KR20230144849A - Device And Method Of Producing Cardboard With The Glue Of Enhanced Air Permeability, And Cardboard Produced Thereof - Google Patents
Device And Method Of Producing Cardboard With The Glue Of Enhanced Air Permeability, And Cardboard Produced Thereof Download PDFInfo
- Publication number
- KR20230144849A KR20230144849A KR1020220044046A KR20220044046A KR20230144849A KR 20230144849 A KR20230144849 A KR 20230144849A KR 1020220044046 A KR1020220044046 A KR 1020220044046A KR 20220044046 A KR20220044046 A KR 20220044046A KR 20230144849 A KR20230144849 A KR 20230144849A
- Authority
- KR
- South Korea
- Prior art keywords
- starch adhesive
- adhesive
- starch
- corrugated cardboard
- cardboard
- Prior art date
Abstract
본 발명은 골판지 제조 장치로서,
전분 접착제 저장조에서 전분 접착와 제추출물 에멀션을 교반하여 접착제 조성물을 형성하도록 하는 교반 보조 수단을 포함하며,
상기 교반 보조 수단이 복수개의 초음파 캐비테이션 수단으로 이루어지며, 상기 전분 접착제 저장조에서 업스트리임으로 전분 접착제 어플리케이터 롤에 전분 접착제가 도포되도록 한다.The present invention is a corrugated cardboard manufacturing device,
It includes a stirring auxiliary means for stirring the starch adhesive and the extract emulsion in the starch adhesive reservoir to form an adhesive composition,
The stirring auxiliary means consists of a plurality of ultrasonic cavitation means, and allows the starch adhesive to be applied to the starch adhesive applicator roll upstream from the starch adhesive reservoir.
Description
본 발명은 골판지 제조 장치에 관한 것으로서, 특히, 골판지를 이루는 골심지와 이면지의 접착부분에 적용되는 전분 접착제에 소정의 특징을 제공하는 골판지 제조 장치 및 제조 방법에 관한 것이다. The present invention relates to a corrugated cardboard manufacturing apparatus, and in particular, to a corrugated cardboard manufacturing apparatus and manufacturing method that provides predetermined characteristics to a starch adhesive applied to the adhesive portion of the corrugated medium and the backing paper forming the corrugated cardboard.
배달 산업이 전세계적으로 호황을 누리면서, 제품 보관 및 운반을 위한 포장재 산업도 급속하게 발전되고 있다. 포장재의 수요가 증가하면서, 다양한 기능 및 효과를 갖는 포장재에 대한 연구도 병행되고 있다. As the delivery industry is booming worldwide, the packaging materials industry for product storage and transportation is also rapidly developing. As the demand for packaging materials increases, research on packaging materials with various functions and effects is also being conducted.
상기 포장재 중에서도 제품에 대한 외부 충격을 방지하기 위한 골판지의 수요는 증가하는데 비해서, 그 성능 및 효과에 대한 기술적 진전은 더디게 진행되고 있다. Among the above packaging materials, while the demand for corrugated cardboard to prevent external shock to products is increasing, technological progress regarding its performance and effectiveness is progressing slowly.
골판지를 활용한 상자등에 식자재를 보관 운송하는 경우, 완충작용 이외에도, 소정의 특성, 예컨대 선도 유지 특성이 제공된 골판지의 필요성도 대두되고 있다. When storing and transporting food ingredients in boxes using corrugated cardboard, the need for corrugated cardboard that provides certain properties, such as freshness retention properties, in addition to the cushioning effect, is also emerging.
도 1 및 도2 에 예시된 바와 같은 골판지(100)는 편면 골판지로서, 골심지(1) 및 이면지(2)로 구성되며, 이러한 골심지(1) 및 이면지(2)는 크레프트지 등으로 이루어진다. 상기 골심지(1)와 이면지(2)는 전분풀 또는 전분 접착제(이후에는, "전분 접착제"로 언급)에 의해 B와 같이 접착되는 형태로 이루어진다.Corrugated cardboard 100 as illustrated in FIGS. 1 and 2 is a single-sided corrugated cardboard and is composed of a corrugated medium (1) and a backing paper (2), and the corrugated medium (1) and the backing paper (2) are made of kraft paper, etc. The corrugated paper (1) and the backing paper (2) are glued together as shown in B using starch paste or starch adhesive (hereinafter referred to as “starch adhesive”).
포장물에 상술한 바와 같은 선도 유지 특성을 갖도록 가공처리를 한 크레프트지를 사용하여 골판지를 제조하기도 한다. 이때, 선도 유지의 효과면에서 배제되는 부분이 골판지를 이루는 골심지(1)와 이면지(2)를 접착하는 전분 접착제가 제공되는 부분이다. Corrugated cardboard is also manufactured using kraft paper that has been processed to have the freshness retention characteristics described above for packaging. At this time, the part that is excluded from the effect of maintaining freshness is the part where the starch adhesive that bonds the corrugated medium (1) and the backing paper (2) forming the corrugated cardboard is provided.
이와 같이, 전분 접착제가 적용되는 부분에 대해서, 목적한 특정 효과, 예컨대 선도 유지 특성을 제공할 수 있는 조성물 제공 공정 및 장치를 제공할 필요성이 대두된다. As such, there is a need to provide a process and device for providing a composition that can provide specific desired effects, such as freshness retention properties, for areas where starch adhesives are applied.
골심지(1)와 이면지(2)에 적용되는 전분 접착제가 적용되는 공정, 및 장치를 개선시켜서, 특수한 효과를 갖는 골판지를 제조할 수 있는 제조 공정이 간단하고, 제조 장치를 제공하는 것을 목적으로 한다. The purpose is to provide a simple manufacturing process and manufacturing device that can produce corrugated cardboard with special effects by improving the process and device in which the starch adhesive applied to the corrugated medium (1) and the backing paper (2) is applied. .
본 발명의 목적은The purpose of the present invention is
골판지 제조 장치로서,As a corrugated cardboard manufacturing device,
교반되어 제공된 전분 접착제에 추출물 에멀션을 부가하여 교반하여 접착제 조성물을 형성하도록 하는 교반 보조 수단을 포함한다.and a stirring auxiliary means for adding the extract emulsion to the stirred provided starch adhesive and stirring it to form an adhesive composition.
바람직하게는, 상기 교반 보조 수단이 복수개의 초음파 캐비테이션 수단이며, 상기 전분 접착제 저장조에서 업스트리임으로 상기 접착제 조성물을 전분 접착제 어플리케이터 롤에 전분 접착제가 도포되도록 한다.Preferably, the stirring auxiliary means is a plurality of ultrasonic cavitation means, and the starch adhesive is applied upstream from the starch adhesive storage tank to the starch adhesive applicator roll.
본 발명의 또 다른 목적은 골판지 제조 방법으로서,Another object of the present invention is a method for manufacturing corrugated cardboard,
전분 접착제에 추출물 에멀션을 부가하여 초음파 캐비테이션 교반하는 에멀션 교반 단계와, 그리고,An emulsion stirring step in which the extract emulsion is added to the starch adhesive and agitated by ultrasonic cavitation, and
상기 전분 접착제 저장조에 담긴 전분 접착제와 상기 추출물 에멀션을 교반한 접착제 조성물을 전분 접착제 어플리케이터 롤에 묻히는 단계를 포함한다.and applying an adhesive composition obtained by stirring the starch adhesive contained in the starch adhesive storage tank and the extract emulsion onto a starch adhesive applicator roll.
바람직하게는, 상기 전분 접착제 저장조에서 업스트리임으로 전분 접착제 어플리케이터 롤에 상기 접착 조성물이 도포되도록 한다.Preferably, the adhesive composition is applied to a starch adhesive applicator roll upstream from the starch adhesive reservoir.
본 발명의 신선도 유지를 개선시킨 골판지를 제조하는 골판지 제조 장치 및 방법을 제공함에 의해, 간단한 전분 접착제 도포 모듈로 구현이 가능하고, 유지 보수가 용이하며, 경제적으로 적용할 수 있도록 한다.By providing a corrugated cardboard manufacturing apparatus and method for manufacturing corrugated cardboard with improved freshness retention of the present invention, it can be implemented with a simple starch adhesive application module, is easy to maintain, and can be applied economically.
제 1도는 종래 기술의 편면 골판지를 예시한 개략도이다.
제 2도는 제1도의 편면 골판지의 단면을 예시한 설명도이다.
제 3도는 종래의 골판지 제조 공정의 일부를 예시한 설명도이다.
제 4도는 제 3도의 C를 확대하여 예시한 도면이다.
제 5도는 본 발명의 일 실시예의 초음파 케비테이션의 배치를 설명한 측단면도이다. 그리고,
도 6은 도 5의 초음파 케비테이션의 배치를 평면에서 예시한 평면도이다. Figure 1 is a schematic diagram illustrating a single-sided corrugated cardboard of the prior art.
Figure 2 is an explanatory diagram illustrating a cross section of the single-sided corrugated cardboard of Figure 1.
Figure 3 is an explanatory diagram illustrating part of a conventional corrugated cardboard manufacturing process.
Figure 4 is an enlarged illustration of C of Figure 3.
Figure 5 is a side cross-sectional view explaining the arrangement of ultrasonic cavitation in one embodiment of the present invention. and,
Figure 6 is a plan view illustrating the arrangement of the ultrasonic cavitation of Figure 5 on a plane.
골판지 제조 장치에서, 도 3에 예시된 바와 같이, 골심지 제조기(미도시)에서 제조된 골심지(1)는 센터 플루트 롤(30)과 탑 플루트 롤(60) 사이로 인입(in)되고, 상기 센터 플루트 롤(30)과 플레셔 롤(70) 사이로 인출(out)되어 나가서, 이면지(2)와 접착 공정(미도시)을 거쳐서 골판지로 형성된다. In the corrugated cardboard manufacturing apparatus, as illustrated in Figure 3, the corrugated medium (1) manufactured in the corrugated medium manufacturing machine (not shown) is introduced between the center flute roll 30 and the top flute roll 60, and the center flute It is pulled out between the roll 30 and the flesher roll 70, and is formed into corrugated cardboard through an adhesion process (not shown) with the backing paper 2.
도 4에 예시된 바와 같이, 골심지(1)가 센터 플루트 롤(30)과 전분 접착제 어플리케이터 롤(10) 사이에서 C부분을 거쳐 가면서, 전분 접착제가 전분 접착제 어플리케이터 롤(10)에 묻었다가, 센터 플루트 롤(30)에 얹혀진 골심지(1)에 도포된다. As illustrated in Figure 4, as the corrugated medium (1) passes through part C between the center flute roll (30) and the starch adhesive applicator roll (10), the starch adhesive is applied to the starch adhesive applicator roll (10), and then the center It is applied to the corrugated medium (1) placed on the flute roll (30).
설명을 명료하기 위해서, 기타 골판지 제조 설비 및 공정을 생략하며, 이는 당해 기술분야에 널리 공지되어 있다. For clarity of explanation, other corrugated cardboard manufacturing equipment and processes are omitted, which are well known in the art.
전분 접착제는 별도로 제공되는 전분 접착제 제조 설비(미도시)에서 교반 생성되어 투입라인(S)을 거쳐서, 전분 접착제 저장조(20)에 제공된 전분 접착제 상에서 전분 접착제 어플리케이터 롤(10)이 회전되면서, 전분 접착제가 상기 전분 접착제 어플리케이터 롤(10)에 묻어난다. 이어서, 상기 전분 접착제 어플리케이터 롤(10)과 같은 방향으로 회전되는 닥터 롤(40)에 의해서, 전분 접착제가 상기 전분 접착제 어플리케이터 롤(10)에 고르게 묻어 도포된다. The starch adhesive is produced by stirring in a separately provided starch adhesive manufacturing facility (not shown) and passes through the input line (S). As the starch adhesive applicator roll 10 rotates on the starch adhesive provided in the starch adhesive storage tank 20, the starch adhesive is applied. is applied to the starch adhesive applicator roll (10). Next, the starch adhesive is evenly applied to the starch adhesive applicator roll 10 by the doctor roll 40 rotating in the same direction as the starch adhesive applicator roll 10.
이와 동시에, 상기 골심지(1)가 탑 플루트 롤(60)과 상기 센터 플루트 롤(30)에 얹혀져서 이동되며, 도 4에 예시된 바와 같이, 상기 전분 접착제 어플리케이터 롤(10)에 도포된 전분 접착제(P')가 골심지(1)로 옮겨져서 도포된다.At the same time, the corrugated medium (1) is moved by being placed on the top flute roll (60) and the center flute roll (30), and as illustrated in Figure 4, the starch adhesive applied to the starch adhesive applicator roll (10) (P') is transferred to the corrugated medium (1) and applied.
도 3에 예시된 바와 같은 종래의 제조 장치에서는, 상술한 바와 같은 공정을 거치면서 골심지(1)의 일측면 전체에 걸쳐서 전분 접착제가 도포되게 된다.In the conventional manufacturing apparatus as illustrated in Figure 3, starch adhesive is applied over the entire one side of the corrugated medium (1) while going through the process described above.
도 3에 도시된 바와 같은 구조의 전분 접착제 저장조(20)를 구비한 전분 접착제 시스템으로는 골판지의 접착 조성물이 제공되는 부분에서의 선도 유지 특성을 개선시키지 못한다The starch adhesive system provided with the starch adhesive reservoir 20 structured as shown in FIG. 3 does not improve the freshness retention characteristics in the area where the adhesive composition of corrugated cardboard is provided.
본 발명의 발명자는 골판지를 이루는 크라프트 원지에 소정의 특성, 예컨대, 선도 유지 특성을 제공하여 선도 유지 특성을 구현하였다. 이와 더불어, 전분 접착제에 선도 유지 특성을 제공하는 조성물을 적용한 골판지를 제공함에 의해 골판지 박스내의 선도 유지 특성을 보다 더 개선시키는 것에 주목하였다. 상기 소정의 특성은 제한이 없으며, 당해업계에서 공지된 물에 잘 녹지 않는 에멀션 형태의 조성물 혼합에 모두 적용이 가능하다.The inventor of the present invention implemented freshness retention properties by providing predetermined properties, such as freshness retention properties, to the kraft base material that makes up the corrugated cardboard. In addition, attention was paid to further improving the freshness-retaining properties in a corrugated cardboard box by providing corrugated cardboard with a composition that provides freshness-retaining properties to a starch adhesive. The above predetermined characteristics are not limited and can be applied to all mixtures of water-insoluble emulsion-type compositions known in the art.
본 발명의 발명자는 상기 선도 유지 특성은 골판지에 나무 추출물을 적용할 때, 바람직하게 구현된다는 점에 주목한다. The inventor of the present invention notes that the above-mentioned freshness retention property is preferably implemented when applying tree extract to corrugated cardboard.
나무 추출물의 성분은 물에 녹지 않아서, 에멀션 용액 상태로 존재한다. 이러한 물질적 특성으로 인해서, 전분 접착제내에서 교반하여 적용하는 것은 용이하지 않다. The components of tree extract are insoluble in water, so they exist in an emulsion solution. Due to these material properties, it is not easy to apply by stirring in the starch adhesive.
추출물 에멀션 형태의 나무 추출물을 전분 접착제 수용액에서 제공함에 있어서, 초음파 케비테이션을 적용시킬때 전분 접착제에서 신선 유지 특성이 우수하게 구현됨이 확인된다. In providing the tree extract in the form of an extract emulsion in an aqueous starch adhesive solution, it was confirmed that the starch adhesive had excellent fresh-retention properties when ultrasonic cavitation was applied.
본 발명에서는 전분 접착제 공급라인(S)에서 전분 접착제 저장조(20)으로 공급되어 추출물 에멀션이 섞이지 않은 것을 전분 접착제로 언급하고, 상기 전분 접착제와 추출물 에멀션 공급라인(S')에서 공급된 추출물 에멀션의 혼합물은 이하, 접착제 조성물로 구분하여 명기한다. In the present invention, what is supplied from the starch adhesive supply line (S) to the starch adhesive storage tank (20) and is not mixed with the extract emulsion is referred to as starch adhesive, and the starch adhesive and the extract emulsion supplied from the extract emulsion supply line (S') are referred to as starch adhesives. The mixture is hereinafter classified and specified as adhesive composition.
본 발명의 일 실시예는 도 5에 도시된 바와 같이, 전분 접착제 저장조(20)에 초음파 케비테이션 수단(50)이 복수 개로 배치된다. 상기 초음파 케비테이션 수단(50)은 그 제한이 없으며, 시판되는 모든 것이 적용될 수 있다. 초음파 케비테이션 수단(50)은 초음파가 유체에서 전파될 때 초음파의 큰 압력 변화에 의해 상당히 큰 압력을 동반하게 되며, 이러한 압력에 의해 물질 분산, 등을 수행하게 된다.In one embodiment of the present invention, as shown in FIG. 5, a plurality of ultrasonic cavitation means 50 are disposed in the starch adhesive storage tank 20. There is no limitation to the ultrasonic cavitation means 50, and any commercially available device may be applied. The ultrasonic cavitation means 50 is accompanied by a considerably large pressure due to a large pressure change of the ultrasonic wave when the ultrasonic wave propagates in the fluid, and this pressure performs material dispersion, etc.
본 발명은 상술한 바와 같이, 상기 전분 접착제 공급라인(S) 이외에, 추출물 에멀션 공급라인(S')을 포함하여, 전분 접착제 저장조(20)에 전분 접착제, 및 추출물 에멀션을 공급한다. 본 발명의 일 실시예에서는 추출물 에멀션으로 나무 추출물 에멀션을 제공한다. As described above, the present invention includes an extract emulsion supply line (S') in addition to the starch adhesive supply line (S) to supply starch adhesive and extract emulsion to the starch adhesive storage tank (20). In one embodiment of the present invention, a tree extract emulsion is provided as the extract emulsion.
이러한 나무 추출물은 그 제한이 없으며, 상기 선도 유지제로서, 적용된다. 상기 나무 추출액으로는 목초액, 수액, 달여서 수득한 추출액(이하 "나무 침출액"으로 칭함)을 포함하며, 이외의 방법으로, 다른 추출 용제등으로 추출한 소재도 본 발명에 포함된다.This tree extract has no limitations and is applied as the freshness maintaining agent. The tree extract includes wood vinegar, sap, and extract obtained by boiling (hereinafter referred to as "tree leachate"), and materials extracted by other methods, such as other extraction solvents, are also included in the present invention.
본 발명에 해당되는 나무는 그 사용에 제한이 없으며, 침엽수, 활엽수 모두 해당되며, 편백나무, 참나무, 소나무, 은행나무, 버드나무, 상수리나무, 떡갈나무 등 제한이 없이 적용이 가능하다. There are no restrictions on the use of trees applicable to the present invention, and both coniferous and broad-leaved trees are applicable, and it can be applied without limitation to cypress trees, oak trees, pine trees, ginkgo trees, willow trees, oak trees, etc.
추출형태에도 제한이 없다. 예를 들어, 목초액은 다음과 같이 생성된다. 나무를 가열하면 탄화라는 현상이 일어나 숯이 된다. 그 과정에서 연기가 발생되는대 황갈색 연기를 공기중에서 냉각하여 액상이 된 것을 회수한 것이다. 목초액의 성분은 숯으로 사용하는 원목의 종류와 수득하는 방법, 수득한 후의 보관 방법과 조건 등에 따라서 품질이 변화한다. There is no limit to the extraction type. For example, wood vinegar is produced as follows: When wood is heated, a phenomenon called carbonization occurs and it becomes charcoal. During the process, smoke was generated, and the yellow-brown smoke was cooled in the air and converted to liquid. The quality of the components of wood vinegar varies depending on the type of log used as charcoal, the method of obtaining it, and the storage method and conditions after obtaining it.
목초액을 제조함에 있어서, 초기에 나오는 연기는 수분이 많고 비중이 가벼워 목초액으로서는 사용하지 못한다. 일반적인 목초액은 연소 후, 소정의 시간을 거친 후, 나무를 70℃ 내지 140~150 ℃의 온도에서 태워서 이 연기에서 채취된 용액이다. 이렇게 수득된 원료 목초액을 소정의 기간 방치하여 걸러서 사용하기도 한다. In manufacturing wood vinegar, the smoke that comes out initially has a lot of moisture and has a light specific gravity, so it cannot be used as wood vinegar. General wood vinegar is a solution collected from the smoke by burning wood at a temperature of 70°C to 140-150°C after combustion and a predetermined period of time. The raw wood vinegar obtained in this way may be left for a certain period of time and then filtered before use.
본 발명의 일 실시예에서는 도 5 및 6에 예시된 바와 같이, 초음파 케비테이션 고정구(51)가 상기 전분 접착제 저장조(20)의 일측에 배치된다. 상기 초음파 케비테이션 수단(50)의 배치 형태 및 구조에는 제한이 없다. 상기 접착제 조성물은 앞서 언급한 바와 같이, 상기 전분 접착제 어플리케이터 롤(10)에 묻혀져서 골심지(1)에 옮겨져서, 골심지(1)와 이면지(2)가 접착되는 공정으로 이어진다. In one embodiment of the present invention, as illustrated in FIGS. 5 and 6, the ultrasonic cavitation fixture 51 is disposed on one side of the starch adhesive reservoir 20. There are no restrictions on the arrangement form and structure of the ultrasonic cavitation means 50. As mentioned above, the adhesive composition is buried in the starch adhesive applicator roll 10 and transferred to the corrugated medium (1), leading to a process in which the corrugated medium (1) and the backing paper (2) are adhered.
상기 전분 접착제 어플리케이터 롤(10)의 원주면이 상기 전분 접착제 저장조(20)내에 저장된 접촉제 조성물의 표면에서 접촉하여, 상기 전분 접착제 어플리케이터 롤(10)의 표면의 접착제 두께(P')가 얇게 묻혀지는 것이 바람직하다. The circumferential surface of the starch adhesive applicator roll 10 is in contact with the surface of the contact agent composition stored in the starch adhesive storage tank 20, so that the adhesive thickness P' of the surface of the starch adhesive applicator roll 10 is thinly buried. It is desirable to lose.
이러한 관점에서, 상기 전분 접착제 저장조(20)에 담긴 접착제 조성물에서 미세교반이 이루어져서 전분 접착제 어플리케이터 롤(10)로 묻혀지도록 하는 것이 바람직하다. 바람직하게는, 상기 초음파 케비테이션 수단(50)이 전분 접착제 저장조(20)의 접착제 조성물의 상류, 즉 상기 전분 접착제 어플리케이터 롤(10)에 인접한 부분에서 작용되도록 하여야 한다. 이를 위해서, 초음파 케비테이션 고정구(51)가 배치되어, 상기 초음파 케비테이션 수단(50)이 접착제 조성물의 상류측에서 미세 교반이 형성되도록 한다. From this point of view, it is preferable that the adhesive composition contained in the starch adhesive reservoir 20 be finely agitated so that it is applied to the starch adhesive applicator roll 10. Preferably, the ultrasonic cavitation means 50 should be operated upstream of the adhesive composition of the starch adhesive reservoir 20, that is, adjacent to the starch adhesive applicator roll 10. For this purpose, an ultrasonic cavitation fixture 51 is disposed so that the ultrasonic cavitation means 50 creates fine agitation on the upstream side of the adhesive composition.
상기 초음파 케비테이션 고정구(51)를 사용하지 않고서, 초음파 케비테이션 수단(50)이 전분 접착제 저장조(20)의 하단에 배치되는 경우, 초음파 케비테이션 수단(50)의 출력을 높여서 해결할 수 있다. 따라서, 상기 초음파 케비테이션 고정구(51)는 선택적인 구조이며, 필수적인 구조는 아니다. When the ultrasonic cavitation means 50 is disposed at the bottom of the starch adhesive reservoir 20 without using the ultrasonic cavitation fixture 51, the problem can be solved by increasing the output of the ultrasonic cavitation means 50. Therefore, the ultrasonic cavitation fixture 51 is an optional structure and is not an essential structure.
상기 도 5 및 도 6에 예시된 바와 같이, 전분 접착제 어플리케이터 롤(10)이 회전하면서, 전분 접착제 저장조(20)의 접착제 조성물이 업스트리임(upstream)으로, 전분 접착제 어플리케이터 롤(10)에 옮겨지도록 하는 위치에, 초음파 케비테이션 수단(50)이 전분 접착제 저장조(20)에 배치되는 것이 바람직하다. As illustrated in FIGS. 5 and 6, as the starch adhesive applicator roll 10 rotates, the adhesive composition in the starch adhesive reservoir 20 is transferred upstream to the starch adhesive applicator roll 10. It is preferable that the ultrasonic cavitation means 50 is disposed in the starch adhesive storage tank 20 in a position so as to hold.
상기 전분 접착제는, 당해 업계에서 통상적으로 적용되는 모든 전분 접착 조성물 및 조성비를 적용한다. 통상적인 전분 접착제는 전분, PVA, 붕사, 수산화나트륨 등의 조성물로 이루어지며, 본 발명에서는 그 제한이 없다. The starch adhesive uses all starch adhesive compositions and composition ratios commonly applied in the industry. A typical starch adhesive consists of a composition such as starch, PVA, borax, and sodium hydroxide, but there is no limitation in the present invention.
상기 전분 접착제는 교반조에서 종래의 조성비로 교반되어진다.The starch adhesive is stirred at a conventional composition ratio in a stirring tank.
본 발명에서 초음파는 20KHz 내지 400KHz까지 가능하며, 20KHz 이하에서는 미세 교반이 일어나지 않으며, 400KHz이상에서는 전분 접착제 용액이 기화되는 현상이 발생되어 미세 교반이 이루어지지 않는다. In the present invention, ultrasonic waves are possible from 20 KHz to 400 KHz, and below 20 KHz, fine agitation does not occur. Above 400 KHz, the starch adhesive solution vaporizes and no fine agitation occurs.
본 발명의 일 실시예에서, 전분 접착제에 대해 25KHz 내지 300KHz의 초음파를 적용하면 미세 교반이 효과적으로 이루어졌다. In one embodiment of the present invention, applying ultrasonic waves of 25 KHz to 300 KHz to the starch adhesive effectively achieved fine agitation.
초음파를 적용할 때, 전분 접착제 및 접착제 조성물의 온도는 중요한 작업 인자이며, 50℃ 내지 90℃에서 감량 공정 수행이 가능하다. 바람직하게는 60℃ 내지 80℃이다. 온도가 상기 범위 보다 낮거나 온도가 높으면, 미세교반이 잘 이루어지지 않는다. When applying ultrasound, the temperature of starch adhesives and adhesive compositions is an important operating factor, and the reduction process can be performed at 50°C to 90°C. Preferably it is 60°C to 80°C. If the temperature is lower or higher than the above range, fine agitation does not occur well.
이와 같이 전분 접착제가 묻혀진 전분 접착제 어플리케이터 롤(10)의 접착제 조성물이 골심지(1)에 묻어서, 상기 센터 플루트 롤(30)과 플레셔 롤(70)에 의해 골심지(1)가 이송되어 합지기(미도시)에서 이면지(2)와 합지되어 접착되어 골판지를 형성하게 된다.In this way, the adhesive composition of the starch adhesive applicator roll (10) in which the starch adhesive is buried is buried in the corrugated medium (1), and the corrugated medium (1) is transferred by the center flute roll (30) and the flesher roll (70) to the joint (Mido). In this case, it is combined with the backing paper (2) and glued to form corrugated cardboard.
실시예 1Example 1
증류수 10L에 수산화나트륨 100g, 나무 추출물 에멀션 100g, 글리세린 100g를 포함하는 접착제 조성물을 형성하였다.An adhesive composition containing 100 g of sodium hydroxide, 100 g of wood extract emulsion, and 100 g of glycerin was formed in 10 L of distilled water.
이러한 전분 접착제로 골판지를 제조하였다. Corrugated cardboard was manufactured with this starch adhesive.
1 m2당 60g의 30cm x 30cm 시편 3개를 취하여, 필터 효율을 시험한 바, 특성이 1.5배 이상 증가된다.The filter efficiency was tested by taking three 30cm
상술한 바와 같은 간단한 설비 및 공정에 의해, 선도 유지가 우수한 골판지를 제조하게 된다. By using simple equipment and processes as described above, corrugated cardboard with excellent freshness retention can be manufactured.
1 : 골심지
2 : 이면지
10 : 전분 접착제 어플리케이터 롤
20 ; 전분 접착제 저장조
30 : 센터 플루트 롤
40 : 닥터 롤
50 : 초음파 캐비테이션 수단
51 : 초음파 캐비테이션 고정구
60 : 톱 플루트 롤
70 : 플레셔 롤
100 : 골판지
S : 전분 접착제 공급라인
S' : 추출물 에멀션 공급라인
H : 전분 접착제 배출부1: Corrugated wick
2: Back paper
10: Starch adhesive applicator roll
20 ; starch adhesive reservoir
30: Center flute roll
40: Doctor Roll
50: ultrasonic cavitation means
51: Ultrasonic cavitation fixture
60: Top flute roll
70: Flesher roll
100: Corrugated cardboard
S: Starch adhesive supply line
S': Extract emulsion supply line
H: Starch adhesive discharge part
Claims (4)
전분 접착제 저장조에서 전분 접착제와 추출물 에멀션을 교반하여 접착제 조성물을 형성하도록 하는 교반 보조 수단을 포함하는 것을 특징으로 하는 선도 유지 성능을 갖는 접착제가 제공된 골판지 제조 장치.As a corrugated cardboard manufacturing device,
A corrugated cardboard manufacturing device provided with an adhesive having freshness retention performance, comprising a stirring auxiliary means for stirring the starch adhesive and the extract emulsion in the starch adhesive reservoir to form an adhesive composition.
상기 교반 보조 수단이 복수개의 초음파 캐비테이션 수단이며, 상기 전분 접착제 저장조에서 업스트리임으로 상기 접착제 조성물을 전분 접착제 어플리케이터 롤에 전분 접착제가 도포되도록 하는 것을 특징으로 하는 선도 유지 성능을 갖는 접착제가 제공된 골판지 제조 장치.According to claim 1,
The stirring auxiliary means is a plurality of ultrasonic cavitation means, and the adhesive composition is applied upstream from the starch adhesive storage tank to a starch adhesive applicator roll. A corrugated cardboard manufacturing device provided with an adhesive having freshness retention performance, characterized in that .
전분 접착제 저장조에서 전분 접착제와 추출물 에멀션을 교반하는 초음파 캐비테이션 교반 단계와, 그리고,
상기 전분 접착제 저장조에 담긴 전분 접착제와 상기 추출물 에멀션을 교반한 접착제 조성물을 전분 접착제 어플리케이터 롤에 묻히는 단계를 포함하는 것을 특징으로 하는 선도 유지 성능을 갖는 접착제가 제공된 골판지 제조 방법.As a method of manufacturing corrugated cardboard,
an ultrasonic cavitation stirring step of agitating the starch adhesive and extract emulsion in the starch adhesive reservoir, and
A method of manufacturing corrugated cardboard provided with an adhesive having freshness retention performance, comprising the step of applying an adhesive composition obtained by stirring the starch adhesive and the extract emulsion contained in the starch adhesive storage tank to a starch adhesive applicator roll.
상기 전분 접착제 저장조에서 업스트리임으로 전분 접착제 어플리케이터 롤에 상기 접착 조성물이 도포되도록 하는 것을 특징으로 하는 선도 유지 성능을 갖는 접착제가 제공된 골판지 제조 방법.
According to claim 3,
A method of manufacturing corrugated cardboard provided with an adhesive having freshness retention performance, characterized in that the adhesive composition is applied to a starch adhesive applicator roll upstream from the starch adhesive reservoir.