KR980700445A - 경질 복합재료용 매트릭스(matrix for a hard composite) - Google Patents
경질 복합재료용 매트릭스(matrix for a hard composite) Download PDFInfo
- Publication number
- KR980700445A KR980700445A KR1019970703509A KR19970703509A KR980700445A KR 980700445 A KR980700445 A KR 980700445A KR 1019970703509 A KR1019970703509 A KR 1019970703509A KR 19970703509 A KR19970703509 A KR 19970703509A KR 980700445 A KR980700445 A KR 980700445A
- Authority
- KR
- South Korea
- Prior art keywords
- weight percent
- tungsten carbide
- sintered
- micrometers
- particle size
- Prior art date
Abstract
마모 원소로서 이용하기 위한 또는 적어도 하나의 분리된 경질 원소를 유지할 때 이용하기 위한 매트릭스 내에 인필트런트와 함께 형성하기 위한 매트릭스 파우더는 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자를 포함한다. 분쇄 및 소결 및 접착된 텅스텐 카바이드의 복합재료는 약 6 및 13 중량 퍼센트 사이의 바인더 금속과, 약 87 및 94 중량 퍼센트 사이의 텅스텐 카바이드를 포함한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제 1도는 제품에 결합된 불연속 다이아몬드의 한 실 시예와 함께 공구 축을 포함하는 제품을 제작하기 위해 이용되는 조립체의 개요도.
제 2도는 제품에 결합된 다이아몬드 복합재료의 다른 실 시예와 함께 공구 축을 포함하는 제품을 제작하기 위해 이용되는 조립체의 개요도.
제 3도는 본 발명와 결합하는 공구 드릴 비트의 사이도.
Claims (34)
- 매트릭스 내에 인필트런트와 함께 형성하기 위한 매트릭스 파우더에 있어서, 상기 매트릭스 파우더는: 37 마이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자와; 약 5중량 퍼센트 및 20 중량 퍼센트 사이의 바인더 금속 및 약 80 중량 퍼센트 및 95 중량 퍼센트 사이의 텅스텐 카바이드를 포함하는 분쇄 및 소결 및 접착된 텅스텐 카바이드의 복합재료를 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속의 코발트이며; 분쇄 및 소결 및 접착된 텅스텐 카바이드의 복합재료가 약 6 중량 퍼센트 및 약 13 중량 퍼센트 사이의 코발트 및 약 87 중량 퍼센트 및 약 94 중량 퍼센트 사이의 텅스텐 카바이드이며, 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자 크기가 53 마이크로미터 이상 및 105 마이크로미터 미만 또는 그와 같은 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속의 코발트이며; 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자 크기가 44 마이크로미터 이상 및 177 이크로미터 미만 또는 그와 같은 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속의 코발트이며; 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자가 다음의 복합재료; 약 6 중량 퍼센트 코발트, 최대 1 중량 퍼센트 철, 최대 1.0 중량 퍼센트 탄탈, 최대 1.0 중량 퍼센트 티타늄, 최대 0.5 중량 퍼센트의 니오븀, 최대 0.5 중량 퍼센트의 다른 불순물 및 약 5 마이크로미터 및 약 25 마이크로 미터 사이의 평균 입자 크기를 가지는 균형 아미크로크리스탈린 텅스텐 카바이드를 가지는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 파우더는 약 100 중량 퍼센트의 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자를 포함하며; 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자 크기가 44이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속이 코발트이며; 파우더는: (a) 약 50 중량 퍼센트까지 파우더가 44 마이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 텅스텐 카바이드이며; (b) 약 50 중량 퍼센트까지 혼합물이 177 마이크로미터 미만 또는 그와 같은 입자 크기의 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자이며, 다음의 복합재료: 약 6 중량 퍼센트 코발트, 최대 1 중량 퍼센트 철, 최대 1.0 중량 퍼센트 탄탈, 최대 1.0 중량 퍼센트 티타늄, 최대 0.5 중량 퍼센트의 니오븀, 최대 0.5 중량 퍼센트의 다른 불순물 및 약 5 마이크로미터 및 약 25 마이크미터 사이의 평균 입자 크기를 가지는 균형 마이크로크리스탈린 텅스텐 카바이드를 가지며; (c) 약 24 중량 퍼센트까지 혼합물이 53 마이크로미터 미만 또는 그와 같은 평균 입자 크기를 가지는 주조된 텅스텐 카바이드이며; (d) 약 0.5 중량 퍼센트 및 약 1.5 중량 퍼센트 사이의 혼합물이 주로 약 0.5 및 약 1.5 마이크로미터 사이의 입자 크기를 가지는 철인 것을 특징으로 하는 매트릭스 파우더.
- 제 6 항에 있어서, 철 성분은 53 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 4600 등급 강철인 약 0.25 중량 퍼센트 및 약 0.75 중량 퍼센트 사이의 혼합물과, 약 3 내지 5 마이크로미터 사이의 입자 크기를 가지는 철인 약 0.25 중량 퍼센트 및 약 0.75 중량 퍼센트 사이의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 6 항에 있어서, 텅스텐 카바이드 입자는 약 50 중량 퍼센트의 혼합물을 포함하며, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 약 25 중량 퍼센트의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 6 항에 있어서, 텅스텐 카바이드 입자는 약 34 중량 퍼센트의 혼합물을 포함하며, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 약 50 중량 퍼센트의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 6 항에 있어서, 텅스텐 카바이드 입자는 약 17 중량 퍼센트의 혼합물을 포함하며, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 약 75 중량 퍼센트의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 분쇄 및 소결 및 접촉된 마이크로크리스탈린 텅스텐 카바이드 입자를 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 11 항에 있어서, 혼합물 파우더는 약 100 중량 퍼센트의 분쇄 소결 및 접촉된 마이크로크리스탈린 텅스텐 카바이드 입자를 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 12 항에 있어서, 바인더 금속이 코발트인 것을 특징으로 하는 매트릭스 파우더.
- 제 13 항에 있어서, 분쇄 및 소결 및 접초고딘 마이크로크리스탈린 텅스텐 카바이드 입자 크기는 44 마이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속이 니켈이며; 분쇄 및 소결 및 접착된 텅스켄 카바이드의 복합재료가 약 6 중량 퍼센트 및 13 중량 퍼센트 사이의 니켈과 약 87 중량 퍼센트 및 94 중량 퍼센트 사이의 텅스텐 카바이드이며, 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자 크기가 53 마이크로미터 이상 및 105 마이크로미터 미만 또는 그와 같은 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속이 니켈이며; 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자 크기가 44 마이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속이 니켈이며; 분쇄 및 소결 및 접착된 텅스텐 카바이드의 입자가 다음과 같은 복합재료: 약 6 중량 퍼센트 니켈, 최대 1 중량 퍼센트 철, 최대 1.0 중량 퍼센트 탄탈, 최대 1.0 중량 퍼센트 티타늄, 최대 0.5 중량 퍼센트 니오븀, 최대 0.5 중량 퍼센트의 다른 불순물 및 약 5 마이크로미터 및 약 25 마이크로미터 사이의 평균 입자 크기를 가지는 균형 텅스텐 카바이드를 가지는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속이 니켈이며; 파우더가 100 중량 퍼센트 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자를 포함하며, 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자 크기가 44 마이크로미터 이상 177 마이크로미터 미만 또는 그와 같은 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 바인더 금속이 니켈이며; 파우더가 다음을 포함하며; (a) 44 마이크로미터 이상 177 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 텅스텐 카바이드 입자인 약 50 중량 퍼센트까지의 파우더; (b) 약 75 중량 퍼센트까지의 혼합물이 177 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자이며, 다음의 조성물: 약 6 중량 퍼센트 니켈, 최대 1 중량 퍼센트 철, 최대 1.0 중량 퍼센트 탄탈, 최대 1.0 중량 퍼센트 티타늄, 최대 0.5 중량 퍼센트의 니오븀, 최대 0.5 중량 퍼센트의 다른 불순물 및 약 5 마이크로미터 및 약 25 마이크로미터 사이의 평균 입자 크기를 가지는 균형 텅스텐 카바이드를 가지는 것과; (c) 약 24 중량 퍼센트까지의 혼합물이 53 마이크로미터 미만 또는 그와 같은 평균 입자 크기를 가지는 주조된 텅스텐 카바이드 이며, (d) 약 0.5 중량 퍼센트 및 1.5 중량 퍼센트 사이의 혼합물이 약 3 마이크로미터 및 5 마이크로미터 미만의 사이의 입자 크기를 가지는 철이 대부분인 것을 특징으로 하는 매트릭스 파우더.
- 제 19 항에 있어서, 철 성분은 44 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 4600 등급 강철인 약 0.25 중량 퍼센트 및 약 0.75 중량 퍼센트 사이의 혼합물과 약 3 내지 5 마이크로미터 사이의 입자 크기를 가지는 철인 약 0.25 중량 퍼센트 및 약 0.75 중량 퍼센트 사이의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 19 항에 있어서, 텅스텐 카바이드 입자는 약 50 중량 퍼센트의 혼합물을 포함하며, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 약 25 중량 퍼센트의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 19 항에 있어서, 텅스텐 카바이드 입자는 약 34 중량 퍼센트의 혼합물을 포함하며, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 약 50 중량 퍼센트의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 19 항에 있어서, 텅스텐 카바이드 입자는 약 17 중량 퍼센트의 혼합물을 포함하며, 분쇄 및 소결 및 접촉된 텅스텐 카바이드 입자는 약 75 중량 퍼센트의 혼합물을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 인필트런트는 약 50 및 70 중량 퍼센트 사이의 구리와, 약 10 및 20 중량 퍼센트 사이의 니켈과, 약 15 및 25중량 퍼센트 사이의 아연을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 24 항에 있어서, 인필트런트는 약 63 및 67 중량 퍼센트 사이의 구리와, 약 14 및 16 중량 퍼센트 사이의 니켈과, 약 19 및 21 중량 퍼센트 사이의 아연을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 1 항에 있어서, 인필트런트는 약 45 및 60 중량 퍼센트 사이의 구리와, 약 10 내지 20 중량 퍼센트 사이의 니켈과, 약 18 내지 30 중량 퍼센트 망간과, 붕소 량 및 실리콘 량을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 제 26 항에 있어서, 인필트런트는 약 52.7 중량 퍼센트 사이의 구리와, 약 24 중량 퍼센트 망간과, 약 15 중량 퍼센트 니켈과, 약 8 중량 퍼센트 아연과, 0.15중량 퍼센트 붕소와, 0.15 중량 퍼센트 실리콘을 포함하는 것을 특징으로 하는 매트릭스 파우더.
- 지지대; 지지대에 부착된 다이아몬드 복합재료; 다이아몬드 복합재가 인필트런트에 의해서 함께 유지된 입자의 덩어리를 포함하는 매트릭스를 포함하며, 입자의 덩어리가 인필트런트의 존재 하에서 파우더 혼합물을 가열함으로써 형성되며, 파우더 혼합물은 다음을: 37 마이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 입자 크기를 가지는 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자; 및 약 5 및 20 중량 퍼센트 사이의 바인더 금속 및 약 80 및 95 중량 퍼센트 사이의 텅스텐 카바이드를 포함하는 분쇄 및 소결 및 접착된 텅스텐 카바이드의 복합재로를 포함하는 것을 특징으로 하는 다이아몬드 합성 부재.
- 제 28 항에 있어서, 파우더는 약 100 중량 퍼센트의 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자를 포함하며, 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자 크기는 44 마이크로미터 이상 및 177 마이크로미터 미만 또는 그와 같은 것을 특징으로 하는 다이아몬드 합성 부재.
- 제 29 항에 있어서, 바인더 금속이 코발트인 것을 특징으로 하는 다이아몬드 합성 부재.
- 제 29 항에 있어서, 바인더 금속이 니켈인 것을 특징으로 하는 다이아몬드 합성 부재.
- 제 28 항에 있어서, 분쇄 및 소결 및 접착된 텅스텐 카바이드 입자는 분쇄 및 소결 및 접착된 마이크로크리스탈링 텅스텐 카바이드 입자인 것을 특징으로 하는 다이아몬드 합성 부재.
- 제 28 항에 있어서, 인필트런트는 약 50 내지 70 중량 퍼센트 사이의 구리와, 약 10 및 20 중량 퍼센트 사이의 니켈과, 약 15 및 25 중량 퍼센트 사이의 아연을 포함하는 것을 특징으로 하는 다이아몬드 합성 부재.
- 제 28 항에 있어서, 인필트런트는 약 45 내지 60 중량 퍼센트 사이의 구리와, 약 10 및 20 중량 퍼센트 니켈과, 약 18 및 30 중량 퍼센트 망간과, 붕소 량 및 실리콘 량을 포함하는 것을 특징으로 하는 다이아몬드 합성 부재.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.