KR840002138B1

KR840002138B1 - Mother-of-pearl coloring method

Info

Publication number: KR840002138B1
Application number: KR1019830004713A
Authority: KR
Inventors: 조경양
Original assignee: 조경양; 조남길
Priority date: 1983-10-05
Filing date: 1983-10-05
Publication date: 1984-11-23

Abstract

Ground mother-of-pearl having a thickness of 0.4-1 mm is immersed in an alk. soln. (pH 9-10, caustic soda water or ammonia water) at 110- 120≰C for 5-6 hrs. in a vapor tube of 1-2 atm. The colloidal ingredient of the mother-of-pearl is decompd. and gushed. Many pores are created in the mother-of-pearl from the expansion phenomenon that results from the heat and pressure. These pores are then permeated with a pigment using a known dyeing process and show uniform color.

Description

How to color mother-of-pearl

본 발명은 단순한 백색의 값싼 자개를 값이 비싼 천연산 유색자개와 동일하게 착색하는 자개의 착색방법에 관한 것이다.The present invention relates to a method of coloring a mother-of-pearl in which the simple mother-of-pearl is colored the same as the expensive natural colored mother-of-pearl.

일반적으로 자개는 오랜 옛날부터 가구류나 목기류 등에 장식효과를 더욱 조화시킬 수 있게 이용되어 왔었고, 이는 세계 각처의 패류 즉, 조개껍질, 소라껍질, 전복껍질 같은 패각류의 산출지 변동에 따라 같은 종류의 패각이라 할지라도 각각 다른 색상과 무늬모양을 지니고 있어서, 하나의 자개공예장식 작품을 만들려면 아무리 내국산 자개가 많아도 색상과 무늬의 조화를 이루기 위하여 세계각처에서 생산되는 유색자개를 매우 비싼 값으로 수입하여 사용하지 않으면 않되는 문제점이 있었다.In general, mother-of-pearl has been used for a long time to harmonize decorative effects on furniture and wood, which is the same type of shellfish, shellfish, shellfish shells, etc. Even though the shells have different colors and patterns, to make a single mother-of-pearl craft work, no matter how many domestic mother-of-pearl are produced, the colored mother-of-pearl produced from all over the world is imported at a very high price to achieve harmony of colors and patterns. There was a problem that must be used.

이러한 현실을 탈피하기 위하여 일부 자개공예업자들은 인공유색자개를 얻을 목적으로 다각적인 염색방법을 연구하여 왔으나 자개의 각질속으로 색소가 침투되지 못하여 자개자체가 지니는 휘광적 색감을 조성할 수 없고 또 자개를 붙이고 광택연마시에 상당한 두께로 연삭될때 색상의 변화가 문제시되어 왔다.In order to escape this reality, some mother-of-pearl craftsmen have studied various dyeing methods for the purpose of obtaining artificial colored mother-of-pearl.However, pigments do not penetrate into the corneum of mother-of-pearl, and they cannot create a bright color of mother-of-pearl. The change of color has been a problem when grinding to a considerable thickness during polishing and polishing.

그러므로, 자개 전체 깊숙히 동일한 색도를 가지는 착색을 할 수 없는 경우 자개로서의 이용가치는 없는 것이다.Therefore, there is no use value as a mother-of-pearl when the coloring with the same chromaticity deeply in the entire mother-of-pearl is not possible.

본 발명은 이와 같은 문제점들로부터 착안하여 견고한 칼슘 주성분의 각질 깊숙히 색소가 침투할 수 있는 다수의 미세한 공극을 형성하는데 주안점을 두고 여러가지를 실험연구한 결과 새로운 착색방법을 개발하기에 이른 것이다.The present invention has been focused on the formation of a number of fine pores through which the pigment can penetrate deep into the keratin of the solid calcium main component, and as a result of various experimental studies, it has led to the development of a new coloring method.

즉, 패각류의 원형으로부터 연마 · 가공처리를 거쳐 두께 0.4-1mm의 자개(색이 없는 단순한 백색형태의 자개)를 증관내에서 pH 9-10의 가성소다수나 암모니아수 또는 3%(물에 대한 중량비율)의 염수에 담근 상태에서 증기 1-2기압(온도 110-120℃ 정도)을 유지하면서 5-8시간 경과시킨후 세척 건조한 결과 패각질 속에 함유된 교질이 높은 온도와 압력 및 주입용액속에서의 분해 · 용출되고 또 열과 압력하에서 용액의 침투작용으로 팽창현상이 발생하여 패각질 전체에 미세한 공극이 발생하여 색소의 침투가 이상적으로 이루어질 수 있게 되므로 천연산의 유색자개보다 더 많은 색상의 인조유색자개를 얻으므로서 자개공예의 품질을 더욱 높일 수 있게 함에 그 특징이 있는 것인바, 이를 공정별로 상술하면 다음과 같다.In other words, the mother-of-pearl shell with a thickness of 0.4-1mm (a simple white form without color) was polished and processed from a shell of a shell, and caustic soda water, ammonia water or 3% (weight to water) After 5-8 hours while maintaining steam at 1-2 atmosphere (temperature 110-120 ℃) while immersed in saline, the colloids contained in the shells at high temperature, pressure and infusion solution. The dissolution and elution of swelling and the expansion of the solution under the heat and pressure cause the expansion of fine pores throughout the shells, making it ideal for the penetration of pigments. It is characterized by being able to further increase the quality of mother-of-pearl craft while obtaining mother-of-pearl.

[제1공정][Step 1]

패각류 즉, 조개껍질 · 소라껍질 또는 전복껍질 같은 패각류(貝殼類)를 연마, 가공처리하여 1mm미만의 자개편을 얻는다. 이때 패각류의 산출지에 따라 자개특유의 천연무늬나 색상이 다르며 색상과 무늬가 매우 아름다운 자개를 제외한 백색과 같은 단순색상을 띈 값싼 자개만을 모은다.Shells, ie shells such as seashells, seashells, or abalone shells, are ground and processed to obtain mother-of-pearl pieces less than 1 mm. At this time, the mother-of-pearl's natural pattern or color is different depending on the place where the shellfish are produced.

[제2공정][Step 2]

공지의 방법으로 가공처리된 값싼 단순색상의 자개를 증관내에 넣고 pH9-10이 되는 가성소다수나 암모니아수 또는 3%(물에 대한 중량비)의 소금이 용해된 염수를 증관내에 주입하여 자개가 공기중으로 노출되지 않고 주입용액속에 잠기게 한 다음 밀폐상태에서 증기 1기압 내지 2기압(약 110℃-120℃)을 유지하면서 5시간-8시간(이때의 시간은 자개의 두께에 따라 증감될 수 있음) 경과후에 꺼내면 용액 속에서의 열과 압력하에 용액의 침투작용으로 팽창현상이 발생하여 칼슘적층에 함유된 교질성분이 일부 분해 용출되고 또 압력하에서 가열되어 미세한 균열로 인한 공극이 자개전체에 생기게 한다.Inexpensive simple colored mother-of-pearl, processed by a known method, is placed in the tube, and caustic soda water, pH 9-10, or ammonia water or 3% (by weight to water) of salt dissolved in the tube is injected into the tube. Submerged in the infusion solution without exposure to the medium, and then kept in a sealed state for 1 to 2 atmospheres (about 110 ℃-120 ℃) for 5 to 8 hours (the time can be increased or decreased depending on the thickness of the mother-of-pearl When it is taken out after evaporation, expansion phenomenon occurs due to infiltration of solution under heat and pressure in solution, and the colloidal component contained in calcium deposit is partially dissolved and eluted and heated under pressure to create voids due to fine cracks.

이때 증관내에서 주입용액의 존재없이 자개가 직접 증기에 노출된 상태로 가열하면 자개는 보기싫게 검은색으로 변색되고 그 강도도 떨어져서 장식자개로서 이용가치가 상실되며, 또 기압을 낮추어도 중관내에 넣은 자개는 내부의 것과 외부의 것이 강도와 공극형성이 각각 다르게 나타나므로 가공제품의 균일성이 없다.At this time, if the mother-of-pearl is heated directly exposed to steam without the presence of injection solution, the mother-of-pearl turns discolored to black and loses its strength as a decorative mother-of-pearl. The mother-of-pearl has different uniformity between the inner and outer ones due to the different strength and void formation.

[제3공정][Step 3]

제2공정을 거쳐 미세한 공극이 형성된 자개를 세척한 다음 공지의 적당한 임의 색상의 색소용액중에 담그어 자개에 형성된 공극으로 색소가 침투하여 착색되게 한다. 이때 용제의 온도는 50℃-70℃가 적당하며 5-10시간 정도 밀폐된 용기내에서 담그어 착색시킨후 표면을 물로 세척하여 열풍 건조시킨다.After the second step, the mother-of-pearl formed with fine pores is washed and then immersed in a pigment solution of any suitable color known in the art to allow the pigment to penetrate into the pores formed in the mother-of-pearl. At this time, the temperature of the solvent is suitable for 50 ℃-70 ℃, soaked in a closed container for 5-10 hours to be colored and washed with water and dried by hot air drying the surface.

색상의 농도는 제2공정에서의 공극형성을 위한 증기압에서도 관계되지만 색소용액의 농도와 침지하는 시간으로 조절된다.The color concentration is also related to the vapor pressure for pore formation in the second process, but is controlled by the concentration of the dye solution and the time of immersion.

본 발명에서의 자개에 공극을 형성하는 증기 가압가열처리는 자개의 두께가 1mm이하의 것일수록 착색효과가 양호하고 1mm이상의 두꺼운 자개는 깊이 착색되지 않은 비교적 불량한 편이다.Steam pressure heating treatment for forming pores in the mother of pearl according to the present invention has a better coloring effect as the mother's thickness is less than 1 mm, and the mother of pearl thicker than 1 mm is relatively poor in not being deeply colored.

본 발명으로 착색된 인공유색자개는 여러가지 색상, 즉 붉은 색상, 황색, 초록 및 남색 등의 다양한 색상으로 착색되는 것으로 천연자개가 띄는 유색자개의 외관적 색상이 거의 동일한 정도로 유사하며 강도의 변화도 없어서 자개를 가구류에 접착하여 샌드페이퍼로 연마 · 광택처리함에도 가공전의 상태와 동일할 뿐만 아니라 색소의 깊은 침투로 인하여 광택작업중에 자개를 상당한 두께로 연삭하여도 그 색상이나 굴절모양의 변화가 없는 것이다. 그러므로 본 발명은 천연색상을 가지는 천연산 자개의 고가함과, 또 이들의 자개를 모두 고가로 수입하는 무역적자의 일부요인을 배제할 수 있고 저렴한 자개로 천연산 자개보다 더 많은 종류의 색상을 인공적으로 얻으므로서 유색자개로 표현되는 다방면의 공예품의 상품가치를 높이고 아름답게 구성시킬 수 있게 되는 효과가 있다.Artificially colored mother-of-pearl colored by the present invention is colored in a variety of colors, such as red, yellow, green and indigo blue color of the mother-of-pearl color with natural mother-of-pearl is similar to almost the same degree and does not change the intensity Even if the mother-of-pearl is glued to the furniture and polished and polished with sandpaper, the mother-of-pearl is not the same as it was before processing. Therefore, the present invention can eliminate some of the factors of the natural mother-of-pearl and the trade deficit of importing all of these mother-of-pearl in high price, and the artificial mother of more colors than the natural mother-of-pearl with low-cost mother-of-pearl As a result, the product value of various crafts represented by colored mother-of-pearl can be enhanced and beautifully constructed.

[실시예 1]Example 1

연마 · 가공처리 된 두께 0.4-1mm의 자개편을 증관내에 넣고 이에 pH 9-10이 되는 가성소다수를 증관내에 넣은 자개가 모두 잠길때까지 붓고 증기 1기압에서 2기압(약 110-120℃)을 유지하면서 8시간 경과후 꺼내었드니 미량의 점성을 띈 교질액이 용출되고 칼슘의 주성분으로 적층현상으로 구성된 자개체 전체에 염색소의 침투가 용이한 이상적인 미세한 공극이 강도의 변화없이 발생되었고 염색후의 색상도 매우 아름답게 착색되었다.Put a mother-in-law piece with a thickness of 0.4-1mm that has been polished and processed into a steaming tube, and pour caustic soda water with a pH of 9-10 into the steaming tube until all the mother-of-pearl is locked. After 8 hours, the traced colloidal solution was eluted, and the ideal micropores, which easily penetrated the dyestuff, were formed without changing the intensity. Later color was also very beautifully colored.

[실시예 2]Example 2

가공처리된 (0.4-1mm) 두께의 자개를 중관내에서 침전용액이 있는 상태하에서 증기 1기압에서 1시간 정도 경과후 꺼내어 세척한후 공지의 방법으로 염색처리한 결과 색상이 매우 고르지 못하고 자개의 표피 부분에만 국한되어 염색되었다.Processed (0.4-1mm) thick mother-of-pearl was removed after 1 hour at 1 atm of steam under the presence of sedimentation solution in a heavy pipe, washed, and then dyed by a known method. Stained only in part.

[실시예 3]Example 3

연마 · 가공처리 된 두께 0.4-1mm의 자개편을 증관내에서 침전용액이 있는 상태하에서 증기 10기압(약160℃)을 8시간 정도 경과후 꺼내었더니 자개의 색상은 변화없었으나 강도가 저하되어 가벼운 충격에도 부스러지는 상태가 되었고 염색후에 색상은 매우 어둡게 착색되었다.The mother-of-pearl, polished and processed 0.4-1mm thick, was taken out after about 10 hours of steam at about 160 ° C under the presence of sedimentation solution. It was crumbly under impact and the color was very dark after dyeing.

[실시예 4]Example 4

연마 · 가공처리 된 두께 0.4-1mm의 자개편을 침전시킬 용액없이 증관내에서 증기 20기압(약 200℃)에서 10시간 경과후 꺼내어보니 자개편이 모두 까맣게 타고 강도는 손으로 만져서 부스러질 정도로 저하되었다.After 10 hours at 20 atm (about 200 ° C) steam in a steam pipe without a solution to precipitate the mother pieces of 0.4-1mm thickness, the mother pieces were burned in black and the strength was reduced by touching them. It became.

이상의 실시예에서의 실험을 통하여 확실해진 바와 같이 증기압이 상승되면 강도의 저하로 장식자개로서의 가공가치가 상실됨을 발견하게 되었고 본 발명의 제2공정에서와 같이 가공처리를 거친 자개를 증관내에서 pH9-10의 가성소다수에 침전시킨 상태에서 증기 1-2기압(약 110-120℃)을 유지하면서 5-8시간 정도 경과후에 꺼내서 세척하면 염료의 색소가 가장 이상적으로 침투될 수 있는 교질성분의 분해, 용출작용과 팽창현상에서 오는 균열과 같은 대량의 공극형성이 매우 이상적으로 발생됨을 실험을 통하여 확인되었다.As can be seen from the above experiments, when the vapor pressure is increased, the processing value as a decorative mother-of-pearl is lost due to a decrease in strength. Decomposition of the colloidal component that can be most ideally penetrated by dye dyes when it is removed and washed after 5-8 hours while maintaining steam at 1-2 atmosphere (about 110-120 ℃) while precipitated in -10 caustic soda water. It was confirmed through experiments that a large amount of pore formation such as cracks from elution and expansion phenomena occurred very ideally.

Claims

As described above, 1-2-1 atm and steam 110-120 ° C in a state in which a mother-of-pearl of 0.4-1 mm thickness, polished by a known method, is immersed in a solution of pH 9-10 (caustic soda water or ammonia water) in a steam pipe. The coloration method of mother-of-pearl is characterized by uniformly and finely coloring the infiltration of dyes during the known dyeing process due to decomposition and elution of the colloidal component in the culturing after 5-8 hours, and the formation of pores due to expansion phenomenon under heat and pressure.