KR900006346B1 - Stone wallpaper and its manufacturing method - Google Patents
Stone wallpaper and its manufacturing method Download PDFInfo
- Publication number
- KR900006346B1 KR900006346B1 KR1019870004405A KR870004405A KR900006346B1 KR 900006346 B1 KR900006346 B1 KR 900006346B1 KR 1019870004405 A KR1019870004405 A KR 1019870004405A KR 870004405 A KR870004405 A KR 870004405A KR 900006346 B1 KR900006346 B1 KR 900006346B1
- Authority
- KR
- South Korea
- Prior art keywords
- stone
- particles
- natural
- adhesive
- crushed
- Prior art date
Abstract
내용 없음.No content.
Description
제 1 도는 본 발명의 돌벽지를 예시하는 참고단면도.1 is a reference cross-sectional view illustrating a stone wall paper of the present invention.
제 2 도는 본 발명의 돌벽지의 제조공정도.2 is a manufacturing process diagram of the stone wall paper of the present invention.
제 3 도는 본 발명의 제1단계에서의 압축처리공정의 전후단계를 예시하는 참고도.3 is a reference diagram illustrating the before and after steps of the compression process in the first step of the present invention.
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 : 돌벽지 2 : 기초재1: stone wallpaper 2: base material
11 : 제 1 접착층 12 : 돌입자11: first adhesive layer 12: stone particles
13 : 자연석의 파쇄석 14 : 제 2 접착층13: crushed stone of natural stone 14: second adhesive layer
15 : 돌비늘입자15: Micascale Particles
본 발명은 입체면을 가진 벽지에 관련된 것으로서, 이는 특히 미립분말이 아니고 자유분방히 파쇄된 자연석을 주재로하여 이뤄지는 돌벽지와 이의 제조방법에 관한 것이다. 일반적으로 이 분야기술과 비교적 관련이 있는 벽지로는 광석분말이나 질석(蛭石), 섬유석, 목분등을 접착제와 혼합하여 종이등의 피부착소재에 피착처리한 것이 알려져 있다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wallpaper having a three-dimensional face, and more particularly, to a stone wallpaper and a method for manufacturing the same, which are mainly made of freely crushed natural stone. In general, wallpaper which is relatively related to the art of the art is known to be deposited on skin-adhesive materials such as paper by mixing ore powder, vermiculite, fibrous stone, and wood powder with an adhesive.
이러한 것의 일예로는 우리나라의 1966년 특허공보 제140호 공고번호 제994호에 공고된 바와 같이, 질석을 주제로한 벽지의 인용예(일예로 인용발명 1이라 한다)와, 일본국 특허공보 소50-3803호에 기재된 바와같은, 펄라이트(pealite)등을 주재로한 벽지의 인용예(일예로 인용발명 2라 한다)를 들 수 있다. 상기예의 인용발명 1은 질석을 고열로 처리하여 대두(大豆)만한 크기의 입자로한 후, 접착제 및 정전기효과에 의한 피부착 소재로의 피착처리와 고무롤러에의 압입공정 및 후처리의 접착제 도포의 공정으로 이뤄지는 것으로서, 되어 있으며, 인용발명 2는 역시 자연석(주로 펄라이트등)을 주재로 하여 이를 미립자로한 후 접착용액등과 함께 조립기(造粒機)로 소정입자(0.5-3.0mm)로 제조하고, 이를 피부착소재에 피복시킨 것으로 되어있다.As an example of this, as disclosed in Korean Patent Publication No. 140, Publication No. 994 of 1966, a citation example of wallpaper based on vermiculite (for example, citation invention 1), and Japanese Patent Publication As mentioned in 50-3803, the citation example of wallpaper based on pearlite etc. (for example, citation invention 2) is mentioned. Invention 1 of the above example treats vermiculite at a high temperature to make particles of the size of soybean, and then adheres to the skin-adhesive material by adhesive and electrostatic effects, press-fits the rubber roller, and applies the adhesive of the post-treatment. Invention 2 is also made of natural stone (mainly pearlite, etc.) as fine particles, and then granulated together with adhesive solution, etc. to predetermined particles (0.5-3.0mm). It manufactured and coat | covered it to the skin adhesion material.
이와같은 선행기술들의 예에 있어서는 하나같이 피부착소재에 피복되는 알맹이가 자연석(특정소재)을 미세분말로 하고 별도의 조립기나 소성로(橈成爐)등에서 인위적인 알맹이입자로 제조되므로 인하여, 그 알맹이의 제조과정에 따른 복잡성이 야기되면서, 이로부터 제조되는 알맹이들도 획일적인 크기와 구(球)에 가까운 입자로 되므로서, 실내벽면등에 부여되는 벽지로서의 실내장식적 효과가 천연적인 미려함등을 나타내는데는 아직도 개선되야할 문제점이 있었다.In the example of such prior art, since the kernels coated on the skin-wearing materials are made of natural grains (specific materials) as fine powders and artificial granules in separate granulators or firing furnaces, Due to the complexity of the manufacturing process, the kernels produced therefrom also become uniform particles and particles close to a sphere, so that the decorative effect as a wallpaper imparted to the interior wall surface shows a natural beauty. There was still a problem that had to be improved.
또, 상기 인용발명 1에서는 소정입자로 제조된 알갱이를 정전효과에 의해 피부착소재로부터 직립시키는공정을 수반하므로서 그 자연적인 조직배열로의 미려한 입체감을 저하시킨다.In the above-mentioned Cited Invention 1, the granules made of the predetermined particles are erected from the skin-bonding material by the electrostatic effect, thereby reducing the beautiful three-dimensional effect of the natural tissue arrangement.
또, 이들에 있어서는 천연소재를 파쇄한 것을 그대로 이용하는데는 피부착소재에 접착처리된 천연소재의 입자가 자유분방한 형태의 것으로 되고, 이로인한 최종 목적물로 되었을때의 육체적 손상이나 타물품등의 긁힘이나 손상을 가져올 우려가 있는데 대해 이를 양호하게 해소할 수 있는 상품적 가치로서의 기술적수단이 마련되어 있지 못하므로 아직도 이러한 천연소재 그대로의 벽지를 제작하는데의 어려움이 있었다.In this case, in order to use the crushed natural material as it is, the particles of the natural material adhered to the skin-coated material are in the form of freely released particles, and thus physical damage or other articles when the final object is obtained. There is a risk of causing scratches or damage, but there is still a difficulty in producing such natural wallpaper because there is no technical means as a commodity value to solve this problem well.
또, 상기와 같이 제조되는 알갱이는 그 소재가 기계적가공시 비교적 미립화되기 쉬운 소재로되며, 일단 소성된 이후에는 견고함을 유지키위한 속성을 가진 소재로 될것이 필요로 되므로서, 그 소재에 일정한 제약이 뒤따르므로 이로인한 소재선정의 융통성이 결여되는 것이었다.In addition, the granules produced as described above are made of a material that is relatively easy to be atomized during mechanical processing, and once fired, it is necessary to be a material having properties for maintaining strength, so that Constraints followed, resulting in a lack of flexibility in material selection.
또, 상기와 같이 별도의 알갱이를 제조하는 기술적수단이 마련되야 하므로서 이로인한 제공정이 증가되고, 결과적인 최종목적물의 가격을 상승시킨다.In addition, as described above, the technical means for manufacturing the granules must be prepared, thereby increasing the number of provided tablets, thereby raising the price of the final end object.
이러한 제원인들은 이들이 보편적인 자연석재의 벽지로서 상업적으로 활용되기 어려운 단점으로 될 수 있다.These specifiers may be a disadvantage that they are difficult to use commercially as a wallpaper of the natural natural stone.
또, 진실하게는 자연석재의 벽지라고 할 수도 없다. 왜냐하면, 자연석재의 벽지라하면 적어도 그 소재가 인위적 가공성의 범위를 좀더 적게 받아야만 벽지화된 상태에서의 자연미를 증가시킬 수 있으리라 기대되나, 상기와 같이 기본소재인 알갱이부터 인위적인 가공으로 이뤄지고 있는 것이므로 그 미분말의 본질이 자연석이지 그 형태적인 면에서는 천연적인 상태가 배제되어 있는 것이기 때문이다.Indeed, it is not a wallpaper of natural stone. Because the natural stone wallpaper is expected to increase the natural beauty in the wallpapered state at least if the material has to receive a smaller range of artificial workability, but since it is made from artificial grains from the basic material as described above, This is because the nature of fine powder is natural stone, but its natural state is excluded from its morphological aspect.
그러므로 이러한 선행기술에 있어서의 벽지는 좀더 천연적인 입체감과 색상 또는 질감의 면에서 그 가치가 떨어지는 것이었다. 그리고 이들에 있어서의 알갱이는 조립기로 제조되는 알갱이가 1색상의 안료치리에 의해 한꺼번에 부여되는 것이 보통이며, 그 소재 또한 미분말에 의한 1개의 그 자체본질의 자연석만이 부여되어진 것이므로서 그 색상에 있어서의 무작위적이며 복합된 색상처리의 효과를 폭넓게 기대하기도 어렵다.Thus, the wallpaper in this prior art was of less value in terms of more natural three-dimensionality and color or texture. The grains in these are usually given at one time by granules of one color, and the material is also given one natural stone of its own nature by fine powder. It is also difficult to expect a wide range of random and complex color processing effects.
본 발명은 이러한 선행기술들에 있어서의 제단점과 그 불합리점을 개선하고자 한 것이다.The present invention seeks to improve the advantages and disadvantages of these prior arts.
즉, 본 발명의 목적은 자연석을 주재로한 벽지에 있어서 그 자연석의 본질적 형태를 변화시키지 않고, 이의 천연적인 모양이 그대로 벽지에 재현되어 있으므로서 실내장식적 효과에 있어서의 인위적인 경향을 되도록 배제할 수 있음에 의해 그 천연적인 입체감이나 질감, 미려함을 양호하게 제공할 수 있도록한 것이다.That is, the object of the present invention is to exclude the artificial tendency in the interior decoration effect without changing the essential form of the natural stone in the wallpaper predominantly natural stone, while the natural shape thereof is reproduced on the wallpaper as it is. By doing so, the natural three-dimensional feeling, texture, and beauty can be provided satisfactorily.
본 발명의 또다른 목적은 자연석이 비교적 천연적형태로 재현되어 있는 돌벽지를 제조하는 방법이 간단하고 용이하면서도, 그 자연석인 소재의 본질적특질에 거의 영향을 받지않는 다양한 소재와 다양한 색상을 손쉽게 1개의 벽지에 무작위적으로 부여할 수 있음에 의해 이러한 벽지에서의 천연적인 미려함등을 좀더 양호히 개선할 수 있고 그 대량생산이 손쉽게 이뤄질 수 있도록 한 것이다.Still another object of the present invention is a simple and easy method of manufacturing a stone wall paper in which natural stones are reproduced in a relatively natural form, and easily various materials and various colors that are hardly affected by the essential properties of the natural stone material. By randomly assigning the wallpaper to the dog, the natural beauty and the like in the wallpaper can be improved better and the mass production can be easily achieved.
그외에도, 상기 천연재의 파쇄석들을 종이재등의 기초재에 피착처리하는 과정에서 쇠에 의한 균질두께롤러로 그 피층면을 균일하게 하면서 본질적인 파쇄석의 자유분방한 놓여집에 여하한 영향을 미치지 않는 자연적 입체감을 부여하게 되는 기술적수단을 제공함에 의해 이러한 물품의 상품적가치등을 양호히 부여할 수 있도록한 것이다.In addition, in the process of depositing the natural crushed stone on the base material such as paper material, the surface of the crushed stone is made uniform by the uniform thickness roller by iron, and does not affect any freely distributed sedimentation of the essential crushed stone. By providing the technical means to give a natural three-dimensional effect, it is possible to give a good product value of these goods.
이하에서 이를 상세히 설명하면 다음과 같다.This will be described in detail below.
제 1 도는 본 발명으로 제조된 돌벽지의 일실시예의 조직구조를 나타내고 있다.Figure 1 shows the structure of one embodiment of the stone wall paper produced by the present invention.
즉, 여기서는 벽면등과 접면되는 기초재(2)에 제1접착층(11) 자연석의 파쇄석(13), 제2접착층(14)외 순서로 피층되어진 것이다.That is, here, the base material 2 which is in contact with the wall surface or the like is layered in the order of the crushed stone 13 of the first adhesive layer 11 natural stone and the second adhesive layer 14.
상기 기초재(2)는 종이, 직포(織布), 편포(編布), 부직포 피혁류등으로 되어질 수 있다.The base material 2 may be made of paper, woven fabric, knitted fabric, nonwoven leather, or the like.
또, 제 1 접착층(12)은 열경화성 합성수지의 투명접착제와 돌가루입자(12)의 혼합층으로 되고, 제 2 접착층(14)은 역시 열경화성 합성수지의 투명접착재와 돌비늘입자(15)의 혼합층으로 되어진다.In addition, the first adhesive layer 12 is a mixed layer of the transparent adhesive of the thermosetting resin and the stone particles 12, the second adhesive layer 14 is also a mixed layer of the transparent adhesive of the thermosetting synthetic resin and the mica particles (15). .
또, 상기 파쇄석(13)은 어떠한 자연석으로 되어도 무관하며 이 파쇄석(13)의 크기는 (28-30)메쉬-150메쉬의 범위로 한다.The crushed stone 13 may be any natural stone, and the size of the crushed stone 13 is in the range of (28-30) mesh to 150 mesh.
한편, 제 2 도에서는 본 발명의 제조공정을 나타내는 계통도로서 이는 자연석의 파쇄석(13)을 기초재(2)에 일단 적층시키는 제 1 단계공정과, 제 1 단계공정에서 제작된 벽지의 외표층을 마무리하는 제2단계의 공정으로 나눠진다.On the other hand, Figure 2 is a schematic diagram showing the manufacturing process of the present invention, which is the first step of laminating the crushed stone 13 of the natural stone on the base material 2, and the outer surface layer of the wallpaper produced in the first step The process is divided into the second stage of finishing.
(제 1 단계)(First step)
제 1 용액의 도포처리공정(20)Coating process of the first solution (20)
기초재(2)에 제 1 용액을 도포한다. 여기서 제 1 용액은 제 1 도에서의 돌가루입자(12)와 투명접착제를 적당량 혼합한 용액이 된다.The first solution is applied to the base material 2. Here, the first solution is a solution obtained by mixing an appropriate amount of the stone powder particles 12 and the transparent adhesive agent in FIG.
경사각도로의 투석처리공정(21)Dialysis treatment process at inclination angle (21)
상기 제1용액에 의한 도포처리공정(20)이후 콘베어밸트등으로 제1도의 제1접착층(11)이 형성된 기초재(2)를 이송시킬때, 그 이송로는 지평면에서 소정각도의 경사면이 이뤄지도록 하고, 상기 경사면의 윗부분에서 파쇄된 자연석의 파쇄석(13)을 임의 위치에서 지평면에 수직으로 투석시킨다.When the base material 2 on which the first adhesive layer 11 of FIG. 1 is formed is transferred to a conveyor belt or the like after the
이때 상기 경사면은 지평면과의 각도가 60°-70°로 되고, 이에 접착밀도를 높이기 위해 경사면에 진동을 가한다.At this time, the inclined surface is an angle with the horizontal plane 60 °-70 °, thereby applying a vibration to the inclined surface to increase the adhesion density.
또, 상기 파쇄석(13)은 (28-30)메쉬-150메쉬의 범위에 있는 크기의 것으로 한다.The crushed stone 13 has a size in the range of (28-30) mesh-150 mesh.
그리고, 파쇄석(13)은 천연소재의 본질적특성에 기인한 단일 또는 복합색상의 것을 소정비율로서 복합해서 또는 단일의 색상으로 선별하여 투석할 수도 있다.In addition, the crushed stone 13 may be combined with a single or complex color due to the essential characteristics of the natural material as a predetermined ratio, or selected and separated into a single color for dialysis.
제1조 건조처리공정(22)Article 1 Drying Process (22)
상기 공정이후의 것을 소정 온도(약 100℃)에서 제1건조시킨다.The thing after the said process is 1st dried at predetermined temperature (about 100 degreeC).
제1차 브러쉬처리공정(23)1st brush processing process (23)
상기 제1건조처리공정에 의해 기초재(2)에 접착된 파쇄석(13)은 제3도와 같이 파쇄석(13)의 상호간 인접계곡등에 존재하거나 끼워져있는 파쇄석이나 투석처리공정(21)에서 약간의 접착제가 뭍혀져 굴르게 되어 붙어있는 파쇄석(13)들이 존재하므로 이들을 브러쉬로 털어낸다.The crushed stone 13 adhered to the base material 2 by the first drying treatment step is slightly present in the crushed stone or dialysis treatment process 21 existing or inserted in the adjacent valleys of the crushed stone 13 as shown in FIG. The adhesive is crushed and rolled, so that there are crushed stones (13) attached to the brushing them off.
균질두께처리공정(24)Homogeneous Thickness Treatment Process (24)
제1차 브러쉬처리공정(23)이후 이를 소망하는 두께의 돌벽지(1)로 하기 위해 쇠로된 상,하롤러에 의해 균질두께의 돌벽지(1)로 한다. 이때는 제3도와 같이 소정두께가 a로 된다고 가정하면 상,하롤러는 그 범위로 회전되고 있으므로 종이일지모를 기초재(2)와 파쇄석(13)의 수직길이로 a를 벗어난 파쇄석(13)의 날카로운 부분등이 부서지고 결과적으로는 그 두께 a의 균질면을 유지하게 된다.After the 1st brush processing process 23, in order to make it into the stone wall paper 1 of desired thickness, it is made into the stone wall paper 1 of homogeneous thickness by the steel up and down roller. In this case, assuming that the predetermined thickness becomes a as shown in FIG. 3, since the upper and lower rollers are rotated in the range, the crushed stone 13 deviating from a by the vertical length of the base material 2 and the crushed stone 13 may be paper. The sharp edges of are broken and consequently maintain a homogeneous surface of thickness a.
이때는 상,하롤러의 이격거리를 조절하므로서 돌벽지(1)의 두께가 조절될 수 있고, 기초재(2)는 쇠로된 일방롤러와 면접촉되어 있어 균질두께처리시의 파쇄석자체에 가해지는 압력에 의하여 그 기초재(2)의 손상을 입히지 않는다.At this time, the thickness of the stone wall paper 1 can be adjusted by adjusting the separation distance of the upper and lower rollers, and the base material 2 is in surface contact with the one-rolled roller, which is applied to the crushed stone itself during the homogeneous thickness treatment. Pressure does not damage the base material 2.
2차 브러쉬처리공정Second Brush Process
상기 공정이후의 것은 상,하롤러에 의해 균질두께가 유지되는 과정에서 두께 a를 벗어난 범위의 파쇄석(13)의 날카로운 부분의 깨짐에 의해 파쇄석(13)사이의 계곡에 존재하게 되는 미분입자 또는 알맹이들은 파쇄석(13)의 천연적인 형성과 모양에 의해 나타나게 되는 입체적 요철등에 의한 자연적 미려함에 기여하는 것이 못되므로서 이들을 2차적으로 브러쉬처리한다.After the above process, the fine particles which are present in the valleys between the crushed stones 13 due to the cracking of the sharp part of the crushed stones 13 outside the thickness a in the process of maintaining the homogeneous thickness by the up and down rollers Alternatively, the kernels do not contribute to the natural beauty due to the three-dimensional irregularities, etc., which are caused by the natural formation and shape of the crushed stone 13, so they are secondarily brushed.
이후 제1단계에 의해 제작된 돌벽지(1)를 1차완료물로서 감이한다.Thereafter, the stone wall paper 1 produced by the first step is wound as a primary finished product.
(2단계)(Step 2)
중간단계의 제2용액 코팅처리공정(30)Second solution coating process of the intermediate stage (30)
상기 1단계로 제작된 완료물은 중간단계재로 되며 이에는 돌벽지로서의 방염, 내열, 또는 광택등의 성능을 높이고자 제2용액으로 코팅처리를 행한다. 여기서, 제2용액은 투명접착제와 돌비늘입자(15)를 혼합한 것이 된다.The finished product produced in the first step is an intermediate step material, which is subjected to a coating treatment with a second solution to improve the performance of flame retardant, heat resistance, or gloss as a stone wall paper. Here, the second solution is a mixture of the transparent adhesive and the mica particles 15.
이후 제 2 건조처리공정(31)을 거쳐 제2단계로 완료된 목적물의 권회공정을 마치게 된다.Thereafter, the winding process of the target object completed in the second step is completed through the second drying treatment step 31.
또, 상기 제 1 단계에서의 경사각도로의 투석처리공정(21)에 있어서의 파쇄석(13)은 이를 통상의 방법과같이 집적안료를 처리한 것으로 할 수도 있다.In addition, the crushed stone 13 in the dialysis treatment step 21 at an inclination angle in the first step may be treated with an integrated pigment as in the conventional method.
이러한 본 발명은 제 1 단계에서의 제 1 용액의 도포처리공정(20)에서 제 1 용액이 돌가루입자(12)를 포함한 제1접착층(11)으로 되므로서 방열 및 방염기능이 양호해지고, 또, 제 2 단계에서의 제 2 용액 코팅처리공정(30)시 제 2 용액에 돌비늘입자(15)가 부여되므로서 2차적인 방염 및 내열기능이 부여되고, 광택효과를 가질 수 있다.In the present invention, since the first solution becomes the first adhesive layer 11 including the stone particles 12 in the
또, 제 1 용액의 돌가루입자(12)는 그것이 단열 또는 방염등의 기능이 우수한 어떠한 소재로 대체가 가능하며, 제 2 단계에서의 제 2 용액의 돌비늘입자도 여하한 광택, 방염(단열)소재로의 대체가 가능하다.In addition, the stone powder particles 12 of the first solution can be replaced with any material having excellent functions such as heat insulation or flameproofing, and the mica particles of the second solution in the second step can be polished or flameproofed (insulation). Replacement with material is possible.
이렇게 기초재에 피층처리된 파쇄석(13)은 그것이 파쇄될시 그 자연적인 형태의 파쇄된 모양으로 그대로 존재하게 되고, 이로인해 인위적으로 형태가 주어지는 기술적수단 보다는 천연적이고 자연스런 미적감각이 그대로 살아있게 되며, 그 입체적 미려함을 증진시킨다.The crushed stone (13) layered on the base material is present as it is in its crushed shape when it is crushed, so that a natural and natural aesthetic sense is alive rather than the technical means artificially given. To enhance its three-dimensional beauty.
또, 천연적인 적재에 의해 실내장식이 손쉽게 이뤄지므로서 실내장식을 천연적으로 조화시키려는 불필요한 노력을 제거할 수도 있는 것이다.In addition, since the interior decoration is made easily by natural loading, it is possible to eliminate unnecessary efforts to harmonize the interior decoration naturally.
또, 돌가루와 돌비늘이 포함된 1,2차의 피층처리에 의한 것과 자연석재에 의해 주어지는 그 자체의 본질적인 내열, 방염효과가 우수하고, 습기등에 강한 벽지가 부여된다. 그리고, 그 제작공정이 간단하고 용이하므로서 그 대량생산에 적합하고 그 가격을 저렴히 할 수도 있다.In addition, by the first and second skin treatments that include crushed stone and scales, and its own natural heat and flame-retardant effect given by natural stone is excellent, the wallpaper is given a strong against moisture. In addition, since the manufacturing process is simple and easy, it is suitable for mass production and the price can be reduced.
Claims (4)