Abstract

Process for manufacturing the weight for fishing is described. Thus, a lots of stone are crushed in a hammer crusher, grinded below the size of a hulled millet, filtered, and mixed with a coagulant. The mixed powder is formed under pressure in a former with a shape of a half weight, a bilateral adhesion tape with a parting paper is attached with a smoothing nonabsorbent(11)(21) of the half-form weight(10)(20), pressed in a roller, and cut to give the weight for fishing with a set of two half-form weight.

Description

Fishing rods and manufacturing method thereof

제1도는 본 발명 일실시예의 제조공정 블럭도.1 is a manufacturing process block diagram of an embodiment of the present invention.

제2도는 본 발명 일실시예의 봉돌 사시도.Figure 2 is a perspective view of the pedestal of one embodiment of the present invention.

제3도는 본 발명 다른 실시예의 봉돌 사시도.3 is a perspective view of the pedestal of another embodiment of the present invention.

제4도는 본 발명 일실시 봉돌의 사용과정 설명도.Figure 4 is a diagram illustrating the use process of one embodiment of the present invention.

제5도는 종래에 봉돌로 사용되던 납봉의 사시도.5 is a perspective view of a lead rod conventionally used as a stick.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

A：봉돌본체 10, 20：반쪽봉돌A: Bonbon body 10, 20: Half stone

11, 21：평활상면 30：이형지11, 21: Smooth upper surface 30: Release paper

40：양면접착테이프40 ： Both sides adhesive tape

본 발명은 돌가루를 소결공법으로 압착성형한 인조석 봉돌이나 초자를 용해하여서 된 유리봉돌로된 낚시용봉돌과 이봉돌을 제조하는 제조방법에 관한 것으로, 더욱 구체적으로는 물고기를 낚시로 낚아올릴때 사용되는 낚시찌의 부력에 따라 낚시찌 올림을 경쾌하게 유지시키기 위하여 사용되는 낚시찌 부력 상승 억제용 봉돌로써, 그 원재료를 대체적으로 비중이 무거운 돌(石)가루나 초자(유리)를 원자재로하여 주므로서 부피를 작게 하여도 부력은 중량에 의하여 강하게 작용하므로 낚시용 봉돌로의 적용이 용이하고 돌가루로 봉돌을 성형함에 있어서는 소결성형시 돌가루의 결속과 융착을 촉진하는 분말상의 응고제를 적당량 혼합하여 소결성형시 발생되는 고열로 분말응고제가 순간적으로 용융되며 돌가루를 상호 융착하므로서 낚시용 봉돌을 형성하는 것으로 상기한 방법으로 성형되는 낚시용 봉돌은 전체를 1로 하였을때 반쪽에 해당하는 1/2로 각각 분리 형성하여 이들을 상호 접착하여 주므로서 전체를 이루게하며 접착되는 부위에는 낚시줄을 함께 부착시켜 놓아 일정기간 동안은 물속에서도 접착부위가 그 형태를 그대로 유지하므로서 낚시대의 사용시 봉돌이 쉽게 분리 이탈되는 것을 방지할 수 있게한 것이다.The present invention relates to a manufacturing method for manufacturing a fishing rod and a bongdol made of glass rods made by melting stone powder by pressing and sintering artificial stone bongdol or choja, more specifically used when fishing fish It is used to keep buoyant floats lightly according to the buoyant buoyancy of buoyant buoyancy, and it is used to suppress buoyancy rise. The buoyancy acts strongly by weight even if it is small, so it is easy to apply to fishing rods, and in forming the stone with stone powder, when sintering, a suitable amount of powder coagulant is mixed to promote binding and fusion of stone powder during sintering. The powder coagulant melts instantaneously with the generated high temperature, and it forms a fishing rod by melting the powder together. When the fishing rods formed by the above-mentioned method are formed in the above-mentioned manner, the whole fishing rods are formed in half corresponding to half when the whole is 1, thereby forming the whole by adhering them to each other and attaching the fishing line to the bonded portion together. By keeping the shape of the adhesive site in water for a certain period of time, it is possible to prevent the separation and separation of the rods easily when using the fishing rod.

특히, 본 발명의 낚시용 봉돌은 재질을 돌가루나 초자로 하였으므로 공해요인이 전혀 발생하지 않으며, 이의 소결성형시 사용되는 응고제도 인체에 무해하며 자연을 파괴하지 않는 무독성의 응고제를 사용하고 봉돌의 내면을 상호 부착시키는 접착제의 경우에도 무해한 접착제를 사용하여 일정기간이 경과한 후 물속이 봉돌이 남게 되어도 물을 오염시키거나 물고기 또는 조류가 이를 삼켰을때도 돌가루로 분해되게 하거나 응고 된 유리로 남게하여서 된 것이다.In particular, the fishing bondol of the present invention is made of stone powder or grass, so no pollution is generated, and the coagulant used in the sintering molding is harmless to the human body and uses a nontoxic coagulant that does not destroy nature. In the case of adhesives that adhere to each other, a harmless adhesive is used to contaminate the water even after a certain period of time, and contaminate the water even when fish or algae swallows it, or leave it as a solidified glass. will be.

종래에도 낚시용 봉돌은 계속적으로 사용되어지고 있는 실정이나 현재까지 낚시용으로 사용되는 봉돌은 납봉과 편납으로 그 주성분이 납(Pb)으로서 원자번호 82, 원자량 207, 21로 자체의 물성이 무르고 청백색인 금속원소이며 대개는 황의 화합물로서 산출되고 중량이 무겁고 전성이 풍부하여 열에 잘녹는 성분을 갖고 있으며 유독성이 강하여 생체조직을 파괴하는 성분을 갖고 있다.Conventionally, fishing rods are used continuously, but to date, the rods used for fishing are lead rods and single rods, whose main components are lead (Pb) with atomic number 82, atomic weight 207, 21, and their properties are soft and blue-white. Phosphorus is a metal element. It is usually a compound of sulfur. It is heavy in weight and rich in qualities, and has a heat-soluble component.

그리고 납의 성분과는 무관하게 중량이 무거우면서도 무른 특성에 의하여 낚시용 봉돌과 같이 낚시찌의 부력에 따른 중량적 효능에 의하여 높은 부력에도 작은 크기로도 무거운 중량을 유지하는 납의 특성이 바람직하고 물성이 무르기 때문에 후가공상태에서 현상변형이나 절단 또는 구부러짐이 용이하여 낚시줄에 나중에 설치하기 용이한 점등이 있어 낚시용 봉돌로써 납으로 된 납봉이나 편납을 사용하고 있으나 사용상의 용이점보다는 현대와 같이 자연환경을 보존하고 자연생태계를 유지하는데 필요한 조류나 각종 짐승들을 보호하는 차원에서는 납의 유독성 때문에 이를 사용하였을경우 납봉을 삼킨 물고기를 짐승이 먹었을경우 그 유독이 짐승의 몸에 퍼져 사망되게하는 경우와 조류의 경우는 납봉이나 편납을 돌이나 모래로 알고 쪼아 먹었을때 납중독에 의하여 사망하는 예가 수시로 발생하여 자연생태계를 위협하는 원인제공의 주범이었다고 할 것이다.In addition, the characteristics of lead, which maintains heavy weight even at high buoyancy and small size, are desirable due to the weight-efficiency according to the buoyancy of the fishing bobber, such as fishing rods, due to its heavy and soft characteristics, regardless of the content of lead. Because it is soft, it is easy to be deformed or cut or bent in post-processing state, so it is easy to install on the fishing line later, and it uses lead rods or braids as lead rods for fishing. In order to preserve the birds and various animals necessary for preservation and to maintain the natural ecosystem, the toxicity of lead causes the poisonous insects to spread and die in the body of the animals when birds are swallowed. If you know that the bee or pike is known as stone or sand, An example of death by poisoning was the culprit will cause provide a threat to natural ecosystems from time to time occur.

그리고, 납은 독성을 갖고 있어 자연생태계 뿐만 아니라 자연환경 특히 수질오염의 녹이 발생하여 우리가 후손에게 물려줄 자연 그대로는 밑에서부터 서서히 오염시키는 주범의 역할을 하고 있는 상태이어서 현재 또는 앞으로는 납을 봉돌로 사용하여 낚시찌의 부력상승 억제용으로서 사용을 억제하고 상호자제하여 수질을 오염시키는 것을 방지하여 자연을 그대로 유지시킬 수 있게함에 본 발명의 목적을 둔 것이다.In addition, lead is toxic, and rust in the natural environment, especially water pollution, occurs as a main culprit that gradually pollutes from the bottom as it is passed down to our descendants. It is an object of the present invention to suppress the use of buoyancy rise of fishing bobbers to prevent use and mutual control to contaminate water quality to maintain nature as it is.

본 발명에 적용되는 낚시용 봉돌의 일실시 제조공정을 과정순서에 따라 각 공정별로 나누어 설명하면 다음과 같다.When explaining the manufacturing process of one embodiment fishing rods applied to the present invention divided by each process according to the process sequence as follows.

제1공정1st process

산이나 채석장에서 채집한 돌이나 개울에서 채집되는 차돌을 햄머 분쇄기에서 먼저 덩어리 상태로 부셔준 다음 이를 절단분쇄기에서 재차 분쇄하여준 것을 미분쇄장치에서 좁쌀크기보다 작은 입자로 분쇄하여 걸름장치를 통과시켜주고 통과하지 못한 것보다 큰 입자의 모래들은 다시 바이패스 되어 미분쇄장치에서 분쇄하여 주고 걸름장치를 통과한 분말입자는 혼합장치로 공급되어 별도의 이송장치로 공급되는 분말응고제와 적당한 상태로 혼합되어지게한 제1공정으로 돌가루의 비중은 무거운 상태이므로 응고제와의 혼합비율은 돌가루의 중량에 비례하여지게 공급하여 지는 것으로 응고제는 인체에 무해하며 자연환경을 손상시키지 않는 약품을 사용함이 바람직하다.The stone collected from the mountain or quarry is first broken into lumps in a hammer grinder, and then crushed again by a crusher to crush into smaller particles than the size of millet in a crusher. The sand of particles larger than the ones that cannot be passed through are bypassed again and pulverized in the pulverizing device, and the powder particles passed through the filtering device are mixed with the powder coagulant which is supplied to the mixing device and supplied to a separate conveying device. As the specific gravity of the stone powder is heavy in the first process, the mixing ratio with the coagulant is supplied in proportion to the weight of the stone powder. The coagulant is preferably harmless to humans and does not damage the natural environment. .

제2공정2nd process

제1공정을 거쳐서 얻어진 돌가루와 응고제 분말이 혼합 된 혼합가루를 봉돌의 반쪽형태로 이루어진 성형장치에 넣고 소결공법으로 압착 성형하면 응고제가 순간적으로 녹으며 소결되는 돌가루를 순간적으로 접착시키며 외면을 매끄럽게하여 봉돌형상(반쪽)을 이룬 상태의 것을 진동자를 구비한 이송장치에서 반원형반쪽(콩반쪽형상)이 눕혀진 상태로 이송하며 이형지를 표면에 갖춘 양면 접착 테이프를 눕혀있는 상면에 로울러의 압착방법으로 긴밀하게 접착하여 준 것을 절단장치에서 두쪽을 한조로 하여 절단하고 이를 일정량씩 포장하여 제품으로 판매할 수 있게하므로서 일실시 방법에 따른 제조과정이 완성되는 것이다.When the mixed powder obtained by the first step is mixed with the coagulant powder into the molding device which is formed into the half-shaped form of the stick stone and press-molded by the sintering method, the coagulant is instantly melted and the sintered stone is momentarily adhered to How to press the roller on the upper surface of the double-sided adhesive tape provided on the surface of the semi-circular half (bean half shape) in the state of smoothing and forming the pedestal shape (half) in the lying state. By closely adhering to the cutting device to cut the two sides in a pair and packaging them by a certain amount to be sold as a product is to complete the manufacturing process according to one embodiment method.

이상에서와 같은 제조방법은 중량비가 무거우며 자연생태계를 전혀 해치지 않는 돌을 원재료로 하여 제조하는 제조공정을 나타낸 것으로써, 본 발명에서 적용되는 원재료는 돌이외에도 인체에 무해하고 자연생태계를 해치지 않는 초자(유리)를 재료로하여 생산할 수도 있는 것으로서 초자를 이용한 경우에도 상기의 분쇄장치 대신 용광로에서 초자를 녹여주고 일정한 크기로 성형기에서 성형한 것을 상기한 공정과 같이 눕혀주고 테이판을 부착절단 포장하여주므로서 완성되는 것이어서 본 발명의 일실시 공정과 일부 상이한 제조공정이 있으나 이와 같은 것은 제품을 성형하는 원재료에 따라 약간의 차이점이 발생할 수 있는 정도의 것이어서 본 발명에서는 자연과 생태계를 해치는 납(Pb)를 이용하지 않고 이와 대체할 수 있는 재질이며 자연의 생태계나 환경을 손상시키지 않는 제품을 얻게한 것이다.The manufacturing method as described above shows a manufacturing process of manufacturing a stone with a heavy weight ratio and does not harm the natural ecosystem at all as a raw material, the raw material applied in the present invention is harmless to the human body in addition to the stone and does not harm the natural ecosystem (Glass) can be produced as a material, and even when using a candle, melt the candle in a blast furnace instead of the above crushing device, and the molded in a molding machine to a certain size, laid down in the same manner as described above, and the tape is attached and cut packaging There is some different manufacturing process from one embodiment of the present invention because it is completed, such as this is a degree that can cause a slight difference depending on the raw material for molding the product in the present invention lead (Pb) that harms nature and ecosystem It is a material that can be replaced without using it and ecology of nature I will get a product that does not damage the environment.

본 발명의 제조공정에 의하여 제조되는 돌가루를 이용한 봉돌의 구조를 보면 콩을 두쪽으로 쪼개어진 것과 같은 형상으로 된 두개의 반쪽봉돌(10)(20)을 눕혀서 평활상면(11)(21)이 되게한 부위에 상면에 이형지(30)가 부착 된 양면 접착테이프(40)를 부착고정하여 두개를 일조로 하여서 된 돌가루를 이용한 봉돌본체(A)로 이루어진 것이다.Looking at the structure of the Bongdol using the stone powder produced by the manufacturing process of the present invention by laying the two halves (10, 20) in the same shape as the bean is split into two smooth top surface (11, 21) Fixing the double-sided adhesive tape 40 attached to the release paper 30 is attached to the upper surface to be made of a doldol main body (A) using a stone made of a pair of two.

이상과 같은 구조로 된 본 발명 일실시예의 돌가루를 이용한 봉돌본체(A)은 비중이 무거운 돌을 주성분으로하여 봉돌을 성형하였고 반쪽형의 것을 맞닿게 접착하여사용하게 하므로서 일정기간(약 24시간 사용예정)동안의 사용후에는 서로 접착하고 있던 접착제층이 수분의 침투로 떨어질수가 있으므로 이중물에 붙은 접착테이프는 떼어내고 수분을 제거한 다음 다른 테이프를 이용하여 다시 부착시켜 재사용할 수 있게 하므로서 봉돌의 사용횟수를 한번에 그치지 않고 여러번 반복하여 사용할 수 있으므로 일단 낚시찌의 부력과 맞춘봉돌은 분식을 하지 않는 상태에서 반복적인 사용이 가능하므로 필요이상의 쓰러게기를 발생시키지 않는 효과를 갖는 것이다.Bongdol main body (A) using the stone powder of an embodiment of the present invention having the above structure as a main component was formed by using a heavy stone as the main component to bond the half-shaped to a certain period (approximately 24 hours After the use), the adhesive layers that have been bonded to each other may fall off due to the penetration of water, so the adhesive tape on the double object can be peeled off, the moisture removed, and then re-attached using another tape so that it can be reused. Since the number of times can be used repeatedly without repeating the number of times, the buoyancy of the bobber and the matched rods can be used repeatedly without being eaten, thus having the effect of not causing more waste than necessary.

그리고, 본 발명에 사용되는 봉돌의 사용방법은 먼저 상기 제조공정에서 만들어진 봉돌본체(A)의 이형지(30)를 떼어내고 낚시바늘의 묶음부를 두쪽의 봉돌중 일측의 봉돌(10)에 위치시킨다음 반대쪽의 봉돌(20)을 얻어 주고 눌러주므로서 낚시바늘에 고정이 이루어지게 하는 것이다.In addition, the method of using the pedestal used in the present invention first removes the release paper 30 of the pedestal body (A) made in the manufacturing process and places the bundle of fishing needles on the pedestal 10 on one side of the two pedestals. By obtaining and pressing the opposite side of the bumper 20 is to be fixed to the fishing needle.

이와 같은 상태로 사용되는 본 발명의 봉돌본체(A)는 그 재질은 돌이나 유리등과 같이 자연의 생태계를 해치지 않고 수질을 오염시키지 않으면서도 각종 조류들이 음식물의 소화를 위하여 인위적으로 섭취하는 모래(콩알크기미만)를 섭취할 때 본 발명의 봉돌본체(A)를 섭취하여도 조류의 몸체는 전혀 다른 장애를 주지 않게 한 것과, 자체성분이 돌이나 유리로 되어 있어 자연과 수질의 오염을 시키지 않아 자연보호차원에서 적극 권장할 수 있는 낚시용 봉돌인 것이다.The Bongdol body (A) of the present invention used in such a state is made of sand which is artificially ingested for digestion of food by various materials without harming natural ecosystems such as stones or glass and contaminating water quality. When the intake of the Bongdol main body (A) of the present invention when the intake of soybeans (less than the size of soybeans) does not cause any other obstacles, and its own components are made of stone or glass and do not contaminate nature and water. It is a fishing rod that can be highly recommended for nature conservation.

Claims

A first step of pressing and crushing the collected stone by grinding the pulverizer with a powder coagulant and a mixing device by grinding the collected stone into a size smaller than that of millet in a crusher and a pulverizer using a sintering method in a half-shaped block forming machine; The second step of packing the half bars formed in the process by laying them in a conveying device using a true automatic, supplying a double-sided adhesive tape with a release paper, pressing them with a roller, cutting them into a pair, and cutting them into a set. Method for manufacturing a fishing rod with raw stone made of a combination of raw materials.

Two half sticks are formed by attaching adhesive tape 40 with release paper 30 to the smooth top surfaces 11 and 21 of the half-shaped sticks 10 and 20 by mixing and molding the stone powder and the coagulant. Fishing rods.

The fishing rod according to claim 2, wherein the raw material of the half rods (10) and (20) is made of choza.