KR870000947B1 - The method for preparing of cigarette paper - Google Patents

Abstract

This invention relates to the manufacturing method of the cigarette paper of great porosity, which is made from arrowroot. An arrowroot is cut in fixed length and resolved by using caustic soda and emulsifying soda at high temperature. The resolved arrowroot is bleached by using a hypochloride acid soda and the arrowroot pulp is made. The cigarette paper of great porosity is made from arrowroot pulp.

Description

Meat ball cigarette paper using 칡 and its manufacturing method

The present invention relates to a meat ball cigarette paper used in the manufacture of tobacco, in particular a meat ball cigarette paper using the 및 and a method of manufacturing the same.

In recent years, smokers' preferences tend to search for mild cigarettes. Here, the groundbreaking factor of cigarette paper is to act as a decisive factor for giving a mild taste to cigarettes. It acts as a supply channel for oxygen during smoking, not only contributes to complete combustion during combustion, but also contributes to the dilution of tobacco smoke by air, resulting in a reduction in carbon monoxide content and low nicotine and low tar content tobacco.

Conventional cigarette-making meat ball cigarette paper is manufactured using the foreign imported linseed linseed or wood pulp, but there are various problems as follows. That is, hemp fiber pulp and wood pulp are all imported, so not only have to pay expensive foreign currency, but wood pulp is short and wide, and it is difficult to increase porosity because it is broken when the altitude is increased. On the other hand, hemp fibers have a longer length, which can increase the porosity compared to wood pulp, but because the fibers are relatively thick, the fibers are entangled in papermaking, resulting in uneven appearance in cigarette papers, resulting in uneven porosity, opacity, whiteness, and tensile strength. There is a problem that can not produce meat ball cigarette paper over a certain limit.

SUMMARY OF THE INVENTION An object of the present invention is to provide a new meat ball cigarette paper and a method of manufacturing the same, which is economical and meat ball by improving the problems of the conventional meat ball cigarette paper.

The present inventors improve the problem of the cigarette paper using the hemp fiber pulp and wood pulp of the above, while making the pulp of the native paper in Korea while researching the manufacture of cigarette paper with this, the fiber of the yarn is very suitable for increasing the porosity It was found that the present invention was completed.

Hereinafter, the present invention will be described in detail.

After collecting wild boar, cut it to a certain size, neutralize it at high temperature with caustic soda and emulsified soda, wash it with clear water so that alkalinity is not detected, and bleach it with soda hydrochloric acid.

When the beet pulp is made to be beaten for 20 minutes using a pulverizer, it is different from wood pulp, which has to be beaten for more than 1 hour. That is, the fibers are long and dispersed well and have a high porosity. Using a pulp alone or a mixture of other pulp and dilution to a certain concentration, the paper is mixed with a filler such as calcium carbonate and a retarder in a perforated paper machine to obtain a soft, high-quality meat ball cigarette paper. The porosity of the cigarette paper (27 g / m ² ) using the obtained pulp and the porosity of the cigarette paper by the other pulp are as follows.

As described above, the meat ball cigarette paper prepared using the pulp according to the present invention has a long and relatively thin fiber, so that the fibers are well dispersed and greatly improve the porosity, as well as whiteness, opacity, and tensile strength. The appearance is good and the quality of the meat in the cigarette paper will have an improved effect.

Moreover, according to the present invention, it is possible to save the foreign currency spent on imported pulp because it uses wild boils that are native to Korea. Economic effects will also appear.

EXAMPLE

After cutting the 칡 collected from the fermentation into 3cm size and immersing it in hot water, mix it with 10% caustic soda and 30% emulsified soda at a liquid ratio of 8: 1. Only fiber is left. This fiber is bleached with sodium hypochlorite to give 6% effective chlorine to give a white pulp. At this time, the seawater yield is 78.9% and the bleaching yield is 83.7%. When the pulp obtained here is beaten to 60-80'SR using a pulverizer, a stock having a bond different from that of ordinary choke wood or hemp pulp is formed.

When the paper is mixed with about 20% precipitated calcium carbonate and titanium dioxide as a filler, and then coated with 1% citric acid soda, a meat ball cigarette paper having a porosity of about 1,700 (Corest unit) is produced.

Claims (2)

A meat ball cigarette paper made from vines made from vinegar, bleached in heavy seas, made into pulp, beaten to 60-80'SR, and then blended with a filler and a supporting agent. Using vinegar as a raw material, it is neutralized with caustic soda, emulsified sodium, hypochlorous acid, etc., bleached to make pulp. The pulp is beaten to 60-80'SR, and pores are prepared by differently formulating fillers and auxiliaries such as calcium carbonate. Method for producing meat ball cigarette paper using the 칡 characterized in that to adjust the degree.