KR20210031073A - Optical film having decoration function and image display device comprising the same - Google Patents
Optical film having decoration function and image display device comprising the same Download PDFInfo
- Publication number
- KR20210031073A KR20210031073A KR1020190112565A KR20190112565A KR20210031073A KR 20210031073 A KR20210031073 A KR 20210031073A KR 1020190112565 A KR1020190112565 A KR 1020190112565A KR 20190112565 A KR20190112565 A KR 20190112565A KR 20210031073 A KR20210031073 A KR 20210031073A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- decoration
- polarizing film
- optical film
- hard coating
- Prior art date
Abstract
Description
본 발명은 편광필름층의 비표시 영역인 베젤부에 데코레이션층을 형성하여, 화상표시장치의 박막화에 기여할 수 있고, 용이한 제조방법으로 화상표시장치의 내부 배선이나 금속전극 등을 가리는 것은 물론, 데코레이션 기능을 갖는 광학필름 및 이를 포함하는 화상표시장치에 관한 것이다.In the present invention, by forming a decoration layer on the bezel part of the non-display area of the polarizing film layer, it can contribute to thinning of the image display device, and cover internal wiring or metal electrodes of the image display device with an easy manufacturing method, as well as It relates to an optical film having a decoration function and an image display device including the same.
최근, 화상 이미지를 포함하는 정보를 표시할 수 있는 표시장치가 활발히 개발되고 있다. 상기 화상표시장치는 액정표시(liquid crystal display: LCD) 장치, 유기발광표시(organic light emitting display: OLED) 장치, 플라즈마표시(plasma display panel: PDP) 장치 및 전계방출표시(field emission display: FED) device) 장치 등을 포함한다. 이러한 화상표시장치에 있어서, 예를 들면 LCD 패널 및 OLED 패널과 같은 표시패널 상부에 외부 환경으로부터 상기 표시패널을 보호하기 위한 윈도우 기판이 배치될 수 있다. 상기 윈도우 기판은 글래스 재질의 베이스 기판을 포함할 수 있으며, 최근 플렉시블 디스플레이가 개발되면서, 상기 베이스 기판으로서 투명 플라스틱 재질도 활용되고 있다. 이러한 베이스 기판에는 내면에 외부에서 내부의 배선이나 금속전극 등이 보이지 않도록 하기 위하여 실제 화상이 표시되는 화상표시영역 외의 비표시 영역에 베젤부가 마련되었다. Recently, display devices capable of displaying information including image images have been actively developed. The image display device includes a liquid crystal display (LCD) device, an organic light emitting display (OLED) device, a plasma display panel (PDP) device, and a field emission display (FED). device) devices, etc. In such an image display device, for example, a window substrate for protecting the display panel from an external environment may be disposed on a display panel such as an LCD panel and an OLED panel. The window substrate may include a base substrate made of a glass material, and with the recent development of flexible displays, a transparent plastic material is also used as the base substrate. In such a base substrate, a bezel part is provided in a non-display area other than the image display area where an actual image is displayed in order to prevent internal wiring or metal electrodes from being seen from the outside.
종래의 기술에 따르면, 상기 비표시 영역인 베젤부 및 상기 베이스 기판의 내면에 필름이나 실크스크린 인쇄기법을 이용하여 블랙칼라층을 코팅함으로써 상기 내부 배선이나 금속전극 등을 가리는 소기의 목적을 달성하였다. According to the prior art, a desired purpose of covering the internal wiring or metal electrodes has been achieved by coating a black color layer on the bezel portion, which is the non-display area, and the inner surface of the base substrate using a film or silk screen printing technique. .
그러나 베이스 기판의 테두리 부분이 곡면과 같은 3D 형상을 갖는 경우 또는 베이스 기판이 플렉시블한 투명 플라스틱 재질인 경우에는 상기와 같이 베이스 기판의 내면에 블랙칼라층을 직접 코팅하는 것은 그 공정이 매우 어렵고 복잡한 문제점이 있었다. However, when the rim of the base substrate has a 3D shape such as a curved surface or the base substrate is made of a flexible transparent plastic material, it is very difficult and complicated to coat the black color layer directly on the inner surface of the base substrate as described above. There was this.
또한, 상기 베이스 기판 및 상기 표시 패널 사이에는 편광판, 터치 스크린 패널과 같은 표시장치의 추가 부재들이 배치될 수 있다. 상기 편광판에 의해 예를 들면, 상기 표시패널의 전극 패턴으로부터 반사된 외광이 차단될 수 있다. 또한, 상기 터치 스크린 패널에 의해 사용자의 명령을 화면을 통해 입력할 수 있다.Further, additional members of a display device such as a polarizing plate and a touch screen panel may be disposed between the base substrate and the display panel. External light reflected from, for example, an electrode pattern of the display panel may be blocked by the polarizing plate. In addition, a user's command may be input through the screen by the touch screen panel.
그러나 상기 베이스 기판의 내면에 필름이나 실크스크린 인쇄기법을 이용하여 블랙칼라층을 코팅하는 경우, 그 두께가 수십 μm로 두껍기 때문에 이후 복수의 층들 또는 구조물들이 적층됨에 따라, 플렉시블 특성 향상, 박막화와 같은 최근의 화상표시장치에서의 요구 사항들이 충분히 구현되기 어려운 한계가 존재하였다. 특히, 상기한 복수의 층들 또는 구조물들을 상기 두꺼운 블랙칼라층이 코팅된 베이스 기판에 부착하기 위하여 점착층을 사용하는 경우, 상기 점착층의 두께도 두꺼워져 상기한 문제점들을 더욱 악화시키는 문제점이 있었다.However, when the black color layer is coated on the inner surface of the base substrate by using a film or silkscreen printing technique, the thickness is several tens of μm. There is a limit in which it is difficult to sufficiently implement the requirements in recent image display devices. In particular, when the adhesive layer is used to attach the plurality of layers or structures to the base substrate coated with the thick black color layer, the thickness of the adhesive layer is also increased, which further exacerbates the above problems.
또한, 상기한 종래 기술의 경우 물리적, 기계적 또는 화학적 불량이 야기될 수 있으며, 공정 비용이 상승할 수 있는 문제점이 있었다.In addition, in the case of the prior art described above, there is a problem in that physical, mechanical or chemical defects may be caused, and the process cost may increase.
한편, 화상표시장치의 심미성 향상을 위하여, 상기 비표시 영역인 베젤부에 다양한 개성을 가진 현대인들의 기호에 맞도록 색상, 광택, 그리고 문양(즉, 패턴) 등이 다양하게 표현될 수 있도록 요구되고 있는 실정이다.On the other hand, in order to improve the aesthetics of the image display device, it is required to be able to express various colors, gloss, and patterns (i.e., patterns) in the bezel part, which is the non-display area, to suit the taste of modern people with various personalities There is a situation.
본 발명의 일 구현예는 상기한 기존 발명의 문제점을 해결하기 위한 것으로, 화상표시장치의 박막화에 기여할 수 있고, 용이한 제조방법으로 화상표시장치의 내부 배선이나 금속전극 등을 가리는 것은 물론, 현대인들의 기호에 맞도록 색상, 광택, 그리고 문양(즉, 패턴) 등이 다양하게 표현될 수 있는 데코레이션 기능을 갖는 광학필름을 제공하고자 하는 것이다. One embodiment of the present invention is to solve the problems of the existing invention described above, can contribute to the thinning of the image display device, and cover the internal wiring or metal electrode of the image display device with an easy manufacturing method, as well as modern people It is intended to provide an optical film with a decoration function that can express various colors, gloss, and patterns (that is, patterns) to suit their preferences.
또한, 본 발명의 다른 일 구현예는 상기 광학필름을 포함하는 화상표시장치를 제공하고자 하는 것이다. In addition, another embodiment of the present invention is to provide an image display device including the optical film.
본 발명의 일 구현예는 표시 영역(101) 및 비표시 영역(102)을 포함하는 광학필름(100)에 있어서, 상기 광학필름(100)은 베이스 기판(1); 상기 베이스 기판(1)의 하부면에 형성되는 제1 점착층(2); 상기 제1 점착층(2)의 하부면에 형성되는 편광필름층(3) 및 상기 편광필름층(3)의 하부면에 형성되는 제2 점착층(4)을 포함하는 것이고, 상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에는 비표시 영역을 따라 형성되는 데코레이션층(5)을 포함하는 것인 데코레이션 기능을 갖는 광학필름을 제공한다.According to an embodiment of the present invention, in an
상기 편광필름층(3)은, 입사되는 빛 중에서 일정 방향으로 편광된 빛을 투과시키는 편광소자층(301), 상기 편광소자층(301)의 상부면에 형성되는 상부면 보호/지지층(302)을 포함하는 것이고, 상기 편광필름층(3)과 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 상부면 보호/지지층(302)의 표면에는 하드코팅층(310)을 형성하는 것이고, 상기 형성되는 하드코팅층(310)의 표면에는 MDD(Micro Dry process Decoration) 열전사 공정에 의하여, 0.1 내지 10 μm 두께의 데코레이션층(5)이 형성되는 것일 수 있다.The polarizing
또한, 상기 편광필름층(3)은, 입사되는 빛 중에서 일정 방향으로 편광된 빛을 투과시키는 편광소자층(301), 상기 편광소자층(301)의 하부면에 형성되는 하부면 보호/지지층(303)을 포함하는 것이고, 상기 편광필름층(3)과 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 하부면 보호/지지층(302)의 표면에는 하드코팅층(320)을 형성하는 것이고, 상기 형성되는 하드코팅층(320)의 표면에는 MDD(Micro Dry process Decoration) 열전사 공정에 의하여, 0.1 내지 10 μm 두께의 데코레이션층(5)이 형성되는 것일 수 있다.In addition, the polarizing
또한, 상기 편광필름층(3)은 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에 하드코팅층(310, 320)을 포함하는 것이고, 상기 하드코팅층(310, 320)은 아크릴레이트계 자외선 경화성 수지 5 내지 20 중량%, 퍼플루오로 폴리에테르를 함유하는 화합물에 다관능 아크릴레이트가 반응되어 형성되는 불소 변성 다관능 아크릴레이트 화합물 0.1 내지 5 중량%, 광중합 개시제 1 내지 10 중량%, 헥사플루오로이소프로판올(Hexafluoroisopropanol, HFP) 30 내지 50 중량%, 및 잔량의 극성 용매를 포함하는 자외선 경화형 하드코팅용 조성물을 사용하여 형성되는 것일 수 있다.In addition, the polarizing
상기 데코레이션층(5)은 색상 또는 모양 중 어느 하나 이상을 표현하는 컬러틴트층(501); 패턴층(502); 투과율 또는 반사율을 조절하는 기능을 수행하는 증착물질을 증착한 증착층(503); 및 차폐인쇄층(504)을 포함하는 것일 수 있다.The
상기 베이스 기판(1)은 평면 형태인 것일 수 있다.The
또한, 상기 베이스 기판(1)은 중앙은 평면 형태인 것이고, 양측은 곡면 형태인 것일 수 있다.In addition, the
본 발명의 다른 일 구현예는 상기 본 발명의 일 구현예에 따른 광학필름을 포함하는 것인 화상표시장치를 제공한다.Another embodiment of the present invention provides an image display device including the optical film according to the embodiment of the present invention.
본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름 및 이를 포함하는 화상표시장치는 베이스 기판의 형상 또는 재질에 구애받지 않도록, 편광필름층의 비표시 영역인 베젤부에 데코레이션층을 형성함으로써, 용이한 제조방법으로 화상표시장치의 내부 배선이나 금속전극 등을 가리는 것은 물론, 현대인들의 기호에 맞도록 색상, 광택, 그리고 문양(즉, 패턴) 등이 다양하게 표현될 수 있는 효과가 있다.In an optical film having a decoration function and an image display device including the same according to an embodiment of the present invention, a decoration layer is formed on the bezel part of the non-display area of the polarizing film layer so as not to be restricted by the shape or material of the base substrate, In addition to covering internal wiring or metal electrodes of an image display device with an easy manufacturing method, colors, gloss, and patterns (ie, patterns) can be expressed in various ways to suit the tastes of modern people.
또한, 상기 데코레이션층은 MDD 열전사 공정에 의하여 형성될 수 있어, 그 두께가 매우 얇아, 이후 인접하여, 적층되는 점착층의 두께를 줄일 수 있는 효과가 있다. 이로써, 화상표시장치의 박막화에 기여할 수 있는 효과가 있다. 뿐만 아니라, 물리적, 기계적 또는 화학적 불량을 획기적으로 줄일 수 있는 효과가 있다.In addition, since the decoration layer may be formed by the MDD thermal transfer process, its thickness is very thin, and there is an effect of reducing the thickness of the adhesive layer that is adjacent to and laminated thereafter. Thereby, there is an effect that can contribute to thinning of the image display device. In addition, there is an effect of remarkably reducing physical, mechanical, or chemical defects.
또한, 이러한 광학필름은 표시패널의 전극 패턴으로부터 반사된 외광이 차단될 수 있는 우수한 편광 효과 뿐만 아니라, 화상표시장치를 외부의 충격으로부터 보호할 수 있는 효과가 있다. In addition, such an optical film has an excellent polarization effect in which external light reflected from the electrode pattern of the display panel can be blocked, as well as an effect of protecting the image display device from external impact.
도 1은 본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름의 개략적인 정면도, 단면도 및 분해사시도를 나타낸 이미지이다.
도 2는 본 발명의 다른 일 구현예에 따른 데코레이션 기능을 갖는 광학필름의 개략적인 단면도 및 분해사시도를 나타낸 이미지이다.
도 3은 중앙은 평면 형태인 것이고, 양측은 곡면 형태인 베이스 기판을 갖는 본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름의 개략적인 단면도를 나타낸 이미지이다.
도 4 및 도 5는 본 발명의 일 구현예에 따른 비표시 영역에 형성되는 데코레이션층을 포함하는 편광필름층의 단면도를 나타낸 이미지이다.
도 6 및 도 7은 본 발명의 일 구현예에 따른 MDD 열전사 공정을 위한 인쇄장치의 구성의 사시도를 나타낸 이미지이다.
도 8은 본 발명의 일 구현예에 따른 데코레이션층의 단면도를 나타낸 이미지이다.1 is an image showing a schematic front view, a cross-sectional view, and an exploded perspective view of an optical film having a decoration function according to an embodiment of the present invention.
2 is an image showing a schematic cross-sectional view and an exploded perspective view of an optical film having a decoration function according to another embodiment of the present invention.
3 is an image showing a schematic cross-sectional view of an optical film having a decoration function according to an embodiment of the present invention having a base substrate having a center shape and a curved shape at both sides.
4 and 5 are images showing a cross-sectional view of a polarizing film layer including a decoration layer formed in a non-display area according to an exemplary embodiment of the present invention.
6 and 7 are images showing a perspective view of the configuration of a printing apparatus for the MDD thermal transfer process according to an embodiment of the present invention.
8 is an image showing a cross-sectional view of a decoration layer according to an embodiment of the present invention.
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구범위의 범주에 의해 정의될 뿐이다.Hereinafter, embodiments of the present invention will be described in detail. However, this is presented as an example, and the present invention is not limited thereby, and the present invention is only defined by the scope of the claims to be described later.
본 발명의 일 구현예는 표시 영역(101) 및 비표시 영역(102)을 포함하는 광학필름(100)에 있어서, 상기 광학필름(100)은 베이스 기판(1); 상기 베이스 기판(1)의 하부면에 형성되는 제1 점착층(2); 상기 제1 점착층(2)의 하부면에 형성되는 편광필름층(3) 및 상기 편광필름층(3)의 하부면에 형성되는 제2 점착층(4)을 포함하는 것이고, 상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에는 비표시 영역을 따라 형성되는 데코레이션층(5)을 포함하는 것인 데코레이션 기능을 갖는 광학필름을 제공한다.According to an embodiment of the present invention, in an
이러한 본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름의 개략적인 정면도, 단면도 및 분해사시도를 도 1 및 도 2에 도시하였다. 보다 구체적으로 상기 데코레이션층(5)은 상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에, 비표시 영역을 따르는 형상에 따라 형성될 수 있다. A schematic front view, a cross-sectional view, and an exploded perspective view of an optical film having a decoration function according to an embodiment of the present invention are shown in FIGS. 1 and 2. More specifically, the
화상표시장치의 플렉시블화 및 박형화를 위하여, 최근에는 베이스 기판의 형태 및 재질을 다양하게 변경하고 있는 실정이다. 이에 종래의 기술에 따라, 베이스 기판에 데코레이션층을 형성하는 경우, 공정의 난이도가 상승하고, 불량이 발생하는 등 여러 문제점이 발생하였다.In order to make the image display device more flexible and thin, recently, the shape and material of the base substrate are variously changed. Accordingly, according to the prior art, when the decoration layer is formed on the base substrate, the difficulty of the process increases, and various problems such as defects occur.
그러나 편광필름층은 우수한 경도를 갖는 등 물리적, 광학적으로 매우 안정한 성질을 갖기 때문에, 데코레이션층을 매우 안정적으로 형성시킬 수 있다는 것을 발견하였다. 즉, 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에 데코레이션층(5)을 형성한 후, 베이스 기판과 제1 점착층(2)에 의해서 합착하는 용이한 제조방법으로 광학필름(100)을 제조할 수 있기 때문에, 베이스 기판의 형상 또는 재질에 구애받지 않고, 데코레이션층(5)을 용이하게 형성할 수 있는 효과가 있는 것이다. 이러한 데코레이션층(5)은 화상표시장치의 내부 배선이나 금속전극 등을 가리는 것은 물론, 현대인들의 기호에 맞도록 색상, 광택, 그리고 문양(즉, 패턴) 등을 다양하게 표현할 수 있는 효과가 있다.However, since the polarizing film layer has very stable properties physically and optically, such as having excellent hardness, it has been found that the decoration layer can be formed very stably. That is, after forming the
따라서 본 발명의 일구현예에 따른 베이스 기판은 형상 또는 재질을 자유롭게 선택하여 사용할 수 있는 효과가 있는 것이다. Therefore, the base substrate according to an embodiment of the present invention has an effect of being able to freely select and use a shape or material.
상기 베이스 기판(1)은 도 1 및 도 2에 도시된 바와 같이, 평면 형태인 것일 수 있다.The
또한, 상기 베이스 기판(1)은 도 3에 도시된 바와 같이, 중앙은 평면 형태인 것이고, 양측은 곡면 형태인 것일 수 있다.In addition, as shown in FIG. 3, the
또한, 이러한 상기 베이스 기판(1)은 예를 들어 투명 필름 또는 유리 기판일 수 있다. 이때, 상기 투명 필름은 투명성이 있는 플라스틱 필름이면 어떤 것이라도 사용 가능하다. 예를 들면, 트리아세틸셀룰로오스, 아세틸 셀룰로오스부틸레이트, 에틸렌-아세트산비닐 공중합체, 프로피오닐 셀룰오로스, 부티릴 셀룰로오스, 아세틸 프로피오닐 셀룰로오스, 폴리에스테르, 폴리스티렌, 폴리아미드, 폴리에테르이미드, 폴리아크릴, 폴리이미드, 폴리에테르술폰, 폴리술폰, 폴리에틸렌, 폴리프로필렌, 폴리메틸펜텐, 폴리염화비닐, 폴리염화비닐리덴, 폴리비닐알콜, 폴리비닐아세탈, 폴리에테르케톤, 폴리에테르에테르케톤, 폴리에테르술폰, 폴리메틸메타아크릴레이트, 폴리에틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트, 폴리에틸렌나프탈레이트, 폴리카보네이트 등의 고분자로 형성된 필름일 수 있다. 이들 고분자는 단독 또는 2종 이상 혼합하여 사용할 수 있다.In addition, the
또한, 제1 점착층(2)은 상기 베이스 기판(1)과 편광필름층(3)의 용이한 부착을 위하여 사용되는 것이다. 또한, 제2 점착층(4)은 상기 편광필름층(3)과 화상표시장치와의 용이한 부착을 위하여 또는 상기 편광필름층(3)과, 터치 스크린 패널과 같은 표시장치의 추가 부재와의 용이한 부착을 위하여 사용되는 것이다. 이로써 본 발명의 일 구형예에 따른 광학필름은 표시패널의 전극 패턴으로부터 반사된 외광이 차단될 수 있는 우수한 편광 효과 뿐만 아니라, 화상표시장치를 외부의 충격으로부터 보호할 수 있는 효과를 갖게되는 것이다.In addition, the first
상기 제1 점착층(2) 및 제2 점착층(4)은 서로 같거나 다른 것으로, 당해 기술분야에 공지된 광학 적층체용 점착제 조성물로 이루어질 수 있다. 보다 구체적으로, 오씨에이(OCA:Optical Clear Adhesive) 또는 접착 수지로 형성되는 것이 바람직하다. 이러한 제1 점착층(2) 및 제2 점착층(4)은 피착체 상에 도포하거나, 상기 광학 적층체용 점착제 조성물로부터 제조된 점착 시트를 부착하여 점착층을 형성할 수 있다. 상기 도포 방법은 당해 분야에서 통상적으로 사용되는 방법이라면 특별히 한정되지 않으며, 예를 들면 메이어바 코팅법, 그라비아 코팅법, 다이 코팅법, 침지 코팅법, 분무법 등에 의해 도포하는 방법을 들 수 있다. The first
또한, 상기 제1 점착층(2) 및 제2 점착층(4)의 두께는 서로 같거나 다를 수 있는 것으로, 그 두께를 특별히 한정하지 않는다. 예를 들면, 5 내지 100 μm일 수 있다. 보다 바람직하기로는 10 내지 50 μm일 수 있다. 이는 본 발명의 일 구현예에 따른 데코레이션층의 두께가 매우 얇아, 이후 인접하여, 적층되는 점착층의 두께를 줄일 수 있게 된 것이다.In addition, the thicknesses of the first
또한, 상기 점착층의 점착력은 피착체에 대해 5 N/25㎜ 이상, 예를 들어 5 내지 40 N/25㎜인 것을 사용하여, 접착력 개선 뿐만 아니라, 화상표시장치를 외부의 충격으로부터 보호할 수 있는 효과를 더욱 개선할 수 있다.In addition, the adhesive strength of the adhesive layer is 5 N/25 mm or more with respect to the adherend, for example, 5 to 40 N/25 mm, so that not only the adhesion strength but also the image display device can be protected from external impact. The effect that there is can be improved further.
상기 편광필름층(3)은, 입사되는 빛 중에서 일정 방향으로 편광된 빛을 투과시키는 편광소자층(301), 상기 편광소자층(301)의 상부면에 형성되는 상부면 보호/지지층(302)을 포함하는 것이고, 상기 편광필름층(3)과 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 상부면 보호/지지층(302)의 표면에는 하드코팅층(310)을 형성하는 것이고, 상기 형성되는 하드코팅층(310)의 표면에는 MDD(Micro Dry process Decoration) 열전사 공정에 의하여, 0.1 내지 10 μm 두께의 데코레이션층(5)이 형성되는 것일 수 있다. 이러한 본 발명의 일 구현예에 따른 데코레이션층을 포함하는 편광필름층의 단면도를 나타낸 이미지를 도 4에 도시하였다. The
또한, 상기 편광필름층(3)은, 입사되는 빛 중에서 일정 방향으로 편광된 빛을 투과시키는 편광소자층(301), 상기 편광소자층(301)의 하부면에 형성되는 하부면 보호/지지층(303)을 포함하는 것이고, 상기 편광필름층(3)과 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 하부면 보호/지지층(302)의 표면에는 하드코팅층(320)을 형성하는 것이고, 상기 형성되는 하드코팅층(320)의 표면에는 MDD(Micro Dry process Decoration) 열전사 공정에 의하여, 0.1 내지 10 μm 두께의 데코레이션층(5)이 형성되는 것일 수 있다. 이러한 본 발명의 일 구현예에 따른 데코레이션층을 포함하는 편광필름층의 단면도를 나타낸 이미지를 도 5에 도시하였다. In addition, the
상기 데코레이션층은 장식적인 요소를 제공하고, 하부 구조, 예를 들어 터치센서의 전극 배선 등이 시인되는 것을 방지하는 층으로서, 베젤, 로고, 아이콘, 카메라창, 적외선창 등을 포함할 수 있다. The decoration layer is a layer that provides a decorative element and prevents a lower structure, for example, electrode wiring of a touch sensor from being visually recognized, and may include a bezel, a logo, an icon, a camera window, an infrared window, and the like.
이러한 상기 데코레이션층은 MDD 열전사 공정에 의하여, 편광필름층(3) 상에 매우 용이한 방법으로 형성될 수 있는 효과가 있다. 뿐만 아니라, 상기 데코레이션층은 MDD 열전사 공정에 의하여, 형성되는 두께가 매우 얇아져, 이후 인접하여, 적층되는 점착층의 두께를 줄일 수 있어, 화상표시장치의 박막화에 기여할 수 있는 효과가 있다. 뿐만 아니라, 물리적, 기계적 또는 화학적 불량을 획기적으로 줄일 수 있는 효과가 있다.This decoration layer has an effect that can be formed in a very easy way on the
보다 구체적으로 상기 데코레이션층(5)의 형성은 편광필름층(3)을 준비하는 단계; 0.1 내지 15 μm 두께의 데코레이션층(5)을 포함하는 MDD 열전사용 리본을 제조하는 단계; 상기 준비된 편광필름층(3) 상에, 상기 제조된 MDD 열전사용 리본을 위치시키고, 상기 편광필름층(3)의 비표시 영역과 상기 MDD 열전사용 리본의 데코레이션층(5)이 마주보도록 위치시키는 단계; 및 MDD 열전사 공정을 수행하여, 상기 편광필름층(3) 상에, 그리고 비표시 영역에 상기 데코레이션층(5)을 용융접합시킴으로써, 0.1 내지 10 μm 두께의 데코레이션층(5)을 형성하는 단계를 포함하는 제조방법에 의하여 제조될 수 있다.More specifically, the formation of the
이러한 본 발명의 일 구현예에 따른 MDD 열전사 공정을 위한 인쇄장치의 구성의 사시도를 도 6 및 도 7에 도시하였다. 보다 구체적으로 상기 MDD 열전사 공정을 위한 인쇄장치는 열전사헤드(10), MDD 열전사리본(11), 플라텐롤러(12) 및 이송부(13)를 포함하여 구성된다. 상기 이송부(13)는 모터(14), 구동롤러(15), 종동롤러(16) 및 필름센서(17)를 포함할 수 있다. 6 and 7 are perspective views of the configuration of a printing apparatus for the MDD thermal transfer process according to an embodiment of the present invention. More specifically, the printing apparatus for the MDD thermal transfer process includes a
상기 열전사헤드(10)는 상기 이송부(13)에 의해 이송되는 편광필름층을 포함하는 필름 및 MDD 열전사리본(11)에 열을 가한다. 상기 플라텐롤러(12)는 상기 편광필름층을 포함하는 필름 및 제조된 MDD 열전사용 리본을 사이에 두고 각각 상기 열전사헤드(10)와 대면되어 MDD 열전사용 리본으로부터 데코레이션층이 편광필름층 상에 흡착될 수 있도록 편광필름층을 포함하는 필름을 지지하며, 상기 편광필름층을 포함하는 필름의 이송에 따라 회전한다.The
상기 모터(14)는 인쇄될 편광필름층을 포함하는 필름을 열전사헤드(10)로 공급하기 위한 구동원이고, 상기 구동롤러(15)는 패턴 입력 장치(미도시)에 의해 기설정된 패턴의 모양을 따라 상기 모터(14)와 맞물려 회전하면서 편광필름층을 포함하는 필름을 이송시킨다. 상기 종동롤러(16)는 편광필름층을 포함하는 필름을 사이에 두고 상기 구동롤러(15)와 맞물려 회전되면서 편광필름층을 포함하는 필름을 이송시킨다. 이때, 상기 필름센서(17)가 편광필름층을 포함하는 필름 상에서 입력된 패턴 모양을 따라 위치를 감지한다. 이에, 상기 데코레이션층은 기설정된 패턴부에만 열 및 압력이 가해짐에 따라 상기 편광필름층 상에 형성될 수 있다. 이로써, 열전사가 완료된 필름은 권취롤(18)에 권취될 수 있다.The
또한, 이러한 MDD 열전사 공정은 도 7에 도시된 바와 같이 다수의 열전사헤드(10) 및 MDD 열전사리본(11)을 통과하는 공정을 통하여, 다층구조를 갖는 데코레이션층을 편광필름층 상에 형성할 수 있다.In addition, the MDD thermal transfer process includes a multi-layered decoration layer on the polarizing film layer through a process of passing through a plurality of thermal transfer heads 10 and MDD
이때, 상기 MDD 열전사 공정은 200 내지 210 V의 전압이 90 내지 105의 초당 펄스수(pps)로 인가되는 열전사 헤드를 사용하여, 150 내지 300 kgf/mm2 범위의 압력 및 80 내지 105 ℃의 온도에서 0.1 내지 2.0 inch/sec의 속도로 수행하여, 반응 안정성이 떨어져 단면이 울퉁불퉁한 필름이 제조되거나, 상기 편광필름층과 데코레이션층 사이의 결합력이 약화되는 문제점을 해결할 수 있다.At this time, the MDD thermal transfer process uses a thermal transfer head in which a voltage of 200 to 210 V is applied at a pulse rate per second (pps) of 90 to 105, and a pressure in the range of 150 to 300 kgf/mm 2 and a pressure of 80 to 105° C. By performing at a rate of 0.1 to 2.0 inch/sec at a temperature of, it is possible to solve a problem in that a film having an uneven cross section due to poor reaction stability is produced, or a bonding force between the polarizing film layer and the decoration layer is weakened.
또한, 상기 편광필름층(3)은 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에 하드코팅층(310, 320)을 포함하는 것이 바람직하다. 이로써, 도 4 및 도 5에 도시된 바와 같이, 상기 데코레이션층은 편광필름층(3)의 하드코팅층 상에 형성되는 것이 바람직하다. 상기 하드코팅층은 데코레이션층(5)이 MDD 열전사에 의하여 불량없이 편광필름층(3)의 표면에 용이하게 형성될 수 있도록 경도 및 부착력을 향상시키는 역할을 한다. 이러한 하드코팅층은 연필경도 7H 이상인 것이 바람직하다.In addition, the
보다 구체적으로, 상기 하드코팅층(310, 320)은 아크릴레이트계 자외선 경화성 수지 5 내지 20 중량%, 퍼플루오로 폴리에테르를 함유하는 화합물에 다관능 아크릴레이트가 반응되어 형성되는 불소 변성 다관능 아크릴레이트 화합물 0.1 내지 5 중량%, 광중합 개시제 1 내지 10 중량%, 헥사플루오로이소프로판올(Hexafluoroisopropanol, HFP) 30 내지 50 중량%, 및 잔량의 극성 용매를 포함하는 자외선 경화형 하드코팅용 조성물을 사용하여 제조됨으로써 상기한 효과를 더욱 개선할 수 있다.More specifically, the hard coating layers 310 and 320 are fluorine-modified polyfunctional acrylates formed by reacting a polyfunctional acrylate with a compound containing 5 to 20% by weight of an acrylate-based ultraviolet curable resin and a perfluoropolyether. Compound 0.1 to 5% by weight,
상기 아크릴레이트계 자외선 경화성 수지는 당분야에서 일반적으로 사용되는 아크릴레이트계 자외선 경화성 수지라면 그 종류를 특별히 제한하지 않는다. 보다 구체적인 예를 들면, 2-(페플루오로데실)에틸 메타크릴레이트, 3-퍼플루오로옥틸-2-하이드록시 프로필 아크릴레이트, 3-(퍼플루오로-9-메틸데실)-1, 2-에폭시프로판, (메타)아크릴산-2,2,2-트리플루오르에틸, (메타)아크릴산-2,2,2-트리 플루오르메틸, 3,3,3,-트리플루오르 프로필 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상을 사용할 수 있다. 또한, 상기 아크릴레이트계 자외선 경화성 수지는 하드코팅층의 크랙발생 또는 점도 상승에 따른 작업성 저하 등의 문제점을 고려하여, 5 내지 20 중량%의 함량으로 포함되는 것이 바람직하다. The type of the acrylate-based UV-curable resin is not particularly limited as long as it is an acrylate-based UV-curable resin generally used in the art. For more specific examples, 2-(fefluorodecyl)ethyl methacrylate, 3-perfluorooctyl-2-hydroxy propyl acrylate, 3-(perfluoro-9-methyldecyl)-1, 2 -Consisting of epoxypropane, (meth)acrylic acid-2,2,2-trifluoroethyl, (meth)acrylic acid-2,2,2-trifluoromethyl, 3,3,3,-trifluoropropyl and mixtures thereof One or more selected from the group may be used. In addition, the acrylate-based UV-curable resin is preferably contained in an amount of 5 to 20% by weight in consideration of problems such as cracking in the hard coating layer or a decrease in workability due to an increase in viscosity.
상기 퍼플루오로 폴리에테르를 함유하는 화합물에 다관능 아크릴레이트가 반응되어 형성되는 불소 변성 다관능 아크릴레이트 화합물은 자외선 경화로 형성된 하드코팅층이 오랜 시간이 경과하거나 주기적인 마찰을 가해도 박리 또는 누락하지 않고, 반영구적으로 표면슬립 효과를 유지할 수 있으며, 표면경도 및 내찰상성을 향상시키는 효과를 부여한다. 이러한 상기 퍼플루오로 폴리에테르를 함유하는 화합물에 다관능 아크릴레이트가 반응되어 형성되는 불소 변성 다관능 아크릴레이트 화합물은 상기한 효과를 고려하여, 0.1 내지 5 중량%의 함량으로 포함되는 것이 바람직하다. The fluorine-modified polyfunctional acrylate compound formed by reacting a polyfunctional acrylate with the compound containing the perfluoropolyether does not peel off or omit even if the hard coating layer formed by UV curing has elapsed for a long time or is subjected to periodic friction. Without, it can semi-permanently maintain the surface slip effect, and gives the effect of improving the surface hardness and scratch resistance. In consideration of the above effects, the fluorine-modified polyfunctional acrylate compound formed by reacting a polyfunctional acrylate with the compound containing the perfluoropolyether is preferably contained in an amount of 0.1 to 5% by weight.
상기 광중합 개시제는 종래부터 널리 이용되는 공지의 광중합 개시제를 제한없이 사용할 수 있다. 예를 들어, 1-하이드록시 시클로헥실페닐케톤과 같은 벤조페논계 화합물을 사용할 수 있다. 보다 구체적으로는 아세토페논류, 벤조페논류, 미클러벤조일벤조에이트, α-아밀옥심에스테르, 및 티옥산톤류를 단독으로 또는 혼합하여 사용할 수 있으나, 이에 한정되는 것은 아니다. 또한, 상기 광중합 개시제는 광경화 시간 및 구현되는 하드코팅층의 경도를 고려하여, 1 내지 10 중량%의 함량으로 포함되는 것이 바람직하다. As the photopolymerization initiator, a known photopolymerization initiator widely used in the prior art may be used without limitation. For example, a benzophenone-based compound such as 1-hydroxycyclohexylphenylketone can be used. More specifically, acetophenones, benzophenones, miklerbenzoylbenzoate, α-amyloxime ester, and thioxanthones may be used alone or in combination, but is not limited thereto. In addition, the photopolymerization initiator is preferably included in an amount of 1 to 10% by weight in consideration of the photocuring time and the hardness of the hard coating layer to be implemented.
상기 헥사플루오로이소프로판올(Hexafluoroisopropanol, HFP)은 플루오르 메틸기(methyl group, -CF3)를 포함하는 알코올(alcohol)계 화학 물질로, 우수한 표면 경도를 갖는 하드코팅층을 제공할 수 있게 한다. 이러한 효과를 고려하여, 상기 헥사플루오로이소프로판올(Hexafluoroisopropanol, HFP)은 30 내지 50 중량%의 함량으로 포함되는 것이 바람직하다. The hexafluoroisopropanol (HFP) is an alcohol-based chemical material containing a fluoromethyl group (-CF 3 ), and it is possible to provide a hard coating layer having excellent surface hardness. In consideration of these effects, the hexafluoroisopropanol (HFP) is preferably included in an amount of 30 to 50% by weight.
상기 극성 용매는 상기 HFP와 끓는 점이 비슷하고, 휘발성이 크지 않은 특성을 갖는 것으로 메탄올(methanol), 이소프로판올(isopropylalcohol, IPA) 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상을 사용할 수 있다. The polar solvent has a boiling point similar to that of the HFP and has a low volatility, and at least one selected from the group consisting of methanol, isopropylalcohol (IPA), and mixtures thereof may be used.
또한, 상기 하드코팅층은 표면에 프라이머 처리, 플라즈마 처리, 코로나 처리 등의 드라이 처리, 알칼리 처리(비누화 처리)등의 화학 처리, 용이한 접착제층을 형성하는 코팅 처리 등을 추가적으로 수행하여, 경도 및 부착력을 더욱 향상시킬 수 있는 효과가 있다.In addition, the hard coating layer additionally performs a primer treatment, a plasma treatment, a dry treatment such as a corona treatment, a chemical treatment such as an alkali treatment (saponification treatment), a coating treatment to form an easy adhesive layer, etc. There is an effect that can be further improved.
상기 데코레이션층(5)은 폴리에스터 또는 에폭시 수지와 특정 색상 구현을 위한 안료 (pigment)의 혼합물일 수 있다. 일반적으로 데코레이션층은 검은색을 많이 사용하였으나, 최근 다양한 색상을 이용하는 제품이 출시되고 있고, 본 발명 또한 특정의 색상에 한정되는 것은 아니다.The
또한, 이러한 데코레이션층(5)은 이형층을 포함하는 MDD 열전사용 리본(11)에 별도로 형성 및 제작한 후, 본 발명의 일 구현예에 따른 MDD 열전사 공정을 수행함으로써, 편광필름층(3)의 하드코팅층 상에 용이하게 전사될 수 있는 것이다.In addition, such a
보다 구체적으로 상기 데코레이션층(5)의 MDD 열전사 공정은 도 7에 도시된 바와 같이 다수의 열전사헤드(10) 및 MDD 열전사리본(11)을 통과하는 공정을 통하여, 다층구조를 갖는 데코레이션층을 편광필름층 상에 형성할 수 있다.More specifically, the MDD thermal transfer process of the
보다 구체적으로 상기 데코레이션층(5)은 색상 또는 모양 중 어느 하나 이상을 표현하는 컬러틴트층(501); 패턴층(502); 투과율 또는 반사율을 조절하는 기능을 수행하는 증착물질을 증착한 증착층(503); 및 차폐인쇄층(504)을 포함하도록 제작함으로써, 화상표시장치의 내부 배선이나 금속전극 등을 가리는 것은 물론, 현대인들의 기호에 맞도록 색상, 광택, 그리고 문양(즉, 패턴) 등이 다양하게 표현될 수 있는 효과가 있다. 이러한 본 발명의 일 구현예에 따른 데코레이션층의 단면도를 나타낸 이미지는 도 8에 도시하였다.More specifically, the
이때, 상기 컬러틴트층(501), 차폐인쇄층(504) 및 상기 두층으로 이루어진 군에서 선택되는 1종 이상은 상기한 편광필름층(3)의 하드코팅층과의 결합력을 더욱 개선하기 위하여, 폴리에스터 또는 에폭시 수지와 특정 색상 구현을 위한 안료 (pigment)의 혼합물 100 중량부에, 아크릴-멜라민 공중합 수지 및 폴리스티렌 수지 20 내지 30 중량부를 더욱 함유할 수 있다. At this time, at least one selected from the group consisting of the
이러한 본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름은 화상표시장치에 부착(200)되어 매우 유용하게 사용될 수 있다. The optical film having a decoration function according to an embodiment of the present invention may be attached 200 to an image display device and thus can be very usefully used.
본 발명의 다른 일 구현예는 상기 본 발명의 일 구현예에 따른 광학필름을 포함하는 것인 화상표시장치를 제공한다.Another embodiment of the present invention provides an image display device including the optical film according to the embodiment of the present invention.
상기 화상표시장치는 액정표시(liquid crystal display: LCD) 장치, 유기발광표시(organic light emitting display: OLED) 장치, 플라즈마표시(plasma display panel: PDP) 장치 및 전계방출표시(field emission display: FED) device) 장치 등을 포함할 수 있으나, 이에 한정되는 것을 아니다.The image display device includes a liquid crystal display (LCD) device, an organic light emitting display (OLED) device, a plasma display panel (PDP) device, and a field emission display (FED). device) may include a device, but is not limited thereto.
또한, 본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름 및 화상표시장치의 사이에는 터치스크린 패널, 비산방지 필름 등과 같은 화상표시장치의 추가 부재가 더 부착될 수 있다.In addition, an additional member of an image display device such as a touch screen panel and a shatterproof film may be further attached between the optical film having a decoration function and the image display device according to an embodiment of the present invention.
본 발명의 일 구현예에 따른 데코레이션 기능을 갖는 광학필름 및 이를 포함하는 화상표시장치는 베이스 기판의 형상 또는 재질에 구애받지 않도록, 편광필름층의 비표시 영역인 베젤부에 데코레이션층을 형성함으로써, 용이한 제조방법으로 화상표시장치의 내부 배선이나 금속전극 등을 가리는 것은 물론, 현대인들의 기호에 맞도록 색상, 광택, 그리고 문양(즉, 패턴) 등이 다양하게 표현될 수 있는 효과가 있다.In an optical film having a decoration function and an image display device including the same according to an embodiment of the present invention, a decoration layer is formed on the bezel part of the non-display area of the polarizing film layer so as not to be restricted by the shape or material of the base substrate, In addition to covering internal wiring or metal electrodes of an image display device with an easy manufacturing method, colors, gloss, and patterns (ie, patterns) can be expressed in various ways to suit the tastes of modern people.
또한, 상기 데코레이션층은 MDD 열전사 공정에 의하여 형성될 수 있어, 그 두께가 매우 얇아, 이후 인접하여, 적층되는 점착층의 두께를 줄일 수 있는 효과가 있다. 이로써, 화상표시장치의 박막화에 기여할 수 있는 효과가 있다. 뿐만 아니라, 물리적, 기계적 또는 화학적 불량을 획기적으로 줄일 수 있는 효과가 있다.In addition, since the decoration layer may be formed by the MDD thermal transfer process, its thickness is very thin, and there is an effect of reducing the thickness of the adhesive layer that is adjacent to and laminated thereafter. Thereby, there is an effect that can contribute to thinning of the image display device. In addition, there is an effect of remarkably reducing physical, mechanical, or chemical defects.
또한, 이러한 광학필름은 표시패널의 전극 패턴으로부터 반사된 외광이 차단될 수 있는 우수한 편광 효과 뿐만 아니라, 화상표시장치를 외부의 충격으로부터 보호할 수 있는 효과가 있다. In addition, such an optical film has an excellent polarization effect in which external light reflected from the electrode pattern of the display panel can be blocked, as well as an effect of protecting the image display device from external impact.
이상의 구현예 등에 관한 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형 가능하다. 따라서 본 발명에 개시된 일 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 일 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The description of the above embodiments, etc., is merely illustrative of the technical idea of the present invention, and those of ordinary skill in the technical field to which the present invention pertains can various modifications and variations without departing from the essential characteristics of the present invention. Do. Accordingly, the exemplary embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain the technical idea, and the scope of the technical idea of the present invention is not limited by this exemplary embodiment. The scope of protection of the present invention should be construed by the following claims, and all technical ideas within the scope equivalent thereto should be construed as being included in the scope of the present invention.
100: 광학필름
101: 표시 영역
102: 비표시 영역
1: 베이스 기판
2: 제1 점착층
3: 편광필름층
4: 제2 점착층
5: 데코레이션층
301: 편광소자층
302, 303: 보호/지지층
310, 320: 하드코팅층
501: 컬러틴트층
502: 패턴층
503: 증착층
504: 차폐인쇄층
200: 화상표시장치 부착부
10: 열전사헤드
11: MDD 열전사리본
12: 플라텐롤러
13 : 이송부
14 : 모터
15 : 구동롤러
16 : 종동롤러
17 : 제2필름센서
18: 권취롤100: optical film
101: display area 102: non-display area
1: base substrate 2: first adhesive layer
3: polarizing film layer 4: second adhesive layer
5: decoration layer
301: polarizing
310, 320: hard coating layer
501: color tint layer 502: pattern layer
503: vapor deposition layer 504: shielding printing layer
200: image display device attachment
10: thermal transfer head 11: MDD thermal transfer ribbon
12: platen roller 13: transfer unit
14: motor 15: drive roller
16: driven roller 17: second film sensor
18: winding roll
Claims (8)
상기 광학필름(100)은 베이스 기판(1); 상기 베이스 기판(1)의 하부면에 형성되는 제1 점착층(2); 상기 제1 점착층(2)의 하부면에 형성되는 편광필름층(3) 및 상기 편광필름층(3)의 하부면에 형성되는 제2 점착층(4)을 포함하는 것이고,
상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에는 비표시 영역을 따라 형성되는 데코레이션층(5)을 포함하는 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
In the optical film 100 including the display area 101 and the non-display area 102,
The optical film 100 includes a base substrate 1; A first adhesive layer 2 formed on the lower surface of the base substrate 1; It includes a polarizing film layer 3 formed on the lower surface of the first adhesive layer 2 and a second adhesive layer 4 formed on the lower surface of the polarizing film layer 3,
An optical film having a decoration function, characterized in that it comprises a decoration layer (5) formed along a non-display area on either one of the upper surface or the lower surface of the polarizing film layer (3).
상기 편광필름층(3)은,
입사되는 빛 중에서 일정 방향으로 편광된 빛을 투과시키는 편광소자층(301), 상기 편광소자층(301)의 상부면에 형성되는 상부면 보호/지지층(302)을 포함하는 것이고,
상기 편광필름층(3)과 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 상부면 보호/지지층(302)의 표면에는 하드코팅층(310)을 형성하는 것이고,
상기 형성되는 하드코팅층(310)의 표면에는 MDD(Micro Dry process Decoration) 열전사 공정에 의하여, 0.1 내지 10 μm 두께의 데코레이션층(5)이 형성되는 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
The method of claim 1,
The polarizing film layer 3,
It includes a polarizing element layer 301 that transmits light polarized in a predetermined direction among incident light, and an upper surface protection/support layer 302 formed on the upper surface of the polarizing element layer 301,
In order to improve the adhesion between the polarizing film layer 3 and the decoration layer 5, a hard coating layer 310 is formed on the surface of the upper surface protection/support layer 302,
An optical film having a decoration function, characterized in that a decoration layer 5 having a thickness of 0.1 to 10 μm is formed on the surface of the formed hard coating layer 310 by a micro dry process decoration (MDD) thermal transfer process.
상기 편광필름층(3)은,
입사되는 빛 중에서 일정 방향으로 편광된 빛을 투과시키는 편광소자층(301), 상기 편광소자층(301)의 하부면에 형성되는 하부면 보호/지지층(303)을 포함하는 것이고,
상기 편광필름층(3)과 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 하부면 보호/지지층(302)의 표면에는 하드코팅층(320)을 형성하는 것이고,
상기 형성되는 하드코팅층(320)의 표면에는 MDD(Micro Dry process Decoration) 열전사 공정에 의하여, 0.1 내지 10 μm 두께의 데코레이션층(5)이 형성되는 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
The method of claim 1,
The polarizing film layer 3,
It includes a polarizing element layer 301 that transmits light polarized in a predetermined direction among incident light, and a lower surface protection/support layer 303 formed on a lower surface of the polarizing element layer 301,
In order to improve the adhesion between the polarizing film layer 3 and the decoration layer 5, a hard coating layer 320 is formed on the surface of the lower surface protection/support layer 302,
An optical film having a decoration function, characterized in that a decoration layer 5 having a thickness of 0.1 to 10 μm is formed on the surface of the formed hard coating layer 320 by a micro dry process decoration (MDD) thermal transfer process.
상기 편광필름층(3)은 데코레이션층(5)과의 접착력을 향상시키기 위하여, 상기 편광필름층(3)의 상부면 또는 하부면 중 어느 한 면에 하드코팅층(310, 320)을 포함하는 것이고,
상기 하드코팅층(310, 320)은 아크릴레이트계 자외선 경화성 수지 5 내지 20 중량%, 퍼플루오로 폴리에테르를 함유하는 화합물에 다관능 아크릴레이트가 반응되어 형성되는 불소 변성 다관능 아크릴레이트 화합물 0.1 내지 5 중량%, 광중합 개시제 1 내지 10 중량%, 헥사플루오로이소프로판올(Hexafluoroisopropanol, HFP) 30 내지 50 중량%, 및 잔량의 극성 용매를 포함하는 자외선 경화형 하드코팅용 조성물을 사용하여 형성되는 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
The method of claim 1,
The polarizing film layer 3 includes a hard coating layer 310, 320 on either the upper or lower surface of the polarizing film layer 3 in order to improve adhesion with the decoration layer 5 ,
The hard coating layers 310 and 320 are fluorine-modified polyfunctional acrylate compounds formed by reacting a polyfunctional acrylate with a compound containing 5 to 20% by weight of an acrylate-based ultraviolet curable resin and a perfluoropolyether 0.1 to 5 Decoration characterized in that it is formed using a composition for UV-curable hard coating containing weight%, photopolymerization initiator 1 to 10% by weight, hexafluoroisopropanol (HFP) 30 to 50% by weight, and the balance of polar solvent Optical film having a function.
상기 데코레이션층(5)은
색상 또는 모양 중 어느 하나 이상을 표현하는 컬러틴트층(501); 패턴층(502); 투과율 또는 반사율을 조절하는 기능을 수행하는 증착물질을 증착한 증착층(503); 및 차폐인쇄층(504)을 포함하는 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
The method of claim 1,
The decoration layer 5 is
A color tint layer 501 expressing any one or more of colors or shapes; A pattern layer 502; A deposition layer 503 on which a deposition material for controlling transmittance or reflectance is deposited; And a shielding printing layer (504).
상기 베이스 기판(1)은 평면 형태인 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
The method of claim 1,
The base substrate (1) is an optical film having a decoration function, characterized in that the flat shape.
상기 베이스 기판(1)은 중앙은 평면 형태인 것이고, 양측은 곡면 형태인 것을 특징으로 하는 데코레이션 기능을 갖는 광학필름.
The method of claim 1,
The base substrate 1 is an optical film having a decoration function, characterized in that the center has a flat shape and both sides have a curved shape.
An image display device comprising the optical film according to any one of claims 1 to 7.