KR102136613B1 - Coating-type flooring, water-soluble resin binder of coating-type flooring, exclusive mortar of coating-type flooring, mixed composition of water-soluble resin binder of coating-type flooring and exclusive mortar, and construction method of coating-type flooring - Google Patents

Coating-type flooring, water-soluble resin binder of coating-type flooring, exclusive mortar of coating-type flooring, mixed composition of water-soluble resin binder of coating-type flooring and exclusive mortar, and construction method of coating-type flooring Download PDF

Info

Publication number
KR102136613B1
KR102136613B1 KR1020140015044A KR20140015044A KR102136613B1 KR 102136613 B1 KR102136613 B1 KR 102136613B1 KR 1020140015044 A KR1020140015044 A KR 1020140015044A KR 20140015044 A KR20140015044 A KR 20140015044A KR 102136613 B1 KR102136613 B1 KR 102136613B1
Authority
KR
South Korea
Prior art keywords
resin binder
coating
water
soluble
type flooring
Prior art date
Application number
KR1020140015044A
Other languages
Korean (ko)
Other versions
KR20150052722A (en
Inventor
희 석 김
김용균
강상우
Original Assignee
주식회사 에스윈
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 에스윈 filed Critical 주식회사 에스윈
Priority to KR1020140015044A priority Critical patent/KR102136613B1/en
Publication of KR20150052722A publication Critical patent/KR20150052722A/en
Application granted granted Critical
Publication of KR102136613B1 publication Critical patent/KR102136613B1/en

Abstract

본 발명의 일 측면은, 시공대상 블럭의 단열성 기능과 온도에 따른 유동으로 인한 크랙을 방지하는 기능과 미끄럼방지 기능을 동시에 갖는 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법을 제공하는 것에 있으며, 이러한 본 발명의 실시예에 따른 도막형 바닥재는, 시공대상 블럭의 상면에 접착용 프라이머가 도포 형성되는 수지바인더 프라이머층;과, 수지바인더 프라이머층의 상면에서 수지바인더 및 전용몰탈 혼합 조성물이 도포 형성되는 수지바인더 및 전용몰탈 혼합층;과, 수지바인더 및 전용몰탈 혼합층의 상면에 도포 형성되는 코팅층;을 포함하는 것을 특징으로 한다. One aspect of the present invention, a coating layer-type flooring material having a function of preventing the cracks due to the heat-insulating function and the temperature-dependent flow of the block to be constructed and the anti-slip function, a water-soluble resin binder of the coating-type flooring material, a dedicated mortar of the coating-type flooring material , It is to provide a construction method of a mixed composition of a water-soluble resin binder and a dedicated mortar of the coating-type flooring material and a coating-type flooring material, the coating-type flooring material according to an embodiment of the present invention has a primer for adhesion to the upper surface of a block to be constructed. Resin binder primer layer formed by coating; And, resin binder and dedicated mortar mixture layer is formed on the upper surface of the resin binder primer layer, and the coating layer is formed on the upper surface of the resin binder and dedicated mortar mixture layer. It characterized in that it contains a.

Description

도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법{Omitted}Coating-type flooring material, water-soluble resin binder of coating-type flooring, exclusive mortar of coating-type flooring, mixed composition of water-soluble resin binder and coating-type mortar of coating-type flooring, and construction method of coating-type flooring{Omitted}

본 발명은 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법에 관한 것으로, 더욱 상세하게는 시공대상 블럭의 단열성 기능과 온도에 따른 유동으로 인한 크랙을 방지하는 기능과 미끄럼방지 기능을 동시에 가지는 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법에 관한 것이다. The present invention relates to a coating composition-type flooring material, a water-soluble resin binder for a coating-type flooring material, a dedicated mortar for a coating-type flooring material, a mixed composition of a water-soluble resin binder and a dedicated mortar-type coating material, and a construction method for a coating-type flooring material, more specifically Water-soluble resin binder for coating-type flooring materials, coating-type flooring materials, anti-slip function for preventing cracks caused by flow and temperature-dependent flow of blocks to be constructed, and exclusive mortar for coating-type flooring materials, water-soluble resin for coating-type flooring materials It relates to a mixture composition of a binder and a dedicated mortar and a construction method of a coating-type flooring material.

최근에는 건강에 대한 관심의 증대로 시나 구청 등에서, 시간이 없는 시민들을 위해 집에서 가까운 곳에 체육시설, 공원, 산책로등의 근린생활공간을 조성하여 시민들에게 건강을 지키고 안락함과 편안함을 제공하고 있다. In recent years, with increasing interest in health, in the city and ward offices, for citizens who do not have time, nearby living spaces, such as sports facilities, parks, and walking trails, have been created to protect citizens and provide comfort and comfort.

이러한 근린생활공간에는 운동장이나 조깅로, 자전거도로 등이 주로 형성되는데, 시민들이 부상방지 및 인체 관절에의 충격완화, 비나 눈이 올 경우 투수, 도심미관등을 고려하여 종래 시멘트나 콘크리트, 쇄석층으로 형성된 기반층 상부에 별도의 바닥재를 더 형성시키고 있다. In these neighborhood living spaces, playgrounds, jogging paths, bicycle roads, etc. are mainly formed, but in the case of citizens' injury, prevention of injury to human joints, pitching in case of rain or snow, urban aesthetics, etc. A separate flooring material is further formed on the top of the base layer.

이러한 바닥재는 도심의 미관을 고려하여 여러가지 색깔이나 문양을 형성시키거나 시민들의 안정을 고려하여 표면이 거칠은 콘크리트나 아스콘 위에, 비나 눈이 올 경우 미끄럽지 않은 바닥재를 상기 기반층 상부에 포설하는 방법을 사용하고 있다. This flooring material is to form various colors or patterns in consideration of the aesthetics of the city center, or to consider the stability of citizens on a rough concrete or asphalt surface, and in the rain or snow, a method of laying a non-slip flooring on the top of the base layer I am using it.

이러한 종래의 바닥재는 콘크리트, 아스콘 또는 쇄석 등으로 형성된 기반층 상부에 우레탄 액상을 직접 도포하는 방식을 많이 사용하고 있는데, 이러한 종래의 도막형 바닥재는 다음과 같은 문제점이 있었다. The conventional flooring material uses a method of directly applying a urethane liquid onto the base layer formed of concrete, asphalt, or crushed stone, and this conventional coating-type flooring has the following problems.

먼저, 종래의 바닥재는 접착력이 떨어져 바닥재의 이탈이 심하게 생기고 크랙부분에 중량이 가해지면 크랙부분부터 이탈을 시작하여 점점 번져나가는 현상이 발생되며, 특히 콘크리트, 아스팔트 및 투수콘 등 구체바닥에서 크랙이 발생하면 쉽게 바닥재의 이탈이 시작되어 번져나가는 문제점이 있었다. First, in the conventional flooring material, the adhesive strength is poor and the separation of the flooring material is severe and the weight is applied to the cracking portion, which starts to detach from the cracking portion and gradually spreads, especially in concrete, asphalt and pitcher cones. When it occurred, there was a problem that the separation of the flooring material was easily started and spread.

또한, 종래의 바닥재는 주차장 바닥인 경우에 대다수가 에폭시로 도포되어 있는데, 이러한 에폭시 바닥은 통상 자량 타이어와 주차장 바닥 사이의 마찰계수가 크기 때문에 마찰음이 상당하게 발생하는 문제점이 있었다. In addition, most of the conventional flooring materials are coated with epoxy in the case of a parking lot floor, but these epoxy floors have a problem in that friction noise is considerably generated because the friction coefficient between the tire and the parking lot floor is large.

또한, 종래의 바닥재는 옥외 또는 옥상 주차장인 경우 더운 여름철에 차량에서 내리는 순간 숨이 막힐 정도의 더운 기운이 올라오는데, 이는 옥외 또는 옥상 주차장의 바닥재가 적외선을 받아 구체바닥이 열을 품고 있기 때문에 대기의 온도보다 바닥표면의 온도는 5~10℃ 정도 더 높기 때문에 발생하는 문제이다. In addition, in the case of an outdoor or rooftop parking lot, the hot air of breathtaking momentum rises as soon as you get off the vehicle in the hot summer season, because the flooring of the outdoor or rooftop parking lot receives heat and the concrete floor contains heat. This is a problem that occurs because the temperature of the floor surface is about 5~10℃ higher than the temperature of.

또한, 종래의 바닥재는 최상층이 코팅이 되어 있기 때문에 비가 왔을 때 상당히 미끄러워 사람들의 보행 또는 차량이 정지할 때 미끄러지는 문제점이 있었다. In addition, the conventional flooring is quite slippery when it rains because the top layer is coated, and thus there is a problem of slipping when people walk or the vehicle stops.

본 발명의 일 측면은, 시공대상 블럭의 단열성 기능과 온도에 따른 유동으로 인한 크랙을 방지하는 기능과 미끄럼방지 기능을 동시에 갖는 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법을 제공하는 것에 있다. One aspect of the present invention, a coating layer-type flooring material having a function of preventing the cracks due to the heat-insulating function and the temperature-dependent flow of the block to be constructed and the anti-slip function, a water-soluble resin binder of the coating-type flooring material, a dedicated mortar of the coating-type flooring material , To provide a mixed composition of a water-soluble resin binder and a dedicated mortar of the coating-type flooring material and a method of constructing the coating-type flooring material.

본 발명의 실시예에 따른 도막형 바닥재는, 시공대상 블럭의 상면에 접착용 프라이머가 도포 형성되는 수지바인더 프라이머층;과, 상기 수지바인더 프라이머층의 상면에서 수지바인더 및 전용몰탈 혼합 조성물이 도포 형성되는 수지바인더 및 전용몰탈 혼합층;과, 상기 수지바인더 및 전용몰탈 혼합층의 상면에 도포 형성되는 코팅층;을 포함하는 것을 특징으로 한다. Coating layer-type flooring according to an embodiment of the present invention, a resin binder primer layer is formed by applying a primer for adhesion to the upper surface of the block to be applied; And, a resin binder and a dedicated mortar mixture composition is formed on the upper surface of the resin binder primer layer It characterized in that it comprises; a resin binder and a dedicated mortar mixture layer; and a coating layer applied and formed on an upper surface of the resin binder and the exclusive mortar mixture layer.

또한, 수지바인더 및 전용몰탈 혼합 조성물은, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~87wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 수용성 수지바인더;와, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 전용몰탈;의 혼합 조성물로 구성되는 것을 특징으로 한다. In addition, the resin binder and the exclusive mortar mixture composition are water-soluble elastic acrylic-urethane formed by mixing acrylic resin having a solid content of 20-25% and urethane resin 38-45% at a mixing ratio of 7:3, respectively. Mixed emulsion resin 82~87wt%, dispersant 1~2wt%, antifoaming agent 0.5~1wt%, antifreeze agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5 Water-soluble resin binder containing ~1wt%; And, 40~50wt% of insulating cement using expanded vermiculite, 20~30wt% of super-steel portland cement, 20~30wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide It is characterized by being composed of a mixture composition of a dedicated mortar containing 5 to 10 wt% of powder.

또한, 수지바인더 프라이머층의 상면에서 콘크리트 표면을 평탄하게 하기 위해 도포 형성되는 제1수지바인더 및 전용몰탈 혼합층;과, 상기 제1수지바인더 및 전용몰탈 혼합층의 상면에서 두께를 보강하기 위해 도포 형성되는 제2수지바인더 및 전용몰탈 혼합층;을 포함하는 것을 특징으로 한다. In addition, a first resin binder and a dedicated mortar mixed layer applied to flatten the concrete surface on the upper surface of the resin binder primer layer; and, formed to be applied to reinforce the thickness on the upper surface of the first resin binder and the dedicated mortar mixed layer And a second resin binder and a dedicated mortar mixed layer.

또한, 코팅층은, 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 8:2의 배합비율로써 배합하여 형성된 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 60~70wt%, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 차열안료 20~30wt%, 증점제 2~3wt%로 구성된 차열 안료를 이용하여 도포된 수용성 차열 칼라 코팅층을 포함하는 것을 특징으로 한다. In addition, the coating layer is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin having a solids content of 35 to 44% and a urethane resin of 38 to 45% at a mixing ratio of 8:2, respectively, 60 to 70 wt% , Heat dissipation pigment consisting of 1~2wt% dispersant, 1~2wt% antifoaming agent, 1~2wt% antifreeze agent, 1~2wt% UV blocking agent, 2~4wt% softener, heat shielding pigment 20~30wt%, thickener 2~3wt% It characterized in that it comprises a water-soluble heat-resistant color coating layer applied by using.

또한, 코팅층은, 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 배합비 8:2의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 87~93wt%와, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 증점제 0.5~1wt%를 포함하는 수용성 투명 코팅제를 이용하여 형성된 수용성 투명 코팅층을 포함하는 것을 특징으로 한다. In addition, the coating layer is a water-soluble elastic acrylic-urethane mixed emulsion resin 87~ formed by mixing an acrylic resin having a content of solids of 35 to 44% and a urethane resin having a ratio of 38 to 45% at a mixing ratio of 8:2, respectively. Using water-soluble transparent coating agent containing 93wt%, dispersant 1~2wt%, antifoaming agent 1~2wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, softener 2~4wt%, thickener 0.5~1wt% It characterized in that it comprises a water-soluble transparent coating layer formed.

또한, 제1수지바인더 및 전용몰탈 혼합층과 상기 제2수지바인더 및 전용몰탈 혼합층의 사이에 형성되는 패턴무늬층을 포함하는 것을 특징으로 한다. In addition, it characterized in that it comprises a pattern pattern layer formed between the first resin binder and a dedicated mortar mixed layer and the second resin binder and a dedicated mortar mixed layer.

본 발명의 실시예에 따른 도막형 바닥재의 수용성 수지바인더는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 것을 특징으로 한다. In the water-soluble resin binder of the coating-type flooring material according to the embodiment of the present invention, acrylic resin having a content of solids of between 20 and 25% and urethane resin having between 38 and 45% are formed by mixing at a mixing ratio of 7:3, respectively. Water-soluble elastic acrylic-urethane mixed emulsion resin 82~89wt%, dispersant 1~2wt%, antifoaming agent 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocker 1~2wt%, surfactant 4~7wt%, softener 2~ Characterized in that it contains 4wt%, AE agent 0.5 ~ 1wt%.

본 발명의 실시예에 따른 도막형 바닥재의 전용몰탈은, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 것을 특징으로 한다. Exclusive mortar of the coating-type flooring according to an embodiment of the present invention, 40-50 wt% of insulating cement using expanded vermiculite, 20-30 wt% of super crude steel port cement, 20-30 wt of expanded cement composed of calcium silicate and gypsum and calcium oxide %, characterized in that it contains 5-10 wt% of ceramic powder.

본 발명의 실시예에 따른 도막형 바닥재의 수지바인더와 전용몰탈의 혼합 조성물은, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 도막형 바닥재의 수용성 수지바인더;와, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 것을 특징으로 하는 도막형 바닥재의 전용몰탈;에서, 상기 수용성 수지바인더 6~10(L)에 상기 전용몰탈 20Kg의 배합비율로써 배합되는 것을 특징으로 한다. In the mixed composition of the resin binder and the exclusive mortar of the coating-type flooring material according to the embodiment of the present invention, the mixing ratio of 7:3 each of the acrylic resin having a solid content of 20 to 25% and the urethane resin having 38 to 45% is respectively Water-soluble elastic acrylic-urethane mixed emulsion resin formed by blending with 82~89wt%, dispersant 1~2wt%, antifoaming agent 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt %, 2~4wt% of softener, 0.5~1wt% of AE agent, water-soluble resin binder of coating-type flooring; and, 40~50wt% of insulation cement using expanded vermiculite, 20~30wt% of super-steel portland cement, calcium silicate And gypsum and expanded cement composed of calcium oxide, 20-30 wt%, ceramic powder 5-10 wt%, characterized in that it comprises a dedicated mortar of a coating-type flooring; in, the water-soluble resin binder 6-10 (L) to the dedicated mortar It is characterized by being blended at a mixing ratio of 20 Kg.

본 발명의 일 실시예에 따른 도막형 바닥재의 시공방법은, (a) 시공대상 자전거 도로의 시공 전처리를 수행하는 단계;와, (b) 상기 시공대상 자전거 도로에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계;와, (c) 상기 프라이머층 위에 수용성 탄성 아크릴 우레탄 혼합 에멀젼 수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, AE제로 구성된 수지바인더와 팽창질석을 이용한 단열시멘트, 초조강 포틀랜트 시멘트, 팽창 시멘트, 세라믹 분말로 구성된 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계;와, (d) 상기 수지바인더 및 전용몰탈 혼합층 위에 수용성 차열 칼라 코팅제를 도포하여 수용성 차열 칼라 코팅층을 형성하는 단계;와, (e) 보강 작업물을 해체하고 양생하는 단계;를 포함하는 것을 특징으로 한다. Construction method of a coating-type flooring according to an embodiment of the present invention, (a) a step of performing a pre-treatment of the construction road bike road; and, (b) the primer to apply the resin binder primer composition to the road bike road construction target Forming a layer; and, (c) an insulating cement using a resin binder and an expanded vermiculite composed of a water-soluble elastic acrylic urethane mixed emulsion resin, a dispersant, an antifoaming agent, an anti-freezing agent, a UV blocking agent, a surfactant, a softener, and an AE agent on the primer layer. , Forming a resin binder and a dedicated mortar mixture layer by applying a dedicated mortar mixture composition composed of super-steel portland cement, expanded cement, and ceramic powder; and (d) a water-soluble heat-resistant color coating agent on the resin binder and the exclusive mortar mixture layer. It characterized in that it comprises a step of forming a water-soluble heat-resistant color coating layer by applying; and (e) dismantling and curing the reinforcement work.

본 발명의 다른 실시예에 따른 도막형 바닥재의 시공방법은, (a) 시공대상 옹벽의 시공 전처리를 수행하는 단계;와, (b) 상기 시공대상 옹벽에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계;와, (c) 상기 프라이머층 위에 수용성 탄성 아크릴 우레탄 혼합 에멀젼 수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, AE제로 구성된 수지바인더와 팽창질석을 이용한 단열시멘트, 초조강 포틀랜트 시멘트, 팽창 시멘트, 세라믹 분말로 구성된 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계;와, (d) 상기 시공대상 옹벽에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층을 형성하는 단계;와, (e) 상기 수지바인더와 차열안료 및 전용몰탈 혼합층 위에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 단계;를 포함하는 것을 특징으로 한다. According to another embodiment of the present invention, a method of constructing a coating-type flooring includes: (a) performing pre-treatment of a retaining wall to be constructed; and (b) applying a resin binder primer composition to the retaining wall to be applied to coat a primer layer. Forming; and, (c) a resin binder composed of a water-soluble elastic acrylic urethane mixed emulsion resin, a dispersant, an antifoaming agent, a UV blocking agent, a surfactant, a softener, and an AE agent on the primer layer, and an insulating cement using an expanded vermiculite, agitation Forming a resin binder and a dedicated mortar mixture layer by applying a dedicated mortar mixture composition comprising steel portland cement, expanded cement, and ceramic powder; and, (d) a resin binder, a heat-resistant pigment, and a dedicated mortar mixture composition on the retaining wall to be constructed. And forming a mixed layer of a resin binder and a heat-insulating pigment and a dedicated mortar; and (e) forming a water-soluble transparent coating layer by applying a water-soluble transparent coating agent on the resin binder and the heat-insulating pigment and a dedicated mortar mixed layer. It is characterized by.

본 발명의 또 실시예에 따른 도막형 바닥재의 시공방법은, (a) 시공대상 인도의 시공 전처리를 수행하는 단계;와, (b) 상기 시공대상 인도에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계;와, (c) 상기 프라이머층 위에 수용성 탄성 아크릴 우레탄 혼합 에멀젼 수지, 분산제, 소포제, 동결방지제, UV차단제, 계면활성제, 연화제, AE제로 구성된 수지바인더와 팽창질석을 이용한 단열시멘트, 초조강 포틀랜트 시멘트, 팽창 시멘트, 세라믹 분말로 구성된 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계;와, (d) 상기 수지바인더 및 전용몰탈 혼합층 위에 패턴무늬부재를 설치하고 시공대상 인도에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층을 형성하는 단계;와, (e) 상기 패턴무늬부재를 제거하고 상기 수지바인더와 차열안료 및 전용몰탈 혼합층 위에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 단계;를 포함하는 것을 특징으로 한다. According to another embodiment of the present invention, a method of constructing a coating-type flooring includes: (a) performing pre-treatment of a construction target delivery; and (b) applying a resin binder primer composition to the construction target delivery to obtain a primer layer. Forming; and, (c) a resin binder composed of a water-soluble elastic acrylic urethane mixed emulsion resin, a dispersant, an antifoaming agent, a UV blocking agent, a surfactant, a softener, and an AE agent on the primer layer, and an insulating cement using an expanded vermiculite, agitation Forming a resin binder and a dedicated mortar mixture layer by applying a dedicated mortar mixture composition composed of steel portland cement, expanded cement, and ceramic powder; and, (d) installing and constructing a pattern pattern member on the resin binder and exclusive mortar mixture layer Forming a mixed layer of a resin binder and a heat-insulating pigment and a dedicated mortar by applying a resin binder, a heat-insulating pigment, and a dedicated mortar mixture composition to the target delivery; and, (e) removing the pattern pattern member and removing the resin binder and the heat-insulating pigment and exclusives And forming a water-soluble transparent coating layer by applying a water-soluble transparent coating agent on the mixed mortar layer.

따라서, 본 발명의 실시예에 따른 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법은, 탄성을 가진 접착제로서의 수용성 수지바인더와 고강도 크랙방지용 전용몰탈 등을 혼합하여 이를 기존 포장 블럭 위에 도포함으로써 단열효과, 크랙방지 효과 및 미끄럼방지 효과의 기능을 동시에 갖도록 하는 효과가 있다. Accordingly, the coating method of the coating-type flooring material, the water-soluble resin binder of the coating-type flooring, the exclusive mortar of the coating-type flooring, the water-soluble resin binder of the coating-type flooring and the exclusive mortar, and the construction method of the coating-type flooring, By mixing a water-soluble resin binder as an adhesive with elasticity and a dedicated mortar for high-strength crack prevention and coating it on an existing packaging block, there is an effect of simultaneously having the functions of heat insulation, crack prevention and anti-slip effects.

본 발명의 실시예에 따른 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법은, 환경 친화적인 수용성 수지 조성물을 이용하여 시공 시 냄새로 인한 환경오염을 방지하여 작업환경을 개선할 수 있는 효과가 있다. The coating method of the coating-type flooring material, the water-soluble resin binder of the coating-type flooring material, the exclusive mortar of the coating-type flooring material, the mixing composition of the coating-type flooring-water-soluble resin binder and the exclusive mortar and the coating-type flooring method are environmentally friendly. It has an effect of improving the working environment by preventing environmental pollution due to odor during construction using a phosphorus-soluble resin composition.

도 1은 본 발명의 일 실시예에 따른 도막형 바닥재 시공방법을 나타낸 공정도이다.
도 2는 본 발명의 일 실시예에 따른 도막형 바닥재를 나타낸 단면도이다.
도 3은 본 발명의 다른 실시예에 따른 도막형 바닥재 시공방법을 나타낸 공정도이다.
도 4는 본 발명의 다른 실시예에 따른 도막형 바닥재를 나타낸 단면도이다.
도 5는 본 발명의 또 다른 실시예에 따른 도막형 바닥재 시공방법을 나타낸 공정도이다.
도 6은 본 발명의 또 다른 실시예에 따른 도막형 바닥재를 나타낸 단면도이다. 1 is a process diagram showing a method for constructing a coating-type flooring according to an embodiment of the present invention.
2 is a cross-sectional view showing a coating-type flooring according to an embodiment of the present invention.
3 is a process diagram showing a method for constructing a coating-type flooring according to another embodiment of the present invention.
4 is a cross-sectional view showing a coating-type flooring according to another embodiment of the present invention.
5 is a process diagram showing a method for constructing a coating-type flooring according to another embodiment of the present invention.
6 is a cross-sectional view showing a coating-type flooring according to another embodiment of the present invention.

이하, 첨부된 도면들을 참조하면서 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 일 실시예에 따른 도막형 바닥재 시공방법을 나타낸 공정도이며, 도 2는 본 발명의 일 실시예에 따른 도막형 바닥재를 나타낸 단면도이다. 1 is a process diagram showing a method for constructing a coating-type flooring according to an embodiment of the present invention, and FIG. 2 is a cross-sectional view showing a coating-type flooring according to an embodiment of the present invention.

도 1 및 도 2에 도시된 바와 같이, 본 발명의 일 실시예에 따른 도막형 바닥재 시공방법은 주차장 또는 자전거 전용도로의 도막형 바닥재 시공방법에 관한 것으로, 이러한 자전거 전용도로 또는 주차장(이하, '자전거 도로'라 한다.)의 도막형 바닥재 시공방법은, (a) 시공대상 자전거 도로의 보강 작업물 설치 등의 전처리를 수행하는 전처리 단계(S10);와, (b) 시공대상 자전거 도로에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계(S20);와, (c) 프라이머층 상면에 시공대상 자전거 도로에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계(S30);와, (d) 수지바인더 및 전용몰탈 혼합층 상면에 수용성 차열 칼라 코팅층을 형성하는 단계(S40);와, (e) 보강 작업물을 해체하고 양생하는 단계(S50);를 포함하여 구성된다. 1 and 2, the method of constructing a coating-type flooring according to an embodiment of the present invention relates to a method of constructing a coating-type flooring of a parking lot or a bicycle-only road, such as a bicycle-only road or a parking lot (hereinafter, ' The method of constructing a coating-type flooring material of'Bicycle Road' is (a) a pre-treatment step (S10) of performing pre-treatment such as installation of a reinforcement work of the bicycle road to be constructed; and (b) resin on the bicycle road to be constructed. Forming a primer layer by applying a binder primer composition (S20); and (c) forming a resin binder and a dedicated mortar mixture layer by applying a resin binder and a dedicated mortar mixture composition to the bicycle road to be constructed on the top surface of the primer layer (S30); And, (d) forming a water-soluble heat-resistant color coating layer on the upper surface of the resin binder and the dedicated mortar mixed layer (S40); and (e) dismantling and curing the reinforcement work (S50); It is composed.

먼저, 본 발명의 일 실시예에 따른 도막형 바닥재 시공방법은, (a) 시공대상 자전거 도로의 물청소 작업 등을 실시하는 전처리 단계(S10)를 포함한다. First, the method for constructing a coating-type flooring according to an embodiment of the present invention includes (a) a pretreatment step (S10) of performing a water cleaning operation on a bicycle road to be constructed.

이러한 (a) 시공대상 자전거 도로의 전처리 단계(S10)는, (a-1) 시공대상 자전거 도로(10a)의 물청소 단계(S11)와, (a-2) 시공대상 자전거 도로(10a)의 크랙을 그라인더로 V커팅을 하고 수지바인더 및 전용몰탈 혼합 조성물로 시공대상 자전거 도로(10a)의 바닥면이 평탄해질 때까지 채우는 바닥면 평탄화 단계(S12)와, (a-3) 시공대상 자전거 도로(10a)의 주변 시설물이 오염되지 않도록 테이프(ex, 카바링 테이프)로 보완하는 단계(S13)를 포함할 수 있다. These (a) the pre-treatment step (S10) of the bicycle road to be constructed, (a-1) the water cleaning step (S11) of the bicycle road (10a) to be constructed, and (a-2) the bicycle road (10a) to be constructed. V-cutting the cracks with a grinder and filling with a resin binder and a dedicated mortar mixture composition until the bottom surface of the bicycle road 10a to be constructed is flat (S12) and (a-3) bicycle roads to be constructed It may include the step (S13) of supplementing with a tape (ex, a covering tape) so that the surrounding facilities of (10a) are not contaminated.

시공대상 자전거 도로의 물청소 단계(S11)는, 시공대상 자전거 도로(10a) 위에 도막형 바닥재를 포장하기 위하여 시공대상 자전거 도로(10a) 표면을 물청소 작업으로 수분, 유분, 모래, 먼지 및 기타 이물질 등이 시공대상 자전거 도로(10a) 표면이 남지 않도록 깨끗하게 청소하는 단계이다. In the water cleaning step (S11) of the bicycle road to be constructed, water, oil, sand, dust, etc. are applied to the surface of the bicycle road (10a) to be constructed by water cleaning in order to wrap the coated flooring material on the bicycle road (10a). This is a step of cleaning cleanly so that the surface of the bicycle road 10a to be constructed does not remain.

바닥 평탄화 단계(S12)는, 시공대상 자전거 도로(10a)의 크랙을 그라인더로 V커팅하여 수지바인더 및 전용몰탈 혼합 조성물을 채워 넣어 시공대상 자전거 도로(10a) 바닥면을 평탄화시키는 단계이다. Floor flattening step (S12) is a step of flattening the bottom surface of the bicycle road 10a to be constructed by filling the resin binder and the exclusive mortar mixture composition by V-cutting the crack of the bicycle road 10a to be constructed with a grinder.

테이프 보완 단계(S13)는, 후술하는 작업으로 인하여 시공대상 자전거 도로(10a) 주변 시설물이 오염되지 않도록 테이프(ex, 카바링 테이프)로 보완하는 단계이다. The tape supplementing step (S13) is a step of supplementing with a tape (ex, a covering tape) so that the facilities around the bicycle road 10a to be constructed are not contaminated due to the operations described below.

한편, 시공대상 자전거 도로(10a)의 재질은 특별히 한정되지 않고, 콘크리트, 투수 콘크리트, 컬러 콘크리트 및 아스팔트 바닥 등을 포함할 수 있다. Meanwhile, the material of the bicycle road 10a to be constructed is not particularly limited, and may include concrete, pitched concrete, colored concrete, and asphalt floor.

다음, 본 발명의 일 실시예에 따른 도막형 바닥재 시공방법은, (b) 시공대상 자전거 도로에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계(S20)를 포함한다. Next, the method for constructing a coating-type flooring according to an embodiment of the present invention includes (b) applying a resin binder primer composition to a bicycle road to be constructed to form a primer layer (S20).

프라이머층(20)은 수지바인더 및 전용몰탈 혼합층(30,40)이 시공대상 자전거 도로(10a)에 접합될 때, 수지바인더 및 전용몰탈 혼합층(30,40)과 시공대상 자전거 도로(10a) 표면 사이의 접착력을 증대시키기 위해 도포되는 것이다. The primer layer 20 is a resin binder and a dedicated mortar mixture layer (30,40) when bonded to the construction target bicycle road (10a), resin binder and dedicated mortar mixture layer (30,40) and the construction target bicycle road (10a) surface It is applied to increase the adhesion between them.

이러한 수지바인더 프라이머 조성물은 발포가 이루어질 때 60℃~80℃의 열이 발생되면서 발포반응이 이루어지는데, 이때 수지바인더 프라이머 조성물은 후술되는 수지바인더 및 전용몰탈 혼합 조성물과의 접착을 도우면서 하부 기층에서 수분이 올라와 이로 인해 발포반응을 저해하는 것을 방지하기 위해 시공대상 자전거 도로(10a)의 상측에 반드시 도포하는 것이다. When the foaming is performed, the resin binder primer composition generates a heat reaction of 60°C to 80°C, and the resin binder primer composition is used in the lower base layer while helping adhesion with a resin binder and a dedicated mortar mixture composition to be described later. In order to prevent the moisture from rising and inhibiting the foaming reaction due to this, it must be applied on the upper side of the bicycle road 10a to be constructed.

이러한 수지바인더 프라이머 조성물은, 고형분의 함량이 17~20% 사이인 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지 90~95wt%, 유동화제 1~2wt%, 소포제 0.5~1wt%, 속경제 1~5wt%, 동결방지제 1~2wt%, 팽창제 6.5~8wt%를 포함하여 구성될 수 있다. The resin binder primer composition, water-soluble acrylic emulsion resin formed of an acrylic resin having a solids content of 17 to 20%, 90 to 95 wt%, 1 to 2 wt% of a fluidizing agent, 0.5 to 1 wt% of an antifoaming agent, and 1 to 5 wt% of a fast economy, It may be composed of 1 to 2 wt% of an antifreeze agent, and 6.5 to 8 wt% of an expanding agent.

한편, 시공대상 자전거 도로(10a) 바닥면의 노후화로 인해 부스러짐이 많을 시에는 연삭작업으로 바닥을 갈아내고 수용성 수지 프라이머를 1차~3차까지 도포하여 시공대상 자전거 도로(10a) 바닥면의 강도를 증진시킬 수 있다. On the other hand, if there is a lot of debris due to the aging of the bottom surface of the bicycle road (10a) to be constructed, the floor is ground by grinding work and water-soluble resin primers are applied from 1st to 3rd to the bottom of the bicycle road (10a) to be constructed. Strength can be enhanced.

본 발명의 일 실시예에 따른 도막형 바닥재 시공방법은, (c) 시공대상 자전거 도로에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층(30,40)을 형성하는 단계(S30)를 포함한다. The method of constructing a coating-type flooring material according to an embodiment of the present invention comprises: (c) forming a resin binder and a dedicated mortar mixture layer (30,40) by applying a resin binder and a dedicated mortar mixture composition to a bicycle road to be constructed (S30) ).

수지바인더 및 전용몰탈 혼합층(30,40)은 프라이머층(20) 상면에 적층되며, 수용성 수바인더와 전용몰탈이 혼합되어 조성된다. The resin binder and the exclusive mortar mixed layers 30 and 40 are laminated on the upper surface of the primer layer 20, and are formed by mixing the water-soluble water binder and the exclusive mortar.

수용성 수지바인더는 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하여 구성된다. The water-soluble resin binder is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin having a solid content of 20-25% and a urethane resin 38-45% with a mixing ratio of 7:3, respectively 82-89wt% , Dispersant 1~2wt%, Anti-foaming agent 0.5~1wt%, Anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, Surfactant 4~7wt%, Softener 2~4wt%, AE agent 0.5~1wt% do.

전용몰탈은, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하여 구성된다. Exclusive mortar contains 40~50wt% of insulating cement using expanded vermiculite, 20~30wt% of super-steel portland cement, 20~30wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, and 5~10wt% of ceramic powder It is composed.

즉, 본 발명의 실시예에 따른 도막형 바닥재의 수지바인더 및 전용몰탈 혼합층(30,40)은, 탄성을 가진 접착제로서의 수용성 수지바인더와 고강도 크랙방지용 전용몰탈을 혼합하여 단열효과, 크랙방지 효과 및 미끄럼방지 효과의 기능을 동시에 갖도록 한다. That is, the resin binder and the exclusive mortar mixing layers 30 and 40 of the coating-type flooring material according to the embodiment of the present invention are mixed with a water-soluble resin binder as an adhesive with elasticity and a dedicated mortar for high-strength cracking to prevent thermal insulation, crack prevention, and It has the function of anti-slip effect at the same time.

이러한 (c) 시공대상 자전거 도로에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계(S30)는, (c-1) 시공대상 자전거 도로에 수지바인더 및 전용몰탈 혼합 조성물을 끌대로 1차 도포 형성된 제1수지바인더 및 전용몰탈 혼합층 형성 단계(S31);와, (c-2) 시공대상 자전거 도로에 수지바인더 및 전용몰탈 혼합 조성물을 끌대 또는 스프레이로 2차 도포 형성된 제1수지바인더 및 전용몰탈 혼합층 형성 단계(S32);를 포함한다. The step (S30) of forming a resin binder and a dedicated mortar mixture layer by applying the resin binder and a dedicated mortar mixture composition to the bicycle road to be constructed (c) is (c-1) mixing a resin binder and a dedicated mortar on the bicycle road to be constructed. A first resin binder and a dedicated mortar mixed layer forming step (S31); and (c-2) a resin binder and a dedicated mortar mixed composition are applied on a bicycle road to be constructed by dragging or spraying the composition. It includes; a first resin binder and a dedicated mortar mixed layer forming step (S32).

(c-1) 제1수지바인더 및 전용몰탈 혼합층 형성 단계(S31)는, 1차 수지바인더 및 전용몰탈 혼합 조성물을 끌대를 이용하여 시공대상 자전거 도로(10a) 바닥의 평탄화를 이루기 위한 작업이다. 즉, 제1수지바인더 및 전용몰탈 혼합층(30)은, 시공대상 자전거 도로 바닥의 요철부분을 메우고 제2수지바인더 및 전용몰탈 혼합 조성물의 도포를 위한 접착력을 증진시킨다. (c-1) The step of forming the first resin binder and the exclusive mortar mixed layer (S31) is an operation for achieving flattening of the floor of the bicycle road 10a to be constructed using a primary resin binder and a dedicated mortar mixed composition using a drag rod. That is, the first resin binder and the exclusive mortar mixture layer 30 fills the uneven portion of the floor of the bicycle road to be constructed and promotes adhesion for application of the second resin binder and the exclusive mortar mixture composition.

이러한 제1수지바인더 및 전용몰탈 혼합층 형성 단계(S31)는, 수용성 수지바인더 9~10(L)에 전용몰탈 20(Kg)의 배합비율로써 배합하여 제1수지바인더 및 전용몰탈 혼합층(30)을 형성할 수 있다. The first resin binder and the exclusive mortar mixed layer forming step (S31), the water-soluble resin binder 9 to 10 (L) by mixing at a mixing ratio of 20 (Kg) dedicated mortar, the first resin binder and the dedicated mortar mixed layer 30 Can form.

(c-2) 제2수지바인더 및 전용몰탈 혼합층 형성 단계(S32)는, 수지바인더 및 전용몰탈 혼합층의 전체적인 두께를 보강하기 위하여 2차 수지바인더 및 전용몰탈 혼합 조성물을 끌대나 스프레이로 도포하는 단계이다. 이때 끌대로 작업 시 전용몰탈에 들어 있는 규사가 돌출되게끔 한다. (c-2) The step of forming the second resin binder and the exclusive mortar mixed layer (S32), applying a secondary resin binder and the exclusive mortar mixed composition with a drag or spray to reinforce the overall thickness of the resin binder and the exclusive mortar mixed layer. to be. At this time, when working with a chisel, let the silica sand in the exclusive mortar protrude.

이렇게 제2수지바인더 및 전용몰탈 혼합층 형성 단계(S32)를 포함하는 이유는, 시공대상 자전거 도로(10a) 바닥의 강도를 증진시켜주며 2~3(mm)의 두께를 가지도록 하기 위한 작업인데, 특히 제1수지바인더 및 전용몰탈 혼합층(30)으로 전체적인 두께를 낼 수는 있지만 한꺼번에 높은 두께로 도포층(40)을 형성하게 되면 접착력이 강하기 때문에 양생 도중에 갈라지는 현상이 발생하기 때문이다. The reason for including the second resin binder and the dedicated mortar mixed layer forming step (S32) is to improve the strength of the floor of the bicycle road 10a to be constructed and have a thickness of 2 to 3 (mm). In particular, although the overall thickness can be achieved with the first resin binder and the dedicated mortar mixture layer 30, when the coating layer 40 is formed with a high thickness at a time, the adhesive force is strong, so that cracking occurs during curing.

이러한 제2수지바인더 및 전용몰탈 혼합층 형성 단계(S32)는, 수용성 수지바인더 6~8(L)에 전용몰탈 20(Kg)의 배합비율로써 배합하여 제2수지바인더 및 전용몰탈 혼합층(40)을 형성할 수 있다. In the second resin binder and dedicated mortar mixed layer forming step (S32), the second resin binder and the exclusive mortar mixed layer 40 are blended in a water-soluble resin binder 6 to 8 (L) at a mixing ratio of 20 (Kg). Can form.

본 발명의 일 실시예에 따른 도막형 바닥재 시공방법은, (d)수지바인더 및 전용몰탈 혼합층 위에 수용성 차열 칼라 코팅제를 도포하여 수용성 차열 칼라 코팅층을 형성하는 단계(S40)를 포함한다. The method of constructing a coating-type flooring according to an embodiment of the present invention includes (d) forming a water-soluble heat-resistant color coating layer by applying a water-soluble heat-resistant color coating agent on a resin binder and a dedicated mortar mixture layer (S40).

이러한 수용성 차열 칼라 코팅층(50)은, 제2수지바인더 및 전용몰탈 혼합층(40)의 상면에 칠하여 고체막을 형성하여 시공대상 자전거 도로(10a)의 표면을 보호하고 아름답게 하는 유동성 물질로서, 한낮의 직사광선에 의해 시공대상 자전거 도로(10a)의 열축적을 근본적으로 차단하는 것이다. The water-soluble heat-shielding color coating layer 50 is a fluid material that paints on the upper surfaces of the second resin binder and the exclusive mortar mixture layer 40 to form a solid film to protect and beautify the surface of the bicycle road 10a to be constructed, and direct sunlight in the middle of the day. By this, the heat accumulation of the bicycle road 10a to be constructed is basically blocked.

이러한 수용성 차열 칼라 코팅층(50)은, 1차, 2차에 걸쳐서 에어리스 또는 롤러를 이용하여 작업할 수 있다.(S51,S52) 이때 작업 후 롤러 자국이나 색상의 얼룩짐이 보이면 그 부분에 도포를 한번 더하여 색상의 얼룩짐이 없도록 하는 것이 바람직하다. The water-soluble heat-shielding color coating layer 50 may be operated using airless or rollers over the first and second stages. In addition, it is preferable to prevent color irregularities.

이렇게, 수용성 차열 칼라 코팅층(50)을 1차, 2차에 걸쳐 작업하는 이유는, 수용성 차열 칼로 코팅층을 1차로 마감 처리하면 코팅제의 침투력이 있어 바닥 상태에 따라서 침투가 많이 되고 적게 되는 부분이 발생되어 침투가 많이 된 부분은 색상이 약하고 침투가 적게 되는 부분은 색상이 진하여 얼룩이 생기는 현상이 발생할 수 있으므로 2차 작업을 해주어야만 색상의 얼룩이 없어지고 마모성이 강해지기 때문이다. In this way, the reason for working the water-soluble heat-resistant color coating layer 50 over the first and second stages is that when the coating layer is first-finished with a water-soluble heat-resistant knife, there is a penetrating power of the coating agent. This is because the part with a lot of penetration is weak in color, and the part with little penetration is dark in color, so staining may occur.

이러한 수용성 차열 칼라 코팅제는, 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 8:2의 배합비율로써 배합하여 형성된 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 60~70wt%, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 차열안료 20~30wt%, 증점제 2~3wt%를 포함하여 구성될 수 있다. The water-soluble heat-resistant color coating agent is a water-soluble elastic acrylic-urethane mixed emulsion resin 60~ formed by mixing an acrylic resin having a solid content of between 35 and 44% and a urethane resin having between 38 and 45% at a mixing ratio of 8:2, respectively. Including 70wt%, dispersant 1~2wt%, antifoaming agent 1~2wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, softener 2~4wt%, heat shielding pigment 20~30wt%, thickener 2~3wt% Can be configured.

본 발명의 일 실시예에 따른 도막형 바닥재 시공방법은, (e) 보강 작업물을 해체하고 양생하는 단계(S50)를 포함한다. The method of constructing a coating-type flooring according to an embodiment of the present invention includes (e) dismantling and curing the reinforcement work (S50).

이러한 보강 작업물의 해체 및 양생 단계(S50)는, 작업 후 완전히 양생이 되면 테이프 등으로 보완 작업을 한 것을 철거하여 완공 후 주차장인 경우는 4일을 양생을 시키고 자전거 도로인 경우는 24시간 양생하는 단계를 포함한다. In the dismantling and curing step (S50) of the reinforcing work, after the work is completely cured, the supplementary work is removed with tape, etc., and after completion, the car is cured for 4 days in the case of a parking lot and 24 hours in the case of a bicycle road. Steps.

따라서, 본 발명의 일 실시예에 따른 자전거 도로용 도막형 바닥재의 시공방법은, 탄성을 가진 접착제로서의 수용성 수지바인더와 고강도 크랙방지용 전용몰탈 등을 혼합하여 이를 기존 포장 블럭 위에 도포함으로써 단열효과, 크랙방지 효과 및 미끄럼방지 효과의 기능을 동시에 가질 수 있을 뿐만 아니라, 환경 친화적인 수용성 수지 조성물을 이용하여 시공 시 냄새로 인한 환경오염을 방지하여 작업환경을 개선할 수 있는 효과가 있다.
Therefore, the construction method of the coating film-type flooring material for a bicycle road according to an embodiment of the present invention is mixed with a water-soluble resin binder as an adhesive with elasticity and a dedicated mortar for preventing high-strength cracks, and coating it on an existing pavement block, thereby providing an insulating effect and a crack. In addition to having the functions of an anti-slip effect and an anti-slip effect, an environmentally friendly water-soluble resin composition is used to prevent environmental pollution due to odor during construction, thereby improving the working environment.

도 3은 본 발명의 다른 실시예에 따른 도막형 바닥재 시공방법을 나타낸 공정도이며, 도 4는 본 발명의 다른 실시예에 따른 도막형 바닥재를 나타낸 단면도이다. 3 is a process diagram showing a method of constructing a coating-type flooring according to another embodiment of the present invention, and FIG. 4 is a cross-sectional view showing a coating-type flooring according to another embodiment of the present invention.

도 3 및 도 4에 도시된 바와 같이, 본 발명의 다른 실시예에 따른 도막형 바닥재 시공방법은 옹벽 전용의 도막형 바닥재 시공방법에 관한 것으로, 이러한 옹벽 전용의 도막형 바닥재 시공방법은, (a) 시공대상 옹벽의 시공 전처리를 수행하는 단계(S10);와, (b) 시공대상 옹벽에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계(S20);와, (c) 시공대상 옹벽에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계(S30);와, (d) 시공대상 옹벽에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층을 형성하는 단계(S40);와, (e) 수지바인더와 차열안료 및 전용몰탈 혼합층 위에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 단계(S50);를 포함하여 구성된다. 3 and 4, a method for constructing a coating-type flooring according to another embodiment of the present invention relates to a method for constructing a coating-type flooring dedicated to a retaining wall, and the method for constructing a coating-type flooring dedicated to a retaining wall is (a ) Step (S10) of performing pre-treatment of the retaining wall to be constructed; and (b) forming a primer layer by applying a resin binder primer composition to the retaining wall to be constructed (S20); and, (c) to the retaining wall to be constructed. Forming a resin binder and a dedicated mortar mixed layer by applying a resin binder and a dedicated mortar mixture composition (S30); and (d) applying a resin binder, a heat-insulating pigment, and a dedicated mortar mixture composition to the retaining wall to be constructed to heat the resin binder and the heat shield It comprises a step (S40) of forming a pigment and a dedicated mortar mixed layer (S40); and (e) forming a water-soluble transparent coating layer by applying a water-soluble transparent coating agent on the resin binder and the heat-resistant pigment and the dedicated mortar mixed layer (S50); .

(a) 시공대상 옹벽(10b)의 시공 전처리를 수행하는 단계(S10)는, (a-1) 시공대상 옹벽(10b)의 물청소 단계(S11)와, (a-2) 시공대상 옹벽(10b)의 크랙을 그라인더로 V커팅을 하고 수지바인더 및 전용몰탈 혼합 조성물로 바닥면이 평탄해질 때까지 채우는 바닥면 평탄화 단계(S12)와, (a-3) 시공대상 옹벽(10b)의 주변 시설물이 오염되지 않도록 테이프로 보완하는 단계(S13)를 포함할 수 있다. (a) The step (S10) of performing the pretreatment of the retaining wall 10b to be constructed includes (a-1) the water cleaning step S11 of the retaining wall 10b to be constructed and (a-2) the retaining wall to be constructed ( V-cutting the crack of 10b) with a grinder and filling the floor surface with a resin binder and a dedicated mortar mixture until the floor surface is flattened (S12) and (a-3) surrounding facilities of the retaining wall 10b to be constructed It may include a step (S13) of supplementing the tape to prevent contamination.

(b) 시공대상 옹벽(10b)에 수지바인더 프라이머 조성물을 도포하여 프라이머층(20)을 형성하는 단계(S20)는, 고형분의 함량이 17~20% 사이인 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지 83~89wt%, 유동화제 1~2wt%, 소포제 0.5~1wt%, 속경제 1~5wt%, 동결방지제 1~2wt%, 팽창제 6.5~8wt%로 구성된 수지바인더 프라이머 조성물을 시공대상 옹벽 위에 도포하여 프라이머층을 형성하는 단계를 포함할 수 있다. (b) The step (S20) of forming a primer layer 20 by applying a resin binder primer composition to the retaining wall 10b to be constructed is a water-soluble acrylic emulsion resin 83 formed of an acrylic resin having a solid content of between 17 and 20%. ~89wt%, 1~2wt% of fluidizing agent, 0.5~1wt% of antifoaming agent, 1~5wt% of fast economy, 1~2wt% of cryoprotectant, and 6.5~8wt% of expansion agent are applied on the retaining wall of the construction target to apply primer And forming a layer.

(c) 시공대상 옹벽(10b)에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층(30,40)을 형성하는 단계(S30)는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 구성되는 수용성 수지바인더;와, 팽창질석을 사용한 단열시멘트 50~60wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 구성되는 전용몰탈;에서, 수용성 수지바인더 7~9(L)에 전용몰탈 20(Kg)의 배합비율로써 배합되는 단계를 포함할 수 있다. (c) The step (S30) of forming a resin binder and a dedicated mortar mixture layer (30,40) by applying a resin binder and a dedicated mortar mixture composition to the retaining wall (10b) to be constructed is a solid content of 20 to 25%. Water-soluble elastic acrylic-urethane mixed emulsion resin 82~89wt%, dispersant 1~2wt%, anti-foaming agent 0.5~1wt%, formed by mixing acrylic resin and urethane resin between 38~45% at 7:3 compounding ratio, respectively. Water-soluble resin binder composed of 1~2wt% of anti-freezing agent, 1~2wt% of UV blocking agent, 4~7wt% of surfactant, 2~4wt% of softener, and 0.5~1wt% of AE agent; and, 50~ of thermal insulation cement using expanded vermiculite 60wt%, 20-30wt% of super-steel portland cement, 20-30wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, exclusive mortar composed of 5-10wt% of ceramic powder; in, water-soluble resin binder 7~9( L) may include a step of mixing with a mixing ratio of 20 (Kg) of exclusive mortar.

(d) 시공대상 옹벽(10b)에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층(40')을 형성하는 단계(S40)는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 구성되는 수용성 수지바인더;와, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 구성되는 전용몰탈;과, 차열안료;에서, 수용성 수지바인더 6~8(L)에 전용몰탈 20(Kg)과 차열안료 0.2(Kg)이 배합되는 단계를 포함할 수 있다. (d) The step (S40) of applying a resin binder and a heat-insulating pigment and a dedicated mortar mixture composition to a retaining wall 10b to be constructed to form a resin binder and a heat-insulating pigment and a dedicated mortar mixed layer 40' (S40) has a solid content of 20 Water-soluble elastic acrylic-urethane mixed emulsion resin 82~89wt%, dispersant 1~2wt%, antifoaming agent formed by mixing acrylic resin between ~25% and urethane resin between 38~45% at a mixing ratio of 7:3 respectively Water-soluble resin binder consisting of 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5~1wt%; and Exclusive mortar consisting of 40~50wt% of used insulation cement, 20~30wt% of super-steel portland cement, 20~30wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, and 5~10wt% of ceramic powder; and ; In, water-soluble resin binder 6 to 8 (L) may include a step of mixing a dedicated mortar 20 (Kg) and a heat-resistant pigment 0.2 (Kg).

(e) 수지바인더와 차열안료 및 전용몰탈 혼합층(40') 위에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층(50)을 형성하는 단계(S50)는, 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 배합비 8:2의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 87~93wt%와, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 증점제 0.5~1wt%로 구성되는 수용성 투명 코팅제를 이용하여 수용성 투명 코팅층(50)을 형성하는 단계를 포함할 수 있다. (e) The step (S50) of forming a water-soluble transparent coating layer 50 by applying a water-soluble transparent coating agent on the resin binder and the heat-insulating pigment and the exclusive mortar mixing layer 40' is an acrylic resin having a solid content of between 35 and 44%. And 38-45% urethane resin, respectively, with a blending ratio of 8:2, respectively, and a water-soluble elastic acrylic-urethane mixed emulsion resin formed by blending ratio of 87 to 93 wt%, dispersant 1 to 2 wt%, antifoaming agent 1 to 2 wt%, freezing It may include the step of forming a water-soluble transparent coating layer 50 using a water-soluble transparent coating agent consisting of 1 to 2 wt% of the inhibitor, 1 to 2 wt% of the UV blocking agent, 2 to 4 wt% of the softener, and 0.5 to 1 wt% of the thickener.

도 5는 본 발명의 또 다른 실시예에 따른 도막형 바닥재 시공방법을 나타낸 공정도이며, 도 6은 본 발명의 또 다른 실시예에 따른 도막형 바닥재를 나타낸 단면도이다. 5 is a process diagram showing a method for constructing a coating-type flooring according to another embodiment of the present invention, and FIG. 6 is a cross-sectional view showing a coating-type flooring according to another embodiment of the present invention.

도 5 및 도 6에 도시된 바와 같이, 본 발명의 또 다른 실시예에 따른 도막형 바닥재 시공방법은 인도 전용의 도막형 바닥재 시공방법에 관한 것으로, 이러한 인도 전용의 도막형 바닥재 시공방법은, (a) 시공대상 인도의 시공 전처리를 수행하는 단계(S10);와, (b) 시공대상 인도에 수지바인더 프라이머 조성물을 도포하여 수지바인더 프라이머층을 형성하는 단계(S20);와, (c) 시공대상 인도에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계(S30);와, (d) 패턴무늬부재를 설치하고 시공대상 인도에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층을 형성하는 단계(S40);와, (e) 패턴무늬부재를 제거하고 수지바인더와 차열안료 및 전용몰탈 혼합층 상면에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 단계(S50);를 포함하여 구성된다. 5 and 6, a method for constructing a coating-type flooring according to another embodiment of the present invention relates to a method for constructing a coating-type flooring exclusively for delivery. a) performing pre-treatment of the construction target delivery (S10); and (b) applying a resin binder primer composition to the construction target delivery to form a resin binder primer layer (S20); and, (c) construction Forming a resin binder and a dedicated mortar mixed layer by applying a resin binder and a dedicated mortar mixture composition to the target delivery (S30); and, (d) installing a patterned member and installing the resin binder and heat-resistant pigment and dedicated mortar on the delivery target Forming a mixed layer of the resin binder and the heat-insulating pigment and the exclusive mortar by applying the mixed composition (S40); and (e) removing the pattern pattern member and applying a water-soluble transparent coating agent on the resin binder and the heat-insulating pigment and the exclusive mortar mixed layer And forming a water-soluble transparent coating layer (S50).

(a) 시공대상 인도의 시공 전처리를 수행하는 단계(S10)는, (a-1) 시공대상 인도의 물청소 단계(S11)와, (a-2) 시공대상 인도의 크랙을 그라인더로 V커팅을 하고 수지바인더 및 전용몰탈 혼합 조성물로 바닥면이 평탄해질 때까지 채우는 바닥면 평탄화 단계(S12)와, (a-3) 시공대상 인도의 주변 시설물이 오염되지 않도록 테이프로 보완하는 단계(S13)를 포함할 수 있다. (a) The step (S10) of performing the pre-treatment of the construction target India (S-1), (a-1) the construction target India water cleaning step (S11), and (a-2) the construction target India crack V-cutting with a grinder And filling with a resin binder and a dedicated mortar mixture composition until the bottom surface is flattened (S12) and (a-3) supplementing with tape to prevent contamination of the surrounding facilities of the construction target side (S13) It may include.

(b) 시공대상 인도에 수지바인더 프라이머 조성물을 도포하는 단계(S20)는, 고형분의 함량이 17~20% 사이인 아크릴 수지로 형성된 수용성 아크릴 에멀젼 수지 83~89wt%, 유동화제 1~2wt%, 소포제 0.5~1wt%, 속경제 1~5wt%, 동결방지제 1~2wt%, 팽창제 6.5~8wt%로 구성된 수지바인더 프라이머 조성물을 시공대상 인도 위에 도포하여 프라이머층(20)을 형성하는 단계를 포함할 수 있다. (B) step (S20) of applying a resin binder primer composition to the construction target delivery, 83~89wt% of a water-soluble acrylic emulsion resin formed of an acrylic resin having a solids content of 17~20%, 1~2wt% of a fluidizing agent, It includes the step of forming a primer layer 20 by applying a resin binder primer composition composed of an antifoaming agent 0.5 to 1 wt%, a fast economy 1 to 5 wt%, a cryoprotectant 1 to 2 wt%, and an expansion agent 6.5 to 8 wt% on a construction target sidewalk. Can.

(c) 시공대상 인도에 수지바인더 및 전용몰탈 혼합 조성물을 도포하는 단계(S30)는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%로 구성되는 수용성 수지바인더;와, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%로 구성되는 전용몰탈;에서, 수용성 수지바인더 9~10(L)에 전용몰탈 20(Kg)의 배합비율로써 배합되는 단계를 포함할 수 있다. (c) In the step (S30) of applying the resin binder and the exclusive mortar mixture composition to the construction target delivery, acrylic resin having a content of solids of 20 to 25% and urethane resin having a content of 38 to 45% are 7:3 respectively. Water-soluble elastic acrylic-urethane mixed emulsion resin formed by blending at a blending ratio of 82 to 89 wt%, dispersant 1 to 2 wt%, antifoaming agent 0.5 to 1 wt%, anti-freezing agent 1 to 2 wt%, UV blocking agent 1 to 2 wt%, surfactant 4 Water-soluble resin binder consisting of ~7wt%, softener 2~4wt%, AE agent 0.5~1wt%; and, 40~50wt% of insulating cement using expanded vermiculite, 20~30wt% of super crude steel cement, calcium silicate and gypsum And a dedicated mortar consisting of 20-30 wt% of expanded cement composed of calcium oxide and 5-10 wt% of ceramic powder; In the water-soluble resin binder 9-10 (L), the compounding ratio of the exclusive mortar 20 (Kg) is blended. It can contain.

(d) 패턴무늬부재를 설치하고 시공대상 인도에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하는 단계(S40)는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 도막형 바닥재의 수용성 수지바인더;와, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 전용몰탈;과, 차열안료에서, 수용성 수지바인더 6~8(L)에 전용몰탈 20(Kg)과 차열안료 0.2(Kg)이 배합되는 단계를 포함할 수 있다. (d) The step of installing a pattern pattern member and applying a resin binder, a heat-resistant pigment, and a dedicated mortar mixture composition to the construction target side (S40), between the acrylic resin having a solid content of 20 to 25% and 38 to 45%. A water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing phosphorus urethane resins at a mixing ratio of 7:3, 82 to 89 wt%, dispersing agent 1 to 2 wt%, antifoaming agent 0.5 to 1 wt%, antifreezing agent 1 to 2 wt%, UV Water-soluble resin binder of a coating-type flooring material containing 1 to 2 wt% of a blocking agent, 4 to 7 wt% of a surfactant, 2 to 4 wt% of an emollient, and 0.5 to 1 wt% of an AE agent; and 40 to 50 wt% of an insulating cement using expanded vermiculite. 20~30wt% of steel portland cement, 20~30wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, and exclusive mortar containing 5~10wt% of ceramic powder; and, in heat-resistant pigment, water-soluble resin binder 6~8( L) may include a step of mixing a dedicated mortar 20 (Kg) and a heat shield pigment 0.2 (Kg).

패턴무늬부재는 다양한 무늬가 연출되도록 천공영역과 비천공영역으로 구분되는 종이 등으로 구성될 수 있고, 종이로 된 테이프로 패턴무늬를 연출할 수도 있다. 패터무늬부재를 이용함에 따라 작업성을 향상시킬 수 있고, 다양한 무늬와 디자인을 쉽고 정교하게 표현할 수 있게 된다.The pattern pattern member may be composed of paper, which is divided into a perforated area and a non-perforated area, so that a variety of patterns are produced, or a pattern pattern may be produced with a tape made of paper. By using the pattern pattern member, workability can be improved, and various patterns and designs can be easily and precisely expressed.

(e) 패턴무늬부재를 제거하고 수지바인더와 차열안료 및 전용몰탈 혼합층 상면에 수용성 투명 코팅층을 형성하는 단계(S50)는. 고형분의 함량이 35~44% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지를 각각 배합비 8:2의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 87~93wt%, 분산제 1~2wt%, 소포제 1~2wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 연화제 2~4wt%, 증점제 0.5~1wt%를 포함하는 수용성 투명 코팅제를 이용하여 수용성 투명 코팅층(50)을 형성하는 단계를 포함할 수 있다. (e) removing the pattern pattern member and forming a water-soluble transparent coating layer on the upper surface of the resin binder, the heat-resistant pigment, and the exclusive mortar mixed layer (S50). Water-soluble elastic acrylic-urethane mixed emulsion resin 87-93wt%, dispersant 1 formed by mixing an acrylic resin having a solid content of between 35-44% and a urethane resin having between 38-45% at a compounding ratio of 8:2, respectively Water-soluble transparent coating layer using a water-soluble transparent coating agent containing ~2wt%, anti-foaming agent 1~2wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, softener 2~4wt%, thickener 0.5~1wt% It may include the step of forming.

상술한 바와 같이, 본 발명의 실시예에 따른 도막형 바닥재, 도막형 바닥재의 수용성 수지바인더, 도막형 바닥재의 전용몰탈, 도막형 바닥재의 수용성 수지바인더와 전용몰탈의 혼합 조성물 및 도막형 바닥재의 시공방법은 탄성을 가진 접착제로서의 수용성 수지바인더와 고강도 크랙방지용 전용몰탈 등을 혼합하여 이를 기존 포장 블럭 위에 도포함으로써 단열효과, 크랙방지 효과 및 미끄럼방지 효과의 기능을 동시에 가지도록 하는 것을 기본적인 기술적 사상으로 하고 있음을 알 수 있다. 따라서, 본 발명의 기본적인 기술적 사상의 범주 내에서 당업계의 통상의 지식을 가진 자에게 있어서는 다른 많은 변형이 가능함은 물론이다. As described above, according to an embodiment of the present invention, the coating composition of the coating-type flooring material, the water-soluble resin binder of the coating-type flooring material, the exclusive mortar of the coating-type flooring, the water-soluble resin binder of the coating-type flooring material and the exclusive mortar, and the construction of the coating-type flooring material The basic technical idea is to mix the water-soluble resin binder as an adhesive with elasticity and a high-strength crack-proof dedicated mortar and apply it on the existing packaging block to have the functions of thermal insulation, crack-prevention and anti-slip effects simultaneously. You can see that there is. Therefore, of course, many other modifications are possible to those skilled in the art within the scope of the basic technical idea of the present invention.

10a,10b,10c...시공대상 블럭 20...프라이머층
30...제1수지 바인더 및 전용몰탈 혼합층 40...제2수지 바인더 및 전용몰탈 혼합층
50...수용성 차열 칼라 코팅층10a, 10b, 10c... Construction target block 20... Primer layer
30...first resin binder and exclusive mortar mixed layer 40...second resin binder and exclusive mortar mixed layer
50...water-soluble heat-resistant color coating layer

Claims (6)

삭제delete 삭제delete 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 도막형 바닥재의 수용성 수지바인더; 및
팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 전용몰탈;을 포함하며,
상기 수용성 수지바인더 6~10(L)에 상기 전용몰탈 20Kg의 배합비율로서 배합되는 것을 특징으로 하는 도막형 바닥재의 수지바인더와 전용몰탈의 혼합 조성물.
Water-soluble elastic acrylic-urethane mixed emulsion resin 82-89 wt% formed by mixing acrylic resin having a solid content of 20-25% and urethane resin 38-45% at a mixing ratio of 7:3, and dispersant 1 ~2wt%, antifoaming agent 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5~1wt% Water-soluble resin binder; And
Exclusive mortar containing 40~50wt% of insulating cement using expanded vermiculite, 20~30wt% of super-steel portland cement, 20~30wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, and 5~10wt% of ceramic powder; Includes,
The water-soluble resin binder 6 to 10 (L) is a mixed composition of a resin binder and a dedicated mortar of the coating film-type flooring, characterized in that the blending ratio of the exclusive mortar 20Kg.
(a) 시공대상 자전거 도로의 시공 전처리를 수행하는 단계;
(b) 상기 시공대상 자전거 도로에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계;
(c) 상기 프라이머층 위에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계;
(d) 상기 수지바인더 및 전용몰탈 혼합층 위에 수용성 차열 칼라 코팅제를 도포하여 수용성 차열 칼라 코팅층을 형성하는 단계;
(e) 보강 작업물을 해체하고 양생하는 단계;를 포함하고,
상기 수지바인더는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 도막형 바닥재의 수용성 수지바인더로 이루어지고,
상기 전용몰탈 혼합 조성물은, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 것을 특징으로 하는 도막형 바닥재의 시공방법.
(A) performing a pre-construction of the construction of the bicycle road to be constructed;
(b) forming a primer layer by applying a resin binder primer composition to the bicycle road to be constructed;
(c) forming a resin binder and a dedicated mortar mixed layer by applying a resin binder and a dedicated mortar mixed composition on the primer layer;
(d) forming a water-soluble heat-resistant color coating layer by applying a water-soluble heat-resistant color coating agent on the resin binder and the exclusive mortar mixture layer;
(e) dismantling and curing the reinforcement work; includes,
The resin binder is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin having a solid content of 20-25% and a urethane resin 38-45% at a mixing ratio of 7:3, respectively, 82-89wt %, dispersant 1~2wt%, anti-foaming agent 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5~1wt% It consists of a water-soluble resin binder of a coating-type flooring material,
The dedicated mortar mixture composition, 40-50 wt% of insulating cement using expanded vermiculite, 20-30 wt% of super-steel portland cement, 20-30 wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, 5-10 wt% of ceramic powder Construction method of the coating-type flooring, characterized in that it comprises a.
(a) 시공대상 옹벽의 시공 전처리를 수행하는 단계;
(b) 상기 시공대상 옹벽에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계;
(c) 상기 프라이머층 위에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계;
(d) 상기 시공대상 옹벽에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층을 형성하는 단계;
(e) 상기 수지바인더와 차열안료 및 전용몰탈 혼합층 위에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 단계;를 포함하고,
상기 수지바인더는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 도막형 바닥재의 수용성 수지바인더로 이루어지고,
상기 전용몰탈 혼합 조성물은, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 것을 특징으로 하는 도막형 바닥재의 시공방법.
(a) performing pre-treatment of the retaining wall to be constructed;
(b) forming a primer layer by applying a resin binder primer composition to the retaining wall to be constructed;
(c) forming a resin binder and a dedicated mortar mixed layer by applying a resin binder and a dedicated mortar mixed composition on the primer layer;
(d) forming a resin binder, a heat-insulating pigment and a dedicated mortar mixed layer by applying a resin binder, a heat-insulating pigment and a dedicated mortar mixture composition to the retaining wall to be constructed;
(e) forming a water-soluble transparent coating layer by applying a water-soluble transparent coating agent on the resin binder and the heat-insulating pigment and the exclusive mortar mixture layer; and
The resin binder is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin having a solid content of 20-25% and a urethane resin 38-45% at a mixing ratio of 7:3, respectively, 82-89wt %, dispersant 1~2wt%, anti-foaming agent 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5~1wt% It consists of a water-soluble resin binder of a coating-type flooring material,
The dedicated mortar mixture composition, 40-50 wt% of insulating cement using expanded vermiculite, 20-30 wt% of super-steel portland cement, 20-30 wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, 5-10 wt% of ceramic powder Construction method of the coating-type flooring, characterized in that it comprises a.
(a) 시공대상 인도의 시공 전처리를 수행하는 단계;
(b) 상기 시공대상 인도에 수지바인더 프라이머 조성물을 도포하여 프라이머층을 형성하는 단계;
(c) 상기 프라이머층 위에 수지바인더 및 전용몰탈 혼합 조성물을 도포하여 수지바인더 및 전용몰탈 혼합층을 형성하는 단계;
(d) 상기 수지바인더 및 전용몰탈 혼합층 위에 패턴무늬부재를 설치하고 시공대상 인도에 수지바인더와 차열안료 및 전용몰탈 혼합 조성물을 도포하여 수지바인더와 차열안료 및 전용몰탈 혼합층을 형성하는 단계; 및
(e) 상기 패턴무늬부재를 제거하고 상기 수지바인더와 차열안료 및 전용몰탈 혼합층 위에 수용성 투명 코팅제를 도포하여 수용성 투명 코팅층을 형성하는 단계;를 포함하고,
상기 수지바인더는, 고형분의 함량이 20~25% 사이인 아크릴 수지와 38~45% 사이인 우레탄 수지가 각각 7:3의 배합비율로써 배합되어 형성되는 수용성 탄성 아크릴-우레탄 혼합 에멀젼수지 82~89wt%와, 분산제 1~2wt%, 소포제 0.5~1wt%, 동결방지제 1~2wt%, UV차단제 1~2wt%, 계면활성제 4~7wt%, 연화제 2~4wt%, AE제 0.5~1wt%를 포함하는 도막형 바닥재의 수용성 수지바인더로 이루어지고,
상기 전용몰탈 혼합 조성물은, 팽창질석을 사용한 단열시멘트 40~50wt%, 초조강 포틀랜트 시멘트 20~30wt%, 칼슘실리케이트와 석고 및 산화칼슘으로 구성된 팽창 시멘트 20~30wt%, 세라믹 분말 5~10wt%을 포함하는 것을 특징으로 하는 도막형 바닥재의 시공방법.(A) performing a pre-construction of India to be constructed;
(b) forming a primer layer by applying a resin binder primer composition to the construction target side;
(c) forming a resin binder and a dedicated mortar mixed layer by applying a resin binder and a dedicated mortar mixed composition on the primer layer;
(d) forming a pattern pattern member on the resin binder and the exclusive mortar mixed layer and applying a resin binder and a heat-insulating pigment and a dedicated mortar mixture composition to a construction target side to form a resin binder, a heat-insulating pigment and a dedicated mortar mixed layer; And
(e) forming a water-soluble transparent coating layer by removing the pattern pattern member and applying a water-soluble transparent coating agent on the resin binder and the heat-resistant pigment and the exclusive mortar mixture layer;
The resin binder is a water-soluble elastic acrylic-urethane mixed emulsion resin formed by mixing an acrylic resin having a solid content of 20-25% and a urethane resin 38-45% at a mixing ratio of 7:3, respectively, 82-89wt %, dispersant 1~2wt%, anti-foaming agent 0.5~1wt%, anti-freezing agent 1~2wt%, UV blocking agent 1~2wt%, surfactant 4~7wt%, softener 2~4wt%, AE agent 0.5~1wt% It consists of a water-soluble resin binder of a coating-type flooring material,
The dedicated mortar mixture composition, 40-50 wt% of insulating cement using expanded vermiculite, 20-30 wt% of super-steel portland cement, 20-30 wt% of expanded cement composed of calcium silicate and gypsum and calcium oxide, 5-10 wt% of ceramic powder Construction method of the coating-type flooring, characterized in that it comprises a.
KR1020140015044A 2014-02-10 2014-02-10 Coating-type flooring, water-soluble resin binder of coating-type flooring, exclusive mortar of coating-type flooring, mixed composition of water-soluble resin binder of coating-type flooring and exclusive mortar, and construction method of coating-type flooring KR102136613B1 (en)