KR20240090293A - Tobacco sheet for non-combustion heating type flavor inhaler, non-combustion heating type flavor inhaler, and non-combustion heating type flavor inhalation system - Google Patents

Abstract

The present invention relates to a tobacco sheet for a non-combustible heated flavor inhaler comprising a fibrous material.

Description

Tobacco sheet for non-combustion heating type flavor inhaler, non-combustion heating type flavor inhaler, and non-combustion heating type flavor inhalation system

The present invention relates to a tobacco sheet for a non-combustion heating type flavor inhaler, a non-combustion heating type flavor inhaler, and a non-combustion heating type flavor inhalation system.

In combustion type flavor inhalers (cigarettes), flavor is obtained by burning tobacco filling including leaf tobacco or tobacco sheets. For example, Patent Document 1 discloses a tobacco sheet used in a combustion type flavor inhaler. As an alternative to the combustion type flavor inhaler, a non-combustion heating type flavor inhaler has been proposed in which flavor is obtained by heating a flavor source such as a cigarette sheet instead of burning it. The heating temperature of the non-combustion heating type flavor inhaler is lower than the combustion temperature of the combustion type flavor inhaler, for example, about 400° C. or lower. In this way, since the heating temperature of the non-combustion heating type flavor inhaler is low, an aerosol generator can be added to the flavor source in the non-combustion heating type flavor inhaler from the viewpoint of increasing the amount of smoke. The aerosol generator is vaporized by heating and generates an aerosol. Since the aerosol is supplied to the user along with flavor components such as tobacco components, the user can obtain sufficient flavor.

The non-combustion heated flavor inhaler may include, for example, a tobacco-containing segment filled with a tobacco sheet, a cooling segment, and a filter segment. The axial length of the tobacco-containing segment of a non-combustion heating type flavor inhaler is usually shorter than the axial length of the tobacco-containing segment of a combustion type flavor inhaler in relation to the heating heater. Therefore, in the non-combustion heating type flavor inhaler, a large amount of tobacco sheets are filled in the section of the short tobacco-containing segment to ensure the amount of aerosol generated during heating. In order to fill a large amount of tobacco sheets within a short period, tobacco sheets with low bulkiness, that is, high density, are usually used in non-combustion heating type flavor inhalers. In addition, the expansion property is a value representing the volume when a piece of a tobacco sheet of a certain mass is compressed at a certain pressure for a certain time. For example, Patent Document 2 discloses a tobacco sheet used in a non-combustion heating type flavor inhaler.

Japanese Patent Publication No. 60-45914 Japanese Patent Publication No. 5969923

However, the present inventors found that when considering the heating method or heater's heating ability and aerosol generation, the total heat capacity of the tobacco-containing segment increases when a tobacco sheet with low expansion (high density) is used, so the ability of the heating method or heater Accordingly, it was found that tobacco sheets filled with tobacco-containing segments did not contribute sufficiently to aerosol generation. In order to solve this problem, it is conceivable to reduce the total heat capacity of the tobacco-containing segment.

The present inventors, in order to reduce the total heat capacity of the tobacco-containing segment, (1) reduce the specific heat of the tobacco raw material contained in the tobacco sheet, (2) use a tobacco sheet with high swelling (low density). reviewed. However, since it is difficult to reduce the specific heat of the tobacco raw material itself with respect to (1), it was considered effective to reduce the total heat capacity of the tobacco-containing segments through (2). Therefore, there is a need to develop a tobacco sheet with high expansion properties (low density) that can be suitably used in a non-combustion heating type flavor inhaler.

The purpose of the present invention is to provide a tobacco sheet for a non-combustion heating type flavor inhaler with high expansion properties, a non-combustion heating type flavor inhaler comprising the tobacco sheet, and a non-combustion heating type flavor inhalation system.

The present invention includes the following embodiments.

Mode 1

A tobacco sheet for a non-combustible heated flavor inhaler comprising a fibrous material.

Mode 2

The sheet according to aspect 1, wherein the arithmetic mean surface roughness Sa of at least one side is 5 to 30 μm.

Mode 3

The sheet according to aspect 1 or 2, which is a pressure formed sheet.

Mode 4

The sheet according to any one of Aspects 1 to 3, comprising a cellulose derivative having a degree of substitution of 0.65 or more.

Mode 5

The sheet according to aspect 4, wherein the degree of substitution is 0.7 or more.

Mode 6

A tobacco-containing segment comprising a tobacco sheet for a non-combustible heated flavor inhaler according to any one of aspects 1 to 5.

A non-combustion heating type flavor aspirator having a.

Mode 7

A non-combustion heating type flavor inhaler according to Embodiment 6,

Heating device for heating the tobacco-containing segments

A non-combustion heated flavor aspiration system comprising a.

According to the present invention, it is possible to provide a tobacco sheet for a non-combustion heating type flavor inhaler with high expansion properties, a non-combustion heating type flavor inhaler comprising the tobacco sheet, and a non-combustion heating type flavor inhalation system.

Fig. 1 is a cross-sectional view showing an example of a non-combustion heating type flavor inhaler according to the present embodiment.
Figure 2 is an example of the non-combustion heating type flavor aspiration system according to the present embodiment, (a) the state before inserting the non-combustion heating type flavor aspirator into the heating device, (b) the non-combustion heating type flavor aspirator being inserted into the heating device. This is a cross-sectional view showing the state of insertion and heating.
Figure 3 is a diagram showing one aspect of a tobacco segment.

[Cigarette sheet for non-combustible heated flavor inhaler]

The tobacco sheet (hereinafter also referred to as “cigarette sheet”) for a non-combustion heating type flavor inhaler according to the present embodiment contains a fibrous material. Since the tobacco sheet according to the present embodiment contains a fibrous material, it is bulky and has high expansion properties. Therefore, by using the tobacco sheet according to the present embodiment, the total heat capacity of the tobacco-containing segment can be reduced, and the tobacco sheet filled in the tobacco-containing segment can sufficiently contribute to aerosol generation. In addition, the tobacco sheet according to the present embodiment preferably further contains a tobacco raw material, an aerosol generator, and a molding agent, and by keeping the mixing ratio of these within a predetermined range, the puffiness of the tobacco sheet is further improved.

(Fiber-like material)

The fibrous material contained in the tobacco sheet according to the present embodiment is not particularly limited as long as it is a material having a fibrous shape such as a fiber. Examples of the fibrous material include fibrous pulp, fibrous tobacco material, and fibrous synthetic cellulose. These may be used one type, or two or more types may be used together. Among these, fibrous pulp is preferable as the fibrous material from the viewpoint of fiber rigidity.

The proportion of fibrous material contained in 100% by mass of the tobacco sheet is preferably 5 to 50% by mass. When the ratio of the fiber-like material is 5% by mass or more, a large volume capable of ensuring function can be realized. Additionally, when the ratio of the fiber-like material is 50% by mass or less, sufficient tobacco scent and aerosol can be generated during heating. The proportion of the fibrous material is more preferably 5 to 47% by mass, more preferably 5 to 45% by mass, and particularly preferably 5 to 40% by mass.

(tobacco raw materials)

When the fibrous material is other than the fibrous tobacco material, the tobacco sheet according to this embodiment may further contain a tobacco raw material. The tobacco raw material is not particularly limited as long as it contains tobacco components, but examples include tobacco powder and tobacco extract. Examples of tobacco powder include leaf tobacco, midribs, remaining stems, etc. These may be used one type, or two or more types may be used together. These can be used as tobacco powder by cutting them into a predetermined size. As for the size of the tobacco powder, it is preferable that the cumulative 90% particle size (D90) in the volume-based particle size distribution measured by dry laser diffraction is 200 ㎛ or more from the viewpoint of further improvement in swelling properties. Examples of the tobacco extract include, for example, a tobacco extract obtained by crushing leaf tobacco, extracting water-soluble components from leaf tobacco by mixing and stirring this with a solvent such as water, and drying and concentrating the obtained water extract under reduced pressure.

The proportion of tobacco raw materials contained in 100% by mass of the tobacco sheet is preferably 30 to 91% by mass. When the proportion of the tobacco raw material is 30% by mass or more, a tobacco aroma can be sufficiently generated during heating. In addition, when the proportion of the tobacco raw material is 91% by mass or less, a sufficient amount of aerosol generator or molding agent can be contained. As for the ratio of the said tobacco raw material, it is more preferable that it is 50-90 mass %, it is still more preferable that it is 55-85 mass %, and it is especially preferable that it is 60-80 mass %.

(molding agent)

When the fibrous material is other than a fibrous molding agent such as fibrous synthetic cellulose, it is preferable that the tobacco sheet according to this embodiment further contains a molding agent from the viewpoint of securing the shape. Examples of molding agents include polysaccharides, proteins, and synthetic polymers. These may be used one type, or two or more types may be used together. Examples of polysaccharides include cellulose derivatives and naturally occurring polysaccharides.

Cellulose derivatives include, for example, methylcellulose, ethylcellulose, hydroxyethylcellulose, hydroxymethylethylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, benzylcellulose, tritylcellulose, cyanoethylcellulose, carboxymethylcellulose, and carboxyethyl. Cellulose ethers such as cellulose and aminoethylcellulose; Organic acid esters such as cellulose acetate, cellulose formate, cellulose propionate, cellulose butyrate, cellulose benzoate, cellulose phthalate, and tosylcellulose; Inorganic acid esters such as cellulose nitrate, cellulose sulfate, cellulose phosphate, and cellulose xanthogenate can be mentioned.

Natural polysaccharides include, for example, guar gum, tara gum, locust bean gum, tamarind seed gum, pectin, gum arabic, gum tragacanth, gum karaya, gum gathi, arabinogalactan, gum flax seed, gum cassia, and psyllium seed. Polysaccharides derived from plants such as gum and yellow sea mugwort seed gum; Polysaccharides derived from algae such as carrageenan, agar, alginic acid, alginic acid propylene glycol ester, percellaran, and vulgaris extract; Polysaccharides derived from microorganisms such as xanthan gum, gellan gum, curdlan, pullulan, Agrobacterium succinoglycan, whelan gum, macrophomopsis gum, and Ramzan gum; Polysaccharides derived from crustaceans such as chitin, chitosan, and glucosamine; Starches such as starch, sodium starch glycolate, pregelatinized starch, and dextrin can be mentioned.

Examples of proteins include grain proteins such as wheat gluten and rye gluten. Examples of synthetic polymers include polyphosphoric acid, sodium polyacrylate, and polyvinylpyrrolidone.

When the tobacco sheet contains a molding agent, the proportion of the molding agent contained in 100% by mass of the tobacco sheet is preferably 0.1 to 15% by mass. When the ratio of the molding agent is 0.1% by mass or more, the mixture of raw materials can be easily molded into a sheet shape. In addition, when the proportion of the molding agent is 15% by mass or less, other raw materials can be sufficiently used to ensure the functions required for the tobacco-containing segment of the non-combustion heating type flavor inhaler. The proportion of the molding agent is more preferably 0.2 to 13 mass%, more preferably 0.5 to 12 mass%, and particularly preferably 1 to 10 mass%.

(Aerosol generator)

It is preferable that the tobacco sheet according to this embodiment further contains an aerosol generator from the viewpoint of increasing the amount of smoke when heated. Examples of aerosol generators include glycerin, propylene glycol, and 1,3-butanediol. These may be used one type, or two or more types may be used together.

When the tobacco sheet contains an aerosol generator, the proportion of the aerosol generator contained in 100 mass% of the tobacco sheet is preferably 5 to 50 mass%. When the proportion of the aerosol generator is 5% by mass or more, sufficient aerosol can be generated during heating from the viewpoint of quantity. Additionally, when the proportion of the aerosol generator is 50% by mass or less, sufficient aerosol can be generated during heating from the viewpoint of heat capacity. The proportion of the aerosol generator is more preferably 6 to 45% by mass, more preferably 8 to 40% by mass, and particularly preferably 10 to 30% by mass.

(Reinforcement agent)

When the fibrous material is other than a fibrous reinforcing agent such as fibrous pulp, the tobacco sheet according to the present embodiment may further contain a reinforcing agent from the viewpoint of further improving physical properties. Examples of reinforcing agents include liquid substances with a surface coating function that form a film when dried, such as pulp and pectin suspension. These may be used one type, or two or more types may be used together.

When the tobacco sheet contains a reinforcing agent, the ratio of the reinforcing agent contained in 100 mass% of the tobacco sheet is preferably 0.1 to 20 mass%. When the ratio of the reinforcing agent is within this range, other raw materials can be sufficiently used to ensure the functions required for the tobacco-containing segment of the non-combustion heating type flavor inhaler. As for the ratio of the said reinforcing agent, it is more preferable that it is 0.2-18 mass %, and it is still more preferable that it is 0.5-15 mass %.

(Moisturizer)

The tobacco sheet according to this embodiment may further contain a moisturizing agent from the viewpoint of quality maintenance. Examples of moisturizing agents include sugar alcohols such as sorbitol, erythritol, xylitol, maltitol, lactitol, mannitol, and reduced maltose syrup. These may be used one type, or two or more types may be used together.

When the tobacco sheet contains a humectant, the ratio of the humectant contained in 100 mass% of the tobacco sheet is preferably 1 to 15 mass%. Within this range, other raw materials can be sufficiently used to ensure the functions required for the tobacco-containing segment of the non-combustion heated flavor inhaler. The ratio of the above-mentioned moisturizer is more preferably 2 to 12% by mass, and even more preferably 3 to 10% by mass.

(Other Ingredients)

The tobacco sheet according to the present embodiment contains, in addition to the fibrous material, the tobacco raw material, the molding agent, the aerosol generating agent, the reinforcing agent, and the moisturizing agent, flavoring agents such as fragrances and flavoring agents, and colorants as necessary. , may include diluents such as wetting agents, preservatives, and inorganic substances.

(Paeng Sung-seong)

The expansion property of the tobacco sheet according to this embodiment is preferably 190 cc/100 g or more. When the expansion property is 190 cc/100 g or more, the total heat capacity of the tobacco-containing segment of the non-combustion heating type flavor inhaler can be sufficiently reduced, and the tobacco sheet filled in the tobacco-containing segment can contribute more to aerosol generation. The swelling property is more preferably 210cc/100g or more, and even more preferably 230cc/100g or more. The upper limit of the swelling range is not particularly limited, but may be, for example, 800 cc/100 g or less. In addition, the paper was recut into a size of 0.8 mm It is a value measured by . The measurement is performed by placing 15 g of the recut tobacco sheet in a cylindrical container with an inner diameter of 60 mm and determining the volume when compressed with a 3 kg load for 30 seconds.

(Composition of cigarette sheet)

In this embodiment, a 'cigarette sheet' means the components constituting the tobacco sheet are molded into a sheet shape. Here, the term 'sheet' refers to a shape having a pair of substantially parallel main surfaces and side surfaces. The length and width of the tobacco sheet are not particularly limited and can be adjusted appropriately according to the filling mode. The thickness of the tobacco sheet is not particularly limited, but is preferably 100 to 1000 μm, and more preferably 150 to 600 μm, in terms of balance between heat transfer efficiency and strength.

(Method of manufacturing cigarette sheets)

The tobacco sheet according to the present embodiment can be manufactured by known methods such as rolling and casting, for example. Details of various tobacco sheets manufactured by this method are disclosed in 'Tobacco Dictionary, Tobacco Research Center, March 31, 2009'.

<Rolling method>

Examples of a method for producing a tobacco sheet by the rolling method include a method including the following steps.

(1) A process of obtaining a mixture by mixing water, tobacco powder, an aerosol generator, a molding agent, and fibrous pulp.

(2) A process of putting the mixture into rolling rollers and rolling it.

(3) A process of peeling the rolled product on the rolling roller with a doctor knife, transferring it to a net conveyor, and drying it in a dryer.

When manufacturing a tobacco sheet by this method, depending on the purpose, the surface of each rolling roller may be heated or cooled, and the rotation speed of each rolling roller may be adjusted. Additionally, by adjusting the spacing between each rolling roller, a tobacco sheet with a desired basis weight can be obtained.

<Cast method>

Examples of a method for producing a tobacco sheet by a casting method include a method including the following steps.

(1) A process of obtaining a mixture by mixing water, tobacco powder, an aerosol generator, a molding agent, and fibrous pulp.

(2) A process of spreading (casting) the mixture thinly, drying it, and forming a tobacco sheet.

When manufacturing tobacco sheets by this method, some components such as nitrosamines are removed by irradiating ultraviolet rays or Additional processes may be added.

[Non-combustion heated flavor aspirator]

The non-combustion heating type flavor inhaler according to the present embodiment is provided with a tobacco-containing segment including the tobacco sheet according to the present embodiment. Since the non-combustion heating type flavor inhaler according to the present embodiment is provided with a tobacco-containing segment filled with the highly expanding tobacco sheet according to the present embodiment, the total heat capacity of the tobacco-containing segment can be sufficiently reduced, and the tobacco-containing The tobacco sheets filled in the segments can contribute more to aerosol generation.

An example of a non-combustion heating type flavor aspirator according to the present embodiment is shown in FIG. 1. The non-combustion heating type flavor aspirator 1 shown in FIG. 1 is a cylindrical cooling device including a tobacco-containing segment 2 filled with the tobacco sheet according to the present embodiment and perforations 8 on the circumference. It is provided with a segment (3), a center hole segment (4), and a filter segment (5). The non-combustion heating type flavor inhaler according to the present embodiment may include other segments in addition to the tobacco-containing segment, cooling segment, center hole segment, and filter segment.

The axial length of the non-combustion heating type flavor aspirator according to the present embodiment is not particularly limited, but is preferably 40 mm or more and 90 mm or less, more preferably 50 mm or more and 75 mm or less, and even more preferably 50 mm or more and 60 mm or less. In addition, the circumferential length of the non-combustion heating type flavor aspirator is preferably 16 mm or more and 25 mm or less, more preferably 20 mm or more and 24 mm or less, and even more preferably 21 mm or more and 23 mm or less. For example, the tobacco containing segment may have a length of 20 mm, the cooling segment may have a length of 20 mm, the center hole segment may have a length of 8 mm, and the filter segment may have a length of 7 mm. Additionally, the length of the filter segment can be selected within the range of 4 mm or more and 10 mm or less. Additionally, the ventilation resistance of the filter segment at that time is selected to be 15 mmH ₂ O/seg or more and 60 mmH ₂ O/seg or less per segment. The length of these individual segments can be appropriately changed depending on manufacturing suitability, required quality, etc. Furthermore, even if only a filter segment is placed on the downstream side of the cooling segment without using a center hole segment, it can function as a non-combustion heating type flavor aspirator.

(Tobacco-containing segment)

The tobacco-containing segment 2 is filled with the tobacco sheet according to the present embodiment in a wrapper (hereinafter also referred to as a "wrapper"). The method of filling the tobacco sheet into the wrapper is not particularly limited, but for example, the tobacco sheet may be wrapped with a wrapper, or the tobacco sheet may be filled into a cylindrical wrapper. When the shape of the tobacco sheet has a longitudinal direction such as a rectangular shape, the tobacco sheet may be filled so that the longitudinal direction is each in an unspecified direction within the wrapper, and may be in the axial direction of the tobacco-containing segment 2 or in the axial direction. The batteries may be aligned and charged in a direction perpendicular to each other.

(cooling segment)

As shown in FIG. 1 , the cooling segment 3 may be comprised of a cylindrical member 7 . The cylindrical member 7 may be, for example, a paper tube obtained by processing thick paper into a cylindrical shape.

The cylindrical member 7 and the mouthpiece lining paper 12 described later are provided with perforations 8 penetrating both. Due to the presence of perforations 8, external air is introduced into the cooling segment 3 during suction. As a result, the aerosol vaporization component generated by heating the tobacco-containing segment 2 comes into contact with the outside air and is liquefied because its temperature is lowered, thereby forming an aerosol. The diameter (diameter length) of the perforation 8 is not particularly limited, but may be, for example, 0.5 mm or more and 1.5 mm or less. The number of perforations 8 is not particularly limited and may be one or two or more. For example, a plurality of perforations 8 may be provided on the circumference of the cooling segment 3.

The amount of external air introduced from the perforation 8 is preferably 85 volume% or less, and more preferably 80 volume% or less, relative to the total volume of gas sucked by the user. When the ratio of the amount of outside air is 85 volume% or less, reduction in flavor due to dilution by outside air can be sufficiently suppressed. In addition, this is also called ventilation ratio in another expression. From the viewpoint of cooling properties, the lower limit of the ventilation ratio range is preferably 55 volume% or more, and more preferably 60 volume% or more.

Additionally, the cooling segment may be a segment comprising sheets of suitable construction material that are wrinkled, pleated, gathered, or folded. The cross-sectional profile of such elements may show randomly oriented channels. The cooling segment may also comprise a bundle of longitudinal extending tubes. Such cooling segments can be formed, for example, by pleating, gathering, or wrapping the folded sheet material into a wrapper.

The axial length of the cooling segment may be, for example, 7 mm or more and 28 mm or less, for example, 18 mm. The cooling segment may also be substantially circular in its axial cross-sectional shape, and its diameter may be, for example, 5 mm or more and 10 mm or less, for example, about 7 mm.

(center hole segment)

The center hole segment is composed of a filled layer including one or more hollow portions and an inner plug wrapper (inner wrapper) covering the filled layer. For example, as shown in FIG. 1, the center hole segment 4 is composed of a second filling layer 9 including a hollow portion and a second inner plug wrapper 10 covering the second filling layer 9. . The center hole segment 4 has the function of increasing the strength of the mouthpiece segment 6. The second filled layer 9 is, for example, filled with cellulose acetate fibers at a high density, and has an inner diameter of ϕ1.0 mm or more, where a plasticizer containing triacetin is added in an amount of 6% by mass or more and 20% by mass or less relative to the mass of cellulose acetate, and hardened. It can be done with a rod of ϕ5.0mm or less. Since the second packed layer 9 has a high packing density of fibers, during suction, air or aerosol flows only through the hollow portion and hardly flows inside the second packed layer 9. Since the second filled layer 9 inside the center hole segment 4 is a fiber filled layer, the tactile sensation from the outside during use rarely causes discomfort to the user. Additionally, the center hole segment 4 may not include the second inner plug wrapper 10 and may maintain its shape by thermoforming.

(filter segment)

The structure of the filter segment 5 is not particularly limited, but may be composed of a single or plural filled layer. The outside of the filling layer may be covered with one or multiple sheets of wrapper. The per-segment ventilation resistance of the filter segment 5 can be appropriately changed depending on the amount and material of the filler filled in the filter segment 5. For example, when the filling is cellulose acetate fiber, increasing the amount of cellulose acetate fiber filled in the filter segment 5 can increase ventilation resistance. When the filling is cellulose acetate fiber, the packing density of the cellulose acetate fiber may be 0.13 to 0.18 g/cm3. In addition, ventilation resistance is a value measured by a ventilation resistance meter (product name: SODIMAX, manufactured by SODIM).

The circumferential length of the filter segment 5 is not particularly limited, but is preferably 16 to 25 mm, more preferably 20 to 24 mm, and even more preferably 21 to 23 mm. The axial length of the filter segment 5 can be selected from 4 to 10 mm, and is selected so that its ventilation resistance is 15 to 60 mmH ₂ O/seg. The axial length of the filter segment 5 is preferably 5 to 9 mm, and more preferably 6 to 8 mm. The cross-sectional shape of the filter segment 5 is not particularly limited, but may be, for example, circular, oval, polygonal, etc. Additionally, destructible capsules containing fragrance, fragrance beads, or fragrance may be added directly to the filter segment 5.

As shown in Fig. 1, the center hole segment 4 and the filter segment 5 can be connected with an outer plug wrapper (outer wrapper) 11. The outer plug wrapper 11 may be, for example, cylindrical paper. Additionally, the tobacco-containing segment 2, the cooling segment 3, and the connected center hole segment 4 and filter segment 5 can be connected by a mouthpiece lining paper 12. These can be connected, for example, by applying glue such as vinyl acetate glue to the inner surface of the mouthpiece lining paper 12 and wrapping the three segments. Additionally, these segments may be divided and connected multiple times with a plurality of lining papers.

[Non-combustion heated flavor aspiration system]

The non-combustion heating type flavor aspiration system according to the present embodiment includes a non-combustion heating type flavor aspirator according to the present embodiment, and a heating device that heats the tobacco-containing segment of the non-combustion heating type flavor aspirator. The non-combustion heating type flavor aspiration system according to the present embodiment may have other configurations in addition to the non-combustion heating type flavor aspirator and the heating device according to the present embodiment.

An example of a non-combustion heating type flavor aspiration system according to the present embodiment is shown in FIG. 2. The non-combustion heating type flavor aspiration system shown in FIG. 2 includes a non-combustion heating type flavor aspirator 1 according to the present embodiment, and a heating device that heats the tobacco-containing segment of the non-combustion heating type flavor aspirator 1 from the outside ( 13) is provided.

Figure 2 (a) shows the state before inserting the non-combustion heating type flavor aspirator 1 into the heating device 13, and Figure 2 (b) shows the non-combustion heating type flavor aspirator 1 with a heating device ( 13) indicates the state of heating. The heating device 13 shown in FIG. 2 includes a body 14, a heater 15, a metal tube 16, a battery unit 17, and a control unit 18. The body 14 includes a cylindrical recess 19, the inner side of the recess 19 corresponding to the tobacco-containing segment of the non-combustion heated flavor aspirator 1 inserted into the recess 19. The heater 15 and the metal tube 16 are placed at the position. The heater 15 may be a heater based on electrical resistance, and power is supplied from the battery unit 17 in response to instructions from the control unit 18 that performs temperature control, thereby heating the heater 15. The heat generated from the heater 15 is transmitted to the tobacco-containing segment of the non-combustion heated flavor inhaler 1 through a metal tube 16 with high thermal conductivity.

In Figure 2(b), since it is schematically shown, there is a gap between the outer periphery of the non-combustion heating type flavor aspirator 1 and the inner periphery of the metal pipe 16, but in reality, For the purpose of efficiently transferring heat, it is preferable that there is no gap between the outer circumference of the non-combustion heating type flavor aspirator (1) and the inner circumference of the metal tube (16). In addition, the heating device 13 heats the tobacco-containing segment of the non-combustion heating type flavor inhaler 1 from the outside, but may heat it from the inside.

The heating temperature by the heating device is not particularly limited, but is preferably 400°C or lower, more preferably 150°C or higher and 400°C or lower, and even more preferably 200°C or higher and 350°C or lower. In addition, the heating temperature refers to the temperature of the heater of the heating device.

Additionally, excellent processability is required for tobacco sheets. Sheets manufactured by the paper-making method are composed of fibrous tobacco leaf residue, and therefore have excellent strength, but the surface smoothness is not sufficient. In addition, since sheets manufactured by the casting method are dried as wet sheets in a moisture-rich state, bubbles are generated on the surface due to steam generation during drying. In addition, the smoothness is not at a sufficient level due to the end of the wet sheet shrinking during the process of evaporation of moisture and shrinkage of the wet sheet. Additionally, when fibrous materials are mixed, the materials are entangled to form blobs, which also impairs the smoothness of the sheet surface. Typically, tobacco sheets are subjected to processing such as molding or cutting and are provided as smoking articles. During this processing, if the surface of the tobacco sheet is not sufficiently smooth, problems such as breakage of the sheet when it comes into contact with the processing device may occur. Accordingly, as a first aspect, a tobacco sheet having excellent processability in addition to high expansion properties will be described below.

In addition, conventional cigarette sheets generate fine particles called fallen shreds during or after use, causing handling problems such as adhesion to clothing. Therefore, if piece falling off can be reduced, handleability can be improved. Hereinafter, as a second embodiment, a tobacco sheet with high expansion properties and reduced flaking will be described below.

[First mode]

The tobacco sheet in this embodiment includes at least a tobacco material and a binder.

(1) Binder

A binder is a type of molding agent described above and is an adhesive used to bind tobacco materials together or tobacco materials and other components. In this embodiment, a known binder can be used. Examples of such binders include polysaccharides such as guar gum and xanthan gum, and cellulose derivatives such as CMC (carboxymethylcellulose), CMC-Na (sodium salt of carboxymethylcellulose), and HPC (hydroxypropylcellulose). The upper limit of the binder content is preferably 6% by mass or less in terms of dry mass (mass excluding mixed water, hereinafter the same) relative to the dry mass of the tobacco sheet, and the lower limit is preferably 1% by mass or more, More preferably, it is 3% by mass or more. If the amount of binder exceeds the upper limit or is less than the lower limit, the above effect may not be sufficiently achieved.

Binders used in this embodiment include polysaccharides, proteins, and synthetic polymers. Below, these specific examples are shown. In this embodiment, these binders can also be used in combination.

1) Polysaccharides

1-1) Cellulose derivatives

[Cellulose ethers]

Methylcellulose, ethylcellulose, hydroxyethylcellulose, hydroxymethylethylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, benzylcellulose, tritylcellulose, cyanoethylcellulose, carboxymethylcellulose, carboxyethylcellulose, aminoethyl cellulose

[Cellulose esters]

Organic acid esters: cellulose acetate, cellulose formate, cellulose propionate, cellulose butyrate, cellulose benzoate, cellulose phthalate, tosylcellulose

Inorganic acid esters: cellulose nitrate, cellulose sulfate, cellulose phosphate, cellulose xanthine

1-2) Naturally derived polysaccharides

[Plant derived]

Guar gum, tara gum, locust bean gum, tamarind seed gum, pectin, gum arabic, gum tragacanth, gum karaya, gum gati, arabinogalactan, flax seed gum, cassia gum, psyllium seed gum, yellow sea mugwort seed gum.

[Algae origin]

Carrageenan, agar, alginic acid, alginic acid propylene glycol ester, perselaran, vulgaris extract

[Origin from microorganisms]

Xanthan gum, gellan gum, curdlan, pullulan, Agrobacterium succinoglycan, whelan gum, Macrophomopsis gum, Ramzan gum

[Crustacean origin]

Chitin, chitosan, glucosamine

[All categories]

Starch, sodium starch glycolate, pregelatinized starch, dextrin

2) protein

Wheat Gluten, Rye Gluten

3) Synthetic polymers

Polyphosphoric acid, sodium polyacrylate, polyvinylpyrrolidone

(2) Tobacco materials

The tobacco material used in this embodiment may be the above-mentioned fibrous tobacco material or the above-mentioned tobacco raw material. In this embodiment, as a tobacco material other than the fiber-like tobacco material, specifically, finely chopped dried tobacco leaves or pulverized leaf tobacco can be used. Pulverized leaf tobacco is particles obtained by crushing leaf tobacco. The particle size (D90) of the pulverized leaf tobacco is preferably 200 ㎛ or more as described above, but its upper limit is preferably 1000 ㎛ or less, and more preferably 50 to 500 ㎛. In addition, the average particle diameter (D50) can be preferably set to 20 to 1000 ㎛, more preferably 50 to 500 ㎛. Grinding can be performed using a known grinding machine, and may be either dry grinding or wet grinding. Therefore, leaf tobacco powder is also called leaf tobacco particles. In this embodiment, the particle size can be determined by a laser diffraction/scattering method, and is specifically measured using a laser diffraction type particle size distribution measuring device (for example, Horiba LA-950). In addition, the type of tobacco is not limited, and yellow types, burley types, oriental types, traditional types, and other varieties of the Nicotiana/tabacum family or varieties belonging to the Nicotiana/rustica family can be used. The amount of tobacco material in the tobacco sheet is not particularly limited, but is preferably 50 to 95% by mass, more preferably 60 to 90% by mass in dry mass.

(3) Aerosol generator

In this embodiment as well, known aerosol generators can be used, examples of which include polyhydric alcohols such as glycerin and propylene glycol (PG), triethyl citrate (TEC) and triacetin, which have a boiling point exceeding 100°C. You can. In this embodiment, the amount of aerosol generator in the tobacco sheet is preferably 5 to 40% by mass, more preferably 10 to 20% by mass in dry mass (mass excluding mixed water, hereinafter the same). If the amount of aerosol generator exceeds the upper limit, manufacturing of cigarette sheets may become difficult, and if it is less than the lower limit, smoke loss may decrease.

(4) Emulsifier

In this aspect, the tobacco sheet may contain an emulsifier. Emulsifiers increase the affinity between the lipophilic aerosol generator and the hydrophilic tobacco material. Therefore, the addition of an emulsifier is effective, especially when using a lipophilic aerosol generator. As the emulsifier, a known emulsifier can be used, and examples thereof include an emulsifier having an HLB value of 8 to 18. The amount of the emulsifier is not particularly limited, but is preferably 0.1 to 3 parts by mass, more preferably 1 to 2 parts by mass, in terms of dry mass, per 100 parts by mass of the tobacco sheet.

(5) Spices

In this aspect, the tobacco sheet may contain fragrance. A fragrance is a substance that provides scent or flavor. The fragrance may be a natural fragrance or a synthetic fragrance. As a fragrance, one type of fragrance may be used or a mixture of multiple types of fragrance may be used. As the flavor, any flavor commonly used in smoking articles can be used, specific examples of which will be described later. Flavoring may be included in the sheet for a smoking article in an amount such that the smoking article can provide a desirable aroma or flavor, for example, the amount thereof is preferably 1 to 30% by mass of the tobacco sheet, more preferably 1% by mass. It is 2-20% by mass.

The type of the fragrance is not particularly limited, and from the viewpoint of providing a good fragrance, acetoanisole, acetophenone, acetylpyrazine, 2-acetylthiazole, alfalfa extract (extract), amyl alcohol, amyl butyrate, trans -Anethole, star anise oil, apple juice, Peruvian balsam oil, beeswax absolute, benzaldehyde, benzoin resinoid, benzyl alcohol, benzyl benzoate, benzyl phenylacetate, benzyl propionate, 2,3-butanedione, 2-butanol, butyric acid. Butyl, butyric acid, caramel, cardamom oil, carob absolute, β-carotene, carrot juice, L-carvone, β-caryophyllene, cassia bark oil, cedarwood oil, celery seed oil, chamomile oil, cinnamaldehyde, cinnamic acid, Cinnamyl alcohol, cinnamyl cinnamate, citronella oil, DL-citronellol, clary sage extract, cocoa, coffee, cognac oil, coriander oil, cuminaldehyde, davana oil, δ-decalactone, γ-decalactone, Decanoic acid, dill herb oil, 3,4-dimethyl-1,2-cyclopentanedione, 4,5-dimethyl-3-hydroxy-2,5-dihydrofuran-2-one, 3,7-dimethyl- 6-octenoic acid, 2,3-dimethylpyrazine, 2,5-dimethylpyrazine, 2,6-dimethylpyrazine, ethyl 2-methylbutyrate, ethyl acetate, ethyl butyrate, ethyl hexanoate, ethyl isovalerate, ethyl lactate, Ethyl laurate, ethyl levulinate, ethyl maltol, ethyl octanoate, ethyl oleate, ethyl palmitate, ethyl phenyl acetate, ethyl propionate, ethyl stearate, ethyl valerate, ethyl vanillin, ethyl vanillin glucoside, 2- Ethyl-3,(5 or 6)-dimethylpyrazine, 5-ethyl-3-hydroxy-4-methyl-2(5H)-furanone, 2-ethyl-3-methylpyrazine, eucalyptol, Fenugreek absolute, Gene absolute, Gentian root infusion, geraniol, geranyl acetate, grape juice, guaiacol, guava extract, γ-heptalactone, γ-hexalactone, hexanoic acid, cis-3-hexen-1-ol, Hexyl acetate, hexyl alcohol, phenyhexyl acetate, honey, 4-hydroxy-3-pentenoic acid lactone, 4-hydroxy-4-(3-hydroxy-1-butenyl)-3,5,5-trimethyl- 2-cyclohexen-1-one, 4-(para-hydroxyphenyl)-2-butanone, sodium 4-hydroxyundecanoate, immortel absolute, β-ionone, isoamyl acetate, isobutyrate Wheat, isoamyl phenyl acetate, isobutyl acetate, isobutyl phenylacetate, jasmine absolute, kola nut tincture, labdanum oil, lemon terpeneless oil, licorice extract, linalool, linalyl acetate, ruby root oil, maltol, Maple syrup, menthol, menthone, L-menthyl acetate, para-methoxybenzaldehyde, methyl-2-pyrrolyl ketone, methyl anthranilate, methyl phenylacetate, methyl salicylate, 4'-methylacetophenone, methylcyclopentenolone, 3 -Methyl valeric acid, mimosa absolute, molasses, myristic acid, nerol, nerolidol, γ-nonalactone, nutmeg oil, δ-octalactone, octanal, octanoic acid, orange flower oil, orange oil, orris root oil, Palmitic acid, ω-pentadecalactone, peppermint oil, petitgrain Paraguay oil, phenethyl alcohol, phenyl phenyl acetate, phenylacetic acid, piperonal, plum extract, propenylguaethol, propyl acetate, 3-propyl Ridenphthalide, plum juice, pyruvic acid, raisin extract, rose oil, rum, sage oil, sandalwood oil, spearmint oil, Styrox absolute, marigold oil, tea distillate, α-terpineol, terpinenyl acetate. , 5,6,7,8-tetrahydroquinoxaline, 1,5,5,9-tetramethyl-13-oxacyclo(8.3.0.0(4.9))tridecane, 2,3,5,6-tetramethyl Pyrazine, thyme oil, tomato extract, 2-tridecanone, triethyl citrate, 4-(2,6,6-trimethyl-1-cyclohexenyl)2-buten-4-one, 2,6,6- Trimethyl-2-cyclohexen-1,4-dione, 4-(2,6,6-trimethyl-1,3-cyclohexadienyl)2-buten-4-one, 2,3,5-trimethylpyrazine, γ-undecalactone, γ-valerolactone, vanilla extract, vanillin, veratrialdehyde, violet leaf absolute, N-ethyl-p-menthane-3-carboamide (WS-3), ethyl-2-(p -Menthane-3-carboxamide) acetate (WS-5), sugar (sucrose, fructose, etc.), cocoa powder, carob powder, coriander powder, licorice powder, orange peel powder, rose hip powder, chamomile flower ( flower) powder, lemon verbena powder, peppermint powder, leaf powder, spearmint powder, black tea powder, natural vegetable fragrances (e.g. jasmine oil, lemon oil, vetiver oil, lobe oil), esters (e.g. menthyl acetate, isoamyl propionate, etc.), alcohols (e.g., phenylethyl alcohol, cis-6-nonen-1-ol, etc.). These fragrances may be used individually or in combination of two or more types.

(6) Characteristics and form of tobacco sheets

1) Arithmetic average surface roughness Sa

The tobacco sheet in this embodiment preferably has Sa of 5 to 30 μm on at least one side. Sa is an indicator of surface roughness, and when the tobacco sheet of the present embodiment has Sa in the above range, processability is excellent and flaking off from the surface is reduced. From this viewpoint, Sa is more preferably 10 to 25 μm, and even more preferably 10 to 20 μm. The tobacco sheet of this embodiment preferably has Sa in the above range on both sides.

2) Thickness

The thickness of the tobacco sheet is not limited, but in one aspect, it is preferably 20 to 2000 μm, more preferably 100 to 1500 μm, and even more preferably 100 to 1000 μm.

3) Mechanical properties

The tobacco sheet in this embodiment preferably has a tensile elongation of 2.0% or more, more preferably 3.0% or more, and even more preferably 5.0% or more. The upper limit of the tensile elongation is not limited, but is usually about 15% or less. Additionally, the tobacco sheet preferably has a tensile stress of 2.0 N/mm or more, more preferably 2.5 N/mm or more, and even more preferably 3.0 N/mm or more.

4) Handleability

The smoothness of the tobacco sheet in this embodiment affects the handleability of the product. For example, smoking articles using tobacco sheets with insufficient smoothness may generate fine powder, called flaking, during or after use, causing handling problems such as adhesion to clothing. However, since the tobacco sheet of the present invention has excellent smoothness, the occurrence of such problems can be suppressed.

(7) Tobacco segment

From tobacco sheets, tobacco segments for use in smoking articles can be manufactured. In one aspect, the tobacco segment is provided with a tubular wrapper, and the wrapper is provided with a tobacco sheet filled in a spiral shape (see Fig. 3 (A)). In the diagram, 20A is a tobacco segment, T is a tobacco sheet, and 22 is a wrapper, usually paper. The tobacco segment is preferably rod-shaped, and its length can be about 15 to 80 mm and its diameter about 5 to 10 mm. Additionally, the tobacco segment 20A shown in Fig. 3(A) can be cut so that the aspect ratio (length/diameter) is about 0.5 to 1.2 (see Fig. 3(B)).

In a separate aspect, the tobacco segment 20A is provided with a cylindrical wrapper 22, and is provided with a tobacco sheet T folded and filled within the wrapper. The ridge created by folding is approximately parallel to the longitudinal direction of the segment (see (C) in Figure 3). The tobacco segment 20A is preferably rod-shaped, and its length can be about 15 to 80 mm and its diameter about 5 to 10 mm. In this embodiment, it is preferable that surface wrinkle processing such as pleating processing or crimp processing is performed on the tobacco sheet T in advance.

The tobacco segment 20A, in a separate aspect, is provided with a tubular wrapper 22, and is provided with cut pieces Tc of the tobacco sheet filled in the wrapper (see (D) in FIG. 3). . The tobacco segment 20A is preferably rod-shaped, and its length can be about 15 to 80 mm and its diameter about 5 to 10 mm. The size of the cutting piece is not limited, but for example, the length of the longest side can be about 2 to 20 mm and the width can be about 0.5 to 1.5 mm.

In a separate aspect, the tobacco segment 20A has a cylindrical wrapper 22, and has strand-type pieces filled in the wrapper (see Fig. 3(E)). The strand-type pieces are packed so that their long direction is approximately parallel to the long direction of the wrapper 22. The width of the strand type piece can be about 0.5 to 1.5 mm.

The tobacco segment 20A, in a separate aspect, is provided with a cylindrical wrapper 22, and is provided with shredded tobacco fillings randomly filled into the wrapper. The shredded tobacco is a re-cut piece and is different from the strand-type piece.

[Manufacturing method]

The tobacco sheet in this embodiment can be manufactured by any method, but is preferably manufactured by a method comprising the following steps.

Step 1 of preparing a mixture by mixing at least a fiber-like material, a tobacco material, a binder, and a medium.

Process 2 of preparing a wet sheet by extruding the mixture from a piezoelectric (pressure-extending) die.

Step 3 of drying the wet sheet.

A sheet formed by applying pressure in this way is called a 'pressure molded sheet', and as described later, 'pressure molded sheet' includes 'laminate sheet' and 'extruded sheet'. A laminated sheet is a sheet obtained by piezoelectricizing the mixture to a target thickness with a roller one or more times and then drying it to a target moisture content. An extruded sheet is a sheet obtained by extruding a mixture to a target thickness using a T-die or the like and then drying it to a target moisture content. Piezoelectricity and extrusion may be combined in pressure forming sheets. For example, after extruding the mixture, it may be further piezoelectrically formed into a sheet.

(1) Process 1

In this process, the fiber-like material, the tobacco material, the binder, and the medium are mixed. If necessary, an aerosol generating base, emulsifier, or fragrance may be added. The compounding amount of each component is adjusted so as to achieve the above-mentioned amount. The medium is preferably made up of a water-soluble organic solvent with a boiling point of less than 100°C, such as water or ethanol, and is more preferably water or ethanol.

This process can be carried out by kneading each component, and is preferably carried out through 1) pulverization of raw materials (for example, single leaves), 2) preparation of moisture, and 3) kneading.

1) Grinding

It is preferable to coarsely crush the raw materials and then finely grind them using a grinder (for example, ACM-5, manufactured by Hosokawa Micron). The particle size (D90) after fine pulverization is preferably 20 to 1000 μm. The particle size is measured using a laser diffraction type particle size meter such as Master Sizer (manufactured by Malvern).

2) Preparation of moisture

Additives such as binders and, if necessary, flavorings or lipids are added to pulverized tobacco raw materials (e.g., tobacco particles) and mixed. Since this mixing is preferably a dry blend, it is preferable to use a mixer as the mixing machine. Next, a medium such as water and, if necessary, an aerosol-generating base material such as glycerin are added to the dry blend, and mixed with a mixer to prepare wet powder (powder in a wet state). The amount of the medium in the moisture can be 20 to 80 mass%, preferably 20 to 40 mass%, and is appropriately prepared in step 2. For example, when piezoelectricity is performed in step 2, the amount of the medium can be 20 to 50 mass%, and when extrusion is performed, the amount can be 20 to 80 mass%. It is preferable that the solid content concentration of the moisture is 50 to 90 mass%.

3) Kneading

The wet powder is kneaded using a kneader (eg, DG-1 manufactured by Dalton). It is desirable to carry out kneading until the medium is evenly spread throughout. For example, it is desirable to knead the mixture until the color of the mixture becomes uniform when viewed with the naked eye.

(2) Process 2

In this process, the mixture (wet content) is extruded from a piezoelectric or die to prepare a wet sheet. For example, the mixture is sandwiched between two base films, using a calendar device (e.g., manufactured by Yuri Roll Machinery) between a pair of rollers until a predetermined thickness (exceeding 100 μm) is reached. and piezoelectricity is applied to obtain a laminate in which a wet sheet exists between two base films. As the base film, a non-adhesive film such as a fluorine-based polymer film is preferable. Piezoelectricity using rollers can be performed multiple times. Additionally, the mixture (wet content) may be extruded from a die (preferably a T die) provided with a predetermined gap to form a wet sheet on the substrate. As the base material, known materials such as glass plates, metal plates, and plastic plates can be used. A known extruder can be used for extrusion.

(3) Process 3

In this process, the wet sheet is dried. For example, in laminate, this process can be performed in the following order. 1) Peel off the base film on one side. 2) The laminate is dried using a ventilated dryer. The drying temperature may be room temperature, but is preferably 50 to 100°C, and the drying time may be 1 to 2 minutes. 3) Next, the remaining base film is peeled off and dried under the above conditions to obtain a tobacco sheet. By performing drying in this way, it is possible to avoid adhesion of the tobacco sheet to other substrates. The tobacco sheet obtained in this way is also called a 'laminated sheet'. A laminated sheet is preferable because it has a smooth surface and can suppress the occurrence of flaking when in contact with another member. Additionally, this method is suitable for producing sheets of 300 μm or less.

Additionally, in the case of extrusion molding, the wet sheet on the substrate is dried by air drying or heating. Drying conditions were as described above. The tobacco sheet obtained in this way is also called an 'extruded sheet'. Extruded sheets are preferable because they have a smooth surface and can suppress the occurrence of flaking when in contact with other members. This method is suitable for the production of sheets of 200 μm or more.

[Second mode]

The tobacco sheet in this embodiment contains a tobacco material and a cellulose derivative with a degree of substitution of 0.65 or more as a binder.

(1) Binder

In this embodiment, a cellulose derivative with a degree of substitution of 0.65 or more is used as the binder. A cellulose derivative is cellulose in which the -OH group of the glucopyranose residue has been modified. Those in which -OH groups are modified with -OR groups (R is an organic group) are called cellulose ethers, and those in which -OH groups are modified with -OX groups (X is a group derived from acid) are called cellulose esters. In the present invention, both are called cellulose esters. Available.

The degree of substitution is the number of substituents per one gluconopyranose residue, that is, the number of modified OH groups. The degree of substitution used in the present invention is preferably 0.65 or more, more preferably 0.7 or more, and still more preferably 0.8 or more. Additionally, the upper limit of the degree of substitution is preferably 3.0 or less, more preferably 2.0 or less, further preferably 1.6 or less, and particularly preferably 1.0 or less.

The degree of substitution is measured by a known method. For example, the degree of substitution is measured by the methanol nitrate method. This method: 1) Accurately weigh about 2.0 g of the sample and place it in a 300 ml rotating Erlenmeyer flask. Add 100 ml of methanol nitrate (a solution obtained by adding 100 ml of special grade concentrated nitric acid to 1 g of anhydrous methanol) and shake for about 2 hours to convert the terminal acid group from the salt form to the hydrogen form (e.g. COONa to COOH). 2) The sample was filtered through glass filter 1G3, washed with 200 ml of 80% methanol, and dried at 105°C for 2 hours. 3) Accurately weigh about 1 to 1.5 g of the dried sample, place in a 300 ml rotating Erlenmeyer flask, moisten with 150 ml of 80% methanol, add 50 ml of 0.1 N NaOH, and shake at room temperature for 2 hours. Phenolphthalein is used as an indicator, and excess NaOH is back-titrated with 0.1N sulfuric acid. 4) Calculate the degree of substitution from the formula below.

Degree of substitution = 0.162A/(1-0.058A)

A=50×F’-amount of sulfuric acid (ml)×F/mass of absolute dry sample (g)×0.1

F: Factor of the sulfuric acid

F': Factor of the above NaOH

In cellulose ethers, there are a maximum of three R, but each R may be the same or different. As R, a straight or branched C1-C3 alkyl group such as a methyl group, ethyl group, or propyl group; C1 to C3 linear or branched hydroxyalkyl groups such as hydroxymethyl group, hydroxyethyl group, and hydroxypropyl group; Arylalkyl groups having C7 to C20 carbon atoms, such as benzyl group and trityl group; Cyanoalkyl groups such as cyanoethyl group; Carboxyalkyl groups such as carboxymethyl group and carboxyethyl group; and aminoalkyl groups such as aminoethyl group. Among them, as R, a carboxyalkyl group is preferable and a carboxymethyl group is more preferable. The degree of substitution in cellulose ethers is also called the degree of etherification.

In cellulose ethers, there are a maximum of three Xs, but each X may be the same or different. As X, groups derived from C0 to C4 carboxylic acids such as formic acid, acetic acid, propionic acid, and butyric acid; Groups derived from C6 to C10 aromatic carboxylic acids such as benzoic acid and phthalic acid; Groups derived from sulfonic acids such as p-toluenesulfonic acid; Groups derived from inorganic acids such as nitric acid, sulfuric acid, and phosphoric acid; A group derived from xantogenic acid can be mentioned. The degree of substitution in cellulose esters is also called the degree of esterification.

Since the cellulose derivative has high hydrophilicity, when it is used as a binder, affinity with the tobacco material is improved. As a result, the strength of the tobacco sheet is improved, making it difficult for pieces to fall off during use.

Additionally, the cellulose derivative is soluble in organic solvents, especially ethanol. Therefore, as will be described later, when a mixture using ethanol as a medium is used in the production of a tobacco sheet, the viscosity of the mixture can be lowered, so it is advantageous in terms of transportation during production, coating processes, etc., compared to a mixture using water as a medium. Additionally, since ethanol is more prone to volatilization than water, the above production method makes it possible to shorten the production time and reduce energy costs during drying.

The amount of the cellulose derivative in the tobacco sheet is not particularly limited, but is preferably 0.1 to 10% by mass, more preferably 0.1 to 10% by mass in terms of dry mass (mass excluding mixed water, hereinafter the same) relative to the dry mass of the tobacco sheet. is 1 to 5 mass%, further 2 to 4 mass%. If the amount of binder exceeds the upper limit or is less than the lower limit, the above effect may not be sufficiently exerted.

Specific examples of cellulose derivatives are given below.

Cellulose ethers: methylcellulose, ethylcellulose, hydroxyethylcellulose, hydroxymethylethylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, benzylcellulose, tritylcellulose, cyanoethylcellulose, carboxymethylcellulose, carboxyethyl. Cellulose, aminoethylcellulose

Cellulose esters: Organic acid esters such as cellulose acetate, cellulose formate, cellulose propionate, cellulose butyrate, cellulose benzoate, cellulose phthalate, tosyl cellulose, and cellulose nitrate; Inorganic acid esters such as cellulose sulfate, cellulose phosphate, and cellulose xanthogenate

(2) Tobacco materials

In this aspect, in addition to the fibrous tobacco material, the tobacco material described in the first aspect can be used.

(3) Aerosol generator

In this aspect, the tobacco sheet may contain the aerosol generating agent described in the first aspect.

(4) Emulsifier

In this aspect, the tobacco sheet may contain the emulsifier described in the first aspect.

(5) Cellulose other than tobacco

In this aspect, the tobacco sheet may contain cellulose other than tobacco. Cellulose other than tobacco includes, for example, the above-mentioned cellulose fibers and cellulose powder, and does not include cellulose derivatives as binders.

(6) Spices

In this aspect, the tobacco sheet may contain the flavoring described in the first aspect.

(7) Characteristics and form of tobacco sheets

1) Thickness

The thickness of the tobacco sheet in this embodiment is not limited, but in one embodiment, it is preferably 20 to 2000 μm, more preferably 100 to 1500 μm, and still more preferably 100 to 1000 μm.

2) Strength

The tobacco sheet in this embodiment preferably has a tensile stress of 1.7 N/mm or more, more preferably 2 N/mm or more, and even more preferably 3 N/mm or more.

3) Arithmetic mean surface roughness Sa

The tobacco sheet in this embodiment preferably has an arithmetic mean surface roughness Sa of 0.03 mm or less. Sa is an index of surface roughness, and when the tobacco sheet in this embodiment has Sa in the above range, flaking off from the surface is reduced. From this viewpoint, the upper limit of Sa is more preferably 0.02 mm or less.

(8) Tobacco segment

From tobacco sheets, tobacco segments for use in smoking articles can be manufactured. The tobacco segment in this aspect is as described in the first aspect.

[Manufacturing method]

The tobacco sheet in this embodiment can be manufactured by any method, but is preferably manufactured by a method comprising the following steps.

Step 1 of preparing a mixture containing at least a tobacco material, the cellulose derivative, and a medium,

Step 2 of preparing a wet sheet by spreading the mixture on a substrate, and

Step 3 of drying the wet sheet.

(1) Process 1

This process mixes the fiber-like material, optionally tobacco material, a cellulose derivative as a binder, and a medium. If necessary, aerosol-generating substrates, emulsifiers or fragrances may be added. The mixing amount of each component is adjusted to achieve the above-mentioned amount. The medium is preferably made up of a water-soluble organic solvent with a boiling point of less than 100°C, such as water or ethanol, and is more preferably water or ethanol. The mixing method is not limited, and known equipment such as a mixer or kneader can be used. The solid content concentration of the mixture obtained by mixing is not limited and is adjusted appropriately to be suitable for Step 2. For example, the upper limit of the solid content concentration is preferably 98 mass% or less, 90 mass% or less, or 80 mass% or less, and the lower limit is preferably 10 mass% or more, 20 mass% or more, or 30 mass% or more. , 40% by mass or more, or 50% by mass or more.

(2) Process 2

In this process, the mixture is spread on a substrate to prepare a wet sheet. The substrate is not limited and includes inorganic material substrates such as glass plates, metal substrates such as aluminum plates, organic material substrates such as PET films and fluoropolymer films, and fibrous material substrates such as non-woven fabrics. The method of spreading the mixture on the substrate is not limited, but includes a rolling method using a roller to apply piezoelectricity, an extrusion method using a die, and a casting method, as described later.

(3) Drying process

In this process, the wet sheet is dried. Drying can be performed according to known methods. For example, the wet sheet can be air-dried at room temperature or dried by heating. The heating temperature is also not limited and can be, for example, 60 to 150°C. The dried sheet is isolated from the substrate to obtain a tobacco sheet.

Below, a preferred embodiment of the manufacturing method of the tobacco sheet in this embodiment will be described.

[Rolling method]

1) Process 1

1-1) Grinding

Raw materials (e.g., leaves) are crushed. Next, fine pulverization is performed using a grinder (for example, ACM-5 manufactured by Hosokawa Micron). The particle size (D90) after fine pulverization is preferably 50 to 800 μm. Particle size is measured using a laser diffraction type particle size meter such as Master Sizer (manufactured by Malvern).

1-2) Preparation of moisture

Additives such as binders, fibrous materials, and, if necessary, flavorings or lipids are added to pulverized tobacco raw materials (e.g., tobacco particles) and mixed. Since this mixing is preferably a dry blend, it is preferable to use a mixer as the mixing machine. Next, a medium such as water and, if necessary, an aerosol-generating base material such as glycerin are added to the dry blend, and mixed with a mixer to prepare wet powder (powder in a wet state). The amount of the medium in the moisture can be 20 to 80 mass%, preferably 20 to 40 mass%, but since piezoelectricity is performed in step 2, it may be 20 to 50 mass%. It is preferable that the solid content concentration of the moisture is 50 to 90 mass%.

1-3) Kneading

The wet powder is kneaded using a single-axis or multi-axis kneader, such as a kneader (DG-1, manufactured by Dalton, etc.). It is desirable to carry out kneading until the medium is evenly spread throughout. For example, it is desirable to knead the mixture until the color of the mixture becomes uniform when viewed with the naked eye.

2) Process 2 (Piezoelectric)

The mixture after kneading is sandwiched between two base films and passed between a pair of rollers using a calendar device (e.g., manufactured by Glass Roll Machinery Co., Ltd.) until a predetermined thickness (exceeding 100 μm) is reached, and the piezoelectric Thus, a laminate in which a wet sheet exists between two base films is obtained. Piezoelectricity using rollers can be performed multiple times. The base film is preferably a non-adhesive film such as a fluorine-based polymer film, and specific examples include Teflon (registered trademark) film.

3) Process 3

In the laminate, one base film is peeled off. The laminate is dried using a ventilated dryer. The drying temperature is preferably 50 to 100°C, and the drying time can be 1 to 2 minutes. Next, the remaining base film is peeled off and further dried under the above conditions to obtain a tobacco sheet. By performing drying in this way, it is possible to avoid adhesion of the tobacco sheet to other substrates.

The tobacco sheet obtained by this method is also called a 'laminated sheet'. A laminated sheet is preferable because it has a smooth surface and can suppress the occurrence of flaking when in contact with another member. Additionally, this method is suitable for producing sheets of 300 μm or less.

[Extrusion method]

1) Process 1

Step 1 in this method is the same as described for the rolling method. Prepare moist powder (wet powder). When extruding in step 2, the amount of medium in the moisture can be selected from the range of 20 to 80 mass%, but is preferably 20 to 40 mass%.

2) Process 2

In this process, moisture is extruded from a die with a predetermined gap to form a wet sheet on the substrate. A known extruder can be used for extrusion.

3) Process 3

In this process, a wet sheet is dried to obtain a tobacco sheet. Drying conditions were the same as described in the rolling method. Tobacco sheets obtained by this method are also called 'extruded sheets'. Extruded sheets are preferable because they have a smooth surface and can suppress the occurrence of flaking when in contact with other members. This method is suitable for producing sheets of 200 μm or more.

In addition, sheets formed by applying pressure in this way are called 'pressure molded sheets', and 'pressure molded sheets' include 'laminate sheets' and 'extruded sheets'. A laminated sheet is a sheet obtained by piezoelectricizing the mixture to a target thickness with a roller one or more times and then drying it to a target moisture content. An extruded sheet is a sheet obtained by extruding a mixture to a target thickness using a T-die or the like and then drying it to a target moisture content. Piezoelectricity and extrusion may be combined in pressure forming sheets. For example, after extruding the mixture, it may be further piezoelectrically formed into a sheet.

[Cast method]

1) Process 1

Step 1 in this method can be performed by any method. For example, a mixture can be prepared by mixing a tobacco raw material having a desired particle size, a cellulose derivative, a medium, and additives as necessary using a mixer or the like. Since the solid content concentration of the mixture obtained in this process is preferably about 3 to 15 mass%, the mixture is also called a slurry.

2) Process 2

In this process, the slurry is cast on the substrate to form a wet sheet. Casting can be performed as known.

3) Process 3

In this process, a wet sheet is dried to obtain a tobacco sheet. Drying conditions were the same as described in the rolling method. The tobacco sheet obtained by this method is also called a 'cast sheet'.

Example

Hereinafter, specific examples of the present embodiment will be described, but the present invention is not limited to these.

[Example 1]

Tobacco lamina (leaf tobacco) was dry-ground in a Hosokawa Micron ACM machine to obtain tobacco powder. For the tobacco powder in question, the cumulative 90% particle size (D90) in the volume-based particle size distribution measured by dry laser diffraction was determined using Master Sizer (brand name, manufactured by Spectris Co., Ltd., Malvern Panalytical Division). When measured, it was 200㎛.

Using the above tobacco powder as a tobacco raw material, a tobacco sheet was manufactured by a rolling method. Specifically, 77 parts by mass of the tobacco raw material, 12 parts by mass of glycerin as an aerosol generator, 1 part by mass of carboxymethyl cellulose as a molding agent, and fiber-shaped pulp (dry type of pulp manufactured by Canfor) as a fiber-shaped material. 10 parts by mass of dry defibrated product were mixed and kneaded in an extrusion molding machine. The kneaded product was molded into a sheet using two pairs of metal rolls and dried in a hot air circulation oven at 80°C to obtain a tobacco sheet. The cigarette sheet was shredded into a size of 0.8 mm x 9.5 mm using a shredder.

For the recarved tobacco sheets, swelling properties were measured. Specifically, the re-engraved tobacco sheet was left in a 60% conditioned room at 22°C for 48 hours, and then the swelling properties were measured using DD-60A (trade name, manufactured by Borgvarts). The measurement was performed by placing 15 g of the recut tobacco sheet in a cylindrical container with an inner diameter of 60 mm and determining the volume when compressed for 30 seconds with a load of 3 kg. The results are shown in Table 1. In addition, in Table 1, the swelling property is based on the swelling property value in Comparative Example 1 described later, and is expressed as an increase rate (%) of the swelling property with respect to the reference value.

[Comparative Example 1]

Tobacco powder was prepared as in Example 1. Using the tobacco powder as a tobacco raw material, a tobacco sheet was manufactured by a rolling method. Specifically, 87 parts by mass of the tobacco raw material, 12 parts by mass of glycerin as an aerosol generator, and 1 part by mass of carboxymethyl cellulose as a molding agent were mixed and kneaded in an extrusion molding machine. The kneaded product was molded into a sheet using two pairs of metal rolls and dried in a hot air circulation oven at 80°C to obtain a tobacco sheet. The cigarette sheet was shredded into a size of 0.8 mm x 9.5 mm using a shredder. For the recarved tobacco sheets, swelling properties were measured in the same manner as in Example 1. The results are shown in Table 1.

[Table 1]

From Table 1, the tobacco sheet of Example 1, which is the tobacco sheet according to the present embodiment, had improved swelling properties compared to the tobacco sheet of Comparative Example 1 which did not contain a fiber-like material. Additionally, in Example 1, the tobacco sheet was manufactured by the rolling method, but even when the tobacco sheet was similarly manufactured by the casting method, the swelling properties were improved.

[Reference example A1]

Tobacco leaves were pulverized using a grinder (ACM-5 manufactured by Hosokawa Micron) until D90 was 204 ㎛ and D50 was 66 ㎛ to obtain leaf tobacco particles. D90 and D50 were measured with a Master Sizer (manufactured by Malvern). Leaf tobacco particles and Sunrose F20HC (cellulose ether manufactured by Nippon Paper Co., Ltd.) as a binder were dry blended using a mixer. Next, glycerin as an aerosol generating base and water as a medium were added to the dry blend, and mixed with a mixer to prepare moisture. The combination of each component is as shown in Table A1.

Using a kneader (DG-1, manufactured by Dalton), the wet powder was kneaded six times at room temperature to obtain a mixture. A T die was used as the die, and the screw rotation speed was 38.5 rpm.

The moisture content was sandwiched between two Teflon (registered trademark) films (NITOFLON(R) No. 900UL, manufactured by Nitto Denko Co., Ltd.), and using a calender device (manufactured by Glass Roll Machinery Co., Ltd.), a predetermined thickness (exceeding 100 ㎛) was obtained. By rolling in four stages until the thickness was reached, a laminate with a thickness of 105 μm having a layer structure of film/wet sheet/film was prepared. The roll gaps in the first to fourth stages were 650 μm, 330 μm, 180 μm, and 5 μm, respectively. The roll gap in the fourth stage is thicker than the thickness of the final sheet obtained, because the sheet, released from the pressure between the rollers, expands to near the final thickness.

One Teflon (registered trademark) film was peeled from the laminate and dried at 80°C for 1 to 2 minutes using a ventilated dryer. Next, another film was peeled off, and the wet sheet was dried under the same conditions to produce and evaluate the tobacco sheet of the present invention.

[Table A1-1]

In the wet mass of Table A1, the tobacco leaf grinds, glycerin, and binder represent the dry mass, and the water represents the total amount of the input mass and the water mass contained in the tobacco leaf grinds, glycerin, and binder.

[Reference examples A2, A4]

Tobacco sheets were produced and evaluated in the same manner as Reference Example A1, except that Sunrose F30MC and Sunrose F20LC were used instead of Sunrose F20HC (cellulose ether manufactured by Nippon Paper Co., Ltd.) as the binder.

[Reference example A3]

As a binder, instead of Sunrose F20HC (cellulose ether manufactured by Nippon Paper Co., Ltd.), Sunrose F30MC was used, the mixing amount was changed as shown in Table A3, and the amount of glycerin was adjusted to 15.5 DB mass% in input mass ratio. Except for the changes, a tobacco sheet was manufactured and evaluated in the same manner as Reference Example A1.

[Reference Comparative Example A1]

Leaf tobacco particles with a D90 of 204 ㎛ and a D50 of 66 ㎛ were obtained in the same manner as Reference Example A1. The same ingredients and pulp as in Reference Example A1 were mixed with a mixer to obtain a mixture. Using the mixture, a tobacco sheet was manufactured by a cast method according to a conventional method.

[Table A1-2]

[Reference Comparative Example A2]

Tobacco sheets were manufactured by the papermaking method according to the established method. Specifically, the water-soluble component of the tobacco raw material is extracted with water, the extraction residue, pulp, and water are mixed, this is ground using a grinder, a sheet is formed with a paper machine, and the sheet is dried, and the extract and Glycerin was added to the sheet. The tobacco sheet was evaluated in the same manner as Reference Example A1. The composition of the sheet is shown in Table A2. Additionally, the evaluation results of the tobacco sheet manufactured in the above example are shown in Table A3.

[Table A2]

[Table A3]

Below, the evaluation method is explained.

[Piece drop volume]

In each example, the prepared tobacco sheets were cut to prepare pieces. The piece was filled at 70% by volume in a wrapper 22 having a length of 12 mm and a diameter of 7 mm, thereby preparing a tobacco-containing segment 20A. Next, a flavor inhalation article 1 shown in FIG. 1 including the tobacco-containing segment was prepared. A system as shown in FIG. 2 (however, it was an internal heating type) was prepared, and it was subjected to a smoking test using a smoker (14 puffs, CIR conditions, constant heating at 350°C). After the smoking test, pieces were carefully removed from the tobacco segment 20A. Subsequently, new pieces were filled into the wrapper 22 again at the above volume percentage and subjected to a second smoking test. In this way, a total of 20 smoking tests were performed, and the volume of total pieces remaining in the wrapper 22 was measured.

[Surface roughness]

Measurements were made using a microscope (VK-X100 manufactured by KEYENCE) using the following procedures.

1) Set the focus position of the lowest part of the sheet

2) Set the focus position of the highest part of the sheet

3) Divide the sections obtained in 1) and 2) above and take images while slightly shifting the focus.

4) Measure the height from the difference between the focus position of each part and the focus position of the lowest part.

5) Calculate the roughness from the height data at each location (automatically calculated by measuring instrument software) and calculate the arithmetic surface roughness Sa.

[Tensile strength, elongation]

The obtained sheet was cut to 15 mm in width x 180 mm in length, and measured using a tensile strength tester (Toyo Seiki Manufacturing Co., Ltd.: Strograph E-S) under the conditions of ROADRANGE: 25 and SPEEDRANGE: 50, and the tensile strength was evaluated by tensile stress. did.

[Reference example B1]

Tobacco leaves were pulverized using a grinder (ACM-5 manufactured by Hosokawa Micron) to a D90 of 50 to 800 ㎛ to obtain leaf tobacco particles. D90 was measured with a Master Sizer (manufactured by Malvern). Leaf tobacco particles and carboxymethyl cellulose (Sunrose F30MC, manufactured by Nippon Paper Co., Ltd.) as a binder were dry blended using a mixer. Next, glycerin as an aerosol generating base and water as a medium were added to the dry blend, and mixed with a mixer to prepare moisture. The combination of each component is as follows.

[Table B1]

In the wet mass of Table B1, the tobacco leaf shreds, glycerin, and binder represent the dry mass, and the water represents the total amount of the input mass and the water mass contained in the tobacco leaf shreds, glycerin, and binder.

Using a kneader (DG-1, manufactured by Dalton), the wet powder was kneaded six times at room temperature to obtain a mixture. The die shape was T-shaped (T die), and the screw rotation speed was 38.5 rpm.

The moisture content was sandwiched between two Teflon (registered trademark) films (NITOFLON(R) No. 900UL, manufactured by Nitto Denko Co., Ltd.), and using a calender device (manufactured by Glass Roll Machinery Co., Ltd.), a predetermined thickness (exceeding 100 ㎛) was formed. By rolling in four steps until the thickness was reached, a laminate with a thickness of 105 μm having a layer structure of film/wet sheet/film was prepared. The roll gaps in the first to fourth stages were 650 μm, 330 μm, 180 μm, and 5 μm, respectively. The roll gap in the fourth stage is thicker than the thickness of the finally obtained sheet, but this is because the sheet, released from the pressure between the rollers, expands to near the final thickness.

One Teflon (registered trademark) film was peeled from the laminate and dried at 80°C for 1 to 2 minutes using a ventilated dryer. Next, another film was peeled off, and the wet sheet was dried under the same conditions to produce a sheet according to this embodiment.

[Reference example B2 to B5]

Tobacco sheets were produced and evaluated in the same manner as Reference Example B1, except that the carboxymethyl cellulose shown in Table B2 (all manufactured by Nippon Paper Co., Ltd.) was used as a binder.

[Reference Comparative Example B1]

Tobacco sheets were produced and evaluated in the same manner as Reference Example B1, except that carboxymethylcellulose (manufactured by Nippon Paper Co., Ltd.) shown in Table B2 was used as a binder. These results are shown in Table B3. In the table, the physical properties of the finished sheet indicate the physical properties of a sheet that has been manufactured through drying as described above and has not been dried to an absolute dry state.

[Table B2]

[Table B3]

Below, the evaluation method is explained.

[Piece drop volume]

In each example, the prepared tobacco sheets were cut to prepare pieces. The piece was filled at 70% by volume in a wrapper 22 having a length of 12 mm and a diameter of 7 mm, and a tobacco-containing segment 20A was prepared. Next, a flavor inhalation article 1 shown in FIG. 1 including the tobacco-containing segment was prepared. A system as shown in FIG. 2 (but internal heating type) was prepared and subjected to a smoking test using a smoker (14 puffs, CIR conditions, constant heating at 350°C). After the smoking test, pieces were carefully removed from the tobacco segment 20A. Subsequently, new pieces were filled into the wrapper 22 again at the above volume percentage and subjected to a second smoking test. In this way, a total of 20 smoking tests were performed, and the volume of total pieces remaining in the wrapper 22 was measured.

[Surface roughness]

Measurements were made using a microscope (VK-X100 manufactured by Keyence) using the following procedures.

1) Set the focus position of the lowest part of the sheet

2) Set the focus position of the highest part of the sheet

3) Divide the sections obtained in 1) and 2) above and take images while slightly shifting the focus.

4) Measure the height from the difference between the focus position of each part and the focus position of the lowest part.

5) Calculate the roughness from the height data at each location (automatically calculated by measuring instrument software) and calculate the arithmetic surface roughness Sa.

[Coagulability after heating]

A non-combustion internal heating type smoking system was prepared under the conditions described in the piece drop volume, and a smoking test was conducted once under the same conditions. After the test, the tobacco segment (20A) is taken out from the system, placed on a jig at a position of 6 mm in the longitudinal direction from the tip, compressed in the radial direction at a constant speed, and the load (N) when the jig reaches the position of 3.5 mm. was obtained and the coagulability was evaluated after heating. The higher the value of the load, the easier it is for the pieces to stick after heating, making it less likely that the pieces will fall off.

[tensile strength]

The obtained sheet was cut to 15 mm in width x 180 mm in length, and measured using a tensile strength tester (Toyo Seiki Manufacturing Co., Ltd.: Strograph E-S) under the conditions of ROADRANGE: 25 and SPEEDRANGE: 50, and the tensile strength was evaluated by tensile stress. did.

[degree of substitution]

It was determined by the measurement method described above.

Embodiments are shown below.

[1] A tobacco sheet for a non-combustible heated flavor inhaler comprising a fibrous material.

[2] The tobacco sheet for a non-combustible heating type flavor inhaler according to [1], wherein the ratio of the fibrous material contained in 100% by mass of the tobacco sheet is 5 to 50% by mass.

[3] The tobacco sheet for a non-combustion heating type flavor inhaler according to [1] or [2], wherein the fibrous material is at least one selected from the group consisting of fibrous pulp, fibrous tobacco material, and fibrous synthetic cellulose. .

[4] The tobacco sheet for a non-combustible heating type flavor inhaler according to [3], wherein the fibrous material is fibrous pulp.

[5] The tobacco sheet for a non-combustion heating type flavor inhaler according to [4], wherein the tobacco sheet further contains a tobacco raw material.

[6] The method for producing a tobacco sheet for a non-combustion heating type flavor inhaler according to [5], wherein the tobacco raw material is at least one type of tobacco powder selected from the group consisting of leaf tobacco, stems, and remaining stems.

[7] The tobacco sheet for a non-combustion heating type flavor inhaler according to [5] or [6], wherein the ratio of the tobacco raw material contained in 100% by mass of the tobacco sheet is 30 to 91% by mass.

[8] The tobacco sheet for a non-combustible heating type flavor inhaler according to any one of [4] to [7], wherein the tobacco sheet further contains a molding agent.

[9] The tobacco sheet for a non-combustible heating type flavor inhaler according to [8], wherein the molding agent is at least one selected from the group consisting of polysaccharides, proteins, and synthetic polymers.

[10] The tobacco sheet for a non-combustion heating type flavor inhaler according to [8] or [9], wherein the proportion of the molding agent contained in 100% by mass of the tobacco sheet is 0.1 to 15% by mass.

[11] The tobacco sheet for a non-combustible heated flavor inhaler according to any one of [1] to [10], wherein the tobacco sheet further contains an aerosol generator.

[12] The tobacco sheet for a non-combustion heating type flavor inhaler according to [11], wherein the aerosol generator is at least one selected from the group consisting of glycerin, propylene glycol, and 1,3-butanediol.

[13] The tobacco sheet for a non-combustible heating type flavor inhaler according to [11] or [12], wherein the proportion of the aerosol generator contained in 100% by mass of the tobacco sheet is 5 to 50% by mass.

[14] A non-combustion heating type flavor inhaler comprising a tobacco-containing segment comprising the tobacco sheet for a non-combustion heating type flavor inhaler according to any one of [1] to [13].

[15] The non-combustion heating type flavor inhaler described in [14],

Heating device for heating the tobacco-containing segments

A non-combustion heated flavor aspiration system comprising a.

[1A] A tobacco sheet comprising a tobacco material and a binder, and having an arithmetic average surface roughness Sa of at least one side of 5 to 30 μm.

[2A] The sheet according to [1A], which is a pressure molded sheet.

[3A] The sheet according to [1A] or [2A], wherein the binder compounding amount is 6% by mass or less in dry mass relative to the dry mass of the tobacco sheet.

[4A] The tobacco sheet according to [1A], wherein the arithmetic average surface roughness Sa of both sides is 5 to 30 μm.

[5A] The sheet according to any one of [1A] to [4A], having a tensile elongation of 5 to 15%.

[6A] A non-combustible heating type smoking article comprising the tobacco sheet according to any one of [1A] to [5A] or a material derived therefrom.

[7A] At least, step 1 of preparing a mixture by mixing the tobacco material, binder, and medium,

Step 2 of preparing a wet sheet by extruding the mixture from a piezoelectric or die, and

Step 3 of drying the wet sheet

The method for producing a sheet according to any one of [1A] to [5A], comprising:

[8A] The manufacturing method according to [7A], wherein step 2 includes preparing a laminate sheet in which a wet sheet exists between two base films.

[9A] The production method according to [7A] or [8A], wherein step 1 includes kneading at least the tobacco material, binder, and medium in a single-axis or multi-axis kneader.

[10A] The production method according to any one of [7A] to [9A], wherein the mixture contains 20 to 80% by mass of a medium based on the total amount of the mixture.

[1B] Tobacco materials,

Containing a cellulose derivative with a degree of substitution of 0.65 or more,

Cigarette sheets.

[2B] The sheet according to [1B], wherein the degree of substitution is 0.7 or more.

[3B] The sheet according to [2B], wherein the degree of substitution is 0.8 or more.

[4B] The sheet according to any one of [1B] to [3B], wherein the cellulose derivative is carboxyalkylated cellulose.

[5B] The sheet according to any one of [1B] to [4B], wherein the arithmetic mean surface roughness Sa is 0.03 mm or less.

[6B] The sheet according to any one of [1B] to [5B], which is a pressure molded sheet.

[7B] Step 1 of preparing a mixture containing at least a tobacco material, the cellulose derivative, and a medium,

Step 2 of preparing a wet sheet by spreading the mixture on a substrate, and

Step 3 of drying the wet sheet,

The method for producing a sheet according to any one of [1B] to [6B], comprising:

[8B] The production method according to [7B] or [8B], wherein step 1 includes kneading the tobacco material, the cellulose derivative, and the medium using a single-axis or multi-axis kneader.

[9B] The manufacturing method according to [7B] or [8B], wherein step 2 includes piezoelectricizing the mixture using a roller or extruding it from a die.

[10B] The manufacturing method described in [9B], wherein step 2 includes preparing a laminate sheet with a wet sheet between two base films.

[11B] A non-combustion heating type smoking article comprising the tobacco sheet according to any one of [1B] to [6B] or a material derived therefrom.

1: Non-combustible heated flavor aspirator
2: Tobacco-containing segment
3: Cooling segment
4: Center hole segment
5: Filter segment
6: Mouthpiece segment
7: Barrel-shaped member
8: perforation
9: Second packed layer
10: Second inner plug wrapper
11: Outer plug wrapper
12: Mouthpiece lining paper
13: Heating device
14: body
15: heater
16: Metal tube
17: Battery unit
18: control unit
19: recess
20A: Tobacco-containing segment
21: filling
22: Rapper
T: Cigarette sheet

Claims (7)

A tobacco sheet for a non-combustible heated flavor inhaler comprising a fibrous material. According to paragraph 1,
A sheet having an arithmetic average surface roughness Sa of at least one side of 5 to 30 μm. According to claim 1 or 2,
Sheet, which is a pressure formed sheet. According to any one of claims 1 to 3,
A sheet comprising a cellulose derivative having a degree of substitution of 0.65 or more. According to clause 4,
A sheet wherein the degree of substitution is 0.7 or more. A tobacco-containing segment comprising a tobacco sheet for a non-combustible heated flavor inhaler according to any one of claims 1 to 5.
A non-combustion heating type flavor aspirator having a. A non-combustion heating type flavor aspirator according to claim 6,
Heating device for heating the tobacco-containing segments
A non-combustion heated flavor aspiration system comprising a.