KR20230148230A - 레올로지 개질제 조성물 및 그로부터 제조된 건축용 코팅 조성물 - Google Patents
레올로지 개질제 조성물 및 그로부터 제조된 건축용 코팅 조성물 Download PDFInfo
- Publication number
- KR20230148230A KR20230148230A KR1020237032321A KR20237032321A KR20230148230A KR 20230148230 A KR20230148230 A KR 20230148230A KR 1020237032321 A KR1020237032321 A KR 1020237032321A KR 20237032321 A KR20237032321 A KR 20237032321A KR 20230148230 A KR20230148230 A KR 20230148230A
- Authority
- KR
- South Korea
- Prior art keywords
- rheology modifier
- cellulose
- composition
- polymer
- modifier composition
- Prior art date
Abstract
본원에 개시된 본 발명의 개념(들)은 일반적으로 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체, 및 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르를 포함하는 레올로지-개질제 조성물에 관한 것이다. 추가로, 본원에 개시된 본 발명의 개념(들)은 또한 레올로지 개질제 조성물을 제조하는 방법 및 그것을 포함하는 수성 코팅 조성물에 관한 것이다.
Description
본원에 개시된 공정(들), 절차(들), 방법(들), 생성물(들), 결과(들), 및/또는 개념(들) (이하 "본 개시내용"이라고 통칭됨)은 일반적으로 레올로지 개질제 조성물(들) 및 그의 용도에 관한 것이다. 본 개시내용은 추가로 레올로지 개질제 조성물(들)로부터 제조된 건축용 코팅 조성물(들)에 관한 것이다.
일반적으로 회합성(associative) 레올로지 개질제로서 공지된 소수성 개질 에틸렌-옥시드 기반 폴리우레탄 (HEUR)과 같은 소수성 개질 비-이온성 합성 증점제 (NSAT)는 페인트를 증점하거나 그의 점도를 증가시켜 평활화, 처짐 저항 등과 같은 최적의 응용 특성을 제공하는 데 널리 사용된다. 이러한 레올로지 개질제는 둘 이상의 소수성 부분을 함유한다. 소수성 부분의 기능은 결합제 라텍스 입자의 표면과 회합하여 개별 라텍스 입자들을 서로 연결하는 그물 구조를 초래하여 점도를 증가시키는 것이다. 또한, 코팅 산업에서는 또 다른 부류의 비-회합성 레올로지 개질제가 사용된다. 비-회합성 레올로지 개질제의 예는 수용성 중합체, 예를 들어, 셀룰로스 (HEC), 전분 등을 포함한다. 비-회합성 레올로지 개질제는 수용액 중 고도로 얽힌 중합체 분자에 의해 도입된 증점 메커니즘을 통해 페인트의 점도를 증가시켜 페인트의 유동성을 제한한다. 비-회합성 증점제로서 폴리아크릴아미드 및 셀룰로스 에테르, 예를 들어, 히드록시에틸 셀룰로스를 개별적으로 사용하는 것은 관련 기술분야에 공지되어 있지만, 그럼에도 불구하고 그것은 특정한 결점, 예를 들어, 끈끈하거나 끈적한 레올로지, 불량한 평활화 및 희석 내성을 갖는 것으로 공지되어 있다.
미국 특허 제4,425,469호에는 수성 시스템에서 피흡착질 및 유동 개질제로서의, 소수성 말단 기를 포함하는 아크릴아미드의 수용성 비닐 부가 중합체의 용도가 교시되어 있다. 아크릴아미드의 중합체는 소수성 사슬 이동제를 통해 도입된 말단 소수성 부분을 갖는 단독중합체 또는 공중합체이다.
중국 특허 제1225934호에는 소듐 카르복시메틸 셀룰로스, 히드록시프로필 셀룰로스 및 폴리아크릴아미드를 함유하는 고점도 분말 건축용 코팅이 교시되어 있다.
허큘레스에게 양도된 미국 특허 제9,834,695호에는 건축용 코팅에 사용되는 레올로지 개질제 조성물이 개시되어 있으며, 여기서 상기 레올로지 개질제 조성물은 셀룰로스 에테르, 예컨대 히드록시에틸 셀룰로스, 에틸 히드록시에틸 셀룰로스, 소수성 개질 히드록시에틸 셀룰로스와, 양이온성 중합체, 예컨대 아크릴아미도프로필 트리모늄 클로라이드, 아크릴아미도프로필 트리모늄 클로라이드/아크릴아미드 공중합체와, 분산제의 블렌드를 포함한다.
그러므로, 관련 기술분야에서는, 아크릴아미드 중합체 및 셀룰로스 에테르를 개별적으로 사용하는 것과 관련된 단점을 극복하는 레올로지 개질제 조성물을 제공하고 개선된 증점 효율, 높은 처짐 저항 및 희석 내성, 및 사용 비용과 같은 일부 예상치 못한 이점을 갖는 비용-효율적인 레올로지 개질제 조성물을 제공하는 것에 대한 오랜 요구가 있다.
발명의 요약
한 측면에서, 본 개시내용은 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르의 블렌드를 포함하는 레올로지 개질제 조성물을 제공한다. 본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체는 비-이온성 단독중합체 또는 음이온성 공중합체 또는 양이온성 공중합체이다. 본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체는 양이온성 중합체이다. 본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체의 중량 평균 분자량은 약 600만 달톤 내지 약 1500만 달톤, 또는 800만 달톤 내지 약 1200만 달톤의 범위에서 달라진다. 본 개시내용의 한 비-제한적 실시양태에서, 셀룰로스 에테르는 글리옥살 처리 셀룰로스 에테르 또는 비-글리옥살 처리 셀룰로스 에테르이다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 셀룰로스 에테르는 히드록시에틸 셀룰로스 또는 카르복시메틸 셀룰로스 단독 또는 그의 조합이다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 셀룰로스 에테르는 비-글리옥살 처리 히드록시에틸 셀룰로스이다. 본 개시내용의 또 다른 실시양태에서, 셀룰로스 에테르는 글리옥살 처리 히드록시에틸 셀룰로스이다. 본 개시내용의 한 비-제한적 실시양태에서, 레올로지 개질제 조성물은 건조 분말 블렌드이다.
또 다른 측면에서, 본 개시내용은 본 개시내용의 레올로지 개질제 조성물을 제조하는 방법을 제공하며, 여기서 상기 방법은 (i) 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 (ii) 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르를 블렌딩하는 것을 포함한다.
또 다른 측면에서, 본 개시내용은 수성-기반 코팅에 있어서의 이러한 레올로지 개질제 조성물의 용도를 제공하며, 여기서 상기 조성물은 (i) 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 (ii) 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르의 블렌드를 포함한다.
또 다른 측면에서, 본 개시내용은 수성 코팅 조성물을 제공하며, 여기서 상기 수성 코팅 조성물은 코팅 조성물의 총 중량을 기준으로 (ia) 0.01 wt% 내지 10.0 wt%의 본 개시내용의 레올로지 개질제 조성물 또는 (ib) 0.01 wt% 내지 10.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 0.01 wt% 내지 10.0 wt%의 적어도 하나의 셀룰로스 에테르; (ii) 5.0 wt% 내지 85.0 wt%의 적어도 하나의 필름 형성 중합체; 및 (iii) 5.0 wt% 내지 15.0 wt%의 물을 포함한다. 본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체 및 셀룰로스 에테르는 둘 다 코팅 조성물 중에 블렌드로서 존재한다. 본 개시내용의 한 비-제한적 실시양태에서, 수성 코팅 조성물은 적어도 하나의 안료를 추가로 포함한다. 본 개시내용의 한 비-제한적 실시양태에서, 수성 코팅 조성물은 건축용 코팅 조성물이다.
본 발명의 개념(들)의 적어도 하나의 실시양태를 예시적인 도면, 실험, 결과, 및 실험실 절차를 통해 상세히 설명하기 전에, 본 발명의 개념(들)은 그의 응용에 있어서 하기 설명에서 설명되거나 도면, 실험 및/또는 결과에 예시된 구성요소의 구성 및 배열의 세부사항으로 제한되지 않는다는 것을 이해해야 한다. 본 발명의 개념(들)은 다른 실시양태를 취할 수 있거나 다양한 방식으로 실시 또는 수행될 수 있다. 따라서, 본원에 사용된 언어는 가능한 가장 넓은 범위 및 의미를 갖도록 의도되며; 실시양태는 예시적인 것이지 완전한 것이 아니다. 또한, 본원에 사용된 표현 및 용어는 설명을 위한 것이지 제한하는 것으로 간주되어서는 안 된다는 것을 이해해야 한다.
달리 본원에 정의되지 않는 한, 본 개시내용과 관련하여 사용되는 과학적 및 기술적 용어는 관련 기술분야의 통상의 기술자에 의해 통상적으로 이해되는 의미를 갖는다. 추가로, 달리 문맥상 요구되지 않는 한, 단수 용어는 복수를 포함하고 복수 용어는 단수를 포함한다. 일반적으로, 관련 학술어 및 본원에 설명된 화학 기술은 관련 기술분야에 널리 공지되어 있으며 통상적으로 사용되는 것들이다. 반응 및 정제 기술은 제조사의 설명서에 따라, 또는 관련 기술분야에서 통상적으로 실행되는 바와 같이, 또는 본원에 설명된 바와 같이 수행된다.
본 명세서에 언급된 모든 특허, 공개된 특허 출원, 및 비-특허 간행물은 본 개시내용이 속하는 관련 기술분야의 통상의 기술자의 기술 수준을 나타낸다. 본 출원의 임의의 부분에서 참조된 모든 특허, 공개된 특허 출원, 및 비-특허 간행물은, 각각의 개별 특허 또는 간행물이 구체적으로 및 개별적으로 참조로 포함되도록 기재되는 것과 같은 정도로, 그 전문이 명확하게 본원에 참조로 포함된다.
본원에 개시되고 청구된 모든 조성물 및/또는 방법은 본 개시내용을 고려하여 과도한 실험 없이 제조되고 실행될 수 있다. 본 발명의 조성물 및 방법은 바람직한 실시양태의 측면에서 설명되었으며, 본 발명의 개념, 진의 및 범위를 벗어나지 않게, 본원에 설명된 조성물 및/또는 방법 및 방법의 단계 또는 단계의 순서가 변경에 적용될 수 있다는 것이 관련 기술분야의 통상의 기술자에게 명백할 것이다. 관련 기술분야의 통상의 기술자에게 명백한 이러한 모든 유사한 대체 및 수정 사항은 첨부된 청구범위에 의해 정의된 바와 같은 본 발명의 개념(들)의 진의, 범위 및 개념 내에 있는 것으로 간주된다.
본 개시내용에 따라 이용되는 바와 같이, 하기 용어는, 달리 기재되어 있지 않는 한, 하기 의미를 갖는 것으로 이해해야 한다:
단어 "하나(a 또는 an)"가 청구범위 및/또는 명세서에서 용어 "포함하는(comprising)"과 함께 사용될 때, 그의 사용은 "하나"를 의미할 수 있지만, 그것은 또한 "하나 이상", "적어도 하나", 및 "하나 또는 하나 초과"의 의미와 일치한다. 청구범위에서 용어 "또는"의 사용은, 비록 개시내용에서 대안만을 및 "및/또는"을 의미하는 정의가 뒷받침된다고 하더라도, 대안만을 의미하거나 대안이 상호 배타적인 것으로 명확하게 기재되어 있지 않는 한, "및/또는"을 의미하는 데 사용된다. 본 출원 전반에 걸쳐, 용어 "약"은 어떤 하나의 값이 상기 값을 결정하는 데 사용되는 장치 및 방법에 대한 고유한 오류 변동 및/또는 연구 대상들 사이에 존재하는 변동을 포함한다는 것을 나타내는 데 사용된다. 용어 "적어도 하나"의 사용은 하나뿐만 아니라 2, 3, 4, 5, 10, 15, 20, 30, 40, 50, 100 등을 포함하지만 이로 제한되지 않는 하나 초과의 임의의 수량을 포함하는 것으로 이해될 것이다. 용어 "적어도 하나"는, 그것과 함께 사용되는 용어에 따라, 100 또는 1000 또는 그 초과까지 확장될 수 있으며; 또한, 100/1000의 수량은 제한적인 것으로 간주되어서는 안 되는데, 왜냐하면 한도가 높을수록 만족스러운 결과가 얻어질 수 있기 때문이다. 또한, 용어 "X, Y 및 Z 중 적어도 하나"의 사용은 X 단독, Y 단독, 및 Z 단독뿐만 아니라 X, Y 및 Z의 임의의 조합을 포함하는 것으로 이해될 것이다.
본 명세서 및 청구범위에 사용되는 바와 같이, 단어 "포함하는(comprising)" (및 "포함하는"의 임의의 형태, 예컨대 "포함하다(comprise 및 comprises)"), "갖는(having)" (및 "갖는"의 임의의 형태, 예컨대 "갖다(have 및 has)"), "포함하는(including)" (및 "포함하는"의 임의의 형태, 예컨대 "포함하다(includes 및 include)") 또는 "함유하는(containing)" (및 "함유하는"의 임의의 형태, 예컨대 "함유하다(contains 및 contain)")은 포함적(inclusive) 또는 개방적(open-ended)이며, 언급되지 않은 추가적인 요소 또는 방법 단계를 배제하지 않는다.
본원에 사용되는 바와 같이, 용어 "또는 그의 조합"은 상기 용어 앞에 나열된 항목들의 모든 순열 및 조합을 의미한다. 예를 들어, "A, B, C, 또는 그의 조합"은 A, B, C, AB, AC, BC, 또는 ABC 중 적어도 하나, 및 특정한 문맥에서 순서가 중요한 경우에, 또한 BA, CA, CB, CBA, BCA, ACB, BAC, 또는 CAB를 포함하도록 의도된다. 이러한 예를 계속하자면, BB, AAA, MB, BBC, AAABCCCC, CBBAAA, CABABB 등과 같이 하나 이상의 항목 또는 용어의 반복을 포함하는 조합이 명확하게 포함된다. 통상의 기술자라면, 달리 문맥상 명백하지 않는 한, 전형적으로 임의의 조합을 이루는 항목 또는 용어의 개수에는 제한이 없다는 것을 이해할 것이다.
본원에 사용되는 바와 같이, 용어 "아크릴아미드 중합체"는 아크릴아미드 기반 반복 단위의 중합에 의해 형성된 중합체를 의미하며, 여기서 상기 아크릴아미드 기반 반복 단위는 아크릴아미드이거나 알파-탄소 원자 또는 질소 원자 상에 치환된 아크릴아미드일 수 있다.
본원에 사용되는 바와 같이, 용어 "수성 코팅"은, 유기 용매의 존재에도 불구하고 액체 코팅 조성물 중에 존재하는 휘발성 용매의 대부분이 물이기 때문에 이러한 코팅이 여전히 수성으로 간주되도록, 물이 휘발성 상의 50% 초과, 바람직하게는 적어도 80%를 구성한다는 전제 하에 이러한 코팅이 소량의 공-용매 및 다른 휘발성 유기 물질을 포함할 수 있다는, 관련 기술분야에서 인정된 의미를 갖는다.
본원에 사용되는 바와 같이, 용어 "건축용 코팅"은, 주로 물인, 연속상이라고 통상적으로 지칭되는 수성 상에 수지 결합제가 용해, 분산 또는 유화되어 있는 것을 특징으로 하는 그러한 수성 페인트를 지칭한다. 적합한 수성 결합제는 전분, 개질 전분, 폴리비닐 알콜, 폴리비닐 아세테이트, 폴리에틸렌/아크릴산 공중합체, 아크릴산 중합체, 폴리아크릴레이트, 폴리아크릴아미드 공중합체, 아크릴로니트릴/부타디엔/스티렌 공중합체 및 폴리아크릴로니트릴과 같은 물질을 포함할 수 있다. 수-불용성 결합제의 적합한 비-제한적 예는 폴리아크릴레이트, 메타크릴레이트, 비닐-아크릴, 스티렌-아크릴 등을 포함할 수 있다.
본 개시내용의 한 측면은 레올로지 개질제 조성물을 제공한다. 본 개시내용의 레올로지 개질제 조성물은 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 적어도 하나의 셀룰로스 에테르의 블렌드를 포함한다. 본 개시내용의 한 비-제한적 실시양태에서, 폴리아크릴아미드 중합체는 약 0.05 wt% 내지 약 70.0 wt%의 양으로 존재할 수 있다. 셀룰로스 에테르는 레올로지 개질제 조성물의 총 중량을 기준으로 약 30.0 wt% 내지 약 99.95 wt%의 양으로 존재할 수 있다.
본 개시내용에 따른 아크릴아미드 중합체는 비-이온성 단독중합체, 음이온성 공중합체 또는 양이온성 공중합체일 수 있다. 본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체는 단독중합체이다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 아크릴아미드 중합체는 음이온성 공중합체이다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 아크릴아미드 중합체는 양이온성 중합체이다. 본 개시내용에 따른 음이온성 공중합체는 하나 이상의 산 관능기 또는 무수물 관능기 또는 그의 임의의 조합과 S, N, O 및 P로 이루어진 군으로부터 선택된 하나 이상의 헤테로 원자를 갖는 적어도 하나의 단량체 단위를 포함한다. 이러한 단량체의 적합한 예는 아크릴산, 메타크릴산, 말레산 또는 무수물, 이타콘산 또는 무수물, 아크릴아미도 프로판 술폰산, 비닐 포스폰산 등을 포함할 수 있지만 이로 제한되지 않는다. 유사하게, 양이온성 중합체의 적합한 예는 3-아크릴아미도 프로필 트리메틸 암모늄 클로라이드, 3-메타크릴아미도 프로필 트리메틸 암모늄 클로라이드 등을 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용에 따른 아크릴아미드 중합체는 약 600만 달톤 내지 약 1500만 달톤 범위의 평균 분자량을 가질 수 있다. 본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체의 분자량은 800만 달톤 내지 1200만 달톤의 범위에서 달라진다.
본 개시내용의 목적에 유용한 아크릴아미드 중합체는 관련 기술분야에 공지된 종래의 방법에 의해 제조될 수 있다. 대안적으로, 상업적으로 입수 가능한 중합체가 또한 조달될 수 있다. 이러한 상업적으로 입수 가능한 중합체의 적합한 예는 플로팜(FLOPAM)®, 예컨대 FA 920 VHM, FA 920 VHR, FA 920 SH, FA 920 SHR, FA 920 SD, FA 920 SHD, FA 920, FA 920 HD, AN 905 SH, AN 905 SHU, AN 910 SH, AN 910 SHU, AN 913 SH, AN 913 SHU, AN 923 SH, AN 923 SHU, AN 926 SH 등 (에스엔에프(SNF)로부터 입수 가능함); 및 프라에스톨(PRAESTOL), 예컨대 2500/2500TR, 2510, 2515/2515TR, 2520, 2525, 2530/2530TR, 2540/2540TR, 2640, 644BC, 650BC 등 (솔레니스(Solenis)로부터 입수 가능함)을 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용의 레올로지 개질제 조성물에 사용되는 셀룰로스 에테르는 히드록시알킬 셀룰로스 에테르일 수 있다. 추가로, 본 개시내용의 목적에 유용한 셀룰로스 에테르는 글리옥살-처리 셀룰로스 에테르 또는 비-글리옥살 처리 셀룰로스 에테르일 수 있다. 이러한 셀룰로스 에테르의 적합한 예는 히드록시에틸 셀룰로스 (HEC), 히드록시프로필 셀룰로스 (HPC), 에틸 히드록시에틸 셀룰로스 (EHEC), 카르복시메틸 셀룰로스 (CMC), 카르복시메틸 히드록시에틸 셀룰로스 (CMHEC), 히드록시프로필 히드록시에틸 셀룰로스 (HPHEC), 메틸 셀룰로스 (MC), 메틸 히드록시프로필 셀룰로스 (MHPC), 메틸 히드록시에틸 셀룰로스 (MHEC), 카르복시메틸 메틸셀룰로스 (CMMC), 소수성 개질 카르복시메틸 셀룰로스 (HMCMC), 소수성 개질 히드록시에틸 셀룰로스 (HMHEC), 소수성 개질 히드록시프로필 셀룰로스 (HMHPC), 소수성 개질 에틸 히드록시에틸 셀룰로스 (HMEHEC), 소수성 개질 카르복시메틸 히드록시에틸 셀룰로스 (HMCMHEC), 소수성 개질 히드록시프로필 히드록시에틸 셀룰로스 (HMHPHEC), 소수성 개질 메틸 셀룰로스 (HM MC), 소수성 개질 메틸 히드록시프로필 셀룰로스 (HMMHPC), 소수성 개질 메틸 히드록시에틸 셀룰로스 (HMMHEC), 소수성 개질 카르복시메틸 메틸셀룰로스 (HMCMMC), 양이온성 히드록시에틸 셀룰로스 (양이온성 HEC), 양이온성 소수성 개질 히드록시에틸 셀룰로스 (양이온성 HMHEC), 및 그의 임의의 조합을 포함할 수 있지만 이로 제한되지 않는다. 본 개시내용의 한 비-제한적 실시양태에서, 셀룰로스 에테르는 글리옥살-처리 히드록시에틸 셀룰로스일 수 있다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 셀룰로스 에테르는 비-글리옥살 처리 히드록시에틸 셀룰로스일 수 있다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 셀룰로스 에테르는 히드록시에틸 셀룰로스 또는 카르복시메틸 셀룰로스 단독 또는 그의 조합일 수 있다.
추가로, 본 개시내용의 목적에 유용한 셀룰로스 에테르는 관련 기술분야에 공지된 방법에 의해 제조될 수 있거나, 또한 임의의 상업적으로 입수 가능한 제품, 예컨대 나트로솔(NATROSOL) 250 HHBR, 나트로솔 250 H4BR, 나트로솔 250 MHBR (애쉬랜드 엘엘씨(Ashland LLC)로부터 입수 가능함)이 사용될 수 있다.
본 개시내용의 한 비-제한적 실시양태에서, 아크릴아미드 중합체는 총 레올로지 개질제 조성물 중량의 약 0.05 wt% 내지 약 50.0 wt%, 또는 약 0.05 wt% 내지 약 30.0 wt% 범위의 양으로 존재할 수 있다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 아크릴아미드 중합체는 양이온성 중합체이고 총 레올로지 개질제 조성물 중량의 약 0.05 wt% 내지 약 50.0 wt%, 또는 약 0.05 wt% 내지 약 30.0 wt%의 양으로 존재할 수 있다. 본 개시내용의 한 비-제한적 실시양태에서, 셀룰로스 에테르의 양은 총 레올로지 개질제 조성물 중량의 약 50.0 wt% 내지 약 99.95 wt%, 또는 약 70.0 wt% 내지 약 99.95 wt%에서 달라질 수 있다. 셀룰로스 에테르가 히드록시에틸 셀룰로스와 카르복시메틸 셀룰로스의 조합인 본 개시내용의 실시양태에서, 그의 총량은 총 레올로지 개질제 조성물 중량의 약 50.0 wt% 내지 약 99.95 wt%, 또는 약 70.0 wt% 내지 약 99.95 wt%의 범위에서 달라질 수 있다.
본 개시내용의 레올로지 개질제 조성물은 소수성 개질 에톡실화 우레탄 중합체, 소수성 개질 폴리아세탈-폴리에테르 중합체, 소수성 개질 알칼리 팽윤성 유화액, 소수성 개질 아미노플라스트, 알칼리 팽윤성 유화액, 및 그의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 회합성 중합체를 추가로 포함할 수 있다. 본 개시내용의 한 비-제한적 실시양태에서, 회합성 중합체는 소수성 개질 폴리아세탈-폴리에테르 중합체이다.
레올로지 개질제 조성물은 계면활성제; 분산제; 증점제; 케이킹방지제; 소포제; 보존제; 왁스, 실리콘 및 탄화수소를 포함하는 소수성 작용제; 상용화제; 접착 촉진제; 안정화제; 가교제; 및 그의 임의의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 첨가제를 추가로 포함할 수 있다.
분산제의 적합한 예는 폴리카르복실산, 카르복실화 다가전해질 염, 트리폴리포스페이트 염 및 테트라포타슘 피로포스페이트, 에톡실화 지방 알콜, 아미노 알콜, 아크릴 공중합체, 나프탈렌 술폰산-포름알데히드 부가물, 술폰화 지방산, 대두 레시틴, 폴리에틸렌 글리콜 디올레에이트, 대두 레시틴, PEG 디올레에이트, 폴리에틸렌 글리콜, 폴리프로필렌 글리콜, 메톡시 폴리에틸렌 글리콜, 폴리에틸렌 글리콜 모노스테아레이트, 폴리에틸렌 글리콜 디-스테아레이트, 및 그의 조합을 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용의 레올로지 개질제 조성물은 아크릴아미드 중합체와 셀룰로스 에테르의 건조 분말 블렌드이다. 본 개시내용에 따른 아크릴아미드 중합체와 셀룰로스 에테르의 건조 분말 블렌드는 아크릴아미드 중합체와 셀룰로스 에테르를 블렌딩함으로써 제조될 수 있다. 본 개시내용의 또 다른 측면은 (i) 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 (ii) 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르를 블렌딩하는 것을 포함하는 본 개시내용의 레올로지 개질제 조성물을 제조하는 방법을 제공한다. 관련 기술분야에 공지된, 건조 분말 블렌드를 제조하기 위한 임의의 건식 블렌딩 기술 또는 장치를 적합하게 사용하여 본 개시내용의 아크릴아미드 중합체와 셀룰로스 에테르를 블렌딩할 수 있다. 이러한 건식 블렌딩 기술 또는 장치의 적합한 예는 막자사발 및 막자, 볼 밀, 또는 어트리터 밀에서의 건식 블렌딩을 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용의 또 다른 비-제한적 실시양태에서, 셀룰로스 에테르는 레올로지 개질제 조성물의 총 중량을 기준으로 약 50.0 wt% 내지 약 99.95 wt%, 또는 약 70.0 wt% 내지 약 99.95 wt%의 양으로 사용될 수 있다. 유사하게, 아크릴아미드 중합체는 본 레올로지 개질제 조성물의 총 중량을 기준으로 약 0.05 wt% 내지 약 50.0 wt% 또는 약 0.05 wt% 내지 약 30.0 wt%의 양으로 사용될 수 있다.
추가로, 추가적인 첨가제가 또한 본 레올로지 개질제 조성물의 제조 동안 첨가될 수 있다. 이러한 첨가제는 계면활성제; 분산제; 증점제; 케이킹방지제; 소포제; 보존제; 왁스, 실리콘 및 탄화수소를 포함하는 소수성 작용제; 상용화제; 접착 촉진제; 가교제; 및 그의 임의의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 첨가제를 포함할 수 있다.
본 개시내용의 레올로지 개질제 조성물은 수성 코팅 조성물에 사용될 수 있다. 특히, 본 개시내용의 레올로지 개질제 조성물은 모든 종류의 코팅, 예컨대 장식용 및 보호용 코팅, 및 종이 코팅에 유용하다. 수성 보호용 코팅 조성물은 통상적으로 라텍스 페인트 또는 분산 페인트로서 공지되어 있으며 상당히 오랫동안 공지되어 있다. 수성 코팅 조성물에 사용되는 레올로지 개질제는 점도를 특정한 가공 조건 및 최종 사용 상황에서 요구되는 수준으로 증가시키고 유지한다. 수성 보호용 코팅 조성물은 레올로지 개질제의 선택을 통해 우수한 평활화 및 탁월한 처짐 저항을 제공해야 한다. 본 개시내용의 또 다른 측면은 수성 기반 코팅에 있어서의 본 개시내용의 레올로지 개질제 조성물의 용도를 제공하며, 여기서 상기 조성물은 (i) 약 0.05 wt% 내지 약 70.0 wt%의 아크릴아미드 중합체; 및 (ii) 약 30.0 wt% 내지 약 99.95 wt%의 적어도 하나의 셀룰로스 에테르의 블렌드를 포함한다.
본 개시내용의 또 다른 측면은 상기에 설명된 바와 같은 본 개시내용의 레올로지 개질제 조성물을 포함하는 수성 코팅 조성물을 제공한다. 수성 코팅 조성물은 600만 달톤 초과의 분자량을 갖는 아크릴아미드 중합체 및 적어도 하나의 셀룰로스 에테르를 포함하는 레올로지 개질제 조성물, 적어도 하나의 필름 형성 중합체, 및 물을 포함하거나 이로 이루어지거나 이로 본질적으로 이루어진다.
본 개시내용의 수성 코팅 조성물에 사용되는 레올로지 개질제 조성물의 양은 원하는 증점 및 레올로지적 특성을 수성 코팅 조성물에 제공하는 데 효과적인 양이므로, 원하는 레올로지적 특성 및 사용되는 분산액 둘 다에 따라 달라질 것이다. 추가로, 레올로지 개질제 조성물은 600만 달톤 초과의 분자량을 갖는 아크릴아미드 중합체와 적어도 하나의 셀룰로스 에테르의 건조 분말 블렌드로서 본 개시내용의 수성 코팅 조성물에 첨가될 수 있다. 대안적으로, 600만 달톤 초과의 분자량을 갖는 아크릴아미드 중합체 및 적어도 하나의 셀룰로스 에테르가 본 개시내용의 수성 코팅 조성물에 개별적으로 첨가될 수 있다.
레올로지 개질제 조성물이 건조 분말 블렌드로서 수성 코팅 조성물에 첨가될 수 있는 본 개시내용의 실시양태에서, 레올로지 개질제 조성물의 양은 수성 코팅 조성물의 총 중량을 기준으로 약 0.01 wt% 내지 약 10.0 wt%의 범위에서 달라질 수 있다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 상기 양은 수성 코팅 조성물의 총 중량의 약 0.05 wt% 내지 약 5.0 wt%의 범위에서 달라질 수 있다.
아크릴아미드 중합체 및 셀룰로스 에테르가 개별적으로 첨가되는 본 개시내용의 실시양태에서, 그의 각각의 양은 전형적으로 총 수성 코팅 조성물 중량의 약 0.01 wt% 내지 약 10.0 wt%의 범위에서 달라진다. 아크릴아미드 중합체 및 셀룰로스 에테르가 수성 코팅 조성물에 개별적으로 첨가되는 경우에, 그것들은 그의 상승작용적 건조 블렌드로서 존재한다. 이러한 경우에, 그의 합산된 중량 비율은 총 수성 코팅 조성물 중량의 약 0.01 wt% 내지 약 10.0 wt%, 또는 약 0.05 wt% 내지 약 5.0 wt%의 범위에서 달라질 수 있다.
본 개시내용의 수성 코팅 조성물은 적어도 하나의 필름 형성 중합체를 포함하는 수성 중합체 분산액이다. 본 개시내용의 수성 코팅 조성물에 사용되는 필름 형성 중합체는 관련 기술분야에 공지된 다양한 중합체로부터 선택될 수 있다. 예를 들어, 이러한 필름 형성 중합체는 다양한 에틸렌계 불포화 단량체, 예컨대 에틸렌, 비닐 및 아크릴 단량체로부터 제조될 수 있다. 이러한 단량체의 예는 아크릴산, 메타크릴산, 메타크릴산 에스테르, 스티렌, α-메틸 스티렌, 비닐 클로라이드, 아크릴로니트릴, 메타크릴로니트릴, 우레이도 메타크릴레이트, 비닐 아세테이트, 분지형 3급 모노카르복실산의 비닐 에스테르, 이타콘산, 크로톤산, 말레산, 푸마르산, 및 에틸렌을 포함할 수 있지만 이로 제한되지 않는다. C4-C8 공액화 디엔, 예컨대 1,3-부타디엔, 이소프렌 및 클로로프렌을 포함하는 것이 또한 가능하다. 필름 형성 중합체는, 특히 휘발성 유기 화합물 (VOC)을 거의 또는 전혀 갖지 않는 라텍스 페인트에 응용되는 경우에, 여러 원하는 특성을 달성하기 위해 하나 초과의 단량체의 공중합 생성물일 수도 있다. 적합한 필름 형성 중합체의 예는 비닐 아세테이트, 메타크릴산, 메틸아크릴레이트, 메틸메타크릴레이트, 에틸아크릴레이트, 부틸 아크릴레이트, 스티렌, 에틸렌, 비닐 클로라이드, 베르사트산의 비닐 에스테르 (VeoVa), 비닐 프로피오네이트, 부타디엔, 아크릴로니트릴, 말레에이트, 및 푸마레이트의 단독- 또는 공-중합체를 포함할 수 있지만 이로 제한되지 않는다. 본 개시내용의 한 비-제한적 실시양태에서, 필름 형성 중합체는 아크릴, 비닐-아크릴 및 스티렌-아크릴, 스티렌-부타디엔 공중합체, 비닐 아세테이트 에틸렌, 부타디엔-아크릴로니트릴 공중합체, 에폭시드, 우레탄, 폴리아미드, 베르사트산의 비닐 에스테르 (VeoVa), 및 폴리에스테르로 이루어진 군으로부터 선택된다.
다른 적합한 필름 형성 중합체의 예는 알키드, 셀룰로스 (셀룰로스 니트레이트 및 셀룰로스 에스테르), 쿠마론-인덴, 에폭시, 에스테르, 탄화수소, 멜라민, 천연 수지, 올레오 수지, 페놀화합물, 폴리아미드, 폴리에스테르, 로진, 실리콘, 테르펜, 요소, 우레탄, 및 비닐을 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용의 수성 코팅 조성물 중 필름 형성 중합체의 양은 총 수성 코팅 조성물 중량을 기준으로 약 5.0 wt% 내지 약 85.0 wt%의 범위에서 달라질 수 있다. 본 개시내용의 한 비-제한적 실시양태에서, 필름 형성 중합체의 양은 총 수성 코팅 조성물 중량을 기준으로 약 40.0 wt% 내지 약 70.0 wt%, 또는 약 50.0 wt% 내지 약 70.0 wt%에서 달라질 수 있다.
본 개시내용의 수성 코팅 조성물은 적어도 하나의 안료를 추가로 포함할 수 있다. 안료는 프탈로시아닌, 산화철, 이산화티타늄, 산화아연, 인디고, 수화된 산화알루미늄, 황산바륨, 규산칼슘, 점토, 실리카, 활석, 탄산칼슘, 및 그의 혼합물로 이루어진 군으로부터 선택될 수 있다. 종종, 수성 코팅 조성물에 사용되는 이산화티타늄 등급은 다양한 무기 산화물, 예컨대 실리케이트, 알루미네이트, 및 지르코네이트로 표면 개질된다. 규산알루미늄, 하석 섬장암, 운모, 탄산칼슘, 및/또는 규조토가 또한 사용될 수 있다.
본 개시내용의 수성 코팅 조성물 중에 존재하는 안료의 유형 및 양은 건조된 필름의 광택, 투과성, 스크럽 저항, 인장 강도 등과 같은 성능 특성을 결정한다. 따라서, 코팅은 그의 안료 부피 농도 (PVC)에 의해 특성화된다. PVC는 백분율이며, 건조된 필름에 존재하는 총 고체에 대한 안료의 부피 비율을 나타낸다. PVC는 하기와 같이 정의된다:
PVC % = 안료 부피/ (안료 부피 + 라텍스 부피) x 100
안료 입자들 사이의 모든 공극이 필름 형성 중합체로 정확히 채워질 때의 농도는 임계 안료-부피 농도 (CPVC)라고 불린다.
본 개시내용의 수성 코팅 조성물은 약 85 중량%의 PVC 상한을 갖는다. 본 개시내용의 한 비-제한적 실시양태에서, 수성 코팅 조성물은 약 75 중량%의 PVC 상한을 갖는다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 수성 보호용 코팅은 약 65 중량%의 PVC 상한을 갖는다. 유사하게, 본 개시내용의 수성 코팅 조성물은 약 10 중량%의 PVC 하한을 갖는다. 본 개시내용의 또 다른 비-제한적 실시양태에서, 수성 코팅 조성물은 약 20 중량%의 PVC 하한을 갖는다. 더 특히, 라텍스 페인트가 고광택 페인트인 경우에, PVC는 약 15 중량% 내지 약 30 중량%이고; 페인트가 반-광택 페인트인 경우에, PVC는 약 20 중량% 내지 약 35 중량%이고; 그것이 무광택 페인트인 경우에, PVC는 약 40 중량% 내지 약 85 중량%이다. 안료는 건조 분말 형태 또는 슬러리 형태로 수성 코팅 조성물에 첨가될 수 있다.
수성 코팅 조성물의 잔여분은 물이다. 물은 필름 형성 중합체 분산액 및 수성 코팅 조성물의 다른 성분에 존재할 수 있다. 대안적으로, 물은 또한 별도로 수성 코팅 조성물에 첨가될 수 있다.
본 개시내용의 수성 코팅 조성물은 적어도 하나의 첨가제를 추가로 포함할 수 있다. 이러한 첨가제의 예는 계면활성제; 분산제, 예컨대 폴리포스페이트, 아미노 알콜, 및 아크릴 공중합체; 증점제; 케이킹방지제; 소포제, 예컨대 비실리콘 및 실리콘 유형; 가소제; 증량제; 보존제; 왁스, 실리콘 및 탄화수소를 포함하는 소수성 작용제; 상용화제; 접착 촉진제; 가교제; 살생물제; 곰팡이방지제(mildewcide); 탈포제, 예컨대 비실리콘 및 실리콘 유형; 공-용매; 응집제, 예컨대 글리콜 에테르/에스테르; 및 그의 임의의 조합을 포함할 수 있지만 이로 제한되지 않는다. 이러한 첨가제는 종래의 수성 코팅 조성물의 관련 기술분야에 공지된 바와 같은 방식 및 양으로 사용될 수 있다.
본원에 설명된 수성 코팅 조성물은 다양한 응용분야에 사용될 수 있다. 특히, 본 개시내용의 레올로지 개질제 조성물은 모든 종류의 코팅, 예컨대 건축 표면, 예를 들어, 벽, 천장, 문, 트림 등을 위한 장식용 및 보호용 코팅; 종이 코팅; 석벽, 벽돌, 목재, 금속, 플라스틱, 및 프라이머 처리된 표면 등을 위한 코팅에 유용하다. 본 개시내용의 한 비-제한적 실시양태에서, 코팅 조성물은 내부 및/또는 외부 건축 표면을 위한 건축용 코팅 조성물이다.
본 개시내용의 또 다른 측면은 본 개시내용의 수성 코팅 조성물을 제조하는 방법을 추가로 제공하며, 여기서 상기 방법은 적어도 하나의 필름 형성 중합체, 본 개시내용의 레올로지 개질제 조성물, 및 물을 교반 하에 혼합 또는 블렌딩하는 것을 포함한다. 수성 건축용 코팅을 제공하기 위해, 유리하게는 안료가 첨가될 수 있다. 상기에 설명된 첨가제는 또한 임의의 적합한 순서로 필름 형성, 레올로지 개질제, 안료, 또는 그의 조합에 첨가될 수 있다.
수성 코팅 조성물은 보호용 코팅으로서 다양한 표면 물질에 도포될 수 있는 안정적인 유체이다. 이러한 물질의 예는 종이, 목재, 콘크리트, 금속, 유리, 세라믹, 플라스틱, 석고, 및 지붕 기재, 예컨대 아스팔트 코팅, 지붕 펠트, 발포 폴리우레탄 단열재; 또는 이전에 페인팅된, 프라이머 처리된, 언더코팅된, 마모된, 또는 풍화된 기재를 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용의 또 다른 측면은 본 개시내용의 수성 코팅 조성물을 다양한 표면에 도포하는 방법을 제공한다. 수성 코팅 조성물은 관련 기술분야의 통상의 기술자에게 공지된 다양한 종래의 방법에 의해 하나 이상의 표면에 도포될 수 있다. 이러한 도포 방법의 예는 에어로졸 스프레이, 브러시, 롤러, 에어리스 스프레이, 공기-보조 스프레이, 정전 스프레이, 고용량 저압 (HVLP) 스프레이 등에 의한 도포를 포함할 수 있지만 이로 제한되지 않는다.
본 개시내용의 레올로지 개질제 조성물은 증점 효율, 처짐 저항 등과 같은 페인트 배합물의 특정한 레올로지적 특성에 유리하게 영향을 미친다. 본 발명자들은 놀랍게도, 아크릴아미드 중합체와 셀룰로스 에테르의 블렌드를 포함하는 이러한 조성물이 순수한 아크릴아미드 중합체 또는 전통적인 비-회합성 증점제, 예컨대 셀룰로스와 비교하여 유사하거나 개선된 응용 성능, 예컨대 더 우수한 희석 내성 및 개선된 은폐능과 함께 일부 독특하고 예상치 못한 속성, 예컨대 개선된 효율 (사용 비용) 및 증점 효율을 나타낸다는 것을 발견하였다. 이러한 레올로지 개질제 조성물은 페인트 배합물의 전반적인 증점 효율 (스토머(Stormer) 점도, 브룩필드(Brookfield) 점도 및 ICI 점도)을 향상시키거나 개선하며, 또한 비닐 아세테이트 에틸렌 (VAE) 라텍스 페인트와 같이 증점하기 어려운 페인트 배합물에 특히 적합하다. 추가적으로, 본 레올로지 개질제 조성물은 또한 개선된 처짐 저항 등과 같은 상당한 구조를 건축용 페인트에 제공한다.
하기 실시예는 본원에 개시 및/또는 청구된 본 발명의 개념(들)을 예시하며, 달리 기재되어 있지 않는 한, 부 및 백분율은 중량을 기준으로 한다. 각각의 실시예는 본원에 개시 및/또는 청구된 본 발명의 개념(들)을 제한하는 것이 아니라 본원에 개시 및/또는 청구된 본 발명의 개념(들)을 설명하기 위해 제공된다. 실제로, 본 발명의 범위 또는 진의를 벗어나지 않게, 본원에 개시 및/또는 청구된 본 발명의 개념(들)은 다양한 수정 및 변경에 적용될 수 있다는 것이 관련 기술분야의 통상의 기술자에게 명백할 것이다. 예를 들어, 한 실시양태의 일부로서 예시 또는 설명된 특징은 또 다른 실시양태에서 사용되어 추가의 실시양태를 이룰 수 있다. 따라서, 본원에 개시 및/또는 청구된 본 발명의 개념(들)은 첨부된 청구범위 및 그 균등물의 범위 내에 있는 이러한 수정 및 변경 사항을 포괄하도록 의도된다.
실시예
시험 방법
달리 기재되어 있지 않는 한, 하기 시험 방법이 실시예에서 이용되었다:
증점 효율 측정
증점 효율을, 활성 물질을 기준으로 0.15 wt%의, 실시예에서 수득된 중합체 샘플을 표 2에 나열된 건축용 코팅 배합물에 첨가함으로써 측정하였다. 증점 효율을 증점된 건축용 코팅 조성물의 스토머 점도 (KU), 브룩필드 점도 및 ICI 점도를 통해 측정하였다.
브룩필드 점도를 30 RPM 및 25℃에서 스핀들 #5를 갖는 브룩필드 점도계를 사용하여 측정하였다. 그것을 mPa.s 단위로 표현한다.
스토머 점도를 스토머 점도계를 사용하여 표준 시험 방법 ASTM D562에 따라 측정하였다. 그것을 크렙(Kreb) 단위 (KU)로 표현한다.
ICI 점도를 ICI 원뿔-평판 점도계를 사용하여 표준 시험 방법 ASTMD4287에 따라 측정하였다. 그것을 mPa.s 단위로 표현한다.
처짐 저항을 다양한 간격의 다중-노치 드로우다운 도포기(multi-notch drawdown applicator) (레네타 컴퍼니(Leneta Company)로부터의 처짐-저항 측정기)를 사용하여 ASTM D4400에 따라 페인트를 드로우다운함으로써 측정하였다. 처짐 저항을 mil 단위의 처짐 지수 수치로서 기록한다.
실시예 1: HEC와 아크릴아미드 중합체 (플로팜 AN 923SH)의 블렌드
실시예 1의 레올로지 개질제 조성물의 모든 샘플을, 건조 과립 형태의 히드록시에틸 셀룰로스 (애쉬랜드 엘엘씨로부터 입수 가능한 HEC HBR 250PA)와 중간 정도의 음이온성 및 1200만-1400만 달톤 Mw를 갖는 일종의 음이온성 아크릴아미드 중합체인 아크릴아미드 중합체 (에스엔에프로부터 입수 가능한 플로팜 AN 923SH)를 표 1에 제시된 바와 같은 중량 비율로 블렌딩함으로써 제조하였다. 전형적인 실험에서는, 히드록시에틸 셀룰로스 (HEC HBR 250PA)를 8 oz 유리병에서 아크릴아미드 중합체 (AN 923SH)와 혼합하고, 그의 균질한 혼합물이 수득될 때까지 하빌(Harbil) 혼합물을 사용하여 블렌딩하였다.
대조 실시예: 대조 레올로지 개질제 조성물 (CE.1A 및 CE.1B):
두 가지의 서로 상이한 대조 레올로지 개질제 조성물들 (CE.1A 및 CE.1B)을, 실시예 1에 설명된 것과 동일한 방식으로, 100 wt%의 아크릴아미드 중합체 (플로팜 AN 923SH) 또는 100 wt%의 HEC HBR 250PA를 사용하여 제조하고, 실시예 1의 레올로지 개질제 조성물과 비교하였다.
<표 1>
실시예 1의 레올로지 개질제 조성물을 페인트 배합물 (표 2A 및 표 2B에 제시됨)에 0.15 wt%로 첨가하였다. 배합된 수성 페인트 조성물을 밤새 평형화한 후에 브룩필드 점도, 스토머 점도 및 ICI 점도 응답을 측정하였다. 습윤 코팅의 처짐 및 적하에 저항하는 건축용 코팅 조성물의 능력인 처짐 저항을 또한 측정하였다. 처짐 지수 수치가 높을수록, 새로 도포된 습윤 코팅의 적하를 방지하는 코팅 조성물의 능력이 더 크다.
<표 2A>
프록셀(Proxel) GXL, 론자 컴퍼니(Lonza Company)로부터 상업적으로 입수 가능한 살생물제.
드류플러스(Drewplus)TM L-475: 애쉬랜드 엘엘씨로부터 상업적으로 입수 가능한 탈포제.
타몰(Tamol)TM 731A: 더 다우 케미칼 컴퍼니(The Dow Chemical Company)로부터 상업적으로 입수 가능한 분산제.
스트로덱스(Strodex)TM PK-90: 애쉬랜드 엘엘씨로부터 상업적으로 입수 가능한 계면활성제.
스트로덱스TM TH-4427: 애쉬랜드 엘엘씨로부터 상업적으로 입수 가능한 계면활성제.
트로녹스(Tronox)® CR-828: 트로녹스 리미티드(Tronox Limited)로부터 상업적으로 입수 가능한 금홍석 이산화티타늄 안료.
옵티화이트(Optiwhite) MX: 버게스 피그먼트 컴퍼니(Burgess pigment company)로부터 상업적으로 입수 가능한 하소된 규산알루미늄 안료.
AMP-95: 앵거스 케미칼 컴퍼니(Angus Chemical company)로부터 상업적으로 입수 가능한 중화제.
<표 2B>
*아크로날(Acronal) 296D: 다우 케미칼즈(Dow Chemicals)로부터 상업적으로 입수 가능한 스티렌 부틸 아크릴레이트 유화액
**옵티필름(Optifilm)TM 강화제 400: 이스트만 케미칼 컴퍼니(Eastman Chemical Company)로부터 상업적으로 입수 가능한 응집제.
실시예 2: HEC와 아크릴아미드 중합체 (프라에스톨 A 2530)의 블렌드
본 실시예의 레올로지 개질제 조성물을, 실시예 1에 설명된 것과 동일한 방식으로, 아크릴아미드 중합체 (솔레니스로부터 입수 가능한 프레아스톨 A 2530 음이온성 중합체) 및 히드록시에틸 셀룰로스 (HEC HBR 250PA) 분말을 표 3에 제시된 바와 같은 중량 비율로 사용하여 제조하였다.
이러한 조성물을 0.15 wt%로 페인트 배합물 (표 2A 및 표 2B에 제시됨)에 첨가하였다. 이러한 조성물을 사용하는 페인트 배합물의 스토머 점도, 브룩필드 점도 및 ICI 점도를 포함하는 점도 데이터; 및 처짐 지수 수치 데이터가 표 3에 제시되어 있다.
<표 3>
실시예 3: HEC와 아크릴아미드 중합체 (플로팜 920 VHM)의 블렌드
본 실시예의 레올로지 개질제 조성물을, 아크릴아미드 중합체 (에스엔에프로부터 입수 가능한 플로팜 920 VHM)를 사용한다는 것을 제외하고는 상기 실시예 2에 설명된 것과 동일한 방식으로 제조하였다. 아크릴아미드 중합체 및 히드록시에틸 셀룰로스 분말을 표 4에 제시된 바와 같은 중량 비율로 건식 블렌딩하였다. 이러한 레올로지 개질제 조성물을 0.15 wt%로 페인트 배합물 (표 2A 및 표 2B)에 첨가하였다. 처짐 저항 지수 수치를 포함한, 스토머 점도 (KU), 브룩필드 점도 및 ICI 점도 데이터가 표 4에 제시되어 있다.
<표 4>
실시예 4: 페인트의 증점 효율에 미치는 아크릴아미드 중합체의 Mw의 영향
본 실시예에서는, 서로 상이한 분자량 (Mw)을 갖는 아크릴아미드 중합체들을 사용하여 아크릴아미드 중합체의 Mw가 페인트 배합물의 증점 효율에 미치는 영향을 평가하였다. 표 5에는 사용된 아크릴아미드 중합체 (에스엔에프로부터 입수 가능한 플로팜 중합체) 및 그의 분자 wt. (Mw)를 포함하는 목록이 제시되어 있다. 이러한 중합체는 0.34 wt% (개별 wt.)로 47 PVC 스티렌 부틸 아크릴레이트 베이스 페인트 배합물 (표 2A 및 표 2B)에 첨가되었다.
<표 5>
표 5의 데이터로부터, 특히 비-이온성 아크릴아미드 중합체에서, 아크릴아미드 중합체의 Mw가 감소함에 따라 페인트 배합물의 증점 효율 (KU, 브룩필드 및 ICI 점도)이 모두 감소한다는 것이 분명하다.
Claims (28)
- (i) 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및
(ii) 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르
의 블렌드를 포함하는 레올로지 개질제 조성물. - 제1항에 있어서, 아크릴아미드 중합체가 비-이온성 단독중합체, 음이온성 공중합체 또는 양이온성 공중합체인 레올로지 개질제 조성물.
- 제1항에 있어서, 아크릴아미드 중합체가 양이온성 중합체인 레올로지 개질제 조성물.
- 제2항에 있어서, 음이온성 공중합체가, 하나 이상의 산 관능기 또는 무수물 관능기 또는 그의 조합과 S, N, O 및 P로 이루어진 군으로부터 선택된 하나 이상의 헤테로 원자를 갖는 적어도 하나의 단량체를 포함하는 것인 레올로지 개질제 조성물.
- 제4항에 있어서, 단량체가 아크릴산, 메타크릴산, 말레산 또는 무수물, 이타콘산 또는 무수물, 크로톤산, 푸마르산 및 시트라콘산으로 이루어진 군으로부터 선택된 것인 레올로지 개질제 조성물.
- 제1항에 있어서, 아크릴아미드 중합체의 중량 평균 분자량이 약 600만 달톤 내지 약 1500만 달톤의 범위에서 달라지는 것인 레올로지 개질제 조성물.
- 제1항에 있어서, 아크릴아미드 중합체의 중량 평균 분자량이 약 800만 달톤 내지 약 1200만 달톤의 범위에서 달라지는 것인 레올로지 개질제 조성물.
- 제1항에 있어서, 셀룰로스 에테르가, 히드록시에틸 셀룰로스 (HEC), 히드록시프로필 셀룰로스 (HPC), 에틸 히드록시에틸 셀룰로스 (EHEC), 카르복시메틸 셀룰로스 (CMC), 카르복시메틸 히드록시에틸 셀룰로스 (CMHEC), 히드록시프로필 히드록시에틸 셀룰로스 (HPHEC), 메틸셀룰로스 (MC), 메틸 히드록시프로필 셀룰로스 (MHPC), 메틸 히드록시에틸 셀룰로스 (MHEC), 카르복시메틸 메틸 셀룰로스 (CMMC), 소수성 개질 카르복시메틸 셀룰로스 (HMCMC), 소수성 개질 히드록시에틸 셀룰로스 (HMHEC), 소수성 개질 히드록시프로필 셀룰로스 (HMHPC), 소수성 개질 에틸 히드록시에틸 셀룰로스 (HMEHEC), 소수성 개질 카르복시메틸 히드록시에틸 셀룰로스 (HMCMHEC), 소수성 개질 히드록시프로필 히드록시에틸 셀룰로스 (HMHPHEC), 소수성 개질 메틸 셀룰로스 (HMMC), 소수성 개질 메틸 히드록시프로필 셀룰로스 (HMMHPC), 소수성 개질 메틸 히드록시에틸 셀룰로스 (HMMHEC), 소수성 개질 카르복시메틸 메틸 셀룰로스 (HMCMMC), 양이온성 히드록시에틸 셀룰로스 (양이온성 HEC), 양이온성 소수성 개질 히드록시에틸 셀룰로스 (양이온성 HMHEC), 및 그의 임의의 조합으로 이루어진 군으로부터 선택된 글리옥살 또는 비-글리옥살 처리 셀룰로스 에테르인 레올로지 개질제 조성물.
- 제1항에 있어서, 셀룰로스 에테르가 히드록시에틸 셀룰로스 (HEC) 또는 카르복시메틸 셀룰로스 단독 또는 그의 조합인 레올로지 개질제 조성물.
- 제1항에 있어서, 셀룰로스 에테르가 비-글리옥살 처리 히드록시에틸 셀룰로스 에테르인 레올로지 개질제 조성물.
- 제1항에 있어서, 셀룰로스 에테르가 글리옥살-처리 히드록시에틸 셀룰로스 에테르인 레올로지 개질제 조성물.
- 제1항에 있어서, 아크릴아미드 중합체가 0.05 wt% 내지 50.0 wt%, 또는 0.05 wt% 내지 30.0 wt%의 양으로 존재하고, 셀룰로스 에테르가 50.0 wt% 내지 99.95 wt%, 또는 70.0 wt% 내지 99.95 wt%의 양으로 존재하는 것인 레올로지 개질제 조성물.
- 제1항에 있어서, 소수성 개질 에톡실화 우레탄 중합체, 소수성 개질 폴리아세탈-폴리에테르 중합체, 소수성 개질 알칼리 팽윤성 유화액, 소수성 개질 아미노플라스트, 알칼리 팽윤성 유화액 및 그의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 회합성 중합체를 추가로 포함하는 레올로지 개질제 조성물.
- 제13항에 있어서, 회합성 중합체가 소수성 개질 폴리아세탈-폴리에테르 중합체인 레올로지 개질제 조성물.
- 제1항에 있어서, 계면활성제; 분산제; 증점제; 케이킹방지제; 소포제; 보존제; 왁스, 실리콘 및 탄화수소를 포함하는 소수성 작용제; 상용화제; 접착 촉진제; 가교제; 및 그의 임의의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 첨가제를 추가로 포함하는 레올로지 개질제 조성물.
- 제1항에 있어서, 건조 분말 블렌드인 레올로지 개질제 조성물.
- (i) 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 (ii) 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르를 블렌딩하는 것을 포함하는, 제1항의 조성물을 제조하는 방법.
- 제17항에 있어서, 아크릴아미드 중합체가 0.05 wt% 내지 50.0 wt%, 또는 0.05 wt% 내지 30.0 wt%의 양으로 존재하고, 셀룰로스 에테르가 50.0 wt% 내지 99.95 wt%, 또는 70.0 wt% 내지 99.95 wt%의 양으로 존재하는 것인 방법.
- 제17항에 있어서, 계면활성제; 분산제; 증점제; 케이킹방지제; 소포제; 보존제; 왁스, 실리콘 및 탄화수소를 포함하는 소수성 작용제; 상용화제; 접착 촉진제; 가교제; 및 그의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 첨가제를 블렌딩하는 단계를 추가로 포함하는 방법.
- 수성-기반 코팅에 있어서의 레올로지 개질제 조성물의 용도로서, 여기서 상기 조성물은 (i) 0.05 wt% 내지 70.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 (ii) 30.0 wt% 내지 99.95 wt%의 적어도 하나의 셀룰로스 에테르의 블렌드를 포함하는 것인, 레올로지 개질제 조성물의 용도.
- 제20항에 있어서, 아크릴아미드 중합체가 0.05 wt% 내지 50.0 wt%, 또는 0.05 wt% 내지 30.0 wt%의 양으로 존재하고, 셀룰로스 에테르가 50.0 wt% 내지 99.95 wt%, 또는 70.0 wt% 내지 99.95 wt%의 양으로 존재하는 것인, 레올로지 개질제 조성물의 용도.
- 수성 코팅 조성물로서, 코팅 조성물의 총 중량을 기준으로,
(ia) 0.01 wt% 내지 10.0 wt%의 제1항의 조성물 또는 (ib) 0.01 wt% 내지 10.0 wt%의, 600만 달톤 초과의 중량 평균 분자량을 갖는 아크릴아미드 중합체; 및 0.01 wt% 내지 10.0 wt%의 적어도 하나의 셀룰로스 에테르;
(ii) 5.0 wt% 내지 85.0 wt%의 적어도 하나의 필름 형성 중합체; 및
(iii) 5.0 wt% 내지 15.0 wt%의 물
을 포함하는 수성 코팅 조성물. - 제22항에 있어서, 아크릴아미드 중합체 및 셀룰로스 에테르가 둘 다 코팅 조성물 중에 블렌드로서 존재하는 것인 수성 코팅 조성물.
- 제22항에 있어서, 필름 형성 중합체가 아크릴, 비닐 아크릴, 및 스티렌-아크릴 스티렌-부타디엔 공중합체, 비닐 아세테이트 에틸렌, 부타디엔-아크릴로니트릴 공중합체, 에폭시드, 우레탄, 폴리아미드, 베르사트산의 비닐 에스테르 (VeoVa), 및 폴리에스테르로 이루어진 군으로부터 선택된 것인 수성 코팅 조성물.
- 제22항에 있어서, 프탈로시아닌, 산화철, 이산화티타늄, 산화아연, 인디고, 수화된 산화알루미늄, 황산바륨, 규산칼슘, 점토, 실리카, 활석, 탄산칼슘, 및 그의 혼합물로 이루어진 군으로부터 선택된 적어도 하나의 안료를 추가로 포함하는 수성 코팅 조성물.
- 제25항에 있어서, 15% 내지 85% 범위의 안료 부피 농도 (PVC)를 갖는 수성 코팅 조성물.
- 제22항에 있어서, 계면활성제; 분산제; 증점제; 케이킹방지제; 소포제; 가소제; 증량제; 보존제; 왁스, 실리콘 및 탄화수소를 포함하는 소수성 작용제; 상용화제; 접착 촉진제; 가교제; 살생물제; 곰팡이방지제; 탈포제; 공-용매; 응집제; 및 그의 임의의 조합으로 이루어진 군으로부터 선택된 적어도 하나의 첨가제를 추가로 포함하는 수성 코팅 조성물.
- 제22항에 있어서, 건축용 코팅 조성물인 수성 코팅 조성물.