KR20220099709A - Wood material not using formaldehyde and its manufacturing method - Google Patents

Wood material not using formaldehyde and its manufacturing method Download PDF

Info

Publication number
KR20220099709A
KR20220099709A KR1020210001934A KR20210001934A KR20220099709A KR 20220099709 A KR20220099709 A KR 20220099709A KR 1020210001934 A KR1020210001934 A KR 1020210001934A KR 20210001934 A KR20210001934 A KR 20210001934A KR 20220099709 A KR20220099709 A KR 20220099709A
Authority
KR
South Korea
Prior art keywords
formaldehyde
fiberboard
manufacturing
wood material
adhesive
Prior art date
Application number
KR1020210001934A
Other languages
Korean (ko)
Other versions
KR102473458B1 (en
Inventor
안상열
양지웅
Original Assignee
주식회사 한솔홈데코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 한솔홈데코 filed Critical 주식회사 한솔홈데코
Priority to KR1020210001934A priority Critical patent/KR102473458B1/en
Publication of KR20220099709A publication Critical patent/KR20220099709A/en
Application granted granted Critical
Publication of KR102473458B1 publication Critical patent/KR102473458B1/en

Abstract

The present invention relates to a wood material not using formaldehyde harmful to the human body and a manufacturing method thereof. The manufacturing method of a wood material not using formaldehyde comprises the steps of: applying a formaldehyde-free adhesive to an upper surface of a fiber board or a rear surface of a decorative surface material manufactured without formaldehyde; laminating a decorative finishing material that does not contain formaldehyde on the upper surface of the fiber board; pressing the laminated decorative finishing material with a press; and curing the laminated decorative finishing material. An embodiment of the present invention relates to an eco-friendly product manufactured using only eco-friendly materials without using formaldehyde at all when manufacturing wooden materials used as flooring materials, wall materials, ceiling materials, molding materials, and other interior materials.

Description

폼알데히드를 사용하지 않는 목질재 및 그의 제조 방법 {Wood material not using formaldehyde and its manufacturing method}Wood material not using formaldehyde and its manufacturing method

본 발명은 폼알데히드를 사용하지 않는 목질재 및 그의 제조 방법에 관한 것으로 특히, 바닥재, 벽면재, 천정재, 몰딩재, 기타 인테리어재로 사용되는 목질재 제조시에 폼알데히드를 사용하지 않고 친환경 재료만을 이용하여 제조한 친환경적인 목질재 및 그의 제조 방법에 관한 것이다.The present invention relates to a wood material that does not use formaldehyde and a method for manufacturing the same. In particular, an eco-friendly material that does not use formaldehyde when manufacturing wood materials used for flooring, wall materials, ceiling materials, molding materials, and other interior materials. It relates to an eco-friendly wood material manufactured using only the wood and a method for manufacturing the same.

일반적으로 목질재는 실내용에 주로 사용되며 주거용과 상업용 공간에 사용되는 자재로서 목질재에 적합한 내구성과 제품 안정성, 디자인 성능, 친환경 성능의 기능 및 성능을 가져야만 한다. In general, wood materials are mainly used for indoor use, and as materials used for residential and commercial spaces, they must have the functions and performance of durability, product stability, design performance, and eco-friendly performance suitable for wood materials.

과거부터 현재까지 목질재에 사용되는 접착제는 강도와 물성 강화 그리고 원가적인 절감을 위해 폼알데히드가 포함된 접착제를 사용하여 제조한, 기재와 표면재를 주로 사용하여 폼알데히드 잔존에 따른 친환경적인 측면에서 자유롭지 못하였다. 현재 국내에서 가장 많이 사용하는 목질졔 제품은 합판과 섬유판 표면위에 HPL을 접착한 마루와 섬우판 표면위에 LPL로 접착한 강하마루와 벽면재, 몰딩재, 기타 인테리어재가 대표적인 제품인데 합판, 섬유판, HPL, LPL을 제조하는 공정에서도 폼알데히드가 포함되어 폼알데히드에는 자유롭지 못하고 일부 잔존하는 제품을 사용하여 종래에는 대부분의 바닥재 제조시에 폼알데히드가 사용되었다.Adhesives used for wood materials from the past to the present have mainly used substrates and surface materials manufactured using adhesives containing formaldehyde to strengthen strength and physical properties and to reduce cost, so they are not free from environmental concerns due to the residual formaldehyde. couldn't Currently, the most widely used wood products in Korea are flooring with HPL glued on the surface of plywood and fiberboard, down-grade flooring with LPL glued on the surface of plywood board, wall materials, molding materials, and other interior materials. Plywood, fiberboard, HPL , Formaldehyde is also included in the process of manufacturing LPL, so formaldehyde is not free and some remaining products are used.

특히, 종래의 합판, 섬유판(MDF), PB, OSB, 코르크 또는 이들이 복합된 복합보드와 LPM, HPL의 표면재의 경우 적용 되는 수지와 접착제는 요소-포르말린, 요소-멜라민-포르말린, 페놀-포르말린 등으로 제조되어 대부분의 제품에서 포르말린이 잔존하는 문제가 발생하였다. In particular, in the case of conventional plywood, fiberboard (MDF), PB, OSB, cork, or composite boards and LPM and HPL surface materials, the resins and adhesives applied are urea-formalin, urea-melamine-formalin, phenol-formalin, etc. In most products, there was a problem that formalin remained.

직접 피부와 맞닿은 표면재의 경우 폼알데히드가 잔존하여 접촉이나 흡입을 통해 아토피와 같은 피부질환과 호흡기 장애의 원인이 되기도 하였다.In the case of the surface material in direct contact with the skin, formaldehyde remained, causing skin diseases such as atopy and respiratory disorders through contact or inhalation.

본 발명이 이루고자 하는 기술적 과제는 종래의 폼알데히드 잔존의 문제점을 해결하고자 하는 것으로, 바닥재, 벽면재, 천정재, 몰딩재, 기타 인테리어재로 사용되는 목질재 제조시에 폼알데히드를 사용하지 않고 친환경 재료만을 이용하여 제조한 친환경적인, 목질재 및 그의 제조 방법을 제공하는 것이다. The technical problem to be achieved by the present invention is to solve the problem of residual formaldehyde in the prior art. To provide an eco-friendly, wood material manufactured using only materials and a method for manufacturing the same.

또한, 본 발명이 이루고자 하는 기술적 과제는 종래의 문제점을 해결하고자 하는 것으로, 폼알데히드를 사용하지 않으면서도 접착력을 강화하는, 목질재 및 그의 제조 방법을 제공하는 것이다. In addition, the technical problem to be achieved by the present invention is to solve the problems of the prior art, and to provide a wood material and a method for manufacturing the same, which enhance adhesion without using formaldehyde.

또한, 본 발명이 이루고자 하는 기술적 과제는 종래의 문제점을 해결하고자 하는 것으로, 미끄럼 방지 기능을 강화하는, 목질재 및 그의 제조 방법을 제공하는 것이다. In addition, the technical problem to be achieved by the present invention is to solve the problems of the prior art, to provide a wood material and a method of manufacturing the same, which strengthen the anti-slip function.

이러한 과제를 해결하기 위한 본 발명의 특징에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법은,A method for producing a wood material without using formaldehyde according to a feature of the present invention for solving these problems,

폼알데히드 무첨가 접착제로 판상재를 성형하여 섬유판을 제조하는 단계; manufacturing a fiberboard by molding a plate-like material with a formaldehyde-free adhesive;

섬유판의 양면에 각각 폼알데히드 무첨가 접착제를 도포하는 단계;applying a formaldehyde-free adhesive to both sides of the fiberboard, respectively;

상기 섬유판의 양면에 제1, 제2 치장마감재를 각각 적층하는 단계;laminating first and second decorative finishing materials on both surfaces of the fiberboard, respectively;

상기 적층된 제1, 제2 치장마감재를 프레스로 가압하는 단계;pressing the laminated first and second decorative finishing materials with a press;

상기 적층된 제1, 제2 치장마감재를 각각 양생하는 단계를 포함한다. and curing the stacked first and second decorative finishing materials, respectively.

상기 접착제는 폼알데히드가 포함되지 않은 EVA 계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼을 주제로 하여 이소시아네이트계 경화제를 주제의 수용성 에멀젼의 5~20% 중량 % 혼합하여 제조된다.The adhesive is prepared by mixing an isocyanate-based curing agent with 5 to 20% by weight of the water-soluble emulsion of the main subject, based on a water-soluble emulsion of an EVA-based, PVAc-based, and co-condensation adhesive without formaldehyde.

상기 섬유판은 폼알데히드가 포함되지 않은 접착제로 제조한 PB, OSB, 합판, 베니어, 섬유판, 코르크 중의 적어도 하나를 포함하는 보드이다. The fiberboard is a board including at least one of PB, OSB, plywood, veneer, fiberboard, and cork manufactured with an adhesive that does not contain formaldehyde.

상기 EVA 계열의 수용성 에멀젼은 고형분 45~65 중량%, pH 5.5~8.5, 점도 7,000~30,000 cps의 조건을 가지는 것을 특징으로 한다.The EVA-based water-soluble emulsion is characterized in that it has a solid content of 45 to 65% by weight, a pH of 5.5 to 8.5, and a viscosity of 7,000 to 30,000 cps.

상기 EVA계열과 PVAc계열, 이의 공축합 접착제의 도포량은 50~150 g/m2으로 상기 섬유판에 균일하게 도포되는 것을 특징으로 한다.The EVA-based, PVAc-based, and the co-condensation adhesive are applied in an amount of 50 to 150 g/m 2 uniformly applied to the fiberboard.

상기 접착제의 도포량은 50~200 g/m2 으로 상기 합판에 균일하게 도포되는 것을 특징으로 한다.The application amount of the adhesive is 50 ~ 200 g / m 2 Characterized in that it is uniformly applied to the plywood.

상기 접착제의 도포량은 50~200 g/m2으로 상기 합판, 섬유판, PB, OSB, 이의 복합보드에 균일하게 도포되는 것을 특징으로 한다.The application amount of the adhesive is 50 ~ 200 g / m 2 It is characterized in that it is uniformly applied to the plywood, fiberboard, PB, OSB, and its composite board.

상기 EVA계열과 PVAc계열, 이의 공축합 접착제를 적용한 적층재를 프레스로 가압하는 단계는, 상온에서 7~15kgf/cm2의 압력으로, 20~60분 동안 가압하는 것을 특징으로 한다. The step of pressing the laminate to which the EVA-based and PVAc-based, co-condensed adhesive is applied with a press is characterized in that it is pressed for 20 to 60 minutes at a pressure of 7 to 15 kgf/cm 2 at room temperature.

상기 적층재를 양생하는 단계는 상온에서 60분 이상 양생하는 것을 특징으로 한다. 상기 치장 마감재는 폼알데히드가 포함되지 않은 올레핀시트, PET, ASA, PVC, 코팅지 중의 하나인 것을 특징으로 한다.The step of curing the laminate is characterized in that it is cured at room temperature for 60 minutes or more. The decorative finishing material is characterized in that it is one of the formaldehyde-free olefin sheet, PET, ASA, PVC, and coated paper.

이러한 과제를 해결하기 위한 본 발명의 특징에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법은,A method for producing a wood material without using formaldehyde according to a feature of the present invention for solving these problems,

섬유판을 제조시 폼알데히드 무첨가 접착제로 판상재를 성형하는 단계;Forming a plate-like material with a formaldehyde-free adhesive when manufacturing a fiberboard;

섬유판의 상면에 폼알데히드 무첨가 접착제를 도포하는 단계;applying a formaldehyde-free adhesive to the upper surface of the fiberboard;

상기 섬유판의 상면에 치장 마감재를 적층하는 단계;laminating a decorative finishing material on the upper surface of the fiberboard;

상기 적층된 치장 마감재를 프레스로 가압하는 단계;pressing the laminated decorative finishing material with a press;

상기 적층된 치장 마감재를 양생하는 단계를 포함한다. and curing the laminated decorative finishing material.

이러한 과제를 해결하기 위한 본 발명의 특징에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법은,A method for producing a wood material without using formaldehyde according to a feature of the present invention for solving these problems,

섬유판의 상면에 폼알데히드 무첨가이고, 폴리우레탄 계열의 PUR접착제를 도포하는 단계;Formaldehyde-free, applying a polyurethane-based PUR adhesive on the upper surface of the fiberboard;

상기 섬유판의 상면에 치장 마감재를 적층하는 단계;laminating a decorative finishing material on the upper surface of the fiberboard;

상기 적층된 치장 마감재를 롤러를 통과시키는 단계;passing the laminated decorative finishing material through a roller;

상기 적층된 치장 마감재를 양생하는 단계를 포함한다. and curing the laminated decorative finishing material.

상기 폴리우레탄 계열의 PUR 접착제는 Urethane prepolyne가 70~90%, Acrylic polymer 10~30%, Diphenylmethane 4,4'-diisocyanate가 1~3%의 조건을 가지는 것을 특징으로 한다. The polyurethane-based PUR adhesive is characterized in that 70 to 90% of urethane prepolyne, 10 to 30% of acrylic polymer, and 1 to 3% of diphenylmethane 4,4'-diisocyanate are present.

PUR 접착제를 사용하는 경우, 적층하여 프레스로 가압할 필요 없이 압축롤러만 통과시키면 된다. In the case of using PUR adhesive, it is only necessary to pass through a compression roller without needing to laminate and press with a press.

상기 PUR의 접착제의 도포량은 30~100 g/m2으로 상기 합판, 섬유판, PB, OSB, 코르크 이의 복합보드에 균일하게 도포된다.The application amount of the PUR adhesive is 30-100 g/m 2 and is uniformly applied to the plywood, fiberboard, PB, OSB, and cork composite boards.

이러한 과제를 해결하기 위한 본 발명의 특징에 따른 폼알데히드를 사용하지 않는 목질재는,Wood material that does not use formaldehyde according to the features of the present invention for solving these problems,

상기 방법에 의해 제조된다.prepared by the above method.

본 발명의 실시 예에서는, 바닥재, 벽면재, 천정재, 몰딩재, 기타 인테리어재로 사용되는 목질재 제조시에 폼알데히드를 사용하지 않고 친환경 재료만을 이용하여 제조한 친환경적인, 목질재 및 그의 제조 방법을 제공할 수 있다. In an embodiment of the present invention, eco-friendly wood material manufactured using only eco-friendly materials without using formaldehyde in manufacturing wood materials used as flooring, wall materials, ceiling materials, molding materials, and other interior materials, and manufacturing thereof method can be provided.

또한, 본 발명의 실시 예에서는, 폼알데히드를 사용하지 않으면서도 접착력을 강화하는, 목질재 및 그의 제조 방법을 제공할 수 있다. In addition, in an embodiment of the present invention, it is possible to provide a wood material and a method for manufacturing the same, which enhances adhesion without using formaldehyde.

또한, 본 발명의 실시 예에서는, 미끄럼 방지 기능을 강화하는, 목질재 및 그의 제조 방법을 제공할 수 있다. In addition, in an embodiment of the present invention, it is possible to provide a wood material and a method of manufacturing the same, which enhance the anti-slip function.

도 1은 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법을 나타낸 도면이다.
도 2 내지 도 5는 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법의 각 단계에 따른 목질재의 상태를 나타낸 도면이다.
도 6는 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 미끄럼 수준 측정치를 나타낸 도면이다.(삭제 검토)
도 7은 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재에 적용되는 PUR 접착제의 성분예를 나타낸 도면이다.
도 8 내지 도 11은 본 발명의 제2 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법의 각 단계에 따른 목질재를 나타낸 도면이다.1 is a view showing a method of manufacturing a wood material without using formaldehyde according to a first embodiment of the present invention.
2 to 5 are views showing the state of the wood material according to each step of the method for manufacturing the wood material without using formaldehyde according to the first embodiment of the present invention.
6 is a view showing the measurement value of the sliding level of the wood material without using formaldehyde according to the first embodiment of the present invention. (Review for deletion)
7 is a view showing a component example of a PUR adhesive applied to a wood material that does not use formaldehyde according to the first embodiment of the present invention.
8 to 11 are views showing the wood material according to each step of the method for manufacturing the wood material without using formaldehyde according to the second embodiment of the present invention.

아래에서는 첨부한 도면을 참고로 하여 본 발명의 실시 예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시 예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.Hereinafter, with reference to the accompanying drawings, embodiments of the present invention will be described in detail so that those of ordinary skill in the art to which the present invention pertains can easily implement them. However, the present invention may be embodied in various different forms and is not limited to the embodiments described herein. And in order to clearly explain the present invention in the drawings, parts irrelevant to the description are omitted, and similar reference numerals are attached to similar parts throughout the specification.

명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. Throughout the specification, when a part "includes" a certain component, it means that other components may be further included, rather than excluding other components, unless otherwise stated.

도 1은 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법을 나타낸 도면이다.1 is a view showing a method of manufacturing a wood material without using formaldehyde according to a first embodiment of the present invention.

도 2 내지 도 5는 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법의 각 단계에 따른 목질재를 나타낸 도면이다.2 to 5 are views showing wood material according to each step of the method for manufacturing wood material not using formaldehyde according to the first embodiment of the present invention.

도 6은 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 미끄럼 수준 측정치를 나타낸 도면이다.6 is a view showing the measured slip level of the wood material without using formaldehyde according to the first embodiment of the present invention.

도 7은 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재에 적용되는 PUR 접착제의 성분예를 나타낸 도면이다.7 is a view showing a component example of a PUR adhesive applied to a wood material that does not use formaldehyde according to the first embodiment of the present invention.

도 1 내지 도 5를 참조하면, 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재는,1 to 5, the wood material that does not use formaldehyde according to the first embodiment of the present invention,

섬유판(100),fiberboard (100),

섬유판(100)의 상면에 도포된 접착제층(110),The adhesive layer 110 applied to the upper surface of the fiberboard 100,

상기 섬유판(100)의 상면에 상기 접착제층(110)에 의해 접착된 치장 마감재(210)를 포함한다.A decorative finishing material 210 adhered to the upper surface of the fiberboard 100 by the adhesive layer 110 is included.

상기 접착제(110)는 폼알데히드가 포함되지 않은 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼을 주제로 하여 이소시아네이트계 경화제를 주제의 수용성 에멀젼의 5~20% 중량 % 혼합하여 제조된다.The adhesive 110 is prepared by mixing an isocyanate-based curing agent with 5 to 20% by weight of the water-soluble emulsion of the main subject, based on a water-soluble emulsion of EVA-based, PVAc-based, and co-condensation adhesives thereof that do not contain formaldehyde.

상기 섬유판(100)은 폼알데히드가 포함되지 않은 접착제로 제조한 PB, OSB, 합판, 베니어, 섬유판, 코르크 중의 적어도 하나를 포함하는 보드이다. The fiberboard 100 is a board including at least one of PB, OSB, plywood, veneer, fiberboard, and cork made with an adhesive that does not contain formaldehyde.

상기 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼은 고형분 45~65 중량%, pH 5.5~8.5, 점도 7,000~30,000 cps의 조건을 가지는 것을 특징으로 한다.The water-soluble emulsion of the EVA-based and PVAc-based, co-condensed adhesives thereof is characterized in that it has a solid content of 45 to 65% by weight, a pH of 5.5 to 8.5, and a viscosity of 7,000 to 30,000 cps.

상기 접착제는 폴리우레탄 계열의 PUR을 사용할 수 있다. As the adhesive, polyurethane-based PUR may be used.

상기 폴리우레탄 계열의 PUR 접착제는 Urethane prepolyne가 70~90%, Acrylic polymer 10~30%, Diphenylmethane 4,4'-diisocyanate가 1~3%의 조건을 가지는 것을 특징으로 한다.The polyurethane-based PUR adhesive is characterized in that 70 to 90% of urethane prepolyne, 10 to 30% of acrylic polymer, and 1 to 3% of diphenylmethane 4,4'-diisocyanate are present.

상기 EVA계열과 PVAc계열, 이의 공축합 접착제의 도포량은 50~150 g/m2으로 상기 섬유판(100)에 균일하게 도포되는 것을 특징으로 한다. The EVA-based, PVAc-based, and the co-condensation adhesives are applied in an amount of 50 to 150 g/m 2 , which is uniformly applied to the fiberboard 100 .

상기 접착제(110)의 도포량은 50~200 g/m2 으로 상기 합판에 균일하게 도포되는 것을 특징으로 한다.The application amount of the adhesive 110 is 50 ~ 200 g / m2 It is characterized in that it is uniformly applied to the plywood.

상기 PUR의 접착제의 도포량은 30~100 g/m2으로 상기 합판, 섬유판(100), PB, OSB, 이의 복합보드에 균일하게 도포된다.The amount of the PUR adhesive is applied uniformly to the plywood, the fiberboard 100, PB, OSB, and its composite board at 30-100 g/m2.

상기 접착제의 도포량은 50~200 g/m2으로 상기 합판, 섬유판(100), PB, OSB, 코르크 이의 복합보드에 균일하게 도포되는 것을 특징으로 한다.The application amount of the adhesive is 50 ~ 200 g / m2 It is characterized in that the plywood, fiberboard 100, PB, OSB, and cork are uniformly applied to the composite board.

상기 EVA계열과 PVAc계열, 이의 공축합 접착제를 적용한 적층재를 프레스로 가압하는 단계는, 상온에서 7~15kgf/cm2의 압력으로, 20~60분 동안 가압하는 것을 특징으로 한다. The step of pressing the laminate to which the EVA-based and PVAc-based, co-condensed adhesive is applied with a press is characterized in that it is pressed for 20 to 60 minutes at a pressure of 7 to 15 kgf/cm 2 at room temperature.

상기 PUR 접착제를 적용한 적층재를 프레스로 가압하는 단계는 상온에서 압축롤러를 통과하여 접착하는 것을 특징으로 한다. The step of pressing the laminate to which the PUR adhesive is applied with a press is characterized in that it is adhered through a compression roller at room temperature.

PUR 접착제를 사용하는 경우, 적층하여 프레스로 가압할 필요 없이 압축롤러만 통과시키면 된다. 상기 적층재를 양생하는 단계는 상온에서60분 동안 양생하는 것을 특징으로 한다. 상기 치장 마감재는 폼알데히드가 포함되지 않은 올레핀시트, PET, ASA, PVC, 코팅지 중의 하나인 것을 특징으로 한다.In the case of using PUR adhesive, it is only necessary to pass through a compression roller without needing to laminate and press with a press. The step of curing the laminate is characterized in that it is cured at room temperature for 60 minutes. do. The decorative finishing material is characterized in that it is one of the formaldehyde-free olefin sheet, PET, ASA, PVC, and coated paper.

상기 치장 마감재(210)의 표면은 엠보싱 등 미끄러짐 방지 처리가 되어 있으며, 제조시의 성분이 미그럼 방지 기능을 하고, 도 5에 미끄럼 방지 수준의 측정치를 도시하였다.The surface of the decorative finishing material 210 is subjected to anti-slip treatment such as embossing, and the components during manufacture function as anti-migm, and the measured value of the anti-slip level is shown in FIG. 5 .

도 6을 참조하면, 본 발명의 제1 실시예에 따른 목질재가 미끄럼 방지력이 가장 큰 것으로 나타났다.Referring to FIG. 6 , it was found that the wood material according to the first embodiment of the present invention had the greatest anti-slip force.

도 7을 참조하면, PUR 접착제의 성분 함량은, 우레탄프리폴리머 77~84%, 아크릴릭폴리머 15-20%, 디페닐메텔렌 4.4-디이소시아네이트 1~3%이다. Referring to FIG. 7 , the component content of the PUR adhesive is 77 to 84% of urethane prepolymer, 15-20% of acrylic polymer, and 1-3% of diphenylmethane 4.4-diisocyanate.

이러한 구성을 가진 본 발명의 제1 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법을 설명하면 다음과 같다. A method of manufacturing a wood material without using formaldehyde according to the first embodiment of the present invention having such a configuration will be described as follows.

먼저, 도 2와 같은 섬유판(100)을 준비한다(S110).First, a fiberboard 100 as shown in FIG. 2 is prepared (S110).

여기서, 섬유판(100)은 폼알데히드가 포함되지 않은 접착제로 제조한 PB, OSB, 합판, 베니어, 섬유판, 코르크(100) 중의 적어도 하나를 포함하는 보드이다. Here, the fiberboard 100 is a board including at least one of PB, OSB, plywood, veneer, fiberboard, and cork 100 made with an adhesive that does not contain formaldehyde.

그리고, 도 3과 같이, 섬유판(100)의 상면에 폼알데히드 무첨가 접착제(110)를 도포한다(S120).Then, as shown in FIG. 3 , the formaldehyde-free adhesive 110 is applied to the upper surface of the fiberboard 100 ( S120 ).

상기 접착제는 폼알데히드가 포함되지 않은 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼을 주제로 하여 이소시아네이트계 경화제를 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼의 5~20% 중량 % 혼합하여 제조된다.The adhesive is based on a water-soluble emulsion of EVA-based, PVAc-based, and co-condensed adhesives without formaldehyde, and isocyanate-based curing agents are added to the water-soluble emulsion of EVA-based, PVAc-based, and co-condensed adhesives 5 to 20% by weight It is prepared by mixing.

상기 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼은 고형분 45~65 중량%, pH 5.5~8.5, 점도 7,000~30,000 cps의 조건을 가지는 것을 특징으로 한다.The water-soluble emulsion of the EVA-based and PVAc-based, co-condensed adhesives thereof is characterized in that it has a solid content of 45 to 65% by weight, a pH of 5.5 to 8.5, and a viscosity of 7,000 to 30,000 cps.

상기 접착제는 폴리우레탄 계열의 PUR을 사용할 수 있다. As the adhesive, polyurethane-based PUR may be used.

상기 폴리우레탄 계열의 PUR 접착제는 Urethane prepolyne가 70~90%, Acrylic polymer 10~30%, Diphenylmethane 4,4'-diisocyanate가 1~3%의 조건을 가지는 것을 특징으로 한다.The polyurethane-based PUR adhesive is characterized in that 70 to 90% of urethane prepolyne, 10 to 30% of acrylic polymer, and 1 to 3% of diphenylmethane 4,4'-diisocyanate are present.

상기 EVA계열의 접착제의 도포량은 50~150 g/m2으로 상기 섬유판(100)에 균일하게 도포되는 것을 특징으로 한다. The application amount of the EVA-based adhesive is 50 to 150 g/m 2 , and it is characterized in that it is uniformly applied to the fiberboard 100 .

상기 접착제의 도포량은 50~200 g/m2 으로 상기 합판에 균일하게 도포되는 것을 특징으로 한다.The amount of adhesive applied is 50-200 g/m2 It is characterized in that it is uniformly applied to the plywood.

상기 PUR의 접착제의 도포량은 30~100 g/m2으로 상기 합판, 섬유판(100), PB, OSB, 코르크 이의 복합보드에 균일하게 도포된다.The application amount of the PUR adhesive is 30-100 g/m2, which is uniformly applied to the plywood, fiberboard 100, PB, OSB, and cork composite boards.

상기 접착제의 도포량은 50~200 g/m2으로 상기 합판, 섬유판(100), PB, OSB, 코르크 이의 복합보드에 균일하게 도포되는 것을 특징으로 한다.The application amount of the adhesive is 50 ~ 200 g / m2 It is characterized in that the plywood, fiberboard 100, PB, OSB, and cork are uniformly applied to the composite board.

그리고 나서, 도 4와 같이, 섬유판(100)의 상면에 치장 마감재(210)를 적층한다(S130).Then, as shown in FIG. 4 , a decorative finishing material 210 is laminated on the upper surface of the fiberboard 100 ( S130 ).

다음, 도 5와 같이, 상기 적층된 치장 마감재(210)를 프레스로 가압하여 섬유판(100)과 접착한다(S140).Next, as shown in FIG. 5 , the laminated decorative finishing material 210 is pressed with a press to adhere to the fiberboard 100 ( S140 ).

상기 EVA계열과 PVAc계열, 이의 공축합 접착제를 적용한 적층재를 프레스로 가압할때에는, 상온에서 7~15kgf/cm2의 압력으로, 20~60분 동안 가압한다.When pressing the laminate to which the EVA-based, PVAc-based, and co-condensation adhesives are applied with a press, pressurized at room temperature at a pressure of 7 to 15 kgf/cm 2 for 20 to 60 minutes.

한편, 상기 PUR 접착제를 적용한 적층재를 프레스로 가압하는 경우에는 상온에서 압축롤러를 통과하여 접착하는 것을 특징으로 한다. 즉, PUR 접착제를 사용하는 경우, 적층하여 프레스로 가압할 필요 없이 압축롤러만 통과시키면 된다. On the other hand, when the laminate to which the PUR adhesive is applied is pressed with a press, it is characterized in that it is adhered through a compression roller at room temperature. That is, when using a PUR adhesive, it is only necessary to pass through a compression roller without needing to laminate and press with a press.

다음, 상기 적층된 치장 마감재(210)를 양생한다(S150). Next, the laminated decorative finishing material 210 is cured (S150).

여기서 양생은 상온에서 60분 이상 양생하는 것을 특징으로 한다. 상기 치장 마감재는 폼알데히드가 포함되지 않은 올레핀시트, PET, ASA, PVC, 코팅지 중의 하나이다.Here, curing is characterized by curing at room temperature for more than 60 minutes. do. The decorative finishing material is one of olefin sheets, PET, ASA, PVC, and coated paper that do not contain formaldehyde.

그리고 나서, 양생된 치장 마감재(210)를 원하는 크기로 재단 및 가공한다(S160). Then, the cured decorative finishing material 210 is cut and processed to a desired size (S160).

이러한 본 발명의 제1 실시예는 다양한 변형이 가능하며, 다른 실시예에 대해 설명하면 다음과 같다.Various modifications are possible to the first embodiment of the present invention, and other embodiments will be described as follows.

도 8 내지 도 11은 본 발명의 제2 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법의 각 단계에 따른 목질재를 나타낸 도면이다.8 to 11 are views showing the wood material according to each step of the method for manufacturing the wood material without using formaldehyde according to the second embodiment of the present invention.

도 7 내지 도 10을 참조하면, 본 발명의 제2 실시예에 따른 폼알데히드를 사용하지 않는 목질재의 제조 방법은,7 to 10, the method of manufacturing a wood material without using formaldehyde according to a second embodiment of the present invention,

섬유판(100)의 양면에 각각 폼알데히드 무첨가 접착제(110, 120)를 도포하는 단계;applying formaldehyde-free adhesives 110 and 120 to both sides of the fiberboard 100, respectively;

상기 섬유판(100)의 양면에 제1, 제2 치장마감재(210, 220)를 각각 적층하는 단계;laminating first and second decorative finishing materials 210 and 220 on both surfaces of the fiberboard 100, respectively;

상기 적층된 제1, 제2 치장 마감재(210, 220)를 프레스로 가압하는 단계;pressing the laminated first and second decorative finishing materials (210, 220) with a press;

상기 적층된 제1, 제2 치장 마감재(210, 220)를 각각 양생하는 단계를 포함한다.and curing the stacked first and second decorative finishing materials 210 and 220, respectively.

제1 실시예에서 섬유판(100)의 상부의 단면에 치장 마감재를 접착한 것에 비해, 본 발명의 제2 실시예는 제1 실시예에서 추가로 하부 단면까지 치장 마감재를 접착 또는 코팅한 실시예이다.Compared to the first embodiment in which the decorative finishing material is adhered to the upper end surface of the fiberboard 100, the second embodiment of the present invention is an embodiment in which the decorative finishing material is further adhered or coated up to the lower end surface in the first embodiment. .

본 발명의 실시 예에서는, 바닥재, 벽면재, 천정재, 몰딩재, 기타 인테리어재로 사용되는 목질재 제조시에 폼알데히드를 사용하지 않고 친환경 재료만을 이용하여 제조한 친환경적인 제품이다. In an embodiment of the present invention, it is an eco-friendly product manufactured using only eco-friendly materials without using formaldehyde in manufacturing wood materials used for flooring, wall materials, ceiling materials, molding materials, and other interior materials.

또한, 본 발명의 실시 예에서는, 폼알데히드를 사용하지 않으면서도 접착력을 강화할 수 있다. In addition, in an embodiment of the present invention, it is possible to strengthen the adhesive force without using formaldehyde.

또한, 본 발명의 실시 예에서는, 미끄럼 방지 기능을 강화할 수 있다.In addition, in an embodiment of the present invention, the anti-slip function can be strengthened.

이상에서 본 발명의 실시 예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.Although the embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improved forms of the present invention are also provided by those skilled in the art using the basic concept of the present invention as defined in the following claims. is within the scope of the right.

Claims (11)

폼알데히드가 포함되지 않은 섬유판의 양면 또는 치장표면재의 후면에 각각 폼알데히드 무첨가 접착제를 도포하는 단계;
상기 섬유판의 양면에 폼알데히드가 포함되지 않은 제1, 제2 치장마감재를 각각 적층하는 단계;
상기 적층된 제1, 제2 치장 마감재를 프레스로 가압하는 단계;
상기 적층된 제1, 제2 치장 마감재를 각각 양생하는 단계를 포함하는 목질재의 제조 방법.applying a formaldehyde-free adhesive to both sides of a fiberboard that does not contain formaldehyde or to the back of a decorative surface material, respectively;
laminating first and second decorative finishing materials not containing formaldehyde on both sides of the fiberboard, respectively;
pressing the laminated first and second decorative finishing materials with a press;
A method of manufacturing a wood material comprising the step of curing the laminated first and second decorative finishing materials, respectively. 제1항에 있어서, 상기 접착제는 폼알데히드가 포함되지 않은 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼을 주제로 하여 이소시아네이트계 경화제를 EVA계열과 PVAc계열, 이의 공축합 접착제의 수용성 에멀젼의 5~20% 중량 % 혼합하여 제조되는 목질재의 제조 방법.The method according to claim 1, wherein the adhesive is a water-soluble emulsion of EVA-based, PVAc-based, and co-condensation adhesives containing no formaldehyde, and isocyanate-based curing agents are used as water-soluble emulsions of EVA-based, PVAc-based, and co-condensed adhesives. A method of manufacturing a wood material prepared by mixing 5 to 20% by weight. 제1항에 있어서, 상기 섬유판은 폼알데히드가 포함되지 않은 접착제로 제조한 PB, OSB, 합판, 베니어, 섬유판, 코르크 중의 적어도 하나를 포함하는 보드인 목질재의 제조 방법.
The method of claim 1 , wherein the fiberboard is a board including at least one of PB, OSB, plywood, veneer, fiberboard, and cork made with an adhesive that does not contain formaldehyde.
 제3항에 있어서,
상기 EVA계열과 PVAc계열, 이의 공축합 접착제의 도포량은 50~150 g/m2으로 상기 섬유판에 균일하게 도포되는 것을 특징으로 하는 목질재의 제조 방법.4. The method of claim 3,
The method of manufacturing a wood material, characterized in that the EVA-based, PVAc-based, and the coating amount of the co-condensation adhesive is uniformly applied to the fiberboard in an amount of 50 to 150 g/m 2 . 제4항에 있어서,
상기 EVA계열과 PVAc계열, 이의 공축합 접착제를 적용한 적층재를 프레스로 가압하는 단계는, 상온에서 7~15kgf/cm2의 압력으로, 20~60분 동안 가압하는 것을 특징으로 하는 목질재의 제조 방법.5. The method of claim 4,
The step of pressing the laminate to which the EVA-based and PVAc-based, co-condensed adhesives thereof are applied with a press is a method of manufacturing a wood material, characterized in that pressurized for 20 to 60 minutes at a pressure of 7 to 15 kgf/cm 2 at room temperature. 제5항에 있어서,
상기 적층재를 양생하는 단계는,
상온에서 60분 이상 양생하는 것을 특징으로 하는 목질재의 제조 방법.6. The method of claim 5,
The step of curing the laminate,
A method for producing a wood material, characterized in that it is cured at room temperature for 60 minutes or more. 폼알데히드가 포함되지 않은 섬유판의 상면에 폼알데히드 무첨가 접착제를 도포하는 단계;
상기 섬유판의 상면에 폼알데히드가 포함되지 않은 치장 마감재를 적층하는 단계;
상기 적층된 치장 마감재를 프레스로 가압하는 단계;
상기 적층된 치장 마감재를 양생하는 단계를 포함하느 목질재의 제조 방법.applying a formaldehyde-free adhesive to the upper surface of the formaldehyde-free fiberboard;
laminating a decorative finishing material that does not contain formaldehyde on the upper surface of the fiberboard;
pressing the laminated decorative finishing material with a press;
A method of manufacturing a wood material comprising the step of curing the laminated decorative finishing material. 섬유판의 상면에 폼알데히드 무첨가이고, 폴리우레탄 계열의 PUR접착제를 도포하는 단계;
상기 섬유판의 상면에 폼알데히드가 포함되지 않은 치장 마감재를 적층하는 단계;
상기 적층된 치장 마감재를 롤러를 통과시키는 단계;
상기 적층된 치장 마감재를 양생하는 단계를 포함하는 목질재의 제조 방법.Formaldehyde-free, applying a polyurethane-based PUR adhesive on the upper surface of the fiberboard;
laminating a decorative finishing material that does not contain formaldehyde on the upper surface of the fiberboard;
passing the laminated decorative finishing material through a roller;
A method of manufacturing a wood material comprising the step of curing the laminated decorative finishing material. 제8항에 있어서,
상기 폴리우레탄 계열의 PUR 접착제는 Urethane prepolyne가 70~90%, Acrylic polymer 10~30%, Diphenylmethane 4,4'-diisocyanate가 1~3%의 조건을 가지는 것을 특징으로 하는 목질재의 제조 방법.9. The method of claim 8,
The polyurethane-based PUR adhesive is a method of manufacturing wood material, characterized in that urethane prepolyne is 70 to 90%, acrylic polymer 10 to 30%, and diphenylmethane 4,4'-diisocyanate is 1 to 3%. 제9항에 있어서,
상기 PUR의 접착제의 도포량은 30~100 g/m2으로 상기 합판, 섬유판, PB, OSB,코르크 이의 복합보드에 균일하게 도포되는 목질재의 제조 방법.10. The method of claim 9,
The application amount of the PUR adhesive is 30-100 g/m 2 A method of manufacturing a wood material that is uniformly applied to the composite board of the plywood, fiberboard, PB, OSB, and cork. 제1항 내지 제10항중 어느 한 항의 제조 방법으로 제조되는 목질재.
A wood material manufactured by the manufacturing method of any one of claims 1 to 10.
KR1020210001934A 2021-01-07 2021-01-07 Wood material not using formaldehyde and its manufacturing method KR102473458B1 (en)