KR950018508A - Method of manufacturing carbon dioxide welding rod steel - Google Patents
Method of manufacturing carbon dioxide welding rod steel Download PDFInfo
- Publication number
- KR950018508A KR950018508A KR1019930027670A KR930027670A KR950018508A KR 950018508 A KR950018508 A KR 950018508A KR 1019930027670 A KR1019930027670 A KR 1019930027670A KR 930027670 A KR930027670 A KR 930027670A KR 950018508 A KR950018508 A KR 950018508A
- Authority
- KR
- South Korea
- Prior art keywords
- steel
- sio
- welding rod
- molten steel
- carbon dioxide
- Prior art date
Abstract
본 발명은 이산화탄소 용접봉으로 사용되는 강재의 제조방법에 관한 것으로써, 보다 상세하게는, 주조시 노즐막힘이 없고, 주편에서 핀홀등이 발생되지 않을 뿐만아니라 용접시 용접결함이 발생하지 않는 CO2용접봉용 강재를 제조하고자 하는데, 그 목적이 있다.The present invention relates to a method of manufacturing a steel product for use as a carbon electrode, more specifically, there is no nozzle clogging during casting, as well as the like pin holes do not occur in the cast steel CO 2 welding electrode does not occur to weld defects during welding To manufacture molten steel, the purpose is.
본 발명은 이산화탄소 용접봉용 강재를 제조하는 방법에 있어서, 전로에서 산소로 취련한 후 레이들로 용강을 출강할 시 Fe-Si및 Fe-Mn을 단독 또는 복합으로 레이들에 투입하여 용강중의 산소함량이 15ppm 이하가 되도록 탈산시킨 다음, CaO-SiO2계 플럭스를 레이들에 투입하여 슬래그를, CaO/SiO2중량비:1.0-1.4, SiO2/Al203중량비:2/0이상, T ㆍFe :1.0%이하 및 Al2O3:15% 이하가 되도록 조절한 후, 빌레트 연주기에서 연주하여 이산화탄소 용접봉용 강재를 제조하는 방법을 그 요지로 한다.The present invention is a method of manufacturing a carbon dioxide welding rod steel, the oxygen content in molten steel by injecting Fe-Si and Fe-Mn into the ladle alone or in combination when the molten steel is removed from the converter after the molten steel is blown with oxygen After deoxidizing to 15 ppm or less, a slag was introduced by adding CaO-SiO 2 flux to the ladle, and CaO / SiO 2 weight ratio: 1.0-1.4, SiO 2 / Al 2 0 3 weight ratio: 2/0 or more, T Fe: and the was adjusted such that more than 15%, the method for producing a carbon steel welding rod for to play on the billet continuous caster to the base: more than 1.0% and Al 2 O 3.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
Claims (1)