KR920003571B1 - Towel and a process for manufacturing the same - Google Patents
Towel and a process for manufacturing the same Download PDFInfo
- Publication number
- KR920003571B1 KR920003571B1 KR1019890010670A KR890010670A KR920003571B1 KR 920003571 B1 KR920003571 B1 KR 920003571B1 KR 1019890010670 A KR1019890010670 A KR 1019890010670A KR 890010670 A KR890010670 A KR 890010670A KR 920003571 B1 KR920003571 B1 KR 920003571B1
- Authority
- KR
- South Korea
- Prior art keywords
- cellulose
- layer
- nylon
- polyester
- towel
- Prior art date
Abstract
Description
첨부도면은 본 발명 수건의 단면도.The accompanying drawings are cross-sectional views of the present invention towel.
본 발명은 니트(KNIT) 또는 오우븐(WOVEN) 직물로써 흡수효과가 우수한 수건 및 이를 제조하기 위한 방법에 관한 것이다.The present invention relates to a towel having excellent absorption effect as a KNIT or WOVEN fabric and a method for manufacturing the same.
종래 수건은 타올 직기를 이용하여 위사와 경사에 의한 제직으로 일반적으로 100% 면을 사용하여 제직, 재단, 봉재하여 제작하였으나 100% 면을 사용한 수건의 흡수효과는 한계가 있고 흡습효과도 떨어졌다.Conventionally, towels are manufactured by weaving, cutting and sewing 100% cotton using weaving yarns and warp yarns using a towel loom, but the absorption effect of the towel using 100% cotton is limited and the moisture absorption effect is inferior.
본 발명은 일반적인 수건보다 흡수속도가 2-5배 이상의 흡수효과가 있으며 흡습량도 1.5배정도 향상효과를 얻을 수 있다.The present invention has an absorption rate of more than 2-5 times the absorption rate than the general towel, and the moisture absorption amount can also be improved by 1.5 times.
본 발명의 구성은 셀룰로오스층(1), 폴리에스텔 또는 나일론으로 된 층(2), 접착층(3), 폴리에스텔 또는 나일론으로 된 층(2') 셀룰로오스층(1')을 차례로 구성하고 셀룰로오스층(1)(1')이 양표면에 위치토록 하였다.The composition of the present invention constitutes a cellulose layer (1), a layer made of polyester or nylon (2), an adhesive layer (3), a layer made of polyester or nylon (2 ') and a cellulose layer (1'), in turn (1) (1 ') was placed on both surfaces.
제조방법은 저 α-목재펄프의 α-셀룰로오스를 90% 이상 함유한 셀룰로오스를 머서화하고, 섬유 굵기를 1.5데니아 이하, 섬유장을 44mm 정도로 된 셀룰로오스 섬유로 방적한 원사를 표면에 사용하고 수분 침투를 방해하는 층을 최소화하여 삼투압효과를 증진시키고 습윤강도를 1.4~2.0g/데니아로 하여 면의 습윤 강도 3.3-6.4g/데니아 보다 약하게 하여 피부와의 접촉부위 손상을 적도록 하고 촉감이 면보다 부드럽도록 하였다.The manufacturing method mercurizes cellulose containing 90% or more of α-cellulose of low α-wood pulp, and uses a yarn spun with cellulose fibers having a fiber thickness of 1.5 denier or less and a fiber length of about 44 mm to the surface and infiltrate moisture. The osmotic effect is minimized by minimizing the layer that hinders, and the wet strength is 1.4-2.0 g / denia, so that the wet strength of cotton is less than 3.3-6.4 g / denia, so that the contact area with skin is less damaged and the touch is softer than cotton. It was made.
편직(제직)시 상기 흡수효과가 좋은 원사를 표면층으로 하고, 내층에는 내구성이 좋은 나일론이나 폴리에스텔을 사용하여 이중구조를 편직(제직)하여 염색 가공후 흡습성이 높은 부분이 앞뒤로 나올 수 있도록 폴리에스텔이나 나일론이 있는 뒤쪽면은 서로 마주보도록 고무성 접착제나 폴리우레탄계 접착제를 이용 접착하여 원단을 만들었다. 이 원단을 재단 봉제하여 수건을 제작한다.When weaving (weaving), the yarn with good absorption effect is used as the surface layer, and the inner layer is made of nylon or polyester with high durability to knit (weaving) the double structure, so that the highly hygroscopic part can come out after dyeing processing. The back surface with nylon or nylon was made of rubber or polyurethane-based adhesive to face each other. The fabric is cut and sewn to make a towel.
[실시예]EXAMPLE
1) 나일론 40D/TR 11%+셀룰로오스원사 89%, 28GG, 10/22, 00/44 조직, 3바, 트리코트로 제조한 1차 원단을 2겹으로 접착하여 2차원단으로 완성함. 549g/47"/YD(접착후 원단의 무게), 2) 상기 1)번 원단의 1차 앞뒤를 뽑삥 가공(고속페이파기모)한 원단으로 2차원단을 완성함. 527g/44"/YD(접착후), 3) 나일론 40D/TR 12%+상기 셀룰로오스원사 82%, 28GG, 트리코트, 10/12, 00/34 조직, 3바 트리코트로 가공한 원단으로 2차원단을 완성함. 495g/50"/YD(접착후), 4) 상기 3)번 원단을 뽑삥(고속페이파기모)가공한 원단으로 2차원단을 완성함. 459g/45"/YD(접착후), 5) 폴리에스타 75D/SD 15%+ 상기 원사 85%, 22GG. 데리조직, 2mm(루으프진이)로 가공한 원단으로 2차원단을 완성함. 757g/62"/YD(접착후), 6) 폴리에스타 75D/SD 15.3%+상기 원사 84.7%, 24GG 벨로아 조직, 루우프길이 3mm로 가공한 원단으로 2차원단을 완성함.1) Nylon 40D / TR 11% + Cellulose yarn 89%, 28GG, 10/22, 00/44 The primary fabric made of tissue, 3 bar, and tricoat is bonded in two layers to complete the two-dimensional stage. 549g / 47 "/ YD (weight of fabric after gluing), 2) Finishing two-dimensional stage with fabric with high-speed paper-papping after pulling 1st front and back of fabric 1). 527g / 44 "/ YD (After Bonding), 3) Nylon 40D / TR 12% + The Cellulose Yarn 82%, 28GG, Tricot, 10/12, 00/34 Tissue, 3 Bar Tricot Complete the Dimensional Step. 495g / 50 "/ YD (After Bonding), 4) Pull out fabric 3) and finish the 2D stage with high speed brushed fabric. 459 g / 45 s / YD (after bonding), 5) Polyestera 75D / SD 15% + 85% of the yarn, 22GG. Pickled tissue, fabricated with 2mm (Loupe Jean), completes a two-dimensional stage. 757g / 62 "/ YD (After Bonding), 6) Polyester 75D / SD 15.3% + 84.7% of the yarn, 24GG bellows tissue, 3mm of loop length.
7) 일반 A사 제품 수건7) Towel of general A company
8) 일반 B사 제품 수건8) Towel made by Company B
9) 일반 C사 제품 수건9) General C Company Towel
본 발명으로 처리한 직물은 상기 실시예 1)~6)번까지이며 시중 일반 제품은 7)~9)임, 9)번은 당사 실험실 측정수치이며 상기 1)~8)번까지 흡수성 및 흡습성은 한국의류 시험검사소에서 시험한 방법임.Fabrics treated with the present invention is the above Examples 1) ~ 6) and the general commercial products 7) ~ 9), 9) is our laboratory measurement value and the absorbency and hygroscopicity up to 1) ~ 8) Korea Tested by the Clothing Testing Laboratory.
일반적인 수건(샘플 7,8,9)보다 흡수성이 2-5배 이상됨을 알 수 있다.It can be seen that the absorbency is 2-5 times or more than a general towel (samples 7,8,9).
<흡수성 대비표><Absorbency comparison table>
흡습성 시험법 : 한국의류시험검사소Hygroscopicity Test Method: Korea Apparel Testing & Research Institute
1. 전처리 : 표준상태(RH 65%±2%, 20℃±2℃)에서 24시간 방치 : A1.Pretreatment: 24 hours at standard condition (RH 65% ± 2%, 20 ℃ ± 2 ℃): A
2. 시험조에서 30℃ 90% RH, 1시간, 3시간, 5시간, 7시간 : B2. 30 ° C 90% RH, 1 hour, 3 hours, 5 hours, 7 hours in the test bath: B
일반수건(샘플 7,8)보다 흡수량이 1.5배 정도 향상됨을 알 수 있다.It can be seen that the absorption is 1.5 times higher than the general towel (Sample 7,8).
Claims (2)