KR101268632B1 - Method of processing rhus verniciflua in a double boiler, Method of coating urushi laquer mixture, and the products - Google Patents
Method of processing rhus verniciflua in a double boiler, Method of coating urushi laquer mixture, and the products Download PDFInfo
- Publication number
- KR101268632B1 KR101268632B1 KR1020110013264A KR20110013264A KR101268632B1 KR 101268632 B1 KR101268632 B1 KR 101268632B1 KR 1020110013264 A KR1020110013264 A KR 1020110013264A KR 20110013264 A KR20110013264 A KR 20110013264A KR 101268632 B1 KR101268632 B1 KR 101268632B1
- Authority
- KR
- South Korea
- Prior art keywords
- lacquer
- coating
- extract
- heating
- hot water
- Prior art date
Abstract
본 발명은 중탕가열에 의한 옻처리방법, 제조된 옻칠액 코팅방법 및 그 제품에 관한 것으로서, 중탕가열에 의한 옻처리방법은 옻 추출물과 테레핀유를 준비하는 단계; 상기 옻 추출물과 상기 테레핀유를 7:3의 비율로 혼합하는 단계; 상기 옻 추출물과 상기 테레핀유 혼합물을 온도 40℃ 에서 60℃ 까지 서서히 중탕가열하는 단계;를 포함하여 구성되며, 중탕가열된 옻칠액 코팅방법은 여기에 상기 중탕가열된 옻칠액을 대상물에 코팅하고 30℃의 온도 및 40% 습도에서 건조시키는 단계;를 더 포함하여 구성되는 것을 특징으로 한다. 이와 같은 중탕가열에 의해 옻을 처리함으로써, 천연 옻액을 이용한 코팅이나 염색시 옻액이 대상물(제품)에 고르게 침투되고 원하는 내구성 및 방수성 등의 기능을 발휘하며, 또한 어떠한 화학약품이나 자외선처리공정 없이도 대상물에 옻액이 투명하게 코팅되어 대상상품의 재질특성이나 대상물에 표현된 다양한 문양 및 색감을 원 색채 그대로 표현할 수 있도록 투명한 옻칠이 되는 효과가 있다.The present invention relates to a lacquer treatment method by heating a hot water, a lacquer coating method and a product thereof. The lacquer treatment method using a hot water heating includes preparing a lacquer extract and terepin oil; Mixing the lacquer extract with terepin oil in a ratio of 7: 3; Step of slowly heating the lacquer extract and the terepin oil mixture from the temperature 40 ℃ to 60 ℃; comprising a, the heated lacquer coating method of the heated bath here coating the heated lacquer liquid to the object 30 Drying at a temperature of 40 ℃ and humidity 40%; characterized in that it further comprises. By treating the lacquer by such hot water heating, the lacquer liquid is evenly penetrated into the object (product) during coating or dyeing using natural lacquer liquid, and exhibits the desired durability and waterproofness, and also without any chemical or ultraviolet treatment process. The lacquer is transparently coated on the material, and the effect of becoming a clear lacquer can be expressed as the original color of various patterns and colors expressed in the material characteristics of the target product.
Description
본 발명은 옻 처리방법, 제조된 옻칠액 코팅방법 및 그 제품에 관한 것으로서, 더욱 상세하게는 천연 옻 추출물과 천연 테레핀유를 7:3의 비율로 혼합한 다음 혼합물을 40℃ 에서 60℃ 까지 서서히 중탕가열하는 방식으로 옻을 처리하고 그와 같은 처리방법에 의해 옻칠액을 제조하는 중탕가열에 의한 옻 처리방법, 제조된 옻칠액 코팅방법 및 그 제품에 관한 것이다.The present invention relates to a lacquer treatment method, a lacquer coating method and a product thereof, and more particularly, natural lacquer extract and natural terepine oil are mixed in a ratio of 7: 3, and then the mixture is slowly heated from 40 ° C to 60 ° C. The present invention relates to a method for treating lacquer by heating a bath, manufacturing a lacquer coating method, and a product thereof, by treating lacquer in a manner of heating a bath and preparing a lacquer solution by such a treatment method.
천연 옻은 오래전부터 공예품등의 도료로서 사용되어져 왔다. 이와 같이 옻이 도료로 사용되어져 온 것은 천연 옻이 매우 높은 도막 강도와 내구성, 방수성 등의 기능성 이외에도 아름다운 광택과 탁월한 촉감을 가지고 있기 때문이다. Natural lacquer has been used as a paint for crafts for a long time. The reason why lacquer has been used as a coating material is that natural lacquer has beautiful luster and excellent touch in addition to very high coating strength, durability and waterproofness.
또한, 요즘에는 한지 등의 종이제품이나 스카프나 의류 등의 섬유제품 등에도 옻성분을 이용하여 염색 또는 코팅을 하거나, 또는 종이나 섬유 등을 바탕으로 한 실용품에 옻을 이용하여 코팅하는 방법 등이 다양하게 연구되고 있다.Also, nowadays, a method of dyeing or coating a paper product such as Hanji or a textile product such as a scarf or clothing by using lacquer or coating a practical product based on paper or fiber using lacquer Various studies have been made.
그러나, 천연 옻액은 기름성분과 물 성분이 불안정하게 현탁상태를 이루고 있기 때문에, 옻액을 코팅 또는 염색하는 경우 상분리가 발생하여 코팅이 불균일하고 기포가 발생하게 되는 문제점이 있다. 이와 같은 문제점을 제거하기 위하여, 종래기술들은 옻의 수분함량을 20% 이하가 되도록 소정온도에서 직접가열하는 전처리공정을 하는 것이 일반적인데, 이때, 옻의 갈변현상 및 공정의 번거로움 문제가 여전히 남아 있다.However, since the natural lacquer is unstable in an oil component and a water component, there is a problem in that the coating is uneven and bubbles are generated when the lacquer is coated or dyed. In order to eliminate such a problem, the prior art is generally a pre-treatment step of heating directly at a predetermined temperature so that the moisture content of the lacquer is less than 20%, at this time, browning phenomenon and troublesome process of the lacquer still remain have.
또한, 옻 성분은 공기와 접촉할 경우, 옻의 주성분인 우루실 성분이 공기중의 산소와 결합하여 진한 갈색으로 변하게 되므로, 이로 인하여 갈색이나 흑색을 제외한 나머지 색상을 구현할 수 없을 뿐만 아니라, 대상물(제품)에 표현된 문양등의 색감을 그대로 표현해 내지 못하는 문제점이 있었다. 이와 같은 갈변현상을 방지하고자 종래의 기술에는 화학약품을 혼합한다든지 또는 자외선처리를 하는 방법이 게재되어 있으나, 이와 같은 방법은 친환경적인 면에서 바람직하지 못할 뿐만 아니라, 사용된 화학약품이 피부에 알러지를 발생시키거나 화학약품이나 자외선처리시 대상물의 문양이나 색감을 그대로 표현하지 못하게 되는 문제점이 있다.In addition, when the lacquer component is in contact with air, the uricyl component, which is the main component of the lacquer, is combined with oxygen in the air and becomes dark brown. Therefore, the lacquer component may not realize colors other than brown or black. There was a problem that can not express the color of the pattern as expressed in the product). In order to prevent such browning phenomenon, a conventional method of mixing a chemical or ultraviolet treatment is disclosed, but such a method is not preferable in terms of environment-friendly, and the chemical used is allergic to the skin. There is a problem that does not generate or represent the pattern or color of the object during chemical or ultraviolet treatment.
또한, 종래기술은 옻액 대비 용제함량이 지나치게 많음에 따라, 대상물(제품)의 원하는 내구성을 갖추지 못하는 문제가 있었다.In addition, the prior art, there is a problem that does not have the desired durability of the object (product) as the solvent content is too much compared to the lacquer.
이에 본 출원인은 예의 연구를 거듭한 결과, 옻액을 이용한 코팅이나 염색시 옻액이 대상물에 고르게 침투되고 원하는 내구성 및 방수성 등의 기능을 발휘하도록 하며, 또한 대상물에 옻액이 투명하게 코팅되어 대상물의 재질특성이나 대상물에 표현된 다양한 문양 및 색감을 원 색채 그대로 표현할 수 있도록 투명한 옻칠이 되도록 하는 본 발명을 고안하게 되었다.Accordingly, the present applicant has made intensive studies, and the coating or dyeing of the lacquer liquid, the lacquer liquid evenly penetrates the object and exhibits the desired durability and waterproofness, and also the lacquer liquid is transparently coated on the object and the material characteristics of the object. In order to express various patterns and colors expressed in the object as it is, the present invention has been devised to make a transparent lacquer.
본 발명은 상기의 문제점을 해결하기 위하여 안출된 것으로서,본 발명의 목적은 옻액을 이용한 코팅이나 염색시 옻액이 대상물에 고르게 침투되고 원하는 내구성 및 방수성 등의 기능을 발휘하도록 하며, 또한 어떠한 화학약품이나 자외선처리공정 없이도 대상물에 옻액이 투명하게 코팅되어 대상물의 재질특성이나 대상물에 표현된 다양한 문양 및 색감을 원 색채 그대로 표현할 수 있도록 투명한 옻칠이 되도록 하는 옻처리방법, 제조된 옻칠액 코팅방법 및 그 제품을 제공하는 것이다. The present invention has been made in order to solve the above problems, an object of the present invention is to make the lacquer evenly penetrated into the object during coating or dyeing using the lacquer solution and to exhibit the desired durability and waterproof properties, and also any chemicals or Lacquer treatment method to make lacquer transparent to the object without UV treatment process to make the lacquer transparent so that the material characteristics and colors of the object can be expressed as the original color. To provide.
상기 목적을 달성하기 위하여, 본 발명에 따른 중탕가열에 의한 옻처리방법은In order to achieve the above object, the lacquer treatment by hot water heating according to the present invention
옻 추출물과 테레핀유를 준비하는 단계; Preparing lacquer extract and terepin oil;
상기 옻 추출물과 상기 테레핀유를 일정비율로 혼합하는 단계; 및Mixing the lacquer extract and terepin oil in a predetermined ratio; And
상기 옻 추출물과 상기 테레핀유 혼합물을 중탕가열하는 단계;를 포함하여 구성된 것을 특징으로 한다.Characterized in that it comprises a; the step of heating the lacquer extract and the terepin oil mixture in a bath.
여기서, 상기 옻 추출물과 상기 테레핀유의 혼합비율은 7:3인 것을 특징으로 한다.Here, the mixing ratio of the lacquer extract and terepin oil is characterized in that 7: 3.
또한, 상기 옻 추출물과 상기 테레핀유의 혼합비율은 3:7 ~ 5:5인 것을 특징으로 한다.In addition, the mixing ratio of the lacquer extract and terepin oil is characterized in that 3: 7 ~ 5: 5.
또한, 상기 중탕가열단계에서 상기 옻 추출물과 상기 테레핀유 혼합물은 온도 40℃ 에서 60℃ 까지 서서히 중탕가열되는 것을 특징으로 한다.In addition, the lacquer extract and the terepin oil mixture in the hot water heating step is characterized in that the hot water is slowly heated to a temperature of 40 ℃ to 60 ℃.
또한, 본 발명에 따라 제조되는 제품은 제 1 항 내지 제 3 항 중 어느 한 항의 옻처리방법에 따라 제조된 옻칠액을 코팅하여 제조되는 것을 특징으로 한다.In addition, the product produced according to the present invention is characterized in that it is prepared by coating a lacquer liquid prepared according to the lacquer treatment method of any one of claims 1 to 3.
또한, 본 발명에 따라 중탕가열된 옻칠액 코팅방법은In addition, the lacquer coating method heated in hot water according to the present invention
옻 추출물과 테레핀유를 준비하는 단계; Preparing lacquer extract and terepin oil;
상기 옻 추출물과 상기 테레핀유를 7:3의 비율로 혼합하는 단계; Mixing the lacquer extract with terepin oil in a ratio of 7: 3;
상기 옻 추출물과 상기 테레핀유 혼합물을 온도 40℃ 에서 60℃ 까지 서서히 중탕가열하는 단계; 및Gradually heating the lacquer extract and the terepin oil mixture from 40 ° C. to 60 ° C .; And
상기 중탕가열된 옻칠액을 대상물에 코팅하고 30℃의 온도 및 40% 습도에서 건조시키는 단계;를 포함하여 구성되는 것을 특징으로 한다.And coating the heated bath lacquer on the object and drying at a temperature of 30 ° C. and a humidity of 40%.
또한, 본 발명에 따라 제조되는 제품은 제 5 항의 방법에 의해 제조되는 제품인 것을 특징으로 한다.In addition, the product produced according to the invention is characterized in that the product produced by the method of claim 5.
본 발명의 옻처리방법, 제조된 옻칠액 코팅방법에 의해, 천연 옻액을 이용한 코팅이나 염색시 옻액이 대상물(제품)에 고르게 침투되고 원하는 내구성 및 방수성 등의 기능을 발휘하며, 또한 어떠한 화학약품이나 자외선처리공정 없이도 대상물에 옻액이 투명하게 코팅되어 대상물의 재질특성이나 대상물에 표현된 다양한 문양 및 색감을 원 색채 그대로 표현할 수 있도록 투명한 옻칠이 되는 효과가 있다.According to the lacquer treatment method of the present invention, the lacquer coating method prepared, the lacquer solution is evenly penetrated into the object (product) during coating or dyeing using the natural lacquer solution, and exhibits the desired durability and waterproof properties, and any chemicals or Even without UV treatment, the lacquer is transparently coated on the object, so that the lacquer can be used as a transparent lacquer so as to express various characteristics and colors of the object.
도 1은 본 발명에 따른 중탕가열에 의한 옻처리방법을 나타내는 블럭도,
도 2는 본 발명에 따른 중탕가열에 의해 제조된 옻칠액을 코팅하는 방법을 나타내는 블럭도,
도 3a ~도 3e는 본 발명에 따라 제조된 투명옻칠액을 코팅하여 건조시킨 제품(공예품, 직물(스카프), 종이(부채 등))을 촬영한 사진.1 is a block diagram showing a lacquer treatment method by heating in hot water according to the present invention,
Figure 2 is a block diagram showing a method for coating a lacquer liquid prepared by hot water heating according to the present invention,
Figure 3a to Figure 3e is a photograph of a product (crafts, fabrics (scarf), paper (debt, etc.) coated and dried by coating a transparent lacquer liquid prepared according to the present invention.
이하 첨부된 도면을 참조하여 본 발명의 실시예를 설명하면 다음과 같다.Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings.
도 1은 본 발명에 따른 중탕가열에 의한 옻처리방법을 나타내는 블럭도, 도 2는 본 발명에 따른 중탕가열에 의해 제조된 옻칠액을 코팅하는 방법을 나타내는 블럭도, 도 3a ~도 3e는 본 발명에 따라 제조된 투명옻칠액을 코팅하여 건조시킨 제품(공예품, 직물(스카프), 종이(부채 등))을 촬영한 사진이다.1 is a block diagram showing a lacquer treatment method by a heated bath according to the present invention, Figure 2 is a block diagram showing a method for coating a lacquer liquid prepared by a heated bath according to the present invention, Figures 3a to 3e It is a photograph of a product (crafts, fabric (scarf), paper (debt, etc.)) coated and dried by the transparent lacquer liquid prepared according to the invention.
도 1에 도시된 바와 같이, 본 발명에 따른 중탕가열에 의한 옻처리방법은, As shown in Figure 1, the lacquer treatment by hot water heating according to the present invention,
(1) 천연 옻 추출물과 천연 테레핀유를 준비하는 단계; (1) preparing a natural lacquer extract and natural terepin oil;
(2) 천연 옻 추출물과 천연 테레핀유를 7:3의 비율로 혼합하는 단계;(2) mixing the natural lacquer extract and natural terepin oil in a ratio of 7: 3;
(3) 혼합물을 온도 40℃ 에서 60℃ 까지 서서히 중탕가열하는 단계;로 구성되는 것이 특징이다.
(3) gradually heating the mixture to a temperature of 40 ℃ to 60 ℃; it is characterized by consisting of.
이하, 본 발명에 따른 중탕가열에 의한 옻처리방법을 상세하게 설명하면 다음과 같다.Hereinafter, the lacquer treatment method by heating the hot water according to the present invention will be described in detail.
(1) 천연 옻 추출물과 천연 테레핀유를 준비하는 단계:(1) preparing natural lacquer extract and natural terepine oil:
여기서, 천연 옻 추출물은 불순물이 걸러진 것이라면, 생옻이든 정제옻이든 관계없다.Here, the natural lacquer extract, regardless of whether the impurities are filtered out, whether raw lacquer or purified lacquer.
테레핀유는 옻과 혼합하여 옻을 녹이는 용제역할과 더불어 경화제 역할도 하는 천연물질로서, 옻액과의 혼합시 그 함량비율에 따라 옻칠액의 점성도가 다르게 되어 대상물에 침투되는 정도에 차이가 있으며 이와 같은 침투정도에 따라 대상물의 품질유지에 차이가 발생된다.Terepene oil is a natural substance that acts as a solvent to melt lacquer by mixing it with lacquer, and also acts as a curing agent.When mixing with lacquer, the viscosity of lacquer liquid is different depending on the content ratio. Depending on the degree of penetration, there is a difference in maintaining the quality of the object.
(2) 천연 옻 추출물과 천연 테레핀유를 일정비율로 혼합하는 단계:(2) mixing the natural lacquer extract and natural terepin oil in a proportion:
준비된 천연 옻 추출물과 천연 테레핀유를 투명한 유리 내열재 용기에 7:3의 비율로 넣고 혼합한다. The prepared natural lacquer extract and natural terepine oil are mixed in a ratio of 7: 3 in a transparent glass heat resistant container.
본 발명에 따른 천연 옻 추출물과 천연 테레핀유의 7:3의 혼합비율은 테레핀유 함량이 옻액 함량보다 현격하게 많은 종래기술들과 관점을 달리하여 고안해 낸 것으로, 종래의 기술들과는 현격한 효과차이를 가져오는 최적의 함량비율이다.The ratio of 7: 3 of natural lacquer extract and natural terpene oil according to the present invention is devised by varying the viewpoints of the conventional terepene oil content from the lacquer content, which is significantly different from those of the conventional lacquer oil content. Optimum content ratio to bring.
물론, 스카프와 같은 부드럽고 얇은 직물에 옻칠액을 코팅시에는 천연 옻추출물과 천연 테리핀유 혼합비율을 3:7~5:5, 바람직하게는 3:7로 하여 직물의 재질특성을 살릴 수도 있음은 물론이다.Of course, when the lacquer coating is applied to a soft thin fabric such as a scarf, the natural lacquer extract and the natural terrypine oil mixing ratio may be 3: 7 to 5: 5, preferably 3: 7, thereby improving the material properties of the fabric. Of course.
이때, 직물에 코팅을 여러번 시행함에 따라 원하는 코팅두께 및 원하는 함량의 옻성분이 코팅되도록 할 수 있음은 물론이다.At this time, by coating the fabric several times, the desired coating thickness and the desired content of the lacquer can be of course coated.
옻액과 테레핀유를 혼합시 종래기술과 같이 옻액의 함량비가 테레핀유의 함량비에 비해 현격하게 적으면, 옻의 성분이 미비하게 되므로, 이와 같이 제조된 옻칠액을 대상물에 코팅하게 되면 원하는 옻의 효과를 얻을 수 없을 뿐만 아니라, 대상물의 품질유지 내지 품질의 지속성을 저해하게 되어 대상물 품질의 수명을 단축시키는 결과를 가져오게 된다.When mixing the lacquer and terepine oil, if the content of the lacquer is significantly less than the content of terepine oil as in the prior art, the components of the lacquer are inadequate. Not only does not achieve the effect, but also impairs the maintenance of the quality of the object or the persistence of the quality, which results in shortening the life of the object quality.
또한, 종래기술과 같이 옻 추출물과 테레핀유를 혼합할때 단순 교반 또는 직접가열할 경우에는, 옻 추출물이 테레핀유보다 적게 되면 혼합이 고르게 안되어 추후 코팅 내지 염색을 수행할 수 없게 된다.In addition, in the case of simple stirring or direct heating when mixing the lacquer extract and terepine oil as in the prior art, when the lacquer extract is less than the terepine oil, the mixing is not even and the coating or dyeing cannot be performed later.
여기서, 옻칠액 자체에 원하는 색을 나타내도록 다양한 천연염료를 원하는 비율로 더 포함시킬 수 있음은 물론이다.Here, of course, various natural dyes may be further included in a desired ratio so as to show a desired color in the lacquer solution itself.
(3) 상기 옻 추출물과 상기 테레핀유 혼합물을 중탕가열하는 단계:(3) heating the lacquer extract and the terepin oil mixture in a bath;
옻액과 테레핀유 혼합물이 든 내열재 용기를 적당량의 물이 들어 있는 가열용기내에 넣고, 혼합물의 온도가 40℃ ~ 60℃ 가 될때까지 서서히 중탕가열한다. Place the heat-resistant container containing the lacquer and terepene oil mixture in a heating container containing an appropriate amount of water, and gradually heat the bath until the temperature of the mixture reaches 40 ° C to 60 ° C.
이와 같이 옻액과 테레핀유 혼합물을 직접가열교반하지 않고 중탕가열함에 따라, 옻액 혼합물의 온도가 급격하게 상승되는 것을 방지할 수 있을 뿐더러, 적은 양의 테레핀유를 혼합하더라도 중탕가열에 의해 옻액 성분과 테레핀유의 고른 혼합이 이루어지게 되고 함유된 수분도 적절하게 제거하므로 대상물(제품)에 코팅시 충분한 양의 옻성분이 함유된 옻칠액이 코팅되므로 대상물의 내구성 및 보존성이 높아지게 된다.Thus, by heating the lacquer and terepin oil mixture without direct heating and stirring, the temperature of the lacquer mixture can be prevented from being rapidly increased, and even if a small amount of terepine oil is mixed, the lacquer component and tere Evenly mixing of the pin oil and appropriately remove the moisture contained in the coating (laminate) lacquer liquid containing a sufficient amount of the lacquer component when coating the object (product) increases the durability and preservation of the object.
또한, 혼합물 온도가 40℃ ~ 60℃ 가 될때까지 서서히 중탕가열함에 의해, 옻칠액의 앙금이 발생되는 것을 방지할 뿐만 아니라, 옻성분이 용제인 테레핀유로부터 분리되는 것을 방지하여 용제에 고르게 혼합되도록 함으로써, 옻칠액이 투명색으로 되는 것을 용이하게 한다. 즉, 중탕가열에 의해 옻칠액이 짙은 갈색 또는 검은색으로 변하는 것을 방지할 수 있게 되는 것이다.In addition, by heating the hot water gradually until the mixture temperature reaches 40 ° C. to 60 ° C., the sediment of the lacquer solution is not only prevented from being generated, but also the lacquer is prevented from being separated from the terepin oil, which is a solvent, and mixed evenly with the solvent. By making it easy, it becomes easy for a lacquer liquid to become a transparent color. That is, it is possible to prevent the lacquer liquid from turning to dark brown or black by heating the bath.
특히, 혼합물 온도가 60℃를 넘게되면, 옻의 앙금이 발생되고 옻성분이 분리될 뿐만 아니라, 옻칠액 색깔이 검게 변하게 된다.In particular, when the mixture temperature exceeds 60 ℃, the sediment of the lacquer is generated and the lacquer component is separated, as well as the color of the lacquer liquid becomes black.
본 발명과 같이 옻액을 중탕가열하게 되면, 종래기술에서의 옻액 갈변현상을 방지할 수 있게 됨에 따라, 투명옻액을 제조하기 위하여 자외선을 쬐거나 별도의 화학약품처리를 하는 공정처리가 필요없게 된다.When the lacquer is heated in a hot bath as in the present invention, it becomes possible to prevent the lacquer browning phenomenon in the prior art, so that a UV treatment or a separate chemical treatment is not necessary to prepare a transparent lacquer.
더욱이, 대상물인 섬유나 공예품 등에 종래기술의 자외선을 쬐거나 별도의 화학약품처리는 피부에 유해한 효과를 미치게 되고 환경적인 차원에서도 적절하지 않으며, 대상물에 인쇄된 문양이나 색감등을 원형 그대로 유지하지 못하게 하여 대상물의 예술적 가치 내지 미감을 저하시키게 된다.
In addition, conventional UV rays or separate chemical treatments on textiles and crafts, which are the object, have a harmful effect on the skin and are not suitable for the environmental level, and the pattern or color printed on the object cannot be maintained as it is. This lowers the artistic value or aesthetics of the object.
또한, 도 2에 도시된 바와 같이, 본 발명에 따른 중탕가열에 의해 제조된 옻칠액을 코팅하는 방법은,In addition, as shown in Figure 2, the method for coating the lacquer liquid prepared by hot water heating according to the present invention,
(1) 천연 옻 추출물과 천연 테레핀유를 준비하는 단계; (1) preparing a natural lacquer extract and natural terepin oil;
(2) 천연 옻 추출물과 천연 테레핀유를 7:3의 비율로 혼합하는 단계;(2) mixing the natural lacquer extract and natural terepin oil in a ratio of 7: 3;
(3) 혼합물을 온도 40℃ 에서 60℃ 까지 서서히 중탕가열하는 단계; 및(3) slowly heating the mixture to a temperature of 40 ° C. to 60 ° C .; And
(4) 상기 중탕가열된 옻칠액을 대상물에 코팅하고 30℃의 온도 및 40% 습도에서 건조시키는 단계;로 구성되는 것이 특징이다.
(4) coating the heated lacquer solution on the object and drying at a temperature of 30 ° C. and 40% humidity.
즉, 이와 같이 중탕가열처리된 옻칠액을 대상물(제품)인 섬유, 목재나 죽재 등의 공예품, 종이 등에 코팅하고 대략 30℃의 온도 및 40% 습도에서 건조시키면 코팅옻칠액 색이 서서히 투명색으로 맑게 올라와 대상물의 품질을 최상으로 유지시키게 된다.In other words, coating the lacquer solution heated in the bath is applied to the objects (products), crafts such as wood, bamboo, etc., and paper, and dried at a temperature of approximately 30 ° C. and 40% humidity, and the coating lacquer color gradually rises to a clear color. Maintain the best quality of the object.
즉, 중탕가열처리된 옻칠액의 고르게 분포된 옻 성분은 대상물인 섬유나 목재등의 조직에 침투가 용이하게 되어 섬유나 목재 등의 품질 및 섬유나 목재 표면에 장식된 작품들의 품질을 최상으로 유지시키면서 내구성을 높이게 된다.In other words, the evenly distributed lacquer component of the heated bath lacquer solution is easily penetrated into tissues such as fibers and wood as objects, while maintaining the quality of fibers and wood and the quality of works decorated on the surface of fibers or wood. It increases durability.
이와 같이 본 발명에 따라 중탕가열처리된 투명옻칠액이 도포된 제품(공예품, 직물(스카프), 종이(부채 등))이 도 3a ~도 3e에 도시되어 있다.Thus, a product (crafts, fabric (scarf), paper (debt, etc.) coated with a bath-heated transparent lacquer solution according to the present invention is shown in Figs. 3a to 3e.
사진자료에서 알 수 있듯이, 제품에는 투명색의 옻칠액이 코팅되어 제품의 본래 인쇄문양이나 색감이 원형 그대로 표현되어 예술적 가치 및 아름다운 미감이 느껴진다는 것을 알 수 있다.
As can be seen from the photographic material, the product is coated with a clear lacquer liquid so that the original printed pattern or color of the product is expressed in its original form, and the artistic value and beautiful aesthetic can be felt.
비록 본 발명이 상기에서 언급한 바람직한 실시예와 관련하여 설명되었지만, 본 발명의 요지와 범위로부터 벗어남이 없이 다른 다양한 수정이나 변형이 가능할 것이다. 따라서, 첨부된 청구범위는 본 발명의 진정한 범위 내에 속하는 그러한 수정 및 변형을 포함함은 물론이다.Although the invention has been described in connection with the preferred embodiments mentioned above, other various modifications and variations will be possible without departing from the spirit and scope of the invention. It is, therefore, to be understood that the appended claims are intended to cover such modifications and changes as fall within the true scope of the invention.
Claims (7)
상기 옻 추출물과 상기 테레핀유를 일정비율로 혼합하는 단계; 및
상기 옻 추출물과 상기 테레핀유 혼합물을 중탕가열하는 단계;를 포함하여 구성된 것을 특징으로 하는 중탕가열에 의한 옻처리방법.Preparing lacquer extract and terepin oil;
Mixing the lacquer extract and terepin oil in a predetermined ratio; And
The lacquer treatment method according to claim 2, wherein the lacquer extract and the terepin oil mixture are heated in a bath.
상기 옻 추출물과 상기 테레핀유의 혼합비율은 7:3인 것을 특징으로 하는 중탕가열에 의한 옻처리방법.The method of claim 1,
The mixing ratio of the lacquer extract and terepin oil is 7: 3 lacquer treatment method by heating in hot water.
상기 옻 추출물과 상기 테레핀유의 혼합비율은 3:7 ~ 5:5인 것을 특징으로 하는 중탕가열에 의한 옻처리방법.The method of claim 1,
The mixing ratio of the lacquer extract and terepin oil is 3: 7 ~ 5: 5 lacquer treatment method by heating the hot water, characterized in that.
상기 중탕가열단계에서 상기 옻 추출물과 상기 테레핀유 혼합물은 온도 40℃ 에서 60℃ 까지 서서히 중탕가열되는 것을 특징으로 하는 중탕가열에 의한 옻처리방법.The method of claim 1,
The lacquer treatment method according to the hot water heating, characterized in that the lacquer extract and the terepin oil mixture in the hot water heating step is gradually heated to 40 ℃ to 60 ℃.
상기 옻 추출물과 상기 테레핀유를 7:3의 비율로 혼합하는 단계;
상기 옻 추출물과 상기 테레핀유 혼합물을 온도 40℃ 에서 60℃ 까지 서서히 중탕가열하는 단계; 및
상기 중탕가열된 옻칠액을 대상물에 코팅하고 30℃의 온도 및 40% 습도에서 건조시키는 단계;를 포함하여 구성되는 것을 특징으로 중탕가열된 옻칠액 코팅방법.Preparing lacquer extract and terepin oil;
Mixing the lacquer extract with terepin oil in a ratio of 7: 3;
Gradually heating the lacquer extract and the terepin oil mixture from 40 ° C. to 60 ° C .; And
Coating the heated bath lacquer on the object and drying at a temperature of 30 ° C. and 40% humidity; the heated bath lacquer coating method, characterized in that it comprises a.