KR20200113321A - Component of floor panel with elasticity, and floor panel comprising the same - Google Patents
Component of floor panel with elasticity, and floor panel comprising the same Download PDFInfo
- Publication number
- KR20200113321A KR20200113321A KR1020190033302A KR20190033302A KR20200113321A KR 20200113321 A KR20200113321 A KR 20200113321A KR 1020190033302 A KR1020190033302 A KR 1020190033302A KR 20190033302 A KR20190033302 A KR 20190033302A KR 20200113321 A KR20200113321 A KR 20200113321A
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- mortar
- elastic
- mixed
- coating
- Prior art date
Abstract
Description
본 발명은 탄성을 갖는 도막형 바닥재용 조성물, 및 이를 포함하는 도막형 바닥재에 관한 것으로, 더욱 상세하게는 탄성을 가져 충격 흡수를 필요로 하는 다양한 분야에 적용할 수 있을 뿐만 아니라, 단열 효과, 크랙방지 효과 및 미끄럼방지 효과도 동시에 제공할 수 있는 탄성을 갖는 도막형 바닥재용 조성물, 및 이를 포함하는 도막형 바닥재에 관한 것이다.The present invention relates to a composition for a coating-type flooring material having elasticity, and to a coating-type flooring material comprising the same, and more particularly, it can be applied to various fields requiring shock absorption due to its elasticity, as well as heat insulation effect and cracking. It relates to a coating-type flooring composition having elasticity capable of simultaneously providing an anti-slip effect and an anti-slip effect, and a coating-type flooring material comprising the same.
최근에는 건강에 대한 관심의 증대로 시나 구청 등에서, 시간이 없는 시민들을 위해 집에서 가까운 곳에 체육시설, 공원, 산책로 등의 근린생활공간을 조성하여 시민들에게 건강을 지키고 안락함과 편안함을 제공하고 있다.In recent years, due to the increasing interest in health, city and ward offices have created neighborhood living spaces such as sports facilities, parks, and walking trails near their homes for citizens who do not have time to protect their health and provide comfort and comfort.
이러한 근린생활공간에는 운동장이나 조깅로, 자전거도로 등이 주로 형성되는데, 시민들이 부상방지 및 인체 관절에의 충격완화, 비나 눈이 올 경우 투수, 도심미관등을 고려하여 종래 시멘트나 콘크리트, 쇄석층으로 형성된 기반층 상부에 별도의 바닥재를 형성시키고 있다.In these neighborhood living spaces, sports grounds, jogging paths, and bicycle paths are mainly formed.Conventional cement, concrete, crushed stone layers in consideration of citizens' injury prevention, impact relief on human joints, water permeability in case of rain or snow, and urban aesthetics. A separate flooring material is formed on the upper part of the base layer formed by
이러한 바닥재는 도심의 미관을 고려하여 여러가지 색깔이나 문양을 형성시키거나 시민들의 안정을 고려하여 표면이 거칠은 콘크리트나 아스콘 위에, 비나 눈이 올 경우 미끄럽지 않은 바닥재를 상기 기반층 상부에 포설하는 방법을 사용하고 있다.Such a flooring material may form various colors or patterns in consideration of the aesthetics of the city center, or a method of installing a non-slip flooring material on the top of the base layer in case of rain or snow on the rough concrete or asphalt concrete in consideration of the stability of citizens. I'm using it.
그러나 이러한 바닥재는 콘크리트, 아스콘 또는 쇄석 등으로 형성된 기반층 상부에 우레탄 액상을 직접 도포하는 방식을 많이 사용하고 있는데, 이러한 종래의 도막형 바닥재는 다음과 같은 문제점이 있었다.However, such a flooring material is widely used in a method of directly applying a liquid urethane to an upper part of a base layer formed of concrete, ascon or crushed stone, and such a conventional coating-type flooring material has the following problems.
먼저, 종래의 바닥재는 접착력이 떨어져 바닥재의 이탈이 심하게 생기고 크랙부분에 중량이 가해지면 크랙부분부터 이탈을 시작하여 점점 번져나가는 현상이 발생되며, 특히 콘크리트, 아스팔트 및 투수콘 등 구체바닥에서 크랙이 발생하면 쉽게 바닥재의 이탈이 시작되어 번져나가는 문제점이 있었다. First, the conventional flooring has a poor adhesive strength, so the separation of the flooring occurs severely, and when weight is applied to the crack, it begins to separate from the crack and spreads gradually.In particular, cracks occur in concrete, asphalt and permeable cones. When it occurs, there is a problem that the floor material easily starts to come off and spread out.
또한, 종래의 바닥재는 주차장 바닥인 경우에 대다수가 에폭시로 도포되어 있는데, 이러한 에폭시 바닥은 통상 자량 타이어와 주차장 바닥 사이의 마찰계수가 크기 때문에 마찰음이 상당하게 발생하는 문제점이 있었다. In addition, in the case of a parking lot floor, a majority of the conventional flooring material is coated with epoxy. However, since the epoxy floor has a large coefficient of friction between the tire and the parking lot floor, there is a problem in that frictional noise occurs considerably.
또한, 종래의 바닥재는 옥외 또는 옥상 주차장인 경우 더운 여름철에 차량에서 내리는 순간 숨이 막힐 정도의 더운 기운이 올라오는데, 이는 옥외 또는 옥상 주차장의 바닥재가 적외선을 받아 구체바닥이 열을 품고 있기 때문에 대기의 온도보다 바닥표면의 온도는 5~10℃ 정도 더 높기 때문에 발생하는 문제이다. In addition, in the case of an outdoor or rooftop parking lot, in the case of an outdoor or rooftop parking lot, the moment you get off the vehicle in the hot summer, a breathtaking heat rises.This is because the floor material of the outdoor or rooftop parking lot receives infrared rays and the spherical floor holds heat. This is a problem that occurs because the temperature of the floor surface is 5~10℃ higher than that of.
또한, 종래의 바닥재는 최상층이 코팅이 되어 있기 때문에 비가 왔을 때 상당히 미끄러워 사람들의 보행 또는 차량이 정지할 때 미끄러지는 문제점이 있었다.In addition, since the top layer of the conventional flooring material is coated, it is quite slippery when it rains, and there is a problem of slipping when people walk or when the vehicle is stopped.
한편, 여가 생활에 대한 비중이 높아짐에 따라 산책 또는 운동을 위한 육상트랙, 테니스장 또는 다목적 구장을 조성할 때 탄성층으로 도포하는 경우가 늘고 있다.On the other hand, as the proportion of leisure life increases, the case of applying with an elastic layer is increasing when constructing a land track, tennis court or multipurpose stadium for walking or exercise.
그러나 탄성층은 충격흡수 기능은 우수하여 부상을 방지할 수는 있으나, 그 탄성층 상에서 구기종목 중 하나를 운동하는 경우에는 공이 탄성을 탄성층에서 흡수함에 따라 반발력이 떨어져 의도하는 플레이를 수행할 수 없다. 따라서 이러한 이유로 테니스장 등의 경기장에는 탄성이 없는 바닥재를 도포하여 사용하게 되므로, 충격에 의한 무릎 등의 부상이 유발되는 경우가 많았다.However, the elastic layer has excellent shock absorbing function and can prevent injury, but in the case of exercising one of the ball games on the elastic layer, the repulsive force decreases as the ball absorbs elasticity from the elastic layer, so that the intended play can be performed. none. Therefore, for this reason, since a non-elastic flooring material is applied and used in stadiums such as tennis courts, injuries such as knees due to impact are often caused.
종래 다른 예로, 수지바인더고무를 이용하여 제조된 수지바인더 탄성바닥재에서는 고무칩입자의 입도분포가 불규칙하여 바인더와 접착시 접착력이 저하되어 고무칩입자 사이에 균열이 발생함으로써 시공 후 하지면과 상부면 사이에서 밀림현상이 발생하는 부분이 생기거나 고무칩입자가 너무 조밀하게 분포되어 탄성도가 저하되 는 부분이 생기기도 하였다.As another example of the related art, in the resin binder elastic flooring material manufactured using resin binder rubber, the particle size distribution of rubber chip particles is irregular, and the adhesion between the rubber chip particles decreases when bonding with the binder, causing cracks between the rubber chip particles. In some cases, there was a part where the slipping phenomenon occurred, or a part where the elasticity was deteriorated due to too dense distribution of rubber chip particles.
또한 상기의 수지바인더 탄성바닥재는 종래에 주로 시공될 도로나 바닥표면에 대한 바인더도포작업후 탄성바닥재를 포설한 다음 양생하는 단순한 과정으로 시공되었는데, 상기 수지바인더 탄성바닥재의 제조에 사용되는 폐고무는 폐기되기전 장시간의 사용으로 그 내구성이 약해져 있는 상태이므로 상기와 같은 단순시공된 탄성바닥재는 균열이 생겨 탄성력이 저하되거나 인장강도의 감소로 상기 수지바인더 탄성바닥재가 시공된 바닥면이 부분부분 훼손되는 경우가 많았다.In addition, the resin binder elastic flooring material was constructed by a simple process of laying and curing the elastic flooring material after applying a binder to the road or floor surface to be mainly constructed in the prior art.The waste rubber used in the manufacture of the resin binder elastic flooring material is Since its durability is weakened due to long-term use before being discarded, the elasticity of the elastic flooring material is reduced due to cracks in the above-described simple constructed elastic flooring material, or the bottom surface on which the resin binder elastic flooring material is installed is partially damaged due to a decrease in tensile strength. There were many cases.
따라서, 상기한 종래의 문제점을 해결하기 위한 본 발명은, 탄성을 가져 충격 흡수를 필요로 하는 다양한 분야에 적용할 수 있을 뿐만 아니라, 단열 효과, 크랙방지 효과 및 미끄럼방지 효과도 동시에 제공할 수 있는 탄성을 갖는 도막형 바닥재용 조성물, 및 이를 포함하는 도막형 바닥재을 제공하는데 그 목적이 있다.Therefore, the present invention for solving the above-described conventional problems can be applied not only to various fields requiring shock absorption due to its elasticity, but also to provide heat insulation effect, crack prevention effect, and anti-slip effect at the same time. It is an object to provide a composition for a coating-type flooring material having elasticity, and a coating-type flooring material including the same.
본 발명의 해결과제는 이상에서 언급한 것들에 한정되지 않으며, 언급되지 아니한 다른 해결과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problem of the present invention is not limited to those mentioned above, and other problems that are not mentioned will be clearly understood by those skilled in the art from the following description.
상기 본 발명의 목적들 및 다른 특징들을 달성하기 위한 본 발명의 제1 관점에 따르면, 도막형 바닥재의 조성물에 있어서, 수지바인더, 및 혼합 탄성 몰탈을 포함하며, 상기 혼합 탄성 몰탈은 몰탈 및 탄성 수지를 포함하는 것을 특징으로 하는 탄성을 갖는 도막형 바닥재용 조성물이 제공된다.According to a first aspect of the present invention for achieving the objects and other features of the present invention, in the composition of a coating-type flooring, a resin binder and a mixed elastic mortar are included, and the mixed elastic mortar is a mortar and an elastic resin There is provided a coating-type flooring composition having elasticity, characterized in that it comprises a.
본 발명의 제1 관점에 있어서, 상기 수지바인더는 아크릴 수지와 우레탄 수지가 합성되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, 및 AE제를 포함하는 수용성 수지바인더로 이루어지고, 상기 혼합 탄성 몰탈의 상기 몰탈은 팽창질석을 사용한 단열시멘트, 초조강 포틀랜트 시멘트, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트, 세라믹 분말을 포함하여 이루어지며, 상기 혼합 탄성 몰탈의 상기 탄성 수지는 PP(polypropylene)와 EPDM(Ethylene Propylene Diene monomer)의 동적 가교 반응을 통해 제조된 열가소성 엘라스토머로 이루어질 수 있다.In the first aspect of the present invention, the resin binder is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by synthesizing an acrylic resin and a urethane resin, a dispersant, an antifoaming agent, an antifreeze agent, a UV blocking agent, a surfactant, a softener, and an AE agent. Consisting of a water-soluble resin binder comprising a, the mortar of the mixed elastic mortar is made of thermal insulation cement using expanded vermiculite, ultra-rough steel portlant cement, expanded cement consisting of calcium silicate and gypsum and calcium oxide, and ceramic powder. , The elastic resin of the mixed elastic mortar may be made of a thermoplastic elastomer prepared through a dynamic crosslinking reaction of polypropylene (PP) and ethylene propylene diene monomer (EPDM).
본 발명의 제1 관점에 있어서, 상기 수지바인더는 고형분의 함량이 20~25% 사이인 아크릴 수지와 고형분의 함량이 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 이루어지고, 상기 혼합 탄성 몰탈의 상기 몰탈은 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 이루어지고, 상기 혼합 탄성 몰탈의 상기 탄성 수지는 PP와 EPDM이 4~7:3~7의 비율의 비율로 혼합되어 이루어지며, 상기 혼합 탄성 몰탈에서 몰탈과 탄성 수지는 1:10의 비율로 혼합되는 것이 바람직하다.In the first aspect of the present invention, the resin binder is formed by mixing an acrylic resin having a solid content of between 20 and 25% and a urethane resin having a solid content of between 38 and 45% at a mixing ratio of 7:3, respectively. Water-soluble elastic acrylic-urethane mixed emulsion resin 82~89wt%, dispersant 1~2wt%, defoaming agent 0.5~1wt%, antifreeze agent 1~2wt%, UV blocker 1~2wt%, surfactant 4~7wt%, softener 2~ It consists of 4wt%, AE agent 0.5~1wt%, and the mortar of the mixed elastic mortar is 40-50wt% of thermal insulation cement using expanded vermiculite, 20-30wt% of portlant cement, calcium silicate and gypsum and calcium oxide. Consists of 20 to 30 wt% of expanded cement and 5 to 10 wt% of ceramic powder, and the elastic resin of the mixed elastic mortar is made by mixing PP and EPDM in a ratio of 4 to 7: 3 to 7, and the mixing In the elastic mortar, the mortar and the elastic resin are preferably mixed in a ratio of 1:10.
본 발명의 제2 관점에 따르면, 상기한 제1 관점에 따른 도막형 바닥재용 조성물을 포함하는 것을 특징으로 하는 도막형 바닥재가 제공된다.According to a second aspect of the present invention, there is provided a coating-type flooring comprising the composition for coating-type flooring according to the first aspect.
본 발명의 제3 관점에 따르면, 도막형 바닥재로서, 도막형 바닥재가 시공될 시공면에 접착용 프라이머가 도포 형성되는 수지바인더 프라이머층; 수지바인더, 및 혼합 탄성 몰탈로 이루어져 상기 수지바인더 프라이머층에 도포 형성되는 수지-몰탈 혼합층; 및 상기 수지-몰탈 혼합층의 상면에 도포 형성되는 코팅층;을 포함하고, 상기 수지바인더 프라이머층은 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지, 유동화제, 소포제, 속경제, 동결방지제, 및 팽창제의 조성으로 이루어지고, 상기 수지-몰탈 혼합층의 상기 수지바인더는 아크릴 수지와 우레탄 수지가 합성되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, 및 AE제를 포함하는 수용성 수지바인더로 이루어지고, 상기 혼합 탄성 몰탈은, 팽창질석을 사용한 단열시멘트, 초조강 포틀랜트 시멘트, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트, 세라믹 분말을 포함하여 이루어지는 몰탈, 및 PP(polypropylene)와 EPDM(Ethylene Propylene Diene monomer)의 동적 가교 반응을 통해 제조된 열가소성 엘라스토머로 이루어지는 탄성수지로 이루어지며, 상기 코팅층은 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 연화제, 차열안료, 및 증점제의 조성으로 이루어지는 수용성 차열 칼라 코팅층인 것을 특징으로 하는 탄성을 갖는 도막형 바닥재가 제공된다.According to a third aspect of the present invention, there is provided a coating-type flooring material, comprising: a resin binder primer layer coated with an adhesive primer on a construction surface on which the coating-type flooring material is to be installed; A resin binder, and a resin-mortar mixed layer formed by coating on the resin binder primer layer made of a mixed elastic mortar; And a coating layer formed by coating on the upper surface of the resin-mortar mixture layer, wherein the resin binder primer layer comprises a composition of a water-soluble acrylic emulsion resin formed of an acrylic resin, a fluidizing agent, a defoaming agent, a fast economy, an antifreeze agent, and an expanding agent. The resin binder of the resin-mortar mixed layer contains a water-soluble elastic acrylic-urethane mixed emulsion resin formed by synthesizing an acrylic resin and a urethane resin, a dispersant, an antifoaming agent, an antifreeze agent, a UV blocker, a surfactant, a softener, and an AE agent. Consisting of a water-soluble resin binder containing, the mixed elastic mortar is, the thermal insulation cement using expanded vermiculite, portland cement made of ultra-rough steel, expanded cement composed of calcium silicate and gypsum and calcium oxide, mortar including ceramic powder, and PP It is made of an elastic resin made of a thermoplastic elastomer prepared through a dynamic crosslinking reaction of (polypropylene) and EPDM (Ethylene Propylene Diene monomer), and the coating layer is a water-soluble elastic acrylic-urethane mixed emulsion resin, a dispersant, an antifoaming agent, an antifreeze agent, and a UV blocking agent. , A softening agent, a heat shielding pigment, and a thickener, and a water-soluble heat shielding color coating layer having elasticity.
본 발명의 제3 관점에 있어서, 상기 수지바인더 프라이머층은 고형분의 함량이 17~20% 사이인 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지 90~95wt%, 유동화제 1~2wt%, 소포제 0.5~1wt%, 속경제 1~5wt%, 동결방지제 1~2wt%, 팽창제 6.5~8wt%의 조성으로 이루어지고, 상기 수지-몰탈 혼합층의 상기 수지 바인더는 고형분의 함량이 20~25% 사이인 아크릴 수지와 고형분의 함량이 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 이루어지고, 상기 혼합 탄성 몰탈의 상기 몰탈은 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 이루어지고, 상기 혼합 탄성 몰탈의 상기 탄성 수지는 PP와 EPDM이 4~7:3~7의 비율의 비율로 혼합되어 이루어지고, 상기 혼합 탄성 몰탈에서 상기 몰탈과 탄성 수지는 1:10의 비율로 혼합되어 이루어지며, 상기 코팅층은 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 8:2의 배합비율로 배합되어 형성된 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 60~70wt%, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 차열안료 20~30wt%, 증점제 2~3wt%로 구성된 차열 안료를 이용하여 도포된 수용성 차열 칼라 코팅층으로 이루어지는 것이 바람직하다.In a third aspect of the present invention, the resin binder primer layer is 90 to 95 wt% of a water-soluble acrylic emulsion resin formed of an acrylic resin having a solid content of between 17 to 20%, a fluidizing agent 1 to 2 wt%, and an antifoaming agent 0.5 to 1 wt% , Fast economy 1~5wt%, freeze inhibitor 1~2wt%, expansion agent 6.5~8wt%, and the resin binder of the resin-mortar mixture layer has a solid content of between 20 and 25% acrylic resin and solid content A water-soluble elastic acrylic-urethane mixture emulsion resin formed by mixing urethane resins with a content of between 38 to 45% at a mixing ratio of 7:3, 82 to 89 wt%, dispersant 1 to 2 wt%, antifoaming agent 0.5 to 1 wt%, freezing Consisting of 1 to 2 wt% inhibitor, 1 to 2 wt% UV blocker, 4 to 7 wt% surfactant, 2 to 4 wt% softener, 0.5 to 1 wt% AE agent, the mortar of the mixed elastic mortar is an insulating cement using expanded vermiculite 40-50wt%, ultra-crude steel portland cement 20-30wt%, expanded cement consisting of calcium silicate, gypsum and calcium oxide 20-30wt%, ceramic powder 5-10wt%, the elastic resin of the mixed elastic mortar PP and EPDM are mixed in a ratio of 4-7:3-7, and in the mixed elastic mortar, the mortar and elastic resin are mixed in a ratio of 1:10, and the coating layer has a solid content A water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin between 35 to 44% and a urethane resin between 38 to 45% at a mixing ratio of 8:2, 60 to 70 wt%, dispersant 1 to 2 wt%, antifoam 1 It is a water-soluble heat shielding color coating layer applied using a heat shielding pigment composed of ~2wt%, freeze inhibitor 1~2wt%, UV blocker 1~2wt%, softener 2~4wt%, heat shielding pigment 20~30wt%, thickener 2~3wt%. It is preferably made.
본 발명에 따른 탄성을 갖는 도막형 바닥재용 조성물, 및 이를 포함하는 도막형 바닥재에 의하면, 탄성을 가져 충격 흡수를 필요로 하는 다양한 분야에 적용할 수 있는 효가가 있다.According to the composition for a coating-type flooring material having elasticity according to the present invention, and a coating-type flooring material including the same, there is an effect that it can be applied to various fields requiring shock absorption due to its elasticity.
또한, 본 발명은 단열 효과, 크랙방지 효과 및 미끄럼방지 효과도 제공할 수 있어 기능성이 현저히 증대된 바닥재를 제공할 수 있는 효과가 있다.In addition, the present invention has the effect of providing a flooring material having a remarkably increased functionality since it can provide a heat insulation effect, a crack prevention effect, and an anti-slip effect.
본 발명의 효과는 이상에서 언급된 것들에 한정되지 않으며, 언급되지 아니한 다른 해결과제들은 아래의 기재로부터 당업자에게 명확하게 이해되어 질 수 있을 것이다.The effects of the present invention are not limited to those mentioned above, and other problems that are not mentioned will be clearly understood by those skilled in the art from the following description.
도 1은 본 발명에 따른 탄성을 갖는 도막형 바닥재의 구성을 도식화하여 나타내는 도면이다.
도 2는 본 발명에 따른 탄성을 갖는 도막형 바닥재를 이용한 도막형 바닥재의 시공 방법의 일 실시 예를 나타내는 플로차트이다.1 is a diagram schematically showing the configuration of a coating-type flooring material having elasticity according to the present invention.
2 is a flowchart showing an embodiment of a method of constructing a coating-type flooring material using a coating-type flooring material having elasticity according to the present invention.
본 발명의 추가적인 목적들, 특징들 및 장점들은 다음의 상세한 설명 및 첨부도면으로부터 보다 명료하게 이해될 수 있다. Additional objects, features, and advantages of the present invention may be more clearly understood from the following detailed description and accompanying drawings.
본 발명의 상세한 설명에 앞서, 본 발명은 다양한 변경을 도모할 수 있고, 여러 가지 실시 예를 가질 수 있는바, 아래에서 설명되고 도면에 도시된 예시들은 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.Prior to the detailed description of the present invention, the present invention is capable of various modifications and various embodiments, and the examples described below and shown in the drawings are intended to limit the present invention to specific embodiments. It should be understood as including all changes, equivalents, and substitutes included in the spirit and scope of the present invention.
어떤 구성요소가 다른 구성요소에 "연결되어" 있다거나 "접속되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 "직접 연결되어" 있다거나 "직접 접속되어" 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.When a component is referred to as being "connected" or "connected" to another component, it is understood that it may be directly connected or connected to the other component, but other components may exist in the middle. Should be. On the other hand, when a component is referred to as being "directly connected" or "directly connected" to another component, it should be understood that there is no other component in the middle.
본 명세서에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도는 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terms used in the present specification are only used to describe specific embodiments, and are not intended to limit the present invention. Singular expressions include plural expressions unless the context clearly indicates otherwise. In this specification, terms such as "comprise" or "have" are intended to designate the presence of features, numbers, steps, actions, components, parts, or a combination thereof described in the specification, but one or more other features. It is to be understood that the presence or addition of elements or numbers, steps, actions, components, parts, or combinations thereof, does not preclude in advance.
또한, 명세서에 기재된 "...부", "...유닛", "...모듈" 등의 용어는 적어도 하나의 기능이나 동작을 처리하는 단위를 의미하며, 이는 하드웨어나 소프트웨어 또는 하드웨어 및 소프트웨어의 결합으로 구현될 수 있다.In addition, terms such as "... unit", "... unit", and "... module" described in the specification mean a unit that processes at least one function or operation, which is hardware, software, or hardware and It can be implemented as a combination of software.
또한, 첨부 도면을 참조하여 설명함에 있어, 도면 부호에 관계없이 동일한 구성 요소는 동일한 참조부호를 부여하고 이에 대한 중복되는 설명은 생략하기로 한다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.In addition, in the description with reference to the accompanying drawings, the same reference numerals are assigned to the same components regardless of the reference numerals, and redundant descriptions thereof will be omitted. In describing the present invention, when it is determined that a detailed description of related known technologies may unnecessarily obscure the subject matter of the present invention, a detailed description thereof will be omitted.
이하, 본 발명의 바람직한 실시 예에 따른 탄성을 갖는 도막형 바닥재용 조성물, 및 이를 포함하는 도막형 바닥재에 대하여 첨부 도면을 참조하여 상세히 설명한다.Hereinafter, a composition for a coating-type flooring material having elasticity and a coating-type flooring material including the same according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.
먼저, 본 발명에 따른 탄성을 갖는 도막형 바닥재용 조성물에 대하여 상세히 설명한다.First, the elastic coating-type flooring composition according to the present invention will be described in detail.
본 발명에 따른 탄성을 갖는 도막형 바닥재용 조성물은, 크게 수지바인더 및 혼합 탄성 몰탈을 포함하며, 상기 혼합 탄성 몰탈은 몰탈 및 탄성 수지를 포함하는 것을 특징으로 한다.The composition for a coating film-type flooring material having elasticity according to the present invention largely includes a resin binder and a mixed elastic mortar, and the mixed elastic mortar includes a mortar and an elastic resin.
상기 수지바인더는 아크릴 수지와 우레탄 수지가 합성되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, AE제를 포함하는 수용성 수지바인더로 이루어진다.The resin binder is made of a water-soluble resin binder containing a water-soluble elastic acrylic-urethane mixed emulsion resin formed by synthesizing an acrylic resin and a urethane resin, a dispersant, a defoaming agent, an antifreeze agent, a UV blocker, a surfactant, a softener, and an AE agent.
여기에서, 상기 수지바인더는 고형분의 함량이 20~25% 사이인 아크릴 수지와 고형분의 함량이 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 이루어질 수 있다.Here, the resin binder is a water-soluble elastic acrylic-urethane formed by mixing an acrylic resin having a solid content of between 20 and 25% and a urethane resin having a solid content of between 38 and 45% at a mixing ratio of 7:3, respectively. Mixed emulsion resin 82~89wt%, dispersant 1~2wt%, antifoam 0.5~1wt%, freeze inhibitor 1~2wt%, UV blocker 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5 It may be made of ~1wt%.
상기 혼합 탄성 몰탈에서 상기 몰탈은 팽창질석을 사용한 단열시멘트, 초조강 포틀랜트 시멘트, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트, 세라믹 분말을 포함하여 이루어지며, 상기 탄성 수지는 PP(polypropylene)와 EPDM(Ethylene Propylene Diene monomer)의 동적 가교 반응을 통해 제조된 열가소성 엘라스토머로 이루어진다.In the mixed elastic mortar, the mortar is made of insulating cement using expanded vermiculite, ultra rough steel portland cement, expanded cement composed of calcium silicate, gypsum and calcium oxide, and ceramic powder, and the elastic resin includes polypropylene (PP) and It consists of a thermoplastic elastomer prepared through a dynamic crosslinking reaction of EPDM (Ethylene Propylene Diene monomer).
상기 몰탈은 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 이루어질 수 있다.The mortar may be made of 40 to 50 wt% of thermal insulation cement using expanded vermiculite, 20 to 30 wt% of super crude steel portland cement, 20 to 30 wt% of expanded cement composed of calcium silicate, gypsum and calcium oxide, and 5 to 10 wt% of ceramic powder. .
그리고 상기 탄성 수지는 PP와 EPDM이 4~7:3~7의 비율, 바람직하게는 6:4의 비율로 혼합되는 것이 바람직하다.In addition, the elastic resin is preferably mixed with PP and EPDM in a ratio of 4-7:3-7, preferably in a ratio of 6:4.
상기 혼합 탄성 몰탈에서 몰탈과 탄성 수지는 1:10의 비율로 혼합되는 것이 바람직하다.In the mixed elastic mortar, the mortar and the elastic resin are preferably mixed in a ratio of 1:10.
이와 같이 구성되는 탄성 수지는 가공시간이 짧으면서 배합 공정이 용이하고, 스크랩 재사용으로 인한 원가 절감 효과와 비중이 낮아서 경량화가 가능한 것으로, 유연성과 탄성회복력 등의 성능 면에서는 고무와 근접한 기능을 가지면서 가공 면에서는 고무보다 월등히 우수하다.The elastic resin composed in this way has a short processing time, easy compounding process, and is capable of reducing cost due to scrap reuse and low specific gravity, so it can be lightweight.In terms of performance such as flexibility and elastic recovery, it has a function close to that of rubber. It is far superior to rubber in terms of processing.
다음으로, 상기와 같이 구성되는 탄성을 갖는 도막형 바닥재용 조성물을 포함하는 도막형 바닥재에 대하여 도 1을 참조하여 설명한다. 아래 도막형 바닥재에 대한 설명에서 앞서 도막형 바닥재용 조성물에서 설명된 내용은 상세한 설명의 간략화와 발명의 명확화를 위하여 그에 대한 상세한 설명은 생략하거나 간략히 설명한다.Next, a coating-type flooring material comprising the composition for a coating-type flooring material having elasticity configured as described above will be described with reference to FIG. 1. In the description of the coating-type flooring material below, the details described in the coating-type flooring composition will be omitted or briefly described in order to simplify the detailed description and clarify the invention.
도 1은 본 발명에 따른 탄성을 갖는 도막형 바닥재의 구성을 도식화하여 나타내는 도면이다.1 is a diagram schematically showing the configuration of a coating-type flooring material having elasticity according to the present invention.
본 발명에 따른 탄성을 갖는 도막형 바닥재는, 도 1에 나타낸 바와 같이, 도막형 바닥재가 시공될 시공면에 접착용 프라이머가 도포 형성되는 수지바인더 프라이머층(110); 상기 수지바인더 프라이머층(120)의 상면에 도포 형성되는 수지-몰탈 혼합층(120); 및 상기 수지-몰탈 혼합층(120)의 상면에 도포 형성되는 코팅층(130);을 포함한다.A coating-type flooring material having elasticity according to the present invention includes, as shown in FIG. 1, a resin
상기 수지바인더 프라이머층(110)은 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지, 유동화제, 소포제, 속경제, 동결방지제, 및 팽창제의 조성을 포함하여 이루어질 수 있다.The resin
구체적으로, 상기 수지바인더 프라이머층(110)은 고형분의 함량이 17~20% 사이인 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지 90~95wt%, 유동화제 1~2wt%, 소포제 0.5~1wt%, 속경제 1~5wt%, 동결방지제 1~2wt%, 팽창제 6.5~8wt%의 조성으로 구성될 수 있다.Specifically, the resin
다음으로, 상기 수지-몰탈 혼합층(120)은 앞서 설명한 바와 같이, 수지바인더 및 혼합 탄성 몰탈을 포함하며, 상기 혼합 탄성 몰탈은 몰탈 및 탄성 수지를 포함하여 이루어지며, 이들의 세부적인 조성과 조성비에 대한 설명은 생략한다.Next, as described above, the resin-mortar
다음으로, 상기 코팅층(130)은 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 연화제, 차열안료, 및 증점제로 구성된 차열 안료를 이용하여 도포된 수용성 차열 칼라 코팅층으로 이루어질 수 있다.Next, the
구체적으로, 상기 코팅층(130)은 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 8:2의 배합비율로써 배합하여 형성된 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 60~70wt%, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 차열안료 20~30wt%, 증점제 2~3wt%로 구성된 차열 안료를 이용하여 도포된 수용성 차열 칼라 코팅층으로 이루어질 수 있다.Specifically, the
한편, 본 발명에 따른 탄성을 갖는 도막형 바닥재의 시공 방법으로 인도(人道)에 시공하는 예를 도 2를 참조하여 상세히 설명한다. 도 2는 본 발명에 따른 탄성을 갖는 도막형 바닥재를 이용한 도막형 바닥재의 시공 방법의 일 실시 예를 나타내는 플로차트이다.On the other hand, an example of construction on the sidewalk by the method of constructing a coating-type flooring material having elasticity according to the present invention will be described in detail with reference to FIG. 2. 2 is a flowchart showing an embodiment of a method of constructing a coating-type flooring material using a coating-type flooring material having elasticity according to the present invention.
본 발명에 따른 탄성을 갖는 도막형 바닥재의 시공 방법은, 인도에 시공하는 예로서, 도 2에 나타낸 바와 같이, 인도의 시공면(B)에 대한 전처리를 수행하는 시공면 전처리 단계(S110); 시공면(B)에 수지바인더 프라이머 조성물을 도포하여 수지바인더 프라이머층을 형성하는 수지바인더 프라이머층 형성 단계(S120); 상기 수지바인더 프라이머층에 혼합 탄성 몰탈을 도포하여 1차 수지-몰탈 혼합층을 형성하는 1차 수지-몰탈 혼합층 형성 단계(S130); 상기 1차 수지-몰탈 혼합층 위에 패턴무늬부재를 설치하고 수지바인더와 차열안료 및 혼합 탄성 몰탈을 도포하여 2차 수지-몰탈 혼합층을 형성하는 2차 수지-몰탈 혼합층 형성 단계(S140); 및 패턴무늬부재를 제거하고 2차 수지-몰탈 혼합층 상면에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 코팅층 형성 단계(S150);를 포함한다.Construction method of a coating-type flooring material having elasticity according to the present invention, as an example of construction on the sidewalk, as shown in Figure 2, the construction surface pretreatment step (S110) of performing a pretreatment on the construction surface (B) of the sidewalk; A resin binder primer layer forming step (S120) of forming a resin binder primer layer by applying a resin binder primer composition to the construction surface (B); Forming a primary resin-mortar mixed layer by applying a mixed elastic mortar to the resin binder primer layer (S130); Forming a secondary resin-mortar mixture layer by installing a patterned member on the primary resin-mortar mixture layer and applying a resin binder, a heat shielding pigment, and a mixed elastic mortar to form a secondary resin-mortar mixture layer (S140); And removing the patterned member and applying a water-soluble transparent coating agent on the upper surface of the secondary resin-mortar mixture layer to form a water-soluble transparent coating layer (S150).
상기 시공면 전처리 단계(S110)는 시공면의 물청소 단계와, 시공면의 크랙을 그라인더로 V커팅을 하고 수지바인더 및 혼합 탄성 몰탈로 시공면이 평탄해질 때까지 채우는 바닥면 평탄화 단계, 및 시공면의 주변 시설물이 오염되지 않도록 테이프로 보완하는 단계를 포함할 수 있다.The construction surface pretreatment step (S110) includes a water cleaning step on the construction surface, a floor surface flattening step in which V-cutting the cracks on the construction surface with a grinder and filling the construction surface with a resin binder and a mixed elastic mortar until the construction surface is flat, and construction It may include the step of supplementing with tape so that the surrounding facilities of the surface are not contaminated.
상기 수지바인더 프라이머층 형성 단계(S120)는 앞서 설명한 수지바인더 프라이머층 조성물을 시공면에 도포하여 형성하게 된다.The resin binder primer layer forming step (S120) is formed by applying the resin binder primer layer composition described above to the construction surface.
상기 1차 수지-몰탈 혼합층 형성 단계(S130)은 앞서 설명한 수지바인더와 혼합 탄성 몰탈을 사용하되, 수용성 수지바인더 9~10(L)에 혼합 탄성 몰탈 20(Kg)의 배합비율로서 배합하여 사용한다.In the step of forming the first resin-mortar mixed layer (S130), the resin binder and the mixed elastic mortar are used as described above, but the mixture is used as the mixing ratio of the mixed elastic mortar 20 (Kg) to the water-soluble resin binder 9-10 (L). .
상기 2차 수지-몰탈 혼합층 형성 단계(S140)는 수지바인더와 혼합 탄성 몰탈을 사용하되, 수용성 수지바인더 6~8(L)에 혼합 탄성 몰탈 20(Kg)과 차열안료 0.2(Kg)의 배합비율로 배합하여 사용한다.In the step of forming the secondary resin-mortar mixed layer (S140), a resin binder and a mixed elastic mortar are used, but the mixing ratio of the mixed elastic mortar 20 (Kg) and the heat shielding pigment 0.2 (Kg) in the water-soluble resin binder 6-8 (L) It is mixed and used.
여기에서, 상기 패턴무늬부재는 다양한 무늬가 연출되도록 천공영역과 비천공영역으로 구분되는 종이 등으로 구성될 수 있고, 종이로 된 테이프로 패턴무늬를 연출할 수도 있다. 패터무늬부재를 이용함에 따라 작업성을 향상시킬 수 있고, 다양한 무늬와 디자인을 쉽고 정교하게 표현할 수 있게 된다.Here, the patterned pattern member may be composed of paper or the like divided into a perforated area and a non-perforated area so that various patterns are displayed, and a patterned pattern may be produced using a tape made of paper. By using the patterned member, workability can be improved, and various patterns and designs can be easily and precisely expressed.
상기 코팅층 형성 단계(S150)는 앞서 설명한 수용성 투명 코팅제를 이용하여 수용성 투명 코팅층을 형성하는데, 복수 회차로 하여 코팅하는 것이 바람직하다. 이와 같이 복수 회차로 코팅층을 형성하는 것은 수용성 차열 칼라 코팅층을 1차로 마감 처리하면 코팅제의 침투력이 있어 바닥 상태에 따라서 침투가 많이 되고 적게 되는 부분이 발생되어 침투가 많이 된 부분은 색상이 약하고 침투가 적게 되는 부분은 색상이 진하여 얼룩이 생기는 현상이 발생할 수 있으므로 2차 작업을 해주어야만 색상의 얼룩이 없어지고 마모성이 강해지기 때문이다.In the coating layer forming step (S150), a water-soluble transparent coating layer is formed using the water-soluble transparent coating agent described above, and it is preferable to coat a plurality of times. Forming the coating layer multiple times in this way is that if the water-soluble heat-shielding color coating layer is first finished, the coating agent has penetrating power, so depending on the condition of the floor, there is a lot of penetration and less penetration. This is because the color of the part that is reduced may be dark and stains may occur, so that color stains disappear and abrasion properties become strong only when the secondary work is performed.
한편, 본 발명에 따른 탄성을 갖는 도막형 바닥재의 시공 방법은, 인도 이외에 자전거 도로, 옹벽, 농구장이나 놀이터 등의 체육근린시설의 바닥에 적용할 수도 있다.On the other hand, the construction method of a coating-type flooring material having elasticity according to the present invention may be applied to the floor of a sports neighborhood facility such as a bicycle road, a retaining wall, a basketball court or a playground in addition to the sidewalk.
이상에서 설명한 바와 같은 본 발명에 따른 탄성을 갖는 도막형 바닥재용 조성물, 및 이를 포함하는 도막형 바닥재에 의하면, 탄성을 가져 충격 흡수를 필요로 하는 다양한 분야에 적용할 수 있으며, 나아가 단열 효과, 크랙방지 효과 및 미끄럼방지 효과도 제공할 수 있어 기능성이 현저히 증대된 바닥재를 제공할 수 있는 이점이 있다.According to the composition for a coating film-type flooring material having elasticity according to the present invention as described above, and a coating film-type flooring material including the same, it has elasticity and can be applied to various fields requiring shock absorption, and furthermore, heat insulation effect, crack There is an advantage of providing a flooring material with remarkably increased functionality since it can also provide an anti-slip effect and an anti-slip effect.
상기한 바와 같은 실시 예들은 비록 한정된 도면에 의해 설명되었으나, 해당 기술분야에서 통상의 지식을 가진 자라면 상기를 기초로 다양한 기술적 수정 및 변형을 적용할 수 있다. 예를 들어, 설명된 기술들이 설명된 방법과 다른 순서로 수행되거나, 및/또는 설명된 시스템, 구조, 장치, 회로 등의 구성요소들이 설명된 방법과 다른 형태로 결합 또는 조합되거나, 다른 구성요소 또는 균등물에 의하여 대치되거나 치환되더라도 적절한 결과가 달성될 수 있다.Although the above-described embodiments have been described by the limited drawings, a person of ordinary skill in the art can apply various technical modifications and variations based on the above. For example, the described techniques are performed in a different order from the described method, and/or components such as a system, structure, device, circuit, etc. described are combined or combined in a form different from the described method, or other components Alternatively, even if substituted or substituted by an equivalent, an appropriate result can be achieved.
본 명세서에서 설명되는 실시 예와 첨부된 도면은 본 발명에 포함되는 기술적 사상의 일부를 예시적으로 설명하는 것에 불과하다. 따라서, 본 명세서에 개시된 실시 예는 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이므로, 이러한 실시 예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아님은 자명하다. 본 발명의 명세서 및 도면에 포함된 기술적 사상의 범위 내에서 당업자가 용이하게 유추할 수 있는 변형 예와 구체적인 실시 예는 모두 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The embodiments described in the present specification and the accompanying drawings are merely illustrative of some of the technical ideas included in the present invention. Accordingly, it is obvious that the embodiments disclosed in the present specification are not intended to limit the technical idea of the present disclosure, but to explain the technical idea, and thus the scope of the technical idea of the present disclosure is not limited by these embodiments. Modification examples and specific embodiments that can be easily inferred by those skilled in the art within the scope of the technical idea included in the specification and drawings of the present invention should be interpreted as being included in the scope of the present invention.
110: 수지바인더 프라이머층
120: 수지-몰탈 혼합층
130: 코팅층
B: 시공면
S110: 시공면 전처리 단계
S120: 수지바인더 프라이머층 형성 단계
S130, S140: 수지-몰탈 혼합층 형성 단계
S150: 코팅층 형성 단계110: resin binder primer layer
120: resin-mortar mixed layer
130: coating layer
B: Construction surface
S110: Construction surface pretreatment step
S120: Resin binder primer layer formation step
S130, S140: resin-mortar mixed layer formation step
S150: coating layer forming step
Claims (6)
수지바인더, 및 혼합 탄성 몰탈을 포함하며,
상기 혼합 탄성 몰탈은 몰탈 및 탄성 수지를 포함하는 것을 특징으로 하는
탄성을 갖는 도막형 바닥재용 조성물.
In the composition of the coating-type flooring material,
It includes a resin binder, and a mixed elastic mortar,
The mixed elastic mortar, characterized in that comprising a mortar and an elastic resin
A coating-type flooring composition having elasticity.
상기 수지바인더는 아크릴 수지와 우레탄 수지가 합성되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, 및 AE제를 포함하는 수용성 수지바인더로 이루어지고,
상기 혼합 탄성 몰탈의 상기 몰탈은 팽창질석을 사용한 단열시멘트, 초조강 포틀랜트 시멘트, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트, 세라믹 분말을 포함하여 이루어지며,
상기 혼합 탄성 몰탈의 상기 탄성 수지는 PP(polypropylene)와 EPDM(Ethylene Propylene Diene monomer)의 동적 가교 반응을 통해 제조된 열가소성 엘라스토머로 이루어지는 것을 특징으로 하는
탄성을 갖는 도막형 바닥재용 조성물.
The method of claim 1,
The resin binder is made of a water-soluble resin binder comprising a water-soluble elastic acrylic-urethane mixed emulsion resin formed by synthesizing an acrylic resin and a urethane resin, a dispersant, a defoamer, an antifreeze agent, a UV blocker, a surfactant, a softener, and an AE agent. ,
The mortar of the mixed elastic mortar comprises insulating cement using expanded vermiculite, ultra rough steel portland cement, expanded cement composed of calcium silicate and gypsum and calcium oxide, and ceramic powder,
The elastic resin of the mixed elastic mortar is made of a thermoplastic elastomer prepared through a dynamic crosslinking reaction of polypropylene (PP) and ethylene propylene diene monomer (EPDM).
A coating-type flooring composition having elasticity.
상기 수지바인더는 고형분의 함량이 20~25% 사이인 아크릴 수지와 고형분의 함량이 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 이루어지고,
상기 혼합 탄성 몰탈의 상기 몰탈은 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 이루어지고,
상기 혼합 탄성 몰탈의 상기 탄성 수지는 PP와 EPDM이 4~7:3~7의 비율의 비율로 혼합되어 이루어지며,
상기 혼합 탄성 몰탈에서 몰탈과 탄성 수지는 1:10의 비율로 혼합되는 것을 특징으로 하는
탄성을 갖는 도막형 바닥재용 조성물.
The method of claim 2,
The resin binder is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin with a solid content of between 20 and 25% and a urethane resin with a solid content of between 38 and 45% at a mixing ratio of 7:3, respectively. 82~89wt%, dispersant 1~2wt%, antifoam 0.5~1wt%, freeze inhibitor 1~2wt%, UV blocker 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5~1wt% Consists of,
The mortar of the mixed elastic mortar is 40 to 50 wt% of thermal insulation cement using expanded vermiculite, 20 to 30 wt% of ultra rough steel portland cement, 20 to 30 wt% of expanded cement consisting of calcium silicate, gypsum and calcium oxide, and 5 to 10 wt of ceramic powder Consists of %,
The elastic resin of the mixed elastic mortar is made by mixing PP and EPDM in a ratio of 4-7:3-7,
In the mixed elastic mortar, the mortar and the elastic resin are mixed in a ratio of 1:10.
A coating-type flooring composition having elasticity.
도막형 바닥재.It characterized in that it comprises a coating-type flooring composition according to any one of claims 1 to 3
Coating type flooring.
도막형 바닥재가 시공될 시공면에 접착용 프라이머가 도포 형성되는 수지바인더 프라이머층;
수지바인더, 및 혼합 탄성 몰탈로 이루어져 상기 수지바인더 프라이머층에 도포 형성되는 수지-몰탈 혼합층; 및
상기 수지-몰탈 혼합층의 상면에 도포 형성되는 코팅층;을 포함하고,
상기 수지바인더 프라이머층은 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지, 유동화제, 소포제, 속경제, 동결방지제, 및 팽창제의 조성으로 이루어지고,
상기 수지-몰탈 혼합층의 상기 수지바인더는 아크릴 수지와 우레탄 수지가 합성되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, 및 AE제를 포함하는 수용성 수지바인더로 이루어지고,
상기 혼합 탄성 몰탈은, 팽창질석을 사용한 단열시멘트, 초조강 포틀랜트 시멘트, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트, 세라믹 분말을 포함하여 이루어지는 몰탈, 및 PP(polypropylene)와 EPDM(Ethylene Propylene Diene monomer)의 동적 가교 반응을 통해 제조된 열가소성 엘라스토머로 이루어지는 탄성수지로 이루어지며,
상기 코팅층은 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지, 분산제, 소포제, 동결방지제, UV차단제, 연화제, 차열안료, 및 증점제의 조성으로 이루어지는 수용성 차열 칼라 코팅층인 것을 특징으로 하는
탄성을 갖는 도막형 바닥재.
As a coating type flooring,
A resin binder primer layer on which an adhesive primer is applied and formed on a construction surface on which a coating-type flooring material is to be installed;
A resin binder, and a resin-mortar mixed layer formed by coating on the resin binder primer layer made of a mixed elastic mortar; And
Including; a coating layer formed by coating on the upper surface of the resin-mortar mixed layer,
The resin binder primer layer is composed of a composition of a water-soluble acrylic emulsion resin formed of acrylic resin, a fluidizing agent, a defoaming agent, a fast economy, an antifreeze agent, and an expanding agent,
The resin binder of the resin-mortar mixed layer comprises a water-soluble elastic acrylic-urethane mixed emulsion resin formed by synthesizing an acrylic resin and a urethane resin, a dispersant, an antifoaming agent, an antifreeze agent, a UV blocker, a surfactant, a softener, and an AE agent. It is made of a water-soluble resin binder,
The mixed elastic mortar is a thermal insulation cement using expanded vermiculite, a super crude steel portlant cement, an expanded cement composed of calcium silicate, gypsum, and calcium oxide, a mortar including ceramic powder, and polypropylene (PP) and ethylene propylene diene (EPDM). monomer), made of an elastic resin made of a thermoplastic elastomer prepared through a dynamic crosslinking reaction,
The coating layer is a water-soluble heat-shielding color coating layer comprising a composition of a water-soluble elastic acrylic-urethane mixed emulsion resin, a dispersant, an antifoaming agent, an antifreeze agent, a UV blocker, a softener, a heat shielding pigment, and a thickener.
A coating-type flooring material with elasticity.
상기 수지바인더 프라이머층은 고형분의 함량이 17~20% 사이인 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지 90~95wt%, 유동화제 1~2wt%, 소포제 0.5~1wt%, 속경제 1~5wt%, 동결방지제 1~2wt%, 팽창제 6.5~8wt%의 조성으로 이루어지고,
상기 수지-몰탈 혼합층의 상기 수지 바인더는 고형분의 함량이 20~25% 사이인 아크릴 수지와 고형분의 함량이 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 이루어지고,
상기 혼합 탄성 몰탈의 상기 몰탈은 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 이루어지고,
상기 혼합 탄성 몰탈의 상기 탄성 수지는 PP와 EPDM이 4~7:3~7의 비율의 비율로 혼합되어 이루어지고,
상기 혼합 탄성 몰탈에서 상기 몰탈과 탄성 수지는 1:10의 비율로 혼합되어 이루어지며,
상기 코팅층은 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 8:2의 배합비율로 배합되어 형성된 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 60~70wt%, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 차열안료 20~30wt%, 증점제 2~3wt%로 구성된 차열 안료를 이용하여 도포된 수용성 차열 칼라 코팅층으로 이루어지는 것을 특징으로 하는
탄성을 갖는 도막형 바닥재.The method of claim 5,
The resin binder primer layer is 90 to 95 wt% of a water-soluble acrylic emulsion resin formed of acrylic resin with a solid content of between 17 to 20%, fluidizing agent 1 to 2 wt%, antifoaming agent 0.5 to 1 wt%, fast economy 1 to 5 wt%, freezing Consisting of a composition of 1 to 2 wt% inhibitor and 6.5 to 8 wt% of expansion agent
The resin binder of the resin-mortar mixture layer is a water-soluble elasticity formed by mixing an acrylic resin with a solid content of between 20 and 25% and a urethane resin with a solid content of between 38 and 45% at a mixing ratio of 7:3, respectively. Acrylic-urethane mixed emulsion resin 82~89wt%, dispersant 1~2wt%, antifoaming agent 0.5~1wt%, freeze inhibitor 1~2wt%, UV blocker 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, It consists of 0.5 ~ 1wt% of the AE agent,
The mortar of the mixed elastic mortar is 40 to 50 wt% of thermal insulation cement using expanded vermiculite, 20 to 30 wt% of ultra rough steel portland cement, 20 to 30 wt% of expanded cement consisting of calcium silicate, gypsum and calcium oxide, and 5 to 10 wt of ceramic powder Consists of %,
The elastic resin of the mixed elastic mortar is made by mixing PP and EPDM in a ratio of 4-7:3-7,
In the mixed elastic mortar, the mortar and the elastic resin are mixed in a ratio of 1:10,
The coating layer is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin having a solid content of between 35 to 44% and a urethane resin having a solid content of between 38 to 45% at a mixing ratio of 8:2, a dispersant Using a heat shielding pigment composed of 1~2wt%, antifoam 1~2wt%, freeze inhibitor 1~2wt%, UV blocker 1~2wt%, softener 2~4wt%, heat shielding pigment 20~30wt%, thickener 2~3wt% Characterized in that consisting of a water-soluble heat shielding color coating layer applied
A coating-type flooring material with elasticity.