KR20200054109A - aluminium laminated paper vessel for environment and human health, and the making method of it - Google Patents

Abstract

The present invention provides an aluminum laminated paper container, which can protect health of people from endocrine-disrupting chemicals of the paper container. Also, provided is the eco-friendly paper container, in which paper can be easily separated so that the paper can be easily recycled when the container is contained in water in case of use of an aqueous adhesive. Therefore, a forest can be preserved so that the paper container contributes to climate change prevention. The container of the present invention is the disposable or multi-use food container which can be used in various food and beverages such as coffee, beer, drinks, cup noodles, cup rice, soup, stew or the like. The container of the present invention can contribute to human health and earth environment preservation.

Description

Aluminum laminated paper vessel for environment and human health, and the making method of it

The present invention relates to an aluminum endothelial container in a paper cup and carton.

The present invention, by placing an aluminum foil inside the paper container, protects human health from synthetic hormones and carcinogens. Reuse and recycling of paper resources are also easy. This is for disposable coffee cups, beverage cups, cup noodles containers, cup noodles containers, cup rice containers, food packaging containers, paper cups, paper packs (milk packs, beverage packs, alcohol packs, etc.) Apply.

Until now, there was no paper container that is safe for health and can be reused and recycled. Paper containers so far are harmful to both health and the environment. Conventional paper containers have synthetic resins such as polyethylene (PE), polypropylene (PP), and nylon (NY) attached to the inner surface, and the hotter the food, the more carcinogens and endocrine disruptors (environmental hormones) are eluted. In addition, it was difficult to recycle or reuse resources due to the fusion of synthetic resin and paper. For paper recycling, the paper envelope must be easily separated, but so far there have been no such products on the market.

In the aluminum endothelial container, it was impossible to seal the area where the aluminum abuts, and it was impossible to form the aluminum endothelial container due to low adhesion between aluminum and synthetic resins such as PE, PP, and PS (polystyrene) used in conventional food containers. PE is somewhat adhesive, but insufficient.

Biodegradable plastics, which are known to be environmentally friendly, are a mixture of biodegradable materials such as starch and synthetic resin. The starch is decomposed upon landfill, but the plastic component is not decomposed, but becomes a fine plastic and enters the ecosystem (aqueous, animal, plant, and soil), which is more harmful to the health of nature and living things. In the end, they are neither green nor pro-health.

In addition, a paper cup made of poly lactic acid (PLA) made of corn starch, which is known as environmentally friendly, is also harmful to health by mixing about 15 to 20% of chemicals. Chemicals are eluted from the PLA cup itself, and when the corn starch is decomposed during landfill, the chemicals are finely dispersed and introduced into the ecosystem, which is harmful to the environment and health.

The health and environmental problems of disposable food containers (paper cups, cartons) have long been a problem that humanity has not been able to solve.

Utility Model Application No. 20-1998-0015053 "Harless structure of disposable container using aluminum sheet or foil" Patent Publication No. 10-1998-0072028 "Packing container for cup noodles and container sides made of aluminum and synthetic resin" Registration Patent No. 10-0607404 "Disposable food container using thin aluminum plate" Registered Patent No. 10-1466224 "Aluminum endothelial disposable food container" Registered Patent No. 10-1616852 "Method for manufacturing aluminum endothelial paper cup ramen container"

Currently used paper containers (paper cups, cartons, etc.) are coffee cups, cup noodles, cup rice, and cup noodles. It is used for milk packs, beverage packs, liquor packs, food containers, beverage containers, soup containers, and stew containers, and has the following problems.

1. There is no paper container that is safe for human health. Synthetic resins such as PE and PP inside the container dissolve a large amount of carcinogens and environmental hormones as the food and beverage gets hot.

2. When food and beverage are put in a synthetic resin inner container, the synthetic resin melts, the taste changes, and air flows, making long-term storage difficult.

3. Synthetic endothelial resin and envelope (paper) are fused, making it difficult to recycle paper.

4. In the aluminum endothelial container, the area where the aluminum surfaces come into contact with each other is not sealed.

5. It is difficult to form aluminum endothelial containers due to low adhesion between aluminum and synthetic resins such as PE, PP, and PS used in existing food containers. PE is somewhat adhesive, but insufficient.

6. Disposal after use once for disposable use.

7. When the synthetic resin layer is placed on the outer surface of the paper, the manufacturing process is added, which increases the cost and makes it difficult to recycle the paper.

8. Synthetic resin does not rot when landfilling.

9. PLA (poly lactic acid), which is made of corn starch, actually contains about 15 to 20% of 12 kinds of chemicals, and there is no true eco-friendly container for health.

10. The amount of synthetic resin used in food containers is high.

In order to achieve the above object, the eco-friendly pro-healthy aluminum endothelial paper container, which is easy to recycle of the present invention, is generally in a paper container including an aluminum foil layer, the inner surface is an aluminum foil layer, and the outer surface is made of paper or synthetic resin. The outer surface may be composed of a composite material including paper. Paper containers include paper cups and cartons.

The aluminum endothelial paper cup consists of a side part (side paper, side board) and a bottom part (base, bottom board, bottom), and a lid can be attached to the top.

In another embodiment of the present invention, the aluminum endothelial can be configured only on the side of the container.

The paper pack is mainly composed of an integral type in which upper, lower, and side portions are all connected, and only the side portion and the lower portion are integrally formed, and the upper portion may be composed of a combined type. It is also possible to combine the upper and lower side parts. The stopper can be attached mainly to the top.

In one embodiment of the paper cup of the present invention, the side portion includes an aluminum inner shell and a paper outer shell formed with paper, which is formed outside the aluminum inner shell. The outer surface of the paper shell may be exposed to the outside of the paper or a synthetic resin or a synthetic resin containing a polar material may be attached to the outside of the paper, the side portion and the bottom portion bonding, the joint forming the side portion round, the roll between the aluminum inner shell and the paper outer shell. Sheet-like bonding; It is joined by one or more of water-soluble adhesives, synthetic resins, and synthetic resins containing polar substances. It is preferable to use a water-soluble adhesive or a synthetic resin containing a polar material to form the side portion and the bottom portion or to form a round side portion.

The melting point or decomposition point of the adhesive to be used may be more than the use temperature of the container, but for general purpose, it is preferably 100 ° C or higher, and more preferably 100 ° C or higher.

At least one of a synthetic resin, a water-soluble adhesive, and a synthetic resin containing a polar material is disposed on the bonding surface 30 under the side surface of FIG.

The aluminum endothelial paper cup of another embodiment of the present invention is a paper cup in which an aluminum foil is located on the inner surface, in one or more of the side surface 20 or the bottom surface 30 of the aluminum surface among the side parts (side sheets) of the container, a melting point or As the decomposition point is 100 ° C or higher, more preferably as the softening point is 100 ° C or higher; One or more of the water-soluble adhesive, synthetic resin, and synthetic resin containing polar materials for adhesion are applied in whole or in part to the side 20 or bottom 30, which is the joining site, when forming the container. More preferably, the molding joint of the side portion and the bottom portion or the joint forming the side portion roundly uses a water-soluble adhesive or a synthetic resin containing a polar material.

In another embodiment of the present invention, in a paper container comprising an aluminum foil layer, the inner surface is an aluminum foil (1), the outer surface is paper or synthetic resin, in a paper container having a side portion and a bottom portion, or a side portion upper bottom portion; When forming the side portion of the paper container, forming and bonding the side portion and the bottom portion, or forming and bonding the side portion and the upper portion; At least one of the adhesives used for the bonding portion is formed by disposing a synthetic resin containing a water-soluble adhesive or a polar substance on the bonding portion.

Mainly rectangular cartons are manufactured by folding and bonding the fabric ends. When viewed in an unfolded state before folding, the entire inner surface can be made of aluminum foil, and the synthetic resin is exposed on the upper and lower junctions of the carton and other parts It can also be made of aluminum endothelium. It is more preferable to place synthetic resin or a synthetic resin containing a polar material at a site where the aluminum endothelial is attached to a part or the entire side of a carton, and is molded into a square, and more preferably, a synthetic resin containing a polar material. When forming the upper and lower parts of the carton, bonding is performed by using a synthetic resin or a synthetic resin containing a polar material, which is disposed on the adhesive site. When even one side of the joint is aluminum, it is more preferable to arrange a synthetic resin containing a polar substance. The adhesive of the carton may be placed on the inner surface, the outer surface, or both sides.

Adhesives that do not come into direct contact with hot substances may have an adhesive that has a melting or decomposition point above the operating temperature.

In the present invention, the water-soluble adhesive is polyvinyl alcohol (Polyvinyl alcohol, PVA) based, polyvinyl acetate (PVAc, vinyl acetate) based, ethylene vinyl acetate (EVA) based, hydroxypropyl methylcellulose (Hydroxypropyl methylcellulose, HPMC), hydroxypropyl methylcellulose phthalate (HPMCP), luxurious vegetable starch, dextrin, soluble starch, oxidized starch, glue, casein, gum arabic, paste, biodegradable adhesive resin, acrylic emulsion, cellophane It may include one or more.

In one embodiment, the synthetic resin containing the polar material is an epoxy resin-based, polyamine-based, acid anhydride-based, polyamide-based, resol resin-based, polysulfide-based, acrylic, phenolic resin-based, polyurethane-based, silicone-based, rubber-based, polyamideimide-based , Polyimide series, polybenzimidazole series, polyester series, polyvinyl acetate series, polyolefin series, nylon series, urea resin series, aniline resin series, toluene sulfonic acid amide series, isocyanate alkyd series, cyanoacrylate series, polydiphenyl It may include any one or more of ether-based, polyvinyl acetate-based, melamine-based.

In one embodiment, the polyamine system comprises at least one of diethyltriamine, triethylenetetramine, diethylaminopropylamine, xylenediamine, modified aliphatic polyamine, phenylenediamine, aminodiphenylsulfone, and the acid The anhydride system may include any one or more of maleic anhydride, phthalic anhydride, and hexahydrophthalic anhydride.

In one embodiment, the synthetic resin or the synthetic resin containing the polar material is a polyolefin-based synthetic resin; Polyester type; Nylon type; It may include any one or more synthetic resins of the polystyrene-based.

In one embodiment, the synthetic resin containing the polar material, HDPE, MDPE, LDPE, LLDPE, PP, polyester, nylon, PS, PET, biodegradable synthetic resins, PLA (poly lactic acid), biodegradable polar materials It is mixed with any one or more of the resins.

In one embodiment, the synthetic resin or the synthetic resin containing the polar material may include biodegradable resins.

In one embodiment, the water-soluble adhesive, the synthetic resin or the synthetic resin containing the polar material may be used as a hot melt adhesive.

In one embodiment, the synthetic resin that can be attached to the outer surface of the paper envelope may include a polar adhesive material or biodegradable resins.

An embodiment of the method for manufacturing a paper cup container in which the aluminum foil of the present invention is located on the inner surface,

Step 1 to remove the oil of the aluminum foil;

A second step of forming a fabric with aluminum attached by bonding the rolled paper and aluminum in a plate shape using a water-soluble adhesive having a melting point or a decomposition point of 100 ° C. or higher, or a synthetic resin containing a polar material;

Step 3 of cutting the fabric produced in the above step 2, rounding it, and forming a side sheet of an aluminum inner paper cup by using a synthetic resin containing a water-soluble adhesive or a polar material having a melting point or a decomposition point of 100 ° C. or higher;

After cutting the base with the fabric or a separately prepared base or base fabric, a step 4 of forming a paper cup using a water-soluble adhesive or a synthetic resin containing a polar material having a melting point or decomposition point of 50 ° C or higher between the side and base;

Provides a method for manufacturing an eco-friendly eco-friendly aluminum endothelial paper cup, which is easy to recycle, comprising the steps regardless of the order.

A method of manufacturing a paper cup in which an aluminum foil of another embodiment of the present invention is located on an inner surface includes manufacturing a side portion, and joining the side portion and a bottom portion, and manufacturing the side portion adhesives the aluminum endothelial and paper envelope in a roll sheet state. It may include bonding, wherein, the outer surface of the paper sheath may be attached with a synthetic resin, when bonding the aluminum inner shell and the paper shell, the adhesive has a melting point or a decomposition point of 100 ° C or higher, water-soluble adhesive, synthetic resin , Use one or more of the synthetic resin containing a polar material; As the adhesive used when forming the container by round-molding the side portion or bonding the side portion and the bottom portion, at least one of a water-soluble adhesive and a synthetic resin containing a polar material is used.

In the carton, the lower portion of the upper side portion may be integrally formed, or only the side portion and the lower portion may be integrated, and the upper portion may be combined with a lid type. Of course, the lower part can also be combined. One example of manufacturing a carton is as follows.

Step 1 of attaching the aluminum foil to the entire inner surface of the paper pack fabric to be used with a water-soluble adhesive or synthetic resin or synthetic resin containing a polar material;

A second step of placing a synthetic resin containing a synthetic resin or a polar material on the upper and lower adhesive parts 20 or a portion to be joined thereto;

3 steps to cut the cartons;

A fourth step of placing a synthetic resin or a synthetic resin containing a polar material in at least one of the side bonding portion 30 of the cut carton or the outer surface portion to be joined thereto;

Step 5 of attaching the stopper to the carton part if necessary;

6 steps of forming a carton;

It provides a method of manufacturing a carton that includes the above steps in any order.

Another example of the carton pack manufacturing is as follows.

A first step of placing a synthetic resin or a synthetic resin containing polar substances on the inner surface of the paper;

A second step of attaching aluminum foil with synthetic resin or synthetic resin containing polar materials to the inner surface except the upper and lower adhesive portions 20;

3 steps to cut the cartons;

A fourth step of placing a synthetic resin or a synthetic resin containing a polar material in at least one of the side bonding portion 30 of the cut carton or the outer surface portion to be joined thereto;

Step 5 of attaching the stopper to the carton part if necessary;

6 steps of forming a carton;

It provides a method of manufacturing a carton that includes the above steps in any order.

Examples of the method of manufacturing the carton are based on the fact that the lower portion of the upper side portion is integral, but can be applied in the same manner when only the side portion and the lower portion are integral. However, in this case, the upper part is made of plastic or metal, which is separately manufactured, with a synthetic resin or a synthetic resin containing polar materials. When bonding, a heating process may be included.

The main effects of the present invention are as follows.

1. By implementing an aluminum endothelial container in a paper container, it prevents carcinogens and environmental hormones.

2. A synthetic resin containing polar material can seal the part where aluminum comes in contact, and realizes an aluminum endothelial container with excellent adhesive strength at the joint.

3. When using water-based adhesives, disposable food containers that facilitate paper recycling are provided.

4. The quality of food does not change due to the prevention of air distribution and the prevention of synthetic resin elution.

5. Provide a luxurious paper cup with metallic luster.

6. Since the inside is made of metal, recycled paper can be used to reduce manufacturing costs.

7. Provide a paper cup that can be washed and reused.

8. By recycling paper, forests are protected and contribute to the prevention of global warming,

9. Reducing the amount of synthetic resin and reducing plastic pollution

10. Promote people's health.

11. Contribute to the relevant industry and economic development.

1 is a schematic representative cross-sectional view mainly focusing on a side portion of an aluminum endothelial paper cup of the present invention. The inner surface is attached with aluminum foil (1), the outside is paper (4), and the paper and aluminum are attached with an aqueous adhesive (3). A synthetic resin layer (which may contain a polar material or biodegradable resins) may be disposed on the outside of the paper. As the outer synthetic resin layer, a foamed synthetic resin (synthetic resin containing gas) may be used.
Figure 2 is an aluminum endothelial paper cup 850cc food container and 13oz beverage cup prototype photo
Figure 3 is an aluminum endothelial paper cup 13 oz (≒ 368cc) beverage cup (coffee cup) prototype photo
4 is an aluminum endothelial paper cup 850cc prototype photo
FIG. 5 is a partial cross-section of an embodiment in which an aqueous adhesive layer 3 is disposed between an aluminum inner shell 1 and a paper jacket 4.
Figure 6 is a partial cross-section of an embodiment in which a synthetic resin adhesive layer 2 is disposed between an aluminum inner shell 1 and a paper jacket 4
7 is a partial cross-section of an embodiment in which a synthetic resin adhesive layer 2 and an aqueous adhesive layer 3 are disposed between an aluminum inner shell 1 and a paper envelope 4;
8 is an embodiment in which a synthetic resin or water-based adhesive containing a polar material for forming a container is locally disposed on the side portion 20 of the paper cup side sheet (side portion) 10.
9 is an embodiment in which the adhesive is disposed on the side portion 20 and the bottom portion 30 of the side surface (side sheet) of the paper cup. In addition to the fan shape, it can be made into a cylindrical shape with the same inner and lower inner diameter.
FIG. 10 is an example in which three pieces of cartons with aluminum endothelium are attached in a plan view before cutting the cartons individually. This figure centers on the side of the carton and may include upper and lower portions.
11 shows an example of a top view of a paper pack cut into pieces.
The outer surface of the paper container of the present invention may be exposed to paper, or a synthetic resin or a polar resin-containing synthetic resin may be attached to the outer surface of the paper. The synthetic resin 5 on the outer surface may be attached in whole or in part.

The aluminum endothelial paper cup and carton will be described by the accompanying drawings and examples. The present invention can be implemented in many different forms, and is not limited to the embodiments described herein. Throughout the specification, the same reference numerals are assigned to the same or similar components. When describing a range in the present specification, "1 to 5" means "1 or more and 5 or less".

The aluminum endothelial paper container, which is a pro-health-friendly disposable food container of the present invention, is generally a paper container including an aluminum foil layer, and the inner surface is mainly aluminum foil, and the outer surface is paper or synthetic resin (a polar material may be included). A synthetic resin may be attached to the outer surface of the paper, and in this case, a synthetic resin containing a polar material is preferable. In the present invention, the paper envelope means the envelope including paper. Inclusive or inclusive means partial to whole. In the present invention, the synthetic resin is used in the same sense as the synthetic resin adhesive. Likewise, biodegradable resins are synonymous with biodegradable resin adhesives. Biodegradable resin means biodegradable synthetic resin and biodegradable natural resin. In the present invention, water-based adhesive is used in the same sense as water-soluble adhesive. The paper cup consists of a side part (side paper, side board) and a bottom part (bottom, base, bottom board). The paper cup may be attached with a lid (top). The aluminum endothelial paper cup may have an aluminum endothelial disposed entirely inside or only a side surface. Paper cups are synonymous with paper cup containers. Paper cups can have the same inner or lower inner diameter.

The paper pack can be used for milk packs, beer packs, beverage packs, etc., and the upper and side parts and the bottom part are mainly composed of an integral type. It may be a structure that combines the top or bottom. Paper containers (paper cups, cartons, etc.) of the present invention are coffee cups, cup noodles, cup rice, cup noodles. It can be used for milk, beverage, liquor, food containers, beverage containers, soup containers, stew containers, etc., and includes these foods. Foods using these containers can be raised to at least 30% to 100% of food value, as consumers prefer healthy foods. Health-conscious consumers prefer food in this container, even if they pay 30% to 100% more on the same food.

In the present invention, the adhesive means a water-soluble adhesive, a synthetic resin, a polar material, and a synthetic resin containing a polar material. In the present invention, synthetic resins or synthetic resins containing polar substances are used in the broad sense including biodegradable resins. Synthetic resins also include synthetic resins containing polar substances.

In one embodiment of the present invention, the side portion of the paper cup is provided with a paper envelope including paper, formed on the outside of the aluminum shell and the aluminum shell, and the outer surface of the paper shell is exposed to the outside of the paper, or on the outside of the paper. Synthetic resins or synthetic resins containing polar materials may be attached, and the adhesive used in the present invention mainly has a melting point or a decomposition point of 100 ° C or higher, and more preferably a softening point of 100 ° C or higher. A roll sheet-like bond between the aluminum inner shell and the paper outer shell; It is joined by one or more of water-soluble adhesives, synthetic resins, and synthetic resins containing polar substances. Water-soluble adhesives or synthetic resins containing polar materials are used to form round joints on the side surfaces or to form joints on the side and bottom parts. Since the 30 parts of FIG. 9, which are the joints of the side and the base, do not directly contact hot food, an adhesive having a melting point or a decomposition point of 100 ° C. or less can be used. Put boiling water in a paper cup and measure the temperature of Fig. 9 30 on the supporting part at room temperature in the room temperature at about 30 ℃ to 50 ℃, so an adhesive with a melting point or a decomposition point of 50 ℃ or higher can be used depending on the use environment.

In one embodiment of the present invention, in a paper container including an aluminum foil layer, the inner surface is an aluminum foil (1), the outer surface is paper or synthetic resin, in a paper container having a side portion and a bottom portion, or a side portion upper bottom portion; When forming the side portion of the paper container, forming and bonding the side portion and the bottom portion, or forming and bonding the side portion and the upper portion; At least one of the adhesives used for the bonding portion is formed by disposing a synthetic resin containing a water-soluble adhesive or a polar substance on the bonding portion.

In addition, aluminum endothelial cartons are made by folding and folding a sheet of paper with aluminum foil attached to it. The entire inner surface of the paper pack fabric may be made of aluminum foil, and in this case, an adhesive is disposed on the upper and lower joints. Alternatively, the top and bottom joining portions of the carton are exposed to the synthetic resin, and the other inner surfaces may be made of aluminum. It is preferable that a synthetic resin containing a polar material is disposed at a portion to be joined by bonding a side portion of a paper pack mainly by forming a square. The placement method can be arranged on the aluminum part of the inner surface or on the outer surface of the paper.

In the case of forming the upper and lower parts of the carton, the synthetic resin is exposed to the adhesive part, and the synthetic resin or the synthetic resin containing the polar material is placed at the time of molding and the synthetic resin containing the polar material is placed even if one of the bonding parts is aluminum. It is desirable to increase the adhesion. The adhesive of the carton may be placed on the inner surface, the outer surface, or both sides. The melting point or the decomposition point of the adhesive to be used may be more than the use temperature of the container, but is generally 100 ° C or higher, and more preferably 100 ° C or higher. However, food containers that are handled below room temperature in the entire process of handling beer, beverages, etc. may use an adhesive having a melting point and a decomposition point of 50 ° C or more in consideration of temperature and room temperature.

The arrangement of aluminum in the carton of the present invention may be arranged entirely on the inner surface of the carton, which is convenient for mass production. Alternatively, as shown in FIGS. 10 and 11, the upper and lower adhesive portions 20 of the carton may be attached to each other. After the aluminum endothelium is attached, the carton is cut as in the embodiment of Fig. 11 so that it can be molded to the required size. The individually cut paper pack fabric passes through a mold and is formed into a paper pack. Mainly in the upper position of the carton, a stopper for pouring and sealing the contents can be attached. When attaching aluminum to the entire inner surface, a synthetic resin or a synthetic resin containing a polar material may be disposed upon bonding to the 20 or 30 parts of FIGS. 10 to 11. It is also possible to place an adhesive on the outer surface, and it is more preferable to bond the synthetic resin containing the polar material. When the synthetic resin is disposed on only one of the inner surface or the outer surface, or when no adhesive is disposed, it is preferable to place a synthetic resin containing a polar substance on a part or the whole of the opposite surface to be adhered thereto.

In the aluminum endothelial paper container of the present invention, at least the inner surface of the side portion is provided with an aluminum foil layer 1, and the outer surface may be made of any material, but preferably includes paper.

One embodiment of a method of manufacturing a paper cup container in which the aluminum foil of the present invention is located on the inner surface

Step 1 to remove the oil of the aluminum foil;

A second step of using a water-soluble adhesive having a melting point or a decomposition point of 100 ° C. or higher, a synthetic resin or a synthetic resin containing polar substances, and bonding the rolled paper envelope and aluminum in a plate shape to form a paper fabric with aluminum attached thereto;

Step 3 of cutting the fabric produced in the above step 2, rounding it, and forming a side sheet of an aluminum inner paper cup by using a synthetic resin containing a water-soluble adhesive or a polar material having a melting point or a decomposition point of 100 ° C. or higher;

A step 4 of forming the paper cup by combining the side paper and the base paper with a water-soluble adhesive or a synthetic resin containing a polar material after cutting the base material with the fabric or a separately produced base material or base material;

Five steps to finish the top of the cup by curling:

Provides a method for manufacturing an eco-friendly eco-friendly aluminum endothelial paper cup, which is easy to recycle, comprising the steps regardless of the order.

The outer surface of the paper envelope may be attached to the synthetic resin 5 in whole or in part, and when attached, it is more preferable to arrange the synthetic resin containing polar material.

Method of manufacturing a paper cup in which an aluminum foil of another embodiment of the present invention is located on the inner surface;

Manufacturing a side part, including bonding the side part and the bottom part, and manufacturing the side part includes bonding an aluminum inner surface of a roll sheet state and a paper outer surface with an adhesive, wherein the outer surface of the paper outer surface is made of synthetic resin. Can be attached, and when the aluminum inner shell and the paper shell are bonded, the adhesive has a melting point or a decomposition point of 100 ° C. or higher, and uses at least one of a water-soluble adhesive, a synthetic resin, and a synthetic resin containing a polar material;

When forming the container by round-molding the side portion or by bonding the side portion and the bottom portion, at least one of the adhesives used is a water-soluble adhesive or at least one of a synthetic resin containing a polar material.

In the carton, the upper, side and lower parts may be integrally formed, or only the side and lower parts may be integrally formed and the upper parts may be combined. One example of the manufacture of a carton is as follows.

Step 1 of attaching aluminum foil to the entire inner surface of the paper fabric to be used with a water-soluble adhesive or synthetic resin or a synthetic resin containing a polar material;

A second step of placing a synthetic resin containing a synthetic resin or a polar material on the upper and lower adhesive parts 20 or a portion to be joined thereto;

3 steps to cut the cartons;

A fourth step of placing a synthetic resin or a synthetic resin containing a polar material in at least one of the side bonding portion 30 of the cut carton or the outer surface portion to be joined thereto;

Step 5 of attaching a stopper to a part of the carton if the stopper is needed;

6 steps of forming a carton;

It provides a method of manufacturing a carton that includes the above steps in any order.

Another example of the carton pack manufacturing is as follows.

A first step of placing a synthetic resin or a synthetic resin containing polar substances on the inner surface of the paper;

A second step of attaching aluminum foil with synthetic resin or synthetic resin containing polar materials to the inner surface except the upper and lower adhesive portions 20;

3 steps to cut the cartons;

A fourth step of placing a synthetic resin or a synthetic resin containing a polar material in at least one of the side bonding portion 30 of the cut carton or the outer surface portion to be joined thereto;

Step 5 of attaching the stopper to the carton part if necessary;

6 steps of forming a carton;

It provides a method of manufacturing a carton that includes the above steps in any order.

The reason why the melting point or decomposition point of the adhesive used in the container containing the hot food is preferably 100 ° C or higher is because the boiling temperature of the water is 100 ° C, so the bonding of the container must be maintained at 100 ° C. As an embodiment of the present invention, when 100 ° C water was contained in a 850cc paper cup, the temperature of the side molded adhesive portion was raised to about 90 ° C, and the paper cup support was 30 ° C to 50 ° C. Therefore, considering the safety factor of 10%, 100 ° C or higher is preferable. When the food is boiled with this container, it can be 100 ℃.

The water-soluble adhesive or synthetic resin (including a synthetic resin containing a polar substance) has a melting point or a decomposition point of 100 ° C. or higher, as well as a case where the entire adhesive has a melting point or a decomposition point of 100 ° C. or higher, as well as a single type or a mixture of several types. It may also include a case in which the melting point or the decomposition point of one component among the plurality of components included in 100 ° C or more. Preferably, the melting point or decomposition point of the entire adhesive component is preferably 100 ° C or higher. More preferably, the softening point of the entire adhesive is preferably 100 ° C or higher. The "melting point", "decomposition point", softening point "can be measured by a conventionally recognized method.

Paper containers are meant to include paper cups or cartons.

In the present invention, it is preferable to use aluminum foil having excellent air barrier properties. A vacuum-deposited aluminum foil can be used, but the adhesion of the endothelium and the air barrier properties are less than that of the aluminum foil.

Detailed means for the present invention are described item by item.

1. Environmental Hormone and Carcinogen Shielding Method-Aluminum foil is placed inside the paper container to prevent carcinogen and environmental hormone from dissolving in food.

2. Resource recycling plan-When water-soluble adhesive is used for bonding the aluminum inner and paper outer shells, the paper outer shell is easily separated when the paper container is immersed in water.

3. A method of sealing the area where the aluminum contacts-At least one of the water-soluble adhesive, synthetic resin, and synthetic resin containing polar material is arranged on the lower part 30 of the side paper. In the case of a carton, a synthetic resin containing polar material is placed on at least one side of the joint.

4. Reusable, advanced and portable optimization method-The interior of the paper cup is made of aluminum, and the synthetic resin is placed on the outside of the container, making it waterproof, so it is more convenient for washing and reuse, so it can be reused for a long time. It is light and portable.

5. Cost reduction plan-Even if recycled paper is used, the quality of the container is maintained, so that the cost of paper can be saved.

6. Adhesion of aluminum inner skin and paper outer skin-Containers mainly for reuse may be used synthetic resin, but containers mainly for paper resource recycling are preferably bonded with water-soluble adhesive and dried. Drying may include heating. It is better to use a water-soluble adhesive that is almost non-toxic.

Recycled containers do not require paper recycling, so you can use synthetic resin. When bonding the aluminum inner skin and the paper outer skin, in addition to the water-soluble adhesive, it can be bonded using biodegradable resins such as synthetic resins such as PE, poly lactic acid (PLA), and starch-containing plastics, which have a melting point or a decomposition point of 100 ° C or higher. In the present invention, the synthetic resin is used as a broad concept that encompasses both general synthetic resins and biodegradable resins.

7. Water-soluble adhesive material for container molding-As adhesive for container (cup) molding needs a large adhesive strength, it is better to have a higher adhesive strength, such as polyvinyl acetate (PVAc) or ethylene vinyl acetate (EVA). Since time is required, increase the solid content as much as possible and make the water content small. It is most preferable to apply to the joint at the joint site (20, 30 in FIG. 9).

If a water-soluble adhesive is used on the joint of the container for storing water for a long time, the joint may be absorbed and peeled off.

8. Synthetic resin adhesive material for forming paper cup containers-It is preferable to use synthetic resin with melting point or decomposition point of 100 ℃ or higher (more preferably, synthetic resin with softening point of 100 ℃ or higher, biodegradable resins), melting point or decomposition point of 100 ℃ It is more preferable that the above-mentioned adhesive polar material is contained, so that the melting point or the decomposition point as a whole is 100 ° C or higher. Of course, when the use temperature of the container is always less than 100 ° C, an adhesive whose melting point or decomposition point exceeds the use temperature may be used. One or more of the following methods may be used for the placement of the synthetic resin joints.

(1) In the roll state of the fabric, synthetic resins containing polar substances are disposed on the outer surfaces of the side (side paper) and bottom (bottom) as a whole. Attach it.)

(2) Partially placed on the joints (20, 30) of the side (side) or bottom (base).

(3) The side paper is placed on the side bonding surface 20 after cutting, and the base is placed on the entire outer surface in the state of the fabric roll.

(4) When placed on the aluminum surface 30 of the lower part of the side paper, the cup can be formed with only synthetic resin attached to the side paper.

9. Not using or reducing synthetic resin-When using water-soluble adhesive, it is possible to significantly reduce the use of synthetic resin to about 0 ~ 10%.

10. Decomposition method during landfill-When biodegradable resins are used among synthetic resins, they are well decomposed during landfill.

11. Paper cup recycling plan-To make it easier to recycle paper, make sure that at least the side paper is exposed on the outside. It is preferable that the container for reuse has a synthetic resin layer on the outer surface for waterproofing of the outer surface during washing.

The melting point or decomposition point of the water-soluble adhesive is preferably 100 ° C or higher, and it is preferable that the synthetic resin for cup molding bonding is higher than the melting temperature at the time of bonding. Water-soluble adhesives include polyvinyl alcohol (PVA), polyvinyl acetate (PVAc, vinyl acetate), EVA (ethylene vinyl acetate), hydroxypropyl methylcellulose (HPMC), hydroxypropyl methylcellulose Phthalates (Hydroxypropyl methylcellulose phthalate, HPMCP), glue, casein, gum arabic, paste, biodegradable adhesive resin, acrylic emulsion, cellophane, may include one or more of vegetable starch. The vegetable starch may include, but is not limited to, one or more of gelatinized starch, dextrin, soluble starch, and oxidized starch. What can be used as a water-soluble adhesive is also possible if it is not soluble in water or in an aqueous emulsion and has significant adhesive strength.

Polyvinyl alcohol is preferred to be used as a water-soluble adhesive when attaching aluminum and paper in a sheet form for ease of recycling of paper cups. To this end, PVA (polyvinyl alcohol) components were examined. The following paper, which investigated the oral toxicity of PVA, which is also used as a coating agent for pharmaceuticals and foods, showed little toxicity. "Review of the oral toxicity of polyvinyl alcohol (PVA)" Author DeMerlis C.C, Schoneker D.R Journal Information Food and Chemical Toxicology 2003, Vol. 3 No. 3 319p ~ 326p ISSN 0278-6915.

Polyvinyl acetate is used to bond aluminum foil and paper when packaging tobacco, and is also used as a base for chewing gum. Korea's Wukong Co. has been certified by the Korean government for this material. The polyvinyl acetate MSDS toxicity data is as follows.

Polyvinyl acetate LD50 25000 mg / kg Rat

The water-soluble adhesive may include one or more of the above listed types, or may be used alone or in combination of two or more. Preferably, the water-soluble adhesive may include one or more of polyvinyl alcohol-based, polyvinyl acetate-based, and ethylene vinyl acetate-based. Polyvinyl acetate (EVA) or polyvinyl acetate (PVAc) has stronger adhesion than PVA.

Other materials that can be used as water-soluble adhesives are all water-soluble adhesives, and after drying, it is possible to loosen the adhesion again upon contact with water.

Water-soluble adhesives can be mixed. You can mix starch (preferably starch) or water-soluble adhesives such as PVAc, PVA or EVA above. For example, the decomposition point of PVA is 200 ° C, and the melting point of PVAc is 135 ° C. The melting point of EVA (ethylene vinyl acetate) is 40 ° C to 110 ° C. When mixing water-soluble adhesives, it can be used if the melting point or decomposition point is 100 ° C or higher as a whole. Of course, the lower bonding portion 30 of the side of the paper cup, even if 100 ° C water is put into the paper cup, the temperature is 50 ° C or less, so in this case, an adhesive having a melting point or a decomposition point of 50 ° C or higher can be used.

3. Safety and convenience of aluminum endothelial:

It is preferable to use a thin foil having a thickness of about 6 μm. This is about the thickness of gum paper. Since the melting point of aluminum is 660 ℃, it melts in an incinerator of about 1000 ℃ or higher to become a fine ash, so there is no problem of incineration residues. Of course, other thicknesses can be used. When aluminum is exposed to oxygen or water, an aluminum oxide protective film having a thickness of about 10 nm is formed with 4Al + 3O ₂ → 2Al ₂ O ₃ . This completely protects the metal in the range of pH 4 to pH 9 (* Source: "Food Packaging Scholarship", p.69, Park Moo-hyun and 2 others, Hyungseol Publishing Company). The aluminum endothelial container is safe for health since the food and beverage to which the present invention is applied is neutral at a pH of about 7.

Examples of the method for making the paper cup of the present invention can be used in the following 1 to 9.

1. When attaching aluminum and paper in roll form, attach the paper surface and aluminum foil to be placed on the inner side of the container in a plate shape with synthetic resin (including biodegradable resin) or water-soluble adhesive. However, when bonding with a water-soluble adhesive, it is preferable to undergo a heat drying process. Of course, synthetic resins containing polar substances can be used. In the present invention, a water-soluble adhesive such as starch starch having a specific melting point and a decomposition point of 200 ° C even at 100 ° C or higher is also included in a water-soluble adhesive having a melting point or a decomposition point of 100 ° C or higher.

2. When using a cellophane film between the aluminum layer and paper, use a one-side moisture-proof cellophane film so that the moisture-proof surface is attached to the surface that comes in contact with the aluminum layer, or place a synthetic resin layer between the aluminum layer and the cellophane film.

3. In order to facilitate resource recycling, it is preferable to apply a water-soluble adhesive or a synthetic resin containing a polar material for adhesion only to the joints of the sides and the base during cup molding, and to adhere them. In this case, it is preferable to cut the side paper and the base paper, and then include them on the adhesive portions 20 and 30. A synthetic resin (including biodegradable resin) or a synthetic resin containing a polar material may be applied to the aluminum portion 30 of the lower side of the side paper. When applying synthetic resin to 30 parts, it is desirable to place synthetic resin containing polar substances on the outer surface of the base.

4. The base (bottom) does not use aluminum, and synthetic resins (including biodegradable resins) can be used on the inner surface like existing bases, and synthetic resin with a melting point of 100 ° C or higher on the outer surface of the base or more preferably for adhesion Synthetic resins containing polar substances can be arranged as a whole. The entire base can be used only as synthetic resin without paper.

5. Synthetic resins used for cup forming bonding, for example, PE and PP, are non-polar materials, which have low adhesion, but can contain one or more polar adhesive materials to increase adhesion. Only polar materials for adhesion may be used.

Looking at <Example 1>, the PE containing a polar material has a stronger adhesive strength of 10 times or more than the adhesive strength of the non-polar LDPE, thereby enabling the adhesion of slippery aluminum and paper. Thus, it was used in the examples of the present invention.

When using PE, it is preferable to use HDPE, MDPE, or LLDPE, which has a higher melting point and softening temperature than LDPE used for the existing paper cup container inner shell, for safety of the cup in a high temperature 100 ℃ environment.

A hot melt having a melting point of 100 ° C. or higher may be used when forming a cup. A hot melt is a type of synthetic resin that increases adhesion by physically mixing or chemically bonding a polar material to synthetic resin, but may be made of a film, but is generally sprayed or applied in a molten state by heating. When hot melt is applied to the adhesive surface, it hardens and adheres in a short time. Of course, an aqueous adhesive can also be used.

6. When forming the container, it is preferable that the synthetic resin for adhesion contains a polar adhesive material, and may be disposed on a part of the aluminum surface, or may be partially or entirely on the outer surface of the paper.

7. Container molding bonding is mainly composed of heat bonding. As the heating method, one or more of direct heating, mold heating, hot air heating, ultrasonic bonding, impulse bonding, high-frequency bonding, and laser bonding may be used. However, as in the case of the hot melt, spraying or coating of a synthetic resin component already heated and melted can be used for bonding without separately heating the joint. It can also be bonded under pressure after application of the adhesive without heating.

8 Natural pulp can be used for the paper used for the envelope, and recycled paper can also be used.

9. For paper cups composed mainly of double containers, such as cup noodles or cup rice containers, the present application relates to an inner paper cup to which an aluminum foil is attached.

Among the water-soluble adhesives, vegetable starch does not melt or decompose below 100 ° C, and decomposes by burning at high temperatures, which corresponds to a material having a melting point or a decomposition point of 100 ° C or higher.

The polar material can form a hydrogen bond with cations of various metals in the aluminum foil, and increase the electrical dipole moment van der Waals force between the materials to strengthen the adhesion. Thus, the adhesion between aluminum and paper synthetic resin can be greatly enhanced during container molding. Non-polar synthetic resins have weak adhesion because only weak dispersion force among van der Waals forces acts.

The polar adhesive material may be one of the following series.

1.Epoxy resin system

2.Polyamine system

(1) Aliphatic polyamines-xylenediamine including diethyltriamine, triethylenetetramine, diethylaminopropylamine, m-xylenediamine, modified aliphatic polyamine, etc.

(2) Aromatic polyamines-phenylenediamine containing metaphenylenediamine, etc., aminodiphenylsulfone, etc.

3. Acid Anhydride System-Maleic anhydride, phthalic anhydride, hexahydrophthalic anhydride, etc.

4.Polyamide system

5. Resol resin system

6.Polysulfide system

7.Acrylic

8.Phenol resin system

9.Polyurethane

10.silicone

11.Rubber

12.Polyamideimide system

13.Polyimide system

14.Polybenzimidazole system

15. Polyester

16.Polyvinyl acetate type

17. Polyolefin

18.Nylon

19. Urea resin system

20.Aniline resin system

21. Toluene sulfonic acid amide system

22. Isocyanate alkyd system

23.Cyanoacrylate system

24.Polydiphenyl ether system

25.Polyvinyl acetate type

26. Melamine.

The water-soluble adhesive or synthetic resin may be a hot melt adhesive, a conductive adhesive, an instantaneous adhesive, or an anaerobic adhesive.

The polar adhesive material used in the present invention may be used alone or in combination of two or more of the types listed above. The two or more types means not only the substances listed above, but also two or more kinds including substances not listed in addition to the substances.

As an example of a material that can be used as a polar material adhesive because it has a melting point of 100 ° C or higher, the melting point of hot melt varies depending on the main raw material. Thermal deformation occurs at 130 ° C to 130.5 ° C, the boiling point is 138.5 ° C, and acrylic methacrylate methyl is 118 to 122 ° C. Several polar substances can be mixed and used.

A polar material adhesive with a melting point of 100 ° C or higher is used alone or in combination, or PE (HDPE, MDPE, LDPE, LLDPE, etc.), PP, polyester, nylon, PS, PET, biodegradable synthetic resins, PLA (poly lactic acid) , Biodegradable resins and the like.

The polar material-containing synthetic resin is polyethylene (eg, one or more of high density polyethylene, medium density polyethylene, low density polyethylene, and ultra low density polyethylene), polyolefin, such as polypropylene; Polyester systems such as polyethylene terephthalate; Nylon type; It may contain one or more synthetic resins of the polystyrene-based.

The adhesive layer may be formed singly or in two or more layers.

The bottom portion of the paper container may be N-shaped or amorphous, such as circular or square, but is not limited thereto.

As a method of simply checking the adhesion of the adhesive, in the peeling test after adhesion

1.Separation of adhesion surface (interface peeling),

2.adhesive fracture peeling,

3. Destructive peeling of adherends

It can be evaluated in three ways. The strongest of these is the third one above. It is preferable that the adhesive forming the container has an adhesive force satisfying this third.

<Example 1> Adhesive adhesion test (aluminum and paper adhesion)

Adhesion between aluminum and paper was tested for various adhesives. After adhesion, a force was applied vertically to measure the force per cm of the adhesive width at which separation occurs for the first time, and the strength is measured in the adhesive strength and shown in Table 1 below.

[Table 1]

<Example 2> Table 2 below shows the peeling time at 20 ° C. in cold water after adhesive bonding of aluminum and paper.

[Table 2]

<Example 3>

-Bond paper fabric and aluminum fabric with water-soluble adhesive, use synthetic resin containing polar material for the cup forming joint, and expose the paper to the entire outer surface of the cup

1. Bond the paper fabric and the aluminum fabric with water-soluble adhesive.

2. Cut the sides and base.

3. Apply synthetic resin containing polar materials for adhesion to the joints of the sides.

4. Round the sides.

5. Combine with base to form cup

<Example 4>

-Bonding the paper fabric and aluminum fabric with water-soluble adhesive, bonding the cup-forming joints with water-soluble adhesive, exposing the paper to the entire outer surface of the cup

1. Bond the paper fabric and the aluminum fabric with water-soluble adhesive.

2. Cut the sides and base.

3. Apply a water-soluble adhesive to the joints of the sides.

4. Round the sides.

5. Combine with base to form cup

<Example 5>

The contents of [Fig. 2] to [Fig. 4], the paper fabric and the aluminum fabric are adhered with synthetic resin, and the other side of the paper is placed with a synthetic resin containing a polar material for adhesion at a melting point of 100 ° C or higher.

1. Bond aluminum fabric to one side of paper fabric with synthetic resin (LDPE).

2. On the other side of the paper, a synthetic resin containing a melting point or a softening point of 100 ° C or higher, containing a polar material for adhesion with a melting point or decomposition point of 100 ° C or higher, is placed.

3. Cut the sides and base.

4. Round the sides.

5. Combine with base to form cup

<Example 6>

-Adhesion of paper and aluminum fabrics with synthetic resin, use of synthetic resins containing polar substances for the cup forming joints, paper exposure on the entire outer surface of the cup

1. Join the aluminum fabric to one side of the paper fabric with synthetic resin.

2. Cut the sides and base.

3. Apply synthetic resin containing polar materials for adhesion to the joints 20 and 30 of the side paper.

4. Round the sides.

5. Combine with base to form cup

Various examples have been described above. This example is part of the present invention. It is possible to mix and use the above-described implementation methods, and changes are possible within the spirit of the present application, but all such changes are within the scope of the present application. Hereinafter, the present invention will be described in detail based on the drawings.

1 is a schematic representative cross-sectional view mainly focusing on the side of the aluminum endothelial paper cup of the present invention. The inner surface is attached with aluminum foil (1), the outside is paper (4), and the paper and aluminum are attached with an aqueous adhesive (3). A synthetic resin layer (which may contain a polar material or biodegradable resins) may be disposed outside the paper, and a synthetic resin containing a polar material is more preferable. As the outer synthetic resin layer, a foamed synthetic resin (a synthetic resin swollen with gas) may be used.

Figure 2 is an aluminum endothelial paper cup 850cc food container and 13oz beverage cup prototype photo

Figure 3 is an aluminum endothelial paper cup 13 oz (≒ 368cc) beverage cup (coffee cup) prototype photo

4 is an aluminum endothelial paper cup 850cc prototype photo

5 is a partial cross-section of an embodiment in which an aqueous adhesive layer 3 is disposed between an aluminum inner shell 1 and a paper jacket 4. A synthetic resin 5 may be attached to the outer surface of the paper. The synthetic resin on the outer surface may be attached in whole or in part.

6 is a partial cross-section of an exemplary embodiment in which a synthetic resin adhesive layer 2 is disposed between an aluminum inner skin 1 and a paper outer skin 4. A synthetic resin 5 may be attached to the outer surface of the paper. The synthetic resin on the outer surface may be attached in whole or in part.

7 is a partial cross-section of an exemplary embodiment in which a synthetic resin adhesive layer 2 and an aqueous adhesive layer 3 are disposed between an aluminum inner shell 1 and a paper envelope 4. A synthetic resin 5 may be attached to the outer surface of the paper. The synthetic resin on the outer surface may be attached in whole or in part.

8 is a position where the synthetic resin or water-based adhesive containing a polar material for forming a container is locally disposed on the side portion 20 of the paper cup side sheet (side portion) 10. When using a non-polar synthetic resin therein, it is preferable that the outer surface to be bonded thereto contains a polar material to improve the bonding strength. The opposite is also true.

9 is a synthetic resin or a synthetic resin containing a polar material is disposed on the side portion 20 of the side portion (side paper) of the paper cup, or an aqueous adhesive is disposed, and a polar material is placed on the aluminum surface of the lower part 30 of the side portion (side paper) 10 This is an example in which a synthetic resin, a non-polar synthetic resin, or a water-soluble adhesive is placed. The shape of FIG. 9 may be the same as the fan shape or trapezoid shape, and the widths of the upper and lower portions may be the same. When arranging the non-polar synthetic resin, it is preferable to arrange a synthetic resin containing a polar substance having a melting point of 100 ° C. or higher on the outer surface of the side (side) or base (bottom, bottom). When placing the adhesive in the lower portion 30 of the side paper, as shown in Fig. 9 30, the width of the base is slightly wider than that of the base, and the container is partially or entirely disposed in 30 portions so that the adhesive is not exposed inside the container. At this time, even if the inside of the base is aluminum, the joint between the side and the base can be doubled in and out, so that the cup can be completely sealed. At this time, even if the paper is exposed on the outer surface of the base, it is possible to sturdy seal bonding, which is advantageous for recycling paper resources.

FIG. 10 is an example in which the aluminum endothelial for the three cartons continued in a series process is attached with aluminum foil in a plan view before cutting the cartons individually. On the paper to which the synthetic resin is attached, aluminum endothelial is attached in the direction of the paper roll, which is the side direction of the carton. When cut individually, the 20 parts on both sides that become the upper and lower adhesive parts of the paper pack become the upper and lower parts of the paper pack or the upper and lower bonding parts, and the adhesive of the synthetic resin or the synthetic resin containing polar material is placed. It becomes a site. This plan view applies to both the upper and side parts and the lower part of the carton, or to the integral part of only the side part and the lower part.

FIG. 11 shows an example of the top view of the paper pack of FIG. 10 cut individually. The top can be fitted with a lid or cap. The upper and lower seals are made of synthetic resin or synthetic resin containing polar materials. Since the 30 part is a side adhesive part with aluminum attached, it is desirable to bond with a synthetic resin containing polar material for safe molding.

Simple modifications or changes of the present invention can be easily carried out by those skilled in the art, and all such modifications or changes are included in the scope of the present invention.

Claims (13)

In the paper cup container comprising an aluminum foil layer and consisting of a side portion and a bottom portion,
The inner surface is an aluminum foil layer, and the outer surface is paper or synthetic resin, and the adhesive used for the joint at the time of molding when the side portion of the paper cup is rounded has a melting point or a decomposition point of 100 ° C. or higher, and a synthetic resin containing a water-soluble adhesive or polar material Characterized by using, aluminum endothelial paper cup In the aluminum inner paper cup container, the aluminum foil layer is located on the inner surface, and is composed of a side portion and a bottom portion,
The entire paper cup, or at least the side portion, is provided with an aluminum inner skin and a paper outer skin including paper,
On the outer surface of the paper sheath, the paper may be exposed to the outside, or a synthetic resin or a synthetic resin containing polar substances may be attached to the outside of the paper,
The roll sheet-like bonding between the aluminum inner shell and the paper outer shell,
A water-soluble adhesive having a melting point or a decomposition point of 100 ° C or higher, a synthetic resin having a melting point or a decomposition point of 100 ° C or higher, and a melting point or a decomposition point of 100 ° C or higher, and bonded by at least one of synthetic resins containing polar substances;
Bonding the side portion and the bottom portion, the bonding to form the side portion, characterized in that is bonded by any one or more of a water-soluble adhesive or a synthetic resin containing a polar material, aluminum endothelial paper cup In the aluminum endothelial paper cup, the aluminum foil layer is located on the inner surface, and is composed of a side portion and a bottom portion,
In the part or the whole of the lower part (FIG. 9 30 part) of the aluminum surface which is the joining part of the side part and the bottom part; Water-soluble adhesive, synthetic resin, one or more of the synthetic resin containing a polar material is disposed, characterized in that the side portion (side paper) and the bottom portion (base) is bonded, aluminum endothelial paper cup. Connected to a carton container containing a thin layer of aluminum,
The inner surface is an aluminum foil layer, and the outer surface is paper or synthetic resin.
The side portion is provided with a paper envelope including an aluminum inner shell and paper,
The joint forming the side portion or the joint joining the side portion and the upper portion,
A water-soluble adhesive having a melting point or a decomposition point of 50 ° C or higher, a synthetic resin having a melting point or a decomposition point of 50 ° C or higher, and a melting point or a decomposition point of 50 ° C or higher, and characterized by being bonded by at least one of synthetic resins containing polar substances. Aluminum endothelial paper container In a paper container comprising an aluminum foil layer,
The inner surface is aluminum foil (1), the outer surface is paper or synthetic resin,
In a paper container having a side portion and a bottom portion, or a side portion top bottom portion;
When forming the side portion of the paper container, forming and bonding the side portion and the bottom portion, or forming and bonding the side portion and the upper portion; At least one of the adhesives used for the bonding portion is formed of a container by disposing a synthetic resin containing a water-soluble adhesive or a polar substance on the bonding portion, and the aluminum endothelial paper container is formed. The water-soluble adhesive is polyvinyl alcohol-based, polyvinyl acetate-based, ethylene vinyl acetate-based, hydroxypropyl methylcellulose, hydroxypropyl methylcellulose phthalate, luxurious vegetable starch according to any one of claims 1 to 5 , Dextrin, soluble starch, oxidized starch, glue, casein, gum arabic, paste, biodegradable adhesive resin, acrylic emulsion, one or more of the cellophane, aluminum endothelial paper cup. The synthetic resin according to any one of claims 1 to 5, wherein the synthetic resin containing the polar material is an epoxy resin-based, polyamine-based, acid anhydride-based, polyamide-based, resol resin-based, polysulfide-based, acrylic, phenolic resin-based , Polyurethane, silicone, rubber, polyamideimide, polyimide, polybenzimidazole, polyester, polyvinyl acetate, polyolefin, nylon, urea resin, aniline resin, toluenesulfonic acid amide, isocyanate An aluminum endothelial paper cup comprising at least one of alkyd, cyanoacrylate, polydiphenyl ether, polyvinyl acetate, and melamine in synthetic resins. The method of claim 7, wherein the polyamine-based diethyltriamine, triethylenetetramine, diethylaminopropylamine, xylenediamine, modified aliphatic polyamine, phenylenediamine, aminodiphenylsulfone, and at least one kind,
The acid anhydride-based one containing at least one of maleic anhydride, phthalic anhydride, hexahydrophthalic anhydride, aluminum endothelial paper cup. According to any one of claims 1 to 5, The synthetic resin containing the polar material, the polar material is included in one or more synthetic resins of polyolefin-based polyester-based nylon-based polystyrene-based, HDPE, MDPE, LDPE, LLDPE, PP, polyester, nylon, PS, PET, biodegradable synthetic resins, PLA (poly lactic acid), characterized in that used in combination with any one or more of biodegradable resins, aluminum endothelial paper cup. In the method of manufacturing a paper cup with aluminum foil located on the inner surface,
Step 1 to remove the oil of the aluminum foil;
A second step of forming a fabric with aluminum attached by bonding the rolled paper and aluminum in a plate shape using a water-soluble adhesive or a synthetic resin or a synthetic resin containing polar substances;
3 steps of cutting the side paper with the fabric produced in the above step 2, rolling it round, and forming a paper cup side sheet of aluminum endothelial using a synthetic resin containing a water-soluble adhesive or a polar material;
After cutting the base with the fabric or a separately prepared base or base fabric, a step 4 of forming a paper cup using a water-soluble adhesive, synthetic resin, or synthetic resin containing polar material between the sides and base;
A method for manufacturing an eco-friendly, eco-friendly aluminum endothelial paper cup that is easy to recycle, comprising the steps in any order. As a method of manufacturing a paper cup in which aluminum foil is located on the inner surface,
Manufacturing a side portion, and including joining the side portion and the bottom portion,
Manufacturing the side portion includes bonding the aluminum inner surface of the roll sheet state and the paper outer surface with an adhesive, wherein the outer surface of the paper outer surface may be attached with a synthetic resin,
When bonding the aluminum inner skin and the paper outer skin, the adhesive uses at least one of a water-soluble adhesive having a melting point or a decomposition point of 100 ° C or higher, a synthetic resin, and a synthetic resin containing a polar material;
When the side portion is roundly molded or the side portion and the bottom portion are bonded to form the container, at least one of the adhesives used has a melting point or a decomposition point of 100 ° C. or higher, a synthetic resin containing a water-soluble adhesive or a polar substance A method of manufacturing an aluminum endothelial paper cup, characterized by using one or more of the above. In the manufacturing method of the paper pack container the inner surface is an aluminum foil layer, the outer surface is paper or synthetic resin,
Step 1 of attaching the aluminum inner sheath with a water-soluble adhesive or synthetic resin or a synthetic resin containing a polar material to the entire inner surface of the paper fabric to be used;
A second step of disposing a synthetic resin containing a synthetic resin or a polar material in the upper and lower adhesive portions 20 or a portion to be joined thereto;
3 steps to cut the cartons;
A step 4 of disposing a synthetic resin or a synthetic resin containing a polar material in at least one of the side joining portion 30 of the cut carton or the outer portion joined to it;
5 steps of forming a carton;
Characterized in that it comprises the steps in any order, the method of manufacturing a carton In the manufacturing method of the paper pack container, the inner surface is an aluminum foil layer, the outer surface is paper or synthetic resin,
A first step of placing a synthetic resin or a synthetic resin containing polar substances on the inner surface of the paper;
Step 2 of attaching the aluminum inner sheath with synthetic resin or a synthetic resin containing a polar material on the inner surface except the upper and lower adhesive portions 20;
3 steps to cut the cartons;
A fourth step of placing a synthetic resin or a synthetic resin containing a polar material in at least one of the side bonding portion 30 of the cut carton or the outer surface portion to be joined thereto;
5 steps of forming a carton;
Characterized in that it comprises the steps in any order, the method of manufacturing a carton