KR950018301A - Glass-fiber reinforced polyamide 66 resin composition with excellent surface properties - Google Patents

Glass-fiber reinforced polyamide 66 resin composition with excellent surface properties Download PDF

Info

Publication number
KR950018301A
KR950018301A KR1019930029308A KR930029308A KR950018301A KR 950018301 A KR950018301 A KR 950018301A KR 1019930029308 A KR1019930029308 A KR 1019930029308A KR 930029308 A KR930029308 A KR 930029308A KR 950018301 A KR950018301 A KR 950018301A
Authority
KR
South Korea
Prior art keywords
polyamide
resin composition
parts
weight
resin
Prior art date
Application number
KR1019930029308A
Other languages
Korean (ko)
Other versions
KR970006758B1 (en
Inventor
이승환
신문철
고동휘
윤호용
Original Assignee
하기주
주식회사 코오롱
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 하기주, 주식회사 코오롱 filed Critical 하기주
Priority to KR1019930029308A priority Critical patent/KR970006758B1/en
Publication of KR950018301A publication Critical patent/KR950018301A/en
Application granted granted Critical
Publication of KR970006758B1 publication Critical patent/KR970006758B1/en

Abstract

본 발명은 표면 특성이 개선된 폴리아미드66 수지조성물에 관한 것으로서, 폴리아미드66 수지 100중량부에 대하여 하기 구조식(I)으로 나타내어지며 상온에서 용액 상태 정도가 3.0~3.5인 폴리아미드 46수지 5~25 중량부를 첨가하여 이루어지는 폴리아미드 수지조성물을 제공한다.The present invention relates to a polyamide 66 resin composition having improved surface properties, which is represented by the following structural formula (I) with respect to 100 parts by weight of polyamide 66 resin, and has a polyamide 46 resin of 5 to 3 in a solution state at room temperature of 3.0 to 3.5. The polyamide resin composition which adds 25 weight part is provided.

-(NHR1NHCOR2CO)n...................................(I)-(NHR 1 NHCOR 2 CO) n ................................... (I)

(여기에서, n은 100~200의 정수이고, R1은 -(CH2)4-이며, R2은 -(CH2)6-이다.Wherein n is an integer from 100 to 200, R 1 is-(CH 2 ) 4- , and R 2 is-(CH 2 ) 6- .

Description

표면 특성이 우수한 유리섬유강화 폴리아미드66 수지조성물Glass-fiber reinforced polyamide 66 resin composition with excellent surface properties

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.

Claims (5)

폴리아미드66 수지 100 중량부에 대하여 하기 구조식 (Ⅰ)의로 나타내어지는 상온에서 용액 상태의 상대점도가 3.0∼3.5인 폴리아미드46 수지 5∼25 중량부를 첨가하여 이루어지는 폴리아미드 수지조성물.A polyamide resin composition comprising 5 to 25 parts by weight of a polyamide 46 resin having a relative viscosity of 3.0 to 3.5 in a solution state at room temperature represented by the following structural formula (I) to 100 parts by weight of polyamide 66 resin. [구조식 1][Formula 1] -(NHR1NHCOR2Co)n -(NHR 1 NHCOR 2 Co) n (여기에서, n은 100∼200의 정수이고, R1은 -(CH2)4-이며, R2은 -(CH2)6-이다.)(Wherein n is an integer from 100 to 200, R 1 is-(CH 2 ) 4- , and R 2 is-(CH 2 ) 6- .) 제1항에 있어서, 유리섬유를 수지조성물 전체 100 중량부에 대하여 10∼60 중량부 되도록 첨가함을 특징으로 하는 폴리아미드66 수지조성물.The polyamide 66 resin composition according to claim 1, wherein the glass fiber is added in an amount of 10 to 60 parts by weight based on 100 parts by weight of the total resin composition. 제1항 또는 제2항에 있어서, 상기한 유리섬유는 아미노 실란계 커플링제를 표면처리된 것임을 특징으로 하는 폴리아미드66 수지조성물.The polyamide 66 resin composition according to claim 1 or 2, wherein the glass fiber is surface treated with an amino silane coupling agent. 제1항에 있어서, 구리계, 힌더드페놀계, 아민계, 인계, 또는 황계로 이루어지는 군에서 선택되어지는 내열제가 폴리아미드66 수지 100 중량부에 대하여 0.05∼2.0 중량부 첨가 되어짐을 특징으로 하는 폴리아미드66 수지 조성물.The heat-resistant agent selected from the group consisting of copper, hindered phenol, amine, phosphorus or sulfur is added in an amount of 0.05 to 2.0 parts by weight based on 100 parts by weight of polyamide 66 resin. Polyamide 66 Resin Composition. 제1항에 있어서, 이형제를 폴리아미드66 수지 100 중량부에 대하여 0.2∼3.0 중량부 첨가되어짐을 특징으로 하는 폴리아미드66 수지조성물.The polyamide 66 resin composition according to claim 1, wherein the release agent is added in an amount of 0.2 to 3.0 parts by weight based on 100 parts by weight of the polyamide 66 resin. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019930029308A 1993-12-23 1993-12-23 Polyamide 66 resin composition KR970006758B1 (en)