KR20190136735A - 생분해성 애완동물용 패드 - Google Patents
생분해성 애완동물용 패드 Download PDFInfo
- Publication number
- KR20190136735A KR20190136735A KR1020180062821A KR20180062821A KR20190136735A KR 20190136735 A KR20190136735 A KR 20190136735A KR 1020180062821 A KR1020180062821 A KR 1020180062821A KR 20180062821 A KR20180062821 A KR 20180062821A KR 20190136735 A KR20190136735 A KR 20190136735A
- Authority
- KR
- South Korea
- Prior art keywords
- biodegradable
- weight
- parts
- nonwoven fabric
- present
- Prior art date
Abstract
본 발명은 생분해성 부직포; 상기 생분해성 부직포 하단에 합지된 카르복실기를 갖는 단분자 화합물과 펄프를 포함하는 흡수층; 및 상기 흡수층 하단에 합지된 생분해성 필름을 포함하되, 상기 생분해성 필름이 PBTA 100중량부 기준으로, PLA 5 내지 30중량부; 열가소성 전분 1 내지 20중량부; 무기필러 5 내지 20중량부; 및 유기필러 5 내지 20중량부를 포함하는 생분해성 애완동물용 패드를 제공한다.
본 발명에 따른 생분해성 부직포 조성물을 포함하는 부직포는 생분해성으로 인해 환경오염을 방지하고, 탄성력이 있을 뿐만 아니라, 평활성이 우수하며, 인장강도 및 경도가 높은 효과가 있다.
본 발명에 따른 생분해성 부직포 조성물을 포함하는 부직포는 생분해성으로 인해 환경오염을 방지하고, 탄성력이 있을 뿐만 아니라, 평활성이 우수하며, 인장강도 및 경도가 높은 효과가 있다.
Description
본 발명은 생분해성 애완동물용 패드에 관한 것으로서, 보다 상세하게는 미생물 등에 의해 분해가 가능한 생분해성 애완동물용 패드에 관한 것이다.
일반적으로 가정에서 키우는 개, 고양이와 같은 애완동물의 배설물 처리를 위하여, 종래에는 신문지, 종이상자 등과 같이 배설물에 포함된 수분을 흡수할 수 있는 재질의 것을 사용하여 왔다.
특히, 최근에는 애완동물의 보호와 더불어 애완동물을 키우는 가정이 급증하면서 이에 따라 애완동물들의 대소변용 패드 또한 소비가 급증하고 있다.
이러한생분해성 애완동물용 패드는 통상적으로, 액체 투과성 표면층과, 액체 불투과성의 배면층과, 상기 표면층과 배면층 사이에 배치되어 액체를 흡수하는 흡수층을 포함하는 구조를 갖는다.
이때, 표면층은 애완동물의 배설물에 포함된 소변 등의 액체성분이 통과되어 인접한 흡수층으로 이동되도록 기능하며, 흡수층은 표면층으로부터 유입된 액체를 받아 들여 흡수 및 보유하는 기능을 가지며, 배면층은 액체 불투과성 필름 재질로 이루어져 흡수층에 보유된 액체가 외부로 배출되는 것을 방지하는 기능을 수행한다.
그러나, 이러한 종래의생분해성 애완동물용 패드는 배설물에 함유된 액체의 흡수량이 적거나 액체의 흡수속도가 느리거나, 액체를 보유한 패드를 가압하였을 때 액체가 다시 표면층으로 흘러나와 역류하는 양(rewet 양, 이하 '역류량'이라 함)이 많은 등 흡수성과 관련된 특성이 나빠 사용상 불편할 뿐만 아니라 신뢰성이 낮다는 문제점이 있다.
더욱이, 공지의생분해성 애완동물용 패드는 액체 불투과성의 배면층과, 액체를 흡수하는 흡수층 및 필름층 등을 포함하는 구조는 생분해되지 않으며, 이로 인해 패드를 땅속에 매립할 때, 패드가 분해되지 않고 잔존하는바, 완전한 분해를 위해서, 패드 전체를 소각처리하거나 또는 분리소각을 위해 분해되는 층을 분리하는 것이 필요하다.
한편, 최근 들어 생분해성 수지는 토양 중에 매립함으로써 미생물 등에 의해 짧은 시간에 이산화탄소와 물로 분해되고, 그 결과 통상적 플라스틱 제품에 비해 적은 환경적 부담을 제공하기 때문에, 섬유 및 부직포 직물 분야에서 진지하게 연구되고 있다.
특히, 폴리락트산, 폴리에틸렌 숙시네이트, 폴리부틸렌 숙시네이트 및 폴리카프로락톤과 같은 지방족 폴리에스테르로 형성된 생분해성 부직포 직물은 다용도의 합성 섬유와 대등한 부직포 직물로서의 성질을 가지며 실제로 사용되고 있다.
여기서, 상기 폴리락트산은 생분해성 지방족 폴리에스테르 중에서 비교적 높은 융점을 가지며, 실용성이 높으므로, 폴리락트산은 다양한 목적에 적용될 것으로 예상된다.
폴리락트산으로 형성된 부직포 직물은 생분해성을 가지며, 다른 지방족 폴리에스테르보다 일반적으로 더 높은 융점을 가지기 때문에 내열성이 우수하다.
그러나 폴리락트산 수지는 양호한 결정성을 갖지만 통상적 방사 조건 하에서 느린 결정화 속도를 가진다.
따라서 방사되고 냉각된 섬유는 웹 축적 공정에서 섬유들간에 여전히 점착성을 가지며, 웹을 구성하는 섬유는 서로 결합되어 가요성이 부족한 부직포 직물을 제공하므로, 사람의 피부에 부직포 직물이 접촉하게 되는 목적에는 적용하기 어렵다.
가요성이 손상되는 것을 방지하도록 제어하면서 폴리락트산으로 형성된 웹을 열적으로 결합하거나 접착제로 수지 결합시킬 때, 얻어지는 부직포 직물은 솜털형(fluffy)이 되거나, 기계적 강도가 나빠지므로, 실제로 사용될 수 있는 부직포 직물을 제공할 수 없게 된다.
연속사(continuous fiber)를 구성하는 폴리락트산 폴리머가, 폴리(L-락트산), D-락트산과 L-락트산의 코폴리머, 및 D-락트산과 하이드로카르복시산의 코폴리머로부터 선택되는, 각각 100℃ 이상의 융점을 가진 폴리머 또는 폴리머들의 블렌드이고, D-락트산과 하이드로카르복시산의 코폴리머 및 폴리락트산 폴리머로 구성되는 연속사는 압력 하에 부분적으로 열-접착되어 있는 폴리락트산 연속형 섬유의 부직포 섬유가 제안되어 있다(참고 문헌예: 일본 특허 제3434628호). 그러나, 부직포 직물은 단일 성분으로 구성되므로, 가요성이 부족하고 딱딱한 질감을 가진다.
상이한 융점을 가진 2종의 폴리락트산 폴리머로 형성된 열-융합성(heat-fusible) 복합 섬유가 제안되어 있다(문헌예; JP-A-7-310236). 상기 복합 섬유는 접착성이 우수하지만, 저융점 성분이 모든 섬유에 대한 접착 성분으로 작용하기 때문에, 그 섬유로 제조된 부직포 직물은 단일 성분으로 구성된 부직포 직물과 유사하게 가요성이 부족하고 딱딱한 질감을 가진다.
본 발명은 이와 같은 종래의 문제점을 감안하여 이루어진 것으로서, 생분해성 지방족 폴리에스테르계 고분자를 포함하는 부직포 및 생분해성 필름 등을 이용하여 생분해성 애완동물용 패드를 제조할 수 있도록 하는 것을 제공한다.
본 발명은
생분해성 부직포;
상기 생분해성 부직포 하단에 합지된 카르복실기를 갖는 단분자 화합물과 펄프를 포함하는 흡수층; 및
상기 흡수층 하단에 합지된 생분해성 필름을 포함하되,
상기 생분해성 필름이 PBTA 100중량부 기준으로, PLA 5 내지 30중량부; 열가소성 전분 1 내지 20중량부; 무기필러 5 내지 20중량부; 및 유기필러 5 내지 20중량부를 포함하는 생분해성 애완동물용 패드를 제공한다.
본 발명에 따른 생분해성 애완동물용 패드는 생분해성으로 인해 환경오염을 방지하고, 흡수성이 좋을 뿐만 아니라, 평활성이 우수하며, 인장강도 및 경도가 높은 효과가 있다.
본 발명을 실시 예들을 설명함에 있어서, 동일부호는 동일한 구성을 의미하고, 중복되거나 발명의 의미를 한정적으로 해석되게 할 수 있는 부가적인 설명은 본 발명의 실시 예들을 설명함에 있어서 생략될 수 있다.
구체적인 설명에 앞서, 본 명세서상에 비록 단수적 표현으로 기재되어 있을지라도 국어 사용에 있어서 단수/복수를 명확하게 구분 짓지 않고 사용되는 환경과 당해 분야에서의 통상적인 용어 사용 환경에 비추어, 발명의 개념에 반하지 않고 해석상 모순되거나 명백하게 다르게 뜻하지 않는 이상 복수의 표현을 포함하는 의미로 사용된다. 또한, 본 명세서에 기재되었거나 기재될 수 있는 '포함한다', '갖는다', '구비한다', '포함하여 이루어진다' 등은 하나 또는 그 이상의 다른 특징이나 구성요소 또는 그들 조합의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
본 발명은 생분해성 부직포; 상기 생분해성 부직포 하단에 합지된 카르복실기를 갖는 단분자 화합물과 펄프를 포함하는 흡수층; 및 상기 흡수층 하단에 합지된 생분해성 필름을 포함하되, 상기 생분해성 필름이 PBTA 100중량부 기준으로, PLA 5 내지 30중량부; 열가소성 전분 1 내지 20중량부; 무기필러 5 내지 20중량부; 및 유기필러 5 내지 20중량부를 포함하는 생분해성 애완동물용 패드를 제공한다.
본 발명에 따른 생분해성 부직포는 보온성, 통기성 및/또는 투습성 등을 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 부직포라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 생분해성 애완동물용 패드에 적용되어 생분해성 애완동물용 패드가 분해처리 될 수 있도록 하는 것이 좋다.
본 발명에 따른 펄프는 천연펄프, 재생펄프가 사용될 수 있고, 바람직하게는 재생펄프를 사용한다.
특정 양태로서 본 발명에 따른 생분해성 부직포는 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로,
물성계량제 8 내지 30중량부;
윤활제 3 내지 20중량부; 및
무기연마제 2 내지 15중량부를 포함하는 것이 좋다.
여기서, 상기 생분해성 부직포를 구성하는 생분해성 지방족 폴리에스테르계 고분자는 미생물에 의한 생분해는 잘 일어나지만, 기계적 물성 및 열적물성이 낮아 다양한 응용분야에서 폴리에틸렌(PE)과 같은 범용성 고분자를 대체하기에 한계가 있지만, 일회용 혹은 단기 사용한 후 폐기되는 여러 응용분야에서 비분해성인 범용성 고분자의 대체제로 사용되고 있다.
바람직한 생분해성 지방족 폴리에스테르계 고분자는 PBS(polybutylene succinate), PCL(polycaprolactone), PBA[poly(butylene adipate)], PBAT(polybutylene adipate-co-terephthalate), PLA(polylactic acid) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물인 것을 포함하는 것이 좋다.
본 발명에 따른 생분해성 부직포를 구성하는 생분해성 지방족 폴리에스테르계 고분자 외 나머지 성분들의 함량은 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 한다.
본 발명에 따른 물성계량제는 인성, 즉 강도는 높지만 신장률이 부족해 쉽게 파단되는 생분해성 지방족 폴리에스테르계 고분자의 특성을 보완하기 위해 사용된 것으로서, 이러한 목적을 갖는 당업계의 통상적인 물성계량제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 디에틸렌 글리콜로 얻어지는 2가 알코올 또는 글리세롤, 트리메틸올 프로판으로부터 얻어지는 3가 알코올과 숙신산, 아디핀산으로부터 얻어지는 2가 산 또는 2가 산의 무수물 형태로부터 축중합에 의해 제조되는 것을 사용하는 것이 좋지만, 추천하기로는 중량 평균 분자량이 50,000 내지 150,000Da이며, 용융지수 20 내지 30g/10min인 2가 알코올, 3가 알코올, 글리세롤, 숙신산, 아디핀산 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.
또한, 본 발명에 따른 물성계량제는 필요에 따라 폴리카프로락톤을 단독 및/또는 부가적으로 더 사용할 수 있다.
바람직한 폴리카프로락톤은 분자량이 30,000 내지 60,000Da이고, 용융지수는 20 내지 30g/10min이며, 융점은 58 내지 60℃인 것을 사용하는 것을 추천한다.
본 발명에 따른 물성계량제의 사용량은 사용자의 선택에 따라 변경 가능하지만, 바람직하게는 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 8 내지 30중량부인 것이 좋다.
본 발명에 따른 윤활제는 생분해성 부직포를 제조하기 위한 모노필라멘트의 방사제조시 윤활성을 향상시키기 위한 것으로서, 이러한 목적을 위해 당업계의 통상적인 윤활제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 장시간 동안의 방사시 친유성 성분이 증가하기 때문에 분자내 친수성 성분과 친유성 성분의 비율을 나타내는 HLB값(Hydrophile-Lipophile balance value)이 7.0 내지 16.0의 범위인 지방산 에스테르, 특정적으로 글리세린 지방산 에스테르, 솔비탄 지방산 에스테르, 피리독신 지방산 에스테르 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.
본 발명에 따른 윤활제의 사용량은 사용자의 선택에 따라 변경 가능하지만, 바람직하게는 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 3 내지 20중량부인 것이 좋다.
본 발명에 따른 무기연마제는 생분해성 부직포의 강성도와 굴곡복원률 특성을 개선함과 동시에 세정력을 향상시키기 위한 것으로서, 이러한 목적을 갖는 무기연마제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 이산화규산(실리카), 인산칼슘, 탄산칼슘, 무수규산, 수산화알루미늄 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.
이때, 상기 무기연마제의 평균입자크기는 수 나노미터 내지 수 마이크로미터, 바람직하게는 10nm 내지 100㎛의 크기를 갖는 것이 좋다.
본 발명에 따른 무기연마제의 사용량은 사용자의 선택에 따라 변경 가능하지만, 바람직하게는 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 2 내지 15중량부인 것이 좋다.
본 발명에 따른 생분해성 부직포는 하기의 특정 양태에 따른 부가물을 1종 또는 1종 이상 더 포함할 수 있다.
특정 양태로서, 본 발명에 따른 생분해성 부직포는 인체에 무해한 천연 유제로서, 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 1 내지 15중량부의 식품첨가제를 더 포함할 수 있다.
여기서, 상기 식품 첨가제는 모노필라멘트로 제조되는 제품, 예를 들면 부직포로 제작되는 경우 모노필라멘트의 집속성은 물론 표면에 우수한 평활성을 부여하여 매끄러운 상태를 유지시켜 피부에 긁히는 일이 없도록 할 수 있다.
또한, 상기 식품첨가제는 모노필라멘트를 제조하기 위한 인발 과정에서 천연유제가 필라멘트 표면으로 흘러나오고, 이 상태에서 열처리가 이루어짐으로써, 강도 및 경도 향상은 물론 우수한 평활성을 제공하게 된다.
바람직한 식품첨가제는 코코넛, 야자, 콩, 카카오피 등에서 추출하는 천연 유제 또는 이들 천연 유제로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.
다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포를 구성하는 필라멘트의 공극을 치밀하게 하고 수분의 방출을 방지함으로써 강도를 향상시키기 위하여 나트륨벤토나이트를 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 1 내지 10중량부로 더 포함할 수 있다.
상기 나트륨벤토나이트는 많은 양의 물을 흡수해 원래 부피의 여러 배로 팽창되며 겔과 같은 상태가 되어 조성물의 공극을 치밀하게 매우게 되어 수분의 방출을 방지하고 강도를 향상시켜 균열방지에 기여하게 된다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 셀프 레벨링(자기충전성능)을 개선하기 위하여 스타치에테르(Starch ether)를 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 3중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포의 점도를 조절하기 위하여 디페닐메탄디이소시아네이트를 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 2중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 1 내지 5중량부로 마그네슘 카보네이트(magnesium carboneate)를 더 포함할 수 있는데, 마그네슘 카보네이트는 백색이면서 가볍고 부수러지기 쉬운 물질로서 화장품의 원료로도 사용되는데 마그네슘 카보네이트가 생분해성 부직포에 포함되면 생분해성 부직포의 결정화도를 증대하여 강성, 투명성 및 광택성 등을 향상시킬 뿐만 아니라, 생분해성 부직포 pH도 조절하는 이중의 기능을 부여하게 되는 것이다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포를 구성하는 필라멘트의 보습력 및 방부력 향상을 위하여 1,3-프로판 디올을 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 3중량부 더 포함할 수 있는데 1,3-프로판 디올은 낮은 점성과 흡수력이 있으며 끈적임이 적어 이를 생분해성 부직포에 포함하면 조성물의 보습력이 향상되고 방부제를 적게 사용하게 되는 잇점이 있어 방부력 또한 상승되게 되는 것이다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포가 토양속에서 분해될 때 토양속의 철 등과 같은 전이금속과 반응하여 생분해성 부직포를 구성하는 필라멘트의 탄소-탄소 결합을 쉽게 파괴할 수 있도록 하기 위하여 리놀레산을 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 2중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포가 자외선에 의한 광산화반응(Photooxidation)을 방지하기 위하여 하이드록시벤조피논(Hydroxybenzophenone)을 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 3중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 지방족 폴리에스테르계 고분자와 폴리락틱산간의 상용성을 향상시키기 위하여 폴리비닐알콜을 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 3중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 지방족 폴리에스테르계 고분자의 구조를 파괴시켜 가소화를 향상시키기 위하여 우레아와 명반화합물이 1;3의 중량비로 혼합된 우레아 및 명반 혼합물을 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있는데, 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1부 이하를 사용할 경우 목적한 효과를 얻을수 없고, 3중량부를 초과하면 타원료에 악영향을 미쳐서 최종제품의 기계적인 물성이 저하된다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포를 구성하는 필라멘트의 인장강도, 점탄성, 냉각성 등을 향상시키기 위하여 3차-부틸퍼벤조에이트를 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 2중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 조성물이 쉽게 부서지거나 찢어지는 현상을 없애고, 가공성을 향상시키기 위하여 디벤조일 퍼옥사이드(Dibenzoyl peroxide)를 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 3중량부 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 생분해성 부직포는 생분해성 부직포를 구성하는 필라멘트의 흐름성을 향상시키기 스테아르산 칼슘을 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로 0.1 내지 2중량부 더 포함할 수 있다.
이와 같은 구성을 갖는 본 발명에 따른 생분해성 부직포를 제조하기 위한 부직포 제조방법을 설명하면 다음과 같다.
본 발명에 따른 부직포 제조방법은 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로, 물성계량제 8 내지 30중량부; 윤활제 3 내지 20중량부; 및 무기연마제 2 내지 15중량부를 포함하는 생분해성 부직포 조성물을 투입하는 투입단계;
상기 투입단계가 종료된 부직포 조성물을 혼합하고, 압축하여 반죽하는 반죽단계;
상기 반죽단계가 종료된 반죽을 강제로 압출하여 압출 다이에 공급하는 압출단계;
상기 압출단계가 종료된 후 압출 다이를 통과시켜 필라멘트를 성형하는 성형단계;
상기 성형단계가 종료된 필라멘트를 인발하는 인발단계;
상기 인발단계가 종료된 필라멘트를 40 내지 60℃의 온도범위에서 5 내지 10시간 동안 열풍가열하는 열처리 단계; 및
상기 열처리 단계가 종료된 필라멘트를 서로 엉키도록 하여 필라멘트 집합체(웹)를 구성하는 부직포 제조단계를 포함한다.
여기서, 상기 열처리 단계는 인발단계가 종료된 필라멘트를 이송하는 이송단계; 열풍기에 투입된 필라멘트를 열처리하는 1차 열처리단계; 상기 1차 열처리단계가 종료된 필라멘트를 뒤집어 반대면이 열처리하는 2차 열처리단계; 및 상기 2차 열처리단계가 종료된 후 필라멘트를 냉각하는 냉각단계를 포함할 수 있다.
특정 양태로서, 본 발명에 따른 열처리단계에서 상기 생분해성 부직포에 식품첨가물이 더 포함되는 경우, 상기 부직포를 구성하는 조성물을 인발하는 인발과정에서 필라멘트 표면으로 새어나오는 식품첨가물을 경화시켜 인장강도 및 경도를 향상시키고, 나아가 평활성이 보유되도록 하는 것이다.
이상과 같이, 본 발명에 따른 부직포는 생분해성 부직포 조성물을 필라멘트, 특정적으로 모노필라멘트 형태로 제조한 뒤 필라멘트 집합체로 구성하여 제조된다.
본 발명에 따른 흡수층은 유연성 및 내부의 습기를 외부로 방출시키는 투습성의 탁월함 뿐 아니라, 큰 균열 또는 파열강도가 높고, 기저귀에 액체가 흡수되면, 액체를 퍼지게 하면서 다량을 흡수할 수 있도록 하는 당업계의 통상적인 흡수층이라면 어떠한 것을 사용하여도 무방하다.
바람직한 흡수층은 카르복실기를 갖는 단분자 화합물과 펄프를 포함할 수 있으며, 상기 카르복실기를 갖는 단분자 화합물 및 펄프의 혼합비는 사용자의 선택에 따라 변경 가능하지만, 바람직하게는 1:9 내지 9:1의 중량비율로 혼합되는 것을 추천한다.
여기서, 상기 카르복실기를 갖는 단분자 화합물은 시트릭산(Citric Acid), 아세틱산(Acetic Acid), 락틱산(Lactic Acid), 탈타릭산(Tartaric Acid) 및 숙시닌산(Succinic Acid) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 바람직하다.
특정 양태로서, 본 발명에 따른 흡수층은 입자형태인 그래뉼을 더 포함할 수 있으며, 그 사용량은 카르복실기를 갖는 단분자 화합물 및 펄프의 총 100중량부 기준으로 10 내지 30중량부인 것이 좋다.
본 발명에 따른 생분해성 필름은 생분해성 애완동물용 패드에 통상적으로 사용되는 생분해성 필름이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 PBTA 100중량부 기준으로, PLA 5 내지 30중량부; 열가소성 전분 1 내지 20중량부; 무기필러 5 내지 20중량부; 및 유기필러 5 내지 20중량부를 포함할 수 있다.
본 발명에 따른 생분해성 필름을 구성하는 PBTA(polybutylene adipate-co-terephthalate)는 당업계의 통상적인 PBTA라면 어떠한 것을 사용하여도 무방하다.
본 발명에 따른 생분해성 필름을 구성하는 PBTA 외 나머지 성분들의 함량은 생분해성 PBTA 100중량부 기준으로 한다.
본 발명에 따른 PLA(poly Lactic acid)는 생분해성 고분자 수지로서, PBTA 100중량부 기준으로 5 내지 30중량부를 포함하는 것이 좋다.
본 발명에 따른 열가소성 전분은 가열시 성형 가능하고, 미생물에 의해 분해될 수 있는 것이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 히드록시프로필 전분인 것이 좋고, 그 사용량은 PBTA 100중량부 기준으로 1 내지 20중량부인 것을 추천한다.
본 발명에 따른 무기필러는 압출되어 형성되는 생분해성 필름에 화학적 방해 또는 역효과를 발생시키지 않으면서, 상기 필름 전체에 균일하게 분산될 수 있는 미립자 및 다른 형태의 무기물로서, 필름에 통기성을 제공할 수 있다.
바람직한 무기필러는 상기 목적을 갖는 당업계의 통상적인 무기필러라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 탄산칼슘, 탄산바륨, 탄산마그네슘, 황산마그네슘, 이산화티탄, 운모(mica), 클레이(clay), 카올린, 규조토(diatomaceous earth) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물인 것이 좋고, 그 사용량은 PBTA 100중량부 기준으로 5 내지 20중량부인 것이 좋다.
본 발명에 따른 유기필러는 압출되어 형성되는 생분해성 필름에 화학적 방해 또는 역효과를 발생시키지 않으면서, 상기 필름 전체에 균일하게 분산될 수 있는 미립자 및 다른 형태의 유기물로서, 필름에 통기성을 제공할 수 있다.
바람직한 유기필러는 상기 목적을 갖는 당업계의 통상적인 유기필러라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 스테아르산 및/또는 팔미트산인 것이 좋고, 그 사용량은 PBTA 100중량부 기준으로 5 내지 20중량부인 것이 좋다.
특정 양태로서, 본 발명에 따른 생분해성 필름은 PBTA 100중량부 기준으로 1 내지 30중량부의 가소제를 더 포함할 수 있다.
여기서, 상기 가소제는 생분해성 필름 제조시 연화되어 외부 막을 뚫고 들어가서, 상기 열가소성 전분 사슬이 물을 흡수하여 팽창되도록 하여 초기에 상기 전분, 특정적으로 전분 과립 안에 압축되어 있던 아밀로오스와 아밀로펙틴 폴리머들을 함유하는 전분 폴리머 사슬이 외부로 뻗어 나와, 일반적으로 무질서하게 혼합된 폴리머 사슬들을 형성할 수 있도록 한다.
바람직한 가소제로는 글루코오스, 슈크로오스, 프록토오스, 라피노오스, 말토덱스트로오스, 갈락토오스, 자일로오스, 말토오스, 락토오스, 만노오스 및 에리트오로스, 에리트리톨, 자일리톨, 말리톨, 만니톨 및 소리비톨, 에틸렌 글리콜, 헥산트리올 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.
다른 특정 양태로서, 본 발명에 따른 생분해성 필름은 전분과 결합 가능한 식물성 단백질을 PBTA 100중량부 기준으로 1 내지 20중량부 더 포함할 수 있다.
바람직한 단백질로는 글루텐, 예를 들면, 귀리 또는 쌀 글루텐, 콘 제인(corn zein), 호르데인(hordein), 아베인(avenin), 카피린(kafirin) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 포함한다.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
생분해성 부직포 제조
[실시예 1]
PBS 100g, 2가 알코올 20g, 글리세린 지방산 에스테르 12g, 인산칼슘 7g을 혼합하여 부직포 조성물을 실린더에 투입하여 반죽하였다.
그 다음, 반죽된 부직포 조성물을 압출다이에 통과시켜 필라멘트를 성형한 후 인발하였다.
그 다음, 인발된 필라멘트를 약 50℃의 온도에서 약 8시간 동안 열풍가열하여 열처리한 뒤 냉각하였다.
그 다음, 냉각된 필라멘트를 서로 엉키도록 하여 필라멘트 집합체로 이루어진 부직포를 제조하였다.
[실시예 2]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 코코넛으로 이루어진 천연유제 7g을 더 부가하여 실시하였다.
[실시예 3]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 나트륨벤토나이트 5g을 더 부가하여 실시하였다.
[실시예 4]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 스타치에테르 2g을 더 부가하여 실시하였다.
[실시예 5]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 디페닐메탄디이소시아네이트 1g을 더 부가하여 실시하였다.
[실시예 6]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 마그네슘 카보네이트 2g을 더 부가하여 실시하였다.
[실시예 7]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 디벤조일 퍼옥사이드 1g을 더 부가하여 실시하였다.
[실시예 8]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 1,3-프로판 디올 1g을 더 부가하여 실시하였다.
[실시예 9]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 리놀레산 1g을 더 부가하여 실시하였다.
[실시예 10]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 하이드록시벤조피논 1g을 더 부가하여 실시하였다.
[실시예 11]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 폴리비닐알콜 2g을 더 부가하여 실시하였다.
[실시예 12]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 우레아와 명반이 1:3의 중량비로 혼합된 우레아 및 명반혼합물 2g을 더 부가하여 실시하였다.
[실시예 13]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 3차-부틸퍼벤조에이트 1g을 더 부가하여 실시하였다.
[실시예 14]
실시예 1과 동일한 방법으로 실시하되, 상기 부직포 조성물에 스테아르산 칼슘 1g을 더 부가하여 실시하였다.
[실시예 15]
실시예 1과 동일한 방법으로 실시하되, 실시예 2 내지 14를 모두 부가하여 실시하였다.
생분해성 필름 제조
[실시예 16]
먼저, PBTA(polybutylene adipate-co-terephthalate) 100g, PLA(poly Lactic acid) 15g, 히드록시프로필 전분 10g, 스테아르산 13g, 및 탄산바륨 13g을 혼합하여 혼합 조성물을 제조하였다.
그 다음, 상기 혼합물을 약 100℃의 온도로 가열압착하는 롤러로 압착하여 생분해성 필름을 제조하였다.
[실시예 17]
실시예 16과 동일한 방법으로 실시하되, 상기 혼합 조성물에 글루코오스 15g을 더 부가하여 실시하였다.
[실시예 18]
실시예 16과 동일한 방법으로 실시하되, 상기 혼합 조성물에 호르데인 10g을 더 부가하여 실시하였다.
생분해성 애완동물용 패드 제조
[실시예 19]
실시예 1에 따라 제조된 생분해성 부직포 하단에 시트릭산과 펄프가 5:5의 중량비율로 혼합되어 형성된 흡수층을 합지하였다.
그 다음, 상기 흡수층의 하단에 실시예 16에 따라 제조된 생분해성 필름을 합지하여 생분해성 애완동물용 패드를 제조하였다.
[실시예 20]
실시예 19와 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 생분해성 부직포 대신 실시예 2에 따라 제조된 생분해성 부직포를 사용하여 실시하였다.
[실시예 21]
실시예 19와 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 생분해성 부직포 대신 실시예 3에 따라 제조된 생분해성 부직포를 사용하여 실시하였다.
[실시예 22]
실시예 19와 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 생분해성 부직포 대신 실시예 4에 따라 제조된 생분해성 부직포를 사용하여 실시하였다.
[실시예 23]
실시예 19와 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 생분해성 부직포 대신 실시예 5에 따라 제조된 생분해성 부직포를 사용하여 실시하였다.
[실험예 1]
상기 실시예 1 내지 실시예 15에 따른 생분해성 부직포를 제조하기 위해 인발되어 냉각된 필라멘트에 대하여 아래 물성을 측정한 뒤 그 결과를 표 1에 나타냈다.
여기서,
(1) 인장강도 - KS M 3001에 의해 측정하였다.
(2) 신장율 - KS [0073] M 3001에 의해 측정하였다.
(3) 인열강도 - KS M 3505 (1mm notch)에 의해
(4) 열융착강도 - KS M 7132 에 의해 측정하였다.
| 인장강도(kgf/cm2) | 신장율(%) | 인열강도(kgf/cm) | 열융착강도 (kgf/cm) | ||||
| 길이방향 | 폭방향 | 길이방향 | 폭방향 | 길이방향 | 폭방향 | ||
| 실시예1 | 343 | 334 | 348 | 337 | 79 | 84 | 8.4 |
| 실시예2 | 354 | 343 | 360 | 325 | 82 | 86 | 9.3 |
| 실시예3 | 357 | 345 | 394 | 332 | 84 | 96 | 9.7 |
| 실시예4 | 352 | 347 | 421 | 345 | 86 | 90 | 9.8 |
| 실시예5 | 351 | 359 | 403 | 339 | 89 | 94 | 11.2 |
| 실시예6 | 361 | 343 | 386 | 341 | 87 | 93 | 10.5 |
| 실시예7 | 374 | 342 | 379 | 320 | 91 | 94 | 10.8 |
| 실시예8 | 341 | 336 | 430 | 349 | 97 | 91 | 11.5 |
| 실시예9 | 354 | 348 | 421 | 336 | 98 | 98 | 11.2 |
| 실시예10 | 369 | 331 | 428 | 359 | 97 | 96 | 11.9 |
| 실시예11 | 348 | 341 | 432 | 349 | 89 | 94 | 11.8 |
| 실시예12 | 359 | 358 | 379 | 338 | 86 | 93 | 10.9 |
| 실시예13 | 342 | 343 | 385 | 341 | 95 | 97 | 9.5 |
| 실시예14 | 373 | 367 | 393 | 346 | 102 | 99 | 11.5 |
| 실시예15 | 369 | 361 | 452 | 334 | 101 | 98 | 11.3 |
표 1에 나타난 바와 같이, 본 발명의 생분해성 부직포는 실시예의 결과처럼, 인장강도, 신장율, 인열강도와 열융착강도가 좋아 우수한 기계적 물성을 나타내는 것을 알 수 있었다.
[실험예 2]
실시예 19 내지 실시예 23에 따라 제조된 생분해성 애완동물용 패드의 종방향 및 횡방향 인장강도, 흡수시간을 측정하여 하기 표 2로 나타냈다.
| 종방향 인장 강도(kg/2in) | 횡방향 인장 강도(kg/2in) | 흡수시간(초) | |
| 실시예 19 | 8.3 | 1.3 | 3.0 |
| 실시예 20 | 8.4 | 1.4 | 2.9 |
| 실시예 21 | 8.3 | 1.4 | 2.9 |
| 실시예 22 | 8.5 | 1.5 | 3.1 |
| 실시예 23 | 8.7 | 1.6 | 2.9 |
표 2에 나타난 바와 같이, 본 발명의 생분해성 애완동물용 패드는 실시예의 결과처럼, 인장강도 및 흡수율이 좋은 것으로 나타났다.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
Claims (3)
- 생분해성 부직포;
상기 생분해성 부직포 하단에 합지된 카르복실기를 갖는 단분자 화합물과 펄프를 포함하는 흡수층; 및
상기 흡수층 하단에 합지된 생분해성 필름을 포함하되,
상기 생분해성 필름이 PBTA 100중량부 기준으로, PLA 5 내지 30중량부; 열가소성 전분 1 내지 20중량부; 무기필러 5 내지 20중량부; 및 유기필러 5 내지 20중량부를 포함하는 생분해성 애완동물용 패드.
- 제1항에 있어서,
상기 생분해성 부직포는 생분해성 지방족 폴리에스테르계 고분자 100중량부 기준으로,
물성계량제 8 내지 30중량부;
윤활제 3 내지 20중량부; 및
무기연마제 2 내지 15중량부를 포함하는 생분해성 애완동물용 패드.
- 제2항에 있어서,
상기 생분해성 지방족 폴리에스테르계 고분자는 PBS, PCL, PBA, PBAT 또는 이들의 혼합물인 것을 포함하는 생분해성 애완동물용 패드.