KR20220135714A - Reinforcing cover of Insulation and Manufacturing Method Thereof - Google Patents

Reinforcing cover of Insulation and Manufacturing Method Thereof Download PDF

Info

Publication number
KR20220135714A
KR20220135714A KR1020210041765A KR20210041765A KR20220135714A KR 20220135714 A KR20220135714 A KR 20220135714A KR 1020210041765 A KR1020210041765 A KR 1020210041765A KR 20210041765 A KR20210041765 A KR 20210041765A KR 20220135714 A KR20220135714 A KR 20220135714A
Authority
KR
South Korea
Prior art keywords
reinforcing
cover
insulation
insulating material
reinforcing cover
Prior art date
Application number
KR1020210041765A
Other languages
Korean (ko)
Other versions
KR102484541B1 (en
Inventor
윤정숙
정학규
김석
Original Assignee
주식회사 그린인슐레이터
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 그린인슐레이터 filed Critical 주식회사 그린인슐레이터
Priority to KR1020210041765A priority Critical patent/KR102484541B1/en
Publication of KR20220135714A publication Critical patent/KR20220135714A/en
Application granted granted Critical
Publication of KR102484541B1 publication Critical patent/KR102484541B1/en

Abstract

The present invention relates to an insulation reinforcing cover in which a reinforcing cover is formed on the outside of a vacuum insulation to increase strength and improve water resistance, and a manufacturing method thereof. Specifically, the insulation reinforcing cover comprises: an insulation in which a core material is formed; a skin material formed on the outside of the insulation and formed to improve impact and insulation performance; and a reinforcing cover wrapping the skin material and formed to reinforce strength.

Description

단열재 보강커버 및 이의 제조방법{Reinforcing cover of Insulation and Manufacturing Method Thereof}Reinforcing cover of Insulation and Manufacturing Method Thereof

본 발명은 진공 단열재의 외측에 보강커버가 형성되어 강도를 높이며, 내수성을 향상시킬 수 있는 단열재 보강커버 및 이의 제조방법에 대한 것이다. The present invention relates to a reinforcing cover formed on the outside of a vacuum insulator to increase strength and improve water resistance, and to a reinforcing cover for insulation and a method for manufacturing the same.

특허문헌 001은 심재와, 상기 심재를 둘러싸며 내부가 진공으로 형성되는 외피를 가지는 진공단열재; 및 일측에 상기 진공단열재가 삽입되는 삽입구를 구비하며 상기 진공단열재가 내장되는 본체와, 상기 본체에 결합되어 상기 삽입구를 폐쇄하는 커버를 구비하는 발포플라스틱을 구비하고, 이때 상기 커버가 상기 본체에 결합되었을 때 상기 본체 내부를 기밀상태로 유지하는 기밀유지부와 상기 기밀유지부는 상기 본체와 상기 커버 중 일측에 형성된 요부와, 타측에 형성되어 상기 요부가 삽입되는 홈부를 포함하는 기술을 제시하고 있다.Patent Document 001 discloses a vacuum insulation material having a core material and an outer shell that surrounds the core material and is formed in a vacuum; and a main body in which the vacuum insulation material is inserted and having an insertion port into which the vacuum insulation material is inserted on one side, and a foamed plastic having a cover coupled to the main body to close the insertion hole, wherein the cover is coupled to the main body When the airtight maintaining portion and the airtight maintaining portion for maintaining the inside of the main body in an airtight state, it proposes a technology including a recess formed on one side of the body and the cover, and a recess formed on the other side into which the recess is inserted.

특허문헌 002는 직관의 곡면에 대응하는 곡면을 가지는 제1플레이트와, 상기 제1플레이트의 일단부에 결합되는 제1마감샤시를 구비하는 적어도 하나의 제1분할체와; 직관의 곡면에 대응하는 곡면을 가지는 제2플레이트와, 상기 제2플레이트의 일단부에 결합되 는 제2마감샤시를 구비하는 적어도 하나의 제2분할체;를 구비하여, 직관을 감싸는 형태로 분리가능하게 조립함에 의해 상기 보호커버를 구성하되, 상기 제1마감샤시는, 상기 제1플레이트의 일단부가 삽입되어 압착 결합되기 위한 제1삽입홈을 가지는"ㄷ"자 단면형상의 제1결합부와, 상기 제1결합부의 단부에서 수직방향으로 꺾여 연장 형성되는 제1지지부를 구비하여 전체적으로 ㄱ"자형 단면형상을 가지고, 상기 제2마감샤시는, 상기 제2플레이트의 일단부가 삽입되어 압착 결합되기 위한 제2삽입홈을 가지는"ㄷ"자 단면형상의 제2결합부와, 상기 제2결합부의 단부에서 상기 제2결합부와는 반대방향으로 연장형성되는 연장부와, 상기 제2결합부의 단부에서 수직방향으로 꺾여 연장형성되어 상기 제2결합부 및 상기 연장부와 수직을 이루는 제2지지부를 구비하여, 전체적으로 "T" 자형 단면형상을 가지는 기술을 제시하고 있다.Patent Document 002 discloses a first plate having a curved surface corresponding to a curved surface of a straight pipe, and at least one first divided body having a first finished chassis coupled to one end of the first plate; A second plate having a curved surface corresponding to the curved surface of the straight pipe, and at least one second divided body having a second finished chassis coupled to one end of the second plate; provided and separated into a shape surrounding the straight pipe The protective cover is configured by assembling possible, but the first finished chassis includes a first coupling part having a "C" cross-sectional shape having a first insertion groove for which one end of the first plate is inserted and press-coupled; , having a first support portion extending vertically by being bent from an end of the first coupling portion to have an overall L-shaped cross-sectional shape, and the second finished chassis, one end of the second plate is inserted and pressed A second coupling part having a "C" cross-sectional shape having a second insertion groove, an extension extending from an end of the second coupling part in the opposite direction to the second coupling part, and at an end of the second coupling part It is bent in the vertical direction to extend and includes the second coupling part and the second support part that is perpendicular to the extended part, and proposes a technology having a "T"-shaped cross-sectional shape as a whole.

특허문헌 003은 코어패널과 이에 일치되는 규격의 베이스필름이 각 코어패널의 밑에 깔리는 형태로 배치되고, 각 코어패널과 베이스필름을 일괄커버하는 커버필름이 그 상면에 안착된 상태에서 이를 진공흡착하는 진공테이블과, 진공테이블상의 상기 베이스필름과 코어패널 및 커버필름을 압착하는 프레스프레임과, 상기 진공테이블과 프레스프레임에 의해 압착된 베이스필름과 코어패널 및 커버필름에 열을 가하여 베이스필름과 커버필름을 용착하는 가열수단을 포함하는 기술을 제시하고 있다.Patent Document 003 discloses a method in which a core panel and a base film of the same standard are placed under each core panel, and a cover film that collectively covers each core panel and the base film is vacuum-adsorbed while seated on the top surface. A vacuum table, a press frame for pressing the base film, the core panel, and the cover film on the vacuum table, and the base film and the cover film by applying heat to the base film, the core panel, and the cover film compressed by the vacuum table and the press frame It presents a technology including a heating means for welding the.

특허문헌 004는 심재와, 상기 심재를 둘러싸며 내부가 진공으로 형성되는 외피를 가지는 진공단열재; 상기 진공단열재가 발포 금형 내부에서 상기 발포 금형의 각 면과 소정 간격 이격되도록 유지하는 간극재; 및 상기 발포 금형 내부에서 발포되어 상기 진공단열재를 감싸면서 상기 간극재와 일체화되는 발포단열재를 포함하는 기술을 제시하고 있다.Patent Document 004 discloses a vacuum insulation material having a core material and an outer shell that surrounds the core material and is formed in a vacuum; a spacer for maintaining the vacuum insulating material to be spaced apart from each side of the foaming mold by a predetermined distance within the foaming mold; and a foamed insulation material that is foamed inside the foam mold and integrated with the gap material while enclosing the vacuum insulation material.

KR 10-2012-0129385 A (2012년11월28일)KR 10-2012-0129385 A (28 November 2012) KR 10-1572169 B1 (2015년11월20일)KR 10-1572169 B1 (November 20, 2015) KR 10-2014-0012853 A (2014년02월04일)KR 10-2014-0012853 A (February 04, 2014) KR 10-2020-0059545 A (2020년05월29일)KR 10-2020-0059545 A (29 May 2020)

본 발명은 진공 단열재의 외측에 보강커버가 형성되어 강도를 높이며, 내수성을 향상시킬 수 있는 단열재 보강커버 및 이의 제조방법에 대한 것이다.The present invention relates to a reinforcing cover formed on the outside of a vacuum insulator to increase strength and improve water resistance, and to a reinforcing cover for insulation and a method for manufacturing the same.

종래발명들의 문제점을 해결하기 위한 것이며, 본 발명은 내부에 심재(110)가 형성되는 단열재(100); 상기 단열재(100)의 외측에 형성되며, 충격 및 단열 성능을 향상시키는 표피재(200); 상기 표피재(200)를 감싸며, 강도를 보강하기 위한 보강커버(300);를 포함하는 구성으로 이루어진다.In order to solve the problems of the prior inventions, the present invention is a heat insulating material 100 in which the core material 110 is formed; a skin material 200 formed on the outside of the heat insulating material 100 and improving impact and heat insulation performance; Surrounding the skin material 200, the reinforcement cover 300 for reinforcing strength; consists of a configuration including.

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 단열재(100); 표피재(200); 보강커버(300);로 이루어지는 발명에 상기 단열재(100)에 형성되며, 상기 심재(110)를 밀봉하는 밀봉필름(120);을 부가한다.The present invention is an invention for a cover for reinforcing a heat insulating material, the heat insulator 100 presented above; skin material 200; Reinforcing cover 300; is formed on the heat insulating material 100 to the invention consisting of, and a sealing film 120 for sealing the core material 110; is added.

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 단열재(100); 표피재(200); 보강커버(300);로 이루어지는 발명에 상기 표피재(200)는 폴리에틸렌(PE), 폴리스티렌(PS), 폴리우레탄(PUR), 폴리프로필렌(PP), 스티로폼(PES보드) 중 선택된 하나로 형성되는 것;을 부가한다.The present invention is an invention for a cover for reinforcing a heat insulating material, the heat insulator 100 presented above; skin material 200; Reinforcing cover 300; In the invention consisting of, the skin material 200 is formed of one selected from polyethylene (PE), polystyrene (PS), polyurethane (PUR), polypropylene (PP), and styrofoam (PES board). add ;

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 단열재(100); 표피재(200); 보강커버(300);로 이루어지는 발명에 상기 보강커버(300)에 형성되며, 상기 표피재(200)를 감싸는 보강필름(310); 상기 보강필름(310)의 외측에 형성되며, 상기 표피재(200)의 강도를 향상시키는 보강재(330);를 부가한다.The present invention is an invention for a cover for reinforcing a heat insulating material, the heat insulator 100 presented above; skin material 200; Reinforcement cover 300; is formed on the reinforcement cover 300 in the invention consisting of, a reinforcement film 310 surrounding the skin material 200; A reinforcing material 330 formed on the outside of the reinforcing film 310 and improving the strength of the skin 200 is added.

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 단열재(100); 표피재(200); 보강커버(300);로 이루어지는 발명에 상기 보강커버(300)에 형성되며, 상기 보강필름(310)의 외측에 부착되어 상기 보강재(330)의 부착 강도를 향상시키는 보강메쉬(320);를 부가한다.The present invention is an invention for a cover for reinforcing a heat insulating material, the heat insulator 100 presented above; skin material 200; A reinforcing mesh 320 formed on the reinforcing cover 300 to the invention consisting of a reinforcing cover 300 and attached to the outside of the reinforcing film 310 to improve the adhesion strength of the reinforcing material 330; is added. do.

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 단열재(100); 표피재(200); 보강커버(300);로 이루어지는 발명에 상기 보강커버(300)는 상기 단열재(100)의 측면에 부착되어 강도를 보강하는 측면보강커버(400);를 부가한다.The present invention is an invention for a cover for reinforcing a heat insulating material, the heat insulator 100 presented above; skin material 200; Reinforcement cover 300; to the invention consisting of the reinforcing cover 300 is attached to the side of the heat insulating material 100, side reinforcing cover 400 for reinforcing strength; is added.

본 발명은 단열재 보강커버의 제조방법에 대한 발명이며, 단열재(100)를 이송하는 이송단계(S1100); 상기 이송단계(S1100) 후, 상기 단열재(100)의 외측에 표피재(200)를 접착시키는 접착단계(S1200); 상기 부착단계(S1300) 후, 상기 보강커버(300)를 상기 단열재(100)의 외측에 부착하는 부착단계(S1300);를 포함하는 구성으로 이루어진다.The present invention relates to a method for manufacturing a cover for reinforcing insulation material, comprising: a transfer step (S1100) of transferring the insulation material 100; After the transfer step (S1100), an adhesion step (S1200) of adhering the skin material 200 to the outside of the heat insulating material 100; After the attaching step (S1300), the attaching step (S1300) of attaching the reinforcing cover 300 to the outside of the insulating material 100;

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 이송단계(S1100); 접착단계(S1200); 부착단계(S1300);로 이루어지는 발명에 상기 부착단계(S1300) 중, 상기 단열재(100)의 외측에 폴리우레아 원료를 도포하는 도포단계(S1310);를 부가한다. The present invention is an invention for a cover for reinforcing insulation, the transfer step (S1100) presented above; Adhesive step (S1200); In the invention comprising an attaching step (S1300); during the attaching step (S1300), an application step (S1310) of applying a polyurea raw material to the outside of the insulating material 100 is added.

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 이송단계(S1100); 접착단계(S1200); 부착단계(S1300);로 이루어지는 발명에 상기 부착단계(S1300) 전, 폴리우레아 원료와 무기물 분말을 각각 정량 공급하는 공급단계(S1210); 상기 공급단계(S1210) 후, 상기 원료와 분말을 혼합하여 혼합원료를 생성하는 혼합단계(S1220);를 부가한다.The present invention is an invention for a cover for reinforcing insulation, the transfer step (S1100) presented above; Adhesive step (S1200); Before the attaching step (S1300) to the invention consisting of an attaching step (S1300); a supplying step (S1210) of quantitatively supplying a polyurea raw material and an inorganic powder, respectively; After the supplying step (S1210), a mixing step (S1220) of mixing the raw material and the powder to produce a mixed raw material; is added.

본 발명은 단열재 보강커버에 대한 발명이며, 앞에서 제시한 이송단계(S1100); 접착단계(S1200); 부착단계(S1300);로 이루어지는 발명에 상기 부착단계(S1300) 중, 상기 단열재(100)를 복수의 제조롤 사이로 진입시키는 진입단계(S1400); 상기 진입단계(S1400) 후, 상기 제조롤에서 상기 혼합원료가 분출되는 분출단계(S1500); 상기 분출단계(S1500) 후, 상기 혼합원료의 평탄화를 위하여 상기 단열재(100)의 상부에 분출된상기 혼합원료를 압착하는 압착단계(S1600);를 부가한다.The present invention is an invention for a cover for reinforcing insulation, the transfer step (S1100) presented above; Adhesive step (S1200); Adhesive step (S1300); of the attachment step (S1300) to the invention consisting of an entry step (S1400) of entering the insulating material 100 between the plurality of manufacturing rolls; After the entry step (S1400), the ejection step (S1500) in which the mixed raw material is ejected from the manufacturing roll; After the ejection step (S1500), a compression step (S1600) of compressing the mixed raw material ejected on the upper portion of the insulator 100 in order to flatten the mixed raw material; is added.

본 발명은 심재를 진공상태로 형성하기 위하여 밀봉필름이 형성되는 것이다.The present invention is to form a sealing film to form the core material in a vacuum state.

본 발명은 심재의 충격을 흡수하기 위하여 표피재가 형성되는 것이다.The present invention is to form a skin material in order to absorb the impact of the core material.

본 발명은 표피재의 외측에 보강커버가 형성됨에 따라 단열재의 강도와 내수성이 향상되는 것이다.The present invention is to improve the strength and water resistance of the heat insulating material as the reinforcing cover is formed on the outside of the skin material.

본 발명은 폴리우레아로 형성되는 보강재에 의하여 단열재에 보강커버를 제조하는 공정이 간단하게 형성될 수 있는 것이다.According to the present invention, the process of manufacturing the reinforcing cover on the heat insulating material can be easily formed by the reinforcing material formed of polyurea.

본 발명은 보강재의 부착 및 강도를 높이기 위하여 보강메쉬가 형성되는 것이다.The present invention is to form a reinforcing mesh in order to increase the adhesion and strength of the reinforcing material.

본 발명은 폴리우레아를 도포하여 단열재에 보강커버를 부착하는 것이다.The present invention is to attach a reinforcing cover to a heat insulating material by applying polyurea.

도 1 내지 도 2는 본 발명의 단열재 보강커버의 사시단면도.
도 3 내지 도 4는 본 발명의 측면보강커버가 설치된 단열재의 사시도.
도 5는 본 발명의 단열재 보강커버의 제조방법을 나타낸 순서도.
도 6 내지 도 7은 도 5에 도시된 단열재 보강커버의 제조방법을 나타낸 예시도.
도 8은 본 발명의 다른 실시 예에 단열재 보강커버의 제조방법을 나타낸 순서도.
도 9는 도 8에 도시된 단열재 보강커버의 제조방법을 나타낸 예시도.1 to 2 are perspective cross-sectional views of the insulation reinforcing cover of the present invention.
3 to 4 are perspective views of the insulating material on which the side reinforcement cover of the present invention is installed.
5 is a flow chart showing a method of manufacturing the insulating material reinforcing cover of the present invention.
6 to 7 are exemplary views showing a method of manufacturing the insulating material reinforcing cover shown in FIG.
8 is a flowchart showing a method of manufacturing a heat insulating material reinforcing cover according to another embodiment of the present invention.
9 is an exemplary view showing a method of manufacturing the insulating material reinforcing cover shown in FIG.

이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 본 발명의 가장 바람직한 실시 예를 상세하게 설명한다.Hereinafter, the most preferred embodiment of the present invention will be described in detail in order to be described in detail enough to be easily practiced by those of ordinary skill in the art to which the present invention pertains.

아래의 실시예에서 인용하는 번호는 인용대상에만 한정되지 않으며, 모든 실시예에 적용될 수 있다. 실시예에서 제시한 구성과 동일한 목적 및 효과를 발휘하는 대상은 균등한 치환대상에 해당된다. 실시예에서 제시한 상위개념은 기재하지 않은 하위개념 대상을 포함한다.The numbers cited in the examples below are not limited only to the objects of reference, and may be applied to all examples. An object that exhibits the same purpose and effect as the configuration presented in the embodiment corresponds to an equivalent replacement object. The higher-level concept presented in the examples includes sub-concept objects that are not described.

(실시예 1-1) 본 발명은 단열재 보강커버에 있어서, 지면(10)에 설치되며, 내부에 심재(110)가 형성되는 단열재(100); 상기 단열재(100)의 외측에 형성되며, 충격 및 단열 성능을 향상시키는 표피재(200); 상기 표피재(200)를 감싸며, 강도를 보강하기 위한 보강커버(300);를 포함한다.(Embodiment 1-1) In the present invention, in the insulating material reinforcing cover, it is installed on the ground (10), the heat insulating material 100 is formed therein the core material (110); a skin material 200 formed on the outside of the heat insulating material 100 and improving impact and heat insulation performance; and a reinforcing cover 300 for enclosing the skin material 200 and reinforcing strength.

(실시예 1-2) 본 발명의 단열재 보강커버는 실시예 1-1에 있어서, 상기 단열재(100)에 형성되며, 상기 심재(110)를 밀봉하는 밀봉필름(120);을 포함한다.(Example 1-2) In Example 1-1, the insulation reinforcing cover of the present invention includes a sealing film 120 formed on the heat insulating material 100 and sealing the core material 110.

(실시예 1-3) 본 발명의 단열재 보강커버는 실시예 1-2에 있어서, 상기 표피재(200)는 폴리에틸렌(PE), 폴리스티렌(PS), 폴리우레탄(PUR), 폴리프로필렌(PP), 스티로폼(PES보드) 중 선택된 하나로 형성되는 것;을 포함한다. (Example 1-3) In Example 1-2, the reinforcing insulation cover of the present invention is made of polyethylene (PE), polystyrene (PS), polyurethane (PUR), and polypropylene (PP). , which is formed of a selected one of Styrofoam (PES board); includes.

본 발명은 단열재 보강커버에 대한 것이며, 구체적으로 도 1에 도시된 바와 같이 진공 단열재(100)의 외측에 보강커버(300)가 형성되어 진공 단열재(100)의 강도를 높임과 동시에 시공성을 향상시킬 수 있는 것이다. 이러한 단열재 보강커버는 내부에 심재(110)가 형성되는 단열재(100)의 외측에 표피재(200)와 보강커버(300)가 형성되며, 단열재(100)의 심재(110)는 글라스 울(glass wool), 폴리우레탄(polyurethan), 실리카(silica) 등으로 형성된다. 그리고 심재(110)는 밀봉필름(120)에 의하여 밀봉되는 것으로 밀봉필름(120)은 단열필름으로서 여러 층의 금속 박막 필름이 적층된 구조가 일반적이며, 가스 배리어(gas barrier)성이 우수한 금속박막의 적층구조로 이루어져 공기나 수분의 통과를 차단하는 역할을 하는 것으로서 시간이 지나도 밀봉필름(120) 내의 진공도가 저하되지 않도록 이루어지는 것이 바람직하다. 그리고 밀봉필름(120)은 심재(110)를 감싸도록 형성되는 것으로 밀봉필름(120)에는 진공노즐이 결합되는 관통홀이 형성되어 밀봉필름(120)이 심재(110)를 감싼 후 관통홀을 통해 심재(110)의 진공을 진행한다.The present invention relates to a reinforcing cover for a heat insulator, and specifically, as shown in FIG. 1 , a reinforcing cover 300 is formed on the outside of the vacuum insulator 100 to increase the strength of the vacuum insulator 100 and improve workability at the same time. it can be In this insulating material reinforcing cover, the skin material 200 and the reinforcing cover 300 are formed on the outside of the heat insulating material 100 in which the core material 110 is formed, and the core material 110 of the heat insulating material 100 is glass wool. wool), polyurethane, silica, and the like. And the core material 110 is sealed by the sealing film 120, and the sealing film 120 is a heat insulating film and generally has a structure in which several layers of metal thin films are laminated, and a metal thin film with excellent gas barrier properties. It is preferably made in such a way that the degree of vacuum in the sealing film 120 does not decrease even over time as it is made up of a laminated structure and serves to block the passage of air or moisture. And the sealing film 120 is formed so as to surround the core material 110, the sealing film 120 is formed with a through hole to which the vacuum nozzle is coupled, the sealing film 120 wraps the core material 110, and then through the through hole. The vacuum of the core 110 is performed.

이와 같이 생성된 단열재(100)는 외측에 표피재(200)가 감싸지도록 형성되며, 표피재(200)는 내부에 수용홀이 형성되어 단열재(100)의 상부 및 하부에 접착된다. 이때, 표피재(200)는 폴리에틸렌(PE), 폴리스티렌(PS), 폴리우레탄(PUR), 폴리프로필렌(PP), 스티로폼(PES보드) 등 다양한 재질로 형성되며, 접착제에 의하여 접착되는 것이다. 표피재(200)가 형성된 단열재(100)는 외부 충격에 의하여 완충 작용을 하며, 단열 성능을 향상시킴과 동시에 내부의 진공을 유지할 수 있다.The heat insulator 100 generated in this way is formed so that the skin material 200 is wrapped on the outside, and the skin material 200 has a receiving hole formed therein and is adhered to the upper and lower portions of the heat insulating material 100 . At this time, the skin material 200 is formed of various materials such as polyethylene (PE), polystyrene (PS), polyurethane (PUR), polypropylene (PP), styrofoam (PES board), and is adhered by an adhesive. The heat insulating material 100 on which the skin material 200 is formed acts as a buffer by an external impact, and can maintain an internal vacuum while improving thermal insulation performance.

그리고 표피재(200)의 외측에 보호커버가 형성되며, 보호커버는 알루미늄, 폴리우레아 등 다양한 재질로 형성되어 단열재(100)의 강도 및 충격 흡수를 진행함과 동시에 강도가 상승하여 외부 충격에 의하여 단열재(100)의 파손을 방지할 수 있다.And a protective cover is formed on the outside of the skin material 200, and the protective cover is formed of various materials such as aluminum, polyurea, etc. It is possible to prevent damage to the insulator 100 .

(실시예 2-1) 본 발명은 단열재 보강커버에 대한 것이며, 실시예 1-1에 있어서, 상기 보강커버(300)에 형성되며, 상기 표피재(200)를 감싸는 보강필름(310); 상기 보강필름(310)의 외측에 형성되며, 상기 표피재(200)의 강도를 향상시키는 보강재(330);를 포함한다.(Embodiment 2-1) The present invention relates to a reinforcing cover for an insulating material, and in Example 1-1, a reinforcing film 310 formed on the reinforcing cover 300 and surrounding the skin 200; and a reinforcing material 330 formed on the outside of the reinforcing film 310 and improving the strength of the skin material 200 .

(실시예 2-2) 본 발명의 단열재 보강커버는 실시예 2-1에 있어서, 상기 보강재(330)에 형성되며, 상기 보강필름(310)의 외측에 부착되어 상기 보강재(330)의 부착 강도를 향상시키는 보강메쉬(320);를 포함한다.(Example 2-2) In Example 2-1, the insulating material reinforcing cover of the present invention is formed on the reinforcing material 330, and is attached to the outside of the reinforcing film 310 to provide an adhesive strength of the reinforcing material 330 Reinforcing mesh 320 to improve the; includes.

(실시예 2-3) 본 발명의 단열재 보강커버는 실시예 2-2에 있어서, 상기 보강필름(310)은 알루미늄으로 형성되는 것;을 포함한다.(Embodiment 2-3) The insulation reinforcing cover of the present invention according to Embodiment 2-2, wherein the reinforcing film 310 is formed of aluminum.

(실시예 2-4) 본 발명의 단열재 보강커버는 실시예 2-3에 있어서, 상기 보강필름(310)은 아크릴 접착제에 의하여 접착되는 것;을 포함한다.(Example 2-4) The insulation reinforcing cover of the present invention according to Example 2-3, wherein the reinforcing film 310 is adhered by an acrylic adhesive.

(실시예 2-5) 본 발명의 단열재 보강커버는 실시예 2-1에 있어서, 상기 보강재(330)는 폴리우레아(polyurea)로 형성되는 것;을 포함한다.(Example 2-5) The insulation reinforcing cover of the present invention according to Example 2-1, wherein the reinforcing material 330 is formed of polyurea.

(실시예 2-6) 본 발명의 단열재 보강커버는 실시예 2-1에 있어서, 상기 보강재(330)는 난연 성질의 무기질 분말이 혼합되는 것;을 포함한다.(Example 2-6) The insulating material reinforcing cover of the present invention according to Example 2-1, wherein the reinforcing material 330 is mixed with an inorganic powder having a flame retardant property.

본 발명은 보강커버(300)에 대한 것이며, 구체적으로 보강커버(300)는 단열재(100)의 표피재(200) 외부에 도포 및 접착되어 단열재(100)의 강도를 높임과 동시에 바탕면을 평평하게 형성하는 것이다. 이러한 보강커버(300)는 표피재(200)를 감싸는 보강필름(310)이 형성되며, 보강필름(310)은 알루미늄 재질로 형성되어 열 차단 및 단열 성능을 향상시킬 수 있다. 이때, 보강필름(310)은 표피재(200)의 외측을 감싸도록 절곡된 후 아크릴 접착제에 의하여 접착되거나 테이프 등에 의하여 접착되는 것이다.The present invention relates to a reinforcing cover 300, and specifically, the reinforcing cover 300 is applied and adhered to the outside of the skin 200 of the heat insulating material 100 to increase the strength of the heat insulator 100 and flatten the base surface at the same time. to form The reinforcing cover 300 is formed with a reinforcing film 310 surrounding the skin material 200, and the reinforcing film 310 is formed of an aluminum material to improve heat blocking and thermal insulation performance. In this case, the reinforcing film 310 is bent to surround the outer side of the skin material 200 and then adhered by an acrylic adhesive or by a tape or the like.

그리고 보강필름(310)의 외측에는 보강재(330)가 형성되며, 보강재(330)는 폴리우레아로 형성되어 보강필름(310)의 외측에 도포되어 형성된다. 이때, 보강재(330)는 폴리우레아의 성질에 의하여 보강필름(310)에 도포된 후 바로 경화되므로 폴리우레아가 일정한 두께로 도포되도록 보강재(330)를 이동시키며 도포한다. 또한, 보강재(330)는 폴리우레아로 형성되나 화재에 의하여 난연 성질의 무기물 분말을 혼합할 수 있다. 이때, 무기물 분말은 도포하기 어려우므로 폴리우레아와 혼합하여 점성을 가지도록 함에 따라 보강패널로 형성한 후 보강필름(310)의 외측에 접착시키거나 점액을 보강필름(310)의 외측에 압착시킬 수 있다.And the reinforcing material 330 is formed on the outside of the reinforcing film 310 , the reinforcing material 330 is formed of polyurea and coated on the outside of the reinforcing film 310 . At this time, since the reinforcing material 330 is cured immediately after being applied to the reinforcing film 310 due to the nature of the polyurea, the reinforcing material 330 is moved and applied so that the polyurea is applied to a certain thickness. In addition, the reinforcing material 330 is formed of polyurea, but inorganic powder having a flame retardant property may be mixed by fire. At this time, since it is difficult to apply the inorganic powder, it is mixed with polyurea to make it viscous, so it is formed into a reinforcing panel and then adhered to the outside of the reinforcing film 310 or the mucus can be compressed to the outside of the reinforcing film 310 have.

그리고 도 2를 참조하면, 보강재(330)와 보강필름(310)의 접착력을 높이기 위하여 보강필름(310)의 외측에 보강메쉬(320)가 형성되며, 보강메쉬(320)는 보강필름(310)에 접착제 등에 의하여 접착된 후 보강재(330)에 의하여 함침되는 것이다. 보강메쉬(320)는 금속재질로 형성됨이 바람직하나 단열재(100)의 무게를 줄이기 위하여 합성수지 등으로 형성될 수 있다.And referring to FIG. 2 , a reinforcing mesh 320 is formed on the outside of the reinforcing film 310 to increase the adhesion between the reinforcing material 330 and the reinforcing film 310 , and the reinforcing mesh 320 is the reinforcing film 310 . It is impregnated with the reinforcing material 330 after being adhered to the surface with an adhesive or the like. The reinforcing mesh 320 is preferably formed of a metal material, but may be formed of a synthetic resin or the like in order to reduce the weight of the heat insulating material 100 .

이와 같이 보강필름(310)의 외측에 도포된 폴리우레아로 형성되는 보강재(330)에 의하여 단열재(100)의 외측면은 경화되어 날카로운 물체 및 외부 충격에 의하여 내부의 심재(110)를 보호할 수 있는 것이다.As such, the outer surface of the insulating material 100 is cured by the reinforcing material 330 formed of polyurea applied to the outside of the reinforcing film 310 to protect the inner core 110 from sharp objects and external impacts. there will be

(실시예 3-1) 본 발명은 단열재 보강커버에 대한 것이며, 실시예 2-1에 있어서, 상기 보강커버(300)는 상기 단열재(100)의 측면에 부착되어 강도를 보강하는 측면보강커버(400);를 포함한다.(Embodiment 3-1) The present invention relates to a reinforcing cover for a heat insulating material. In Example 2-1, the reinforcing cover 300 is attached to a side surface of the heat insulator 100 to reinforce strength. 400);

(실시예 3-2) 본 발명의 단열재 보강커버는 실시예 3-1에 있어서, 상기 측면보강커버(400)에 형성되며, 상기 단열재(100)의 측면에 접하는 측판(410); 상기 측판(410)의 상부 및 하부에서 각각 연장되어 상기 단열재(100)에 체결되는 체결판(420);을 포함한다.(Embodiment 3-2) In the embodiment 3-1, the insulating material reinforcing cover of the present invention is formed on the side reinforcing cover 400, and includes: a side plate 410 in contact with the side surface of the insulating material 100; and a fastening plate 420 extending from the upper and lower portions of the side plate 410 and fastened to the insulating material 100 , respectively.

(실시예 3-3) 본 발명의 단열재 보강커버는 실시예 3-2에 있어서, 상기 측면보강커버(400)는 가요성 재질로 형성되는 것;을 포함한다.(Embodiment 3-3) The insulation reinforcing cover of the present invention according to Embodiment 3-2, wherein the side reinforcing cover 400 is formed of a flexible material; includes.

본 발명은 측면보강커버(400)에 대한 것이며, 구체적으로 도 3 내지 도 4를 참조하면, 측면보강커버(400)는 단열재(100)와 표피재(200)의 측면에 부착되어 표피재(200)가 단열재(100)에서 이탈되는 것을 방지함과 동시에 단열재(100) 시공시 서로 이웃하는 단열재(100)와의 접촉 면적을 높일 수 있는 것이다. 이러한 측면보강커버(400)는 가요성 재질로 형성되어 단열재(100) 시공시 단열재(100)간의 접촉 면적을 높임과 동시에 압착되어 형성된다. 그리고 측면보강커버(400)는 단열재(100)의 측면에 접하는 측판(410)이 형성되며, 측판(410)은 평평하게 형성되어 서로 이웃하는 단열재(100)와의 접촉면을 높인다. 구체적으로 단열재(100)의 외측에 형성되는 표피재(200)는 단열재(100)의 상부와 하부에 각각 결합되는 것으로 복수의 표피재(200)가 접함에 따라 평탄화가 진행되지 않아 서로 이웃하는 단열재(100) 사이로 열교 현상이 발생할 수 있다. 그럼에 따라 측판(410)에 의하여 서로 이웃하는 단열재(100) 사이의 간격이 좁아지도록 하는 것이다.그리고 측판(410)의 상부 및 하부에는 체결판(420)이 형성되며, 체결판(420)은 단열재(100) 및 표피재(200)의 상부 및 하부에 체결되는 것으로 체결판(420)이 단열재(100)에서 이탈되는 것을 방지한다.The present invention relates to a side reinforcing cover 400, and specifically referring to FIGS. 3 to 4 , the side reinforcing cover 400 is attached to the side surfaces of the heat insulating material 100 and the skin material 200 to form the skin material 200. . The side reinforcing cover 400 is formed of a flexible material to increase the contact area between the insulators 100 at the time of construction of the insulator 100 and is formed by compression. And the side reinforcement cover 400 is formed with a side plate 410 in contact with the side surface of the insulating material 100, the side plate 410 is formed to be flat to increase the contact surface with the insulating material 100 adjacent to each other. Specifically, the skin material 200 formed on the outside of the heat insulating material 100 is coupled to the upper and lower portions of the heat insulating material 100, respectively. As the plurality of skin materials 200 come into contact with each other, planarization does not proceed, and thus adjacent heat insulating materials. A thermal bridge phenomenon may occur between (100). Accordingly, the distance between the adjacent insulators 100 is narrowed by the side plate 410. And the fastening plate 420 is formed on the upper and lower portions of the side plate 410, and the fastening plate 420 is By being fastened to the upper and lower portions of the insulator 100 and the skin 200 , the fastening plate 420 is prevented from being separated from the insulator 100 .

이와 같은 측면보강커버(400)는 단열재(100)의 측면에 결합되는 것이며, 보강커버(300)가 감싸지도록 형성됨에 따라 단열재(100)의 측면을 보강함과 동시에 형태를 평평하게 형성할 수 있다.This side reinforcement cover 400 is coupled to the side surface of the heat insulating material 100, and as the reinforcement cover 300 is formed to be wrapped, the side surface of the insulation material 100 can be reinforced and a flat shape can be formed at the same time. .

(실시예 4-1) 본 발명은 단열재 보강커버의 제조방법에 대한 것이며, 실시예 3-1에 있어서, 단열재 보강커버의 제조방법에 있어서, 상기 단열재(100)를 이송하는 이송단계(S1100); 상기 이송단계(S1100) 후, 상기 단열재(100)의 외측에 표피재(200)를 접착시키는 접착단계(S1200); 상기 부착단계(S1300) 후, 상기 보강커버(300)를 상기 단열재(100)의 외측에 부착하는 부착단계(S1300);를 포함한다.(Example 4-1) The present invention relates to a method of manufacturing a reinforcing cover for insulation, and in Example 3-1, in the method for manufacturing a reinforcing cover for insulation, a transfer step of transferring the insulation 100 (S1100) ; After the transfer step (S1100), an adhesion step (S1200) of adhering the skin material 200 to the outside of the heat insulating material 100; After the attaching step (S1300), the attaching step (S1300) of attaching the reinforcing cover 300 to the outside of the insulating material 100; includes.

(실시예 4-2) 본 발명의 단열재 보강커버의 제조방법은 실시예 4-1에 있어서, 상기 이송단계(S1100) 전, 심재(110)에 밀봉필름(120)을 부착하는 필름부착단계(S1300);를 포함한다.(Example 4-2) In Example 4-1, the method of manufacturing the insulation reinforcing cover of the present invention includes a film attachment step of attaching the sealing film 120 to the core 110 before the transfer step (S1100) (S1100) ( S1300); includes.

(실시예 4-3) 본 발명의 단열재 보강커버의 제조방법은 실시예 4-2에 있어서, 상기 부착단계(S1300) 중, 상기 단열재(100)의 외측에 폴리우레아 원료를 도포하는 도포단계(S1310);를 포함한다.(Example 4-3) In Example 4-2, in the method of manufacturing the insulation reinforcing cover of the present invention, during the attaching step (S1300), a coating step of applying a polyurea raw material to the outside of the heat insulating material 100 ( S1310);

(실시예 4-4) 본 발명의 단열재 보강커버의 제조방법은 실시예 4-3에 있어서, 상기 이송단계(S1100)에 형성되며, 상기 단열재(100)는 복수의 이송롤 및 이송레일에 의하여 이송되는 것;을 포함한다.(Example 4-4) In Example 4-3, the method for manufacturing a reinforcing cover for insulation of the present invention is formed in the conveying step (S1100), and the heat insulating material 100 is formed by a plurality of conveying rolls and conveying rails. transported; includes.

(실시예 4-5) 본 발명의 단열재 보강커버의 제조방법은 실시예 4-3에 있어서, 상기 접착단계(S1200) 후, 측면보강커버(400)를 부착하는 측면보강단계;를 포함한다.(Example 4-5) In Example 4-3, the method of manufacturing the insulation reinforcing cover of the present invention includes a side reinforcing step of attaching the side reinforcing cover 400 after the bonding step (S1200).

본 발명은 단열재 보강커버의 제조방법에 대한 것이며, 구체적으로 단열재(100)의 외측에 보강커버(300)를 형성하는 것이다. 이러한 단열재 보강커버의 제조방법은 도 5 내지 도 7을 참조하면, 심재(110)에 밀봉필름(120)을 부착하는 필름부착단계(S1300)가 형성되며, 심재(110)를 이동시킴과 동시에 심재(110)의 상부와 하부에 밀봉필름(120)을 부착하는 것이다. 이때, 심재(110)에는 접착재가 도포된 후 상부와 하부에 밀봉필름(120)이 부착되는 것으로 밀봉필름(120)은 롤에 권취되어 형성되며, 심재(110)에 의하여 롤이 회전하며 풀리는 것이다. 그리고 심재(110)에 밀봉필름(120)이 부착되면 밀봉필름(120)을 일정한 길이로 절단한다. 이때, 밀봉필름(120)이 심재(110)의 측면에도 부착되도록 밀봉필름(120)은 심재(110)의 상부면보다 크게 절단된다. 그리고 밀봉필름(120)은 접착제 외에 심재(110)에 열에 접착되는 등 다양한 방법으로 접착될 수 있다. 밀봉필름(120)이 심재(110)에 접착된 후 심재(110)의 공기를 배출하여 진공상태로 형성한 후 단열재(100)를 이송단계(S1100)에서 이송시킨다. 이송단계(S1100)에서 복수의 이송롤 및 이송레일에 의하여 이송되는 단열재(100)의 상부와 하부에는 표피재(200)가 접착제에 의하여 접착되는 접착단계(S1200)가 형성되며, 표피재(200)는 폴리에틸렌(PE), 폴리스티렌(PS), 폴리우레탄(PUR), 폴리프로필렌(PP), 스티로폼(PES보드) 중 적어도 하나로 형성된다. The present invention relates to a method of manufacturing a reinforcing cover for a heat insulator, and specifically to form a reinforcing cover (300) on the outside of the heat insulator (100). 5 to 7, the film attaching step (S1300) of attaching the sealing film 120 to the core material 110 is formed, and at the same time moving the core material 110, the core material The sealing film 120 is attached to the upper and lower portions of the 110 . At this time, the sealing film 120 is attached to the upper and lower portions after the adhesive is applied to the core 110. The sealing film 120 is wound on a roll and is formed, and the roll is rotated and unwound by the core 110. . And when the sealing film 120 is attached to the core material 110, the sealing film 120 is cut to a predetermined length. At this time, the sealing film 120 is cut larger than the upper surface of the core material 110 so that the sealing film 120 is also attached to the side surface of the core material 110 . In addition to the adhesive, the sealing film 120 may be adhered to the core material 110 by various methods such as thermal bonding. After the sealing film 120 is adhered to the core material 110 , the air of the core material 110 is discharged to form a vacuum state, and then the heat insulating material 100 is transferred in the transfer step S1100 . In the transfer step (S1100), an adhesion step (S1200) in which the skin material 200 is adhered by an adhesive is formed on the upper and lower portions of the insulating material 100 transferred by a plurality of transfer rolls and transfer rails, and the skin material 200 ) is formed of at least one of polyethylene (PE), polystyrene (PS), polyurethane (PUR), polypropylene (PP), and styrofoam (PES board).

그리고 표피재(200)가 접착된 단열재(100)는 보강커버(300)에 의하여 부착단계(S1300)에서 보강커버(300)가 부착될 수 있으며, 보강커버(300)는 표피재(200)를 감싸도록 보강필름(310)을 감싼 후 폴리우레아로 형성되는 원료를 단열재(100)의 외측에 도포하여 보강재(330)를 형성할 수 있다.And the reinforcing cover 300 may be attached to the heat insulating material 100 to which the skin material 200 is adhered in the attaching step (S1300) by the reinforcing cover 300, and the reinforcing cover 300 is the skin material 200. After wrapping the reinforcing film 310 so as to surround it, the reinforcing material 330 may be formed by applying a raw material formed of polyurea to the outside of the insulating material 100 .

그리고 보강커버(300)를 부착하기 전 표피재(200)가 접착된 단열재(100)에는 측면보강커버(400)가 부착되는 측면보강단계가 형성되며, 측면보강커버(400)는 표피재(200)의 사면에 모두 설치되어 복수의 표피재(200) 사이로 열교현상이 발생하는 것을 방지할 수 있다. 이러한 측면보강단계는 생략할 수 있다. 따라서, 본 발명의 단열재 보강커버의 제조방법은 단열재(100)의 외측에 보강커버(300)가 형성되어 단열재(100)의 충격에 대한 파손을 방지하는 특징을 가진다. And before attaching the reinforcing cover 300, a side reinforcing step in which the side reinforcing cover 400 is attached is formed in the heat insulating material 100 to which the skin 200 is adhered, and the side reinforcing cover 400 is the skin 200 ), it is possible to prevent thermal bridges from occurring between the plurality of skin materials 200 by being installed on all the slopes. This side reinforcement step can be omitted. Accordingly, the method of manufacturing the insulating material reinforcing cover of the present invention has a feature that the reinforcing cover 300 is formed on the outside of the insulating material 100 to prevent damage to the insulating material 100 due to impact.

(실시예 5-1) 본 발명은 단열재 보강커버의 제조방법에 대한 것이며, 실시예 2-1에 있어서, 상기 부착단계(S1300) 전, 폴리우레아 원료와 무기물 분말을 각각 정량 공급하는 공급단계(S1210); 상기 공급단계(S1210) 후, 상기 원료와 분말을 혼합하여 혼합원료를 생성하는 혼합단계(S1220);을 포함한다.(Example 5-1) The present invention relates to a method for manufacturing a reinforcing insulation cover, and in Example 2-1, before the attaching step (S1300), a supply step ( S1210); After the supplying step (S1210), a mixing step (S1220) of mixing the raw material and the powder to produce a mixed raw material; includes.

(실시예 5-2) 본 발명의 단열재 보강커버의 제조방법은 실시예 5-1에 있어서, 상기 부착단계(S1300) 중, 상기 단열재(100)를 복수의 제조롤 사이로 진입시키는 진입단계(S1400);를 포함한다. (Example 5-2) In the method of manufacturing the insulation reinforcing cover of the present invention in Example 5-1, during the attaching step (S1300), the entry step (S1400) of entering the heat insulating material 100 between the plurality of production rolls ); includes.

(실시예 5-3) 본 발명의 단열재 보강커버의 제조방법은 실시예 5-2에 있어서, 상기 진입단계(S1400) 후, 상기 제조롤에서 상기 혼합원료가 분출되는 분출단계(S1500);를 포함한다.(Example 5-3) In the method of manufacturing the insulation reinforcing cover of the present invention, in Example 5-2, after the entry step (S1400), the ejection step (S1500) in which the mixed raw material is ejected from the manufacturing roll; include

(실시예 5-4) 본 발명의 단열재 보강커버의 제조방법은 실시예 5-3에 있어서, 상기 분출단계(S1500) 후, 상기 혼합원료의 평탄화를 위하여 상기 단열재(100)의 상부에 분출된상기 혼합원료를 압착하는 압착단계(S1600);를 포함한다.(Example 5-4) In Example 5-3, in the method of manufacturing the insulation reinforcing cover of the present invention, after the ejection step (S1500), the sprayed on the top of the insulation material 100 for flattening the mixed raw material. It includes a pressing step (S1600) of pressing the mixed raw material.

본 발명은 부착단계(S1300)에 대한 것이며, 구체적으로 도 8 내지 도 9를 참조하면,보강커버(300)를 폴리우레아 원료와 난연 재질의 무기물 분말을 혼합하여 단열재(100)에 접착하는 것이다. 이러한 보강커버(300)는 폴리우레아 원료와 난연 재질의 무기물 분말을 분출하여 보강커버(300)를 제조하는 것으로 단열재(100)를 복수의 제조롤 사이로 진입시켜 원료를 접착시키는 것이다. 이와 같이 보강커버(300)는 단열재(100)에 부착하기 전 폴리우레아 원료와 무기물 분말은 각각 다른 저장케이스에 저장되며, 정량이 공급되어 혼합된다. 이렇게 혼합된 혼합원료는 점성이 높게 형성되며, 단열재(100)를 복수의 제조롤에 공급된다. 이때, 제조롤에는 회전함에 따라 혼합원료가 분출되는 복수의 분출홀이 형성된다. 그리고 복수의 제조롤 사이로 단열재(100)가 진입하면 제조롤에서 분출되는 혼합원료가 단열재(100)의 상부에 분출된다. 그리고 단열재(100)는 복수의 제조롤 사이로 진입함에 따라 제조롤의 압력에 의하여 단열재(100)에 분출된 혼합원료가 평평하게 형성되는 것이다.The present invention relates to the attaching step (S1300), and specifically, referring to FIGS. 8 to 9 , the reinforcing cover 300 is mixed with a polyurea raw material and an inorganic powder of a flame retardant material to adhere to the insulating material 100 . The reinforcing cover 300 is to manufacture the reinforcing cover 300 by ejecting the polyurea raw material and the inorganic powder of the flame-retardant material. In this way, before the reinforcement cover 300 is attached to the heat insulating material 100 , the polyurea raw material and the inorganic powder are stored in different storage cases, and a fixed amount is supplied and mixed. The mixed raw material thus mixed is highly viscous, and the heat insulating material 100 is supplied to a plurality of manufacturing rolls. At this time, the manufacturing roll is formed with a plurality of ejection holes through which the mixed raw material is ejected as it rotates. And when the insulating material 100 enters between the plurality of manufacturing rolls, the mixed raw material ejected from the manufacturing roll is ejected on the upper portion of the insulating material 100 . And as the heat insulating material 100 enters between the plurality of manufacturing rolls, the mixed raw material ejected to the insulating material 100 by the pressure of the manufacturing rolls is formed to be flat.

100: 단열재 110: 심재
120: 밀봉필름 200: 표피재
300: 보강커버 310: 보강필름
320: 보강메쉬 330: 보강재
400: 측면보강커버 410: 측판
420: 체결판
S1100: 이송단계 S1200: 접착단계
S1210: 공급단계 S1220: 혼합단계
S1300: 부착단계 S1310: 도포단계
S1400: 진입단계 S1500: 분출단계
S1600: 압착단계 100: insulation 110: core material
120: sealing film 200: skin material
300: reinforcing cover 310: reinforcing film
320: reinforcing mesh 330: reinforcing material
400: side reinforcement cover 410: side plate
420: fastening plate
S1100: transfer step S1200: adhesion step
S1210: supply step S1220: mixing step
S1300: attaching step S1310: applying step
S1400: entry phase S1500: ejection phase
S1600: compression step

Claims (10)

내부에 심재(110)가 형성되는 단열재(100);
상기 단열재(100)의 외측에 형성되며, 충격 및 단열 성능을 향상시키는 표피재(200);
상기 표피재(200)를 감싸며, 강도를 보강하기 위한 보강커버(300);를 포함하는 단열재 보강커버.
a heat insulating material 100 having a core 110 formed therein;
a skin material 200 formed on the outside of the heat insulating material 100 and improving impact and heat insulation performance;
A reinforcing cover comprising a; reinforcing cover (300) for enclosing the skin material (200) and reinforcing strength.
 청구항 1에 있어서,
상기 단열재(100)에 형성되며, 상기 심재(110)를 밀봉하는 밀봉필름(120);을 포함하는 단열재 보강커버.
The method according to claim 1,
Insulation reinforcing cover comprising a; is formed on the insulating material (100), sealing film (120) for sealing the core (110).
 청구항 2에 있어서,
상기 표피재(200)는 폴리에틸렌(PE), 폴리스티렌(PS), 폴리우레탄(PUR), 폴리프로필렌(PP), 스티로폼(PES보드) 중 선택된 하나로 형성되는 것;을 포함하는 단열재 보강커버.
3. The method according to claim 2,
The skin material 200 is formed of a selected one of polyethylene (PE), polystyrene (PS), polyurethane (PUR), polypropylene (PP), styrofoam (PES board); Insulation reinforcement cover comprising a.
 청구항 1에 있어서,
상기 보강커버(300)에 형성되며, 상기 표피재(200)를 감싸는 보강필름(310);
상기 보강필름(310)의 외측에 형성되며, 상기 표피재(200)의 강도를 향상시키는 보강재(330);를 포함하는 단열재 보강커버.
The method according to claim 1,
a reinforcing film 310 formed on the reinforcing cover 300 and surrounding the skin 200;
A reinforcing material formed on the outside of the reinforcing film (310), the reinforcing material (330) for improving the strength of the skin material (200); Insulation reinforcing cover comprising a.
 청구항 4에 있어서,
상기 보강커버(300)에 형성되며, 상기 보강필름(310)의 외측에 부착되어 상기 보강재(330)의 부착 강도를 향상시키는 보강메쉬(320);를 포함하는 단열재 보강커버.
5. The method according to claim 4,
A reinforcing mesh (320) formed on the reinforcing cover (300) and attached to the outside of the reinforcing film (310) to improve the adhesion strength of the reinforcing material (330); Insulation reinforcing cover comprising a.
 청구항 4에 있어서,
상기 보강커버(300)는 상기 단열재(100)의 측면에 부착되어 강도를 보강하는 측면보강커버(400);를 포함하는 단열재 보강커버.
5. The method according to claim 4,
The reinforcing cover 300 is a side reinforcing cover 400 that is attached to the side surface of the heat insulator 100 to reinforce strength.
 단열재 보강커버의 제조방법에 있어서,
청구항 1의 상기 단열재(100)를 이송하는 이송단계(S1100);
상기 이송단계(S1100) 후, 상기 단열재(100)의 외측에 표피재(200)를 접착시키는 접착단계(S1200);
상기 부착단계(S1300) 후, 상기 보강커버(300)를 상기 단열재(100)의 외측에 부착하는 부착단계(S1300);를 포함하는 단열재 보강커버의 제조방법.
In the manufacturing method of the insulating material reinforcing cover,
A transfer step of transferring the heat insulating material 100 of claim 1 (S1100);
After the transfer step (S1100), an adhesion step (S1200) of adhering the skin material 200 to the outside of the heat insulating material 100;
After the attaching step (S1300), the attaching step (S1300) of attaching the reinforcing cover 300 to the outside of the insulator 100; Method of manufacturing a reinforcing cover for insulation comprising a.
 청구항 7에 있어서,
상기 부착단계(S1300) 중, 상기 단열재(100)의 외측에 폴리우레아 원료를 도포하는 도포단계(S1310);를 포함하는 단열재 보강커버의 제조방법.
8. The method of claim 7,
Method of manufacturing a reinforcing insulation cover comprising a; during the attaching step (S1300), a coating step (S1310) of applying a polyurea raw material to the outside of the heat insulating material (100).
 청구항 7에 있어서,
상기 부착단계(S1300) 전, 폴리우레아 원료와 무기물 분말을 각각 정량 공급하는 공급단계(S1210);
상기 공급단계(S1210) 후, 상기 원료와 분말을 혼합하여 혼합원료를 생성하는 혼합단계(S1220);를 포함하는 단열재 보강커버의 제조방법.
8. The method of claim 7,
Before the attaching step (S1300), a supply step (S1210) of supplying a quantity of the polyurea raw material and the inorganic powder, respectively;
After the supplying step (S1210), a mixing step (S1220) of mixing the raw material and the powder to create a mixed raw material; Method of manufacturing a reinforcing cover for insulation comprising a.
 청구항 9에 있어서,
상기 부착단계(S1300) 중, 상기 단열재(100)를 복수의 제조롤 사이로 진입시키는 진입단계(S1400);
상기 진입단계(S1400) 후, 상기 제조롤에서 상기 혼합원료가 분출되는 분출단계(S1500);
상기 분출단계(S1500) 후, 상기 혼합원료의 평탄화를 위하여 상기 단열재(100)의 상부에 분출된상기 혼합원료를 압착하는 압착단계(S1600);를 포함하는 단열재 보강커버의 제조방법.

10. The method of claim 9,
In the attachment step (S1300), the entry step (S1400) of entering the insulating material 100 between the plurality of manufacturing rolls;
After the entry step (S1400), the ejection step (S1500) in which the mixed raw material is ejected from the production roll;
After the ejection step (S1500), a compression step (S1600) of compressing the mixed raw material ejected on the upper portion of the insulator 100 for flattening the mixed raw material;
KR1020210041765A 2021-03-31 2021-03-31 Reinforcing cover of Insulation and Manufacturing Method Thereof KR102484541B1 (en)