MX2016013422A - Riel con alto contenido de acero al carbono con ductibilidad mejorada. - Google Patents
Riel con alto contenido de acero al carbono con ductibilidad mejorada.Info
- Publication number
- MX2016013422A MX2016013422A MX2016013422A MX2016013422A MX2016013422A MX 2016013422 A MX2016013422 A MX 2016013422A MX 2016013422 A MX2016013422 A MX 2016013422A MX 2016013422 A MX2016013422 A MX 2016013422A MX 2016013422 A MX2016013422 A MX 2016013422A
- Authority
- MX
- Mexico
- Prior art keywords
- carbon steel
- mass
- high carbon
- steel rail
- enhanced ductility
- Prior art date
Abstract
Esta invención se relaciona con un riel con alto contenido de acero al carbono con ductibilidad mejorada, que comprende 0.65-1.4% en masa de carbono, 0.1-1.5% en masa de silicio, 0.01-0.4% en masa de manganeso, 0.1-1.5% en masa de cromo y 0.005-0.05% en masa de titanio, con tolerancias adicionales para Mo, Nb, V, Cu, Ni, Co, B, N, Ca, Mg, Zr, Al y W, con el resto que comprende hierro y las impurezas inevitables, que muestra una dureza de la superficie del cabezal de al menos 3.25 HB y una microestructura que comprende al menos 90% de perlita a una profundidad de entre 2-20 mm por debajo de la superficie del cabezal del riel. La invención también se relaciona con el proceso para fabricar el riel con alto contenido de acero al carbono con ductibilidad mejorada.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CA2849133A CA2849133C (en) | 2014-04-17 | 2014-04-17 | High carbon steel rail with enhanced ductility |
US14/255,693 US9670570B2 (en) | 2014-04-17 | 2014-04-17 | High carbon steel rail with enhanced ductility |
PCT/CA2015/000263 WO2015157856A1 (en) | 2014-04-17 | 2015-04-16 | High carbon steel rail with enhanced ductility |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2016013422A true MX2016013422A (es) | 2017-05-30 |
Family
ID=54323310
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2016013422A MX2016013422A (es) | 2014-04-17 | 2015-04-16 | Riel con alto contenido de acero al carbono con ductibilidad mejorada. |
Country Status (3)
Country | Link |
---|---|
BR (1) | BR112016024079B1 (es) |
MX (1) | MX2016013422A (es) |
WO (1) | WO2015157856A1 (es) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN114015941B (zh) * | 2021-11-03 | 2022-10-11 | 攀钢集团攀枝花钢铁研究院有限公司 | 一种连铸复合轧制钢轨及其生产方法 |
Family Cites Families (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE69523149T2 (de) * | 1994-11-15 | 2002-06-20 | Nippon Steel Corp | Perlitschiene mit hoher abriebfestigkeit und verfahren zu deren herstellung |
JPH09316598A (ja) * | 1996-03-27 | 1997-12-09 | Nippon Steel Corp | 耐摩耗性および溶接性に優れたパーライト系レールおよびその製造法 |
JP5238930B2 (ja) * | 2009-02-12 | 2013-07-17 | Jfeスチール株式会社 | 耐摩耗性レールおよびその製造方法 |
KR101421368B1 (ko) * | 2010-06-07 | 2014-07-24 | 신닛테츠스미킨 카부시키카이샤 | 강 레일 및 그 제조 방법 |
-
2015
- 2015-04-16 MX MX2016013422A patent/MX2016013422A/es unknown
- 2015-04-16 BR BR112016024079-0A patent/BR112016024079B1/pt active IP Right Grant
- 2015-04-16 WO PCT/CA2015/000263 patent/WO2015157856A1/en active Application Filing
Also Published As
Publication number | Publication date |
---|---|
BR112016024079A2 (pt) | 2018-12-18 |
BR112016024079B1 (pt) | 2021-01-12 |
WO2015157856A1 (en) | 2015-10-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2015162939A8 (ja) | 厚鋼板及びその製造方法 | |
MX2019005067A (es) | Aleaciones metalicas ferrosas duras imprimibles en 3d para fusion de lecho en polvo. | |
WO2016105064A8 (ko) | 취성균열전파 저항성이 우수한 고강도 강재 및 그 제조방법 | |
MX2015014099A (es) | Hoja de acero laminada en caliente y metodo de fabricacion de la misma. | |
MX2017001374A (es) | Procedimiento para la fabricacion de laminas de acero para el endurecimiento por presion y piezas obtenidas por este procedimiento. | |
PH12019501995A1 (en) | High-mn steel and production method therefor | |
PH12019501270A1 (en) | HIGH-Mn STEEL PLATE AND MANUFACTURING METHOD THEREFOR | |
MX2016007953A (es) | Lamina de acero de alta resistencia y metodo para la produccion de la misma. | |
WO2016105059A8 (ko) | 취성균열전파 저항성이 우수한 고강도 강재 및 그 제조방법 | |
MX357839B (es) | Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas. | |
UA109963C2 (uk) | Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва | |
CA3025617C (en) | Method for producing a twip steel sheet having an austenitic microstructure | |
MX2017003732A (es) | Acero para pernos y perno. | |
PH12017500557A1 (en) | Steel sheet for cans and method for manufacturing steel sheet for cans | |
MX2018014321A (es) | Hoja de acero twip (de plasticidad inducida por fusion) con una matriz austenitica. | |
MX2016014990A (es) | Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas. | |
MX2018000917A (es) | Acero de alta resistencia con limite minimo de elasticidad elevado y procedimiento para la produccion de un acero de este tipo. | |
WO2016105062A8 (ko) | 취성균열전파 저항성이 우수한 고강도 강재 및 그 제조방법 | |
MX2017016905A (es) | Acero resistente a la corrosion, metodo para producir dicho acero y uso del mismo. | |
WO2012091394A3 (ko) | 고내식 마르텐사이트 스테인리스강 및 그 제조방법 | |
CO2017009718A2 (es) | Hoja de acero para una lata y método para fabricarla | |
MX2017012063A (es) | Alambre de acero para piezas estructurales mecanicas. | |
MX2017013834A (es) | Acero inoxidable martensitico, metodo para la produccion de un producto semiacabado del acero y herramienta de corte producida a partir del producto semiacabado. | |
MX2018011889A (es) | Chapa de acero, chapa de acero revestida, metodo para producir chapa de acero laminada en caliente, metodo para producir chapa de acero muy dura laminada en frio, metodo para producir chapa de acero y metodo para producir chapa de acero revestida. | |
MX2019001258A (es) | Metodo de fabricacion de parte de acero que incluye la adicion de metal fundido a una parte de soporte y parte obtenida de esta manera. |