KR920000134B1 - Cosmetic soap composition with polyethyleneoxide polymer - Google Patents
Cosmetic soap composition with polyethyleneoxide polymer Download PDFInfo
- Publication number
- KR920000134B1 KR920000134B1 KR1019890019026A KR890019026A KR920000134B1 KR 920000134 B1 KR920000134 B1 KR 920000134B1 KR 1019890019026 A KR1019890019026 A KR 1019890019026A KR 890019026 A KR890019026 A KR 890019026A KR 920000134 B1 KR920000134 B1 KR 920000134B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- soap
- molecular weight
- polyethylene glycol
- high molecular
- Prior art date
Abstract
Description
본 발명은 고분자량의 폴리에틸렌옥사이드가 첨가된 화장비누 조성물에 관한 것이며, 보다 상세하게는 첨가된 고분자량의 폴리에틸렌옥사이드의 용해성을 개선시킨 화장비누 조성물에 관한 것이다.The present invention relates to a cosmetic soap composition to which a high molecular weight polyethylene oxide is added, and more particularly, to a cosmetic soap composition having improved solubility of the added high molecular weight polyethylene oxide.
화장비누의 바람직한 특성은 거품의 감촉이 좋아야 하고, 비누 사용시의 감촉이 매끄러워야 하며, 물에 잘 부풀지 않아야 하고, 또한 사용후에는 피부가 당기지 않고 피부의 감촉이 부드러워야 한다. 화장비누에서 이러한 바람직한 특성을 나타내기 위하여 비누제조업자들은 고분자량의 폴리에틸렌옥사이드를 비누에 첨가하여 왔는 바, 고분자량의 폴리에틸렌옥사이드를 건조분말상태 그대로 비누소지와 함께 혼용기에서 혼합한 후, 향 및 기타 첨가제를 첨가하여 성형하고 압출형타하여 비누를 제조하였다.Desirable characteristics of the cosmetic soap should be a good feeling of foam, a smooth feeling when using soap, not swelling well in water, and after use, the skin should be soft and not soft. Soap makers have added high molecular weight polyethylene oxide to soap in order to exhibit such desirable properties in cosmetic soap. After mixing high molecular weight polyethylene oxide with dry soap, mixed in soap, The soap was produced by molding by addition of other additives and by extrusion molding.
그러나, 이러한 방법으로 제조된 비누는 비누속에서 폴리에틸렌옥사이드가 서로 응집되어 반점으로 나타나게 되며 이로 인해 비누표면이 거칠어지게 되며 사용할 때 비누감촉이 나빠지는 문제점이 있었다. 이는 비누속에서 분말상태의 폴리에틸렌옥사이드가 비누내의 수분을 흡수하여 가공하는 과정에서 서로 결합하기 때문인 것으로 설명될 수 있다.However, the soap prepared by this method has a problem that the polyethylene oxide is agglomerated in each other in the soap and appear as spots, resulting in a rough surface of the soap and deteriorated soap texture when used. This may be explained by the fact that the powdered polyethylene oxide in the soap binds to each other in the process of absorbing and processing the water in the soap.
고분자량의 폴리에틸렌옥사이드를 화장비누에 첨가할 때 나타나는 이러한 문제점들을 해결하기 위하여, 미합중국특허 제4,148,743호와 제4,169,067호 및 제4,582,628호에서는 고분자량의 폴리에틸렌옥사이드를 먼저 물이나 지방산 혹은 미네랄오일과 같은 성분과 혼용기에서 혼합한 다음에, 이를 비누제조시에 사용하는 방법들이 제시되어 있다. 그러나, 이러한 방법들은, 혼용기를 사용하지 않고 향료 및 색상용액을 비누성형기에 연속적으로 첨가하여 비누를 제조하는 연속식 공정에는 적용하기 어려웠다. 또한 고분자량의 폴리에틸렌옥사이드를 건조분말상태 그대로 연속식 공정의 비누성형기에 투여하게 되면 폴리에틸렌옥사이드가 서로 응집되어 비누표면에 반점이 나타나게 되는 문제점이 있었다.In order to solve these problems when adding high molecular weight polyethylene oxide to cosmetic soap, U.S. Pat. Methods for mixing with and in a mixing vessel and then using them in soap production are presented. However, these methods have been difficult to apply to the continuous process of preparing soap by continuously adding perfume and color solution to the soap molding machine without using a mixing machine. In addition, when the high molecular weight polyethylene oxide is administered in a soap molding machine of a continuous process as it is dry powder, polyethylene oxide is agglomerated with each other, there is a problem that spots appear on the soap surface.
이에 본 발명자들은 상기 연속식 비누제조 공정을 적용하며 비누를 제조하면서도 고분자량의 폴리에틸렌옥사이드가 비누내에서 응집되지 않도록 첨가시킬 수 있는 방법을 개발하고자 예의 연구한 결과, 특정성분을 특정비율로 함유하는 향료용액에 고분자량의 폴리에틸렌옥사이드를 첨가용해시키게 되면 상기 목적을 달성할 수 있음을 알게 되어 본 발명을 완성하였다.Accordingly, the present inventors have studied intensively to develop a method for applying the continuous soap manufacturing process and adding a high molecular weight polyethylene oxide so as not to aggregate in the soap while preparing the soap. When the high molecular weight polyethylene oxide was dissolved in the fragrance solution, it was found that the above object can be achieved.
즉, 본 발명의 목적은 연속식 비누제조공정을 적용하여 고분자량의 폴리에틸렌옥사이드가 첨가된 화장비누를 제조할 때 고분자량의 폴리에틸렌옥사이드가 비누내에서 응집되지 않도록 하여 비누에 반점이 나타나지 않고, 사용감이 매끄러우면서 사용후의 촉감이 부드러운 고분자량의 폴리에틸렌옥사이드가 첨가된 화장비누 조성물을 제공하는데 있다.That is, an object of the present invention is to apply a continuous soap manufacturing process to produce a cosmetic soap to which a high molecular weight polyethylene oxide is added to prevent the high molecular weight polyethylene oxide from agglomerating in the soap does not appear spots in the soap, feeling The present invention provides a cosmetic soap composition to which a high molecular weight polyethylene oxide is added.
이하 본 발명을 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail.
본 발명은, 화장비누 조성물에 있어서, 0.1 내지 2.0중량%의 고분자량의 폴리에틸렌옥사이드를 향료와 0.1 내지 1.5중량%의 폴리에틸렌글리콜, 0.2 내지 2.0중량%의 에틸렌옥사이드가 부가된 비이온성 계면활성제 및 0.3 내지 1.5중량%의 아실글루타메이트 알카리염으로 이루어진 용액에 용해시킨 것임을 특징으로 하는 고분자량의 폴리에틸렌옥사이드가 첨가된 화장비누 조성물이다.The present invention relates to a cosmetic soap composition comprising 0.1 to 2.0% by weight of a high molecular weight polyethylene oxide, 0.1 to 1.5% by weight of polyethylene glycol, 0.2 to 2.0% by weight of a nonionic surfactant and 0.3 To 1.5 wt% acyl glutamate alkaline salt is dissolved in a solution comprising a high molecular weight polyethylene oxide, characterized in that dissolved in a solution.
이와 같은 본 발명을 더욱 상세히 설명하면 다음과 같다.Referring to the present invention in more detail as follows.
본 발명에 있어서 고분자량의 폴리에틸렌옥사이드는 비누제조시에 일반적으로 사용되는 것을 사용하는 바, -O-CH2-CH2-의 반복 단위를 갖는 분말상의 비이온성 수용성 중합체이며 분자량이 100,000 내지 5,000,000인 것이 바람직하며, 더욱 바람직하게로는 1,000,000 이하, 특히 300,000 내지 400,000인 폴리에틸렌옥사이드를 사용한다.In the present invention, the high molecular weight polyethylene oxide is generally used in soap production, and is a powdery nonionic water-soluble polymer having a repeating unit of -O-CH 2 -CH 2 -and has a molecular weight of 100,000 to 5,000,000. Preference is given to using polyethylene oxide which is more preferably 1,000,000 or less, in particular 300,000 to 400,000.
이러한 고분자량의 폴리에틸렌옥사이드는 이들이 갖고 있는 비누 사용시에 감촉을 매끄럽게 하고 사용후 피부를 부드럽게 하는 효과를 나타내기 위하여서는 일반적으로 전체 비누 조성물중에 0.1중량% 이상 사용하여야 하므로, 본 발명에 있어서도 고분자량의 폴리에틸렌옥사이드를 0.1중량% 이상 사용하며, 또한 고분자량의 폴리에틸렌옥사이드를 전체 조성물중에 2.0중량%를 초과하여 함유시키는 경우에는 본 발명에 의해 제공된 조성물에 의해서도 완전히 용해되지 않아 비누로 제조된 후에 반점을 발생시키게 되므로, 본 발명에 있어서 고분자량의 폴리에틸렌옥사이드는 2.0중량% 이하로 사용한다. 따라서, 본 발명에서 고분자량의 폴리에틸렌옥사이드는 전체 조성물중에 0.1 내지 2.0중량% 함유시키는 것이 좋다.Such high molecular weight polyethylene oxide generally has to be used in an amount of 0.1% by weight or more in the entire soap composition in order to smooth the texture and to soften the skin after use. When 0.1% by weight or more of polyethylene oxide is used, and when a high molecular weight polyethylene oxide is contained in the total composition by more than 2.0% by weight, it is not completely dissolved even by the composition provided by the present invention, so that spots are generated after being made of soap. In the present invention, the high molecular weight polyethylene oxide is used at 2.0% by weight or less. Therefore, the high molecular weight polyethylene oxide in the present invention is preferably contained in 0.1 to 2.0% by weight in the total composition.
상기와 같은 고분자량의 폴리에틸렌옥사이드는, 적당량의 향료와 0.1 내지 1.5중량%의 폴리에틸렌글리콜, 0.1 내지 2.0중량%의 에틸렌옥사이드가 부가된 비이온성 계면활성제 및 0.3 내지 1.5중량%의 아실글루타메이트 알카리 염으로 이루어진 용액에 용해된다.The above high molecular weight polyethylene oxide is a suitable amount of perfume and 0.1 to 1.5% by weight of polyethylene glycol, 0.1 to 2.0% by weight of nonionic surfactant added and 0.3 to 1.5% by weight of acyl glutamate alkaline salt. Dissolved in a solution.
상기 조성의 용액에 고분자량의 폴리에틸렌옥사이드가 어떤 이유로 용해될 수 있는지는 명확하지 않으나, 상기 조성에서 한 성분이라도 빠지거나 모자르거나 과하여도 고분자량의 폴리에틸렌옥사이드가 용해되지 않는다.It is not clear why the high molecular weight polyethylene oxide can be dissolved in the solution of the composition, but the high molecular weight polyethylene oxide is not dissolved even if one component is omitted, missing or excessive in the composition.
본 발명에 따른 상기 조성에 있어서, 향료는 화장비누에 통상적으로 사용되는 것을 통상의 양으로 함유시킨다.In the above composition according to the present invention, the fragrance contains a conventional amount commonly used in cosmetic soap.
본 발명에 있어서, 폴리에틸렌글리콜은 분자량이 200 내지 1,000인 것을 사용하는 것이 바람직하며, 더욱 바람직하게는 300 내지 600의 분자량을 갖는 것을 사용한다. 이러한 폴리에틸렌글리콜은 본 발명의 전체조성물중에 0.1 내지 1.5중량% 사용하는 바, 0.1중량% 미만으로 사용하면 고분자량의 폴리에틸렌옥사이드를 용해시킬 수 없고 1.5중량%보다 많이 사용하면 비누의 경도가 낮아져 비누의 제조가 어렵게 된다.In this invention, it is preferable to use the polyethyleneglycol whose molecular weight is 200-1,000, More preferably, the thing which has the molecular weight of 300-600 is used. The polyethylene glycol is used in 0.1 to 1.5% by weight of the total composition of the present invention, when used in less than 0.1% by weight can not dissolve high molecular weight polyethylene oxide, when used more than 1.5% by weight of the soap is lowered Manufacturing becomes difficult.
본 발명에 있어서, 에틸렌옥사이드가 부가된 비이온성 계면활성제로는 폴리에틸렌글리콜 알킬페닐에테르 및 폴리에틸렌글리콜 라놀린알코올 중에서 1종 또는 2종 이상을 선택하여 사용하는 것이 바람직하다. 이때, 상기 폴리에틸렌글리콜 알킬페닐에테르는 그의 알킬기가 탄소원자가 8 내지 12인 것이 더욱 바람직하며, 그의 에틸렌옥사이드의 부가몰수는 2 내지 16인 것이 바람직하고, 상기 폴리에틸렌글리콜 라놀린알코올은 그의 에틸렌옥사이드의 부가몰수가 15 내지 120인 것이 바람직하다. 이러한 에틸렌옥사이드가 부가된 비이온성 계면활성제는 본 발명의 전체 조성물중에 0.1 내지 2.0중량% 사용하는 바, 0.1중량% 미만으로 사용할 경우 고분자량의 폴리에틸렌옥사이드를 용해시킬 수 없고, 2.0중량%보다 많이 사용하게 되면 사용할 때 비누가 부풀고 경도가 낮아져 비누제조가 어렵게 된다.In the present invention, as the nonionic surfactant added with ethylene oxide, it is preferable to use one or two or more selected from polyethylene glycol alkylphenyl ether and polyethylene glycol lanolin alcohol. In this case, the polyethylene glycol alkylphenyl ether is more preferably an alkyl group of 8 to 12 carbon atoms, the number of added moles of ethylene oxide is preferably 2 to 16, the polyethylene glycol lanolin alcohol is added mole number of its ethylene oxide. Is preferably from 15 to 120. The nonionic surfactant added with ethylene oxide is used in 0.1 to 2.0% by weight of the total composition of the present invention. When used in less than 0.1% by weight, the polyethylene oxide of high molecular weight cannot be dissolved, and more than 2.0% by weight is used. If you do so, the soap swells and the hardness becomes low, making it difficult to manufacture soap.
본 발명에 있어서 아실글루타메이트 알카리염으로는 다음의 일반식(I)로 표시되는 것을 사용하는 것이 바람직하다.In this invention, it is preferable to use what is represented by following General formula (I) as an acyl glutamate alkaline salt.
여기서, R은 탄소원자수가 10 내지 20인 지방산으로부터 유도된 것이고, M은 나트륨 또는 트리에탄올아민이며, x는 1 또는 2이다.Wherein R is derived from fatty acids having 10 to 20 carbon atoms, M is sodium or triethanolamine, and x is 1 or 2.
이들 아실글루타메이트 알카리염은 본 발명에서 15중량%의 수용액으로 만들어 사용한다. 이러한 아실글루타메이트는 본 발명의 전체 조성물중에 0.3 내지 1.5중량% 사용하는 바, 0.3중량% 미만으로 사용하면 고분자량의 폴리에틸렌옥사이드를 용해시킬 수 없고, 1.5중량% 보다 많이 사용하면 사용할 때 비누가 부풀어 흘러내리게 된다.These acyl glutamate alkaline salts are used in the present invention as 15% by weight aqueous solution. When the acyl glutamate is used in the total composition of the present invention 0.3 to 1.5% by weight, less than 0.3% by weight can not dissolve high molecular weight polyethylene oxide, when used more than 1.5% by weight soap swells when used Get off.
본 발명의 조성물에는, 상기 이외의 성분으로서 비누소지를 포함하는 바, 화장비누에 통상적으로 사용되는 비누소지로서 탄소원자수가 10 내지 20인 지방산의 알카리염을 사용한다. 여기서 지방산은 야자유, 팜유, 대두유, 피마자유, 올리브유, 팜핵유 등의 식물유와 우지, 돈지, 양지, 어유 등의 동물유지로부터 얻어지고, 알칼리금속염은 가성소다나 가성카리를 단독 또는 혼합하여 사용한다.In the composition of the present invention, bar soap bases are included as components other than the above, and alkali salts of fatty acids having 10 to 20 carbon atoms are used as bar soap bases commonly used in cosmetic soaps. Here, fatty acids are obtained from vegetable oils such as palm oil, palm oil, soybean oil, castor oil, olive oil, palm kernel oil, and animal fats and oils such as tallow, pork, sunny and fish oils. .
그밖에도 본 발명의 조성물에는 본 발명의 효과를 떨어뜨리지 않는 범위내에서 살균제, 방부제, 피부보호제 등과 같은 기타 첨가제가 사용될 수 있다.In addition, other additives such as fungicides, preservatives, skin protectants and the like may be used in the composition of the present invention without departing from the effects of the present invention.
이상에서 설명한 바와 같은 본 발명에 따른 고분자량의 폴리에틸렌옥사이드가 첨가된 화장비누 조성물은, 먼저 향료에다 0.1 내지 1.5중량%의 폴리에틸렌글리콜과 0.1 내지 2.0중량%의 에틸렌옥사이드가 부가된 비이온 계면활성제 및 0.3 내지 1.5중량%의 아실글루타메이트 알카리염을 혼합하고, 여기에 0.1 내지 2.0중량%의 고분자량의 폴리에틸렌옥사이드를 완전히 용해시켜서, 이를 연속식 비누제조공정에 적용시키면 된다.As described above, the cosmetic soap composition to which the high molecular weight polyethylene oxide is added according to the present invention is a non-ionic surfactant to which 0.1-1.5% by weight of polyethylene glycol and 0.1-2.0% by weight of ethylene oxide are added to the fragrance. What is necessary is just to mix 0.3-1.5 weight% of acyl glutamate alkali salts, and 0.1-2.0 weight% of high molecular weight polyethylene oxide is melt | dissolved here, and apply it to a continuous soap manufacturing process.
이러한 본 발명에 따르면, 제조된 비누에 반점이 생기지 않음은 물론 비누의 감촉이 매끄럽고 비누 사용후의 피부감촉이 부드러우며 비누 사용시 비누가 부풀지 않고 수분도 덜 흡수하며, 비누의 소성이 증대되어 제조시 작업성이 개선되는 효과가 있다.According to the present invention, not only does not produce spots on the soap, as well as the smooth texture of the soap and soft skin texture after using the soap, the soap does not swell and absorbs less moisture when using soap, the plasticity of the soap is increased Workability is improved.
이하 본 발명을 실시예에 의거하여 보다 구체적으로 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail with reference to Examples.
[실시예 1]Example 1
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 96.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance and 0.2% by weight high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.5% by weight polyethylene glycol lanolin alcohol (additional molar number 75) and After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, the solution and 96.9 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 2]Example 2
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 12) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 96.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.5 wt% polyethylene glycol nonylphenyl ether (additional mole number 12) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and this solution and 96.9% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 1]Comparative Example 1
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000) 및 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400)을 잘 혼합용해시킨 후, 이 용액과 97.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.After dissolving 1.4% by weight of fragrance, 0.2% by weight of high molecular weight polyethylene oxide (Polyox WSRN 3000) and 0.5% by weight of polyethylene glycol (PEG 400; average molecular weight 400), the solution and 97.9% by weight of soap The base was put in a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 2]Comparative Example 2
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000) 및 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75)을 잘 혼합용해시킨 후, 이 용액과 97.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.After dissolving 1.4% by weight of fragrance, 0.2% by weight of high molecular weight polyethylene oxide (Polyox WSRN 3000) and 0.5% by weight of polyethylene glycol lanolin alcohol (additional molar number 75), the solution and 97.9% by weight of soap Was added to a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 3]Comparative Example 3
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000) 및 0.5중량%의 폴리에틸렌글리콜노닐페닐 에테르(부가몰수 12)를 잘 혼합용해시킨 후, 이 용액과 97.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.After dissolving 1.4% by weight of fragrance, 0.2% by weight of high molecular weight polyethylene oxide (Polyox WSRN 3000) and 0.5% by weight of polyethylene glycol nonylphenyl ether (additional mole number 12), the solution and 97.9% by weight of soap The base was put in a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 4][Comparative Example 4]
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.After mixing 1.4% by weight of fragrance, 0.2% by weight of high molecular weight polyethylene oxide (Polyox WSRN 3000) and 0.5% by weight of cocoylglutamate monosodium salt (15%), the solution and 97.9% by weight of soap The base was put in a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 5][Comparative Example 5]
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 weight% fragrance, 0.2 weight% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 weight% polyethylene glycol (PEG 400; average molecular weight 400) and 0.5 weight% cocoylglutamate monosodium salt (15%) After mixing and dissolving well, this solution and 97.4% by weight of soap were put in a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 6]Comparative Example 6
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400) 및 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75)을 잘 혼합용해시킨 후, 이 용액과 97.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400) and 0.5 wt% polyethylene glycol lanolin alcohol (additional molar number 75) After mixing and dissolving well, this solution and 97.4% by weight of soap were put in a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 7]Comparative Example 7
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜 노닐페닐에테르(부가몰수 12) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 weight% fragrance, 0.2 weight% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 weight% polyethylene glycol nonylphenyl ether (additional mole number 12) and 0.5 weight% cocoylglutamate monosodium salt (15%) After mixing and dissolving well, this solution and 97.4% by weight of soap were put in a continuous soap molding machine to prepare a cosmetic soap composition.
이렇게 하여 제조된 상기 실시예 1, 2 및 비교예 1 내지 7의 화장비누 조성물에서 고분자량의 폴리에틸렌옥사이드의 용해성을 조사하여, 그 결과를 다음의 표 I에 나타내었다.The solubility of high molecular weight polyethylene oxide was investigated in the cosmetic soap compositions of Examples 1 and 2 and Comparative Examples 1 to 7 thus prepared, and the results are shown in Table I below.
[표 I]TABLE I
상기 표 I에 나타낸 바와 같이, 고분자량의 폴리에틸렌옥사이드를 용해시킬 때 비교예 1 내지 7에서와 같이 본 발명의 조성물중 한성분이라도 사용하지 않았을 경우에는 비누에 반점이 발생되는 바람직하지 못한 결과를 나타내나, 실시예 1, 2와 같이 고분자량의 폴리에틸렌옥사이드를 본 발명의 특징적인 조성을 갖는 향료용액에 완전히 용해시켜서 비누를 제조할 경우 제조된 비누에 반점이 생기지 않고 사용감이 매끄럽게 된다. 그러므로, 본 발명에 따르면 연속식 비누제조공정에 의해서도 고분자량의 폴리에틸렌옥사이드를 첨가시킬 수 있음을 알 수 있다.As shown in Table I, when dissolving a high molecular weight polyethylene oxide, as shown in Comparative Examples 1 to 7, even if one component of the composition of the present invention is not used, there is an undesirable result of spots on the soap. B. When soaps are prepared by completely dissolving high molecular weight polyethylene oxide in the perfume solution having the characteristic composition of the present invention as in Examples 1 and 2, the soaps produced are smooth without any spots. Therefore, according to the present invention, it can be seen that a high molecular weight polyethylene oxide can be added even by a continuous soap manufacturing process.
[실시예 3]Example 3
1.4중량%의 향료와 0.1중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.3중량%의 폴리에틸렌글리콜 노닐페닐에테르(부가몰수 9) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.2중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.1 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.3 wt% polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and then the solution and 97.2% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 4]Example 4
1.4중량%의 향료와 1.0중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.3중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 30) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 96.3중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 weight percent fragrance, 1.0 weight percent high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 weight percent polyethylene glycol (PEG 400; average molecular weight 400), 0.3 weight percent polyethylene glycol lanolin alcohol (additional molar number 30), After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 96.3 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 5]Example 5
1.4중량%의 향료와 2.0중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.3중량%의 폴리에틸렌글리콜 노닐페닐에테르(부가몰수 9) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 95.3중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 2.0 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.3 wt% polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and this solution and 95.3% by weight of soap were placed in a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 8]Comparative Example 8
1.4중량%의 향료와 0.05중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.3중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 30) 및 0.5중량%의 코코일글루타메이트모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.25중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance, 0.05% by weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.3% by weight polyethylene glycol lanolin alcohol (additional mole number 30) and After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 97.25 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 9]Comparative Example 9
1.4중량%의 향료와 2.5중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.3중량%의 폴리에틸렌글리콜 노닐페닐에테르(부가몰수 9) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 94.8중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 2.5 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.3 wt% polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and this solution and 94.8% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
이렇게 하여 제조된 상기 실시예 3 내지 5 및 비교예 8, 9의 화장비누 조성물에서 고분자량의 폴리에틸렌옥사이드의 용해성과 비누소지를 제외한 나머지 성분, 즉 본 발명의 특징적인 성분으로 된 향료용액의 점도 및 비누의 사용감을 조사하여 그 결과를 다음의 표 II에 나타내었다.In the cosmetic soap compositions of Examples 3 to 5 and Comparative Examples 8 and 9 thus prepared, the viscosity of the fragrance solution as the remaining components, ie, the characteristic components of the present invention, except for the solubility and high molecular weight of polyethylene oxide The use of soap was investigated and the results are shown in Table II below.
[표 II]TABLE II
상기 표 II에 나타낸 바와 같이 고분자량의 폴리에틸렌옥사이드의 사용량이 0.1중량% 미만일 경우 비누의 사용감에 효과를 나타내지 않으며 2.0중량%가 초과되면 비누소지를 제외한 본 발명의 특정성분을 함유하는 향료용액의 점도가 매우 높아 첨가하기가 어려울 뿐만 아니라 고분자량의 폴리에틸렌옥사이드가 완전히 용해되지 않아 제조된 비누에서 반점이 발생되는 바람직하지 못한 결과를 나타낸다. 또한 고분자량의 폴리에틸렌옥사이드를 2.0중량% 보다 많이 사용하여 완전히 용해시키기 위해서는 본 발명의 조성물 성분의 사용량을 증가시켜야 되므로 결국 비누경도가 저하되는 결과를 나타내므로 본 발명에서의 폴리에틸렌옥사이드의 사용량은 0.1 내지 2.0중량%가 가장 바람직함을 알 수 있다.As shown in Table II, when the amount of the high molecular weight polyethylene oxide is less than 0.1% by weight, it does not show an effect on the feeling of soap, and when the amount exceeds 2.0% by weight, the viscosity of the fragrance solution containing the specific component of the present invention except for soap Is very high and difficult to add, and the high molecular weight polyethylene oxide is not completely dissolved, resulting in spots in the soap produced. In addition, in order to completely dissolve the high molecular weight polyethylene oxide using more than 2.0% by weight, the amount of the composition component of the present invention must be increased, and thus the hardness of the soap is reduced. It can be seen that 2.0% by weight is most preferred.
[실시예 6]Example 6
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.1중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.3중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance, 0.2% by weight of high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight of polyethylene glycol (PEG 400; average molecular weight 400), 0.1% by weight of polyethylene glycol lanolin alcohol (additional mole number 75) and After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 97.3 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 7]Example 7
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.2중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 12) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.2중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance, 0.2% by weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.2% by weight polyethylene glycol nonylphenyl ether (additional mole number 12) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and then the solution and 97.2% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 8]Example 8
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 1.0중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 96.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 weight percent fragrance, 0.2 weight percent high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 weight percent polyethylene glycol (PEG 400; average molecular weight 400), 1.0 weight percent polyethylene glycol lanolin alcohol (additional molar number 75), After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 96.4 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 9]Example 9
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 2.0중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 12) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 95.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 weight% fragrance, 0.2 weight% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 weight% polyethylene glycol (PEG 400; average molecular weight 400), 2.0 weight% polyethylene glycol nonylphenyl ether (addition mole number 12) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and then the solution and 95.4% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 10]Comparative Example 10
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.05중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.35중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance, 0.2% by weight high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.05% by weight polyethylene glycol lanolin alcohol (additional molar number 75) and After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 97.35 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 11]Comparative Example 11
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 2.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 75) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 94.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance and 0.2% by weight high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 2.5% by weight polyethylene glycol lanolin alcohol (additional molar number 75) and After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, the solution and 94.9 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
이렇게 하여 제조된 상기 실시예 6 내지 9 및 비교예 10, 11의 화장비누 조성물에서 고분자량의 폴리에틸렌옥사이드의 용해성과 비누의 경도를 조사하여 그 결과를 다음의 표 III에 나타내었다.The solubility of high molecular weight polyethylene oxide and the hardness of soap were investigated in the cosmetic soap compositions of Examples 6 to 9 and Comparative Examples 10 and 11 thus prepared, and the results are shown in Table III below.
[표 III]TABLE III
상기 표 III에 나타낸 바와 같이, 에틸렌옥사이드가 부가된 비이온성 계면활성제의 사용량이 0.1중량% 미만일 경우 폴리에틸렌옥사이드가 용해되지 않으며, 2.0중량%를 초과할 경우 사용량이 많아 비누가 물러져 비누의 제조가 어려움을 알 수 있다. 그러므로 본 발명에서 에틸렌옥사이드가 부가된 비이온성 계면활성제는 0.1 내지 2.0중량% 사용하는 것이 바람직하다.As shown in Table III, when the amount of the non-ionic surfactant to which ethylene oxide is added is less than 0.1% by weight, polyethylene oxide is not dissolved. I can see the difficulty. Therefore, in the present invention, it is preferable to use 0.1 to 2.0% by weight of the nonionic surfactant added with ethylene oxide.
[실시예 10]Example 10
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.1중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 9) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.3중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.1 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.5 wt% polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and this solution and 97.3% by weight of soap were placed in a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 11]Example 11
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 1.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 30) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 95.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 1.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.5 wt% polyethylene glycol lanolin alcohol (additional molar number 30) and After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 95.9 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 12]Example 12
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 9) 및 0.3중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.1중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.5 wt% polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.3% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and then the solution and 97.1% by weight of soap were placed in a continuous soap molding machine to prepare a cosmetic soap composition.
[실시예 13]Example 13
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 30) 및 1.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 95.9중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance and 0.2% by weight high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.5% by weight polyethylene glycol lanolin alcohol (additional molar number 30) and After dissolving 1.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 95.9 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 12]Comparative Example 12
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.05중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 9) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.35중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance, 0.2% by weight polyethylene oxide (Polyox WSRN 3000), 0.05% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.5% by weight polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.5% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and then the solution and 97.35% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 13]Comparative Example 13
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 2.0중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 30) 및 0.5중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 95.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 2.0 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.5 wt% polyethylene glycol lanolin alcohol (additional molar number 30), After dissolving 0.5 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 95.4 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 14]Comparative Example 14
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜노닐페닐에테르(부가몰수 9) 및 0.1중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 97.3중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4 wt% fragrance, 0.2 wt% high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5 wt% polyethylene glycol (PEG 400; average molecular weight 400), 0.5 wt% polyethylene glycol nonylphenyl ether (additional mole number 9) And 0.1% by weight of cocoyl glutamate monosodium salt (15%) were mixed and dissolved well, and then the solution and 97.3% by weight of soap were put into a continuous soap molding machine to prepare a cosmetic soap composition.
[비교예 15]Comparative Example 15
1.4중량%의 향료와 0.2중량%의 고분자량의 폴리에틸렌옥사이드(Polyox WSRN 3000), 0.5중량%의 폴리에틸렌글리콜(PEG 400; 평균분자량 400), 0.5중량%의 폴리에틸렌글리콜 라놀린알콜(부가몰수 30) 및 2.0중량%의 코코일글루타메이트 모노소듐염(15%)을 잘 혼합용해시킨 후, 이 용액과 95.4중량%의 비누소지를 연속식 비누성형기에 투입하여 화장비누 조성물을 제조하였다.1.4% by weight fragrance and 0.2% by weight high molecular weight polyethylene oxide (Polyox WSRN 3000), 0.5% by weight polyethylene glycol (PEG 400; average molecular weight 400), 0.5% by weight polyethylene glycol lanolin alcohol (additional molar number 30) and After dissolving 2.0 wt% of cocoyl glutamate monosodium salt (15%) well, this solution and 95.4 wt% of soap were poured into a continuous soap molding machine to prepare a cosmetic soap composition.
이렇게 하여 제조된 상기 실시예 10 내지 13 및 비교예 12 내지 15의 화장비누 조성물에서 고분자량의 폴리에틸렌옥사이드의 용해성과 비누의 경도를 조사하여 그 결과를 다음의 표 IV에 나타내었다.The solubility of high molecular weight polyethylene oxide and the hardness of soap were investigated in the cosmetic soap compositions of Examples 10 to 13 and Comparative Examples 12 to 15 thus prepared, and the results are shown in Table IV below.
[표 IV]TABLE IV
상기 표 IV에 나타낸 바와 같이 폴리에틸렌글리콜의 사용량이 0.1중량% 미만일 경우 고분자량의 폴리에틸렌옥사이드가 용해되지 않으며, 아실글루타메이트 알카리염도 마찬가지로 0.3중량% 미만일 경우에는 고분자량의 폴리에틸렌옥사이드가 용해되지 않았다. 또한 폴리에틸렌글리콜이나 아실글루타메이트 알카리염의 사용량이 각각 1.5중량%를 초과한 경우에는 제조된 비누가 무르고 작업하기가 어려워졌다. 그러므로 본 발명에서의 폴리에틸렌글리콜의 사용량은 0.1 내지 1.5중량%의 바람직하며 아실글루타메이트 알카리염은 0.3 내지 1.5중량% 사용하는 것이 바람직함을 알 수가 있다.As shown in Table IV, when the amount of polyethylene glycol used is less than 0.1% by weight, high molecular weight polyethylene oxide is not dissolved, and when acyl glutamate alkaline salt is less than 0.3% by weight, high molecular weight polyethylene oxide is not dissolved. In addition, when the amount of polyethylene glycol or acyl glutamate alkaline salt exceeded 1.5% by weight, respectively, the soap produced was soft and difficult to work. Therefore, it is understood that the amount of polyethylene glycol used in the present invention is preferably 0.1 to 1.5% by weight, and the acyl glutamate alkaline salt is preferably used in an amount of 0.3 to 1.5% by weight.
Claims (3)