KR20190129304A - Bamboo stick and manufacturing method of this - Google Patents

Bamboo stick and manufacturing method of this Download PDF

Info

Publication number
KR20190129304A
KR20190129304A KR1020180053751A KR20180053751A KR20190129304A KR 20190129304 A KR20190129304 A KR 20190129304A KR 1020180053751 A KR1020180053751 A KR 1020180053751A KR 20180053751 A KR20180053751 A KR 20180053751A KR 20190129304 A KR20190129304 A KR 20190129304A
Authority
KR
South Korea
Prior art keywords
bamboo
stick
manufacturing
length adjustment
reinforcing
Prior art date
Application number
KR1020180053751A
Other languages
Korean (ko)
Inventor
한준혁
Original Assignee
한준혁
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한준혁 filed Critical 한준혁
Priority to KR1020180053751A priority Critical patent/KR20190129304A/en
Publication of KR20190129304A publication Critical patent/KR20190129304A/en

Abstract

The present invention relates to a bamboo stick for manufacturing a stable stick using bamboo and a manufacturing method thereof. To this end, the manufacturing method of the bamboo stick comprises: a purging step of boiling bamboo in an aqueous solution; a surface treatment step of removing foreign matters from a surface of the bamboo after the purging step; a drying step of drying the bamboo after the surface treatment step; and a length adjusting step of cutting the bamboo to the predetermined length after the drying step. In the purging step, bamboo is boiled for 60 to 90 minutes using the aqueous solution in which 25 to 35 wt% of sodium hydroxide is mixed with 65 to 75 wt% of water.

Description

대나무 지팡이와 이것의 제조방법{BAMBOO STICK AND MANUFACTURING METHOD OF THIS}BAMBOO STICK AND MANUFACTURING METHOD OF THIS

본 발명은 대나무 지팡이와 이것의 제조방법에 관한 것으로, 보다 구체적으로는 대나무를 이용하여 안정된 지팡이를 제조하기 위한 대나무 지팡이와 이것의 제조방법에 관한 것이다.The present invention relates to a bamboo stick and a method of manufacturing the same, and more particularly to a bamboo stick for producing a stable stick using bamboo and a method for producing the same.

일반적으로, 지팡이는 등산가, 노인 등 신체의 보조기구로 사용되기도 하고, 때로는 신분이 높은 사람이 권위의 상징으로 사용되기도 하며, 호신용으로도 사용하기도 한다. 지팡이는 본래 나뭇가지나 대나무 등의 막대기를 뜻하는 것이지만, 정확히는 워킹스틱(Walking stick)·스탭(Staff)이며, 캐 인(Cane)이라고도 한다.In general, the cane is used as an aid to the body, such as mountaineers and the elderly, and sometimes a high-ranking person is used as a symbol of authority and may also be used for self-defense. The wand originally meant a stick such as a twig or bamboo, but it is exactly a walking stick, a staff, or a cane.

지팡이의 역사는 오래되어 고대 이집트부터 오리엔탈 유물 가운데서도 찾아 볼 수 있다. 고대사회에 있어서는 일반인의 보행용 외 왕이나 신의 존엄성과 위력의 상징으로 등장했다. 중세에는 군주나 승려의 표상으로도 사용되었고, 여행자, 순례자, 농부에게도 일상용품으로 사용되었으며, 여성의 액세서리로 출현 된 것은 11세기이며, 15세기에도 일시 보급되었으나 성행한 것은 18세기였고 요즈음은 고령화 사회가 되어 많은 노약자가 앞길을 가늠해주는 지팡이를 사용하고 있는 실정이다.The history of the cane is old, and can be found in ancient artifacts from ancient Egypt. In ancient times, it appeared as a symbol of the dignity and power of ordinary kings and gods. In the Middle Ages, it was used as a representation of monarchs and monks, and was used as daily necessities for travelers, pilgrims, and farmers.It appeared as a women's accessory in the 11th century. As a society, many elderly people are using canes to measure the way ahead.

대한민국 공개특허공보 제2013-0071460호(발명의 명칭 : 롤러와 고정밴드가 설치된 지팡이, 2013. 06. 28. 공개)Republic of Korea Patent Application Publication No. 2013-0071460 (Invention name: cane with roller and fixing band, 2013. 06. 28. published)

본 발명의 목적은 종래의 문제점을 해결하기 위한 것으로서, 대나무를 이용하여 안정된 지팡이를 제조하기 위한 대나무 지팡이와 이것의 제조방법을 제공함에 있다.An object of the present invention is to solve the conventional problems, to provide a bamboo stick and a method of manufacturing the same for producing a stable stick using bamboo.

상술한 본 발명의 목적을 달성하기 위한 바람직한 실시예에 따르면, 본 발명에 따른 대나무 지팡이의 제조방법은 수용액에서 대나무를 끓이는 퍼징단계; 상기 퍼징단계를 거친 다음, 상기 대나무의 표면에서 이물질을 제거하는 표면처리단계; 상기 표면처리단계를 거친 다음, 상기 대나무를 건조시키는 건조단계; 및 상기 건조단계를 거친 다음, 상기 대나무를 기설정된 길이로 절단하는 길이조정단계;를 포함하고, 상기 퍼징단계는 65 중량% 내지 75 중량%의 물에 25 중량% 내지 35 중량%의 수산화나트륨을 혼합한 수용액을 이용하여 상기 대나무를 60분 내지 90분 간 끓인다.According to a preferred embodiment for achieving the above object of the present invention, the manufacturing method of the bamboo stick according to the present invention is a purging step of boiling bamboo in an aqueous solution; After the purging step, the surface treatment step of removing foreign matter from the surface of the bamboo; After the surface treatment step, the drying step of drying the bamboo; And a length adjusting step of cutting the bamboo to a predetermined length after the drying step, wherein the purging step includes 25% to 35% by weight of sodium hydroxide in 65% to 75% by weight of water. Boil the bamboo for 60 to 90 minutes using the mixed aqueous solution.

본 발명에 따른 대나무 지팡이의 제조방법은 상기 길이조정단계를 거친 다음, 상기 대나무의 중심에 보강재를 삽입하는 강도보강단계;를 더 포함한다.Bamboo stick manufacturing method according to the invention after the length adjustment step, the strength reinforcing step of inserting a reinforcing material in the center of the bamboo; further includes.

여기서, 상기 강도보강단계는, 기설정된 직경으로 상기 대나무의 중심에 보강홀부를 형성하는 타공단계; 상기 보강홀부에 접착제를 주입하는 주입단계; 및 상기 주입단계를 거친 다음, 상기 보강홀부에 보강재를 삽입하는 보강재삽입단계;를 포함한다.Here, the strength reinforcing step, the punching step of forming a reinforcing hole in the center of the bamboo with a predetermined diameter; Injecting an adhesive into the reinforcing hole; And a reinforcing material insertion step of inserting a reinforcing material into the reinforcing hole part after the injection step.

본 발명에 따른 대나무 지팡이의 제조방법은 상기 길이조정단계를 거친 다음, 상기 대나무의 양단부 중 적어도 어느 하나를 가공하는 마감단계; 상기 길이조정단계를 거친 다음, 상기 대나무의 표면에 문양을 새기는 버닝단계; 및 상기 길이조정단계를 거친 다음, 상기 대나무의 표면을 코팅하는 코팅단계; 중 적어도 어느 하나를 더 포함할 수 있다.Bamboo stick manufacturing method according to the invention after the length adjustment step, the finishing step of processing at least one of both ends of the bamboo; After the length adjustment step, the burning step of carving a pattern on the surface of the bamboo; And after the length adjustment step, the coating step of coating the surface of the bamboo; It may further include at least one of.

본 발명에 따른 대나무 지팡이는 90cm 내지 100cm의 길이를 갖는 대나무가 포함되는 본체부;를 포함하고, 상기 대나무는, 본 발명에 따른 대나무 지팡이의 제조방법에 의해 가공된다.Bamboo stick according to the present invention includes a body portion containing a bamboo having a length of 90cm to 100cm; The bamboo is processed by the method of manufacturing a bamboo stick according to the invention.

본 발명에 따른 대나무 지팡이와 이것의 제조방법에 따르면, 대나무를 이용하여 안정된 지팡이를 제조할 수 있다. 특히, 퍼징단계의 수치한정을 통해 대나무의 섬유질에서 진액을 충분히 제거할 수 있고, 대나무가 갈라지거나 대나무의 섬유질이 손상되는 것을 방지하며, 대나무의 직진도를 간편하게 조정할 수 있다.According to the bamboo stick and the manufacturing method thereof according to the present invention, it is possible to manufacture a stable stick using bamboo. In particular, through the numerical limitation of the purging step can be sufficiently removed from the fibrous fiber of bamboo, to prevent the bamboo split or damage the fiber of the bamboo, it is possible to easily adjust the straightness of the bamboo.

또한, 본 발명은 강도보강단계를 통해 대나무의 강도를 보강하고, 자연 환경에 대응하여 대나무의 변형을 억제 또는 방지할 수 있다.In addition, the present invention reinforces the strength of the bamboo through the strength reinforcement step, and can suppress or prevent deformation of the bamboo in response to the natural environment.

또한, 본 발명은 국가 무형문화제 제60호의 낙죽장도기법이 적용됨으로써, 과거와 현재의 융복합 효과를 나타내고, 실버 세대에게 문화재를 향유할 수 있다.In addition, the present invention exhibits a convergence effect of the past and the present by applying the Nakjangjang pottery technique of National Intangible Cultural Heritage No. 60, and can enjoy the cultural property to the silver generation.

또한, 본 발명은 대나무의 고유 특성인 높은 강도와 경량감을 최대한 활용할 수 있다.In addition, the present invention can take full advantage of the high strength and lightness of the inherent properties of bamboo.

또한, 본 발명은 탄소섬유가 포함된 보강재가 부가됨으로써, 대나무의 고유 특성과 탄소 섬유의 재질적 특성(강철의 인장강도보다 10배 이상 강하고, 강철의 무게보다 10배 이상 가벼움)이 결합하여 지팡이의 내구성을 극대화시키고, 사용자의 안전에 기여할 수 있다.In addition, the present invention by adding a reinforcing material containing carbon fiber, the inherent properties of the bamboo and the material properties of the carbon fiber (10 times stronger than tensile strength of steel, 10 times lighter than the weight of steel) cane combined To maximize the durability of the user can contribute to the safety of the user.

도 1은 본 발명의 일 실시예에 따른 대나무 지팡이를 도시한 도면이다.
도 2는 본 발명의 일 실시예에 따른 대나무 지팡이의 변형예를 도시한 도면이다.
도 3은 본 발명의 일 실시예에 따른 대나무 지팡이의 제조방법을 도시한 도면이다.1 is a view showing a bamboo stick according to an embodiment of the present invention.
2 is a view showing a modification of the bamboo stick according to an embodiment of the present invention.
3 is a view showing a method of manufacturing a bamboo stick according to an embodiment of the present invention.

이하, 첨부된 도면들을 참조하여 본 발명에 따른 대나무 지팡이와 이것의 제조방법의 일 실시예를 설명한다. 이때, 본 발명은 실시예에 의해 제한되거나 한정되는 것은 아니다. 또한, 본 발명을 설명함에 있어서, 공지된 기능 혹은 구성에 대해 구체적인 설명은 본 발명의 요지를 명확하게 하기 위해 생략될 수 있다.Hereinafter, with reference to the accompanying drawings will be described an embodiment of a bamboo stick and a method for manufacturing the same according to the present invention. At this time, the present invention is not limited or limited by the embodiment. In addition, in describing the present invention, a detailed description of known functions or configurations may be omitted to clarify the gist of the present invention.

도 1 내지 도 3을 참조하면, 본 발명의 일 실시예에 따른 대나무 지팡이는 본체부(10)를 포함하고, 밴드부(20)와 머리부(30)와 지지부(40) 중 적어도 어느 하나를 더 포함할 수 있다.1 to 3, the bamboo stick according to an embodiment of the present invention includes a body portion 10, and further includes at least one of the band portion 20, the head portion 30, and the support portion 40. It may include.

본체부(10)는 기설정된 길이를 갖는 대나무가 포함된다. 본체부(10)에서 기설정된 길이는 90cm 내지 100cm의 길이를 포함할 수 있다. 대나무는 본 발명의 일 실시예에 따른 대나무 지팡이의 제조방법에 의해 제조된다.The body portion 10 includes bamboo having a predetermined length. The predetermined length in the body portion 10 may include a length of 90cm to 100cm. Bamboo is produced by the method for producing a bamboo stick according to an embodiment of the present invention.

본체부(10)에서 대나무는 직진도가 높은 것으로, 구갑죽 또는 분죽을 사용할 수 있다. 구갑죽의 경우, 직진도가 높은 것으로, 마디가 곧은 것을 선정하는 것이 유리하다. 분죽의 경우, 직진도가 높은 것으로, 뿌리째 채취된 것을 선정하는 것이 유리하다.Bamboo in the body portion 10 is a high straightness, it can be used beetle or powdered. In the case of the beaded porridge, it is advantageous to select a straight one with a high straightness. In the case of the powder, it is advantageous that the straightness is high, and that the root sample is selected.

지금부터는 본 발명의 일 실시예에 따른 대나무 지팡이의 제조방법에 대하여 설명한다.Hereinafter, a method of manufacturing a bamboo stick according to an embodiment of the present invention.

본 발명의 일 실시예에 따른 대나무 지팡이의 제조방법은 퍼징단계(S2)와, 표면처리단계(S3)와, 건조단계(S4)와, 길이조정단계(S5)를 포함하고, 선별단계(S1)와, 강도보강단계(S6)와, 마감단계(S7)와, 버닝단계(S8)와, 코팅단계(S9) 중 적어도 어느 하나를 더 포함할 수 있다.Bamboo stick manufacturing method according to an embodiment of the present invention includes a purging step (S2), surface treatment step (S3), drying step (S4), length adjustment step (S5), selection step (S1) ), And may further include at least one of strength reinforcing step (S6), finishing step (S7), burning step (S8), coating step (S9).

선별단계(S1)는 기설정된 길이와 같거나 큰 형태로 대나무를 선정한다. 기설정된 길이는 90cm 내지 100cm의 길이를 포함할 수 있다. 대나무는 직진도가 높은 것으로, 구갑죽 또는 분죽을 사용할 수 있다. 구갑죽의 경우, 직진도가 높은 것으로, 마디가 곧은 것을 선정하는 것이 유리하다. 분죽의 경우, 직진도가 높은 것으로, 뿌리째 채취된 것을 선정하는 것이 유리하다. 선별단계(S1)에서 선정되는 대나무는 통상 100cm 내지 140cm의 길이를 가짐으로써, 길이조정단계(S5)에서 기설정된 길이로 줄일 수 있고, 대나무의 폐기량을 줄일 수 있다.In the selection step S1, bamboo is selected to have a shape equal to or larger than a predetermined length. The predetermined length may include a length of 90 cm to 100 cm. Bamboo has a high straightness, and can be used beetle or powder. In the case of the beaded porridge, it is advantageous to select a straight one with a high straightness. In the case of the powder, it is advantageous that the straightness is high, and that the root sample is selected. Bamboo selected in the sorting step (S1) is usually having a length of 100cm to 140cm, can be reduced to a predetermined length in the length adjustment step (S5), it is possible to reduce the waste of bamboo.

퍼징단계(S2)는 선정된 대나무를 수용액에서 끓인다. 특히, 퍼징단계(S2)는 65 중량% 내지 75 중량%의 물에 25 중량% 내지 35 중량%의 수산화나트륨이 혼합한 수용액을 이용한다. 또한, 선정된 대나무는 수용액에서 60분 내지 90분 간 끓인다. 또한, 수용액은 섭씨 100도 내지 섭씨 120도의 온도를 유지하도록 한다.Purging step (S2) to boil the selected bamboo in an aqueous solution. In particular, the purging step (S2) uses an aqueous solution in which 25% to 35% by weight of sodium hydroxide is mixed with 65% to 75% by weight of water. In addition, the selected bamboo boils for 60 to 90 minutes in an aqueous solution. In addition, the aqueous solution is to maintain a temperature of 100 degrees Celsius to 120 degrees Celsius.

그러면, 퍼징단계(S2)의 수치한정을 통해 대나무의 섬유질에서 진액을 충분히 제거할 수 있고, 대나무가 갈라지거나 대나무의 섬유질이 손상되는 것을 방지하며, 대나무의 직진도를 간편하게 조정할 수 있다.Then, through the numerical limitation of the purging step (S2) it is possible to sufficiently remove the essence from the fiber of the bamboo, to prevent the bamboo split or damage the fiber of the bamboo, it is possible to easily adjust the straightness of the bamboo.

하지만, 퍼징단계(S2)의 수치한정범위보다 작을 경우, 좀더 자세하게, 수산화나트륨의 함량이 25 중량%보다 작을 경우, 수용액의 끓는 시간이 60분보다 작을 경우, 수용액의 끓는 온도가 섭씨 100도 보다 작을 경우, 수용액을 끓이는 시간이 늘어나고, 대나무의 섬유질에서 진액을 충분히 배출시키지 못하며, 후술하는 건조단계(S4), 강도보강단계(S6), 마감단계(S7), 버닝단계(S8) 중 적어도 어느 하나에서 대나무가 갈라지는 문제점이 있었다.However, if less than the numerical limit of the purging step (S2), in more detail, when the content of sodium hydroxide is less than 25% by weight, when the boiling time of the aqueous solution is less than 60 minutes, the boiling temperature of the aqueous solution is more than 100 degrees Celsius When small, the time to boil the aqueous solution is increased, the liquid is not sufficiently discharged from the fiber of bamboo, at least any of the drying step (S4), strength reinforcing step (S6), finishing step (S7), burning step (S8) to be described later There was a problem of splitting bamboo in one.

또한, 퍼징단계(S2)의 수치한정범위보다 클 경우, 좀더 자세하게, 수산화나트륨의 함량이 35 중량%보다 클 경우, 수용액의 끓는 시간이 90분보다 클 경우, 수용액의 끓는 온도가 섭씨 120도 보다 클 경우, 수용액을 끓이는 시간을 조정하기 어렵고, 대나무의 섬유질에서 진액의 배출 정도를 조절하기 어려우며, 대나무의 섬유질이 손상되며, 대나무의 직진도를 조정할 때, 대나무가 파손되는 문제점이 있었다.In addition, when greater than the numerical limit of the purging step (S2), in more detail, when the content of sodium hydroxide is greater than 35% by weight, when the boiling time of the aqueous solution is greater than 90 minutes, the boiling temperature of the aqueous solution is more than 120 degrees Celsius If large, it is difficult to adjust the boiling time of the aqueous solution, it is difficult to control the degree of discharge of the juice from the fiber of the bamboo, the fiber of the bamboo is damaged, when adjusting the straightness of the bamboo, there was a problem that the bamboo is broken.

표면처리단계(S3)는 퍼징단계(S2)를 거친 다음, 대나무의 표면에서 이물질을 제거한다. 표면처리단계(S3)는 삶아진 대나무에서 변형된 부분의 직진도를 간편하게 조정할 수 있다.Surface treatment step (S3) is a purging step (S2), and then removes foreign matter from the surface of the bamboo. Surface treatment step (S3) can be easily adjusted the straightness of the deformed portion of the boiled bamboo.

건조단계(S4)는 표면처리단계(S3)를 거친 다음, 대나무를 건조시킨다. 건조단계(S4)에서는 직사광선을 피하고, 통풍이 잘되는 그늘을 이용한다. 건조단계(S4)는 2개월 내지 3개월의 소요시간이 요구된다. 건조단계(S4)는 건조 과정에서 대나무의 뒤틀림을 방지하고, 대나무의 직진도를 유지시킬 수 있다.The drying step (S4) is subjected to the surface treatment step (S3), and then dried bamboo. In the drying step (S4) to avoid direct sunlight, use a well-ventilated shade. Drying step (S4) is required for two months to three months. Drying step (S4) may prevent the distortion of the bamboo in the drying process, it is possible to maintain the straightness of the bamboo.

길이조정단계(S5)는 건조단계(S4)를 거친 다음, 대나무를 기설정된 길이로 절단한다. 길이조정단계(S5)에서 기설정된 길이는 90cm 내지 100cm의 길이를 포함할 수 있다. 길이조정단계(S5)에서는 대나무의 마디 끝단이 지팡이의 단부가 되도록 하여 대나무의 강도를 보강하고, 후속 공정에서 대나무의 갈라짐 또는 대나무의 변형 또는 대나무의 파손을 방지할 수 있다.Length adjusting step (S5) is subjected to a drying step (S4), and then cut bamboo to a predetermined length. The predetermined length in the length adjustment step (S5) may include a length of 90cm to 100cm. In the length adjustment step (S5) it is possible to reinforce the strength of the bamboo by the end of the bar of the bamboo to the end of the cane, and to prevent cracking or deformation of the bamboo or breakage of the bamboo in a subsequent process.

강도보강단계(S6)는 길이조정단계(S5)를 거친 다음, 대나무의 중심에 보강재를 삽입한다.Strength reinforcement step (S6) after the length adjustment step (S5), insert the reinforcement in the center of the bamboo.

강도보강단계(S6)는 기설정된 직경으로 대나무의 중심에 보강홀부를 형성하는 타공단계(S61)와, 보강홀부에 접착제를 주입하는 주입단계(S62)와, 주입단계(S62)를 거친 다음 보강홀부에 보강재를 삽입하는 보강재삽입단계(S63)를 포함한다.Strength reinforcement step (S6) is a punching step (S61) to form a reinforcing hole in the center of the bamboo with a predetermined diameter, the injection step (S62) and the injection step (S62) to inject the adhesive to the reinforcing hole reinforcement Reinforcement inserting step (S63) for inserting the reinforcement to the hole portion.

강도보강단계(S6)는 보강재삽입단계(S63)를 거친 다음, 접착제를 경화시키는 경화단계(S64)를 더 포함할 수 있다.Strength reinforcement step (S6) may further comprise a curing step (S64) after the reinforcing material insertion step (S63), to cure the adhesive.

기설정된 직경은 대나무의 직경에 대응하여 5mm 내지 10mm를 포함할 수 있다. 좀더 자세하게, 기설정된 직경은 6mm 내지 8mm를 포함할 수 있다. 그러면, 보강재의 직경에 대응하여 대나무의 강도를 충분히 보강할 수 있다.The preset diameter may include 5 mm to 10 mm corresponding to the diameter of the bamboo. In more detail, the predetermined diameter may include 6mm to 8mm. Then, the strength of the bamboo can be sufficiently reinforced corresponding to the diameter of the reinforcing material.

하지만, 기설정된 직경이 수치한정범위보다 작은 경우, 보강재를 삽입하는 과정에서 보강홀부가 막히는 문제점이 있었다. 또한, 기설정된 직경이 수치한정범위보다 큰 경우, 접착제와 보강재를 과다하게 사용하게 되며, 보강재에 의해 지팡이의 하중이 증가하는 문제점이 있었다.However, when the predetermined diameter is smaller than the numerical limit, there is a problem that the reinforcing hole is blocked in the process of inserting the reinforcing material. In addition, when the predetermined diameter is larger than the numerical limit, the adhesive and the reinforcement is used excessively, there is a problem that the load of the cane is increased by the reinforcement.

접착제는 대나무와 보강재를 안정되게 접착 고정시키고, 대나무와 보강재의 변형을 억제 또는 방지하기 위해 아교를 포함할 수 있다.The adhesive may comprise glue to stably bond and secure the bamboo and the reinforcement and to inhibit or prevent deformation of the bamboo and the reinforcement.

보강재는 수분에 의한 부식 및 굽힘 방지를 위해 탄소섬유를 포함할 수 있다.The reinforcement may include carbon fiber to prevent corrosion and bending by moisture.

강도보강단계(S6)를 거침에 따라 지팡이의 강도가 보강되고, 지팡이의 굽힘을 방지하며, 지팡이의 탄성을 향상시킬 수 있다.By following the strength step (S6) can be reinforced the strength of the cane, to prevent bending of the cane, can improve the elasticity of the cane.

마감단계(S7)는 길이조정단계(S5) 또는 강도보강단계(S6)를 거친 다음, 대나무의 양단부 중 적어도 어느 하나를 가공한다.Finishing step (S7) after the length adjustment step (S5) or strength reinforcement step (S6), at least one of the two ends of the bamboo is processed.

마감단계(S7)는 대나무에서 사용자가 파지하는 부분 쪽에 밴드결합부(14)를 관통 형성할 수 있다. 밴드결합부(14)에는 사용자와의 결합을 위한 밴드부(20)가 끼움 결합될 수 있다. 밴드부(20)는 국내에 알려진 전통매듭 방식의 끈을 적용할 수 있다. 밴드부(20)는 본체부(10)를 파지하는 사용자의 손을 구속하거나 장식용으로 사용할 수 있다.Finishing step (S7) may be formed through the band coupling portion 14 on the side of the gripping portion of the bamboo. The band coupling portion 14 may be fitted with a band portion 20 for coupling with the user. Band portion 20 may apply a string of traditional knots known in the country. The band part 20 may restrain the user's hand holding the main body 10 or use it for decoration.

마감단계(S7)는 대나무에서 사용자가 파지하는 부분의 단부에 머리부(30)를 구비할 수 있다. 머리부(30)는 대나무의 뿌리를 포함할 수 있다. 그러면, 마감단계(S7)는 대나무의 뿌리를 가공하거나, 가공된 대나무의 뿌리를 사용자가 파지하는 부분의 단부에 결합할 수 있다.Finishing step (S7) may be provided with a head 30 at the end of the portion of the user grips in bamboo. Head 30 may include the root of the bamboo. Then, the finishing step (S7) may process the roots of the bamboo, or combine the processed bamboo roots with the end of the part grasped by the user.

마감단계(S7)는 대나무에서 사용자가 파지하는 부분의 반대쪽에 지지부(40)를 결합할 수 있다. 지지부(40)는 대나무에서 바닥에 접촉되는 부분의 단부에 결합될 수 있다. 지지부(40)는 동물의 뿔(우각 등), 동물의 뼈, 우레탄 중 어느 하나의 재질을 가질 수 있다. 지지부(40)는 하나의 돌부로 이루어져 바닥에 접촉되거나, 둘 이상의 돌부로 이루어져 바닥에 접촉될 수 있다.Finishing step (S7) may be coupled to the support 40 on the opposite side of the gripping portion of the bamboo. The support 40 may be coupled to the end of the portion of bamboo that is in contact with the floor. The support 40 may have any one material of an animal's horn (eg, an angle), an animal's bone, or urethane. The support part 40 may be made of one protrusion to be in contact with the bottom, or may be made of two or more protrusions to be in contact with the bottom.

버닝단계(S8)는 길이조정단계(S5) 또는 강도보강단계(S6) 또는 마감단계(S7)를 거친 다음, 대나무의 표면에 문양을 새긴다. 문양은 지팡이의 로고 또는 각종 마크 등을 포함함으로써, 지팡이의 외관을 미려하게 할 수 있다.Burning step (S8) after the length adjustment step (S5) or strength reinforcement step (S6) or finishing step (S7), and then carves a pattern on the surface of the bamboo. The pattern can be made beautiful by the appearance of the cane by including the cane's logo or various marks.

버닝단계(S8)는 낙죽기법 또는 버닝기법을 이용하여 대나무의 외주면에 문양을 표시할 수 있다.The burning step S8 may display a pattern on the outer circumferential surface of the bamboo by using the larch or burning method.

코팅단계(S9)는 길이조정단계(S5) 또는 강도보강단계(S6) 또는 마감단계(S7) 또는 버닝단계(S8)를 거친 다음, 대나무의 표면을 코팅한다. 코팅단계(S9)는 대나무의 표면에 옻칠을 1회 이상 반복 실시한다. 코팅단계(S9)에서는 대나무의 표면에 코팅된 코팅제를 경화시킬 수 있다. 코팅단계(S9)에서는 대나무의 표면에 코팅제를 코팅한 다음, 통풍이 잘되는 그늘에서 30시간 내지 40시간 건조시킴으로서, 코팅제를 경화시킬 수 있다.Coating step (S9) after the length adjustment step (S5) or strength reinforcement step (S6) or finishing step (S7) or burning step (S8), and then coating the surface of the bamboo. Coating step (S9) is carried out by repeating the lacquer one or more times on the surface of the bamboo. In the coating step (S9) can be cured coating agent coated on the surface of the bamboo. In the coating step (S9) by coating the coating on the surface of the bamboo, and then dried for 30 to 40 hours in a well-ventilated shade, the coating can be cured.

코팅단계(S9)는 대나무의 강도를 보강하면서 대나무를 보호할 수 있고, 버닝단계(S8)를 거쳐 새겨진 문양을 보호할 수 있으며, 지팡이의 수명을 연장시킬 수 있다.Coating step (S9) can protect the bamboo while reinforcing the strength of the bamboo, can protect the pattern carved through the burning step (S8), can extend the life of the cane.

상술한 대나무 지팡이와 이것의 제조방법에 따르면, 대나무를 이용하여 안정된 지팡이를 제조할 수 있다. 특히, 퍼징단계(S2)의 수치한정을 통해 대나무의 섬유질에서 진액을 충분히 제거할 수 있고, 대나무가 갈라지거나 대나무의 섬유질이 손상되는 것을 방지하며, 대나무의 직진도를 간편하게 조정할 수 있다.According to the above-mentioned bamboo stick and the manufacturing method thereof, it is possible to manufacture a stable stick using bamboo. In particular, through the numerical limitation of the purging step (S2) it is possible to sufficiently remove the essence from the fiber of the bamboo, to prevent the bamboo split or damage the fiber of the bamboo, it is possible to easily adjust the straightness of the bamboo.

또한, 강도보강단계(S6)를 통해 대나무의 강도를 보강하고, 자연 환경에 대응하여 대나무의 변형을 억제 또는 방지할 수 있다.In addition, the strength reinforcement step (S6) to reinforce the strength of the bamboo, it can be suppressed or prevented deformation of the bamboo in response to the natural environment.

또한, 국가 무형문화제 제60호의 낙죽장도기법이 적용됨으로써, 과거와 현재의 융복합 효과를 나타내고, 실버 세대에게 문화재를 향유할 수 있다.In addition, the application of the Nakjangjang pottery technique of National Intangible Cultural Heritage No. 60 shows the convergence effect of the past and the present, and it is possible to enjoy the cultural property to the silver generation.

또한, 대나무의 고유 특성인 높은 강도와 경량감을 최대한 활용할 수 있다.In addition, it is possible to take full advantage of the high strength and lightness of the unique characteristics of bamboo.

또한, 탄소섬유가 포함된 보강재가 부가됨으로써, 대나무의 고유 특성과 탄소 섬유의 재질적 특성(강철의 인장강도보다 10배 이상 강하고, 강철의 무게보다 10배 이상 가벼움)이 결합하여 지팡이의 내구성을 극대화시키고, 사용자의 안전에 기여할 수 있다.In addition, by adding reinforcing material containing carbon fiber, the inherent properties of bamboo and the material properties of carbon fiber (more than 10 times stronger than steel tensile strength and 10 times lighter than steel weight) combine to improve the durability of the cane. To maximize the user's safety.

상술한 바와 같이 도면을 참조하여 본 발명의 바람직한 실시예를 설명하였지만, 해당 기술분야의 숙련된 당업자라면, 하기의 청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 또는 변경시킬 수 있다.Although the preferred embodiments of the present invention have been described with reference to the drawings as described above, those skilled in the art can variously change the present invention without departing from the spirit and scope of the present invention as set forth in the claims below. Can be modified or changed.

10: 본체부 14: 밴드결합부 20: 밴드부
30: 머리부 40: 지지부
S1: 선별단계 S2: 퍼징단계 S3: 표면처리단계
S4: 건조단계 S5: 길이조정단계 S6: 강도보강단계
S61: 타공단계 S62: 주입단계 S63: 보강재삽입단계
S64: 경화단계 S7: 마감단계 S8: 버닝단계
S9: 코팅단계10: main body portion 14: band coupling portion 20: band portion
30: head 40: support part
S1: screening step S2: purging step S3: surface treatment step
S4: drying step S5: length adjusting step S6: strength reinforcing step
S61: punching step S62: injection step S63: reinforcing material insertion step
S64: curing step S7: finishing step S8: burning step
S9: Coating Step

Claims (5)

수용액에서 대나무를 끓이는 퍼징단계;
상기 퍼징단계를 거친 다음, 상기 대나무의 표면에서 이물질을 제거하는 표면처리단계;
상기 표면처리단계를 거친 다음, 상기 대나무를 건조시키는 건조단계; 및
상기 건조단계를 거친 다음, 상기 대나무를 기설정된 길이로 절단하는 길이조정단계;를 포함하고,
상기 퍼징단계는 65 중량% 내지 75 중량%의 물에 25 중량% 내지 35 중량%의 수산화나트륨을 혼합한 수용액을 이용하여 상기 대나무를 60분 내지 90분 간 끓이는 것을 특징으로 하는 대나무 지팡이의 제조방법.Purging step of boiling bamboo in an aqueous solution;
After the purging step, the surface treatment step of removing foreign matter from the surface of the bamboo;
After the surface treatment step, the drying step of drying the bamboo; And
After the drying step, the length adjustment step of cutting the bamboo to a predetermined length; includes,
The purging step is a method of producing a bamboo stick, characterized in that to boil the bamboo for 60 to 90 minutes using an aqueous solution of 25% to 35% by weight of sodium hydroxide in 65% to 75% by weight of water . 제1항에 있어서,
상기 길이조정단계를 거친 다음, 상기 대나무의 중심에 보강재를 삽입하는 강도보강단계;를 더 포함하는 것을 특징으로 하는 대나무 지팡이의 제조방법.The method of claim 1,
After the length adjustment step, the strength reinforcing step of inserting a reinforcing material in the center of the bamboo; manufacturing method of the bamboo stick further comprising. 제2항에 있어서,
상기 강도보강단계는,
기설정된 직경으로 상기 대나무의 중심에 보강홀부를 형성하는 타공단계;
상기 보강홀부에 접착제를 주입하는 주입단계; 및
상기 주입단계를 거친 다음, 상기 보강홀부에 보강재를 삽입하는 보강재삽입단계;를 포함하는 것을 특징으로 하는 대나무 지팡이의 제조방법.The method of claim 2,
The strength reinforcement step,
A perforating step of forming a reinforcing hole in the center of the bamboo with a predetermined diameter;
Injecting an adhesive into the reinforcing hole; And
After the injection step, the reinforcing material inserting step of inserting a reinforcing material into the reinforcing hole; manufacturing method of the bamboo stick comprising a. 제1항에 있어서,
상기 길이조정단계를 거친 다음, 상기 대나무의 양단부 중 적어도 어느 하나를 가공하는 마감단계;
상기 길이조정단계를 거친 다음, 상기 대나무의 표면에 문양을 새기는 버닝단계; 및
상기 길이조정단계를 거친 다음, 상기 대나무의 표면을 코팅하는 코팅단계;
중 적어도 어느 하나를 더 포함하는 것을 특징으로 하는 대나무 지팡이의 제조방법.The method of claim 1,
After the length adjustment step, the finishing step of processing at least one of both ends of the bamboo;
After the length adjustment step, the burning step of carving a pattern on the surface of the bamboo; And
After the length adjustment step, the coating step of coating the surface of the bamboo;
Method for producing a bamboo stick, characterized in that it further comprises at least any one of. 90cm 내지 100cm의 길이를 갖는 대나무가 포함되는 본체부;를 포함하고,
상기 대나무는,
제1항 내지 제4항 중 어느 한 항에 기재된 제조방법에 의해 가공되는 것을 특징으로 하는 대나무 지팡이.
It includes; a main body portion including a bamboo having a length of 90cm to 100cm, including,
The bamboo,
The bamboo stick processed by the manufacturing method in any one of Claims 1-4.
KR1020180053751A 2018-05-10 2018-05-10 Bamboo stick and manufacturing method of this KR20190129304A (en)