건축용 축광바닥제의 제조방법Manufacturing method of building photoluminescent floor
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
제1도는 본 발명의 사시도. 제2도는 제1도의 (가)부분 확대 단면도.1 is a perspective view of the present invention. 2 is a partially enlarged cross-sectional view of FIG.
Claims (3)
표면강화층(1), 인쇄층(2), 축광층(3), 특수시트(4)의 다층구조의 바닥재료들은 가열, 가압, 냉각을 동시에 행할 수 있는 대형 금형 사이에 적층한 후 170~200℃의 온도로 20~30분 가열하면서 대형 유압 실린더를 이용하여 80~100㎏/㎤의 압력으로 가압하고 가열이 끝나면 지하수를 이용하여 상기 압력을 유지하면서 강제순환 방식으로 상온이 될때까지 냉각하여 제조하는 건축용 축광바닥제 제조방법.Floor materials of the multi-layer structure of the surface reinforcement layer (1), the printing layer (2), the photoluminescent layer (3), and the special sheet (4) are laminated between large molds capable of heating, pressing, and cooling at the same time. Pressurized at a pressure of 80-100 kg / cm3 using a large hydraulic cylinder while heating at a temperature of 200 ° C. for 20-30 minutes, and after heating, it is cooled until it reaches room temperature by forced circulation while maintaining the pressure using ground water. Method for manufacturing a photoluminescent floor for construction.제1항에 있어서 축광층(3)은, 염화비닐수지 100을 기준으로 가소제 50부, 축광안료 50부를 혼입하여 카렌다공법으로 제조한 것을 특징으로 하는 건축용 축광바닥제 제조방법.The method of manufacturing a photoluminescent floor according to claim 1, wherein the photoluminescent layer (3) is manufactured by calendering by mixing 50 parts of plasticizer and 50 parts of photoluminescent pigment based on the vinyl chloride resin 100.제1항에 있어서 축광층(3)은, 염화비닐수지 위에 그라비야용 잉크나 UMCH등의 수지 100부를 기준으로 축광안료 50부 혼입하여 그라비야공법, 롤도포공법, 다이프도포공법으로 제조한 것을 특징으로 하는 건축용 축광바닥제 제조방법.The photoluminescent layer (3) according to claim 1 is prepared by gravure, roll coating, or dip coating by mixing 50 parts of photoluminescent pigment on a vinyl chloride resin based on 100 parts of a resin such as gravure ink or UMCH. Method for manufacturing a photoluminescent floor for building, characterized in that.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019900007400A1990-05-231990-05-23
Manufacturing method of building photoluminescent floor
KR910019767A
(en)
Ultra-light insulation material composition with nonflammability and thermal resistance characteristic, apparatus for manufacturing the same, and method for manufacturing the sameby using the apparatus