KR20210009469A - Curtain sheet with low-e film - Google Patents

Curtain sheet with low-e film Download PDF

Info

Publication number
KR20210009469A
KR20210009469A KR1020190085730A KR20190085730A KR20210009469A KR 20210009469 A KR20210009469 A KR 20210009469A KR 1020190085730 A KR1020190085730 A KR 1020190085730A KR 20190085730 A KR20190085730 A KR 20190085730A KR 20210009469 A KR20210009469 A KR 20210009469A
Authority
KR
South Korea
Prior art keywords
film
low
curtain fabric
printing
manufactured
Prior art date
Application number
KR1020190085730A
Other languages
Korean (ko)
Inventor
김태훈
이원형
Original Assignee
김태훈
이원형
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김태훈, 이원형 filed Critical 김태훈
Priority to KR1020190085730A priority Critical patent/KR20210009469A/en
Publication of KR20210009469A publication Critical patent/KR20210009469A/en

Abstract

The present invention relates to a curtain fabric with a low-e film. More particularly, the present invention relates to a curtain fabric with a low-e film, capable of maximizing a thermal insulation effect as well as a decorative effect by bonding a low-e film having a thermal barrier effect to a printing film made of a synthetic resin for use in curtains or blinds. The present invention has an effect of preventing cold or warm air from escaping to the outside without replacing windows by adding a heat blocking function to the film of curtains or blinds that can be installed on windows, doors, ventilation windows, etc.

Description

로이필름 커튼원단{CURTAIN SHEET WITH LOW-E FILM}Low-E film curtain fabric{CURTAIN SHEET WITH LOW-E FILM}

본 발명은 로이필름 커튼원단에 관한 것으로서, 보다 상세하게는 열차단 효과를 갖는 로이필름을 합성수지로 된 인쇄필름에 접합하여 커튼 또는 블라인드에 사용함으로써 장식 효과와 함께 단열효과를 극대화할 수 있도록 하는 로이필름 커튼원단에 관한 것이다.The present invention relates to a low-E film curtain fabric, and more particularly, a low-E film that has a heat shielding effect is bonded to a printing film made of synthetic resin and used for curtains or blinds, thereby maximizing the insulation effect as well as the decorative effect. It relates to film curtain fabric.

오늘날 세계 각국은 고유가 시대를 맞아 에너지 문제 해결을 최우선 과제로 선정하고 그에 대한 대비책 마련을 서두르고 있다. 다양한 종류의 대비책 중 하나는 산업 현장이나 건축물 등 주요 에너지 사용 부문에서 에너지 소실을 줄이고, 효율을 높일 수 있는 기술을 통해 에너지 사용량을 절감하는 것이다.Today, in the era of high oil prices, many countries around the world are in a hurry to prepare solutions for energy problems as their top priority. One of the various types of countermeasures is to reduce energy consumption in major energy use sectors such as industrial sites and buildings, and to reduce energy use through technologies that can increase efficiency.

건축물에 있어서, 창호(windows and doors)는 벽체에 비해 약 8배 내지 약 10배 이상의 낮은 단열 특성이 있기 때문에 창호를 통한 열손실은 건물 전체의 열손실의 약 25% 내지 약 45%를 차지할 정도로 심각하다.In buildings, windows and doors have about 8 to about 10 times lower insulation properties than walls, so heat loss through windows accounts for about 25% to about 45% of the total heat loss of the building. Serious.

따라서 창호에서의 열손실을 줄이기 위해 로이유리(LOW-Emissivity Glass)가 사용되고 있다.Therefore, LOW-Emissivity Glass is used to reduce heat loss in windows.

로이유리는 일반 유리의 일면에 적외선 반사율이 높은 금속막을 코팅한 구조를 가지며, 단층 또는 복층 구조를 가진다. 금속막은 가시광선을 투과시켜 실내의 채광성을 높여주고, 적외선을 반사하여 실내외에서의 열 이동을 감소시켜 실내의 온도 변화를 적게 만들어 준다.Low-E glass has a structure in which a metal film with high infrared reflectance is coated on one surface of a general glass, and has a single-layer or multi-layer structure. The metal film transmits visible light to increase indoor lighting, and reflects infrared rays to reduce heat transfer indoors and outdoors, thereby reducing indoor temperature changes.

최근에는 일반적인 형태의 유리창에 금속막이 코팅된 로이필름을 부착하여 열차단율을 높이는 기술도 개시되고 있다.Recently, a technology for increasing the heat shielding rate by attaching a low-E film coated with a metal film to a general type of glass window has also been disclosed.

별도로 부착할 수 있는 로이필름에는 로이(저-방사) 특성을 갖는 필름 다중층을 포함하며, 상기 로이 필름 다중층은 적외선 및/또는 태양광선을 반사시킬 수 있는 하나 이상의 기능성 금속성 필름, 특히 은 또는 금속성 은-함유 합금 기재의 하나 이상의 기능성 금속성 필름을 포함한다.The Ro-E film that can be attached separately includes a film multi-layer having low-E (low-emission) properties, and the Ro-E film multi-layer is one or more functional metallic films capable of reflecting infrared and/or sunlight, especially silver or And one or more functional metallic films based on metallic silver-containing alloys.

도 1은 유리창과 로이필름으로 구성된 열차단유리창의 구성을 나타낸 분해사시도이며, 도 2는 열차단유리창의 열차단 기능을 나타낸 개념도이다.1 is an exploded perspective view showing the configuration of a heat shielding glass window composed of a glass window and a low-E film, and FIG. 2 is a conceptual diagram showing the heat shielding function of a heat shielding glass window.

창호유리의 제조시에 금속막의 코팅을 통해 열차단기능을 부여하지 않은 경우에는 도 1과 2에 도시된 것과 같이 일반적인 유리창(10)의 표면에 로이필름(20)을 접착시켜 에너지 투과계수를 감소시킴으로써 열차단 기능을 추가할 수 있다.When the window glass is not provided through the coating of a metal film, the energy transmission coefficient is reduced by bonding the low-E film 20 to the surface of the general window 10 as shown in FIGS. 1 and 2 By doing so, it is possible to add a thermal blocking function.

로이필름(20)이 부착된 유리창(10)은 열차단 효율이 높아져서 외부의 태양(30)으로부터 방사되는 가시광선이나 열선을 차단함으로써 하절기에 실내의 온도가 상승하는 것을 막을 수 있다. 또한 실내의 냉난방기(40)로부터 발생하는 냉기나 열기를 차단시켜 실내 환경을 쾌적하게 유지할 수 있다.The glass window 10 to which the low-E film 20 is attached can prevent an increase in the indoor temperature in summer by blocking visible or hot rays radiated from the external sun 30 because the heat shielding efficiency is high. In addition, it is possible to keep the indoor environment comfortable by blocking cold air or heat generated from the indoor air conditioner 40.

그런데, 창호 유리창을 로이유리로 교체할 수 없거나 로이필름을 부착할 수 없는 환경에서는 창호를 통해 열전달이 이루어지는 것을 막을 수 없어서 열효율이 나빠지는 문제가 있다.However, there is a problem in that thermal efficiency deteriorates because it is impossible to prevent heat transfer through the windows in an environment in which a low-E glass cannot be replaced or a low-E film cannot be attached.

KRKR 10-2018-009373910-2018-0093739 AA KRKR 10-119389710-1193897 B1B1 KRKR 10-155483810-1554838 B1B1

전술한 문제점을 해결하기 위한 본 발명은 열차단 계수가 높은 금속막으로 이루어진 로이필름을 인쇄필름에 부착하여 커튼원단을 제작하고, 커튼원단으로 커튼이나 블라인드를 제작함으로써 열차단 효율이 높은 커튼이나 블라인드를 제작할 수 있도록 하는 로이필름 커튼원단을 제공하는 것을 목적으로 한다.The present invention for solving the above-described problem is to produce a curtain fabric by attaching a low-E film made of a metal film having a high heat shielding coefficient to a printing film, and fabricate curtains or blinds with the curtain fabric, thereby providing curtains or blinds with high heat shielding efficiency. Its purpose is to provide a low-y film curtain fabric that enables the production of.

또한 인쇄필름에 도형이나 문자, 색깔 등을 적용함으로써 심미감을 향상시키는 커튼이나 블라인드를 제조할 수 있도록 하는 로이필름 커튼원단을 제공하는 것을 목적으로 한다.In addition, it is an object of the present invention to provide a low-E film curtain fabric capable of manufacturing curtains or blinds that improve aesthetics by applying figures, characters, colors, etc. to a printing film.

전술한 문제점을 해결하기 위해 안출된 본 발명은 열차단 효과와 장식 효과를 동시에 구현하는 커튼원단으로서, 합성수지 필름의 표면에 문양이나 도형, 문자 중 어느 하나 이상을 인쇄하여 제조되는 인쇄필름(102)과; 합성수지 필름의 표면에 금속막을 코팅하여 제조되는 로이필름(104);을 포함하며, 상기 인쇄필름(102)과 상기 로이필름(104)은 접착제에 의해 접착되며, 상기 로이필름(104)은 적외선 또는 태양광선의 차단기능 및 반사기능을 갖는 것을 특징으로 한다.The present invention conceived to solve the above-described problem is a curtain fabric that simultaneously implements a heat shielding effect and a decorative effect, and is a printing film 102 manufactured by printing any one or more of patterns, figures, and characters on the surface of a synthetic resin film. and; Including; a low-E film 104 manufactured by coating a metal film on the surface of a synthetic resin film, wherein the printing film 102 and the low-E film 104 are bonded by an adhesive, and the low-E film 104 is infrared or It is characterized by having a function of blocking and reflecting sunlight.

상기 인쇄필름(102) 및 상기 로이필름(104)은 PET 소재로 제작되는 것을 특징으로 한다.The printing film 102 and the low-E film 104 are made of PET material.

상기 커튼원단은 상기 인쇄필름(102)의 양쪽 표면에 두 개의 로이필름(104)을 각각 접착시켜 제조되는 것을 특징으로 한다.The curtain fabric is characterized in that it is manufactured by bonding two low-E films 104 to both surfaces of the printing film 102, respectively.

상기 커튼원단은 상기 로이필름(104)의 양쪽 표면에 두 개의 인쇄필름(102)을 각각 접착시켜 제조되는 것을 특징으로 한다.The curtain fabric is characterized in that it is manufactured by bonding two printing films 102 to both surfaces of the low-E film 104, respectively.

본 발명에 따르면 창호나 출입문, 환기창 등에 설치할 수 있는 커튼이나 블라인드의 필름에 열차단 기능을 부가하여 창호의 교체없이도 냉기나 온기가 외부로 빠져나가는 것을 막을 수 있는 효과가 있다.According to the present invention, a heat shielding function is added to the film of curtains or blinds that can be installed on windows, doors, ventilation windows, etc., so that cold air or warmth can be prevented from escaping to the outside without replacing the windows.

또한 단순히 열차단 기능을 갖는 필름만을 사용하는 것보다 장식효과를 높일 수 있어서 보다 아름다운 실내 인테리어를 구성할 수 있는 효과가 있다.In addition, it is possible to increase the decorative effect rather than simply using a film having a heat shielding function, so there is an effect of configuring a more beautiful interior interior.

도 1은 유리창과 로이필름으로 구성된 열차단유리창의 구성을 나타낸 분해사시도.
도 2는 열차단유리창의 열차단 기능을 나타낸 개념도.
도 3은 본 발명의 커튼원단의 구성을 나타낸 분해사시도.
도 4는 커튼원단에 인쇄부가 표시되는 상태를 나타낸 사시도.
도 5는 커튼원단의 내부 구조를 나타낸 단면도.
도 6은 다른 실시예에 따른 커튼원단의 구조를 나타낸 단면도.
도 7은 또 다른 실시예에 따른 커튼원단의 구조를 나타낸 단면도.
도 8은 본 발명의 커튼원단이 적용된 커튼의 구조를 나타낸 사시도.1 is an exploded perspective view showing the configuration of a heat shielding glass window composed of a glass window and a low-E film.
2 is a conceptual diagram showing the heat shield function of the heat shield window.
Figure 3 is an exploded perspective view showing the configuration of the curtain fabric of the present invention.
4 is a perspective view showing a state in which a printing unit is displayed on a curtain fabric.
5 is a cross-sectional view showing the internal structure of the curtain fabric.
6 is a cross-sectional view showing the structure of a curtain fabric according to another embodiment.
7 is a cross-sectional view showing the structure of a curtain fabric according to another embodiment.
8 is a perspective view showing the structure of a curtain to which the curtain fabric of the present invention is applied.

이하에서 도면을 참조하여 본 발명의 실시예에 따른 "로이필름 커튼원단"(이하, '커튼원단'이라 함)을 설명한다.Hereinafter, a "low-E film curtain fabric" (hereinafter, referred to as a "curtain fabric") according to an embodiment of the present invention will be described with reference to the drawings.

도 3은 본 발명의 커튼원단의 구성을 나타낸 분해사시도이며, 도 4는 커튼원단에 인쇄부가 표시되는 상태를 나타낸 사시도, 도 5는 커튼원단의 내부 구조를 나타낸 단면도이다.Figure 3 is an exploded perspective view showing the configuration of the curtain fabric of the present invention, Figure 4 is a perspective view showing a state in which a printing unit is displayed on the curtain fabric, and Figure 5 is a cross-sectional view showing the internal structure of the curtain fabric.

본 발명의 커튼원단(100)은 커튼이나 블라인드를 제작할 수 있도록 필름이나 원단 형태로 제작되는 것이 바람직하다. 통상적으로는 금속코팅을 용이하게 하고, 다양한 크기와 두께로 성형이 용이한 PET 필름을 사용한다.It is preferable that the curtain fabric 100 of the present invention is manufactured in the form of a film or fabric so that curtains or blinds can be manufactured. Typically, a PET film that facilitates metal coating and is easily molded in various sizes and thicknesses is used.

본 발명의 커튼원단(100)은 장식을 위해 문양이나 도형 등을 인쇄하는 인쇄필름(102)과, 열차단 기능을 구현하는 로이필름(104)으로 구성된다. 합성수지 필름으로 제조되는 인쇄필름(102)과 로이필름(104)은 독립적으로 제조된 후, 접착제 등을 사용하여 접착시킨다. 또한 인쇄필름(102)과 로이필름(104)을 하나의 공압출장치를 통해 동시에 압출시키면서 한 번에 제작할 수도 있을 것이다.The curtain fabric 100 of the present invention is composed of a printing film 102 for printing patterns or figures for decoration, and a low-e film 104 for implementing a heat shielding function. The printing film 102 and the low-E film 104 made of a synthetic resin film are independently manufactured and then bonded using an adhesive or the like. In addition, the printing film 102 and the low-E film 104 may be simultaneously extruded through a single coextrusion device and produced at a time.

인쇄필름(102)의 전면 또는 이면에는 특정 문양이나 도형, 문자 등을 인쇄할 수 있다. 인쇄필름(102)은 투명한 PET 소재를 사용할 수 있지만, 실내 인테리어 효과를 내고 직사광선 차단을 위해서는 반투명이나 불투명 소재를 사용하는 것이 바람직하다.A specific pattern, figure, character, etc. may be printed on the front or back surface of the printing film 102. The printing film 102 may use a transparent PET material, but it is preferable to use a translucent or opaque material in order to create an interior interior effect and block direct sunlight.

로이필름(104)은 PET 필름에 열차단 기능의 부여를 위해 금속막을 코팅한 형태로 제작된다. 로이필름(104)은 반투명이나 불투명 소재로 제작될 수 있지만, 인쇄필름(102)에 형성된 문양을 인식할 수 있도록 투명 소재로 제작하는 것이 바람직하다.The low-E film 104 is manufactured in a form in which a metal film is coated in order to impart a heat shield function to the PET film. The low-E film 104 may be made of a translucent or opaque material, but it is preferable to be made of a transparent material so that the pattern formed on the printing film 102 can be recognized.

인쇄필름(102)과 로이필름(104)은 PET 필름에 인쇄작업을 하거나 금속막 코팅작업을 하여 제작되며, 각각 제작된 인쇄필름(102)과 로이필름(104)을 접착제로 부착시켜 커튼원단(100)을 제작한다.The printing film 102 and the low-E film 104 are produced by printing or coating a metal film on a PET film, and attaching the produced printing film 102 and the low-E film 104 with an adhesive to a curtain fabric ( 100).

두 개의 필름을 접착한 상태에서 인쇄필름(102)의 표면에 형성된 인쇄부(102a)는 로이필름(104)과 접하거나 로이필름(104)의 반대쪽 표면으로 노출될 수 있다. 인쇄필름(102)에 형성된 인쇄부(102a)는 투명 소재의 로이필름(104)을 통과하여 노출되거나, 인쇄필름(102)의 표면으로부터 직접 노출되면서 심미감을 향상시킬 수 있다.The printing unit 102a formed on the surface of the printing film 102 in a state in which the two films are bonded may be exposed to the low-E film 104 or the opposite surface of the low-E film 104. The printing unit 102a formed on the printing film 102 may be exposed through the low-E film 104 made of a transparent material, or directly exposed from the surface of the printing film 102 to improve aesthetics.

인쇄필름(102)과 로이필름(104)을 접착하여 제조되는 커튼원단(100)은 별도로 유리창에 접착할 필요없이 그대로 커튼이나 블라인드로 제조된다.The curtain fabric 100 manufactured by bonding the printing film 102 and the low-y film 104 is manufactured as curtains or blinds without the need to separately adhere to the glass window.

도 6은 다른 실시예에 따른 커튼원단의 구조를 나타낸 단면도이며, 도 7은 또 다른 실시예에 따른 커튼원단의 구조를 나타낸 단면도이다.6 is a cross-sectional view showing the structure of a curtain fabric according to another embodiment, and FIG. 7 is a cross-sectional view showing the structure of a curtain fabric according to another embodiment.

커튼원단(100)의 열차단 효율을 증대시키기 위해서는 열차단 기능을 갖는 로이필름(104)을 이중으로 접착할 필요가 있다. 도 6에 도시된 커튼원단(100)은 가운데 인쇄필름(102)의 양쪽면에 로이필름(104)을 각각 접착시켜 제조된다. 두 개의 로이필름(104)을 구비한 경우에는 열차단계수가 더 증가한다.In order to increase the heat shielding efficiency of the curtain fabric 100, it is necessary to double-adher the low-E film 104 having a heat shielding function. The curtain fabric 100 shown in FIG. 6 is manufactured by bonding the low-E film 104 to both sides of the middle printing film 102, respectively. In the case of having two low-E films 104, the number of train stages is further increased.

그리고 커튼원단(100)에 장식효과를 더 크게 하기 위해서는 인쇄필름(102)을 로이필름(104)의 양쪽면에 접착시켜 구성한다. 앞면과 뒷면에 접착되는 인쇄필름(102)에는 각각 다른 문양을 인쇄할 수 있으며, 문자나 도형 등을 부가하여 표시기능을 구현할 수도 있다.In addition, in order to increase the decorative effect on the curtain fabric 100, the printing film 102 is adhered to both sides of the low-e film 104. Different patterns may be printed on the printing film 102 adhered to the front and rear surfaces, and a display function may be implemented by adding characters or figures.

이와 같은 구성을 통해 제조된 커튼원단(100)은 커튼이나 블라인드로 제작되는데, 도 8은 본 발명의 커튼원단이 적용된 커튼의 구조를 나타낸 사시도이다.The curtain fabric 100 manufactured through this configuration is made of curtains or blinds, and FIG. 8 is a perspective view showing the structure of a curtain to which the curtain fabric of the present invention is applied.

도 8에 도시된 바와 같이, 인쇄필름(102)과 로이필름(104)을 접착시켜 제조된 커튼원단(100)을 적절한 크기로 재단하고, 상부에 관통공을 형성하거나 아일렛을 설치한다. 그리고 관통공이나 아일렛에 고리(130)를 연결한 후, 커튼봉(120)에 고리(130)를 끼워서 커튼을 제작할 수 있다.As shown in FIG. 8, the curtain fabric 100 manufactured by bonding the printing film 102 and the low-E film 104 is cut to an appropriate size, and a through hole is formed on the top or an eyelet is installed. And after connecting the ring 130 to the through hole or the eyelet, the curtain can be manufactured by inserting the ring 130 on the curtain rod 120.

블라인드의 경우에는 롤러에 커튼원단(100)을 감아서 천장에 고정시키고, 체인이나 줄을 롤러에 연결하여 사용자가 아래위로 당겨서 위치를 조정하는 방법으로 사용할 수 있다.In the case of blinds, the curtain fabric 100 is wound around a roller and fixed to the ceiling, and a chain or string is connected to the roller, and the user pulls up and down to adjust the position.

본 발명에서는 PET 소재로 된 인쇄필름(102)과 로이필름(104)을 직접 접착시켜 커튼원단(100)을 제조하는 것으로 설명하였는데, 이외에도 다양한 방식의 적용이 가능하다. 즉, 패브릭 소재로 제작된 커튼에 투명 재질의 로이필름(104)을 직접 접착하여 열차단기능을 부여할 수 있다. 또한 여러 겹으로 된 패브릭 소재의 원단 내부에 로이필름(104)을 삽입하고, 패브릭을 재단하여 커튼을 제작할 수도 있을 것이다. 이 경우에도 창호를 통해 일어나는 열교환을 감소시킬 수 있어서 실내의 냉난방 환경을 개선할 수 있는 효과가 있다.In the present invention, it has been described that the curtain fabric 100 is manufactured by directly bonding the printed film 102 made of PET material and the low-E film 104, but various other methods can be applied. In other words, it is possible to impart a heat shielding function by directly adhering the low-E film 104 of a transparent material to a curtain made of a fabric material. In addition, it will be possible to insert the Roy film 104 into the fabric of a multi-ply fabric material and cut the fabric to produce a curtain. Even in this case, it is possible to reduce the heat exchange that occurs through the windows, thereby improving the indoor cooling and heating environment.

이상 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 설명하였지만, 상술한 본 발명의 기술적 구성은 본 발명이 속하는 기술 분야의 당업자가 본 발명의 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해되어야 하고, 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.Although preferred embodiments of the present invention have been described above with reference to the accompanying drawings, the technical configuration of the present invention described above is another specific form without changing the technical spirit or essential features of the present invention by those skilled in the art. It will be appreciated that it can be implemented with. Therefore, the embodiments described above should be understood as illustrative and non-limiting in all respects, and the scope of the present invention is indicated by the claims to be described later rather than the detailed description, and the meaning and scope of the claims and All changes or modified forms derived from the equivalent concept should be interpreted as being included in the scope of the present invention.

10 : 유리창 20 : 로이필름
30 : 태양 40 : 냉난방기
100 : 커튼원단 102 : 인쇄필름
104 : 로이필름 120 : 커튼봉
130 : 고리10: glass window 20: low-e film
30: sun 40: air conditioner
100: curtain fabric 102: printing film
104: Roy film 120: curtain rod
130: ring

Claims (4)

열차단 효과와 장식 효과를 동시에 구현하는 커튼원단으로서,
합성수지 필름의 표면에 문양이나 도형, 문자 중 어느 하나 이상을 인쇄하여 제조되는 인쇄필름(102)과;
합성수지 필름의 표면에 금속막을 코팅하여 제조되는 로이필름(104);을 포함하며,
상기 인쇄필름(102)과 상기 로이필름(104)은 접착제에 의해 접착되며,
상기 로이필름(104)은 적외선 또는 태양광선의 차단기능 및 반사기능을 갖는 것을 특징으로 하는, 로이필름 커튼원단.As a curtain fabric that realizes the heat shielding effect and decoration effect at the same time,
A printing film 102 manufactured by printing one or more of patterns, figures, and characters on the surface of the synthetic resin film;
Including; Low-E film 104 manufactured by coating a metal film on the surface of the synthetic resin film,
The printing film 102 and the low-E film 104 are adhered by an adhesive,
The low-E film 104 is characterized in that it has a function of blocking infrared rays or sunlight and a reflection function, the low-E film curtain fabric. 제1항에 있어서,
상기 인쇄필름(102) 및 상기 로이필름(104)은 PET 소재로 제작되는 것을 특징으로 하는, 로이필름 커튼원단.The method of claim 1,
The printing film 102 and the low-E film 104, characterized in that made of a PET material, low-e film curtain fabric. 제1항에 있어서,
상기 커튼원단은 상기 인쇄필름(102)의 양쪽 표면에 두 개의 로이필름(104)을 각각 접착시켜 제조되는 것을 특징으로 하는, 로이필름 커튼원단.The method of claim 1,
The curtain fabric is manufactured by bonding two low-E films 104 to both surfaces of the printing film 102, respectively. 제1항에 있어서,
상기 커튼원단은 상기 로이필름(104)의 양쪽 표면에 두 개의 인쇄필름(102)을 각각 접착시켜 제조되는 것을 특징으로 하는, 로이필름 커튼원단.The method of claim 1,
The curtain fabric is manufactured by bonding two printing films 102 to both surfaces of the low-E film 104, respectively.
KR1020190085730A 2019-07-16 2019-07-16 Curtain sheet with low-e film KR20210009469A (en)