KR950025113A - Carburized Gear Steel - Google Patents
Carburized Gear Steel Download PDFInfo
- Publication number
- KR950025113A KR950025113A KR1019940033589A KR19940033589A KR950025113A KR 950025113 A KR950025113 A KR 950025113A KR 1019940033589 A KR1019940033589 A KR 1019940033589A KR 19940033589 A KR19940033589 A KR 19940033589A KR 950025113 A KR950025113 A KR 950025113A
- Authority
- KR
- South Korea
- Prior art keywords
- carburizing
- steel
- tempering
- quenching
- less
- Prior art date
Abstract
중량%로 C 0.18~0.25%, Si 0.45~1.00%, Mn 0.40~0.70%, Ni 0.30~0.70%, Cr 1.00~1.50%, MO 0.30~0.70%, Cu 0.50%이하, Al 0.015~0.030%, V 0.03~0.30%, Nb 0.010~0.030%, O 0.0015%이하, N 0.0100~0.0200%이고, 나머지가 Fe 및 불가피한 불순물로 구성되며, 침탄후의 820℃이상에서 담금질하여도, 침탄강 중심부의 경화된 조직에 페라이트를 형성하는 일이 없으며, 담금질후 160~180℃의 온도로 뜨임을 행하고, 이 뜨임온도를 포함하여 300℃까지의 온도중 어느 하나의 온도로 재가열하여서, 침탄, 담금질 및 뜨임후 침탄강의 침단층의 강도가 HV 50이상까지 감소되지 않는 것을 특징으로 하는 연화저항을 갖는 침탄기어용강.By weight% C 0.18 ~ 0.25%, Si 0.45 ~ 1.00%, Mn 0.40 ~ 0.70%, Ni 0.30 ~ 0.70%, Cr 1.00 ~ 1.50%, MO 0.30 ~ 0.70%, Cu 0.50% or less, Al 0.015 ~ 0.030%, V 0.03 ~ 0.30%, Nb 0.010 ~ 0.030%, O 0.0015% or less, N 0.0100 ~ 0.0200%, the remainder is composed of Fe and unavoidable impurities, and hardened at the center of the carburized steel even if quenched at 820 ℃ or higher after carburizing There is no formation of ferrite in the tissue, and after quenching, tempering is performed at a temperature of 160 to 180 ° C, and reheating to any one of temperatures up to 300 ° C including this tempering temperature, thereby carburizing, quenching and carburizing after tempering Carburizing gear steel having a softening resistance, characterized in that the strength of the steel sedimentation layer is not reduced to more than HV 50.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
제2도는 재가열실험에 적용되는 열처리조건의 설명도,2 is an explanatory diagram of heat treatment conditions applied to the reheating test,
제3도는 재가열후의 경도감소 및 Si함유량의 관계를 나타내는 그래프.3 is a graph showing the relationship between the decrease in hardness and the Si content after reheating.
Claims (2)