preparation of bronze glasses with a dominant wavelength λβ anywhere between 570 nm and 590 nm.
10 In het algemeen zijn de bekende bronsglazen gemaakt vanwege nun zonwerende eigenschappen, terwijl hun toepassing in glazen voorgevels van moderne gebouwen algemeen bekend is.Generally, the known bronze glasses have been made for their solar shading properties, while their use in glass facades of modern buildings is well known.
In verband met dergelijke glazen wordt gewezen op het Amerikaanse octrooischrift 4.104.076 (Saint-Gobain Industries, 15 corresponderend met het Franse octrooischrift 2.082.459) . Zoals in dat octrooischrift vermeld is, is het om architectonische redenen bijzonder gewenst, dat de zuiverheid van excitatie van het licht, dat door een venster uit een dergelijk glas wordt doorgelaten, niet te hoog is, teneinde een zo goed 20 mogelijke neutraliteit in de lichtgevende omgeving te behouden, met het gevolg, dat de zuiverheid van excitatie tot 14% dient te worden beperkt. Teneinde de vereiste mate van zonwering te bereiken, dient een 6,2 mm dikke plaat van het glas minder dan 50% van de opvallende zonne-energie door te laten, 25 waarbij de lichtfactor beperkt dient te worden teneinde dit doel te bereiken, doch dient groot genoeg te zijn voor het behouden van een aangenaam aspect en voor het doorlaten van vol-„ doende licht bij somber weer. Voor bronsglas dient de licht factor te liggen tussen 40% en 55%.In connection with such glasses, reference is made to U.S. Patent 4,104,076 (Saint-Gobain Industries, 15 corresponding to French Patent 2,082,459). As stated in that patent, it is particularly desirable for architectural reasons that the purity of excitation of the light transmitted through a window from such a glass is not too high, in order to achieve the best possible neutrality in the luminous environment, with the consequence that the purity of excitation should be limited to 14%. In order to achieve the required degree of shading, a 6.2 mm thick sheet of the glass must transmit less than 50% of the incident solar energy, whereby the light factor must be limited in order to achieve this goal, but large enough to maintain a pleasant aspect and to transmit sufficient light in bleak weather. For bronze glass, the light factor should be between 40% and 55%.
30 Andere samenstellingen voor het maken van brons glazen met speciale eigenschappen zijn eveneens voorgesteld.Other compositions for making bronze glasses with special properties have also been proposed.
Zo worden bijvoorbeeld in het Belgische octrooischrift No.For example, in the Belgian patent no.
848.372, Saint-Gobain Industries, glazen voorgesteld met een lichtfactor van 45-60%, een totale zonne-energiedoorlaatfac-35 tor van 35-55%, een dominante golflengte λβ tussen 578 nm en 583 nm, en een zuiverheid van excitatie Ρε tussen 20% en 35%, bij voorkeur tenminste 25%, voor toepassing voor glazen gebouwen, in het bijzonder winkelramen, waar een hoge mate van afscherming tegen warmte en ultraviolet vereist is.848,372, Saint-Gobain Industries, glasses proposed with a light factor of 45-60%, a total solar transmittance factor of 35-55%, a dominant wavelength λβ between 578 nm and 583 nm, and a purity of excitation Ρε between 20% and 35%, preferably at least 25%, for use in glass buildings, especially shop windows, where a high degree of shielding from heat and ultraviolet is required.
B502162B502162
» XX
- 4 -- 4 -
De onderhavige uitvinding beoogt het verschaffen van bronsglas, dat in het bijzonder geschikt is voor toepassing in beglaasd meubilair en dat in het bijzonder kan worden gebruikt voor de vervaardiging van planken in display- of andere 5 kabinetten. Voor dergelijke doeleinden is het van belang, dat het glas met de werkelijk toegepaste dikte een relatief hoog gedeelte van het opvallende licht doorlaat. Glas, dat wordt gebruikt voor planken, dienen gewoonlijk twee tot drie keer dikker te zijn dan glas, dat gebruikt voor vensters, waarbij 10 het lastig is gebleken te voldoen aan dit vereiste voor hoge doorlating onder het verkrijgen van een goede kleur en kleur-diepte, teneinde een kleurharmonie met diverse houtsoorten te verkrijgen, hetgeen eveneens belangrijk is.The present invention aims to provide bronze glass, which is particularly suitable for use in glazed furniture and which can be used in particular for the manufacture of shelves in display or other cabinets. For such purposes it is important that the glass with the actual thickness used transmits a relatively high part of the incident light. Glass used for planks should usually be two to three times thicker than glass used for windows, where it has been found difficult to meet this high transmittance requirement while obtaining good color and color depth , in order to obtain a color harmony with various woods, which is also important.
Het is een doel van de uitvinding een scala samen-15 stellingen te verschaffen voor de bereiding van bronsglazen, die voldoen aan de genoemde wensen.It is an object of the invention to provide a range of compositions for the preparation of bronze glasses that meet the aforementioned wishes.
De· uitvinding verschaft een gekleurd soda-limeglas, bestaande uit een basissamenstelling van de glasvormende bestanddelen samen met kleurstoffen, met het kenmerk, dat ten 20 minste drie van de metalen ijzer, seleen, kobalt, nikkel, chroom en mangaan in het glas als kleurstof aanwezig zijn in een hoeveelheid, die overeenkomt met de volgende gewichtsper-centages van het glasThe invention provides a colored soda-lime glass consisting of a basic composition of the glass-forming constituents together with dyes, characterized in that at least three of the metals iron, selenium, cobalt, nickel, chromium and manganese in the glass are used as a dye are present in an amount corresponding to the following weight percentages of the glass
Fe203 0,2 . tot 0,5 25 Se 0,0015 tot 0,0120Fe2 O3 0.2. to 0.5 Se 0.0015 to 0.0120
Co 0 tot 0,0020Co 0 to 0.0020
Ni 0 tot 0,0120Ni 0 to 0.0120
Cr203 * 0 tot 0,0220Cr203 * 0 to 0.0220
MnO 0 tot 0,4000, 30 de som: de hoeveelheid van het eventueel aanwezige Cr203 in het glas plus tien keer de hoeveelheid van het aanwezige Co in het glas dient ten minste 0,0100 gew.% van het glas te bedragen, terwijl de hoeveelheid van de kleurstoffen zodanig dient te zijn, dat het verkregen glas de volgende lichtdoor-35 latende eigenschappen heeft:MnO 0 to 0.4000, 30 the sum: the amount of any Cr2O3 present in the glass plus ten times the amount of the Co present in the glass should be at least 0.0100% by weight of the glass, while the amount of the dyes should be such that the resulting glass has the following light transmissive properties:
Zuiverheid van excitatie tussen 12% en 22% Dominante golflengte tussen 576 nm en 584 nmPurity of excitation between 12% and 22%. Dominant wavelength between 576 nm and 584 nm
Zichtbaar licht-doorlaat-factor ten minste 55%.Visible light transmission factor at least 55%.
85021tik.85021 tick.
; « - 5 -; «- 5 -
Glas volgens de uitvinding heeft een goede doorlating en kleur voor de beoogde doeleinden.Glass according to the invention has good transmittance and color for the intended purposes.
In feite kan glas met globaal dezelfde kleureigenschappen bij en onder de ondergrens van de dominerende golf-5 lengte worden bereid onder toepassing van nikkel als enige of voornaamste kleurstof, waarbij nikkel aanwezig is in een hoeveelheid van ca. 0,1 gew.% van het glas. De aanwezigheid van dergelijke grote hoeveelheden nikkel is echter nadelig, in het bijzonder waar het glas dient te worden bereid volgens 10 de drijfmethode. In de drijfmethode wordt een glasstrook gelegd langs het oppervlak van een gesmolten tinbad, terwijl dit heet is, zodat zijn oppervlak praktisch echt vlak en evenwijdig wordt. Teneinde oxidatie van het tin aan het oppervlak van het bad te voorkomen, hetgeen zal leiden tot tinoxide, 15 dat door de strook zou worden opgenomen, wordt boven het bad een reducerende atmosfeer gewaarborgd. Wanneer het glas een zodanig grote hoeveelheid nikkel bevat, zou dit ten dele worden gereduceerd door de atmosfeer boven het tinbad, hetgeen resulteert in een onaanvaardbare waas in het verkregen glas.In fact, glass with roughly the same color properties at and below the lower limit of the dominant wavelength can be prepared using nickel as the sole or major dye, with nickel being present in an amount of about 0.1% by weight of the glass. However, the presence of such large amounts of nickel is disadvantageous, especially where the glass is to be prepared by the float method. In the float method, a glass strip is laid along the surface of a molten tin bath while it is hot, so that its surface becomes practically flat and parallel. In order to prevent oxidation of the tin on the surface of the bath, which will lead to tin oxide, which would be absorbed by the strip, a reducing atmosphere is ensured above the bath. When the glass contains such a large amount of nickel, it would be partially reduced by the atmosphere above the tin bath, resulting in an unacceptable haze in the resulting glass.
20 Dit nadeel is niet of nauwelijks aanwezig wanneer de hoeveelheid nikkel in het glas beperkt is tot 0,0120%, zoals in de onderhavige uitvinding, hetgeen betekent, dat glas volgens de uitvinding gevormd kan worden tot platen volgens de drijfmethode, alsmede volgens andere klassieke trekmethoden. Van-25 zelfsprekend kan glas volgens de uitvinding ook gevormd worden tot andere producten, bijvoorbeeld holle producten.This drawback is not or hardly present when the amount of nickel in the glass is limited to 0.0120%, as in the present invention, which means that glass according to the invention can be formed into plates according to the floating method, as well as according to other classic pulling methods. It goes without saying that glass according to the invention can also be formed into other products, for instance hollow products.
In sommige voorkeursuitvoeringsvormen van de uitvinding is Cr2Og praktisch afwezig, terwijl Co in het glas aanwezig is in een hoeveelheid van ten minste 0,0010 gew.% van 30 het glas. Dit maakt het mogelijk, dat de zichtbare lichtdoor-laatfactor van het glas kan worden verlaagd in die uitvoeringsvormen volgens de uitvinding waar het gewenst is. Dit is, omdat de toevoeging van kobalt binnen de vermelde hoeveelheden de toevoeging van grotere hoeveelheden ijzer en seleen moge-35 lijk maakt, wederom binnen de aangegeven grenzen zonder de noodzaak van grote verandering in de positie op het CIE-dia-gram. De reden hiervoor is, dat het kleureffect van kobalt zodanig kan worden gearrangeerd, dat het in evenwicht komt met dat van ijzer en seleen. In feite 2ijn de kleureffecten van 8302162 ♦ l - 6 - de diverse kleurstoffen, beoogd voor toepassing in een glas volgens de uitvinding, als volgt ("Le Verre", Horst Scholze, Trans. J. Le Dü, Institut du Verre, Paris 1969) .In some preferred embodiments of the invention, Cr2Og is practically absent, while Co is present in the glass in an amount of at least 0.0010% by weight of the glass. This allows the visible light transmission factor of the glass to be lowered in those embodiments of the invention where it is desired. This is because the addition of cobalt within the stated amounts allows the addition of larger amounts of iron and selenium, again within the stated limits without the need for large change in position on the CIE diagram. The reason for this is that the color effect of cobalt can be arranged to balance that of iron and selenium. In fact, the color effects of 8302162-1-6 - the various dyes intended for use in a glass according to the invention are as follows ("Le Verre", Horst Scholze, Trans. J. Le Dü, Institut du Verre, Paris 1969 ).
IJzer. IJzer is in feite aanwezig in praktisch alle 5 commercieel bereid glazen, hetzij als verontreiniging, hetzij als bewust toegevoegde kleurstof. De aanwezigheid van 3 +Iron. Iron is in fact present in practically all 5 commercially prepared glasses, either as an impurity or as a deliberately added dye. The presence of 3+
Fe -ionen in glas geeft aanleiding tot geringe absorptie van zichtbaar licht met een korte golflengte en tot een zeer sterke absorptieband in het ultraviolet gebied, terwijl de aan- 2+ 10 wezigheid van Fe -ionen aanleiding geeft tot sterke absorptie in het infrarood. Ferri-ionen geven aan het glas een zachtgele kleur, terwijl ferro-ionen aan glas een sterkere groenblauwe kleur geven.Fe ions in glass give rise to low absorption of short wavelength visible light and to a very strong absorption band in the ultraviolet region, while the presence of Fe ions gives rise to strong absorption in the infrared. Ferric ions give the glass a soft yellow color, while ferrous ions give glass a stronger green-blue color.
4 +4+
Seleen. Het Se -kation heeft praktisch geen kleur- 15 effect, terwijl het ongeladen Se^-element een rose kleur 2- geeft. Het Se -anion vormt een chromofoor met de eventueel aanwezige ferri-ionen en dit geeft aanleiding tot een bruinrode kleur bij glas.Selenium. The Se cation has practically no color effect, while the uncharged Se 2 element gives a pink color 2. The Se anion forms a chromophore with any ferric ions present and this gives rise to a brown-red color in glass.
Kobalt. De groep [co^O^] geeft een intens blauwe 20 kleur onder oplevering van een dominante golflengte, die praktisch tegenovergesteld is aan die welke wordt veroorzaakt door ij zer-seleenchromofoor.Cobalt. The group [co ^ O ^] gives an intense blue color to yield a dominant wavelength, which is practically opposite to that caused by iron-selenium chromophore.
Nikkel. De groep [Νί^Ο.] geeft aanleiding tot eenNickel. The group [Νί ^ Ο.] Gives rise to one
** T T** T T
blauwe kleur, terwijl de groep [Ni^Ogl tot een gele kleur 25 van het glas aanleiding geeft.blue color, while the group [Ni ^ Ogl gives rise to a yellow color of the glass.
Chroom. De aanwezigheid van het coördinaat [Cr ±Og] geeft aanleiding tot absorptiebanden bij 650 nm onder oplevering van een heldergroene kleur. Sterke oxidatie geeft aanleiding tot het coördinaat [CrVI0^ t dat een zeer intensieve 30 absorptieband oplevert bij 365 nm onder oplevering van een gele kleur.Chrome. The presence of the coordinate [Cr ± Og] gives rise to absorbance bands at 650 nm to yield a bright green color. Strong oxidation gives rise to the coordinate [CrVI0 ^ t which yields a very intensive absorbance band at 365 nm to yield a yellow color.
2 +2+
Mangaan. Mn -ionen hebben geen bijzonder kleureffect, en dit is de normale toestand, waarin mangaan in glas voorkomt. Echter in een glas, dat rijk is aan alkalimetaalionen, komt de 35 groep [Mnx x0g] voor, die een violette kleur geeft.Manganese. Mn ions do not have a special color effect, and this is the normal state in which manganese occurs in glass. However, in a glass, which is rich in alkali metal ions, the group [Mnx x0g] occurs, which gives a violet color.
In de uitvoeringsvormen volgens de uitvinding, die de meeste voorkeur verdienen, is MnO in het glas aanwezig in een hoeveelheid van ten minste 0,0400 gew.% van het glas. Dat de toevoeging van dergelijke grote hoeveelheden mangaan gewenst 8502162 J * - 7 - zou zijn is bijzonder verrassend. Tot nu toe werd gedacht, dat de toevoeging van grote hoeveelheden mangaan zou leiden tot ongewenste solarisatie-effecten. Omdat mangaan slechts een zeer gering kleureffect heeft bij toevoeging aan gewoon 5 soda-limeglas zou het voor de hand liggen, dat er geen beperking is voor de toevoeging van mangaan. Het is echter thans gevonden, dat zulke hoeveelheden mangaan kunnen worden toegevoegd zonder solarisatie en wel met een aanzienlijk voordeel.In the most preferred embodiments of the invention, MnO is present in the glass in an amount of at least 0.0400% by weight of the glass. That the addition of such large amounts of manganese would be desirable is 8502162 J * 7 - is particularly surprising. Until now it was thought that the addition of large amounts of manganese would lead to unwanted solarization effects. Since manganese has only a very small color effect when added to ordinary soda lime glass, it would be obvious that there is no restriction on the addition of manganese. However, it has now been found that such amounts of manganese can be added without solarization and with considerable advantage.
De toevoeging van dergelijke hoeveelheden mangaan blijkt een 10 indirecte werking te hebben op de vorming van ijzer-seleen-chromofoor. Het wordt thans aangenomen, dat dit het geval is, omdat de toevoeging van mangaan een stabiliserend effect op de partiële zuurstofdruk in het glas heeft. Of dit nu waar is of niet, het feit blijft, dat tengevolge van de aanwezigheid 15 van dergelijke hoeveelheden mangaan de vorming van het ijzer-seleenchromofoor in geringere mate wordt beïnvloed door veranderingen in de smeltomstandigheden, in het bijzonder de atmosfeer binnen de glassmeltoven, hetgeen belangrijke praktische voordelen biedt.The addition of such amounts of manganese appears to have an indirect effect on the formation of iron-selenium chromophore. This is now believed to be the case because the addition of manganese has a stabilizing effect on the oxygen partial pressure in the glass. Whether or not this is true, the fact remains that due to the presence of such amounts of manganese, the formation of the iron-selenium chromophore is less affected by changes in melting conditions, especially the atmosphere within the glass melting furnace, which offers important practical benefits.
20 Het aanwezig zijn van gunstige eigenschappen voor de primair beoogde doeleinden wordt bevorderd wanneer een of meer van de volgende voorkeursfactoren in acht wordt genomen.The presence of beneficial properties for the primary intended purposes is promoted when one or more of the following preferred factors are taken into account.
I. ^r2^3 ket glas aanwezig in een hoeveelheid van ten minste 0,0120 gew.% van het glas, terwijl Co in het glas 25 aanwezig is in een hoeveelheid van 0 tot 0,0015 gew.% van het glas. Een dergelijk glas heeft een groenere tint, hetgeen zeer goed harmonieert met bepaalde houtsoorten, zoals mahonie.I. ^ r2 ^ 3 the glass is present in an amount of at least 0.0120 wt.% Of the glass, while Co is present in the glass in an amount of 0 to 0.0015 wt.% Of the glass. Such a glass has a greener tint, which harmonizes very well with certain types of wood, such as mahogany.
II. De zuiverheid van excitatie van het door het glas doorgelaten licht is maximaal 20% en bij voorkeur 18%. Een 30 zuiverheid van excitatie binnen dergelijke grenzen komt overeen met een meer neutraal aspect.II. The purity of excitation of the light transmitted through the glass is a maximum of 20% and preferably 18%. A purity of excitation within such limits corresponds to a more neutral aspect.
III. Cr2°3 Praktisch afwezig in het glas, Ni is aanwezig in een hoeveelheid tussen 0,0030 en 0,0115 gew.% van het glas, Se in een hoeveelheid van 0,0040-0,0080 gew.% van 35 het glas, terwijl de zuiverheid van excitatie van het door het glas doorgelaten licht ten minste gelijk is aan 16%. Dergelijke glazen hebben een warme tint, hetgeen bijzonder harmonieert met houtsoorten met een lichte kleur.III. Cr2 ° 3 Practically absent in the glass, Ni is present in an amount between 0.0030 and 0.0115 wt% of the glass, Se in an amount of 0.0040-0.0080 wt% of the glass, while the purity of excitation of the light transmitted through the glass is at least 16%. Such glasses have a warm tint, which harmonizes particularly with light-colored woods.
IV. Se is aanwezig in een hoeveelheid van 0,0030-0,0080 3502 1 'oiIV. Se is present in an amount of 0.0030-0.0080 3502-1000
VV
- 8 - gew.% van het glas. Bij een dergelijke hoeveelheid aan selenium is het mogelijk aan glas een warme tint mee te geven op een - economische wijze. Seleen is een kostbaar ingrediënt, reden waarom grote hoeveelheden seleen aan glas niet worden 5 toegevoegd. Binnen het aangegeven gebied kan seleen in het glas worden opgenomen zonder te veel verkwisting.- 8% by weight of the glass. With such an amount of selenium it is possible to impart a warm tint to glass in an economical manner. Selenium is a costly ingredient, which is why large amounts of selenium are not added to glass. Within the specified range, selenium can be incorporated into the glass without too much waste.
V. Ni is in het glas aanwezig in een hoeveelheid van ten minste 0,0080 gew.% van het glas. Het volgen van dit aspect maakt het mogelijk, dat de hoeveelheid Cr203 kan worden 10 verminderd of achterwege gelaten, terwijl een bepaalde kleur wordt behouden: toename van het Ni-gehalte accentueert de kleur en maakt de harmonisatie met diverse houtkleuren mogelijk.V. Ni is present in the glass in an amount of at least 0.0080% by weight of the glass. Following this aspect allows the amount of Cr 2 O 3 to be reduced or omitted while retaining a certain color: increasing the Ni content accentuates the color and allows harmonization with various wood colors.
VI. Het glas geeft een dominante golflengte tussen 580 nm 15 en 584 nm aan doorgelaten licht. Dergelijk glas heeft een relatief neutrale bruine tint: zijn kleur is minder aangenaam voor een gegeven zuiverheid van excitatie.VI. The glass gives a dominant wavelength between 580 nm and 584 nm in transmitted light. Such glass has a relatively neutral brown tint: its color is less pleasant for a given purity of excitation.
De onderhavige uitvinding zal thans nader worden beschreven aan de hand van de bijgaande tekeningen, waarin: 20 Fig. 1 een basis CIE-kleurdiagram weergeeft, terwijlThe present invention will now be described in more detail with reference to the accompanying drawings, in which: FIG. 1 represents a basic CIE color chart, while
Fig. 2 een detail op grotere schaal van een deel van dat diagram weergeeft.Fig. 2 shows an enlarged detail of part of that diagram.
In fig. 1 is de uitgezette spectrumlocus, waarop de coördinaatpunten van licht met zuiverheid van excitatie Ρε = 25 100% van alle zichtbare dominante golflengten XD van 380 nm tot 780 nm en de rechte purperlijn, die de eindpunten van de spectrumlocus verbindt, is reeds beschreven, alsmede ook de locatie van punt C, hetgeen wit licht weergeeft met een zuiverheid van excitatie van Ρε = 0 voor alle golflengten. In fig. 1 30 zijn voorts afgeheeld dominante golflengtelijnen van 570 nm en 590 nm en een rechthoek, die het oppervlak van het diagram, dat in fig. 2 op grotere schaal aanwezig is, voorstelt.In Fig. 1, the plotted spectrum locus at which the coordinate points of light with purity of excitation Ρε = 25 is 100% of all visible dominant wavelengths XD from 380 nm to 780 nm and the straight purple line connecting the end points of the spectral locus is already as well as the location of point C, which represents white light with an excitation purity of Ρε = 0 for all wavelengths. Also shown in FIG. 130 are dominant wavelength lines of 570 nm and 590 nm and a rectangle representing the area of the diagram, which is more widely represented in FIG. 2.
In fig. 2 zijn diverse dominante golflengtelijnen tussen 570 nm en 590 nm weergegeven, alsmede diverse loci van 35 constante zuiverheid van excitatie P tussen 10% en 22%. Het door conclusie 1 gedefinieerde gebied, zuiverheid van excitatie Ρε tussen 12% en 22% dominante golflengte λβ tussen 576 nm en 584 nm is eveneens aangegeven.In Fig. 2, various dominant wavelength lines between 570 nm and 590 nm are shown, as well as various loci of constant purity of excitation P between 10% and 22%. The range defined by claim 1, purity of excitation Ρε between 12% and 22%, dominant wavelength λβ between 576 nm and 584 nm is also indicated.
850216k - 9 - ♦850216k - 9 - ♦
Fig 2 toont bovendien coördinatiepunten van diverse voorbeelden van glas overeenkomstig de uitvinding, waarvan nadere bijzonderheden in de volgende tabellen zijn vermeld.In addition, Fig. 2 shows coordination points of various examples of glass according to the invention, details of which are given in the following tables.
De door lagere letters i, j. en t aangegeven punten komen over-5 een met voorbeelden I, J en T na solarisatie.The points indicated by lower letters i, j and t correspond with examples I, J and T after solarization.
Thans volgens bepaalde specifieke voorbeelden van glassamenstellingen volgens de uitvinding.Now according to certain specific examples of glass compositions according to the invention.
De volgende tabel A toont basisglassamenstellingen van de diverse voorbeelden, terwijl tabellen B-E het volgende 10 laten zien: I. Voorraadsamenstellingen van glasvormers voor smelten teneinde glas volgens de uitvinding te bereiden. De hoeveelheden materialen zijn aangegeven in tonnen voor de bereiding van 1000 ton glas.The following Table A shows base glass compositions of the various examples, while Tables B-E show the following: I. Stock compositions of melt glassmakers to prepare glass according to the invention. The quantities of materials are indicated in tons for the preparation of 1000 tons of glass.
15 II. Kleurstoffen worden aan de voorraad toegevoegd. De hoeveelheden van materialen zijn aangegeven in kilogrammen voor de bereiding van 1000 ton glas. In feite zijn de kleurstoffen niet noodzakelijk toe te voegen in de aangegeven vorm. Het is echter gebruikelijk en conventioneel de toegevoegde 20 hoeveelheden kleurstoffen aan te geven als hun molaire equivalenten in de vermelde vorm.15 II. Dyes are added to the stock. The amounts of materials are indicated in kilograms for the preparation of 1000 tons of glass. In fact, the dyes are not necessarily to be added in the indicated form. However, it is common and conventional to indicate the amounts of dyes added as their molar equivalents in the stated form.
III. Gewichtshoeveelheden van de kleurstoffen in het bereide glas, bepaald volgens röntgenstraal-fluorescentieana-lyse van het glas en omgezet in moleculaire gegevens, zijn 25 vermeld.III. Weights of the dyes in the prepared glass, determined by X-ray fluorescence analysis of the glass and converted into molecular data, have been reported.
IV. Een indicatie van de optische eigenschappen van het bereide glas in termen van X?Y-coördinaten op het CIE-kleur-diagram, de dominante golflengte nm en de zuiverheid van excitatie Ρε% van het door het glas doorgelaten licht en de 30 zichtbare lichtdoorlaatfactor van glas zijn alle berekend uit de specifieke inwendige doorlaat van een 5 mm dikke glasplaat .IV. An indication of the optical properties of the prepared glass in terms of X? Y coordinates on the CIE color diagram, the dominant wavelength nm and the purity of excitation Ρε% of the light transmitted through the glass and the visible light transmission factor of glass are all calculated from the specific internal passage of a 5 mm thick glass plate.
V. Een indicatie van de optische eigenschappen van sommige van de voorbeelden van het bereide glas, nadat zij zijn 35 onderworpen aan een solarisatiebehandeling. Deze behandeling bestond uit bestraling van de proefstukken van het glas gedurende een vermeld aantal uren onder gebruikmaking van een 125 watt Philips HPR lamp.V. An indication of the optical properties of some of the examples of the prepared glass after they have been subjected to a solarization treatment. This treatment consisted of irradiating the test specimens of the glass for a specified number of hours using a 125 watt Philips HPR lamp.
? 5 0 216 2 * - 10 -? 5 0 216 2 * - 10 -
TABEL ATABLE A
Basisglasanalyse (gew.%)Basic glass analysis (wt%)
VOORBEELD A tot G H,I,J,N,P,R K,L,M,S,TEXAMPLES A to G H, I, J, N, P, R K, L, M, S, T
Si02 72,45 71,5 70,8 5 A1203 1,55 1,55 0,9SiO2 72.45 71.5 70.8 5 Al2 O3 1.55 1.55 0.9
CaO 8,05 8,05 8,7CaO 8.05 8.05 8.7
Mg O 4,0 4,0 4,7Mg O 4.0 4.0 4.7
Na20 13,2 14,2 14,1 K20 0,1 0,1 0,2 10 S03 de rest de rest de rest 3502162 - 11 -Na20 13.2 14.2 14.1 K20 0.1 0.1 0.2 10 SO3 the rest, the rest, the rest 3502 162 - 11 -
TABEL BTABLE B
VOORBEELD - A_B_C_D_EEXAMPLE - A_B_C_D_E
Glasvormers (tonnen) zand 682/17 682,17 682,17 682,17 682,17 5 veldspaat 71,1 71,1 71,1 71,1 71,1 kalksteen 42,2 42,2 42,2 42,2 42,2 dolomiet 185,9 185,9 185,9 185,9 185,9Glass formers (tons) of sand 682/17 682.17 682.17 682.17 682.17 5 feldspar 71.1 71.1 71.1 71.1 71.1 limestone 42.2 42.2 42.2 42.2 42.2 dolomite 185.9 185.9 185.9 185.9 185.9
Na2C03 195,2 195,2 195,2 195,2 195,2 sulfaat 13,0 13,0 13,0 10,0 10,0 10 nitraat 11,25 11,25 11,25 15,0 15,0Na2 CO3 195.2 195.2 195.2 195.2 195.2 sulfate 13.0 13.0 13.0 10.0 10.0 10 nitrate 11.25 11.25 11.25 15.0 15.0
Kleurstoffen (kg) berekend als:Dyes (kg) calculated as:
Fe203 3000 3000 3000 3000 3000Fe203 3000 3000 3000 3000 3000
CoO 0 0 17 17 17CoO 0 0 17 17 17
NiO 38 63,5 38 38 38 15 Se 225 750 225 750 750 K2Cr207 241 241 0 0 135NiO 38 63.5 38 38 38 15 Se 225 750 225 750 750 K2Cr207 241 241 0 0 135
Mn02 00000Mn02 00000
Kleurstoffen (gew.% in glas na analyse berekend als)Dyes (wt% in glass after analysis calculated as)
Fe203 0,365 0,365 0,363 0,372 0,373 20 Co - 0,0010 · 0,0010 0,0011Fe203 0.365 0.365 0.363 0.372 0.373 20 Co - 0.0010 0.0010 0.0011
Ni 0,0039 0,0043 0,0028 0,0036 0,0028Ni 0.0039 0.0043 0.0028 0.0036 0.0028
Se 0',0029 0,0041 0,0035 0,0058 0,0034 ^r2®3 0,0137 0,0123 Sporen - 0,0070Se 0 ', 0029 0.0041 0.0035 0.0058 0.0034 ^ r2®3 0.0137 0.0123 Traces - 0.0070
MnO - 25 x 0,3382 0,3467 0,3400 0,3488 0,3339 Y 0,3456 0,3500 0,3396 0,3439 0,3395 XD nm 577 578,7 580,7 582,3 577,9 Ρε % 15,4 18,9 14,3 -17,8 12,6 LT % 70,76 66,98 65,21 62,45 68,33 55 5 0 2 1 6 2 51 -12-.MnO - 25 x 0.3382 0.3467 0.3400 0.3488 0.3339 Y 0.3456 0.3500 0.3396 0.3439 0.3395 XD nm 577 578.7 580.7 582.3 577.9 Ρε% 15.4 18.9 14.3 -17.8 12.6 LT% 70.76 66.98 65.21 62.45 68.33 55 5 0 2 1 6 2 51 -12-.
TABEL CTABLE C
VOORBEELD_F_G_H_I_JEXAMPLE_F_G_H_I_J
Glasvormers (tonnen) zand 682,17 682,17 672,17 672,17 672,17 5 veldspaat 71,1 71,1 71,1 71,1 71,1 kalksteen 42,2 42,2 42,2 42,2 42,2 dolomiet 185,9 185,9 185,9 185,9 185,9Glass formers (tons) of sand 682.17 682.17 672.17 672.17 672.17 5 feldspar 71.1 71.1 71.1 71.1 71.1 limestone 42.2 42.2 42.2 42.2 42.2 dolomite 185.9 185.9 185.9 185.9 185.9
Na2C03 197,1 195,2 211,5 211,5 211,5 sulfaat 7,5 10,0 13,3 13,3 13,3 10 nitraat 15,0 15,0 13,3 13,3 13,3Na2 CO3 197.1 195.2 211.5 211.5 211.5 sulfate 7.5 10.0 13.3 13.3 13.3 10 nitrate 15.0 15.0 13.3 13.3 13.3
Kleurstoffen (kg) berekend alsDyes (kg) calculated as
Fe203 3000 3000 2310 1810 1400Fe203 3000 3000 2310 1810 1400
CoO 17 17 17 17 17'CoO 17 17 17 17 17 '
NiO 38 90 114 114 114 15 Se 520 375 525 525 375 K2Cr20? 96 241NiO 38 90 114 114 114 15 Se 520 375 525 525 375 K2Cr20? 96 241
MnO- — — — 1220 1220 _ ___MnO- - - - 1220 1220 _ ___
Kleurstoffen (gew.% in glas na analyse berekend als)Dyes (wt% in glass after analysis calculated as)
Fe203 0,360 0,362 0,302 0,254 0,214 .Fe203 0.360 0.362 0.302 0.254 0.214.
20 Co 0,0011 0,0010 0,0009 0,0010 0,0010Co 0.0011 0.0010 0.0009 0.0010 0.0010
Ni 0,0031 0,0059 0,0082 0,0102 0,0100Ni 0.0031 0.0059 0.0082 0.0102 0.0100
Se 0,0075 0,0051 0,0035 0,0055 0,0042Se 0.0075 0.0051 0.0035 0.0055 0.0042
Cr203 0,0054 - 0,0126Cr2 O3 0.0054 - 0.0126
MnO - 0,1020 0,1000 25 X 0,3509 0,3496 0,3425 0,3435 0,3375 y 0,3475 0,3458 0,3475 0,3428 0,3383 XD nm 581,3 581,6 578,1 580,8 580,6 Ρε % 19,3 18,5 17,1 16,09 13,28 LT % 61,42 60,90 62,44 64,33 67,47 30 En na solarisatie (i) (j) tijd (uren) 167 167 X 0,3432 0,3374 Y 0,3427 0,3381 ad nm 580,7 580,6 35 Ρε % 15,9 13,15 LT % 63,95 67,19 8502162 * .?·MnO - 0.1020 0.1000 25 X 0.3509 0.3496 0.3425 0.3435 0.3375 y 0.3475 0.3458 0.3475 0.3428 0.3383 XD nm 581.3 581.6 578 , 1 580.8 580.6 Ρε% 19.3 18.5 17.1 16.09 13.28 LT% 61.42 60.90 62.44 64.33 67.47 30 And after solarization (i) ( j) time (hours) 167 167 X 0.3432 0.3374 Y 0.3427 0.3381 ad nm 580.7 580.6 35% 15.9 13.15 LT% 63.95 67.19 8502162 *. ?
- 13 -TABEL D- 13 TABLE D
VOORBEELD_K_L_M_N_PEXAMPLE_K_L_M_N_P
Glasvormers (tonnen) zand 682,17 682,17 682,17 672,17 672,17 5 veldspaat 35,06 35,06 35,06 79,9 79,9 kalksteen 32,52 32,52 32,52 42,2 42,2 dolomiet 223,48 223,48 223,48 185,9 185,9Glass formers (tons) of sand 682.17 682.17 682.17 672.17 672.17 5 feldspar 35.06 35.06 35.06 79.9 79.9 limestone 32.52 32.52 32.52 42.2 42.2 dolomite 223.48 223.48 223.48 185.9 185.9
Na2C03 212,05 212,05 212,05 211,5 211,5 sulfaat 11,73 11,73 11,73 13,3 13,3 10 nitraat 12,05 12,05 12,05 13,3 13,3Na2 CO3 212.05 212.05 212.05 211.5 211.5 Sulphate 11.73 11.73 11.73 13.3 13.3 10 Nitrate 12.05 12.05 12.05 13.3 13.3
Kleurstoffen (kg) berekend alsDyes (kg) calculated as
Fe203 2310 2310 2310 1810 1810Fe203 2310 2310 2310 1810 1810
CoO 19 19 19 17 17CoO 19 19 19 17 17
NiO 127 127 127 114 114 15 Se 300 525 150 525 525 K2Cr2°7NiO 127 127 127 114 114 15 Se 300 525 150 525 525 K2Cr2 ° 7
Mn02 - - - 2440 3660Mn02 - - - 2440 3660
Kleurstoffen (gew.% in glas na analyse berekend als)Dyes (wt% in glass after analysis calculated as)
Fe203 0,302 0,307 0,301 0,263' 0,252 20 Co 0,0013 0,0013 0,0013 0,0011 0,0011Fe203 0.302 0.307 0.301 0.263 0.252 20 Co 0.0013 0.0013 0.0013 0.0011 0.0011
Ni 0,0102 0,0108 0,0115 0,0095 0,0085Ni 0.0102 0.0108 0.0115 0.0095 0.0085
Se 0,0048 0,00645 0,0039 0,0075 0,0078Se 0.0048 0.00645 0.0039 0.0075 0.0078
Cr203 "Cr203 "
MnO Sporen Sporen - 0,1830 0,2630 25 X 0,3456 0,3489 0,3426 0,3411 0,3426 Y 0,3435 0,3452 0,3420 0,3410 0,3424 λ0 nm 581,2 581,7 580,8 580,7 580,6 Ρε % 16,84 18,18 15,63 14,94 15,75 LT % 60,52 59,18 62,82 65,56 65,01 850 2 1 Si Λ - 14 - TABEL Ε VOORBEELD_R_S_T_MnO Traces Tracks - 0.1830 0.2630 25 X 0.3456 0.3489 0.3426 0.3411 0.3426 Y 0.3435 0.3452 0.3420 0.3410 0.3424 λ0 nm 581.2 581, 7 580.8 580.7 580.6 Ρε% 16.84 18.18 15.63 14.94 15.75 LT% 60.52 59.18 62.82 65.56 65.01 850 2 1 Si Λ - 14 - TABLE Ε EXAMPLE_R_S_T_
Glasvormers (tonnen) zand 672,17 682,17 682,17 5 veldspaat 79,9 35,06 35,06 kalksteen 42,2 32,52 32,52 dolomiet 185,9 223,48 223,48Glass formers (tons) of sand 672.17 682.17 682.17 5 feldspar 79.9 35.06 35.06 limestone 42.2 32.52 32.52 dolomite 185.9 223.48 223.48
Na2C03 211,5 212,05 212,05 sulfaat 13,3 11,73 11,73 10 nitraat 13,3 12,05 12,05Na2 CO3 211.5 212.05 212.05 sulfate 13.3 11.73 11.73 10 nitrate 13.3 12.05 12.05
Kleurstoffen (kg) berekend alsDyes (kg) calculated as
Pe-O-, 1810 2310 3000 2 3Pe-O-, 1810 2310 3000 2 3
CoO 17 19 17CoO 17 19 17
NiO 114 127 114 15 Se 525 375 375 K2Cr2°7NiO 114 127 114 15 Se 525 375 375 K2Cr2 ° 7
Mn02 4880 1220 488Mn02 4880 1220 488
Kleurstoffen (gew.% in glas na analyse berekend als)Dyes (wt% in glass after analysis calculated as)
Pe203 0,255 0,308 0,353 20 Co 0,0011 0,0012 0,0014Pe203 0.255 0.308 0.353 20 Co 0.0011 0.0012 0.0014
Ni 0,0092 0,0109 . 0,0084Ni 0.0092 0.0109. 0.0084
Se 0,0066 0,0060 0,0070Se 0.0066 0.0060 0.0070
Cr2°3Cr2 ° 3
MnO 0,3630 0,1030 0,0450 25 X 0,3388 0,3460 0,3553 Y , 0,3410 0,3458 0,3503 λ0 nm 579,6 580,3 581,6 Ρε % 14,35 17,56 21,26 LT % 65,86 62,18 56,18 30 En na solarisatie (t) tijd (uren) 119 X , 0,3553 Y 0,3507 λβ nm 581,4 35 Ρε % 21,38 LT % _ 56,12 8502162MnO 0.3630 0.1030 0.0450 25 X 0.3388 0.3460 0.3553 Y, 0.3410 0.3458 0.3503 λ0 nm 579.6 580.3 581.6 Ρε% 14.35 17. 56 21.26 LT% 65.86 62.18 56.18 30 And after solarization (t) time (hours) 119 X, 0.3553 Y 0.3507 λβ nm 581.4 35 Ρε% 21.38 LT% _ 56.12 8502162
Claims (10)