KR950000792A - Thermoplastic resin composition - Google Patents

Thermoplastic resin composition Download PDF

Info

Publication number
KR950000792A
KR950000792A KR1019930011049A KR930011049A KR950000792A KR 950000792 A KR950000792 A KR 950000792A KR 1019930011049 A KR1019930011049 A KR 1019930011049A KR 930011049 A KR930011049 A KR 930011049A KR 950000792 A KR950000792 A KR 950000792A
Authority
KR
South Korea
Prior art keywords
weight
resin composition
thermoplastic resin
parts
butadiene
Prior art date
Application number
KR1019930011049A
Other languages
Korean (ko)
Inventor
김기수
정익수
김윤기
Original Assignee
구창남
동양나이론 주식회사
배도
동양폴리에스터 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 구창남, 동양나이론 주식회사, 배도, 동양폴리에스터 주식회사 filed Critical 구창남
Priority to KR1019930011049A priority Critical patent/KR950000792A/en
Publication of KR950000792A publication Critical patent/KR950000792A/en

Abstract

본 발명은 (A) 공액 디앤계 고무 존재하에서 방향족 비닐화합물, 시안화 비닐화합물 및 카르본산 알킬에스테르로 부터 선택된 2종 이상의 단량체로 중합한 ABS계 중합체: 10 내지 95중량%, (B) 폴리카보네이트수지: 90 내지 10중량%, (C) 메틸메타크릴레이트-부타디엔-스티렌공중합체: (A)+(B)에 대해 1 내지 50중량부, (D) 페놀계 및 인계 안정제: (A)+(B)+(C)에 대해 각각 0.01 내지 5중량부, (E) 폴리올레핀 왁스: (A)+(B)+(C)에 대해 0.01 내지 5중량부를 함유한 것을 특징으로 하는 열가소성 수지 조성물로써, 다양한 두께와 넓은 온도범위에서 높은 충격강도를 나타내면서 우수한 가공성, 내열안정성을 가진다.The present invention relates to an ABS polymer polymerized with (A) at least two monomers selected from aromatic vinyl compounds, vinyl cyanide compounds and carboxylic acid alkyl esters in the presence of conjugated diane rubbers: 10 to 95% by weight, (B) polycarbonate resins. : 90 to 10% by weight, (C) methyl methacrylate-butadiene-styrene copolymer: 1 to 50 parts by weight based on (A) + (B), (D) phenolic and phosphorus stabilizers: (A) + ( 0.01 to 5 parts by weight of each of B) + (C), and (E) polyolefin wax: 0.01 to 5 parts by weight of (A) + (B) + (C), the thermoplastic resin composition comprising: It has high impact strength at various thicknesses and wide temperature ranges, and has excellent processability and heat stability.

Description

열가소성 수지 조성물Thermoplastic resin composition

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.

Claims (6)

(A) 공액 디앤계 고무 존재하에서 방향족 비닐화합물, 시안화 비닐화합물 및 카르본산 알킬에스테르로 부터 선택된 2종 이상의 단량체로 중첩한 ABS계 중합체: 10 내지 90중량%, (B) 폴리카보네이트 수지: 90 내지 10중량%, (C) 메틸메타크릴레이트-부타디엔-스티렌공중합체: (A)+(B)에 대해 1 내지 50중량부, (D) 페놀계 및 인계 안정제: (A)+(B)+(C)에 대해 각각 0.01 내지 5중량부, (E) 폴리올레핀 왁스: (A)+(B)+(C)에 대해 0.01 내지 5중량부를 함유하여 조성되는 것을 특징으로 하는 열가소성 수지 조성물(A) ABS polymer overlapped with two or more monomers selected from aromatic vinyl compounds, vinyl cyanide compounds and carboxylic acid alkyl esters in the presence of conjugated diane rubber: 10 to 90% by weight, (B) polycarbonate resin: 90 to 10% by weight, (C) methyl methacrylate-butadiene-styrene copolymer: 1 to 50 parts by weight relative to (A) + (B), (D) phenolic and phosphorus stabilizers: (A) + (B) + 0.01 to 5 parts by weight relative to (C) and (E) polyolefin wax: 0.01 to 5 parts by weight based on (A) + (B) + (C) 제1항에 있어서, 폴리카보네이트 수지는 방향족 폴리카보네이트로서, 평균분자량이 10,000 내지 200,000인 것을 특징으로 하는 열가소성 수지 조성물.The thermoplastic resin composition according to claim 1, wherein the polycarbonate resin is an aromatic polycarbonate, and has an average molecular weight of 10,000 to 200,000. 제1항에 있어서, ABS계 중합체는 아크릴로니트릴-부타디엔-스티렌수지, 또는 아크릴로니트릴-부타디엔-스티렌-알파-메틸스티렌 수지인 것을 특징으로 하는 열가소성 수지 조성물.The thermoplastic resin composition according to claim 1, wherein the ABS polymer is acrylonitrile-butadiene-styrene resin or acrylonitrile-butadiene-styrene-alpha-methylstyrene resin. 제1항에 있어서, 메틸메타크릴레이트-부타디엔-스티렌 공중합체의 유리온도가 140℃ 내지 170℃인 것을 특징으로 하는 열가소성 수지 조성물.The thermoplastic resin composition according to claim 1, wherein the methyl methacrylate-butadiene-styrene copolymer has a glass temperature of 140 ° C to 170 ° C. 제1항에 있어서,페놀계 및 인계 안정제는 각각 트리스(3,5-디-t-부틸-4-히드록시벤질)이소시아눌레이트 및 시크릭네오펜탄 테트라일 비스(2-t-부틸-4-메틸페닐포스파이트)인 것을 특징으로 하는 열가소성 수지 조성물.2. The phenolic and phosphorus stabilizers of claim 1 are tris (3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate and cycloneopentane tetrayl bis (2-t-butyl- 4-methylphenyl phosphite). 제1항에 있어서, 폴리올레핀 왁스는 평균 분자량이 1,000 내지 5,000인 폴리에틸렌, 또는 결정성 저분자량 폴리프로필렌, 또는 평균분자량이 450 이상인 파라핀 왁스인 것을 특징으로 하는 열가소성 수지 조성물.The thermoplastic resin composition according to claim 1, wherein the polyolefin wax is polyethylene having an average molecular weight of 1,000 to 5,000, crystalline low molecular weight polypropylene, or paraffin wax having an average molecular weight of 450 or more. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019930011049A 1993-06-17 1993-06-17 Thermoplastic resin composition KR950000792A (en)