NL8003872A

NL8003872A - Wax emulsion compsn. for preparing wall surface prior to papering - allowing good adhesion and easy peeling

Info

Publication number: NL8003872A
Application number: NL8003872A
Authority: NL
Original assignee: Zinsser William & Co
Priority date: 1979-07-23
Filing date: 1980-07-04
Publication date: 1981-01-27
Also published as: BE884415A

Abstract

Compsn. for prepg. a wall surface to ensure good adhesion between that surface and a subsequently applied wall covering while allowing easy removal of the covering by pulling comprises an aqs. dispersion contg. a wax, an emulsifier and a film-forming polymer. Pref. the mixt. of wax and emulsifier has a m.pt. >=80, pref. >=100 degrees C, and amt. of polymer is 8-12 wt.% w.r.t. wax. Compsn. is also storage stable and does not tend to flow after application.

Description

( * * “ -1- 21383/Vk/mv(* * “-1- 21383 / Vk / mv

Aanvrager: William Zinsser & Co., Inc., Sommerset, New Jersey, Verenigde Staten van Amerika.Applicant: William Zinsser & Co., Inc., Sommerset, New Jersey, USA.

Korte aanduiding: Werkwijze voor het aanbrengen van een deklaag op een wand en het hierbij te gebruiken preparaat.Short indication: Method for applying a coating on a wall and the preparation to be used for this.

55

De uitvinding heeft betrekking op een preparaat dat aangebracht kan worden op een oppervlak voordat behang en de hierbij te gebruiken pasta worden opgebracht zodat een goede hechting wordt bewerkstelligd van het behang op het oppervlak terwijl het behang · toch makkelijk kan 10 worden verwijderd, door aftrekken waarbij het preparaat een stabiele emulsie is. De uitvinding heeft verder betrekking op een werkwijze voor het aanbrengen van een laag zoals behang op een te bedekken oppervlak en op een werkwijze voor het bereiden van het preparaat.The invention relates to a composition which can be applied to a surface before applying wallpaper and the paste to be used therewith, so that a good adhesion of the wallpaper to the surface is achieved while the wallpaper can still be easily removed, by subtracting the preparation is a stable emulsion. The invention further relates to a method for applying a layer such as wallpaper to a surface to be covered and to a method for preparing the preparation.

Wandbekledingsmateriaal zoals behang wordt tegenwoordig uit 15 een groot aantal materialen vervaardigd en is verkrijgbaar in diverse kwaliteiten en patronen. De keuze is nagenoeg onbeperkt. Veel mensen aarzelen echter om behang te gebruiken omdat ze weten dat een groot deel van het werk samenhangt met het verwijderen van het behang wanneer het moet worden vernieuwd. Er zijn de laatste jaren een aantal voorstellen 20 gedaan om dit probleem te overwinnen en hierbij zijn diverse materialen toegepast die zouden kunnen worden verwijderd en een van die oplossingen gaf een materiaal omde wand te bedekken waardoor een goede verwijdering van het behangsel mogelijk was. Van veel behangselsoorten wordt gezegd dat deze verwijderbaar zijn dank zij de bekleding die aan de achterkant is 25 aangebracht. De vinyl-type behangsoorten die een plastische film hebben op het oppervlak , bijvoorbeeld een kunstmatige deklaag aan de achterzijde' waardoor het tot zekere mate verwijderbaar zijn wanneer het behang wordt aangebracht op wanden die op de juiste wijze zijn geprepareerd.Wallcovering material such as wallpaper is nowadays made from a large number of materials and is available in various qualities and patterns. The choice is virtually unlimited. However, many people hesitate to use wallpaper knowing that much of the work involves removing the wallpaper when it needs to be refreshed. A number of proposals have been made in recent years to overcome this problem, using various materials that could be removed, and one of those solutions provided a material to cover the wall allowing good removal of the wallpaper. Many types of wallpaper are said to be removable thanks to the back coating. The vinyl-type wall coverings that have a plastic film on the surface, for example an artificial backing on the back, which makes it removable to some extent when the wallpaper is applied to walls that have been properly prepared.

Zelfs met deze grondlaag kunnen de vinyl-type behangsoorten niet makkelijk 30 worden verwijderd van bepaalde oppervlakken zoals kwalitatief minder goed wandbord, dat vaak toegepast wordt bij nieuwe constructies. Papierhoudend behang kan gewoonlijk niet worden gebruikt samen met deze bekleding en zodoende is ook dit moeilijk te verwijderen,. Zelfs wanneer echter een dergelijke deklaag is aangebracht is het niet makkelijk verwijderbaar van 35 kwalitatief minder goed wandbord.Even with this primer, the vinyl-type wallcoverings cannot easily be removed from certain surfaces, such as a lower quality wallboard, which is often used in new constructions. Paper-based wallpaper cannot usually be used in conjunction with this coating and is therefore difficult to remove. However, even when such a covering layer is applied, it is not easy to remove the wall plate of lesser quality.

Een eerdere oplossing voor dit probleem heeft men voorgesteld met de bereiding van een samenstelling die gebaseerd is op een dispersie van carnaubawas in water. De samenstelling werd aangebracht op een wand- 8003872 -2- 21383/Vk/mv oppervlak voordat behang werd aangebracht en hiermee kon een goede verwijdering worden verkregen van het behang van de aldus behandelde wand.An earlier solution to this problem has been proposed with the preparation of a composition based on a dispersion of carnauba wax in water. The composition was applied to a wall 8003872-2-21383 / Vk / mv surface before wallpaper was applied and this allowed good removal of the wallpaper from the thus treated wall.

Deze samenstelling had echter een relatief beperkte houdbaarheid en de emulsie had de neiging cm te destabiliseren, vaak voordat deze emulsie kon 5 worden verkocht of gebruikt . Bovendien had het product een slechte stabiliteit bij vriezen en ontdooien en was niet bestendig tegen de over-gang van vriezen naar dooien. Op dezelfde wijze was de samenstelling niet bestendig tegen temperaturen boven 40 °C die normaal plaats hebben bij het vervoeren en gebruik van producten van dit type. 'Bovendien had deze 10 bekende samenstelling een aantal nadelen die direct het gebruik nadelig beïnvloeden. Op de eenste plaats had het hierop aangebrachte behang de neiging om hiervan af te glijden bij zowel hoge als lage temperatuur. Dit resulteerde in spleten bij de uiteinden van het behang. Bovendien was er het probleem, en dit was ernstiger, van het vroegtijdig loslaten. Zodoende 15 kan gesteld worden dat hoewel met deze samenstelling het behang makkelijk op een gewenst tijdstip kon worden verwijderd het niet de noodzakelijke hechteigenschappen had om een goede hechting mogelijk te maken van het behang gedurende de normale tijdsperiode tot het tijdstip dat het behang moest worden verwijderd.However, this composition had a relatively limited shelf life and the emulsion tended to destabilize many times before this emulsion could be sold or used. In addition, the product had poor freezing and thawing stability and was not resistant to the transition from freezing to thawing. Likewise, the composition was not resistant to temperatures above 40 ° C which normally occur when transporting and using products of this type. Moreover, this known composition had a number of drawbacks which directly affect the use. In the first place, the wallpaper applied to it tended to slip off at both high and low temperature. This resulted in gaps at the ends of the wallpaper. In addition, there was the problem, and this was more serious, of premature letting go. Thus, it can be stated that while with this composition the wallpaper could be easily removed at a desired time, it did not have the necessary adhesive properties to allow good adhesion of the wallpaper during the normal period of time until the wallpaper was to be removed.

20 Een van de doelstellingen van de uitvinding is het verkrij gen van een verbeterde samenstelling voor een preparaat dat aangebracht kan worden op wanden voordat behang hierop wordt aangebracht zodat een goede hechting kon worden bewerkstelligd van het behang op de wand terwijl het bovendien mogelijk was om het behang makkelijk te. verwijderen wanneer 25 dit gewenst was.One of the objects of the invention is to obtain an improved composition for a composition which can be applied to walls before wallpaper is applied thereon, so that a good adhesion of the wallpaper to the wall could be achieved while, moreover, it was possible to wallpaper easy to. remove when desired.

Een andere» doelstelling volgens de uitvinding is het verkrijgen van een .preparaatsamenstelling die aangebracht moet worden op wanden voordat behang wordt aangebracht waardoor een goede hechting mogelijk werd van het behang op de wand zonder dat er een afglijden plaatshad 30 bij hoge of lage temperaturen en toch een makkelijk verwijderbaarheid van het behang mogelijk was op een gewenst tijdstip.Another object of the invention is to obtain a composition composition to be applied to walls before wallpaper is applied, allowing good adhesion of the wallpaper to the wall without slipping at high or low temperatures and yet easy removal of the wallpaper was possible at a desired time.

Verder wordt .gestreefd volgens de uitvinding naar het verkrijgen van een preparaatsamenstelling die kan worden aangebracht op wanden voordat behang wordt opgebracht waardoor een goede hechting wordt bewerk.-35 stelligd van behang op de wand terwijl het behang makkelijk kan worden verwijderd door het van de wand af te trekken waarin de samenstelling stabiel blijft gedurende een lange periode onder mogelijke wisselingen van de opslagtemperatuur die normaal plaats heeft bij het bereiden en het gebruik 8003872 * * -3- 21383/Vk/mv van deze samenstelling.Furthermore, according to the invention the aim is to obtain a composition composition which can be applied to walls before applying wallpaper, thereby ensuring a good adhesion of wallpaper to the wall, while the wallpaper can be easily removed by removing it from the wall in which the composition remains stable for a long period of time under possible changes of the storage temperature that normally occurs in the preparation and use of 8003872 * * -3- 21383 / Vk / mv of this composition.

Ook wordt in het kader van de uitvinding gestreefd naar het verkrijgen van een werkwijze voor het aanbrengen van behang op een wand waarbij deze wand eerst wordt geprepareerd voordat behang wordt aangebracht 5 met welk preparaat een goede hechting wordt bewerkstelligd van het behang op de wand terwijl dit later moet kunnen worden verwijderd wanneer dit gewenst ie. Ook wordt gestreefd naar een werkwijze voor het aanbrengen van behang op een wand waarbij het behang goed hecht op het wandoppervlak maar \ hiervan toch makkelijk kan worden verwijderd wanneer dit gewenst is.Within the scope of the invention, the aim is also to obtain a method for applying wallpaper to a wall, wherein this wall is first prepared before wallpaper is applied, with which preparation ensures a good adhesion of the wallpaper to the wall while this it should be possible to delete it later if desired ie. We also strive for a method for applying wallpaper to a wall, in which the wallpaper adheres well to the wall surface, but can still be easily removed from it if this is desired.

10 Deze en andere doelstellingen volgens de uitvinding kunnen worden bewerkstelligd met een preparaat volgens de uitvinding en wordt hierdoon gekenmerkt dat het preparaat is samengesteld uit water als continue fase een was, gedispergeerd in het water, een emulgeermiddel in een voldoende hoeveelheid om een emulsiestabiliteit te verkrijgen en een in water disper-15 geerbaar filmvormend polymeer in een hoeveelheid die effectief is om een evenwicht te vormen tussen de hechting en het verwijderen van het preparaat en daarbij de hechting van het behang verbetert terwijl het verwijderen toch makkelijk uitvoerbaar is. De uitvinding heeft verder betrekking op een werkwijze voor het prepareren voor een oppervlak voordat hierop behang wordt 20 aangebracht welke werkwijze hieruit bestaat dat het preparaat zoals boven aangegeven wordt aangebracht op het oppervlak en dit oppervlak wordt gedroogd voordat het behang wordt aangebracht. Volgens een bij voorkeur toegepaste uitvoeringsvorm is de was polyethyleenwas met een hoge dichtheid en het film-vormende polymeer is een oplosbaar zout van een acrylzuurcopolymeer.These and other objects according to the invention can be achieved with a composition according to the invention and is characterized in that the composition is composed of water as a continuous phase wax, dispersed in the water, an emulsifying agent in an amount sufficient to obtain an emulsion stability and a water-dispersible film-forming polymer in an amount effective to balance the adhesion and removal of the composition thereby improving the adhesion of the wallpaper while still being easy to perform. The invention further relates to a method of preparing for a surface before wallpaper is applied to it, which method consists in that the preparation as stated above is applied to the surface and this surface is dried before the wallpaper is applied. In a preferred embodiment, the wax is high density polyethylene wax and the film-forming polymer is a soluble salt of an acrylic acid copolymer.

25 De in deze samenhang gebruikt uitdrukking "behang” heeft be trekking op diverse.soorten behang zoals vervaardigd uit papier, vinyl, weefsel en folieachtcg materiaal evenals op behang waarbij een combinatie van materialen wordt toegepast, Het behang kan zuiver decoratief zijn of beschermend of worden toegepast om commerciële of andere informatie over 30 te brengen. Hoewel de verdere beschrijving zal zijn gericht op het aanbrengen van behang op wanden moet de uitdrukking "viand” alle mogelijk oppervlakken omvatten met inbegrip van reclameborden en ook niet verticale oppervlakken, zals plafonds, en de toepassing van het behang op deze oppervlakken is bij een dergelijke werkwijze inbegrepen.The term "wallpaper" as used in this context refers to various types of wallpaper such as made of paper, vinyl, fabric and foil material as well as to wallpaper using a combination of materials. The wallpaper may be purely decorative or protective used to convey commercial or other information about 30. Although the further description will focus on applying wallpaper to walls, the term "viand" should include all possible surfaces including billboards and also non-vertical surfaces, such as ceilings, and the application of the wallpaper to these surfaces is included in such a method.

35 De samenstelling van het preparaat volgens de uitvinding is een stabiele emulsie die eerst wordt aangebracht en deze vormt een stabiele grondlaag waarop het behang wordt gehecht met behulp van een geschikt wandbedekkend kleefmiddel. Met een "stabiele emulsie" wordt een emulsie be- 8003872 -4- 21383/Vk/mv doeld die niet ontleedt onder normale omstandigheden bij transport en opslag gedurende redelijke tijdsduren voor producten van dit type.Met name verdient het voorkeur dat de emulsie stabiel blijft gedurende ten minste drie cycli waarbij een overgang plaats heeft van vriezen naar dooien en 5 dat de emulsie bestendig is tegen bewaren bij temperaturen zelfs van 40 °C gedurende een periode van ten minste 30 dagen. Verder moet de emulsie bestendig zijn tegen scheiding gedurende ten minste 2 jaren wanneer de emulsie wordt opgeslagen onder meer gewone omstandigheden met name een tempera-oo tuur tussen 5 C en 35 C. Met "stabiliteit gedurende de beoogde tijsduur" 10 wordt bedoeld dat de wandbedekking die wordt aangebracht over de prepa-raatsamenstelling a) niet verschuift bij hoge of lage temperatuur, te weten bij een temperatuur tot ongeveer 50 °C, b) niet vroegtijdig loslaat en c) makkelijk kan worden verwijderd wanneer dit gewenst is. Deze eigenschappen moeten niet significant wijzigen na 5 jaren vanaf het tijdstip dat de 15 eigenschappen zijn bepaald.The composition of the composition according to the invention is a stable emulsion which is applied first and forms a stable primer on which the wallpaper is adhered using an appropriate wall covering adhesive. By "stable emulsion" is meant an emulsion 8003872-4-21383 / Vk / mv that does not decompose under normal conditions of transport and storage over reasonable periods of time for products of this type. In particular, it is preferred that the emulsion remain stable for at least three cycles with a transition from freezing to thawing and the emulsion being resistant to storage at temperatures as high as 40 ° C for a period of at least 30 days. Furthermore, the emulsion must be resistant to separation for at least 2 years when the emulsion is stored under more ordinary conditions, in particular a temperature between 5 ° C and 35 ° C. By "stability for the intended duration of time" is meant that the wall covering applied over the composition composition a) does not slip at high or low temperature, i.e. at a temperature up to about 50 ° C, b) does not release prematurely and c) is easily removable if desired. These properties should not change significantly after 5 years from the time the properties are determined.

Bij de wekrwijze volgens de uitvinding en bij het toegepaste preparaat is het gebruik van een was van belang die een voldoende hoog smeltpunt heeft en voldoende stabiel is wat betreft de fysische eigenschappen om bestendig te zijn tegen verschuiven en stabiel bij zowel hoge als 20 lage temperaturen. Bij voorkeur moet de was wanneer deze gemengd wordt met het emulgeermiddel en het adhesie-modificerend, filmvormend polymeer volgens de uitvinding een smeltpunt hebben boven 80 °C ai bij voorkeur boven 100 °C. Het is hierbij van belang om een onderscheid te maken tussen deze wassoorten die een hoog smeltpunt hebben in de oorspronkelijke 25 toestand maar geen voldoende hoog smeltpunt of bestendigheid tegen afschuiven wanneer deze gemengd worden met effectieve hoeveelheden van een emulgeermiddel en adhesie-modificatieraiddel, filmvormend polymeer volgens de uitvinding. Van de verschillende wassoorten die toegepast kunnen worden kunen worden genoemd natuurlijke was zoals carnabauwas, montanwas, bijen-30 was, candelillawas,schellakwas en dergelijke , synthetische wassoorten zoals polyethyleenwas, bij voorkeur polyethyleen met een hoge dichtheid, polypropyleenwas, polyoxyethyleenglycolwas, die in de handel gebracht is onder het merk Carbowas, Fisbher-Tropschwas, hetgeen een katalylitisch reactieproduct is van koolmonoxyde en waterstof, vetzure aminen en derge-35 lijke. Petroleumwassoorten zoals paraffinen en microkristallijne was <?n dergelijke en diverse combinaties hiervan. De keuze van een bepaalde wassoort is niet van kritisch belang, zolang de was een voldoende hoog smeltpunt heeft wanneer deze gemengd wordt met de andere componenten van de 8003872 <ρ· -c -5- 21383/Vk/mv samenstelling en voldoende fysische eigenschappen behoudt om het verschuiven te voorkomen bij lage en hoge temperaturen.Wanneer economische omstandigheden een rol spelen of andere factoren het gebruik van aanzienlijke hoeveelheden van een was met een laag /smeltpunt noodzakelijk maken, is het 5 mogelijk om deze was met een voldoende hoeveelheid van een of meer hoger smeltende wassoorten te mengen ter verkrijging van een mengsel met het gewenste smeltpunt.In the method of the invention and in the composition used, it is important to use a wax which has a sufficiently high melting point and is sufficiently stable in physical properties to be slip resistant and stable at both high and low temperatures. Preferably, when mixed with the emulsifying agent and the adhesion-modifying film-forming polymer of the invention, the wax should have a melting point above 80 ° C and preferably above 100 ° C. It is important here to distinguish between these waxes which have a high melting point in the original state but do not have a sufficiently high melting point or shear resistance when mixed with effective amounts of an emulsifying agent and adhesion modifying agent, film-forming polymer of the invention. Among the various waxes that can be used are mentioned natural waxes such as carnabao wax, montan wax, bee wax, candelilla wax, shellac wax and the like, synthetic waxes such as polyethylene wax, preferably high density polyethylene, polypropylene wax, polyoxyethylene glycol wax, which are commercially available has been marketed under the trademark Carbowas, Fisbher-Tropschwas, which is a catalytic reaction product of carbon monoxide and hydrogen, fatty acid amines and the like. Petroleum waxes such as paraffins and microcrystalline waxes and the like and various combinations thereof. The choice of a particular wax type is not critical, as long as the wax has a sufficiently high melting point when mixed with the other components of the 8003872 <ρ · -c -5- 21383 / Vk / mv composition and maintains sufficient physical properties to prevent shifting at low and high temperatures. When economic conditions come into play or other factors necessitate the use of significant amounts of a low / melting point wax, it is possible to wash it with a sufficient amount of one or more to mix more higher melting waxes to obtain a mixture having the desired melting point.

Bij voorkeur wordt een wassoort toegepast zoals polyethyleenwas * met een hoge dichtheid die een smeltpunt heeft van'100-140 °C. De meest 10 bij voorkeur toegepaste was is polyethyleenwas met een hoge dichtheid van een soort die een dichtheid heeft van 0,94 tot ongeveer 0,99 en met een smeltpunt boven ongeveer 100 °C. Een voorbeeld' van een dergelijk geschikt materiaal is polyethyleenwas met een hoge dichtheid in de handel gebracht door Allied Chemical .onder de aanduiding AC 392 en AC 316 en 15 de wassoort in de handel gebracht door American Hoechst, onder de aanduiding VP PED 121.Preferably, a wax such as high density polyethylene wax * having a melting point of 100-140 ° C is used. The most preferred wax is high density polyethylene wax of a kind having a density of from 0.94 to about 0.99 and a melting point above about 100 ° C. An example of such a suitable material is high-density polyethylene wax marketed by Allied Chemical under the designation AC 392 and AC 316 and the wax type marketed by American Hoechst, under the designation VP PED 121.

Verder is het bij de uitvinding van belang'dat een emulgeer- middel aanwezig is in het preparaat waarmme een stabiele emulsie kan worden verkregen zoals boven is aangegeven. Van de geschikte emulgeermiddelen 20 kunnen worden genoemd aminehoudende zepen zoals triethanolaminestearafcen, oleaten of mengsels van dergelijke verbindingen. Ook zijn metaalzepen geschikt die in wezen anionische emulgeermiddelen zijn zoals de natrium- en kaliustearaten, de oleaten en gemengde vetzure zepen en dergelijke.Furthermore, it is important in the invention that an emulsifying agent is present in the composition with which a stable emulsion can be obtained as indicated above. Among the suitable emulsifying agents 20 may be mentioned amine-containing soaps such as triethanolamine stearafcen, oleates or mixtures of such compounds. Also suitable are metal soaps which are essentially anionic emulsifying agents such as the sodium and potassium tearates, the oleates and mixed fatty acid soaps and the like.

Op dezelfde wijze kunnen niet ionogene emulgeermiddelen worden gebruikt 25 zoals polyoxyethyleen of polyoxypropyleenderivaten van organische zuren, alkoholen, alkylfenolen, amines en dergelijke verbindingen. Geëthoxyleerde alkylfenolen zijn met name geschikt gebleken, welke stoffen in de handel zijn onder de merkaanduiding Igepal van GAF Corporation. Een bij voorkeur toegepaste geëthoxyleerde alkylfenol als emulgeermiddel wordt aangegeven 30 als Igepal CO. 710 en bevat 10 mol ethyleenoxyde per mol fenol en C1QH_0 alkylgroepen. Evenals bij de wassoorten is niet gebleken dat een »y jy bepaald emulgeermiddel een kritische invloed heeft op de samenstelling van het preparaat volgens de uitvinding. Het is echter wel van belang dat een emulgeermiddel aanwezig is in een zodanige hoeveelheid dat deze 35 effectief is om een stabiele emulsie te bewerkstelligen. Omdat de hoeveelheden van de verschillende emulgeermiddelen afhankelijk zullen zijn van het bepaalde systeem waarin ze worden toegepast, zijn geen verdere numerieke grenzen aangegeven voor de algemene toepassing. De mate van 8003872 -6- 21383/Vk/mv effectiviteit kan echter makkelijk worden bepaald en zal gelegen zijn bij een hoeveelheid van ongeveer 10 tot ongeveer 30 % gebaseerd pp de gewichtshoeveelheid was.Likewise, nonionic emulsifiers such as polyoxyethylene or polyoxypropylene derivatives of organic acids, alcohols, alkylphenols, amines and the like compounds can be used. Ethoxylated alkyl phenols have been found to be particularly suitable which are commercially available under the trademark Igepal from GAF Corporation. A preferred ethoxylated alkyl phenol as an emulsifying agent is designated Igepal CO. 710 and contains 10 moles of ethylene oxide per mole of phenol and C14H10 alkyl groups. As with the waxes, it has not been found that a specific emulsifier has a critical influence on the composition of the composition according to the invention. However, it is important that an emulsifying agent is present in an amount such that it is effective to effect a stable emulsion. Since the amounts of the different emulsifiers will depend on the particular system in which they are used, no further numerical limits are indicated for the general application. However, the degree of 8003872-21383 / Vk / mv effectiveness can be easily determined and will be in an amount of from about 10 to about 30% based on pp weight amount.

Hoewel het mogelijk is om een preparaat samen te stellen dat een 5 goede verwijdering mogelijk maakt van het behang van de wand onder toepassing van alleen een was en een emulgeermiddel in een waterige emulsie hebben dergelijke smenstellingen de neiging om een vroegtijdige losmaking te bewerkstelligen van het behang omdat hiermee geen oppervlaktelaag wordt verkregen waaraan de kleeftaiddelen voor het behang goed hechten.While it is possible to formulate a composition that allows good removal of the wallpaper from the wall using only a wax and an emulsifier in an aqueous emulsion, such blends tend to effect premature detachment from the wallpaper because this does not provide a surface layer to which the adhesives for the wallpaper adhere well.

10 Om dit nadeel te overwinnen omvat het preparaat volgens de uitvinding als een noodzakelijke stof een filmvormerrd polymeer materiaal dat de oppervlakte eigenschappen van de aangebrachte samenstelling modificeert zodat een evenwicht wordt verkregen tussen de hechting van de samenstelling zodat het behang op de gewenste wijze kan hechten terwijl anderzijds 15 toch een makkelijke verwijdering kan worden uitgevoerd. Het filmvorrnende polymere materiaal wordt toegepast in een hoeveelheid die effectief is cm het evenwicht te ’ bewerkstelligen tussen de hechting van de samenstel-ling'en waarbij de hechting van het behang wordt verbeterd terwijl dit toch makkelijk kan worden verwijderd.To overcome this drawback, the composition according to the invention comprises as a necessary substance a film-forming polymeric material that modifies the surface properties of the applied composition so that a balance is achieved between the adhesion of the composition so that the wallpaper can adhere in the desired manner while on the other hand, an easy removal can nevertheless be carried out. The film-forming polymeric material is used in an amount effective to balance the adhesion of the compositions while improving the adhesion of the wallpaper while still being easy to remove.

20 Van de filmvorrnende polymere stoffen die geschikt zijn voor dit doel kunnen worden genoemd, acrylharsoplossingen emulsies hiervan, poly-vinylacetaatpolymeren of copolymeren in emulsie, polyvinylalkoholpoly-meer of copplymeer in emulsie, styreen-malelnezuuranhydridepolymeren en andere geschikte in water of in een alkalische stof oplosbare natuur-25 lijke en synthetische polymeren.Bij voorkeur worden de oplosbare zouten van acrylzuurcopolymeren toegepast met zuurwaarden tussen ongeveer 60 en 180 evenals styreenJmalelnezuuranhydridecopolymeren. Het verdient de voorkeur om hoeveelheden te gebruiken van 8 tot ongeveer 15% van het filmvorrnende polymere materiaal , gebaseerd op het gewicht van de was.Among the film-forming polymeric materials suitable for this purpose can be mentioned acrylic resin solutions emulsions thereof, polyvinyl acetate polymers or emulsion copolymers, polyvinyl alcohol polymer or emulsion copolymer, styrene-maleic anhydride polymers and other suitable water or alkaline soluble natural and synthetic polymers. Preferably, the soluble salts of acrylic acid copolymers are used with acid values between about 60 and 180 as are styrene maleic anhydride copolymers. It is preferable to use amounts of from 8 to about 15% of the film-forming polymeric material based on the weight of the wax.

30 Met behulp van de gegevens van het hierna vermelde voorbeeld II en kennis van een bepaald.systeem zal het mogelijk zijn om de effectieve hoeveelheid te bepalen om een evenwicht te bewerkstelligen met betrekking tot de hechting. De hechting van de preparaatsamenstelling zal worden beschouwd als zijnde "in evenwicht" voor een bepaald type behang en behangkleefsel 35 wanneer het behang niet zal verschuiven op de wand bij hoge en lage temperaturen en de kracht die nodig is om het bahng van de wand te verwijderen bij voorkeur 30 tot 90% en in het bijzonder 40 tot 60 % zal zijn van de trekkrachtlimiet van het behang. Met andere woorden geldt dat de samenstel- 8003872 -7- 21383/Vk/mv lingen volgens de uitvinding een voldoende hoeveelheid van een modificatie-middel ten aanzien van de hechting moet bevatten om het behang beter hechtend te-maken aan de wand dan deze zou zijn zonder toepassing van het preparaat, maar dat het verwijderen van het behang mogelijk moet zijn 5 zonder dat het gaat scheuren.Using the data from Example 2 below and knowledge of a particular system, it will be possible to determine the effective amount to achieve an equilibrium with regard to adhesion. The adhesion of the composition composition will be considered to be "in balance" for a particular type of wallpaper and wallpaper 35 if the wallpaper will not shift on the wall at high and low temperatures and the force required to remove the bahng from the wall preferably 30 to 90% and in particular 40 to 60% will be the tensile limit of the wallpaper. In other words, the compositions of the invention must contain a sufficient amount of an adhesion modifier in order to make the wallpaper more adhesive to the wall than it would. without application of the preparation, but that the wallpaper must be able to be removed 5 without cracking.

Desgewenst kunnen de eigenschappen van het preparaat volgens de uitvinding *.die van belang zijn voor het vernederen verder worden verbeterd onder toevoeging van een materiaal dat het verwijderen zal be- \ vorderen. Hiertoe kunnen kleine hoeveelheden het verwijderen bevorderende 10 middelen worden toegevoegd zoals siliconolie, met'name Dow Corning 17, microfijn verdeelde polytetrafluorethyleenpolyrceren zoals in de handel gebracht door Micro Powders Ine onder de merkaanduiding Polyfluo 400, calcium-, natrium- en magnesiumstearaten, oliesoorten en amides zoals in de handel gebracht door Kraftco onder de merkaanduiding Kemamide 15 E erucamide en Kemamide F stearamide, welke stoffen effectief zijn gebleken.If desired, the properties of the composition of the invention * which are important for humiliation can be further improved with the addition of a material which will aid removal. To this end, small amounts of the promoters may be added such as silicone oil, especially Dow Corning 17, microfine dispersed polytetrafluoroethylene polymer as marketed by Micro Powders Ine under the trade designation Polyfluo 400, calcium, sodium and magnesium stearates, oils and amides as marketed by Kraftco under the brand designation Kemamide 15 E erucamide and Kemamide F stearamide, which substances have proven effective.

Ter verkrijging van een stabiliteit bij het vriezen en dooien evenals om de eigenschappen van de wassen te modificeren en het vermogen om de samenstelling te bevochtigen verdient het de voorkeur om een meerwaardige alkohol toe te voegen zoals glycerol, ethyleenglycol,propyleen-20 glycol en butyleenglycol of een ester van een van deze stoffen. Het is gebleken dat wanneer ongeveer 2 tot ongeveer 4% van deze stoffen wordt toegepast«berekend op de hoeveelheid water in de emulsie,dit een verbeterde vries-dooistabiliteit zal bewerkstelligen. Bovendien is gebleken dat bepaalde stoffen effectief zijn bij het remmen of voorkomen van 25 de microbiologische gréei in afhankelijkheid van de concentratie en de activiteit van het water van de oplossing.In order to obtain freezing and thawing stability as well as to modify the properties of the waxes and the ability to wet the composition, it is preferable to add a polyhydric alcohol such as glycerol, ethylene glycol, propylene glycol and butylene glycol or an ester of one of these substances. It has been found that when about 2 to about 4% of these materials are used, based on the amount of water in the emulsion, it will achieve improved freeze-thaw stability. In addition, certain substances have been found to be effective in inhibiting or preventing microbiological growth depending on the concentration and activity of the water of the solution.

Ook kunnen pigment-vulmiddelen worden toegepast bij het preparaat volgens de uitvinding zoals silicaten, mica, calciumcarbènaat, klei, titaandioxyde ai andere hiermee > vergelijkbare stoffen. Deze pigment -30 vulmiddelen kunnen een gewenste kleur geyen aan het preparaat, hetgeen van belang is bij het opbrengen van het preparaat zodat men door de kleur-indicatie kan zien hoeveel en waar het preparaat is aangebracht op het oppervlak.Pigment fillers can also be used in the preparation according to the invention, such as silicates, mica, calcium carbonate, clay, titanium dioxide and other similar substances. These pigment fillers can impart a desired color to the composition, which is important when applying the composition so that the color indication shows how much and where the composition has been applied to the surface.

Wanneer het gewenst is om het preparaat te verpakken zonder 35 steralisatie na het verpakken of wanneer het preparaat wordt gebruikt uit een reeds geopende houder kan het noodzakelijk zijn om een effectieve hoeveelheid van een middel ter bestrijding_van barteriën of andere verduurzamende middelen om de microbiologische verontreiniging tegen te gaan.When it is desired to package the preparation without sterilization after packaging, or when the preparation is used from an already opened container, it may be necessary to use an effective amount of an anti-barter or other preservative to prevent microbiological contamination. to go.

8003872 -8- 21383/Vk/mv8003872 -8- 21383 / Vk / mv

Geschikte raeeldauWbestrrdende stoffen zijn fenyikwikacetaat, 2-(-4-thiazo-'lyl)benzimidazool, organometallische complexen en dergelijke. Van de geschikte bacteriebestrijdende middelen kunnen worden genoemd natriumortho-fenylfenol, 1-(3,1-chlooralkyl)triazo-1-azoniadamantaanchloride, 2-(-5 hydroxymethyl)-amino-2-methylpropanol en dergelijke. Zoals boven aangegeven kunnen de meerwaardige alkoholen en esters ten minste gedeeltelijk effectief zijn voor het regelen van de microbiële groei.Suitable window dusts are phenylic mercury acetate, 2 - (- 4-thiazollyl) benzimidazole, organometallic complexes and the like. Among the suitable bactericidal agents may be mentioned sodium ortho-phenylphenol, 1- (3,1-chloroalkyl) triazo-1-azonia adamantane chloride, 2 - (- 5 hydroxymethyl) amino-2-methylpropanol and the like. As noted above, the polyvalent alcohols and esters can be at least partially effective in controlling microbial growth.

Het is ook bij bepaalde toepassingen van belang dat het pse-peraat' een geschikte viscositeit heeft zodat het Makkelijk is aan te brengen, 10 Het is uit de gedane experimenten gebleken dat samenstellingen met een puddingachtige consistentie makkelijker zijn aan te brengen zonder dat veel wordt geknoeid. Hiertoe kunnen verdikkingsmiddelen worden toegevoegd zoals cellulosehoudende verdikkingsmiddelen met name -methylcellulose en hydroxypropylcellulose, polysacchariden, polyacrylzuren. kleisoorten en 15 andere dergelijke verdikkingsmiddelen. Het bij voorkeur toegepaste verdikkingsmiddel is hydroxypropylcellulose.It is also important in certain applications that the peptate 'has a suitable viscosity so that it is easy to apply. 10 The experiments done have shown that compositions with a pudding-like consistency are easier to apply without much spillage . Thickeners can be added for this purpose, such as cellulosic thickeners, in particular -methylcellulose and hydroxypropylcellulose, polysaccharides, polyacrylic acids. clays and 15 other such thickeners. The preferred thickener is hydroxypropyl cellulose.

Ook is het vanbelang:met het oog op het bereiden van de samenstelling, onder vermijding van ongewenst hoge kosten voor ontluchtingsorganen, dat antischuimmiddelen worden toegevoegd. Een aantal hiervoor bekende stoffen 20 zijn in de handel verkrijgbaar. Hiervan kunnen worden genoemd Colloid 688, hetgeen een olie-wasmengsel is, Foamkill FBF, hetgeen op pretroleum is gebaseerd en Troykyd 666. Andere dergelijke stoffen zijn van het sili-contype en kunnen ook worden toegepast in effectieve hoeveelheden om de schuimvorming te onderdrukken.It is also important: in order to prepare the composition, while avoiding undesirably high costs for deaerators, that anti-foaming agents are added. A number of known materials 20 are available commercially. Among these can be mentioned Colloid 688, which is an oil-wax mixture, Foamkill FBF, which is pre-oil based and Troykyd 666. Other such materials are of the silicone type and can also be used in effective amounts to suppress foaming.

25 Bij het bereiden van het preparaat volgens de uitvinding is het van voordeel ora eerst een emulsie van was in water te bereiden. Dit kan worden bewerkstelligd op een hiertoe 'geschikte wijze door het toevoegen van de was aan water of water aan was. Hoewel de omstandigheden voor het emulgeren kunnen worden gekozen evenals het emulgeermiddel en de was verdient 30 het de voorkeur om het water te verwarmen tot een temperatuur die ten minste voldoende is om de was in gesmolten toestand te houden tijdens het mengen. Omdat de bij voorkeur toegepaste wasssoorten smeltpunten hebben ' boven het kookpunt van water kan het mengen onder een druk boven atmosferische druk noodzakelijk zijn wanneer een van deze wassoorten wordt toegepast. Het mengen 35 wordt bij vorkeur uitgevoerd in een menger waarin hoge afschuifkrachten kunnen worden bewerkstelligd, welke menger op zich bekend is en waarbij gewerkt kan worden bij een druk tussen ongeveer 5 tot 10 atmosfeer. Het water, het emulgeermiddel en de was worden bij voorkeur gemengd in geschikte 8003872 -9- 21383/Vk/rav hoeveelheden bij verhoogde temperatuur gedurende een voldoende tijd om een homogene emulsie te verkrijgen en vervolgens gedurende een periode van 5 minuten tot een uur om een stabiele emulsie te verkrijgen. De verkregen emulsie wordt vervolgens toegepast om het preparaat samen te stellen 5 door. het hieraan toevoegen van de andere componenten voor of na afkoelen. Bij voorkeur wordt de emulsie afgekoeld voordat andere stoffen hiermee worden gemengd en het roeren of mengen wordt tijdens het. afkoelen voortgezet. Een voorbeeld van een dergelijke samenstelling en de trajecten waarin deze componenten kunnen worden gebruikt blijkt uit de gegevens van 10 tabel A.When preparing the preparation according to the invention it is advantageous to first prepare an emulsion of wax in water. This can be accomplished in a suitable manner by adding the wax to water or water to wax. Although the emulsification conditions can be selected as well as the emulsifying agent and the wax, it is preferable to heat the water to a temperature at least sufficient to keep the wax in the molten state during mixing. Since the preferred waxes have melting points above the boiling point of water, mixing at a pressure above atmospheric pressure may be necessary when using one of these waxes. Mixing is preferably carried out in a mixer in which high shear forces can be effected, which mixer is known per se and which can be operated at a pressure between about 5 to 10 atmospheres. The water, the emulsifying agent and the wax are preferably mixed in suitable 8003872-9383 / Vk / rav aliquots at elevated temperature for a sufficient time to obtain a homogeneous emulsion and then for a period of 5 minutes to an hour to stable emulsion. The resulting emulsion is then used to formulate the composition by. adding to it the other components before or after cooling. Preferably, the emulsion is cooled before other substances are mixed with it and stirring or mixing is made during the process. cooling continued. An example of such a composition and the ranges in which these components can be used is shown in the data in Table A.

TABEL ATABLE A

component ____gew.%__ filmvormend polymeer (25% vaste stof in oplossing) 5 tot 15 15 verdikkingsmiddel 0,1 tot 0,3 ontschuimingsmiddel 0,5 tot 1 vulmiddel op basis van klei 1 tot 3 glycolen 2 tot 4 bacteriostatisch middel 0,1 tot 0,2 20 schimmelbestrijdend middel 0,05 tot 0,1 water 10 tot 20 was-emulsie of dispersie (35% "raste stof) 60 tot 80 losmaakmiddel 0,1 tot 0,2 kleurstof 0,1 tot 0,2 25 I___component ____ wt% __ film-forming polymer (25% solid in solution) 5 to 15 thickener 0.1 to 0.3 defoaming agent 0.5 to 1 clay filler 1 to 3 glycols 2 to 4 bacteriostatic agent 0.1 up to 0.2 20 fungicidal agent 0.05 to 0.1 water 10 to 20 wax emulsion or dispersion (35% solids) 60 to 80 release agent 0.1 to 0.2 dye 0.1 to 0.2 25 I___

De samenstelling volgens de uitvinding wordt aangebracht op een oppervlak in een effectieve hoeveelheid cm een makkelijke verwijdering van het behang mogelijk te maken. De aan te brengen hoeveelheid is 30 afhankelijk van een aantal factoren, zoals de concentratie van de was en het de hechting modificerende middel en het filmvormende polymeer.The composition of the invention is applied to a surface in an effective amount to allow easy removal of the wallpaper. The amount to be applied depends on a number of factors, such as the concentration of the wax and the adhesion modifier and the film-forming polymer.

Wanneer de samenstelling ongeveer 15 tot 20 % was bevat, ongeveer 5 tot 15% filmvormend polymeer en ongeveer! 505tot 75% water kan het worden aangebracht in een hoeveelheid van 1 tot ongeveer 1,25 gallon (1 gallon is 3,79 liter) 35 per 1000 vierkante foot (1 foot is 30,48 cm). Nadat: de samenstelling is gedroogd wordt een behang op hiertoe geschikte wijze van een kleefïaiddel voorzien en op gebruikelijk wijze aangebracht. Wanneer het gewenst is om het behang te verwijderen wordt het behang eenvoudig afgetrokken onder 8003872 -10- 21383/Vk/mv uitoefening van voldoende kracht om het te verwijderen.When the composition contains about 15 to 20% wax, about 5 to 15% film-forming polymer and about! From 505 to 75% water, it can be applied in an amount from 1 to about 1.25 gallons (1 gallon is 3.79 liters) per 1000 square feet (1 foot is 30.48 cm). After the composition has dried, a wallpaper is suitably provided with an adhesive for this purpose and applied in the usual manner. When it is desired to remove the wallpaper, the wallpaper is simply subtracted under 8003872 -10-21383 / Vk / mv exerting enough force to remove it.

Het is gebleken dat cellulosehoudende hechtmiddelen het best samengaan met de eigenschappen van het preparaat volgens de uitvinding en bovendien kunnen deze hechtmiddelen worden toegepast bij elke soort behang.Cellulose-containing adhesives have been found to best combine with the properties of the composition of the invention and, in addition, these adhesives can be used with any type of wallpaper.

5 Zodoende wordt een hechtmiddel op basis van een cellulosesamenstelling aanbevolen en bij voorkeur toegepast met de samenstelling volgens de uitvinding. Vinylhoudende pasta's of pasta's op basis van tarwebloem worden bij voorkeur toegepast bij weefsel of bij vinylhoudend behang dat voorzien %! % is van een weefsel-grondlaag doch deze hechtmiddelen kunnen niet worden 10 toegepast bij behang dat voorzien is van een papieren grondlaag of behang op basis van type-m vinylsoorten. De type-III. vinylbehan esoor ten hebbeen een gewicht van ongeveer 32 tot 36 ounce (1 ounce is 28,35 g) per vierkante yard (1 yard is 91 »44 can) en deze zijn te zwaar om bestendig te zijn tegen afglijden van een verticaal oppervlak dat geprepareerd is met 15 een samenstelling volgens de uitvinding binnen de bovenvermelde trajecten voor de samenstellende stoffen. Het is echter mogelijk on een samenstelling volgens de uitvinding zodanig te bereiden dat het meer hechtmiddel-modificatiemiddel bevat en dat ook een type-m vinylbehang kan worden aangebracht met een vinylpasta. Wanneer een hechtmiddel op basis ·. van tarwe* 20 bloem wordt toegepast verdient het -.-de voorkeur om behang te gebruiken dat aan de achterzijde voorzien is van een weefsellaag.Thus, an adhesive based on a cellulose composition is recommended and preferably used with the composition of the invention. Wheat flour-based pastes or pastes are preferably used for fabrics or for vinyl-containing wallpaper that provide%! % is of a fabric base coat, but these adhesives cannot be used with wallpaper provided with a paper base coat or wallpaper based on type-m vinyls. The type III. vinyl treatment systems have a weight of about 32 to 36 ounces (1 ounce is 28.35 g) per square yard (1 yard is 91 »44 can) and these are too heavy to withstand sliding off a vertical surface that has been prepared is a composition of the invention within the above ranges for the constituent substances. However, it is possible to prepare a composition according to the invention in such a way that it contains more adhesive modifier and that a type-m vinyl wallpaper can also be applied with a vinyl paste. When an adhesive based on ·. of wheat * flour is used, it is preferable to use wallpaper which is provided with a fabric layer on the back.

De uitvinding zal nader worden toegelicht aan de hand van de volgende voorbeelden, die niet als beperkend moeten worden opgevat. Tenzij het tegendéél is aangegeven zijn de vermelde delen en percentages berekend 25 op het gewicht.The invention will be further illustrated by the following examples, which are not to be construed as limiting. Unless indicated to the contrary, the parts and percentages stated are calculated on weight.

Voorbeeld IExample I

Een samenstelling voor een preparaat dat toegepast kan worden om op een wand te worden gedaan voordat behang wordt aangebracht wordt bereid uit een.hiervoor bekende samenstelling. Wasemulsies onder toe-30 passing van Camabau,schellak, montan en candelilla wassoorten werden bereid in de volgende hoeveelheden: 25 gew.% was, 10 gew.% natriumstea-raat en 65 gew.% water.A composition for a composition which can be used to be placed on a wall before wallpaper is applied is prepared from a previously known composition. Wax emulsions using Camabau, shellac, montan and candelilla waxes were prepared in the following amounts: 25 wt% wax, 10 wt% sodium stearate and 65 wt% water.

Ter 'bereiding van de emulsies werd water en natriumstearaat verwarmd tot koken in een houder die voorzien is van een menger die kan ro-35 teren met een hoge snelheid. De bepaalde was werd verwarmd in een afzonderlijk vat en vervolgens druppelsgewijs langzaam toegevoegd aan het’- kokende. mengïel van natriumstearaat en water onder roeren. De verkregen emulsie werd vervolgens langzaam afgekoeld. Ondanks het type toegepaste 8003872 9 9 -11- 21383/Vk/mv was waren de emulsies niet homogeen en hadden een slechte stabiliteit bij het overgaan van vriezen naar dooien. De emulsies werden aangebracht op testoppervlakken in een hoeveelheid van ongeveer 1,25 gallon ( 1 gallon is 3,79 liter) per 1000 vierkante foot (1 foot is 30,48 cm) waarna de 5 laag werd gedroogd. Een licht gewicht behang werd vervolgens aangebracht op het oppervlak onder toepassing van een cellulose-type plaksel. Het opgebrachte behang bleef niet op zijn plaats op het oppervlak maar was onderhevig aan een verschuiving bij zowel hoge temperaturen als lage temperaturen.To prepare the emulsions, water and sodium stearate were heated to boiling in a container equipped with a high speed stirrer mixer. The assay was heated in a separate vessel and then slowly added dropwise to the boiling. mix of sodium stearate and water with stirring. The resulting emulsion was then cooled slowly. Despite the type of 8003872 9-11-21383 / Vk / mv used, the emulsions were not homogeneous and had poor stability from freezing to thawing. The emulsions were applied to test surfaces in an amount of about 1.25 gallons (1 gallon is 3.79 liters) per 1000 square feet (1 foot is 30.48 cm) after which the layer was dried. A light weight wallpaper was then applied to the surface using a cellulose type adhesive. The applied wallpaper did not remain in place on the surface but was subject to shifting at both high and low temperatures.

In alle gevallen was het behang makkelijk te verwijderen van het oppervlak 10 en in feite te makkelijk verwijderbaar.In all cases, the wallpaper was easy to remove from the surface 10 and in fact too easily removable.

Deze experimenten werden herhaald onder toepassing van kleef-middel op basis van tarwebloem en met vinyl-behang voorzien van een weefsel, en hierbij werden dezelfde resultaten verkregen.These experiments were repeated using wheat flour adhesive and fabric-backed vinyl wallpaper, and the same results were obtained.

Voorbeeld IIExample II

15 Hierbij werd de bereiding en het gebruik nader aangegeven vanThe preparation and use of

een aantal preparaten volgens de uitvinding en een aantal samenstellingen die niet volgens de uitvinding zijn bereid. De te onderzoeken samenstellingen zijn aangegeven in tabel Ba number of preparations according to the invention and a number of compositions which have not been prepared according to the invention. The compositions to be investigated are shown in Table B.

TABEL BTABLE B

20 __ _gewichtsdelen__________ component__a__b__c__d__e was emulsie 50 60 70 80 90 polyacrylzure oplossing 30 20 10 0 0 25 verdikkingsmiddel 0,25 0,25 0,25 0,25 0,25 ethyleenglycol 2 2222 losmaakmiddel (silicon) 0,5 0,5 0,5 0,5 0,5 water 17 17 17 17 17 3020 ___ parts by weight__________ component__a__b__c__d__e wax emulsion 50 60 70 80 90 polyacrylic acid solution 30 20 10 0 0 25 thickener 0.25 0.25 0.25 0.25 0.25 ethylene glycol 2 2222 release agent (silicon) 0.5 0.5 0, 5 0.5 0.5 water 17 17 17 17 17 30

Van deze samenstellingen zijn a, b en c bereid volgens de uitvinding terwijl de samenstellingen d en e als vergelijkende samenstellingen moeten worden beschouwd. Bij alle samenstellingen werd polyethy-leenwas met een hoge dichtheid gebruikt met een smeltpunt van 138 °C 35 en met een dichtheid van 0,99 als wascomponent in de wasemulsie. De bereiding van de emulsie had plaats onder toepassing van de volgende stoffen die toegevoerd werden aan een drukketel onder toepassing van de volgende stoffen: 8003872 -12- 21383/Vk/mv polyethyleenwas met een hoge dichtheid 40 gew.delenOf these compositions, a, b and c have been prepared according to the invention, while compositions d and e are to be considered as comparative compositions. All compositions used high density polyethylene wax with a melting point of 138 ° C and a density of 0.99 as the wax component in the wax emulsion. The emulsion was prepared using the following materials which were fed to a pressure boiler using the following materials: 8003872 -12- 21383 / Vk / mv high density polyethylene wax 40 parts by weight

Igepal CO.710 geëthoxyleerde alkylfenol als emulgeermiddèl 10 gew.delen KOH 0,9 gew.deel 5 water 93 gew.délênIgpal CO.710 ethoxylated alkyl phenol as an emulsifier 10 parts by weight KOH 0.9 parts by weight 5 water 93 parts by weight

Al deze stoffen behalve het water in een hoeveelheid van 43 gew.delen werden toegevoerd aan de ketel en verwarmd onder roeren onder uitoefening van schuifspanning . Toen de ^temperatuur een waarde 10 had bereikt van 95 °C werd de ketel onder druk gebracht door het 1 sluiten van de kleppen. Het verwarmen werd voortgezet tot de temperatuur een waarde had bereikt van 145-150 °C, welke temperatuur werd gehandhaafd onder constant roeren gedurende nogmaals een half uur. Daarna werd de emylsie verdund met de resterende 43 gew.delen water die onder druk werden 15 toegevoerd met behulp van een pomp, De emulsie werd vervolgens afgekoeld tot kamertemperatuur onder voortdurend roeren. De verkregen 'wasemulsie was stabiel en had een fijne wasdeeltjesgrootte.All these materials except the water in an amount of 43 parts by weight were fed to the kettle and heated with stirring under shear stress. When the temperature reached a value of 95 ° C, the kettle was pressurized by closing the valves. Heating was continued until the temperature reached 145-150 ° C, which temperature was maintained with constant stirring for another half hour. Then the emulsion was diluted with the remaining 43 parts by weight of water which were supplied under pressure by means of a pump. The emulsion was then cooled to room temperature with continuous stirring. The wax emulsion obtained was stable and had a fine wax particle size.

De polyacrylzure oplossing werd toegevoegd als een 25 gewicht.% waterige oplossing van een oplosbaar zout van een acrylzuur copolymeer met 20 een zuurwaarde van ongeveer 160. De hulpstof voor het verwijderen was een emulsie van Dow Corning 17 siliconolie. Als verdikkingsmiddel werd hy droxypropylme thylcellulose toegepas t.The polyacrylic acid solution was added as a 25 weight% aqueous solution of a soluble salt of an acrylic acid copolymer having an acid value of about 160. The removal aid was an emulsion of Dow Corning 17 silicone oil. Hydroxypropyl methylcellulose was used as the thickener.

Met deze samenstellingen werden niet-geverfde minder goede gedeelten van een droge wand bestreken en met het in de handel verkrijg-25 bare eerder genoemde preparaat dat dient ter vergelijking. Nadat het preparaat gedurende een uur was gedroogd bij kamertemperatuur werd behang (lichtgewicht) ingesmeerd met hechtmiddel en aangebracht op d® wandgedeel-ten onder toepassing van cellulosehoudend hechtmiddel. De hierbij verkregen resultaten zijn weergegeven in tabel C 30 TABEL CWith these compositions, unpainted dry wall inferior portions were coated and with the commercially available aforementioned composition for comparison. After the composition was dried at room temperature for one hour, wallpaper (lightweight) was smeared with adhesive and applied to d® wall sections using cellulosic adhesive. The results obtained are shown in Table C. TABLE C

— " ...........*—“ '-i""" -------------- ·ι|· preparaat loslaten hechten a redelijk goed b goed goed 35 c goed redelijk d goed slecht e goed slecht bekend middel goed slecht 8003872 -13- 21383/Vk/mv- "........... * -" '-i "" "-------------- · ι | · release preparation attach a fairly good b good good 35 c good reasonable d good bad e good bad known medium good bad 8003872 -13- 21383 / Vk / mv

Uifc deze gegevens blijkt dat het preparaat volgens de uitvinding een goede hechting en/of loslating bij verwijdering bewerkstelligde van het behang terwijl het bekende middel of de ter vergelijking dienende preparaten d) en e) een slechte hechting gaven van het behang op de 5 wand die voorzien is van het bekende preparaat of het ter vergelijking diendende preparaat.From these data it appears that the preparation according to the invention achieved a good adhesion and / or release upon removal of the wallpaper, while the known agent or the comparative preparations d) and e) gave a poor adhesion of the wallpaper to the wall which is provided with the known preparation or the comparative preparation.

i ^ -conclusies- 8003872Claims 8003872

Claims

1. Preparation that can be applied to a surface before applying wallpaper and the paste to be used therewith, so that a good adhesion of the wallpaper to the surface is achieved, while the wallpaper can still be easily removed by pulling off the preparation. stable emulsion, characterized in that the composition is composed of water as a continuous phase, a wax dispersed in the water, an emulsifying agent in an amount sufficient to obtain an emulsion stability and a water-dispersible film-forming polymer in an amount effective to strike a balance between the adhesion and the removal of the composition, thereby improving the adhesion of the wallpaper, while still being easy to remove.

2. A composition according to claim 1, characterized in that the wax and the emulsifying agent are mixed in such amounts that the resulting mixture of wax and emulsifying agent in the final composition has a melting point of at least 80 ° C.

3. A composition according to claim 2, characterized in that the melting point of the mixture consisting of wax and emulsifying agent is at least 100 ° C.

4. A composition according to claim 1, characterized in that the water-dispersible film-forming polymer is used in an amount from about 8% to about 12% based on the weight of the wax.

5. A composition according to claim 1, characterized in that further a polyhydric alcohol is added in an amount effective to obtain stability of the composition upon transition from freezing to thawing.

Preparation according to claim 1, characterized in that an agent is further added which facilitates release.

7. Preparation according to claim 1? characterized in that a pigment is further added.

8. Preparation according to claim 1, characterized in that it also contains a thickening agent.

Preparation according to claim 1, characterized in that it contains a sufficient amount of a mildew repellent and a bactericidal agent so that the microbial growth can be inhibited. 8003872% r -15- 21383 / Vk / mv

Preparation according to claim 1, characterized in that it contains an anti-foaming agent.

11. A method of applying wallpaper to a surface, wherein the wallpaper is provided with an adhesive and applied to the surface 5 after applying a preparation to the surface, characterized in that a stable emulsion is applied to the surface consisting of water as a continuous phase, a wax dispersed in the water, an emulsifying agent in an effective amount to obtain an emulsion stability and a water-dispersible film-forming polymer in an amount effective to form an equilibrium between the adhesive properties and the release properties of the composition, thereby improving the adhesion of the wallcovering while still being easy to remove, which composition is dried on the surface after application.

Method for preparing a composition which can be used to improve the adhesion of wallpaper to surfaces by facilitating the removal of the wallpaper, characterized in that a mixture is prepared consisting of water, an emulsifying agent and an aqueous dispersible film-forming polymer in 20 amounts so that the properties can be achieved as claimed in claim 11. $ 003872