KR970009400B1 - Preparation process of coatings for coated surface - Google Patents

Abstract

The painting membrane protection liquid is manufactured by (1) forming first solution by mixing cleansing dampness agent and preventing agent against static electricity with water. (2) blending coating agent, soluble agent, hydrophilic compound and emulsifier respectively at 1:1:1:1 ratio and then form second solution by mixing film packing agent and catalyst. (3) forming third solution by mixing brilliant protection agent and antiseptic. (4) mixing first and third solution first and stirring the mixture after adding third solution.

Description

Manufacturing method of coating film protection material

The present invention relates to a method of manufacturing a coating film protection material, and more particularly, to a method of manufacturing a coating film protection material for improving the glossiness of a car, a motorcycle, a household appliance, a kitchen cabinet, a wooden furniture, and preventing a change in the coating film.

Hereinafter, an example of the conventional coating film protection method will be described taking the case of a vehicle as an example.

In order to protect the coating film from various hazards such as acid rain, salt, ultraviolet rays, solar heat, etc. in the vehicle, washing with soap, synthetic detergent, etc. must be performed before washing. Next, after a certain period of time, the surface of the polishing component should be removed by rubbing with a cloth or the like.

However, according to this method, since detergents such as soap and synthetic detergent are used, water pollution caused by car wash waste water is caused. In addition, not only a lot of time is required for the work to protect the coating film, but also efforts to remove contaminants are required. Moreover, even if the work by the above-mentioned method was completed, there existed a problem that protection of a coating film does not last very long.

An object of the present invention is to solve the above problems, and to provide a method for producing a coating film protective material that can protect the coating film in a simple method in a short time.

In order to achieve the above object, the manufacturing method of the coating film protection material of the present invention is a process for forming a first solution by mixing a washing wetting agent and an antistatic agent in water, a coating agent, a solvent, a hydrophilic admixture and an emulsifier, respectively. : 1: 1 to form a second solution by mixing in a ratio, a step of forming a third solution by mixing a gloss protective agent and preservative, and after mixing the first solution and the third solution It consists of the process of mixing and stirring in the solution of 2, and finally, by immersing a nonwoven fabric in a coating film protective solution.

Hereinafter, the manufacturing method of the coating film protective solution of the present invention will be described in detail.

Example 1

1.5 g of carboxymethyl cellulose, which is a film enhancer, is added to a first container having 100 cc of water, and then stirred by using a stirrer or the like to dissolve.

Into the solution was added 1 ratio of silicone oil, which is a gloss and coating agent (hereinafter, 1 ratio means 6cc) and 1 ratio of sorbitan monooleic, which is a hydrophilic admixture, and then strongly to be a homogeneous milky mixture. Stir. Subsequently, 1% of ethyl acetate as a solvent was added to the solution, followed by stirring. Then, 1% of butyl cellosolve and 1% of Triton X-100 as an emulsifier were added, and a gelling liquid such as a homogeneous soap was obtained. Stir well with stirrer.

In a second container containing 1000 cc of water, propylene glycol 2 ratio as a washing and wetting agent was added and stirred, and 6 g of polyethylene glycol as a lubricating and antistatic agent was added and dissolved.

In a third container containing glycerin 1 ratio, which is a cleaning and gloss protection agent, 1.5-2 g of anoboric acid, preferably 1.7 g, as an antiseptic agent and a catalyst, is added thereto and stirred to dissolve completely. After complete dissolution, a proper amount of dilution methyl alcohol is added to dilute.

The solution in the third container diluted in this way is introduced into the second container to form a mixed liquid.

When the solution of the first container, which is the mixed solution, is slowly introduced into the second container by using a mixer or the like at high speed, the coating film protective solution according to the first embodiment of the present invention, such as milk, is obtained.

Example 2

20 cc of acetone, a solvent, is dissolved in a fourth container containing 0.5 g of cellulose acetate, which is a protective film coating agent. After about 24 hours, 1% of amyl acetate as a solvent is added, and 1% of sorbitan monooleic, which is a hydrophilic admixture, is mixed and mixed in a fifth container incorporating 2% of silicone oil as a film varnish.

The solution in the fourth vessel is added to the fifth vessel and mixed, and then a ratio of diacetone alcohol, an auxiliary admixture, is added and mixed well. Next, Triton X-100, an emulsifier, was added to the solution in a ratio of 1, and then stirred slowly with a low speed mixer to obtain a homogeneous transparent mixture.

Next, 2 parts of propylene glycol, a washing and wetting agent, was added and stirred in a sixth vessel containing 1000 cc of water, and then 6 g of polyethylene glycol, a lubricating and antistatic agent, was dissolved in a high speed mixer, and then glycerin was 1 in proportion. 1.7 g of oxoboric acid is added to the intrinsic seventh container and stirred to dissolve well without lumps. After complete dissolution, dilute by adding 20 cc of methyl alcohol. 4.5 g of trisodium phosphate as a cleaning agent was added to this diluted solution to dissolve it.

After mixing the solution in the sixth vessel and the solution in the seventh vessel, the mixture is stirred in a seventh vessel little by little by electric mixer.

By the above-described process, the coating film protective solution according to the second embodiment of the present invention is obtained.

The coating film protective material of the present invention is prepared using the coating film protective solution prepared by Example 1 or Example 2.

That is, the non-woven fabric (Yuhan Kimberly, Non-woven Fabric L150) is selected, which is excellent in absorbency and water retention, and foreign matters such as fine dusts do not damage the coating film, and the coating film protective solution of Example 1 or 2 above. After immersing in a predetermined time, the weight should be about 60 ~ 65g and then used.

In addition, when using for a single use, when the nonwoven fabric processed as mentioned above is inserted into a wrapping paper, and the opening part is heat-sealed and closed, the coating film protective material of this invention is completed.

As described above, according to the present invention, not only the coating film damage due to various hazards can be prevented, but also the effects of washing and glossing can be simultaneously obtained.

As mentioned above, although the invention made by this inventor was demonstrated according to the said Example, this invention is not limited to the said Example, Of course, it can change in various ways within the range which does not deviate from the summary.

For example, an appropriate amount of fragrance or the like may be added to the coating film protective solutions of the first and second embodiments.

In addition, methyl acetate, trichloroethylene, triethanol amine, or the like may be used instead of the ethyl acetate solution used in the coating film protective solution of the first embodiment.

In addition, methyl acetate may be used instead of the amyl acetate solution used in the coating film protective solution of the second embodiment, and TCE, TEA, butyl cell, or the like may be used instead of diacetone alcohol.

Claims (1)

In the manufacturing method of the coating film protective material prepared by immersing the nonwoven fabric in the coating film protective solution, the coating film protective solution is a cleaning wetting agent of two ratios (wherein one ratio is 6CC) and an antistatic agent of 1 ratio with respect to 1000CC water Mixing the process to form the first solution, coating agent, dissolving agent, hydrophilic admixture and emulsifier in the ratio of 1: 1: 1: 1, respectively, and then mixing the film filler and the catalyst to form a second solution The step of mixing, the ratio of the gloss protector of 1 ratio and 1.5 to 2g preservatives to form a third solution, after mixing the first solution and the third solution, and then mixed and stirred in the second solution The manufacturing method of the coating film protective material which consists of a process to make.