KR20230004209A - Fixing tape for Ultra Thin Glass etching - Google Patents
Fixing tape for Ultra Thin Glass etching Download PDFInfo
- Publication number
- KR20230004209A KR20230004209A KR1020210120696A KR20210120696A KR20230004209A KR 20230004209 A KR20230004209 A KR 20230004209A KR 1020210120696 A KR1020210120696 A KR 1020210120696A KR 20210120696 A KR20210120696 A KR 20210120696A KR 20230004209 A KR20230004209 A KR 20230004209A
- Authority
- KR
- South Korea
- Prior art keywords
- etching
- utg
- tape
- fixing tape
- adhesive layer
- Prior art date
Abstract
Description
본 발명은 UTG 식각공정의 강산성 용액에서 테이핑 접착 및 고정력 소실을 방지하는 동시에 잔류물 생성을 억제하여 원활한 식각공정과 식각품질증대에 도움을 주는 UTG 식각용 고정 테이프에 관한 것이다.The present invention relates to a fixing tape for UTG etching that aids in a smooth etching process and an improvement in etching quality by preventing taping adhesion and loss of fixing force in a strong acidic solution in a UTG etching process and suppressing the formation of residues.
최근 폴더블 휴대폰에 적용되는 디스플레이 커버용 글라스는 미크론 단위의 초정밀한 두께를 갖는 UTG(Ultra Thin Glass; 초박막 유리)가 사용되고 있는데, 이러한 UTG는 강산성의 에칭(식각)용액을 이용하여 원하는 초박막의 두께로 얇게 형성시키는 식각공정을 거쳐 제조된다.Recently, UTG (Ultra Thin Glass) with an ultra-precise thickness in micron units is used for display cover glass applied to foldable mobile phones. It is manufactured through an etching process to form a thin layer.
그리고, 취성에 약하고 극히 얇은 두께의 UTG는 강산성 용액에 대응시키기 위하여 식각 고정용 지그(PVC 재질)에 견고히 고정시킨 상태에서 그 지그와 함께 강산성 용액이 담긴 식각통에 담구거나 또는 식각용액이 분사되는 스프레이 분사기에 대응시키는 방법으로 식각이 이루어진다.In addition, UTG, which is weak in brittleness and has an extremely thin thickness, is immersed in an etching bucket containing a strong acid solution together with the jig while being firmly fixed to an etching fixing jig (PVC material) in order to respond to the strong acid solution, or the etching solution is sprayed. Etching is done in a way that corresponds to the spray injector.
이때 식각공정을 수행하는데 사용되는 식각용 지그에 피가공물인 UTG를 고정시키는 방법으로 클립 등과 같은 다양한 수단들이 이용될 수 있지만 얇은 두께의 식각용 고정 테이프를 부착시키는 것이 일반적이다.At this time, as a method of fixing the UTG, which is a workpiece, to the etching jig used to perform the etching process, various means such as clips may be used, but it is common to attach a thin fixing tape for etching.
그러나 식각용 지그(PVC 재질)에 피가공물인 UTG를 고정시키는데 사용되는 기존의 식각용 고정 테이프는 강산성 용액의 열악한 조건을 견디지 못하고 산성에 점차적으로 녹으면서 접착력이 약화 또는 소실되거나, 강산성 용액내에 잔류물을 생성하여 식각용액의 오염도를 높이고 식각용액의 수명을 단축하며 식각품질을 현저히 저하시키는 등 문제점이 있었으며,However, the existing fixing tape for etching, which is used to fix UTG, a workpiece, to an etching jig (PVC material) cannot withstand the poor conditions of a strong acidic solution, and gradually dissolves in acid, weakening or losing its adhesive strength, or remaining in a strong acidic solution. There were problems such as increasing the contamination level of the etching solution by generating water, shortening the lifetime of the etching solution, and significantly degrading the etching quality.
또한, UTG의 두께가 극히 얇기 때문에 UTG가 지그에 고정된 상태에서 외부의 작은 충격이나 진동으로 인해 손상되는 문제점도 발생하고 있다.In addition, since the thickness of the UTG is extremely thin, there is a problem in that the UTG is damaged due to a small external shock or vibration while being fixed to the jig.
한편, 본원 기술의 용도인 UTG 식각용 고정 테이프와 직접적으로 관련된 특허선행기술은 현재까지 확인되지 않았으며, 다만 식각시 UTG를 고정시키는 용도가 아닌 액정표시장치의 기판제조시 식각이 필요한 부분과 그렇지 않는 부분을 구분하기 위한 용도의 식각 테이프가 공지된 바 있다.On the other hand, prior art patents directly related to the fixing tape for UTG etching, which is the use of the technology of the present application, has not been identified until now. Etching tape for the purpose of distinguishing the non-distinguished part has been known.
즉, 특허등록 제10-1188425호(식각 테이프 및 이를 이용한 액정 표시 장치용 어레이기판의 제조 방법)는, 베이스 시트; 및 상기 베이스 시트 상에 젤(gel) 상태로 식각 물질이 도포되어 있는 식각 물질층을 포함하는 것과; 상기 식각 물질층의 상부에 위치하는 보호시트를 더 포함하는 것과; 상기 보호 시트는 PET(Poly Ethylene Terephthalate) 필름, PVC(Poly Vinyl Chloride) 필름, PE(Poly Ethylene) 필름 또는 PP(Poly Propylene) 필름인 것과; 베이스 시트는 셀로판 필름, 고분자 수지 필름 또는 서스(SUS; Steel Use Stainless) 필름인 것과; 상기 식각 물질은 질화실리콘(SiNx)을 식각시키는 식각물질인 것과; 상기 식각 물질은 NH4HF 또는 KOH인 것으로 되어 있음을 알 수 있다.That is, Patent Registration No. 10-1188425 (Etching tape and method for manufacturing an array substrate for a liquid crystal display using the same) includes a base sheet; and an etching material layer in which an etching material is applied in a gel state on the base sheet; Further comprising a protective sheet positioned on top of the etching material layer; The protective sheet is a PET (Poly Ethylene Terephthalate) film, a PVC (Poly Vinyl Chloride) film, a PE (Poly Ethylene) film, or a PP (Poly Propylene) film; The base sheet is a cellophane film, a polymer resin film or a SUS (Steel Use Stainless) film; The etching material is an etching material for etching silicon nitride (SiNx); It can be seen that the etching material is NH4HF or KOH.
이에 본 발명에서는 지그에 UTG를 부착하여 고정시킨 후 식각용액과의 접촉을 통하여 식각 중 그 테이핑 접착력의 소실을 명확히 방지하여 보다 안전하고 원활한 식강공정수행이 가능토록하고 나아가 식각용 고정 테이프로부터 떨어져나가는 잔류물의 생성까지 억제하여 식각용액의 오염방지, 사용수명연장, 식각품질증대에 크게 도움이 될뿐아니라 지그와 UTG 간에 텐션을 부여하여 외부 충격이나 진동으로부터 글라스가 손상되는 것도 방지할 수 있는 UTG 식각용 고정 테이프를 제공함에 그 기술적 과제의 주안점을 두고 완성한 것이다.Therefore, in the present invention, after attaching and fixing the UTG to the jig, it clearly prevents the loss of the taping adhesive force during etching through contact with the etching solution to enable a safer and smoother etching process, and furthermore, to separate from the fixing tape for etching UTG etching that not only greatly helps prevent contamination of etching solution, extends service life, and improves etching quality by suppressing the formation of residues, but also prevents damage to glass from external shock or vibration by providing tension between the jig and UTG. It was completed with the main focus on the technical task by providing a fixing tape for use.
위 기술적 과제를 달성하기 위한 본 발명은 강산성(불산, 황산, 질산 등)의 식각용액에 UTG(10)를 대응시키는 식각공정 중 식각용 지그(20)에 피가공물인 UTG(10)를 고정시키기 위해 사용되는 UTG 식각용 고정 테이프(A)를 제조함에 있어서, 상기 UTG 식각용 고정 테이프(A)는 베이스필름(100)을 기준으로 그 일측면에는 테이프의 접착성을 제공하는 접착층(200)이 형성되고, 타측면에는 테이프의 용이한 풀림성을 고려한 이형처리층(300)이 형성되되, 상기 베이스필름(100)은, PET(polyethylene terephthalate)를 그 재질로 하는 것과; 테이프의 접착성을 제공하는 상기 접착층(200)은 축합형 실리콘(Silicone Condensation Cure System)을 적용하여서된 것이며, 상기 지그(20)와 UTG 사이에는 PET재질의 완충필름(B)이 개재된 것이 특징이다.The present invention for achieving the above technical problem is to fix the UTG (10), which is a workpiece, to the etching jig (20) during the etching process of corresponding the UTG (10) to an etching solution of strong acidity (hydrofluoric acid, sulfuric acid, nitric acid, etc.) In manufacturing the UTG etching fixing tape (A) used for etching, the UTG etching fixing tape (A) has an
이상과 같은 해결수단을 갖는 본 발명의 UTG 식각용 고정 테이프는 그 기본 재질을 PET 필름으로 하되, 그 일측이 축합형 실리콘을 접착제로 도포하기 때문에 UTG를 고정하기 위한 부착성이 뛰어나면서도 열악한 강산성의 식각용액과의 접촉에도 부착력이 약화되거나 소실되지 않을 뿐 아니라 잔류물의 생성도 억제되어 식각용액의 오염방지는 물론 더욱 장시간 사용이 가능하고, 또한 식각공정시에 극히 얇은 두께의 UTG에 가해질 수 있는 충격이나 진동으로부터 손상을 방지하는 완충효과도 있는 등 식각공정의 원활성과 식각품질의 증대에도 크게 기여할 수 있는 유용한 발명이다.The UTG etching fixing tape of the present invention having the above solutions has a PET film as its base material, but since one side thereof is coated with condensation-type silicone as an adhesive, it has excellent adhesion for fixing UTG and has poor strong acidity. Adhesion is not weakened or lost even in contact with the etching solution, and the formation of residues is suppressed, preventing contamination of the etching solution as well as enabling use for a longer period of time, and impact that can be applied to extremely thin UTG during the etching process It is a useful invention that can greatly contribute to the smoothness of the etching process and the improvement of the etching quality, such as having a buffering effect to prevent damage from vibration.
도 1은 본 발명의 바람직한 일실시예를 보인 정면 예시도
도 2는 본 발명의 측단면상태 예시도
도 3은 본 발명의 측단면상태의 요부를 확대하여 나타낸 예시도
도 4는 본 발명에 따른 UTG 식각용 고정 테이프의 단면상태를 나타낸 예시도1 is a front exemplary view showing a preferred embodiment of the present invention
2 is an exemplary view of a side cross-sectional state of the present invention
Figure 3 is an exemplary view showing an enlarged main part of the side cross-sectional state of the present invention
Figure 4 is an exemplary view showing a cross-sectional state of a fixing tape for UTG etching according to the present invention
본 발명의 UTG 식각용 고정 테이프를 첨부된 각 도면에 의거하여 보다 상세히 설명하면 하기와 같다.The fixing tape for UTG etching of the present invention will be described in more detail based on the accompanying drawings.
본 발명은 강산성(불산, 황산, 질산 등)의 식각용액에 UTG(10)를 대응시키는 식각공정 중 식각용 지그(20)에 피가공물인 UTG(10)를 고정시키기 위해 사용되는 UTG 식각용 고정 테이프(A)를 제조함에 있어서,The present invention is a UTG etching fixing used to fix the UTG (10), which is a workpiece, to an etching jig (20) during an etching process of making the UTG (10) correspond to an etching solution of strong acidity (hydrofluoric acid, sulfuric acid, nitric acid, etc.) In manufacturing the tape (A),
상기 UTG 식각용 고정 테이프(A)는 베이스필름(100)을 기준으로 그 일측면에는 테이프의 접착성을 제공하는 접착층(200)이 형성되고, 타측면에는 테이프의 용이한 풀림성을 고려한 이형처리층(300)이 형성되되,The UTG etching fixing tape (A) is formed with an
상기 베이스필름(100)은, PET(polyethylene terephthalate)을 그 재질로 하는 것과;The
테이프의 접착성을 제공하는 상기 접착층(200)은, 축합형 실리콘(Silicone Condensation Cure System)인 것을 그 특징적 요지로 하였다.The
이때 상기 베이스필름(100)은 PET(polyethylene terephthalate)를 이용하여 얇게 제작하되, UTG와의 부착시 UTG의 움직임을 견고히 잡아주고 강산성 용액과의 접촉에도 우수한 내구성을 갖도록 50㎛ ~ 100㎛ 두께의 범위로 설정하는 것이 바람직하다.At this time, the
즉, 베이스필름(100)을 50㎛ 이하로 극히 얇게 설정하면 부착과정에서 테이프가 원하지 않게 늘어나거나 끊어질 우려가 있을 뿐 아니라 UTG의 움직임을 명확하게 잡아주지 못하는 등 취약할 수 있고, 100㎛ 이상으로 너무 두께우면 극히 불필요한 소재 및 그 원가의 낭비를 초래함으로 50㎛ ~ 100㎛로 설정하는 것이 바람직한 것이며, 본 출원인의 테스트결과 75㎛ 정도가 가장 이상적임을 도출할 수 있었다.That is, if the
상기 접착층(200)은, 액상의 실리콘(Silicone) 중에서도 접착성이 뛰어나고 다양한 환경에도 물성변화가 거의 없으며, 경화도 빠르면서 내후성과 내구성이 우수한 축합형 실리콘(Silicone Condensation Cure System)을 적용하였다.For the
그리고, 상기 접착층(200)에는 테이프의 부착여부를 손쉽게 식별할 수 있도록 Green 색상 연출을 위한 Green 안료와, 소량의 Clear 안료 및 경화를 촉진하는 경화촉진제와, 내열성과 내화학성 등 특성을 보강하기 위한 보강제가 더 첨가되며, 그 두께는 30㎛ ~ 50㎛ 정도가 이상적임을 테스트를 통해 확인할 수 있었다.In addition, the
이때, 상기 Green 안료는 시중에 판매되는 SUM Green 908을 사용하였으며, Clear 안료는 SUM Clear 315P를 사용하였고, 경화촉진제는 고온경화형 Perbutyl-Z(t-BPO(Benzoylperoxide)) 경화제를 사용하였으며, 보강제는 어느한 제품에 특정하지 아니하고 내열성과 내화학성 보강에 사용될 수 있는 것 중에서 임의로 선택 적용하였다.At this time, the Green pigment used commercially available SUM Green 908, the Clear pigment used SUM Clear 315P, the hardening accelerator used a high-temperature curing type Perbutyl-Z (t-BPO (Benzoylperoxide)) hardener, and the reinforcing agent It was randomly selected and applied among those that can be used for heat resistance and chemical resistance reinforcement without being specific to any product.
상기 Green 안료, Clear 안료, 경화촉진제, 보강제의 투입량은 상기 접착층(200)의 중량이 100g 일 경우, 4g, 1g, 1.3g, 0.1g 으로 각각 첨가하였다.When the weight of the
특히 상기 접착층(200)은, 액상의 실리콘(Silicone) 중에서도 축합형 실리콘(Silicone Condensation Cure System)을 적용함으로써, 접착성이 뛰어나고 다양한 환경에도 물성변화가 없을 뿐만 아니라 강산성(불산, 황산, 질산 등)의 식각용액과의 접촉에도 견디는 내후성과 내구성이 우수한 특성을 갖출 수 있다.In particular, the
즉, 축합형 실리콘(Silicone Condensation Cure System)은 수분(공기중)의 존재 하에서 가수분해 및 축합반응에 의해 가교 경화되는 물질이며, 혼합, 탈포와 같은 조작이 불필요하며, 온도변화에 따른 점도변화가 다른 재료에 비하여 매우 작고, 그외 가교제 종류의 변화에 따라서 경화성이나 물성 등의 특징을 변화 시킬 수 있으며, 경화시 발열이나, 흡열이 없어서 주위의 부재료에 열 스트레스나 열 쇼크를 주는 일도 없고, 경화시의 질량감소 및 수축율도 작으며, 경화 후에는 온도에 따른 물성변화가 거의 없고, 섭씨 -50 ~ 200℃의 넓은 온도 범위에서 고무탄성 등을 유지하여, 내후성과 내구성, 전기적 특성 등의 우수한 특징도 보유하고 있다.In other words, condensation type silicone (Silicone Condensation Cure System) is a material that is cross-linked and cured by hydrolysis and condensation reaction in the presence of moisture (in the air), and operations such as mixing and defoaming are unnecessary, and viscosity change due to temperature change is not necessary. It is very small compared to other materials, and characteristics such as curability and physical properties can be changed depending on the type of crosslinking agent, and there is no heat stress or thermal shock to surrounding auxiliary materials because there is no heat or heat absorption during curing. has a small decrease in mass and shrinkage rate, almost no change in physical properties according to temperature after curing, maintains rubber elasticity in a wide temperature range of -50 to 200 ° C, and has excellent characteristics such as weather resistance, durability, and electrical properties I have it.
상기 베이스필름(100)의 타측면인 배면에 코팅되는 이형처리제(300)는 롤 테이프의 용이한 풀림성을 고려하여 상기 베이스필름(100)의 타측면인 배면에 코팅되는 것으로 왁스 등 통상 이형처리를 위해 사용될 수 있는 다양한 재료가 선택될 수 있다.The
한편, UTG(10)의 두께가 얇기 때문에 UTG(10)가 지그에 곧바로 고정된 상태에서는 식각공정시에 외부의 충격이나 진동으로 인해 쉽게 파손되거나 손상될 수 있는데, 이를 방지하기 위하여 상기 지그(20)와 UTG(10) 사이에는 완충필름(B)을 개재한다.On the other hand, since the UTG 10 is thin, it can be easily damaged or damaged due to external shock or vibration during the etching process when the UTG 10 is directly fixed to the jig. To prevent this, the jig 20 ) and a buffer film (B) is interposed between the UTG (10).
이때, 상기 완충필름(B)은 지그의 일측과 반대측에 구성되며, 재질은 상기 베이스필름(10)과 동일한 PET재질로 구성되고, 두께는 100㎛ ~ 188㎛의 두께로 구성하여 충격흡수를 하는 기능이 부여되도록 한다.At this time, the buffer film (B) is composed of one side and the opposite side of the jig, the material is composed of the same PET material as the
부연설명하자면, 100㎛보다 얇은 경우에는 찢어지는 등의 손상 우려가 있고, 200㎛ 이상인 경우에는 필요이상의 과도한 재료의 낭비가 우려됨은 물론 무게감으로 인한 UTG 식각용 고정 테이프(A)의 접착력을 오히려 저하시킬 수도 있기 때문에, 본 출원인에 의한 테스트결과 완충필름(B)의 두께가 100㎛ ~ 188㎛ 정도에서 가장 적합하고 효과적인 것으로 확인할 수 있었다.To elaborate, if it is thinner than 100㎛, there is a risk of damage such as tearing, and if it is more than 200㎛, there is a concern about excessive waste of material more than necessary, and the adhesive strength of the fixing tape (A) for UTG etching is rather reduced due to the sense of weight. As a result of testing by the present applicant, it was confirmed that the thickness of the buffer film (B) is most suitable and effective at about 100 μm to 188 μm.
본 발명에서 제시하는 UTG 식각용 고정 테이프(A)는 상기 지그(20)와 완충필름(B) 및, 상기 완충필름(B)과 UTG(10)를 고정테이핑시키고 동시에 강산성의 식각용액 내에서도 접착성을 유지할 수 있도록 구성된 것인데,The UTG etching fixing tape (A) presented in the present invention fixes the
첨부된 도 1에서와 같이 UTG(10) 또는 완충필름(B)의 일측(도면상 상측)과 타측(도면상 하측)에 UTG 식각용 고정 테이프(A)를 부착시키고 양측에는 부착하지 않는 것이 바람직하다. 이는 외부로부터의 충격이나 진동에 대응할 수 있는 충격완화효과를 보다 더 향상시키기 위한 목적을 포함하고 있는 것이다.As shown in the attached FIG. 1, it is preferable to attach the fixing tape (A) for UTG etching to one side (upper side on the drawing) and the other side (lower side on the drawing) of the UTG (10) or the buffer film (B) and not to attach it to both sides. Do. This includes the purpose of further improving the shock mitigation effect capable of responding to shock or vibration from the outside.
10 : UTG
20 : 지그
100 : 베이스필름
200 : 접착층
300 : 이형처리제
A : UTG 식각용 고정 테이프
B : 완충필름10: UTG 20: Jig
100: base film 200: adhesive layer
300: release treatment agent A: fixing tape for UTG etching
B: buffer film
Claims (4)
상기 UTG 식각용 고정 테이프(A)는 베이스필름(100)을 기준으로 그 일측면에는 테이프의 접착성을 제공하는 접착층(200)이 형성되고, 타측면에는 테이프의 용이한 풀림성을 고려한 이형처리층(300)이 형성되되,
상기 베이스필름(100)은, PET(polyethylene terephthalate)를 그 재질로 하는 것과;
테이프의 접착성을 제공하는 상기 접착층(200)은, 축합형 실리콘(Silicone Condensation Cure System)인 것과;
상기 지그(20)와 UTG 사이에는 PET재질의 완충필름(B)이 개재된 것;을 특징으로 한 UTG 식각용 고정 테이프.
In manufacturing the fixing tape (A) for UTG etching used to fix the UTG (10), which is a workpiece, to the etching jig (20) during the etching process of making the UTG (10) correspond to the strongly acidic etching solution,
The UTG etching fixing tape (A) is formed with an adhesive layer 200 providing adhesiveness of the tape on one side of the base film 100 as a reference, and on the other side, a release process considering the easy release of the tape. Layer 300 is formed,
The base film 100 is made of polyethylene terephthalate (PET);
The adhesive layer 200, which provides adhesiveness of the tape, is a condensation type silicone (Silicone Condensation Cure System);
A fixing tape for UTG etching, characterized in that a buffer film (B) made of PET is interposed between the jig 20 and the UTG.
PET(polyethylene terephthalate) 재질로 제조된 상기 베이스필름(100)의 두께는, 50㎛ ~ 100㎛ 로 설정하는 것을 특징으로 한 UTG 식각용 고정 테이프.
According to claim 1,
A fixing tape for UTG etching, characterized in that the thickness of the base film 100 made of PET (polyethylene terephthalate) is set to 50 μm to 100 μm.
상기 접착층(200)에는 Green 안료, Clear 안료, 경화촉진제, 보강제를 첨가하되,
상기 Green 안료, Clear 안료, 경화촉진제, 보강제의 투입량은, 상기 실리콘접착제 100g 대비 4g, 1g, 1.3g, 0.1g 으로 각 첨가되는 것을 특징으로 한 UTG 식각용 고정 테이프.
According to claim 1,
Green pigment, clear pigment, curing accelerator, and reinforcing agent are added to the adhesive layer 200,
The green pigment, the clear pigment, the curing accelerator, and the reinforcing agent are added at 4g, 1g, 1.3g, and 0.1g, respectively, relative to 100g of the silicone adhesive.
상기 완충필름(B)은 100㎛ ~ 188㎛의 두께로 구성된 것을 특징으로 하는 UTG 식각용 고정 테이프.According to claim 1,
The buffer film (B) is a fixing tape for UTG etching, characterized in that composed of a thickness of 100㎛ ~ 188㎛.