KR20240126613A - Methods of manufacture of coral calcium nutrients - Google Patents
Methods of manufacture of coral calcium nutrients Download PDFInfo
- Publication number
- KR20240126613A KR20240126613A KR1020230019285A KR20230019285A KR20240126613A KR 20240126613 A KR20240126613 A KR 20240126613A KR 1020230019285 A KR1020230019285 A KR 1020230019285A KR 20230019285 A KR20230019285 A KR 20230019285A KR 20240126613 A KR20240126613 A KR 20240126613A
- Authority
- KR
- South Korea
- Prior art keywords
- coral
- hours
- powder
- alcohol
- same
- Prior art date
Abstract
본 발명은 산호칼슘영양소 제조방법에 관한 것으로, 강알카리성 천연풍화조초 산호사 분말 90중량비%에 구연산 과립상 10중량비%를 첨가하여 중성화를 이루고 4시간 동안 95도-110도의 고온에서 중탕교반가열후 분말로 분쇄하여 연질캡슐형태의 칼슘영양소를 제조하도록 한 것이다.
본 발명은 천연 풍화조초 산호사를 정제수에 침수시켜 염분을 제거하고, 밀폐로내에서 1000℃-1300℃로 8-10시간 소성가공하여 강알카리성 분말로 분쇄하며, 알콜주정으로 가공하여 구연산 과립상 100g, 알콜 10ℓ, 산호분미립자 500g을 95-110℃에서 4시간 동안 중탕교반가열하고, 97-100℃압력용기에서 6시간 교반농축되게 가열하여 연질캡슐형태로 정제한다.The present invention relates to a method for manufacturing coral calcium nutrients, wherein 10 wt% of citric acid granules is added to 90 wt% of strongly alkaline natural weathered algae coral sand powder to neutralize the resultant, and then the resultant is heated in a double boiler at a high temperature of 95 to 110 degrees Celsius for 4 hours and then ground into powder to manufacture calcium nutrients in the form of soft capsules.
The present invention relates to a method for producing a natural weathered coral, comprising: submerging natural weathered coral in purified water to remove salt; calcining the same in a sealed furnace at 1000-1300°C for 8-10 hours; crushing the same into a strongly alkaline powder; and processing the same with alcohol; heating 100 g of citric acid granules, 10 L of alcohol, and 500 g of coral powder fine particles in a double boiler at 95-110°C for 4 hours; stirring and concentrating the same in a pressure vessel at 97-100°C for 6 hours; and refining the same into a soft capsule form.
Description
본 발명은 산호칼슘영양소 제조방법에 관한 것으로, 특히 강알카리성 천연풍화조초 산호사 분말 90중량비%에 구연산 과립상 10중량비%를 9:1비율로 첨가하여 중성화를 이루고 4시간 동안 95도-110도의 고온에서 중탕교반 가열후 분말로 분쇄하여 연질캡슐 형태의 칼슘영양소를 제조하도록 한 것이다.The present invention relates to a method for manufacturing coral calcium nutrients, and more particularly, to neutralizing 90% by weight of highly alkaline natural weathered algae coral sand powder by adding 10% by weight of citric acid granules in a ratio of 9:1, and then heating in a double boiler at a high temperature of 95 to 110 degrees for 4 hours, followed by grinding into powder to manufacture calcium nutrients in the form of soft capsules.
일반적으로 경제가 성장하면서 식생활이 풍족해짐에 따라 사람들은 육류와 가공된 인스턴트 식품을 많이 섭취하므로 사람들의 체질이 점차 산성체질로 변하며, 유아나 소아의 경우에는 칼슘이 부족하여 골조가 빈약해지는 경향이 있다.In general, as the economy grows and eating habits become more abundant, people consume more meat and processed instant foods, so people's constitutions gradually change to acidic ones, and in the case of infants and children, they tend to have weak bones due to calcium deficiency.
임산부 또는 폐경의 부녀가 칼슘이 부족할 경우 골다공증이 빈번하게 발생되어 노후 건강관리에 심각한 영향을 미치고 있다.Pregnant women or postmenopausal women frequently suffer from osteoporosis when they are calcium deficient, which has a serious impact on their health in old age.
현재, 시중에서 여러종류의 칼슘영양소가 판매되고 있으나, 단순히 조개류 등의 분말에 불과하여 인체에서 충분히 소화되지 못한 상태에서 체외로 배출되고, 칼슘의 함유량이 적어 제기능을 발휘하지 못하는데, 이는 칼슘영양제를 제조하는 방법의 기술이 낙후된 것에 그 원인이 있다.Currently, various types of calcium nutrients are sold on the market, but they are simply powders of shellfish, etc., and are excreted from the body without being fully digested, and the calcium content is low, so they do not function properly. This is because the technology for manufacturing calcium nutrients is outdated.
본 발명은 상기와 같은 종래의 결점을 해결하기 위한 것으로, 본 발명의 목적은, 체내에 흡수가 잘되는 칼슘영양소를 제조하기 위한 것으로, 풍화조초 산호사를 정제수에 침수한 후 먼저 밀폐로에서 소성가공한 후 분말로 분쇄한 강알카리성 분말 90중량비%에 구연산 과립상 10중량비%를 9:1비율로 첨가하여 중성화시키는 산호칼슘영양소 제조방법을 제공하는데 있다.The present invention is to solve the above-mentioned conventional shortcomings, and the purpose of the present invention is to provide a method for producing a coral calcium nutrient which is well absorbed in the body, by submerging weathered coral sand in purified water, first calcining it in a sealed furnace, and then neutralizing it by adding 10 weight % of citric acid granules to 90 weight % of a strongly alkaline powder which is ground into powder at a ratio of 9:1.
이와 같은 목적을 달성하기 위한 본 발명은, 풍화조초 산호사를 정제수에 침수시켜 고농도칼슘, 이온화칼슘성분의 흡수성이 좋게하고, 염분이 제거된 풍화조초 산호사를 밀폐로내에서 1000℃-1300℃로 8-10시간 소성가공하여 강알카리성 분말로 미세하게 분쇄하며, 알콜주정으로 가공하여 구연산 과립상 100g, 알콜 10ℓ, 산호분 미립자 500g을 95-110℃에서 4시간 동안 중탕 교반가열후 분쇄하고, 97-100℃ 압력용기에서 6시간 교반 농축되게 가열하여 연질캡슐형태로 정제하여 이루어짐을 특징으로 한다.To achieve the above purpose, the present invention is characterized in that the weathered coral sand is immersed in purified water to improve the absorbency of high-concentration calcium and ionized calcium components, the weathered coral sand from which salt has been removed is calcined in a sealed furnace at 1000-1300°C for 8-10 hours to finely grind into a strong alkaline powder, and the mixture is processed with alcohol, 100 g of citric acid granules, 10 ℓ of alcohol, and 500 g of coral powder fine particles are stirred and heated in a double boiler at 95-110°C for 4 hours, then ground, and then stirred and concentrated and heated in a pressure vessel at 97-100°C for 6 hours to purify into a soft capsule form.
이상에서 상세히 설명한 바와 같이 본 발명은, 양질의 천연 풍화조초 산호사를 원료로 정제수에서 침수하여 염분을 제거하고 소성가공 공정과 중탕 교반 가열 공정을 거쳐 농축된 연질캡슐형태로 체내에 잘 흡수되는 칼슘영양소를 제조할 수 있는 효과가 있다.As described in detail above, the present invention has the effect of producing calcium nutrients that are well absorbed in the body in the form of concentrated soft capsules by using high-quality natural weathered coral as a raw material, submerging it in purified water to remove salt, and then going through a calcination process and a double-boiler stirring and heating process.
도 1은 본 발명에 사용되는 통상적인 내열 전기로의 개략도
도 2는 본 발명에 따른 산호칼슘영양소의 제조 공정도이다.Figure 1 is a schematic diagram of a typical heat-resistant electric furnace used in the present invention.
Figure 2 is a manufacturing process diagram of coral calcium nutrients according to the present invention.
이하, 본 발명의 바람직한 실시예를 상세히 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail.
도 1은 본 발명에 사용되는 통상적인 내열 전기로의 개략도로, 풍화조초 산호사를 밀폐로내에서 소성가공하여 강알카리성 분말로 미세하게 분쇄하고, 분쇄된 산호알갱이(1)를 촉매기능을 수행할 수 있는 활성탄소(2)와 함께 주입구(3)와 배출구(4) 및 두쌍의 교류전극(5) 및 변압기(6), 온도제어기(7), 컨버터(8) 등을 갖춘 내열전기로(4) 내에 투입하고 가열하도록 구성된다.Figure 1 is a schematic diagram of a typical heat-resistant electric furnace used in the present invention, in which weathered coral sand is sintered and processed in a sealed furnace to finely crush it into a strong alkaline powder, and the crushed coral grains (1) are fed into a heat-resistant electric furnace (4) equipped with an inlet (3), an outlet (4), two pairs of AC electrodes (5), a transformer (6), a temperature controller (7), a converter (8), etc., and heated together with activated carbon (2) capable of performing a catalytic function.
도 2는 본 발명에 따른 산호칼슘영양소의 제조 공정도로, 천연 풍화조초 산호사를 정제수에 침수시켜 고농도칼슘, 이온화칼슘성분의 흡수성을 좋게 하고, 천연 풍화조초 산호사를 밀폐로내에서 1000℃-1300℃로 8-10시간 소성가공하여 강알카리성 분말로 분쇄하며, 알콜주정으로 가공하여 구연산과립상 100g, 알콜 10ℓ, 산호분미립자 500g을 95-110℃에서 4시간 동안 중탕 교반 가열후 분말로 분쇄하고, 97-100℃ 압력용기에서 6시간 동안 농축되게 가열하여 연질캡슐형태로 정제한다.Figure 2 is a process diagram for manufacturing coral calcium nutrients according to the present invention. Natural weathered coral sand is immersed in purified water to improve the absorbency of high-concentration calcium and ionized calcium components, the natural weathered coral sand is calcined in a sealed furnace at 1000-1300℃ for 8-10 hours and ground into a strongly alkaline powder, and processed with alcohol. 100 g of citric acid granules, 10 ℓ of alcohol, and 500 g of coral powder fine particles are stirred and heated in a double boiler at 95-110℃ for 4 hours, then ground into powder, and concentrated and heated in a pressure vessel at 97-100℃ for 6 hours and purified into a soft capsule form.
단, 상기 중탕교반시 초음파로 진동시켜 내부에서 추출물이 빠져나오도록 설정할 수 있다.However, the above double boiling stirring can be set to vibrate with ultrasonic waves so that the extract comes out from inside.
단, 상기 강알카리분말 90중량비%에 구연산 과립상 10중량비%를 첨가한다. However, 10 weight % of citric acid granules is added to 90 weight % of the above strong alkaline powder.
천연 풍화조초 산호사를 정제수에 침수시켜 고농도칼슘, 이온화칼슘성분의 흡수성이 우수해지도록 제조하고, 바다에서 채취한 천연산호사를 깨끗하게 세척, 건조후 이를 분쇄기나 파쇄기 및 믹싱기를 이용하여 미세하게 분쇄한다.Natural weathered coral sand is soaked in purified water to produce a product with excellent absorbability of high-concentration calcium and ionized calcium components. Natural coral sand collected from the sea is thoroughly washed, dried, and then finely ground using a crusher, shredder, or mixer.
상기 천연산호사는 긴세월 동안 풍화되고 물결의 작용으로 침식되어 덩어리 또는 입상이 되어 해저에 퇴적한 것으로, 유공충의 겉껍데기나 패각 등의 파편에 섞여 해저에 퇴적하며, 풍화에 퇴적한 것이 풍화조초 산호사이고 이를 식용에 가공한 것이 산호칼슘이다.The above natural coral sand has been weathered and eroded by the action of waves over a long period of time, forming lumps or granules and depositing on the seabed. It is deposited on the seabed mixed with fragments such as the outer shells or shells of foraminifera. Weathered coral sand that has been deposited through weathering is called weathered coral sand, and coral calcium is processed for consumption.
본 발명은 도 2와 같이 풍화조초 산호사를 밀폐로내에서 1000℃-1300℃로 8-10시간 소성가공하여 강알카리성 분말로 미세하게 분쇄한다.The present invention, as shown in Fig. 2, finely grinds weathered coral sand into a strong alkaline powder by firing it in a closed furnace at 1000°C-1300°C for 8-10 hours.
그리고 분쇄된 산호알갱이(1)를 촉매기능을 수행할 수 있는 활성탄소(2)와 함께 주입구(3)와 배출구(4) 및 두쌍의 교류전극(5) 및 변압기(6), 온도제어기(7), 컨버터(8) 등을 갖춘 내열전기로(4) 내에 투입하고 가열한다.Then, the crushed coral granules (1) are placed in a heat-resistant electric furnace (4) equipped with an inlet (3), an outlet (4), two pairs of AC electrodes (5), a transformer (6), a temperature controller (7), a converter (8), etc., together with activated carbon (2) capable of performing a catalytic function, and heated.
상기에서 촉매제로 사용되는 활성탄소(2)는 야자열매의 껍질을 소각하여 얻을 수 있으며, 활성탄소(2)와 혼합된 알갱이 상태의 산호는 고열로 가열됨에 따라 미립자 상태 분말로 된다.The activated carbon (2) used as a catalyst in the above can be obtained by incinerating the shell of a palm fruit, and the granular coral mixed with the activated carbon (2) becomes a fine particle powder when heated at high temperature.
그리고 알콜주정으로 구연산과립상 100g, 알콜 10ℓ, 산호분미립자 500g을 95-110℃에서 4시간 동안 중탕 교반가열하여 부유물을 제거하고, 미립자상태의 산호분말에 함유된 활성탄소 찌꺼기를 축류팬 또는 원심팬을 회전시켜 발생하는 회전력에 의해 제거하는 것으로, 상기 중탕교반시 초음파로 진동시키면 내부에서 추출물이 빠져나오게 된다.And, by stirring and heating in a double boiler at 95-110℃ for 4 hours to remove floating matters by mixing 100g of citric acid granules, 10ℓ of alcohol, and 500g of coral powder fine particles, and removing activated carbon residue contained in the coral powder fine particles by the rotational force generated by rotating an axial fan or centrifugal fan, the extract is extracted from the inside by vibrating ultrasonic waves during the double boiler stirring.
상기 알콜주정으로 구연산과립상 100g, 알콜 10ℓ, 산호분미립자 500g을 중탕 교반 가열전에, 강알카리성분말 90중량비%에 구연산과립상 10중량비%를 첨가하여 9:1 중량비%로 중성화를 이룬다.Before heating in a double boiler by stirring 100 g of citric acid granules, 10 liters of alcohol, and 500 g of coral powder fine particles, 10 wt% of citric acid granules are added to 90 wt% of strong alkaline component powder to neutralize at a wt% of 9:1.
다음에, 97-100℃ 압력용기에서 6시간 교반 농축되게 가열하여 연질캡슐형태로 정제하는데, 미립자상태 산호분말과 양조주에 함유된 알콜이 상호이온반응을 일으킴과 동시에 양조주의 용액이 투명한 적색상태로 변색된다.Next, it is heated in a pressure vessel at 97-100℃ for 6 hours to be stirred and concentrated, and purified into a soft capsule form. At the same time, the fine particle coral powder and the alcohol contained in the brewed liquor undergo a mutual ionic reaction, and the brewed liquor solution changes color to a transparent red state.
상기 용액을 상온에서 대략 30분 동안 서냉하며 용액에 혼탁한 상태로 함유된 미립자를 침전시키고 미립자를 제외한 상태에서 용액을 분리하여 연질캡슐형태로 정제한 칼슘영양소는 인체에 유익한 칼슘 즉, 천연산호사에 함유된 칼슘과 타닌이 함유된다.The above solution is cooled at room temperature for approximately 30 minutes to precipitate the fine particles contained in the turbid state in the solution, and the solution is separated with the fine particles excluded. The calcium nutrient purified in the form of a soft capsule contains calcium that is beneficial to the human body, i.e. calcium and tannin contained in natural coral sand.
이하, 본 발명의 완성된 칼슘영양소의 사용 실시예에 대해 설명한다.Hereinafter, examples of use of the completed calcium nutrient of the present invention will be described.
[실시예 1][Example 1]
알콜농도 13%이상을 함유한 술 100%에 대해 본 발명에 의해 제조된 산호칼슘영양소 0001%를 용해하면 칼슘영양소와 술에 함유된 알콜이 반응하며, 산성을 가진 술은 알칼리성으로 변화된다.When 0001% of coral calcium nutrient manufactured by the present invention is dissolved in 100% of alcohol containing 13% or more alcohol, the calcium nutrient reacts with the alcohol contained in the alcohol, and the acidic alcohol changes into alkaline.
[실시예 2][Example 2]
장기간 보관하여 산화변질되어 변색된 채소류와 과일류를 본 발명에 따른 칼슘영양소를 소정량 떨어뜨린 후 소정량의 산호칼슘영양소가 용해된 물로 세척하면 산화된 채소류와 과일류는 최초 상태로 환원되고, 변색되었던 색상도 원래의 색상대로 환색되는데, 이는 칼슘영양소에 함유된 타닌에 의한 것이다.When vegetables and fruits that have been stored for a long period of time and have oxidized and discolored are washed with water in which a predetermined amount of a calcium nutrient according to the present invention has been dropped and a predetermined amount of a coral calcium nutrient has been dissolved, the oxidized vegetables and fruits are restored to their original state and the discolored color is restored to its original color. This is due to the tannin contained in the calcium nutrient.
[실시예 3][Example 3]
본 발명의 산호칼슘영양소 100cc를 물3ℓ∼5ℓ에 용해한 상태에서 장기간 음료대용으로 복용할 수 있다.The coral calcium nutrient of the present invention, 100 cc, can be dissolved in 3 to 5 liters of water and taken as a long-term beverage substitute.
상기와 같은 본 발명의 실시예는 이에 국한되는 것은 아니며, 본 발명이 속하는 기술분야에서 다양하게 변형되어 유용하게 적용할 수 있음은 물론이다.The above-described embodiments of the present invention are not limited thereto, and it goes without saying that the present invention can be modified in various ways and usefully applied in the technical field to which the present invention belongs.
1:산호알갱이 2:활성탄소
3:주입구 4:배출구
5:교류전극 6:변압기
7:온도제어기 8:컨버터1:Coral granules 2:Activated carbon
3:Inlet 4:Outlet
5: AC electrode 6: Transformer
7: Temperature controller 8: Converter
Claims (2)
A method for manufacturing coral calcium nutrients, characterized in that natural weathered coral sand is submerged in purified water to remove salt, calcined in a sealed furnace at 1000-1300℃ for 8-10 hours, ground into a strongly alkaline powder, processed with alcohol, and 100 g of citric acid granules, 10 ℓ of alcohol, and 500 g of coral powder fine particles are heated in a double boiler at 95-110℃ for 4 hours, and then stirred and heated in a pressure vessel at 97-100℃ for 6 hours to refine into a soft capsule form, and the mixture is vibrated ultrasonically during the double boiler stirring so that the extract is extracted from the inside.