KR20220138997A - A method of manufacturing ornaments using mother-of-pearl stickers - Google Patents
A method of manufacturing ornaments using mother-of-pearl stickers Download PDFInfo
- Publication number
- KR20220138997A KR20220138997A KR1020210045061A KR20210045061A KR20220138997A KR 20220138997 A KR20220138997 A KR 20220138997A KR 1020210045061 A KR1020210045061 A KR 1020210045061A KR 20210045061 A KR20210045061 A KR 20210045061A KR 20220138997 A KR20220138997 A KR 20220138997A
- Authority
- KR
- South Korea
- Prior art keywords
- mother
- pearl
- sticker
- manufacturing
- ornament
- Prior art date
Abstract
Description
본 발명은 자개 스티커를 이용한 장식품 제조방법에 관한 것이다. The present invention relates to a method of manufacturing an ornament using a mother-of-pearl sticker.
자개를 붙이는 방법은 크게 나누어 감입법(嵌入法:나전의 문양대로 목심을 도려내고 거기에 끼우는 법)·첩부법(貼附法:문양을 아교나 풀로 붙이는 법)·살부법(撒附法:나전을 잘게 썰어 뿌려 붙이는 법)의 3가지 방법이있다. The methods of attaching the mother-of-pearl are divided into broad categories: the engraving method (嵌入法: cut out the chestnut according to the pattern of the mother-of-pearl and put it there), the pasting method (the method of attaching the pattern with glue or glue), and the salbu method (撒附法: the method of attaching the mother-of-pearl) There are 3 methods: how to chop finely, sprinkle and paste).
이러한 방법은 얇은 자개를 이용하여 정교한 문양을 만드는 방법이므로 자칫하면 자개가 부스러지거나 깨질 수 있으므로 매우 숙달된 전문가라야 비로소 실시할 수 있는 방법이다. 실제 우리나라 전통 공예제품인 "나전칠기"의 경우, 상이나 장 등의 가구 제작시 1년이상의 시간이 걸리게 된다.Since this method is a method of making elaborate patterns using thin mother-of-pearl, the mother-of-pearl can be crushed or broken, so it is a method that can only be performed by a very skilled expert. In the case of "Najeon Lacquerware", a traditional Korean craft product, it takes more than a year to make furniture such as statues and cabinets.
이러한 제작상의 어려움으로 인하여 자개 제품을 제작하기가 어려워, 자개 제품의 가격이 올라가게 되어 자개제품의 저변이 얇아지게 된다.Due to such manufacturing difficulties, it is difficult to manufacture the mother-of-pearl product, and the price of the mother-of-pearl product increases, and the base of the mother-of-pearl product becomes thin.
상기와 같은 문제점을 해결하기 위하여 대량생산을 통한 자개제품들이 출시되고 있기는 하나, 이러한 제품들은 일부 소품이나 장신구에 한정되어 있으며, 섬세한 현대적 디자인이나 색상을 온전하게 표현하지 못하여 제품의 질이 떨어진다는 문제점이 있었다.In order to solve the above problems, mother-of-pearl products are being released through mass production, but these products are limited to some small items or ornaments, and the quality of products is poor because they cannot fully express delicate modern designs or colors. There was a problem.
본 발명이 해결하고자 하는 과제는 자개 스티커를 이용한 장식품 제조방법을 제공하는 것을 목적으로 한다.An object of the present invention is to provide a method for manufacturing ornaments using mother-of-pearl stickers.
본 발명의 과제들은 이상에서 언급한 과제로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problems of the present invention are not limited to the problems mentioned above, and other technical problems not mentioned will be clearly understood by those skilled in the art from the following description.
상기 과제를 해결하기 위한 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법은, 자개를 가공하는 단계와, 가공된 상기 자개를 이용하여 자개 스티커를 제조하는 단계와, 상기 자개 스티커를 절단하는 단계와, 액자 판에 도안을 각인하는 단계 및 절단된 상기 자개 스티커를 각인된 상기 도안에 부치는 단계를 포함한다.A method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment for solving the above problems includes the steps of: processing the mother-of-pearl; manufacturing the mother-of-pearl sticker using the processed mother-of-pearl sticker; cutting the mother-of-pearl sticker; , the step of engraving the design on the frame plate and the step of attaching the cut mother-of-pearl sticker to the engraved design.
상기 자개를 가공하는 단계는, 자개를 잘게 부수어 자개 단편으로 가공하는 단계 및 자개를 염색하는 단계를 포함하고, 상기 자개 단편의 두께는 0.05mm 내지 0.2mm일 수 있다.The step of processing the mother-of-pearl includes the steps of crushing the mother-of-pearl into small pieces, processing the mother-of-pearl fragments, and dyeing the mother-of-pearl pieces, and the thickness of the mother-of-pearl fragments may be 0.05 mm to 0.2 mm.
상기 가공된 상기 자개를 이용하여 자개 스티커를 제조하는 단계는, 일면에 제1 접착층이 형성된 베이스 필름 상에 자개를 부착하여 자개층을 형성하는 단계를 포함하고, 상기 베이스 필름은 합성수지로 이루어지며, 상기 베이스 필름의 두께는 0.1mm 내지 0.15mm이고, 상기 제1 접착층의 두께는 0.07mm 내지 0.12mm이며, 상기 자개층의 두께는 0.09mm 내지 0.25mm일 수 있다.The manufacturing of the mother-of-pearl sticker using the processed mother-of-pearl includes forming a mother-of-pearl layer by attaching the mother-of-pearl on a base film having a first adhesive layer formed on one surface, wherein the base film is made of a synthetic resin, The thickness of the base film may be 0.1 mm to 0.15 mm, the thickness of the first adhesive layer may be 0.07 mm to 0.12 mm, and the thickness of the mother-of-pearl layer may be 0.09 mm to 0.25 mm.
상기 베이스 필름의 타면에는 제2 접착층 및 이형지가 배치될 수 있다.A second adhesive layer and a release paper may be disposed on the other surface of the base film.
상기 자개층 상에 코팅층이 더 배치되고, 상기 코팅층은 우레탄 수지를 포함하여 이루어질 수 있다.A coating layer is further disposed on the mother-of-pearl layer, and the coating layer may include a urethane resin.
상기 자개 스티커를 절단하는 단계는, 상기 자개층 상에 도료를 칠하고 건조하는 단계를 더 포함하고, 상기 도료는 고분자코팅도료와 경화제가 1:1의 중량비로 혼합되어 이루어지며, 상기 건조는 91℉의 온도 환경에서 13시간 동안 수행될 수 있다.The step of cutting the mother-of-pearl sticker further includes applying a paint on the mother-of-pearl layer and drying, wherein the paint is made by mixing a polymer coating paint and a curing agent in a weight ratio of 1:1, and the drying is 91 It can be carried out for 13 hours in a temperature environment of °F.
상기 자개 스티커를 절단하는 단계는, 자개 스티커를 절단하여 자개 스티커 단편을 제조하는 단계를 포함하고, 상기 자개 스티커 단편의 두께는 0.25mm 내지 0.35mm일 수 있다.The step of cutting the mother-of-pearl sticker may include cutting the mother-of-pearl sticker to prepare a mother-of-pearl sticker piece, and the thickness of the mother-of-pearl sticker piece may be 0.25 mm to 0.35 mm.
일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에 의하면, 사용자가 손쉽게 자개 장식품을 직접 제작할 수 있게 되어 자개 공예의 저변을 확대시킬 수 있게 된다. According to the method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment, a user can easily produce the mother-of-pearl ornament directly, thereby expanding the base of the mother-of-pearl craft.
실시예들에 따른 효과는 이상에서 예시된 내용에 의해 제한되지 않으며, 더욱 다양한 효과들이 본 명세서 내에 포함되어 있다.Effects according to the embodiments are not limited by the contents exemplified above, and more various effects are included in the present specification.
도 1은 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법을 개략적으로 나타낸 도면이다.
도 2는 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 자개 스티커를 절단하는 모습을 개략적으로 나타낸 도면이다.
도 3은 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 절단된 자개 스티커를 개략적으로 나타낸 도면이다.
도 4는 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 각인된 도안의 모습을 개략적으로 나타낸 도면이다.
도 5는 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 절단된 자개 스티커를 각인된 도안에 부치는 모습을 개략적으로 나타낸 도면이다.
도 6은 다른 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 절단된 자개 스티커를 각인된 도안에 부치는 모습을 개략적으로 나타낸 도면이다.
도 7은 일 실시예에 따른 자개 스티커를 이용한 장식품의 모습을 개략적으로 나타낸 도면이다.
도 8은 다른 실시예에 따른 자개 스티커를 이용한 장식품의 모습을 개략적으로 나타낸 도면이다.1 is a view schematically showing a method of manufacturing an ornament using a mother-of-pearl sticker according to an embodiment.
2 is a diagram schematically illustrating a state in which a mother-of-pearl sticker is cut in a method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment.
3 is a view schematically showing a mother-of-pearl sticker cut in a method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment.
4 is a view schematically showing the appearance of a design engraved in the method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment.
5 is a diagram schematically illustrating a state in which a mother-of-pearl sticker cut in a method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment is attached to an engraved design.
6 is a view schematically illustrating a state in which a mother-of-pearl sticker cut in a method for manufacturing an ornament using a mother-of-pearl sticker according to another embodiment is attached to an engraved design.
7 is a view schematically showing the appearance of an ornament using a mother-of-pearl sticker according to an embodiment.
8 is a view schematically showing the appearance of an ornament using a mother-of-pearl sticker according to another embodiment.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. Advantages and features of the present invention and methods of achieving them will become apparent with reference to the embodiments described below in detail in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in a variety of different forms, only these embodiments allow the disclosure of the present invention to be complete, and common knowledge in the technical field to which the present invention belongs It is provided to fully inform the possessor of the scope of the invention, and the present invention is only defined by the scope of the claims.
이하 첨부된 도면을 참조하여 구체적인 실시예들에 대해 설명한다. Hereinafter, specific embodiments will be described with reference to the accompanying drawings.
도 1은 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법을 개략적으로 나타낸 도면이고, 도 2는 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 자개 스티커를 절단하는 모습을 개략적으로 나타낸 도면이며, 도 3은 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 절단된 자개 스티커를 개략적으로 나타낸 도면이고, 도 4는 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 각인된 도안의 모습을 개략적으로 나타낸 도면이며, 도 5는 일 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 절단된 자개 스티커를 각인된 도안에 부치는 모습을 개략적으로 나타낸 도면이고, 도 6은 다른 실시예에 따른 자개 스티커를 이용한 장식품 제조방법에서 절단된 자개 스티커를 각인된 도안에 부치는 모습을 개략적으로 나타낸 도면이며, 도 7은 일 실시예에 따른 자개 스티커를 이용한 장식품의 모습을 개략적으로 나타낸 도면이고, 도 8은 다른 실시예에 따른 자개 스티커를 이용한 장식품의 모습을 개략적으로 나타낸 도면이다.1 is a view schematically showing a method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment, and FIG. 2 is a view schematically showing a state of cutting a mother-of-pearl sticker in the method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment. , FIG. 3 is a view schematically showing a mother-of-pearl sticker cut in a method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment, and FIG. 4 is a view of a design engraved in the method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment It is a schematic view, and FIG. 5 is a view schematically showing a state in which a mother-of-pearl sticker cut in a method for manufacturing an ornament using a mother-of-pearl sticker according to an embodiment is attached to an engraved design, and FIG. 6 is a mother-of-pearl sticker according to another embodiment It is a view schematically showing a state of attaching a mother-of-pearl sticker cut in a method for manufacturing an ornament using a mother-of-pearl sticker to an engraved design, FIG. 7 is a view schematically showing the appearance of an ornament using a mother-of-pearl sticker according to an embodiment, and FIG. It is a diagram schematically showing the appearance of an ornament using a mother-of-pearl sticker according to an embodiment.
도 1 내지 도 8을 참조하면, 따른 자개 스티커를 이용한 장식품 제조방법은, 자개를 가공하는 단계(S10), 가공된 자개를 이용하여 자개 스티커를 제조하는 단계(S20), 자개 스티커를 절단하는 단계(S30), 액자 판에 도안을 각인하는 단계(S40) 및 절단된 자개 스티커를 각인된 도안에 부치는 단계(S50)를 포함할 수 있다. 1 to 8 , the method for manufacturing an ornament using a mother-of-pearl sticker according to the method includes processing a mother-of-pearl (S10), manufacturing a mother-of-pearl sticker using the processed mother-of-pearl sticker (S20), and cutting the mother-of-pearl sticker. (S30), the step of engraving the design on the frame plate (S40) and the step of posting the cut mother-of-pearl sticker on the engraved design (S50).
몇몇 실시예에서 자개를 가공하는 단계(S10)는, 자개를 잘게 부수어 자개 단편으로 가공하는 단계일 수 있다. 자개는 소라류의 야광패, 수도리패와 전복류의 청패, 호주패, 색패, 대만패, 멕시코패, 얼룩이패와 진주류의 노란진주패, 흑진주패, 홍진주패, 흰진주패로 분류되며 이 중 어느 하나 이상을 재료로 사용하여 가공할 수 있다. 몇몇 실시예에서 가공되는 자개 단편의 두께는 0.05mm 내지 0.2mm일 수 있으나, 이에 한정되는 것은 아니다. 몇몇 실시예에서 자개를 가공하는 단계(S10)는 자개를 염색하는 단계를 더 포함할 수 있다. 자개를 염색하는 단계는 각 색상별로 염색용 물감을 탄 각 물에 자개 및 소금을 넣고 끓여 자개를 염색하는 단계 일 수 있다. 다만, 이에 한정되는 것은 아니고, 자개에 색을 입히는 다양한 방법을 통하여 재개를 원하는 색상으로 염색할 수 있다.In some embodiments, the step of processing the mother-of-pearl (S10) may be a step of crushing the mother-of-pearl into small pieces of mother-of-pearl. Mother-of-pearl is classified into luminous shells of conch, blue and abalone, Australian, colored, Taiwanese, Mexican, yellow, black, red, and white pearls. Any one or more may be used as a material and processed. In some embodiments, the thickness of the mother-of-pearl fragment to be processed may be 0.05 mm to 0.2 mm, but is not limited thereto. In some embodiments, processing the mother-of-pearl ( S10 ) may further include dyeing the mother-of-pearl. The step of dyeing the mother-of-pearl may be a step of dyeing the mother-of-pearl by boiling the mother-of-pearl and salt into each water with the dye for each color. However, the present invention is not limited thereto, and may be dyed in a desired color to resume through various methods of coloring the mother-of-pearl.
몇몇 실시예에서 가공된 자개를 이용하여 자개 스티커를 제조하는 단계(S20)는, 일면에 제1 접착층이 형성된 베이스 필름 상에 자개를 부착하여 자개층을 형성하는 단계일 수 있다. 여기서, 베이스 필름은 자개 스티커의 형태를 판상(板狀, plate shape)으로 유지하고, 가공된 자개를 원하는 모양으로 고정 배치시키기 위한 것으로서, 가공된 자개가 제1 접착층을 매개하여 원하는 패턴으로 부착될 수 있는 통상의 합성수지 필름이 베이스 필름으로 사용될 수 있다. 예를 들면, 베이스 필름은 폴리에틸렌(polyethylene), 폴리프로필렌(Polypropylene), 폴리에스테르(polyester) 등의 합성수지로 이루어질 수 있고, 바람직하게는 투명하고 휘어질(flexible) 수 있는 합성수지 필름으로 이루어진다. 베이스 필름이 투명 필름인 경우, 베이스 필름을 통하여, 자개의 형태를 육안으로 직접 확인할 수 있는 이점이 있고, 베이스 필름이 휘어질 수 있는 필름인 경우, 물품 표면에 굴곡이 있거나, 물품 표면이 거친 경우에도 부착이 용이한 이점이 있다.In some embodiments, the step of manufacturing a mother-of-pearl sticker using the processed mother-of-pearl sticker ( S20 ) may be a step of forming a mother-of-pearl layer by attaching the mother-of-pearl on a base film having a first adhesive layer formed on one surface. Here, the base film is to maintain the shape of the mother-of-pearl sticker in a plate shape, and to fix and arrange the processed mother-of-pearl in a desired shape, and the processed mother-of-pearl will be attached in a desired pattern through the first adhesive layer. A conventional synthetic resin film that can be used may be used as the base film. For example, the base film may be made of a synthetic resin such as polyethylene, polypropylene, or polyester, and is preferably made of a transparent and flexible synthetic resin film. When the base film is a transparent film, there is an advantage that the shape of mother-of-pearl can be directly confirmed with the naked eye through the base film. It also has the advantage of easy attachment.
몇몇 실시예에서 판상의 원형 유지를 위해 베이스 필름의 두께는 0.1mm 내지 0.15mm일 수 있으며, 자개층의 오염을 방지하기 위하여 제1 접착층의 두께는 0.07mm 내지 0.12mm일 수 있고, 자개층의 두께는 0.09mm 내지 0.25mm일 수 있다.In some embodiments, the thickness of the base film may be 0.1 mm to 0.15 mm to maintain the circular shape of the plate, and the thickness of the first adhesive layer may be 0.07 mm to 0.12 mm to prevent contamination of the mother-of-pearl layer. The thickness may be between 0.09 mm and 0.25 mm.
몇몇 실시예에서 베이스 필름의 일면에 반대인 타면에는 이형지가 부착될 수 있으며, 이형지와 베이스 필름의 타면 사이에는 제2 접착층이 형성될 수 있다. 제2 접착층은 베이스 필름의 일면 상에 부착된 자개층의 반대면 및 베이스 필름의 자개가 부착되지 않은 영역을 덮어, 자개층을 베이스 필름에 고정시키는 역할과, 향후 자개층을 절단하여 물품에 부착시키는 접착층의 역할을 수행한다.In some embodiments, a release paper may be attached to the other surface opposite to one surface of the base film, and a second adhesive layer may be formed between the release paper and the other surface of the base film. The second adhesive layer covers the opposite side of the mother-of-pearl layer attached on one side of the base film and the area to which the mother-of-pearl of the base film is not attached to fix the mother-of-pearl layer to the base film, and cut the mother-of-pearl layer and attach it to the article in the future It acts as an adhesive layer.
몇몇 실시예에서 제2 접착층은 별도로 제조된 양면 접착 시트를 사용할 수 있다. 또한, 제2 접착층은, 상술한 특성을 만족하는 통상의 접착제를 제한없이 사용할 수 있고, 예를 들면, 아크릴 접착제, 에폭시 접착제 및 페놀 접착제 등을 사용할 수 있다.In some embodiments, the second adhesive layer may use a separately prepared double-sided adhesive sheet. In addition, as the second adhesive layer, a conventional adhesive satisfying the above-described properties may be used without limitation, and for example, an acrylic adhesive, an epoxy adhesive, and a phenol adhesive may be used.
몇몇 실시예에서 이형지는, 통상적인 스티커 제품의 일면에 부착되어, 스티커 제품이 사용되기 전까지, 스티커 제품의 접착면을 보호하는 통상의 이형지로서, 예를 들면, 상기 이형지의 표면에는 실리콘이 코팅되어, 제2 접착층과 용이하게 분리될 수 있도록 구성될 수 있다. 다만, 이에 한정되는 것은 아니며, 베이스 필름의 타면에는 이형지가 및 접착층이 배치되지 않을 수도 있다.In some embodiments, the release paper is a conventional release paper that is attached to one side of a conventional sticker product and protects the adhesive surface of the sticker product until the sticker product is used, for example, the surface of the release paper is coated with silicone. , may be configured to be easily separated from the second adhesive layer. However, the present invention is not limited thereto, and a release paper and an adhesive layer may not be disposed on the other surface of the base film.
몇몇 실시예에서 자개층 상면에는 코팅층이 배치될 수 있다. 코팅층은 자개층의 손상을 방지하기 위한 층으로, 투명하게 이루어질 수 있다. 코팅층은 에폭시 수지 또는 우레탄 수지 중 어느 하나를 포함하는 투명 접착제로 이루어질 수 있다. 다만, 이에 한정되는 것은 아니다.In some embodiments, a coating layer may be disposed on the upper surface of the mother-of-pearl layer. The coating layer is a layer for preventing damage to the mother-of-pearl layer, and may be made transparent. The coating layer may be formed of a transparent adhesive including either an epoxy resin or a urethane resin. However, the present invention is not limited thereto.
몇몇 실시예에서 자개 스티커를 절단하는 단계(S30)는, 자개 스티커를 단편으로 절단하는 단계일 수 있다. 이와 같은 절단은 도 2와 같이 레이저 커팅기를 이용하여 이루어질 수 있으며, 도 3과 같이 자개 스티커 단편은 각인된 도안의 형태에 따라 다양한 형태로 절단될 수 있다. 몇몇 실시예에서 절단된 자개 스티커 단편의 두께는 0.25mm 내지 0.35mm 일 수 있다.In some embodiments, the step of cutting the mother-of-pearl sticker (S30) may be a step of cutting the mother-of-pearl sticker into fragments. Such cutting may be performed using a laser cutter as shown in FIG. 2 , and as shown in FIG. 3 , the mother-of-pearl sticker fragment may be cut into various shapes according to the shape of the engraved design. In some embodiments, the cut mother-of-pearl sticker piece may have a thickness of 0.25 mm to 0.35 mm.
몇몇 실시예에서 자개 스티커를 절단하는 단계(S30)는 절단 전 자개층 상에 도료를 칠하고 건조하는 단계를 더 포함할 수 있다. 건조는 80~95℉의 온도 환경에서 12~32시간 동안 수행될 수 있으며, 도료는 고분자코팅도료와 경화제가 1:1의 중량비로 혼합된 것일 수 있으며, 경화제는 'EnviroTex Lite'일 수 있다. 이때 도료는 고분자코팅도료와 경화제가 1:1의 중량비로 혼합됨에 따라 적절한 시간 내에 경화되어 공정이 원활하게 수행되도록 할 수 있다. 다만, 이에 한정되는 것은 아니다.In some embodiments, the step of cutting the mother-of-pearl sticker (S30) may further include applying a paint on the mother-of-pearl layer before cutting and drying. Drying can be performed for 12 to 32 hours in a temperature environment of 80 to 95° F. The paint may be a mixture of a polymer coating paint and a curing agent in a weight ratio of 1:1, and the curing agent may be 'EnviroTex Lite'. At this time, the paint is cured within an appropriate time as the polymer coating paint and the curing agent are mixed in a weight ratio of 1:1 so that the process can be performed smoothly. However, the present invention is not limited thereto.
몇몇 실시예에서 액자 판에 도안을 각인하는 단계(S40)는, 도 4와 같이 절단된 자개 스티커 단편이 부착될 수 있는 도안에 따라 액자 판을 각인하는 단계 일 수 있다. 이와 같은 각인은 양각 또는 음각 기법을 이용할 수 있으나, 이에 한정되는 것은 아니며, 인쇄 기법을 통하여 각인을 형성할 수도 있다. In some embodiments, the step (S40) of imprinting a design on the frame plate may be a step of imprinting the frame plate according to the design to which the cut mother-of-pearl sticker fragment can be attached as shown in FIG. 4 . Such an engraving may use an embossed or engraved technique, but is not limited thereto, and the engraving may be formed through a printing technique.
몇몇 실시예에서 절단된 자개 스티커를 각인된 도안에 부치는 단계(S50)는, 도 5 및 도 6과 같이 각인된 도안에 절단된 자개 스티커 단편을 부치는 단계이며, 이는 전술한 이형지의 제거를 통하여 제2 접착층을 통하여 이루어질 수 있다. 예를 들어, 절단된 자개 스티커 단편의 이형지를 제가하여 제2 접착층을 노출시키고, 제2 접착층을 도인이 각인된 액자판에 접착시켜 절단된 자개 스티커 단편을 부칠 수 있다. 다만, 이에 한정되는 것은 아니며, 전술한 바와 같이, 절단된 자개 스티커는 제2 접착층 및 이형지 없이 제작될 수 있고, 이 경우에는 별도의 접착물질을 이용하여 절단된 자개 스티커 단편을 도안이 각인된 액자판에 접착시킬 수 있다. 이와 같이 절단된 자개 스티커 단편을 도안이 각인되 액자판에 부착함으로써 도 7 및 도 8과 같은 작품을 제작할 수 있다. 도 7 및 도 8에는 그림 작품을 일 예시로 나타내었으나, 이에 한정되는 것은 아니며, 자개 스티커를 이용하여 다양한 장식품을 제조할 수 있다.In some embodiments, the step (S50) of attaching the cut mother-of-pearl sticker to the engraved design is a step of posting the cut mother-of-pearl sticker fragment on the engraved design as shown in FIGS. 2 It can be achieved through an adhesive layer. For example, by removing the release paper of the cut mother-of-pearl sticker fragment to expose the second adhesive layer, the second adhesive layer may be adhered to a picture frame plate engraved with the mother-of-pearl sticker, and the cut mother-of-pearl sticker fragment may be sent. However, the present invention is not limited thereto, and as described above, the cut mother-of-pearl sticker may be manufactured without the second adhesive layer and release paper, and in this case, the cut mother-of-pearl sticker fragment using a separate adhesive material is engraved with a picture frame. It can be glued to the plate. By attaching the cut mother-of-pearl sticker fragment to the frame plate after the design is engraved, it is possible to produce works as shown in FIGS. 7 and 8 . 7 and 8 illustrate a picture work as an example, but the present invention is not limited thereto, and various ornaments may be manufactured using mother-of-pearl stickers.
이상 첨부된 도면을 참조하여 본 발명의 실시예들을 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.Although the embodiments of the present invention have been described above with reference to the accompanying drawings, those of ordinary skill in the art to which the present invention pertains may be embodied in other specific forms without changing the technical spirit or essential features of the present invention. you will be able to understand Therefore, it should be understood that the embodiments described above are illustrative in all respects and not restrictive.
Claims (7)
가공된 상기 자개를 이용하여 자개 스티커를 제조하는 단계;
상기 자개 스티커를 절단하는 단계;
액자 판에 도안을 각인하는 단계; 및
절단된 상기 자개 스티커를 각인된 상기 도안에 부치는 단계를 포함하는 자개 스티커를 이용한 장식품 제조방법.
processing mother-of-pearl;
manufacturing a mother-of-pearl sticker using the processed mother-of-pearl;
cutting the mother-of-pearl sticker;
Imprinting the design on the frame plate; and
A method of manufacturing an ornament using a mother-of-pearl sticker, comprising the step of attaching the cut mother-of-pearl sticker to the engraved design.
상기 자개를 가공하는 단계는, 자개를 잘게 부수어 자개 단편으로 가공하는 단계 및 자개를 염색하는 단계를 포함하고,
상기 자개 단편의 두께는 0.05mm 내지 0.2mm인 자개 스티커를 이용한 장식품 제조방법.
The method of claim 1,
The step of processing the mother-of-pearl includes the steps of crushing the mother-of-pearl into pieces and dyeing the mother-of-pearl,
A method of manufacturing an ornament using a mother-of-pearl sticker having a thickness of 0.05 mm to 0.2 mm of the mother-of-pearl fragment.
상기 가공된 상기 자개를 이용하여 자개 스티커를 제조하는 단계는, 일면에 제1 접착층이 형성된 베이스 필름 상에 자개를 부착하여 자개층을 형성하는 단계를 포함하고,
상기 베이스 필름은 합성수지로 이루어지며,
상기 베이스 필름의 두께는 0.1mm 내지 0.15mm이고,
상기 제1 접착층의 두께는 0.07mm 내지 0.12mm이며,
상기 자개층의 두께는 0.09mm 내지 0.25mm인 자개 스티커를 이용한 장식품 제조방법.
3. The method of claim 2,
The manufacturing of the mother-of-pearl sticker using the processed mother-of-pearl includes forming a mother-of-pearl layer by attaching the mother-of-pearl on a base film having a first adhesive layer formed on one surface,
The base film is made of a synthetic resin,
The thickness of the base film is 0.1mm to 0.15mm,
The thickness of the first adhesive layer is 0.07 mm to 0.12 mm,
A method of manufacturing an ornament using a mother-of-pearl sticker having a thickness of the mother-of-pearl layer of 0.09 mm to 0.25 mm.
상기 베이스 필름의 타면에는 제2 접착층 및 이형지가 배치되는 자개 스티커를 이용한 장식품 제조방법.
4. The method of claim 3,
A method of manufacturing an ornament using a mother-of-pearl sticker in which a second adhesive layer and a release paper are disposed on the other surface of the base film.
상기 자개층 상에 코팅층이 더 배치되고,
상기 코팅층은 우레탄 수지를 포함하여 이루어진 자개 스티커를 이용한 장식품 제조방법.
5. The method of claim 4,
A coating layer is further disposed on the mother-of-pearl layer,
The coating layer is a method of manufacturing an ornament using a mother-of-pearl sticker comprising a urethane resin.
상기 자개 스티커를 절단하는 단계는, 상기 자개층 상에 도료를 칠하고 건조하는 단계를 더 포함하고,
상기 도료는 고분자코팅도료와 경화제가 1:1의 중량비로 혼합되어 이루어지며,
상기 건조는 91℉의 온도 환경에서 13시간 동안 수행되는 자개 스티커를 이용한 장식품 제조방법.
5. The method of claim 4,
The step of cutting the mother-of-pearl sticker further includes applying a paint on the mother-of-pearl layer and drying it,
The paint is made by mixing a polymer coating paint and a curing agent in a weight ratio of 1:1,
The drying is a method of manufacturing ornaments using mother-of-pearl stickers that is performed for 13 hours in a temperature environment of 91°F.
상기 자개 스티커를 절단하는 단계는, 자개 스티커를 절단하여 자개 스티커 단편을 제조하는 단계를 포함하고,
상기 자개 스티커 단편의 두께는 0.25mm 내지 0.35mm인 자개 스티커를 이용한 장식품 제조방법.
7. The method of claim 6,
The step of cutting the mother-of-pearl sticker includes the step of cutting the mother-of-pearl sticker to produce a fragment of the mother-of-pearl sticker,
A method of manufacturing an ornament using a mother-of-pearl sticker having a thickness of 0.25 mm to 0.35 mm of the mother-of-pearl sticker fragment.