KR20230076436A - Eco-friendly carrier composition for dyeing polyester textile - Google Patents
Eco-friendly carrier composition for dyeing polyester textile Download PDFInfo
- Publication number
- KR20230076436A KR20230076436A KR1020210163361A KR20210163361A KR20230076436A KR 20230076436 A KR20230076436 A KR 20230076436A KR 1020210163361 A KR1020210163361 A KR 1020210163361A KR 20210163361 A KR20210163361 A KR 20210163361A KR 20230076436 A KR20230076436 A KR 20230076436A
- Authority
- KR
- South Korea
- Prior art keywords
- dyeing
- carrier composition
- polyester
- environmentally friendly
- carrier
- Prior art date
Abstract
본 발명은 벤질 벤조에이트 (Benzyl Benzoate) 및 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상을 포함하는, 환경 친화형 폴리에스터 염색용 캐리어 조성물에 관한 것이다. 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은 독성이 없는 환경 친화형 성분을 포함함으로써, 무독성 저온 폴리에스터 염색용 캐리어 조성물을 제공할 수 있다.The present invention relates to an environmentally friendly polyester dyeing carrier composition comprising at least one of benzyl benzoate and dibenzyl ether. The carrier composition for dyeing an environmentally friendly polyester according to an embodiment of the present invention includes a non-toxic environmentally friendly component, thereby providing a non-toxic, low-temperature carrier composition for dyeing polyester.
Description
본 발명은 환경 친화형 폴리에스터 염색용 캐리어 조성물에 관한 것이다.The present invention relates to a carrier composition for dyeing environmentally friendly polyester.
폴리에틸렌테레프탈레이트로 대표되는 폴리에스터 섬유는 우수한 물리, 화학적 성질 및 내열성으로 의류용으로 널리 이용되고 있으나 화학 구조 중에 염료와 반응할 수 있는 반응기를 갖고 있지 않으며 물리적 구조가 치밀하여 염료의 침투 능력을 감소시켜 분산 염료에 의한 염색이 용이하지 않아서 고온 및 고압 하에서의 염색이 필수적이었다. Polyester fiber, represented by polyethylene terephthalate, is widely used for clothing due to its excellent physical, chemical properties and heat resistance. It was not easy to dye with disperse dyes, so dyeing under high temperature and high pressure was essential.
한편, 폴리에틸렌 테레프탈레이트 섬유는, 염색성이 불량하기 때문에 고온(예, 약 130℃) 및 고압 조건하에서 염색할 필요가 있다. On the other hand, since polyethylene terephthalate fibers have poor dyeability, they need to be dyed under conditions of high temperature (eg, about 130° C.) and high pressure.
따라서, 이러한 섬유를 제조하는 데는 염색을 위한 특정 장치가 필요한 단점이 있다. 또한, 일반적인 폴리에스터 섬유는 스판덱스나 천연섬유와 같이 내열성이 부족한 타 섬유와 혼섬이 제한되므로 다양한 용도로의 전개 및 제품화가 한정된다는 문제가 있었다. Therefore, the production of such fibers has the disadvantage of requiring specific equipment for dyeing. In addition, since general polyester fibers are limited in blending with other fibers that lack heat resistance, such as spandex or natural fibers, there is a problem that development and commercialization for various uses are limited.
따라서 폴리에스터계 섬유가 100℃ 이하에서 염색할 수 있게 되면 스판덱스나 천연섬유와 혼합하여 사용할 수 있게 되고 반응 염료 등과 같은 내열성이 낮은 염료로 염색을 할 수 있어 다양한 소재와 혼섬이 가능하게 된다. Therefore, when polyester fibers can be dyed at 100 ° C or less, they can be mixed with spandex or natural fibers and dyed with dyes with low heat resistance such as reactive dyes, making it possible to mix with various materials.
상압 하에서의 폴리에틸렌 테레프탈레이트 섬유의 염색성을 개량하는 여러 가지 시도가 제안되었다. 예를 들면, 소위 캐리어라 불리우는 촉염제를 염색에 이용하는 방법이 알려져 있다. PET 섬유의 저온 염색법으로는 캐리어 염색법이 있으며, 캐리어라는 물질을 이용하여 PET 섬유 내로 염료를 침투시키는 염색법으로 저온(100℃)에서도 염색이 가능하여 T/W와 같은 복합사에서는 필수적으로 사용되고 있다.Various attempts to improve the dyeability of polyethylene terephthalate fibers under atmospheric pressure have been proposed. For example, a method is known in which a dye accelerator, so-called carrier, is used for dyeing. As a low-temperature dyeing method for PET fiber, there is a carrier dyeing method, which is a dyeing method in which a dye is penetrated into the PET fiber using a material called a carrier, and dyeing is possible even at a low temperature (100 ° C), so it is essentially used in composite yarns such as T / W.
그러나, 그 공정은 수많은 단점이 있다. 특히, 인체에 해로우며 자극성 있는 그러한 캐리어는 염색 공장의 작업 환경 위생을 악화시키며 염색 폐기물의 처리에 어려움이 있다. 즉, PET의 염색 온도를 낮춰 에너지 소비를 줄일 수 있다는 장점을 가지고 있지만 캐리어는 자일렌이나 메틸나프탈렌 등 벤젠 유도체를 가지는 독성물질이 사용되고 있어 작업 환경이 악화되고 환경 오염을 야기할 수 있다.However, the process has numerous drawbacks. In particular, such carriers, which are harmful to the human body and are irritating, deteriorate the working environment hygiene of dyeing factories and make it difficult to dispose of dyeing waste. That is, it has the advantage of reducing energy consumption by lowering the dyeing temperature of PET, but the carrier uses toxic substances having benzene derivatives such as xylene and methylnaphthalene, which deteriorates the working environment and may cause environmental pollution.
또한, 캐리어 염색법은 원단에 캐리어 스팟이나 불균염 등 염색불량을 초래할 수 있으며, 섬유원단에서 캐리어가 완전히 제거되지 않으면 화학약품 냄새가 발생하고 착용자가 독성에 노출될 위험이 있다. 또한 캐리어는 염색된 제품에 잔류하여 염색된 제품의 일광 견뢰도를 저하시킬 수 있다. 또한, 캐리어 염색은 강도 감소와 신도 증가와 같은 폴리에틸렌 테레프탈레이트 섬유의 물리적 성질의 변화를 야기한다. In addition, the carrier dyeing method may cause dyeing defects such as carrier spots or uneven dyeing on the fabric, and if the carrier is not completely removed from the textile fabric, there is a risk of chemical smell and the wearer being exposed to toxicity. In addition, the carrier may remain in the dyed product and deteriorate the light fastness of the dyed product. In addition, carrier dyeing causes changes in the physical properties of polyethylene terephthalate fibers, such as decreased strength and increased elongation.
또한, 자일렌, 메틸나프탈렌 등 캐리어에 사용되는 주원료는 대부분 유독물질이며 특히 자일렌의 경우 심각한 환경 오염 물질 중 하나로서 세계적으로 사용이 금지되고 있어 환경 친화형 캐리어 원료 대체를 위한 연구가 시급한 상황이다.In addition, most of the main raw materials used in carriers, such as xylene and methylnaphthalene, are toxic substances, and in particular, xylene is one of the serious environmental pollutants, and its use is banned worldwide, so research for replacing raw materials for environmentally friendly carriers is urgently needed. .
현재 친환경 단체 및 일부 국가들을 중심으로 친환경 산업에 대한 요구 및 제재가 진행되고 있으며, 특히 다량의 화학 약품이 사용되고 많은 양의 폐수가 발생되는 섬유 산업의 경우 환경 규제가 수출 규제로 이어지고 있어, 환경 친화적인 캐리어 조성물이 필요한 실정이다.Currently, demands and sanctions for eco-friendly industries are being carried out by eco-friendly organizations and some countries. In particular, in the case of the textile industry, which uses a large amount of chemicals and generates a large amount of wastewater, environmental regulations are leading to export regulations, which is environmentally friendly. There is a need for a phosphorus carrier composition.
따라서, 이러한 문제점들을 해결하기 위해 우수한 염착률, 마찰 및 일광 견뢰도를 구현할 수 있는 환경 친화형 폴리에스터 염색용 캐리어 조성물을 개발할 필요성이 증대되고 있는 실정이다.Therefore, in order to solve these problems, there is an increasing need to develop an environmentally friendly polyester dyeing carrier composition capable of implementing excellent dyeing rate, friction and light fastness.
본 발명은 환경 친화형 폴리에스터 염색용 캐리어 조성물에 관한 것이다.The present invention relates to a carrier composition for dyeing environmentally friendly polyester.
상기한 기술적 과제를 해결하고자, 본 발명은 하기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 하기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상을 포함하는,In order to solve the above technical problem, the present invention includes at least one of benzyl benzoate represented by the following formula (1) and dibenzyl ether represented by the following formula (2),
환경 친화형 폴리에스터 염색용 캐리어 조성물을 제공한다:An environment-friendly polyester dyeing carrier composition is provided:
[화학식 1][Formula 1]
[화학식 2][Formula 2]
상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상은 상기 캐리어 조성물 100 wt%에 대하여 35 wt% 내지 50 wt%의 함량으로 포함하는 것을 특징으로 한다. At least one of benzyl benzoate represented by Formula 1 and dibenzyl ether represented by Formula 2 is present in an amount of 35 wt% to 50 wt% based on 100 wt% of the carrier composition. It is characterized by including.
상기 캐리어 조성물은 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)을 포함하는 것을 특징으로 한다.The carrier composition is characterized in that it includes benzyl benzoate represented by Chemical Formula 1 and dibenzyl ether represented by Chemical Formula 2 above.
상기 캐리어 조성물은 유화제를 더 포함하는 것을 특징으로 한다.The carrier composition is characterized in that it further comprises an emulsifier.
상기 유화제는 상기 캐리어 조성물 100 wt%에 대하여 30 wt% 이하의 함량으로 포함하는 것을 특징으로 한다.The emulsifier is characterized in that it is included in an amount of 30 wt% or less based on 100 wt% of the carrier composition.
본 발명의 다른 측면으로는 상기 환경 친화형 폴리에스터 염색용 캐리어 조성물을 포함한 염료로 염색된 폴리에스터 섬유 제품을 제공한다.Another aspect of the present invention provides a polyester fiber product dyed with a dye including the environmentally friendly polyester dyeing carrier composition.
상기 폴리에스터 섬유 제품은 100 ℃ 이하에서 염색된 것을 특징으로 한다.The polyester fiber product is characterized in that it is dyed at 100 ℃ or less.
본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은 독성이 없는 환경 친화형 성분을 포함함으로써, 무독성 저온 폴리에스터 염색용 캐리어 조성물을 제공할 수 있다.The carrier composition for dyeing an environmentally friendly polyester according to an embodiment of the present invention includes a non-toxic environmentally friendly component, thereby providing a non-toxic, low-temperature carrier composition for dyeing polyester.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은 모든 성분을 친환경적인 성분으로 대체함으로써, 해외 규제에 대응할 수 있으며, 작업자의 작업 환경을 개선할 수 있다. In addition, the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention can respond to foreign regulations and improve the working environment of workers by replacing all components with environmentally friendly components.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은, 무독성의 환경 친화형 폴리에스터 염색용 캐리어 조성물로서 폴리에스터 캐리어 염색 공정에서 발생하는 다량의 독성 유증기와 환경 오염 물질이 없고, 가성비가 뛰어나고 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않고, 제반 견뢰도의 저하가 없는 우수한 성능을 발휘할 수 있다. In addition, the carrier composition for dyeing environmentally friendly polyester according to an embodiment of the present invention is a non-toxic, environmentally friendly carrier composition for dyeing polyester, and a large amount of toxic vapors and environmental pollutants generated in the polyester carrier dyeing process It has excellent cost performance, fast dyeing speed, no damage to dyed polyester fibers, and excellent performance without any decrease in fastness.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물의 주원료인 Polyester 팽윤제는 식품 첨가물로도 사용되고 있어 소량 음용이 가능한 원료로서 인체 무독하며, 냄새 역시 과일 향이 나오므로 작업환경을 저해시키지 않는 효과가 있다.In addition, the polyester swelling agent, which is the main raw material of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention, is also used as a food additive, so it is non-toxic to the human body as a raw material that can be consumed in small amounts, and the smell is also fruity, so it is good for the working environment. has the effect of not impairing
도 1은 본 발명의 실시예 및 비교예의 K/S 값 결과와 ΔE 결과를 나타내는 도면이다.1 is a view showing K / S value results and ΔE results of Examples and Comparative Examples of the present invention.
이하, 실시예 및 실험예를 통해 본 발명을 보다 구체적으로 설명한다. 그러나 이들 예는 본 발명의 이해를 돕기 위한 것일 뿐 어떠한 의미로든 본 발명의 범위가 이들 예로 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail through Examples and Experimental Examples. However, these examples are only for helping the understanding of the present invention, and the scope of the present invention is not limited to these examples in any sense.
본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은 하기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 하기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상을 포함한다:An environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention contains at least one of benzyl benzoate represented by the following formula (1) and dibenzyl ether represented by the following formula (2). contains:
[화학식 1][Formula 1]
[화학식 2][Formula 2]
일반적으로 폴리에틸렌테레프탈레이트로 대표되는 폴리에스터 섬유는 우수한 물리, 화학적 성질 및 내열성으로 의류용으로 널리 이용되고 있으나 화학 구조 중에 염료와 반응할 수 있는 반응기를 갖고 있지 않으며 물리적 구조가 치밀하여 염료의 침투 능력을 감소시켜 분산 염료에 의한 염색이 용이하지 않아서 고온 및 고압 하에서의 염색이 필수적이었다. 상기 폴리에틸렌 테레프탈레이트 섬유는, 염색성이 불량하기 때문에 고온(예, 약 130℃) 및 고압 조건하에서 염색할 필요가 있다. In general, polyester fibers represented by polyethylene terephthalate are widely used for clothing due to their excellent physical, chemical properties and heat resistance, but do not have a reactive group capable of reacting with dyes in their chemical structure, and have a dense physical structure, allowing dyes to penetrate. It was not easy to dye with disperse dyes by reducing the dyeing, so dyeing under high temperature and high pressure was essential. Since the polyethylene terephthalate fibers have poor dyeability, they need to be dyed under conditions of high temperature (eg, about 130° C.) and high pressure.
따라서, 이러한 섬유를 제조하는 데는 염색을 위한 특정 장치가 필요한 단점이 있다. 또한, 일반적인 폴리에스터 섬유는 스판덱스나 천연섬유와 같이 내열성이 부족한 타 섬유와 혼섬이 제한되므로 다양한 용도로의 전개 및 제품화가 한정된다는 문제가 있었다. 따라서 폴리에스터계 섬유가 100℃ 이하에서 염색할 수 있게 되면 스판덱스나 천연섬유와 혼합하여 사용할 수 있게 되고 반응 염료 등과 같은 내열성이 낮은 염료로 염색을 할 수 있어 다양한 소재와 혼섬이 가능하게 된다. Therefore, the production of such fibers has the disadvantage of requiring specific equipment for dyeing. In addition, since general polyester fibers are limited in blending with other fibers that lack heat resistance, such as spandex or natural fibers, there is a problem that development and commercialization for various uses are limited. Therefore, when polyester fibers can be dyed at 100 ° C or less, they can be mixed with spandex or natural fibers and dyed with dyes with low heat resistance such as reactive dyes, making it possible to mix with various materials.
상압 하에서의 폴리에틸렌 테레프탈레이트 섬유의 염색성을 개량하기 위해, PET 섬유의 저온 염색법으로서 캐리어 염색법이 있으며, 캐리어라는 물질을 이용하여 PET 섬유 내로 염료를 침투시키는 염색법으로 저온(100℃)에서도 염색이 가능하여 T/W와 같은 복합사에서는 필수적으로 사용되고 있다.In order to improve the dyeability of polyethylene terephthalate fibers under normal pressure, there is a carrier dyeing method as a low-temperature dyeing method for PET fibers, and a dyeing method in which dyes are penetrated into PET fibers using a material called carrier, which enables dyeing even at low temperatures (100 ° C). It is indispensably used in complex verbs such as /W.
그러나, 상기 캐리어를 이용한 염색법은 PET의 염색 온도를 낮춰 에너지 소비를 줄일 수 있다는 장점을 가지고 있지만 캐리어는 자일렌이나 메틸나프탈렌 등 벤젠 유도체를 가지는 독성물질이 사용되고 있어 작업 환경이 악화되고 환경 오염을 야기할 수 있다.However, the dyeing method using the carrier has the advantage of reducing energy consumption by lowering the dyeing temperature of PET, but the carrier uses toxic substances having benzene derivatives such as xylene and methylnaphthalene, which deteriorates the working environment and causes environmental pollution. can do.
또한, 캐리어 염색법은 원단에 캐리어 스팟이나 불균염 등 염색불량을 초래할 수 있으며, 섬유원단에서 캐리어가 완전히 제거되지 않으면 화학약품 냄새가 발생하고 착용자가 독성에 노출될 위험이 있다. 또한 캐리어는 염색된 제품에 잔류하여 염색된 제품의 일광 견뢰도를 저하시킬 수 있다. 또한, 캐리어 염색은 강도 감소와 신도 증가와 같은 폴리에틸렌 테레프탈레이트 섬유의 물리적 성질의 변화를 야기한다. In addition, the carrier dyeing method may cause dyeing defects such as carrier spots or uneven dyeing on the fabric, and if the carrier is not completely removed from the textile fabric, there is a risk of chemical smell and the wearer being exposed to toxicity. In addition, the carrier may remain in the dyed product and deteriorate the light fastness of the dyed product. In addition, carrier dyeing causes changes in the physical properties of polyethylene terephthalate fibers, such as decreased strength and increased elongation.
또한, 자일렌, 메틸나프탈렌 등 캐리어에 사용되는 주원료는 대부분 유독물질이며 특히 자일렌의 경우 심각한 환경 오염 물질 중 하나로서 세계적으로 사용이 금지되고 있어 환경 친화형 캐리어 원료 대체를 위한 연구가 시급한 상황이다.In addition, most of the main raw materials used in carriers, such as xylene and methylnaphthalene, are toxic substances, and in particular, xylene is one of the serious environmental pollutants, and its use is banned worldwide, so research for replacing raw materials for environmentally friendly carriers is urgently needed. .
본 발명의 일 실시형태에 따르면, 상기 환경 친화형 폴리에스터 염색용 캐리어 조성물은 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상을 포함하기 때문에, 상술한 바와 같이 종래의 캐리어 조성물에 사용되는 유독물질을 사용하지 않으며, 이로 인하여 환경 친화형 무독성 캐리어 조성물을 제공할 수 있다.According to one embodiment of the present invention, the environmentally friendly polyester dyeing carrier composition is any one of benzyl benzoate represented by Formula 1 and dibenzyl ether represented by Formula 2 Since it includes the above, it does not use toxic substances used in conventional carrier compositions as described above, thereby providing an environmentally friendly non-toxic carrier composition.
상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)를 포함하는 본 발명의 환경 친화형 무독성 캐리어 조성물은 기존에 사용되고 있는 벤젠, 자일렌 등 유해물질을 배제하기 때문에 환경 친화형이고 독성이 없으며, 작업 환경 개선 효과도 우수하다.The environmentally friendly non-toxic carrier composition of the present invention containing benzyl benzoate represented by the above formula 1 and dibenzyl ether represented by the above formula 2 is free from harmful substances such as benzene and xylene that have been used in the past. Because it excludes substances, it is environmentally friendly and non-toxic, and the effect of improving the working environment is excellent.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물의 주원료인 Polyester 팽윤제는 식품 첨가물로도 사용되고 있어 소량 음용이 가능한 원료로서 인체 무독하며, 냄새 역시 과일 향이 나오므로 작업환경을 저해시키지 않는 효과가 있다.In addition, the polyester swelling agent, which is the main raw material of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention, is also used as a food additive, so it is non-toxic to the human body as a raw material that can be consumed in small amounts, and the smell is also fruity, so it is good for the working environment. has the effect of not impairing
또한, 본 발명의 일 실시형태에 따른 환경 친화형 캐리어 조성물은 무독성의 환경 친화형 폴리에스터 염색용 캐리어로서 폴리에스터 캐리어 염색 공정에서 발생하는 다량의 독성 유증기와 환경 오염 물질이 없고, 가성비가 뛰어나고 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않는 우수한 효과가 있다.In addition, the environmentally friendly carrier composition according to an embodiment of the present invention is a non-toxic, environmentally friendly carrier for dyeing polyester, free from a large amount of toxic vapors and environmental pollutants generated in the polyester carrier dyeing process, has excellent cost performance, and dyes It is fast and has excellent effects that do not damage dyed polyester fibers.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은 모든 성분을 친환경적인 성분으로 대체함으로써, 해외 규제에 대응할 수 있으며, 작업자의 작업 환경을 개선할 수 있다. In addition, the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention can respond to foreign regulations and improve the working environment of workers by replacing all components with environmentally friendly components.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은, 무독성의 환경 친화형 폴리에스터 염색용 캐리어 조성물로서 폴리에스터 캐리어 염색 공정에서 발생하는 다량의 독성 유증기와 환경 오염 물질이 없고, 가성비가 뛰어나고 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않고, 제반 견뢰도의 저하가 없는 우수한 성능을 발휘할 수 있다. In addition, the carrier composition for dyeing environmentally friendly polyester according to an embodiment of the present invention is a non-toxic, environmentally friendly carrier composition for dyeing polyester, and a large amount of toxic vapors and environmental pollutants generated in the polyester carrier dyeing process It has excellent cost performance, fast dyeing speed, no damage to dyed polyester fibers, and excellent performance without any decrease in fastness.
일반적으로, 염료 분자를 폴리에스터 섬유에 빠르게 침투하도록 하기 위해서는 폴리에스터 섬유가 팽윤되어야 하고, 염료 분자가 염료 미셀을 형성하여 섬유 내부로 이동이 빠르게 진행되어야 한다.In general, in order to allow dye molecules to quickly penetrate the polyester fiber, the polyester fiber must be swollen, and the dye molecules must form dye micelles to rapidly move into the fiber.
이 때, 캐리어 조성물이 폴리에스터 섬유의 팽윤 및 내부로의 확산을 촉진시켜서 저온에서 염색이 가능하도록 한다.At this time, the carrier composition promotes swelling and internal diffusion of the polyester fiber to enable dyeing at a low temperature.
본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물이 포함하는 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)는 폴리에스터 섬유의 팽윤제로서, 폴리에스터의 비결정 영역을 팽윤시켜 염료의 침투를 용이하게 하는 역할을 수행한다.Benzyl Benzoate represented by Formula 1 and Dibenzyl Ether represented by Formula 2 included in the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention are polyester As a swelling agent for fibers, it swells the amorphous region of polyester to facilitate the penetration of dyes.
상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상은 상기 캐리어 조성물 100 wt%에 대하여 35 wt% 내지 50 wt%의 함량으로 포함하는 것을 특징으로 한다. At least one of benzyl benzoate represented by Formula 1 and dibenzyl ether represented by Formula 2 is present in an amount of 35 wt% to 50 wt% based on 100 wt% of the carrier composition. It is characterized by including.
상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상은 상기 캐리어 조성물 100 wt%에 대하여 35 wt% 내지 50 wt%의 함량으로 포함함으로써, 무독성의 환경 친화형 폴리에스터 염색용 캐리어 조성물로서 폴리에스터 캐리어 염색 공정에서 발생하는 다량의 독성 유증기와 환경 오염 물질이 없고, 가성비가 뛰어나고 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않고, 제반 견뢰도의 저하가 없는 우수한 성능을 발휘할 수 있다. At least one of benzyl benzoate represented by Formula 1 and dibenzyl ether represented by Formula 2 is present in an amount of 35 wt% to 50 wt% based on 100 wt% of the carrier composition. By including, as a non-toxic and environmentally friendly carrier composition for dyeing polyester, there is no large amount of toxic vapors and environmental pollutants generated in the polyester carrier dyeing process, excellent cost performance, fast dyeing speed, and no damage to dyed polyester fibers. It is possible to exhibit excellent performance without deterioration of various fastness.
상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상이 상기 캐리어 조성물 100 wt%에 대하여 35 wt% 미만의 함량으로 포함될 경우, 폴리에스터 섬유의 팽윤제 함량이 낮아 폴리에스터 섬유의 팽윤 효과가 낮고 염료의 침투 효과가 우수하지 못하여 저온에서 염색 효과 저하의 문제가 발생할 수 있다.When at least one of benzyl benzoate represented by Formula 1 and dibenzyl ether represented by Formula 2 is included in an amount of less than 35 wt% with respect to 100 wt% of the carrier composition, Since the content of the swelling agent in the polyester fiber is low, the swelling effect of the polyester fiber is low and the penetration effect of the dye is not excellent, which may cause a problem of lowering the dyeing effect at low temperatures.
상기 조성물 100 wt%에 대하여 50 wt%를 초과할 경우에는 소수성인 상기 성분의 함량이 과도하게 많아 유화제의 함량도 증가하게 되어 가성비가 저하될 수 있고, 상대적으로 계면활성제 및 기타 성능 보조제의 함량이 감소하여 캐리어 조성물의 균염성 및 세척성 등 기능성 문제가 발생할 수 있다.When the amount exceeds 50 wt% with respect to 100 wt% of the composition, the content of the hydrophobic component is excessively large, so the content of the emulsifier is increased and the cost ratio may be lowered, and the content of the surfactant and other performance aids is relatively high. As a result, functional problems such as leveling and washability of the carrier composition may occur.
특히, 본 발명의 일 실시형태에 따르면, 상기 캐리어 조성물은 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)을 포함하는 것을 특징으로 한다. 상기 캐리어 조성물이 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)을 모두 포함할 경우, 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않고, 제반 견뢰도의 저하가 없는 우수한 성능을 발휘할 수 있다. In particular, according to one embodiment of the present invention, the carrier composition is characterized in that it includes benzyl benzoate represented by Chemical Formula 1 and dibenzyl ether represented by Chemical Formula 2. When the carrier composition includes both benzyl benzoate represented by Chemical Formula 1 and dibenzyl ether represented by Chemical Formula 2, the dyeing speed is fast and the dyed polyester fiber is not damaged. It is possible to exhibit excellent performance without deterioration of various fastness.
상기 환경 친화형 폴리에스터 염색용 캐리어 조성물은 유화제를 더 포함하는 것을 특징으로 한다.The environmentally friendly polyester dyeing carrier composition is characterized in that it further comprises an emulsifier.
상기 환경 친화형 폴리에스터 염색용 캐리어 조성물이 포함하는 벤질 벤조에이트 (Benzyl Benzoate) 및 디벤질 에테르(Dibenzyl Ether)는 폴리에스터 섬유의 팽윤제로서 소수성을 가지고 있으므로, 침염에서 사용하기 위해서는 유화제를 사용하여야 하며, 본 발명의 일 실시형태에 따른 상기 환경 친화형 폴리에스터 염색용 캐리어 조성물은 유화제를 더 포함한다.Since benzyl benzoate and dibenzyl ether included in the environmentally friendly polyester dyeing carrier composition have hydrophobicity as a swelling agent for polyester fibers, an emulsifier must be used for use in dyeing And, the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention further includes an emulsifier.
상기 유화제는 상기 캐리어 조성물 100 wt%에 대하여 30 wt% 이하의 함량으로 포함하는 것을 특징으로 한다.The emulsifier is characterized in that it is included in an amount of 30 wt% or less based on 100 wt% of the carrier composition.
상기 유화제를 상기 캐리어 조성물 100 wt%에 대하여 30 wt% 이하의 함량으로 포함함으로써, 가성비가 뛰어나고 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않고, 제반 견뢰도의 저하가 없는 우수한 성능을 발휘할 수 있다. By including the emulsifier in an amount of 30 wt% or less with respect to 100 wt% of the carrier composition, excellent cost performance, fast dyeing speed, no damage to dyed polyester fibers, and excellent performance without any degradation in fastness can be exhibited. can
상기 유화제를 상기 캐리어 조성물 100 wt%에 대하여 30 wt% 초과로 함유할 경우, 유화제의 함량이 원료 대비 과다하게 사용됨으로써 가성비가 저하되고, 상대적으로 계면활성제 및 기타 성능 보조제의 함량이 감소하여 캐리어 조성물의 균염성 및 세척성 등 기능성 문제가 발생할 수 있다.When the emulsifier is contained in an amount of more than 30 wt% with respect to 100 wt% of the carrier composition, the content of the emulsifier is excessively used compared to the raw material, resulting in a decrease in cost performance and a relatively decrease in the content of surfactants and other performance aids in the carrier composition. Functional problems such as leveling and washability may occur.
본 발명의 일 실시형태에 따르면, 상기 환경 친화형 폴리에스터 염색용 캐리어 조성물은 물성 향상을 위하여 추가의 물질을 더 포함할 수 있다.According to one embodiment of the present invention, the environmentally friendly polyester dyeing carrier composition may further include an additional material to improve physical properties.
예를 들어, 상기 환경 친화형 폴리에스터 염색용 캐리어 조성물은 균염제, 캐리어 안정제 및 타르 방지제 등을 더 포함할 수 있다.For example, the environmentally friendly polyester dyeing carrier composition may further include a leveling agent, a carrier stabilizer, and an anti-tar agent.
상기 균염제는 본 발명의 유화제와 상용성이 좋은 것을 사용할 필요가 있으며, 일반적으로 분산력이 큰 조제가 바람직하다.It is necessary to use the leveling agent that has good compatibility with the emulsifier of the present invention, and in general, an auxiliary having a high dispersing power is preferable.
본 발명의 다른 측면으로는 상기 환경 친화형 폴리에스터 염색용 캐리어 조성물을 포함한 염료로 염색된 폴리에스터 섬유 제품을 제공한다.Another aspect of the present invention provides a polyester fiber product dyed with a dye including the environmentally friendly polyester dyeing carrier composition.
상기 폴리에스터 섬유 제품은 100 ℃ 이하에서 염색된 것을 특징으로 한다.The polyester fiber product is characterized in that it is dyed at 100 ℃ or less.
본 발명의 다른 실시형태에 따른 폴리에스터 섬유 제품은 환경 친화형 폴리에스터 염색용 캐리어 조성물을 포함하여 염색되기 때문에, 독성이 없는 작업 환경에서 100 ℃ 이하의 저온 염색이 가능하다.Since the polyester fiber product according to another embodiment of the present invention is dyed by including the environmentally friendly polyester dyeing carrier composition, it is possible to dye at a low temperature of 100 ° C. or less in a non-toxic working environment.
본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물이 포함하는 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)는 하기 표 1과 같은 물성을 가지고 있다.Benzyl Benzoate represented by Chemical Formula 1 and Dibenzyl Ether represented by Chemical Formula 2 included in the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention are shown in the following table. It has the same properties as 1.
150.17 g/mol
150.17 g/mol
212℃
212℃
1.04
1.04
108℃
108℃
본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물의 구체적인 조성은 벤질 벤조에이트 (Benzyl Benzoate) 및 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상이 35 wt% 내지 50 wt%, 유화제 10 내지 30 wt%, 균염제, 캐리어 안정제 및 타르 방지제 10 내지 30 wt% 및 잔량의 물을 포함한다.The specific composition of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention includes 35 wt% to 50 wt% of at least one of benzyl benzoate and dibenzyl ether, emulsifier 10 to 30 wt%, 10 to 30 wt% of a leveling agent, carrier stabilizer and anti-tar agent and the balance of water.
상기 환경 친화형 폴리에스터 염색용 캐리어 조성물의 pH는 특별히 제한되는 것은 아니나, 예를 들어 6-8인 것을 특징으로 한다.The pH of the environmentally friendly polyester dyeing carrier composition is not particularly limited, but is characterized in that, for example, 6-8.
이하에서는 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물을 포함한 염료로 폴리에스터 섬유를 염색하는 공정에 대하여 설명하도록 한다.Hereinafter, a process of dyeing polyester fibers with a dye including an environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention will be described.
우선 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물과 염료를 준비한다. 이 때, 캐리어 조성물의 농도는 3~5 g/L이며, 본 캐리어 조성물의 농도가 3 g/L 미만의 경우에는 염료의 침투가 어렵고, 농도가 너무 높은 경우에는 캐리어 침투 후 이탈이 용이하여 염착성이 떨어진다는 단점을 가지고 있으며, 특히 농도가 심하게 높으면 잔류되는 캐리어의 양이 많아 수세 과정에서도 염료가 빠져나올 수 있다.First, an environmentally friendly polyester dyeing carrier composition and dye according to an embodiment of the present invention are prepared. At this time, the concentration of the carrier composition is 3 to 5 g / L, and if the concentration of the carrier composition is less than 3 g / L, it is difficult to penetrate the dye, and if the concentration is too high, it is easy to escape after carrier penetration, so that the dyeing property In particular, when the concentration is extremely high, the amount of remaining carrier is large, and the dye may come out even in the washing process.
다음으로, 소요량의 연화수를 50℃로 가온하고, 조제 및 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물 등을 무첨가한 상태로 피염물을 넣고 약 10분간 처리한다.Next, the required amount of softening water is heated to 50 ° C., and the dye is added without the addition of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention and treated for about 10 minutes.
다음으로 정련제와 빙초산을 넣고 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물을 첨가 후 약 5분 정도 지나서 별도로 준비한 염료 분산액을 넣는다.Next, a refining agent and glacial acetic acid are added, and about 5 minutes after the addition of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention, a separately prepared dye dispersion is added.
염료 첨가 후 약 10분간 유지하고, pH 체크를 한다. 염욕의 pH는 4~5로 조절하는 것이 바람직하다. 상기 pH 체크 후 1℃/분 이하의 승온 속도로 승온 공정을 진행한다. 본 발명에서는 1℃/분의 승온 속도로 승온 공정을 진행하였으나 2℃/분 의 승온 속도로 승온 공정을 진행하더라도 무방하다. 이 후 소정 시간 (30~60 분) 동안 염색을 진행한다. 소정 시간 염색 공정 완료 후 샘플링을 통해 컬러를 확인한다. 이 때 필요한 경우 쉐이딩(Shading) 공정이 추가될 수 있다.After adding the dye, keep it for about 10 minutes and check the pH. It is preferable to adjust the pH of the salt bath to 4-5. After checking the pH, a temperature raising process is performed at a temperature raising rate of 1° C./min or less. In the present invention, the temperature raising process was performed at a temperature raising rate of 1° C./min, but the temperature raising process may be performed at a temperature raising rate of 2° C./min. After this, dyeing is performed for a predetermined time (30 to 60 minutes). After the completion of the dyeing process for a predetermined time, the color is checked through sampling. In this case, a shading process may be added if necessary.
컬러가 만족될 경우 냉각(냉각수 주입)하고 배액 공정을 수행한다. 본 공정은 70℃ 내지 80℃까지 천천히 냉각하면서 수행되는 것이 바람직하다.If the color is satisfied, cooling (cooling water injection) and draining process are performed. This process is preferably carried out while slowly cooling to 70 ℃ to 80 ℃.
수세의 경우 가성소다와 Hydrosulfite를 사용한 환원 수세(RC)를 사용하여 80℃에서 20분간 진행할 수 있으나, 염색물의 농도, 색상에 따라 시간과 농도는 상이할 수 있다.In the case of water washing, reducing water washing (RC) using caustic soda and hydrosulfite can be used at 80 ° C for 20 minutes, but the time and concentration may vary depending on the concentration and color of the dyed material.
텐터는 기본 조건인 180℃에서 약 2분간 진행하며, 원단의 종류에 따라 시간은 변동될 수 있다.The tenter proceeds for about 2 minutes at 180℃, which is the basic condition, and the time may vary depending on the type of fabric.
구체적으로, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물을 포함한 염료로 폴리에스터 섬유를 염색하는 공정은 아래의 표 2에 따라 진행되었다.Specifically, the process of dyeing polyester fibers with dyes including the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention was performed according to Table 2 below.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물의 구체적인 조성은 아래 표 3과 같다.In addition, the specific composition of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention is shown in Table 3 below.
본 발명의 실시예와 비교예 샘플에 대하여 세탁견뢰도와 일광견뢰도, 마찰견뢰도 테스트 및 발색성(K/S)과 균염성 테스트를 진행하였다.Wash fastness, daylight fastness, rubbing fastness test, color development (K/S) and leveling test were conducted on the samples of Examples and Comparative Examples of the present invention.
본 발명의 실시예는 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물을 포함하여 캐리어 염색을 진행한 샘플로서, 100℃에서 염색이 수행된 샘플이다. 비교예 1은 기존 일반적인 PET 염색에 의해 130℃에서 염색이 수행된 샘플이며, 비교예 2는 타사 캐리어 조성물을 포함하여 캐리어 염색이 수행된 샘플이다.An example of the present invention is a sample in which carrier dyeing was performed including the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention, and dyeing was performed at 100 ° C. Comparative Example 1 is a sample in which dyeing was performed at 130 ° C. by conventional general PET dyeing, and Comparative Example 2 is a sample in which carrier dyeing was performed including a carrier composition of another company.
세탁견뢰도는 KS K ISO 105 C06, 일광견뢰도는 KS K ISO 105-B02:2015 제논아크법, 마찰견뢰도는 KS K 0650-1:2017 기준으로 테스트를 진행하였으며, 세탁견뢰도는 표준세탁포와 염색물을 연결한 후 쇠구슬과 같이 세탁한 후 표준세탁포에 이염된 정도를 통해 판단하였다. 표준세탁포는 면, PET 등 6종류로 이루어져 있으며, 그 중 가장 낮은 등급을 세탁견뢰도 등급으로 확정하였다. 일광견뢰도는 제논아크법으로 테스트를 진행하였으며, 제논아크 일광테스트기를 통해 빛이 조사된 원단과 조사되지 않은 원단 간의 색차를 통해 평가하였다. 마찰견뢰도는 염색물과 마찰 시 이염되는 정도를 통해 판단하며, 습/건 조건 별로 테스르를 진행하였다. 장비에 기준포를 부착 후 염색물과 10초간 마찰시켜 이염된 정도로 판단하였다.Washing fastness was tested according to KS K ISO 105 C06, daylight fastness was tested according to KS K ISO 105-B02:2015 xenon arc method, and friction fastness was tested according to KS K 0650-1:2017. After connecting and washing with steel beads, it was judged through the degree of transfer to a standard laundry cloth. The standard laundry cloth is composed of six types, including cotton and PET, and the lowest grade among them was determined as the washing fastness grade. The light fastness was tested by the xenon arc method, and the color difference between the light-irradiated fabric and the unirradiated fabric was evaluated through the xenon-arc sunlight tester. Friction fastness was judged by the degree of color migration when rubbing with dyes, and tests were conducted for each wet/dry condition. After attaching a standard cloth to the equipment, rubbing it with the dye for 10 seconds was determined to determine the degree of transfer.
아래 표 4는 본 발명의 실시예, 비교예 1 및 2의 세탁견뢰도와 마찰견뢰도 테스트 결과이다.Table 4 below shows the washing fastness and rubbing fastness test results of Examples and Comparative Examples 1 and 2 of the present invention.
세탁견뢰도와 일광견뢰도 및 마찰견뢰도는 일반 분산염료로 염색한 비교예 1의 경우 4급 정도 나오는데 기존 캐리어를 사용하여 염색한 비교예 2의 경우 3.5급 정도 나오지만 본 발명의 실시예의 경우 일반 염색법에 의한 비교예 1과 유사한 4급이 나왔다. 즉, 일반 분산염료로 염색한 경우에는 130℃에서 염색이 수행되나, 본 발명의 실시예의 경우 100℃에서 염색이 수행될 수 있어, 염색시간과 에너지를 절감할 수 있으며, 세탁견뢰도와 일광견뢰도 및 마찰견뢰도 모두 우수한 것을 알 수 있다.In the case of Comparative Example 1 dyed with general disperse dyes, the washing fastness, daylight fastness, and friction fastness were about 4th grade, but in the case of Comparative Example 2 dyed using an existing carrier, about 3.5th grade. A grade 4 similar to that of Comparative Example 1 came out. That is, in the case of dyeing with general disperse dyes, dyeing is performed at 130 ° C., but in the case of the embodiment of the present invention, dyeing can be performed at 100 ° C., so that dyeing time and energy can be saved. It can be seen that both the friction fastness are excellent.
다음으로, 본 발명의 실시예와 일반 분산염료로 염색한 비교예 1의 발색성(K/S) 및 균염성을 테스트하기 위해 좌우색차(ΔE)를 측정하였다.Next, the left and right color difference (ΔE) was measured to test the color development (K / S) and level dyeing of the examples of the present invention and Comparative Example 1 dyed with general disperse dyes.
K/S와 ΔE는 CCM(측색기) 통해 측정이 가능하며, K/S는 빛의 흡수 및 산란에 따라 CCM에서 측정 및 산출되는 값이며 좌우색차의 경우 CCM이 측정하는 L, a, b값을 토대로 기준값과 목표값을 비교하여 나오는 값으로 일반적으로 ΔE 값이 0.5 이내로 나오면 이색이 없는 것으로 판단할 수 있다.K/S and ΔE can be measured through CCM (colorimeter), and K/S is a value measured and calculated in CCM according to light absorption and scattering. Based on this, it is a value obtained by comparing the reference value and the target value. In general, if the ΔE value is within 0.5, it can be judged that there is no exoticism.
구체적인 실험 조건은 아래 표 5와 같다.Specific experimental conditions are shown in Table 5 below.
도 1은 본 발명의 실시예 및 비교예의 K/S 값 결과와 ΔE 결과를 나타내는 도면이다.1 is a view showing K / S value results and ΔE results of Examples and Comparative Examples of the present invention.
도 1을 참조하면, 발색성의 경우 Black으로 염색하여 측정하였으며, 일반염색인 비교예 1의 경우 26.7, 캐리어 염색인 본 발명의 실시예의 경우 26.6으로 일반 염색물인 비교예 1과 유사한 값으로 측정되었다.Referring to Figure 1, in the case of color development was measured by dyeing with Black, 26.7 in the case of Comparative Example 1, which is a general dye, and 26.6 in the case of the embodiment of the present invention, which is a carrier dye, similar to Comparative Example 1, which is a general dye. It was measured.
균염성은 원단의 중심을 기준값으로 잡고 좌측과 우측 각각 측정하여 중심 대비 좌우 색차를 통해 판단하였으며, 본 발명의 실시예의 경우 좌우 모두 0.5 이내로 측정되어 본 테스트의 기준을 만족하였다.The uniformity was determined through the left and right color difference compared to the center by measuring the center of the fabric as a reference value and measuring the left and right sides respectively.
본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물은, 무독성의 환경 친화형 폴리에스터 염색용 캐리어 조성물로서 폴리에스터 캐리어 염색 공정에서 발생하는 다량의 독성 유증기와 환경 오염 물질이 없고, 가성비가 뛰어나고 염색 속도가 빠르며, 염색된 폴리에스터 섬유에 손상을 주지 않고, 제반 견뢰도의 저하가 없는 우수한 성능을 발휘할 수 있다. The carrier composition for dyeing environmentally friendly polyester according to an embodiment of the present invention is a non-toxic, environmentally friendly carrier composition for dyeing polyester, and does not have a large amount of toxic vapors and environmental pollutants generated in the polyester carrier dyeing process, It can exhibit excellent performance with excellent cost performance, fast dyeing speed, no damage to dyed polyester fibers, and no deterioration in overall fastness.
또한, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물의 주원료인 Polyester 팽윤제는 식품 첨가물로도 사용되고 있어 소량 음용이 가능한 원료로서 인체 무독하며, 냄새 역시 과일 향이 나오므로 작업환경을 저해시키지 않는 효과가 있다.In addition, the polyester swelling agent, which is the main raw material of the environmentally friendly polyester dyeing carrier composition according to an embodiment of the present invention, is also used as a food additive and is non-toxic to the human body as a raw material that can be consumed in small amounts. has the effect of not impairing
일반적인 폴리에스터 섬유는 스판덱스나 천연섬유와 같이 내열성이 부족한 타 섬유와 혼섬이 제한되므로 다양한 용도로의 전개 및 제품화가 한정된다는 문제가 있었으나, 본 발명의 일 실시형태에 따른 환경 친화형 폴리에스터 염색용 캐리어 조성물을 사용할 경우 폴리에스터계 섬유를 100℃ 이하에서 염색할 수 있어 스판덱스나 천연섬유와 혼합하여 사용할 수 있게 되고 반응 염료 등과 같은 내열성이 낮은 염료로 염색을 할 수 있어 다양한 소재와 혼섬이 가능하다는 장점이 있으며, 종래 캐리어 조성물의 문제점인 독성, 환경 오염 문제 및 해외 규제에 대응할 수 있으며, 작업자의 작업 환경을 개선할 수 있다. Common polyester fibers have a problem in that they are limited in development and commercialization for various uses because they are limited in blending with other fibers that lack heat resistance such as spandex or natural fibers. When using a carrier composition, polyester fibers can be dyed at 100 ° C or less, so that they can be mixed with spandex or natural fibers and dyed with dyes with low heat resistance such as reactive dyes, so that they can be mixed with various materials. There are advantages, and it can respond to toxicity, environmental pollution problems and overseas regulations, which are problems of conventional carrier compositions, and can improve the working environment of workers.
이상에서 설명한 본 발명은, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 있어서 본 발명의 기술적 사상을 벗어나지 않는 범위내에서 여러 가지 치환, 변경이 가능하므로 전술한 실시예에 한정되는 것은 아니다.The present invention described above is not limited to the above-described embodiments, since various substitutions and changes can be made to those skilled in the art within the scope of the technical idea of the present invention. .
Claims (7)
환경 친화형 폴리에스터 염색용 캐리어 조성물:
[화학식 1]
[화학식 2]
Containing at least one of benzyl benzoate represented by the following formula (1) and dibenzyl ether represented by the following formula (2),
Carrier composition for environmentally friendly polyester dyeing:
[Formula 1]
[Formula 2]
상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether) 중의 어느 하나 이상은 상기 캐리어 조성물 100 wt%에 대하여 35 wt% 내지 50 wt%의 함량으로 포함하는 것을 특징으로 하는,
환경 친화형 폴리에스터 염색용 캐리어 조성물.
According to claim 1,
At least one of benzyl benzoate represented by Formula 1 and dibenzyl ether represented by Formula 2 is present in an amount of 35 wt% to 50 wt% based on 100 wt% of the carrier composition. characterized in that it contains,
A carrier composition for dyeing environmentally friendly polyester.
상기 캐리어 조성물은 상기 화학식 1로 표시되는 벤질 벤조에이트 (Benzyl Benzoate) 및 상기 화학식 2로 표시되는 디벤질 에테르(Dibenzyl Ether)을 포함하는 것을 특징으로 하는,
환경 친화형 폴리에스터 염색용 캐리어 조성물.
According to claim 1,
The carrier composition is characterized in that it comprises benzyl benzoate represented by the above formula (1) and dibenzyl ether represented by the above formula (2),
A carrier composition for dyeing environmentally friendly polyester.
상기 캐리어 조성물은 유화제를 더 포함하는 것을 특징으로 하는,
환경 친화형 폴리에스터 염색용 캐리어 조성물.
According to claim 1,
Characterized in that the carrier composition further comprises an emulsifier,
A carrier composition for dyeing environmentally friendly polyester.
상기 유화제는 상기 캐리어 조성물 100 wt%에 대하여 30 wt% 이하의 함량으로 포함하는 것을 특징으로 하는,
환경 친화형 폴리에스터 염색용 캐리어 조성물.
According to claim 4,
The emulsifier is characterized in that it comprises an amount of 30 wt% or less with respect to 100 wt% of the carrier composition,
A carrier composition for dyeing environmentally friendly polyester.
A polyester fiber product dyed with a dye comprising the carrier composition for dyeing environmentally friendly polyester according to any one of claims 1 to 5.
상기 폴리에스터 섬유 제품은 100 ℃ 이하에서 염색된 것을 특징으로 하는,
폴리에스터 섬유 제품.
According to claim 6,
Characterized in that the polyester fiber product is dyed at 100 ° C or less,
polyester fiber products.