KR970011015A - Color coated metal plate and manufacturing method thereof - Google Patents

Color coated metal plate and manufacturing method thereof Download PDF

Info

Publication number
KR970011015A
KR970011015A KR1019960033832A KR19960033832A KR970011015A KR 970011015 A KR970011015 A KR 970011015A KR 1019960033832 A KR1019960033832 A KR 1019960033832A KR 19960033832 A KR19960033832 A KR 19960033832A KR 970011015 A KR970011015 A KR 970011015A
Authority
KR
South Korea
Prior art keywords
metal plate
coated metal
color
coating film
resin coating
Prior art date
Application number
KR1019960033832A
Other languages
Korean (ko)
Other versions
KR100213541B1 (en
Inventor
아쓰시 기하라
다다시게 나카모또
Original Assignee
구마모토 마사히로
가부시끼가이샤 고베세이꼬쇼
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 구마모토 마사히로, 가부시끼가이샤 고베세이꼬쇼 filed Critical 구마모토 마사히로
Publication of KR970011015A publication Critical patent/KR970011015A/en
Application granted granted Critical
Publication of KR100213541B1 publication Critical patent/KR100213541B1/en

Abstract

고가가 아니고 간단한 장치로 칼라수지도장금속판을 제조공급하기 위한 것으로 본 발명은 수지도막을 도장하기 전에 원판의 색조를 반사하는 안정되고 우수한 표면광택도를 가지고, 아울러 우수한 내식성, 우수한 내크를 용해성을 가진 원판 및 제조방법을 제공한다.The present invention relates to a method for manufacturing a color coated metal plate using a simple apparatus rather than an expensive apparatus, and has a stable and excellent surface gloss reflecting the color tone of the original plate before coating the water marking film, and also has excellent corrosion resistance, A disc and a manufacturing method thereof.

본 발명상의 착색안료를 함유하는 수지도막을 가진 칼라수지도장금속판은, 상술한 바의 본 발명으로 제조되는 바, 여기에서 칼라수지의 도막형성전의 금속판의 60°거울 광택도를 G0그리고 도장후의 금속판의 60° 거울광택도를 G1이라 할 때The color coated metal plate having the water-leading film containing the colored pigment according to the present invention is manufactured by the present invention as described above. Here, the gloss of the metal plate before forming the coating film of the color resin is G 0, Assuming that the 60 ° mirror gloss of the metal sheet is G 1

G0〉G1≥0.5 G0(1)G 0 > G 1? 0.5 G 0 (1)

의 공식을 만족하는 G1의 조건을 가진 칼라수지도장금속판이다., Which is a color resin coated metal plate having a condition of G 1 satisfying the following formula.

Description

칼라수지도장금속판 및 그 제조방법Color coated metal plate and manufacturing method thereof

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is a trivial issue, I did not include the contents of the text.

Claims (7)

착색안료를 함유하는 수지도막이 형성된 칼라수지도장금속판에 있어서, 이 착색수지도막형성전의 금속판의 60° 거울 광택도를 G0수지도막형성후의 도장금속판의 60° 거울광택도를 G1이라 할 때, G1이 다음식(1)을 만족하는 것을 특징으로 하는 칼라수지도장금속판.Wherein a 60 ° mirror gloss of the metal plate before forming the colored resin coating film is defined as G 1 , and a 60 ° mirror gloss of the coated metal sheet after forming the G 0 resin coating film is defined as G 1 , in a color resin coated metal plate on which a resin coating film containing a coloring pigment is formed, Wherein G 1 satisfies the following expression (1). G0〉G1≥0.5 G0(1)G 0 > G 1? 0.5 G 0 (1) 제1항에 있어서, 상기 착색수지도막의 부착량이 건조도막중량으로 환산해서 0.2~3.0g/㎡이고, 착색안료가 건조도막중 1~30중량%를 함유하도록 한 것을 특징으로 하는 칼라수지도장금속판.The coated metal plate according to any one of claims 1 to 3, wherein the amount of the colored resin coating film is 0.2 to 3.0 g / m 2 in terms of dry film weight, and the colored pigment contains 1 to 30 wt% . 제1항 또는제2항에 있어서, 헌터의 색차이식에 있어서의 크로마틱넥스지수(psychometic chroma coordinates)의 지수 a 및 b가 다음 (2)식을 만족하여 황금색의 색조를 가지도록 한 칼라수지도장금속판.The color image forming apparatus according to any one of claims 1 to 3, characterized in that the exponents a and b of the psychometic chroma coordinates in the color difference transfer of the hunter satisfy the following formula (2) plate. -4≤a≤6 및 2≤b≤25 (2)4 ≤ a ≤ 6 and 2 & 제1항 내지 제3항 중 어느 하나의 항에 있어서, 상기 수지도장전의 금속판이, 전기 아연도금강판의 칼라수지도장금속판.4. The metal plate according to any one of claims 1 to 3, wherein the metal plate of the electro-galvanized steel sheet is a colored resin-coated metal plate. 제4항에 있어서, 전기 아연독금강판의 Zn 도금층의 6방정 Zn의 결정의 방향성이 다음 (3)식을 만족하는 칼라수지도장금속판5. The electro-optical device according to claim 4, wherein the zinc plating layer of the electrodeless zinc-plated steel plate satisfies the following formula (3) 제4항 또는 제5항 중 어느 하나의 항에 있어서, 상기 전기 아연도금강판의 Zn 도금층표면의 임의 관찰영역에 있어서, 길이 5㎛ 이상의 Zn 단결정이 일정한 방향성이 가지고 성장하고 있는 영역의 면적이 상기 임의의 관찰영역의 전면적이 70% 이하인 칼라수지도장금속판.6. The Zn-coated steel sheet according to any one of claims 4 to 5, wherein an area of a region in which a Zn single crystal having a length of 5 占 퐉 or longer has a certain directionality and grows in an arbitrary observation region on the surface of the Zn- A color coated metal plate having a total area of an observation area of 70% or less. 착색안료를 함유하는 수분산형 또는 수용성 페인트를 사용하는 상기 청구항 제1항~6항중 어느 하나의 항에 기재되어 있는 칼라수지도장 금속판의 제조방법.A method for producing a color coated metal plate as set forth in any one of claims 1 to 6, wherein a water-dispersible or water-soluble paint containing a color pigment is used. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: It is disclosed by the contents of the first application.
KR1019960033832A 1995-08-29 1996-08-16 Metal plate of color resin-coated and the manufacturing method thereof KR100213541B1 (en)