Description

Decorative sticker which cuts by printing method

제1도는 본 고안의 일부 확대 사시도.1 is a partially enlarged perspective view of the present invention.

제2a, b, c, d도는 공정 예시도.2a, b, c, d is a diagram illustrating the process.

제3도는 본 고안의 스티카를 접착 사용시 단면 예시도.Figure 3 is an exemplary cross-sectional view when using the sticky stick of the present invention.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1 : 반투명 이형대지 2 : 경질수지층1: Translucent release land 2: Hard resin layer

3 : 연질수지층 3' : 중경질 유연성 씨이트3: soft resin layer 3 ': hard flexible sheet

4 : 엠보싱층 5 : 점착층4: embossing layer 5: adhesive layer

본 고안은 유리, 타일 또는 가구 등의 광활면상에 부착하는 스티카를 스크린 인쇄방법에 의해 다색도 인쇄하여 별도의 프레스 및 재단의 공정을 거치지 아니하고 컷팅의 효과를 낼 수 있는 장식용 스티카에 관한 것으로, 특히 본 고안은 유광지 또는 모조지 등의 원지에 석유수지를 토루엔에 용해시킨 용제로서 코팅처리하여 반투명성을 부여하고 이의 상면에 실리콘 코팅처리하여 반투명의 이형대지를 형성하며, 코팅처리된 반투명의 이형대지상에 P.V.C 레진, 아크릴수지와 아농, 토루엔 및 안료 충진제를 혼합한 수지로서 스크린 인쇄하여 점착성이 없는 경질의 수지층을 형성하고, 이에 염화비닐수지, 염화 초산비닐 및 D.O.P, 부틸세로솔부(B.C), 안정제, 증진제와 층진제를 일정 비율로 혼합한 연질의 수지를 경질 수지층 상면에 일정 형태의 모양으로 스크린 인쇄하여 연질수지가 점착성이 없는 경질의 수지층 내부로 흡수되면서 중경질의 씨이트로 변환시켜 주게하여, 이에 다시 비닐계 중공합물, D.O.P, 니트릴고무(NBR), SBR 라바, 토루엔, 부틸세로솔부, 염화초산비닐, 메틸에칠렌(MEK)을 중합한 점착수지를 중경질의 씨이트화 된 연질수지층 상면에 스크린 인쇄하여 점착성이 우수한 스티카를 형성하고, 점착면은 실리콘 코팅처리한 이형대지를 부착시켜 보관하는 것으로 점착면상의 대지를 박리시켜 유리등의 표면에 점착 사용시 유연성과 점착성을 지닌 스티카를 반투명의 이형대지를 통해 유리 등의 표면상 점착위치를 용이하게 식별하여 요구되는 부위에 간단히 부착시켜 주게 되며, 점착후 스티카의 반투명 이형대지 박리시 이형대지상의 경질수지층은 반투명의 이형대지와 함께 일체로 박리되게 되어 스티카와 이형대지상의 점착성이 없는 경질수지층 사이의 경계면이 서로 분리되어 프레스 및 재단작업에 의한 컷팅의 효과를 낼 수 있도록 한 것이다.The present invention relates to a decorative sticker which can make a cutting effect without a separate press and cutting process by printing multicolored stickers on a wide surface such as glass, tile or furniture by a screen printing method, and in particular, The present invention is coated with a petroleum resin in toluene on a base paper such as glossy paper or imitation paper to give translucency, and a semi-transparent release paper is formed by coating a silicone on the upper surface thereof to form a translucent release paper. PVC resin, acrylic resin and ananone, toluene, and pigment filler were mixed with screen printing to form a hard resin layer with no stickiness. Thus, vinyl chloride resin, vinyl chloride and DOP, and butyl serosol (BC) were formed. Soft resin mixed with stabilizer, enhancer and layering agent in a certain ratio on top of hard resin layer By printing, the soft resin is absorbed into the hard resin layer without adhesiveness and converted into a medium hard sheet, which in turn is made of vinyl-based composites, DOP, nitrile rubber (NBR), SBR lava, toluene, and butyl serosol. , Adhesive printing polymerized with vinyl chloride and methyl ethylene (MEK) is screen-printed on the upper surface of the hard, citrated soft resin layer to form a sticky sticky sticky film, and the adhesive surface is attached with a silicone coated release paper. By peeling the earth on the adhesive surface, it is easy to identify the sticking position on the surface of glass through the semi-transparent release paper and easily attach it to the required area by using the sticky stick with flexibility and adhesiveness when using the adhesive on the surface of glass. When peeling off the translucent release sheet of the stick after adhesion, the hard resin layer on the release sheet will be peeled off together with the translucent release sheet. The interface between the adhesive and the hard resin layer with no adhesive on the release paper is separated from each other to produce the effect of cutting by pressing and cutting work.

일반적으로 종래의 스티카에 있어서는 점착처리된 별도의 스티카 원지상에 소정 무늬모양으로 스크린 인쇄방법에 의해 인쇄하여 이에 유광성 투명 합성수지층을 형성시켜 인쇄된 도안의 크기에 관계없이 원지 전체를 스티카로 형성시켜 주게 되었던 것으로, 도형에 따라 필요한 형태를 재단등에 의한 컷팅작업의 공정을 별도로 거쳐야 하는 문제점이 있었으며, 또한 완성된 스티카를 원하는 위치에 부착시켜 주기 위하여 이형지로부터 분리시킨 스티카편을 각각 부착면상에 부착하게 되었던 것이며, 전체적인 형상을 조화시키기 위하여 필요 부분의 스티카를 제외한 여백을 제거한 후 부착면에 부착할 경우에 있어서도 이형지가 불투명지로 되어 있는 관계로 정확하게 요구되는 부위상에 부착함이 불가능한등의 여러가지 결함이 있었다.In general, the conventional sticky paper is printed by a screen printing method in a predetermined pattern on a separate sticky sticky paper, and is formed on the sticky transparent synthetic resin layer so that the entire paper is made of sticky regardless of the size of the printed pattern. According to the figure, there was a problem that the necessary shape must be separately processed by cutting, etc. according to the figure, and the sticky pieces separated from the release paper are attached on the attaching surface to attach the finished sticky to the desired position. In order to harmonize the overall shape, it is impossible to attach it on the required part precisely because the release paper is opaque even after removing the margin except the sticky part of the necessary part. There was this.

이와 같은 제반 결함을 해소하기 위하여 안출한 본 고안은 유리, 타일 또는 가구 등의 광활면상에 부착하는 스티카를 스크린 인쇄방법에 의해 다색도 인쇄하여 별도의 가공처리 과정인 프레스 및 재단공정을 거치지 아니한고 컷팅의 효과를 낼 수 있도록 하기 위하여 석유수지, 파라핀유 및 식물유, 용제 등을 토루엔에 용해시킨 용제로 유광지 또는 모조지 등의 원지를 코팅처리하여 이의 상면에 실리콘 코팅처리한 반투명의 이형대지상에 P.V.C 레진, 아크릴수지, 아농, 토루엔, 안료 충진제 등을 혼합한 수지로서 전면 또는 일정무늬 형태로 스크린 인쇄하여 점착성이 없는 경질의 수지층을 형성하고, 염화비닐수지, 염화초산비닐, D.O.P, 부틸세로솔부와 안정제, 증진제, 충진제 등을 혼합한 수지로서 경질수지층 상면에 일정형태의 모양으로 스크린인쇄하여 연질수지가 경질의 점착성이 없는 수지층의 내부로 흡수되면서 중경질의 유연성 씨이트로 변환시켜 그의 상부에 비닐계 중공합물, D.O.P, 니트릴고무, SBR 라바, 토루엔 및 부틸세로솔부, 염화초산비닐, 에틸에칠렌 등을 중합한 점착수지를 중경질의 씨이트화된 연질수지층 상면에 스크린 인쇄방법으로 도포하여 점착성이 우수한 스티카를 형성하는 것이다.The present invention devised to solve such defects is printed by multi-color printing on the light stick of glass, tile or furniture, etc. by screen printing method, and it does not go through the press and cutting process, which is a separate processing process. In order to make cutting effect, PVC is coated on semi-transparent release paper coated with base paper such as gloss paper or imitation paper by dissolving petroleum resin, paraffin oil, vegetable oil and solvent in toluene. It is resin mixed with resin, acrylic resin, anon, toluene, pigment filler, etc., and is screen-printed in the form of a front surface or a certain pattern to form a hard resin layer without adhesiveness. Vinyl chloride resin, vinyl chloride acetate, DOP, butyl vertical Screen printing in the shape of a certain shape on the upper surface of the hard resin layer. The soft resin is absorbed into the inside of the resin layer which is not sticky and hard to convert into a hard flexible sheet, and on top of it, a vinyl-based hollow material, DOP, nitrile rubber, SBR lava, toluene and butyl cersol, vinyl chloride Adhesive resin obtained by polymerizing ethyl ethylene or the like is applied to the upper surface of the hard, citized soft resin layer by a screen printing method to form a sticky sticky film.

이에 앞서 열경화성 또는 열가소성 수지분말을 중경질의 씨이트화된 연질수지층 상에 도포시켜 엠보싱 처리하여 줌으로서 내외 양면 장식성을 구비한 장식용 스티카를 제공할 수 있는 것으로, 이를 첨부한 도면에 의거 자세히 설명하면 다음과 같다.Prior to this, by applying a thermosetting or thermoplastic resin powder on a medium hard sheeted soft resin layer and embossing, it is possible to provide a decorative sticker having internal and external decorative properties, which will be described in detail with reference to the accompanying drawings. Same as

즉, 유광지 모조지 등의 원지상에 석유수지 20중량%에 대하여 파라핀유 20중량%, 식물유 20중량%, 용제20중량%를 토루엔에 용해시킨 용제로 코팅처리하여 이의 상면에 다시 실리콘 코팅처리한 반투명 이형대지(1)상에 P.V.C 레진 40중량%에 대하여 아크릴수지5중량%, 아농 20줄량%, 토루엔30중량%, 안료 15중량%, 충진제5-10중량%를 중합한 수지로서, 전면 또는 일정무늬 형태로 스크린 인쇄하여 충진제와 안료가 적정량 이상의 혼합에서 오는 점착성이 없이 부서지는 성질을 지닌 경질의 수지층(2)을 형성하고, 이 상부에 염화수지비닐 50중량%에 대하여 염화초산비닐 10중량%, 가소제(D.O.P)100중량%, 부틸세로솔부(B.C) 5중량%, 안정제5중량%, 증진제 5-10중량%, 충진제 미량을 혼합한 연질수지(3)를 경질수지층(2) 상면에 일정 형태의 모양으로 스크린 인쇄하여 연질수지(3)가 경질의 점착성이 없는 수지층(2) 내부로 흡수되면서 중경질의 유연성 씨이트(3')로 변환시켜 주게 하고, 이에 열경화성 또는 열가소성 수지분말을 도포시켜 엠보싱층(4)을 형성하며, 여기에 다시 비닐계 중공합물 10중량%에 대하여 D.O.P 약간 니트릴고무(NBR)10중량%,SBR 라바 30중량%, 토루엔 25중량%,메칠에칠렐 25중량%, 부틸세로솔부와 염화초산비닐 각 5-10중량%씩 중합한 점착수지(5)층을 스크린 인쇄하여 점착성이 우수한 내의 양면 장식성을 구비한 스티카(S)를 소비자의 취향 및 사용 용도에 따라 용이하게 제공할 수 있는 것으로, 필요에 따라 자외선 흡수제(U.V)를 첨가 사용함으로서 장기간 변색이 되지 않는 목적을 얻을 수 있는 것이다.That is, 20% by weight of paraffin oil, 20% by weight of vegetable oil, and 20% by weight of solvent are dissolved in toluene, and the upper surface thereof is silicon-coated again. A resin obtained by polymerizing 5% by weight of acrylic resin, 20% by weight of aconium, 30% by weight of toluene, 15% by weight of pigment, and 5-10% by weight of filler based on 40% by weight of PVC resin on translucent release paper (1). Or screen-printed in the form of a certain pattern to form a hard resin layer (2) having a cracking property without stickiness coming from the mixing of the filler and pigment more than an appropriate amount, on top of which 50% by weight of vinyl chloride vinyl acetate 10% by weight, 100% by weight of plasticizer (DOP), 5% by weight of butyl vertical sol (BC), 5% by weight of stabilizer, 5-10% by weight of enhancer, and a small amount of filler (3) to the hard resin layer (2) ) The screen is printed in the form of a certain shape on the upper surface and the soft resin (3) It is absorbed into the resin layer 2 having no hard tack and converted into a medium hard flexible sheet 3 ', and the thermosetting or thermoplastic resin powder is applied thereto to form the embossed layer 4 again. 10% by weight of DOP nitrile rubber (NBR), 30% by weight of SBR lava, 25% by weight of toluene, 25% by weight of methyl ethylene, butyl-cerosol and 5% of vinyl acetate It is possible to easily provide a sticker (S) having double-sided decorative property with excellent adhesiveness by screen printing the adhesive resin (5) layer polymerized by weight percent according to consumer's taste and use purpose. By adding and using (UV), the object which does not discolor for a long time can be obtained.

미설명 부호 6은 부착면이다.Reference numeral 6 is an attachment surface.

이와 같은 본 고안은 석유수지 20중량%에 대하여 파라핀유, 식물유, 용제 각 20중량%씩을 토루엔에 용해시킨 용제로 코팅처리하고 상면에 실리콘 코팅처리하여 반투명의 이형대지(1)를 형성시켜 줌으로서 이형대지(1) 상에 구성된 경질수지층(2)의 내부로 상부의 연질 수지층(3)을 흡수하여 중경질 유연성씨이트(3')화된 스티카(S)를 부착편(6) 상의 소정위치에 용이하게 선별 부착시킬 수 있는 것이다.The present invention is coated with a solvent in which 20% by weight of paraffin oil, vegetable oil, and solvent are dissolved in toluene with respect to 20% by weight of petroleum resin, and a silicone coating is applied to the upper surface to form a translucent release sheet (1). As a result, the upper soft resin layer 3 is absorbed into the hard resin layer 2 formed on the release sheet 1, and the hardened flexible sheet 3 'is formed on the sticking piece 6 on the attachment piece 6. It can be easily attached to a predetermined position.

또한 반투명 이형대지(1) 상면에는 P.V.C 레진 40중량%에 대하여 아크릴수지 5중량%, 아농 20중량%, 토루엔 30중량%, 안료 15중량%, 충진제 5-10%를 중합한 수지로 전면 또는 일정무늬 형태로 스크린 인쇄한 경질의 수지층(2)과 염화비닐수지 50중량%에 대하여 염화초산비닐 10중량%, 가소제 100중량%, 부틸세로솔부 5중량%, 안정제 5중량%, 증진제 5-10중량%, 충진제 미량을 혼합한 수지로 스크린 인쇄하여 형성한 연질 합성수지층(3)을 각각 적층시켜 주어 연질의 합성수지(3)가 비점성상태의 경질수지층(2) 내부로 흡수되면서 유연성을 가지는 중경질의 씨이트(3')로 변환하게 되어 경질수지층(2)은 상면에 연질수지층(3)을 인쇄 도포하여 중경질씨이트(3')화된 부위와 연질수지층(3)이 인쇄되지 않은 비점성상태의 부서지는 성질을 지닌 경질수지층(2)으로 분리되어 존재하게 되어 중경질의 씨이트(3')화된 연질수지층(3) 하단의 경질수지층(2)은 스티카(S) 박리 사용시 중경질씨이트(3') 상면에 스크린 인쇄한 비닐계 중공합물 10중량% 대하여 니트릴고무 10중량%, SBR라바 30중량%, 토루엔 25중량%, 부틸세로솔부 5-10중량%, 염화초산비닐 5-10중량%, 메틸에칠렌 25중량%와 가소제 미량을 중합한 점착수지(5)에 의해 부착면(6) 상에 견고히 점착되며, 중경질의 씨이트(3')화된 경질수지층(2) 이외의 부분인 충진제와 안료를 적정 혼합비 이상으로 혼합하여 비점성 상태의 부서지는 성질을 지닌 경질수지층(2)은 반투명의 이형대지(1)와 일체로 박리되는 것으로, 반투명 이형대지(1) 상 중경질씨이트(3')화된 스티카(S)는 점착수지(5)로 인해 부착면(6) 상에 용이하게 점착되어 스크린 인쇄수단에 의해 별도의 프레스 또는 재단의 공정을 거치지 아니하고 컷팅의 효과를 낼 수 있을 뿐만 아니라, 컷팅 작업이 극히 어려운 선, 문자 또는 도형의 무늬 등을 간단한 인쇄공정을 통해 용이하게 다색도 스크린 인쇄하여 중경질싸이트(3')화 함으로서 컷팅의 효과를 내는 스티카(S)를 얻을 수 있는 것이다.In addition, on the upper surface of the translucent release sheet (1), a resin obtained by polymerizing 5% by weight of acrylic resin, 5% by weight of ananol, 30% by weight of toluene, 15% by weight of pigment, and 5-10% of filler with respect to 40% by weight of PVC resin 10% by weight of vinyl acetate, 100% by weight of plasticizer, 5% by weight of butyl vertical sol, 5% by weight of stabilizer, and 5 to 5% by weight of hard resin layer (2) and 50% by weight of vinyl chloride resin screen-printed in the form of a pattern. 10 wt% of the soft synthetic resin layer (3) formed by screen printing with resin mixed with a small amount of filler is laminated so that the soft synthetic resin (3) is absorbed into the non-viscous hard resin layer (2) to increase flexibility. The hard resin layer 2 is converted into a hard sheet 3 ', and the hard resin layer 2 is coated with a soft resin layer 3 on the upper surface thereof, whereby the hardened layer 3' and the soft resin layer 3 are formed. It is separated and separated into hard resin layer (2) having a non-printing non-viscous state of brittleness. The hard resin layer (2) at the bottom of the hard sheet (3 ') into the hard sheet (3') is a vinyl-based hollow composite screen printed on the upper surface of the hard sheet (3 ') when peeling off the stick (S). 10% by weight of nitrile rubber, 30% by weight of SBR lava, 25% by weight of toluene, 5-10% by weight of butyl cersol, 5-10% by weight of vinyl chloride, 25% by weight of methyl ethylene and a small amount of plasticizer It is adhered firmly on the adhesion surface 6 by the adhesive resin 5, and the non-viscous state by mixing the filler and the pigment which is a part other than the hard resin layer 2 into which the hard sheet (3 ') was made more than a suitable mixing ratio. The hard resin layer (2) having a cracking property of is peeled integrally with the translucent release sheet (1), and the hardened sheet (3 ') on the translucent release sheet (1) is made of adhesive resin. (5) is easily adhered on the attachment surface (6) so that the screen printing means does not undergo a separate press or cutting process In addition to the effect of cutting, the screening of lines, characters or figures, which are extremely difficult to cut, can be easily printed by multi-color screen printing through a simple printing process to make a hard surface (3 '). I can get the sticker (S).

중경질씨이트(3')화된 연질수지층(3) 상면에 점착수지(5) 층을 스크린 인쇄하여 형성된 스티카(S)를 유리등의 표면상 부착면(6)에 점착 사용시 석유수지를 토루엔에 용해시킨 용제로 코팅처리한 반투명 이형대지(1)를 사용함으로서 반투명지상의 인쇄층이 뒷면에서 식별이 용이하게 되어 부착면(6)의 위치를 자유로이 선정할 수 있는 것으로, 이에 열경화성 또는 열가소성 수지분말을 도포시켜 엠보싱층(4)을 형성시켜 줌으로서 입체감이 탁월한 장식용스티카(S)를 기대할 수 있는 것으로, 사용자의 취향 및 사용용도에 적합한 스티카를 간단한 인쇄의 공정을 통해 다색도 인쇄하여 평면 인쇄시 인쇄 용제의 표면 확산에서 오는 무늬 형태등의 외곽면의 곡선 상태로서 흐름을 방지할 수 있는 것으로, 통상의 스티카 원지를 프레스 또는 재단등의 공정을 통해 컷팅한 효과를 동일한 컷팅의 효과를 기대할 수 있는 것이다.Sticking the sticky resin (S) formed by screen-printing the adhesive resin (5) layer on the upper surface of the hard sheet (3 ') softened layer (3') to the petroleum resin By using the semi-transparent release sheet (1) coated with a solvent dissolved in yen, the printing layer on the translucent paper can be easily identified from the back side, and the position of the attachment surface 6 can be freely selected. By applying the resin powder to form the embossing layer (4), it is possible to expect a decorative sticker (S) excellent in three-dimensional effect, and by printing a multi-colored sticker suitable for the user's taste and use through a simple printing process, It is possible to prevent the flow as a curved state of the outer surface such as the pattern form coming from the surface diffusion of the printing solvent at the time of printing, and through the process such as pressing or cutting the normal sticky paper Tinghan the effects would be expected that the effect of the same cut.

두께 또한 인쇄 횟수의 다수 반복으로 인해 용이하게 조절가능한 스티카를 제공할 수 있는 것이며, 열가소성, 수지분말 또는 열경화성 수지분말을 도포하여 줌으로서 엠보싱 효과를 부여하여 장식용 스티카의 내외 양면 장식성을 배가시킬 수 있는 매우 유용하고도 실용적인 고안인 것이다.The thickness can also provide a stably adjustable stica due to the multiple repetition of the number of prints, and by applying a thermoplastic, resin powder or thermosetting resin powder, the embossing effect can be given to double the decorative properties of the decorative stica. It is a very useful and practical design.

Claims

In the composition of Styka (S), translucent release paper coated with 20% by weight of paraffin oil and vegetable oil solvent dissolved in toluene with respect to 20% by weight of petroleum resin on base paper such as gloss paper or imitation paper. (1) On the upper surface, a hard resin layer (2) polymerized with 5% by weight of acrylic resin, 20% by weight of anacone, 30% by weight of toluene, 15% by weight of pigment, and 5-10% by weight of filler based on 40% by weight of PVC resin. A screen-printed soft resin layer containing 10% by weight of vinyl acetate, 100% by weight of plasticizer, 100% by weight of plasticizer, 5% by weight of butyl cersol, stabilizer, 5-10% by weight of filler, and a small amount of filler. After screen printing (3) to convert the hard flexible sheet (3 ') into an embossed layer (4), 10% by weight of nitrile rubber, 30% by weight of SBR lava, and mound to 10% by weight of the vinyl copolymer. 25% by weight of yen, butyl vertical sole, 5-10% by weight of vinyl acetate each and Ethylene 25% by weight, ornamental seutika that the effect of the cut by a printing method, characterized in that provided to form a pressure-sensitive adhesive layer as the adhesive resin 5, a small amount of polymerization of the plasticizer.