CN106426476B - A kind of manufacture craft of bamboo-root carving flowerpot - Google Patents

A kind of manufacture craft of bamboo-root carving flowerpot Download PDF

Info

Publication number
CN106426476B
CN106426476B CN201610945658.9A CN201610945658A CN106426476B CN 106426476 B CN106426476 B CN 106426476B CN 201610945658 A CN201610945658 A CN 201610945658A CN 106426476 B CN106426476 B CN 106426476B
Authority
CN
China
Prior art keywords
root
bamboo
skill product
bamboo section
carbonization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610945658.9A
Other languages
Chinese (zh)
Other versions
CN106426476A (en
Inventor
穆仁平
殷其惠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chishui Zhibo Art Carving Crafts Co Ltd
Original Assignee
Chishui Zhibo Art Carving Crafts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chishui Zhibo Art Carving Crafts Co Ltd filed Critical Chishui Zhibo Art Carving Crafts Co Ltd
Priority to CN201610945658.9A priority Critical patent/CN106426476B/en
Publication of CN106426476A publication Critical patent/CN106426476A/en
Application granted granted Critical
Publication of CN106426476B publication Critical patent/CN106426476B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of manufacture crafts of bamboo-root carving flowerpot, include the following steps：1) selection；2) shaping；3) boiling；4) carbonization treatment；5) preservative treatment；6) dry；7) it polishes；8) priming, photocuring, mill prime treatment；9) casting resin.Flowerpot internal structure made from this technique is hard, should not rot, deform, flowerpot anatomic shape obtained, has higher ornamental value and practical value.

Description

A kind of manufacture craft of bamboo-root carving flowerpot
Technical field
The present invention relates to ornameutal handiwork technique, more particularly to a kind of manufacture craft of bamboo-root carving flowerpot.
Background technology
Carving root, be using the spontaneous form of tree root, bamboo root etc. and distortion form as artistic creation object, by design conception, Art processing, creates the artistic works such as personage, animal, implements.Carving root art is to find natural beauty and show creative add The plastic arts of work, mainly using the natural form of root timber come expression art image, complementary progress artificial treatment modification, carving root Be otherwise known as the art of root.
Bamboo-root carving belongs to one kind of carving root art, mainly by the way that bamboo root to be carried out to the processing of artistry, then uses more Kind process makes it that deformation of rotting will not occur, so that people watch for a long time.Current bamboo-root carving effect is single, and practical value is not It is high, if it is possible to existing bamboo-root carving processing technology is improved, the utility function for having certain is enabled, undoubtedly will Increase more temperament and interest for people's lives.
Invention content
In view of this, the object of the present invention is to provide a kind of manufacture craft of bamboo-root carving flowerpot, the bamboo-root carving produced is spent Basin is highly practical, and dimensionally stable is unlikely to deform, beautiful and practical.
The purpose of the present invention is what is be achieved through the following technical solutions：
A kind of manufacture craft of bamboo-root carving flowerpot, includes the following steps：
1) selection：The bamboo root for including bamboo section of undried suitable shape is chosen, wherein bottom bamboo root is as pedestal, position Bamboo section in middle and upper part is used as container, the diameter of the bamboo section to be not less than 18cm；
2) shaping：Root is trimmed first, then digs out profile with chisel, then is engraved as root skill product, the pedestal after engraving It should remain able to steadily place；
3) boiling：Root skill product is put into 60-80 DEG C of hot water tank and is stood, time 10-20min, then Water in container is carried out to be heated to fluidized state, and is kept for 8-10 hours；
4) carbonization treatment；
5) preservative treatment：Root skill product after carbonization preservative is impregnated into 3-5h；
6) dry：It will be through processed skill product natural air drying of step 5)；
7) it polishes：It is first integrally polished carving root with coarse sandpaper when polishing, is then polished with fine sandpaper；
8) priming, photocuring, mill prime treatment：Fight each other it is honed after root skill product carry out successively priming, photocuring, Grind prime treatment；
9) casting resin：Cast mold is put into bamboo section, the mold is cylinder or cylindric, and internal diameter is slightly less than Bamboo section internal diameter 2-6cm, bottom be slightly above bamboo section bottom about 1-3cm, the anchor ring of the mold externally be provided with can on move down Dynamic cyclic annular stay hook, after being aligned according to concentric manner, mobile stay hook is allowed to catch on the top edge of bamboo section, in mold Casting space is formed between outer surface and the inner surface of bamboo section, resin solution is poured into casting space and fills and places to resin Solution cures.
Further, in step 4), bamboo-root carving is handled using secondary carbonization technique, will specifically pass through step 3) Processed skill product is put into carbide furnace, is once carbonized, and temperature is controlled at 100-120 DEG C, and the time was at 1-3 hours；
After root skill product cooling completely after primary carbonization, secondary carbonization is carried out, secondary carbonization first exists root skill product It is carbonized at a high temperature of 110-120 DEG C, the time is 1-2 hours, then heats to 130-140 DEG C, the time is 1-1.5 hours.
Further, further include step 10), after resin solution curing, several air holes are opened up in the lower half of bamboo section.
Further, used resin solution is the resin containing curing agent, weight of the curing agent in resin solution It is 1%-3% than content.
The beneficial effects of the invention are as follows：
A kind of manufacture craft of bamboo-root carving flowerpot of the present invention, operation is relatively simple, by boiling, makes to receive inside bamboo wood Contracting reduces water loss, so as to prevent bamboo-root carving craftwork of long duration rear dry and cracked, makes in bamboo wood additionally by carbonization treatment Organic matter such as sugar, starch, protein decompose in the environment of high temperature, high humidity, so that the insects such as fungi is lost source of nutrition, simultaneously The worm's ovum being attached in bamboo wood and fungi are killed again, therefore the technique can prevent bamboo-root carving craftwork mouldy, then uses preservative After processing, craftwork internal structure is harder, should not rot, deform, and flowerpot obtained is both artistic and practical, has higher ornamental Value and practical value, more temperament and interest are brought to people's lives.
Other advantages, target and the feature of the present invention will be illustrated in the following description to a certain extent, and And to a certain extent, based on will be apparent to those skilled in the art to investigating hereafter, Huo Zheke To be instructed from the practice of the present invention.The target and other advantages of the present invention can by following specification realizing and It obtains.
Specific implementation mode
The preferred embodiment of the present invention will be described in detail below.Preferred embodiment be should be appreciated that only for saying The bright present invention, the protection domain being not intended to be limiting of the invention.
Embodiment one
A kind of manufacture craft of bamboo-root carving flowerpot of the present invention, includes the following steps：
1) selection：The bamboo root for including bamboo section of undried suitable shape is chosen, wherein bottom bamboo root is as pedestal, position Bamboo section in middle and upper part is used as container, a diameter of 16cm of bamboo section；
2) shaping：Root is trimmed first, then digs out profile with chisel, then is engraved as root skill product, the pedestal after engraving It should remain able to steadily place；
3) boiling：Root skill product is put into 60 DEG C of hot water tank and is stood, time 20min, then by container In water be heated to fluidized state, and kept for 8 hours；
4) carbonization treatment：In the present embodiment, bamboo-root carving is handled using secondary carbonization technique, will specifically pass through step Rapid 3) processed skill product is put into carbide furnace, is once carbonized, and temperature is controlled at 100 DEG C, and the time was at 3 hours；
After root skill product cooling completely after primary carbonization, secondary carbonization is carried out, secondary carbonization first exists root skill product It is carbonized at a high temperature of 110 DEG C, the time is 2 hours, then heats to 130 DEG C, the time is 1.5 hours.
5) preservative treatment：Root skill product after carbonization preservative is impregnated into 3h；
6) dry：It will be through processed skill product natural air drying of step 5)；
7) it polishes：It is first integrally polished carving root with coarse sandpaper when polishing, is then polished with fine sandpaper；
8) priming, photocuring, mill prime treatment：Fight each other it is honed after root skill product carry out successively priming, photocuring, Grind prime treatment；
9) casting resin：Cast mold is put into bamboo section, mold is cylinder or cylindric, and internal diameter is slightly less than bamboo section Internal diameter 2cm, bottom be slightly above bamboo section bottom about 1cm state the anchor ring of mold externally be provided with it is moving up and down cyclic annular fixed Hook, after being aligned according to concentric manner, mobile stay hook is allowed to catch on the top edge of bamboo section, in the outer surface of mold and bamboo section Inner surface between form casting space, resin solution is poured into casting space and fills and places to resin solution curing, is adopted Resin solution is the resin containing curing agent, and weight ratio content of the curing agent in resin solution is 1%-3%.
10) after resin solution curing, several air holes are opened up in the lower half of bamboo section, consequently facilitating plant is ventilative, more Be conducive to the growth of plant.
The resin grade used in the present embodiment is 198B#, and corrosion resistance and good, intensity is higher, and the service life is also longer. In step 2), for the ease of the cast of step 9), can multiple tracks shallow trench be chiseled out in the interior surface of bamboo section in advance, to make Resin and the adhesive force on bamboo intersegmental part surface are more preferable, bond strength higher.
Embodiment two
A kind of manufacture craft of bamboo-root carving flowerpot of the present invention, includes the following steps：
1) selection：The bamboo root for including bamboo section of undried suitable shape is chosen, wherein bottom bamboo root is as pedestal, position Bamboo section in middle and upper part is used as container, a diameter of 14cm of bamboo section；
2) shaping：Root is trimmed first, then digs out profile with chisel, then is engraved as root skill product, the pedestal after engraving It should remain able to steadily place；
3) boiling：Root skill product is put into 80 DEG C of hot water tank and is stood, time 10min, then by container In water be heated to fluidized state, and kept for 10 hours；
4) carbonization treatment：In the present embodiment, bamboo-root carving is handled using secondary carbonization technique, will specifically pass through step Rapid 3) processed skill product is put into carbide furnace, is once carbonized, and temperature is controlled at 120 DEG C, and the time was at 1 hour；
After root skill product cooling completely after primary carbonization, secondary carbonization is carried out, secondary carbonization first exists root skill product It is carbonized at a high temperature of 120 DEG C, the time is 1 hour, then heats to 140 DEG C, the time is 1 hour.
5) preservative treatment：Root skill product after carbonization preservative is impregnated into 5h；
6) dry：It will be through processed skill product natural air drying of step 5)；
7) it polishes：It is first integrally polished carving root with coarse sandpaper when polishing, is then polished with fine sandpaper；
8) priming, photocuring, mill prime treatment：Fight each other it is honed after root skill product carry out successively priming, photocuring, Grind prime treatment；
9) casting resin：Cast mold is put into bamboo section, mold is cylinder or cylindric, and internal diameter is slightly less than bamboo section Internal diameter 6cm, bottom be slightly above bamboo section bottom about 3cm state the anchor ring of mold externally be provided with it is moving up and down cyclic annular fixed Hook, after being aligned according to concentric manner, mobile stay hook is allowed to catch on the top edge of bamboo section, in the outer surface of mold and bamboo section Inner surface between form casting space, resin solution is poured into casting space and fills and places to resin solution curing, is adopted Resin solution is the resin containing curing agent, and weight ratio content of the curing agent in resin solution is 1%-3%.The present embodiment The middle resin grade used is 199M#；
10) after resin solution curing, several air holes are opened up in the lower half of bamboo section, consequently facilitating plant is ventilative, more Be conducive to the growth of plant.
A kind of manufacture craft of bamboo-root carving flowerpot of the present invention makes bamboo-root carving be provided with more functions, and corrosion-resistant, no Deformation, step is simple, easily operated, at low cost.
Finally illustrate, the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although with reference to compared with Good embodiment describes the invention in detail, it will be understood by those of ordinary skill in the art that, it can be to the skill of the present invention Art scheme is modified or replaced equivalently, and without departing from the objective and range of the technical program, should all be covered in the present invention Right in.

Claims (3)

1. a kind of manufacture craft of bamboo-root carving flowerpot, it is characterised in that：Include the following steps：
1) selection：The bamboo root for including bamboo section of undried suitable shape is chosen, wherein bottom bamboo root is as pedestal, in being located at The bamboo section on top is used as container, the diameter of the bamboo section to be not less than 18cm；
2) shaping：Root is trimmed first, then digs out profile with chisel, then is engraved as root skill product, and the pedestal after engraving should be protected Holding steadily to place；
3) boiling：Root skill product is put into 60-80 DEG C of hot water tank and is stood, then time 10-20min will hold Water in device carries out being heated to fluidized state, and is kept for 8-10 hours；
4) carbonization treatment；Bamboo-root carving is handled using secondary carbonization technique, will specifically pass through processed of step 3) Skill product is put into carbide furnace, is once carbonized, and temperature is controlled at 100-120 DEG C, and the time was at 1-3 hours；
After root skill product cooling completely after primary carbonization, secondary carbonization is carried out, secondary carbonization is first by root skill product in 110- It is carbonized at a high temperature of 120 DEG C, the time is 1-2 hours, then heats to 130-140 DEG C, the time is 1-1.5 hours；
5) preservative treatment：Root skill product after carbonization preservative is impregnated into 3-5h；
6) dry：It will be through processed skill product natural air drying of step 5)；
7) it polishes：It is first integrally polished carving root with coarse sandpaper when polishing, is then polished with fine sandpaper；
8) priming, photocuring, mill prime treatment：Fight each other it is honed after root skill product carry out successively priming, photocuring, mill bottom Paint processing；
9) casting resin：Multiple tracks shallow trench is chiseled out in the interior surface of bamboo section, cast mold, the mould are put into bamboo section Tool is cylinder or cylindric, and internal diameter is less than bamboo section internal diameter 2-6cm, and bottom is higher than the bottom 1-3cm of bamboo section, and the mold is along outer The anchor ring in portion is provided with cyclic annular stay hook moving up and down, and after being aligned according to concentric manner, mobile stay hook is allowed to catch on bamboo The top edge of section pours into form casting space between the outer surface of mold and the inner surface of bamboo section in casting space Resin solution is filled and is placed to resin solution curing.
2. a kind of manufacture craft of bamboo-root carving flowerpot as described in claim 1, it is characterised in that：Further include step 10), is setting After solution curing, several air holes are opened up in the lower half of bamboo section.
3. a kind of manufacture craft of bamboo-root carving flowerpot as described in claim 1, it is characterised in that：Used resin solution is Resin containing curing agent, weight ratio content of the curing agent in resin solution are 1%-3%.
CN201610945658.9A 2016-11-02 2016-11-02 A kind of manufacture craft of bamboo-root carving flowerpot Active CN106426476B (en)