LU500525B1 - Preparation method of banana stem and leaf straw fiber composite material - Google Patents

Preparation method of banana stem and leaf straw fiber composite material Download PDF

Info

Publication number
LU500525B1
LU500525B1 LU500525A LU500525A LU500525B1 LU 500525 B1 LU500525 B1 LU 500525B1 LU 500525 A LU500525 A LU 500525A LU 500525 A LU500525 A LU 500525A LU 500525 B1 LU500525 B1 LU 500525B1
Authority
LU
Luxembourg
Prior art keywords
banana stem
leaf
straw
leaf straw
composite material
Prior art date
Application number
LU500525A
Other languages
English (en)
Inventor
Puwang Li
Yunhao Liu
Shuhui Song
Yaqi Liu
Ziming Yang
Zuyu He
Chuang Zhou
Chao Wang
Original Assignee
Inst Of South Subtropical Crops Chinese Academy Of Tropical Agricultural Sciences
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inst Of South Subtropical Crops Chinese Academy Of Tropical Agricultural Sciences filed Critical Inst Of South Subtropical Crops Chinese Academy Of Tropical Agricultural Sciences
Priority to LU500525A priority Critical patent/LU500525B1/en
Application granted granted Critical
Publication of LU500525B1 publication Critical patent/LU500525B1/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L99/00—Compositions of natural macromolecular compounds or of derivatives thereof not provided for in groups C08L89/00 - C08L97/00
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C43/00—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor
    • B29C43/003—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor characterised by the choice of material
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08H—DERIVATIVES OF NATURAL MACROMOLECULAR COMPOUNDS
    • C08H99/00—Subject matter not provided for in other groups of this subclass, e.g. flours, kernels
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
    • C08J5/045—Reinforcing macromolecular compounds with loose or coherent fibrous material with vegetable or animal fibrous material
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
    • C08J5/06—Reinforcing macromolecular compounds with loose or coherent fibrous material using pretreated fibrous materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C43/00—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor
    • B29C43/02—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor of articles of definite length, i.e. discrete articles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C43/00—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor
    • B29C43/32—Component parts, details or accessories; Auxiliary operations
    • B29C43/52—Heating or cooling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2003/00—Use of starch or derivatives as moulding material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2031/00—Use of polyvinylesters or derivatives thereof as moulding material
    • B29K2031/04—Polymers of vinyl acetate, e.g. PVAc, i.e. polyvinyl acetate
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2311/00—Use of natural products or their composites, not provided for in groups B29K2201/00 - B29K2309/00, as reinforcement
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2311/00—Use of natural products or their composites, not provided for in groups B29K2201/00 - B29K2309/00, as reinforcement
    • B29K2311/10—Natural fibres, e.g. wool or cotton
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2303/00—Characterised by the use of starch, amylose or amylopectin or of their derivatives or degradation products
    • C08J2303/02—Starch; Degradation products thereof, e.g. dextrin
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2329/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an alcohol, ether, aldehydo, ketonic, acetal, or ketal radical; Hydrolysed polymers of esters of unsaturated alcohols with saturated carboxylic acids; Derivatives of such polymer
    • C08J2329/02—Homopolymers or copolymers of unsaturated alcohols
    • C08J2329/04—Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2399/00—Characterised by the use of natural macromolecular compounds or of derivatives thereof not provided for in groups C08J2301/00 - C08J2307/00 or C08J2389/00 - C08J2397/00
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/24—Acids; Salts thereof
    • C08K3/26—Carbonates; Bicarbonates
    • C08K2003/265—Calcium, strontium or barium carbonate

Claims (10)

PATENTANSPRUCHE LU500525
1. Verbundwerkstoff aus Strohfasern aus Bananenstingeln und -blättern ist dadurch gekennzeichnet, dass es die folgenden Komponenten in Masseteilen umfasst: 5-40 Teile Bananenstamm- und Blattstrohfasern, 10-30 Teile Klebstoff, 5-10 Teile Stabilisator und 10-30 Teile Füllstoff.
2. Der Verbundwerkstoff aus Strohfasern aus Bananenstängeln und -blättern nach Anspruch 1 ist dadurch gekennzeichnet, dass der Klebstoff Kartoffelstärke, PVA oder Pfirsichgummi ist, der Stabilisator Calciumstearat oder Calciumlaurat ist und der Füllstoff Calciumcarbonat oder Kaolin ist.
3. Der Verbundwerkstoff aus Strohfasern aus Bananenstängeln und -blättern nach Anspruch 1 ist dadurch gekennzeichnet, dass die Strohfasern aus Bananenstängeln und -blättern durch mechanische Behandlung, Vorbehandlung und Oberflächenmodifikation von Bananenstängeln und -blättern hergestellt werden.
4. Das Verfahren zur Herstellung des Verbundwerkstoffes aus Strohfasern aus Bananenstängeln und -blättern nach einem der Ansprüche 1-3 ist dadurch gekennzeichnet, dass es die folgenden Schritte umfasst: Schritt 1: Mechanische Behandlung der Bananenstängel und -blätter, um die Segmenten der Bananenstängel und -blätter zu erhalten; Schritt 2: Vorbehandlung der Segmenten der Bananenstängel und -blätter, um vorbehandelte Bananenstängel und -blätter zu erhalten; Schritt 3: Oberflächenmodifizierung des vorbehandelten Bananenstängel und —blätter, um die Strohfasern aus Bananenstängeln und -blättern zu erhalten; Schritt 4: gleichmäBiges Mischen von den Strohfasern aus Bananenstängeln und -blättern, Klebstoff, Stabilisator und Füllstoff, HeiBpressen und Formen, dann natürliches Abkühlen, um das Verbundmaterial der Strohfasern aus Bananenstängeln und -blättern zu erhalten.
5. Das Verfahren zur Herstellung der Verbundmaterial der Strohfasern aus Bananenstängeln LU500525 und -blattern nach Anspruch 4 ist dadurch gekennzeichnet, dass in Schritt 1 das Stroh der Bananenstängel und -blätter in kleine Stücke mit einer Länge von 1-5 cm und einer Breite von 1-10 mm geschnitten wird.
6. Das Verfahren zur Herstellung der Verbundmaterial der Strohfasern aus Bananenstängeln und -blättern nach Anspruch 4 ist dadurch gekennzeichnet, dass der spezifische Vorgang von Schritt 2 darin besteht, dass die Bananenstamm- und Blattstrohsegmente in Natriumhydroxidlosung eingeweicht, erhitzt, mit Säure neutralisiert, mit Wasser bis zur Neutralität gewaschen und getrocknet werden, um vorbehandeltes Bananenstamm- und Blattstroh zu erhalten.
7. Das Verfahren zur Herstellung der Verbundmaterial der Strohfasern aus Bananenstängeln und -blättern nach Anspruch 6 ist dadurch gekennzeichnet, dass die Massenkonzentration der Natrtumhydroxidlôsung 2-5% beträgt, das Masse-Flüssigkeits-Verhältnis von Bananenstamm- und Blattstrohsegmente zu Natriumhydroxidlôsung 1 g:20 ml-50 ml beträgt, die Temperatur beim Erhitzen 60-80°C für 30-60 min beträgt und die Temperatur bei der Trocknung 80-100°C für 5-8 h beträgt.
8. Das Verfahren zur Herstellung der Verbundmaterial der Strohfasern aus Bananenstängeln und -blättern nach Anspruch 4 ist dadurch gekennzeichnet, dass der spezifische Vorgang von Schritt 3 darin besteht, dass eine Haftvermittlerlôsung zu vorbehandeltem Bananenstamm und Blattstroh unter Hochgeschwindigkeitsrühren zugegeben wird, dann 20-30 Minuten lang nach der Zugabe zur gleichmäBigen Mischung kontinuierlich gerührt wird, um ein Gemisch zu erhalten; das Gemisch bei 70-110°C 4-10 Stunden lang getrocknet wird, um Strohfasern aus Bananenstängeln und -blättern zu erhalten, wobei die Drehgeschwindigkeit des Hochgeschwindigkeitsrührens 1000-2000 U/min beträgt.
9. Das Verfahren zur Herstellung der Verbundmaterial der Strohfasern aus Bananenstängeln und -blättern nach Anspruch 8 ist dadurch gekennzeichnet, dass der gelöste Stoff der LU500525 Kupplungsmittellôsung ein Silan-Kupplungsmittel oder ein Titanat-Kupplungsmittel ist, das Lôsungsmittel Ethanol ist, das Volumenverhältnis von gelôstem Stoff zu Lôsungsmittel 1: S ist, das Massenverhältnis von vorbehandeltem Bananenstamm und Blattstroh zu Kupplungsmittel 100: 1-6 ist.
10. Das Verfahren zur Herstellung der Verbundmaterial der Strohfasern aus Bananenstängeln und -blättern nach Anspruch 4 ist dadurch gekennzeichnet, dass die Temperatur in Schritt 4 beim HeiBpressen und Formen 160-180°C ist, der Druck 3-6 MPa beträgt und die Zeit 2-6 Minuten beträgt.
LU500525A 2021-08-10 2021-08-10 Preparation method of banana stem and leaf straw fiber composite material LU500525B1 (en)