KR20190081528A

KR20190081528A - Comsmetic mask having adhesion property

Info

Publication number: KR20190081528A
Application number: KR1020170184134A
Authority: KR
Inventors: 원종호
Original assignee: 원종호
Priority date: 2017-12-29
Filing date: 2017-12-29
Publication date: 2019-07-09
Also published as: KR102031159B1

Abstract

The present invention relates to an adhesive cosmetic mask sheet. More specifically, the present invention relates to an adhesive cosmetic mask sheet that is adhesive-fixed to the skin without being limited in movement, can be used semi-permanently by washing, and is dry, thereby causing no inconvenience due to cosmetic formulation flowing down. In the adhesive cosmetic mask sheet of the present invention, a surface layer formed of a thermally conductive silicone composition; a design forming layer comprising an image print or a lace; a support layer having a mesh structure formed by tricot; and a skin adhesive layer formed of a skin adhesive composition and adhesive-fixed to the skin, are sequentially stacked.

Description

{COMSMETIC MASK HAVING ADHESION PROPERTY}

본 발명은 점착성 미용 마스크 시트에 관한 것으로서, 보다 상세하게는 피부에 점착고정되어 움직임의 제한을 받지 않고, 세척하여 반영구적으로 사용할 수 있으며, 건식으로 화장료 제제가 흐르는 불편함이 없는 점착성 미용 마스크 시트에 관한 것이다.More particularly, the present invention relates to a viscous cosmetic mask sheet which can be used semi-permanently without being restricted by movement, and can be used semi-permanently, .

일반적으로 마스크 시트는 미백, 보습, 진정, 주름개선 등의 기능성을 갖는 액상의 화장료 제제를 부직포, 셀룰로오스 펄프, 겔 등의 기재에 흡수시켜 통용되고 있다.In general, a mask sheet is commonly used by absorbing a liquid cosmetic preparation having functions such as whitening, moisturizing, soothing, and wrinkling on a base material such as a nonwoven fabric, a cellulose pulp, and a gel.

이처럼 대부분의 마스크 시트는 액상의 화장료 제제를 기재에 흡수시켰기 때문에 피부에 적용시, 액상의 화장료 제제가 피부 굴곡을 따라 흘러 불편함을 유발하였고, 인체의 움직임에 따라 쉽게 마스크 시트의 위치가 이동하거나 이탈되기 때문에 마스크 시트 사용시에는 이동에 제한을 받아왔다.Since most of the mask sheet absorbs the liquid cosmetic preparation into the substrate, the liquid cosmetic preparation flows along the skin curl when the liquid is applied to the skin, causing inconvenience, and the position of the mask sheet easily moves according to the movement of the human body It has been restricted in movement when using the mask sheet.

또한, 개봉과 동시에 화장용 제제의 증발이 시작되며, 피부 부착 후 화장용 제제가 모두 증발하면 마스크 시트 본연의 효과를 발휘할 수 없기 때문에 실질적으로 1회용으로 사용하는 것이 당연시 되어왔다.In addition, evaporation of the cosmetic preparation starts at the same time as opening the skin, and when the cosmetic preparation is completely evaporated after the skin attachment, the mask sheet can not exhibit its original effect.

이와 관련하여, 한국공개실용신안 제20-2017-0001761호는 안면에 마스크 팩을 착용한 후에도 활동이 용이하도록 피부에 대한 밀착성이 향상된 귀걸이형 페이스 마스크 팩을 제시하고 있으나, 이는 종래의 마스크 시트에 귀걸이가 형성된 것에 불과하여 종래의 마스크 시트의 화장료 제제의 증발과 1회용 사용과 같은 근본적인 문제점을 해결하지 못하였다.In this regard, Korean Utility Model No. 20-2017-0001761 discloses an ear-type face mask pack having improved skin adhesion so that even after wearing a mask pack on the face, It has been difficult to solve fundamental problems such as evaporation of the cosmetic preparation of the conventional mask sheet and disposable use.

한국공개실용신안 제20-2017-0001761호(귀걸이형 페이스 마스크 팩)Korean Utility Model Application No. 20-2017-0001761 (Earring Face Mask Pack)

상기와 같은 문제점을 해결하기 위한 본 발명의 목적은 피부에 점착고정되어 움직임의 제한을 받지 않고, 세척하여 반영구적으로 사용할 수 있으며, 건식으로 화장료 제제가 흐르는 불편함이 없는 점착성 미용 마스크 시트를 제공하는 것이다.An object of the present invention to solve the above problems is to provide a cosmetic beauty mask sheet which can be used semi-permanently without being restricted by movement, and can be used semi-permanently and without inconvenience that a cosmetic preparation flows dryly will be.

본 발명의 다른 목적은 토르말린이 방향성을 가지고 배열되어 외부 열의 전달과 음이온 및 원적외선 발산 효과를 극대화할 수 있는 점착성 미용 마스크 시트를 제공하는 것이다.Another object of the present invention is to provide a viscous cosmetic mask sheet in which tourmaline is arranged with directionality to maximize the effect of external heat transmission and anion and far-infrared radiation.

상기 과제를 해결하기 위한 본 발명의 점착성 미용 마스크 시트는 열전도 실리콘 조성물로 형성되는 표면층;과 이미지 인쇄물 또는 레이스를 포함하는 디자인 형성층;과 트리코트 방법으로 형성된 메쉬 구조를 갖는 지지층;과 피부 점착 조성물로 형성되어 피부에 점착 고정되는 피부 점착층;이 순차적으로 적층된 것을 특징으로 한다.In order to achieve the above object, the present invention provides a viscous cosmetic mask sheet comprising a surface layer formed of a thermally conductive silicone composition, a design forming layer comprising an image print or a lace, a support layer having a mesh structure formed by a tricot method, And a skin adhesive layer formed and fixed to the skin, are sequentially laminated.

상기 표면층은 수직으로 배열된 토르말린 펠렛을 포함하는 것을 특징으로 한다.Wherein the surface layer comprises a vertically arranged tourmaline pellet.

상기 피부 점착층은 폴리우레탄 수지, 아크릴 수지, 천연고무 수지, 합성고무 수지, 실리콘 수지 및 이들의 조합으로 이루어지는 베이스 수지 100중량부에 대하여, 아로마 캡슐 0.5 내지 3중량부, 토르말린 펠렛 5 내지 30중량부, 피톤치드 조성물로 코팅 처리된 광물 나노 입자 5 내지 10중량부를 포함하는 피부 점착 조성물에 의해 형성되는 것을 특징으로 한다.Wherein the skin adhesive layer comprises 0.5 to 3 parts by weight of an aromatic capsule, 5 to 30 parts by weight of a tourmaline pellet, 5 to 30 parts by weight of a tourmaline pellet to 100 parts by weight of a base resin comprising a polyurethane resin, an acrylic resin, a natural rubber resin, And 5 to 10 parts by weight of the mineral nanoparticles coated with the phytoncide composition.

상기 피부 점착층은 수평으로 배열된 토르말린 펠렛을 포함하는 것을 특징으로 한다.Wherein the skin adhesive layer comprises horizontally arranged tourmaline pellets.

상기 디자인 형성층과 상기 지지층은 열압착된 것을 특징으로 한다.And the design forming layer and the supporting layer are thermocompression bonded.

상기 디자인 형성층과 상기 지지층 사이에는 표면층보다 경도가 낮은 열전도성 실리콘 조성물로 형성되는 중간층을 더 포함하는 것을 특징으로 한다.And an intermediate layer formed between the design-forming layer and the support layer, the intermediate layer being formed of a thermoconductive silicone composition having a hardness lower than that of the surface layer.

상술한 바와 같이, 본 발명에 따른 점착성 미용 마스크 시트에 의하면, 피부에 점착고정되어 움직임의 제한을 받지 않고, 세척하여 반영구적으로 사용할 수 있으며, 건식으로 화장료 제제가 흐르는 불편함이 없는 효과가 있다. As described above, the viscous cosmetic mask sheet according to the present invention has an effect that it is fixed to the skin and is not restricted by movement, and can be used semi-permanently, and there is no inconvenience that the cosmetic preparation flows in a dry manner.

또한, 본 발명에 따른 점착성 미용 마스크 시트에 의하면, 토르말린이 방향성을 가지고 배열되어 외부 열의 전달과 음이온 및 원적외선 발산 효과를 극대화할 수 있는 효과가 있다. In addition, according to the viscous cosmetic mask sheet of the present invention, tourmaline is arranged with directionality so as to maximize the effect of external heat transmission, anion and far-infrared radiation.

도 1은 본 발명의 일 실시예에 따른 점착성 미용 마스크 시트(1)의 적층구조 단면도.
도 2는 본 발명에 따른 피부 점착층의 실시예.
도 3은 본 발명의 다른 실시예에 따른 점착성 미용 마스크 시트(2)의 적층구조 단면도. 1 is a sectional view of a layered structure of a viscous cosmetic mask sheet 1 according to an embodiment of the present invention.
Fig. 2 shows an embodiment of a skin adhesive layer according to the present invention. Fig.
3 is a cross-sectional view of a layered structure of a viscous cosmetic mask sheet 2 according to another embodiment of the present invention.

본 발명의 구체적 특징 및 이점들은 이하에서 첨부도면을 참조하여 상세히 설명한다. 이에 앞서 본 발명에 관련된 기능 및 그 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 구체적인 설명을 생략하기로 한다.Specific features and advantages of the present invention will be described in detail below with reference to the accompanying drawings. The detailed description of the functions and configurations of the present invention will be omitted if it is determined that the gist of the present invention may be unnecessarily blurred.

본 발명은 점착성 미용 마스크 시트에 관한 것으로서, 보다 상세하게는 피부에 점착고정되어 움직임의 제한을 받지 않고, 세척하여 반영구적으로 사용할 수 있으며, 건식으로 화장료 제제가 흐르는 불편함이 없는 점착성 미용 마스크 시트에 관한 것이다. More particularly, the present invention relates to a viscous cosmetic mask sheet which can be used semi-permanently without being restricted by movement, and can be used semi-permanently, .

도 1은 본 발명에 따른 점착성 미용 마스크 시트(1)의 적층구조의 일 실시예를 보여준다. 1 shows an embodiment of a laminated structure of a sticky cosmetic mask sheet 1 according to the present invention.

본 발명의 점착성 미용 마스크 시트(1, 이하, 마스크 시트로 축약함)는 열전도 실리콘 조성물로 형성되는 표면층(400)과 이미지 인쇄물 또는 레이스를 포함하는 디자인 형성층(300)과 트리코트 방법으로 형성된 메쉬 구조를 갖는 지지층(200)과 피부 점착 조성물로 형성되어 피부에 점착고정되는 피부 점착층(100)이 순차적으로 적층된다. The viscous cosmetic mask sheet 1 (abbreviated as mask sheet hereinafter) of the present invention comprises a surface layer 400 formed of a heat conductive silicone composition, a design forming layer 300 including an image print or a lace, and a mesh structure And a skin adhesive layer 100 formed of a skin adhesive composition and fixed to the skin are sequentially laminated.

표면층(400)은 열전도성 실리콘 조성물을 이용하여 제조된 시트 상의 층으로서, 외부로부터 받아들인 열을 마스크 시트의 내부 및 피부에 전달하는 역할을 수행한다.The surface layer 400 is a layer on a sheet made of a thermally conductive silicone composition and serves to transfer the heat received from the outside to the inside of the mask sheet and the skin.

이때, 외부 열은 스팀 타올, 스팀 공급기, 온풍 수단, 손 마찰에 의한 열 등을 통하여 공급될 수 있다.At this time, the external heat may be supplied through a steam towel, a steam feeder, a hot air means, heat by hand friction, or the like.

제 1실시예에 따른 열전도성 실리콘 조성물은 폴리오르가노실록산과 실리카, 실란 커플링제, 열전도성 필러, 촉매 등을 포함하여 제조된다.The thermally conductive silicone composition according to the first embodiment is prepared by including a polyorganosiloxane and silica, a silane coupling agent, a thermally conductive filler, a catalyst and the like.

제 2실시예에 따른 열전도성 실리콘 조성물은 상기 제 1실시예에 따른 열전도성 실리콘 조성물을 베이스로 하여 상기 열전도성 실리콘 베이스 100중량부에 대하여, 토르말린과 은을 이용하여 제조된 토르말린 펠렛을 10 내지 25 중량부 포함하여 열전도성을 향상시키고, 토르말린이 갖는 음이온 및 원적외선 발산 기능을 부가할 수 있게 된다.The thermally conductive silicone composition according to the second embodiment is prepared by using the thermally conductive silicone composition according to the first embodiment as a base and adding 10 to 30 parts by weight of the tourmaline pellet prepared using tourmaline and silver to 100 parts by weight of the thermally conductive silicone base. 25 parts by weight can be added to improve the thermal conductivity and add the anion and far-infrared ray diverging function of tourmaline.

토르말린은 전기 분극을 가져 자기장을 인가할 경우 특정 방향으로 배열될 수 있는 특징을 가지며, 은(silver)는 높은 열전도도를 가지며, 항균 특성이 우수하다. Tourmaline has characteristics that it can be arranged in a certain direction when applying a magnetic field due to electric polarization, and silver has high thermal conductivity and excellent antibacterial property.

상기 토르말린 펠렛은 토르말린과 은을 50 내지 200nm의 평균 입경으로 분말화한 후 토르말린과 은을 2~1: 1의 중량비로 혼합한 후 이를 펠렛 형상으로 소성 성형시켜 제조된다. The tourmaline pellet is prepared by powdering tourmaline and silver at an average particle size of 50 to 200 nm, mixing tourmaline and silver at a weight ratio of 2 to 1: 1, and calcining the mixture in a pellet form.

상기 토르말린 펠렛은 1500 내지 5000nm 의 평균입경을 갖는 입상을 갖는 것을 사용하거나, 기둥형 및 긴 형상을 갖는 것을 사용할 수 있는데, 보다 바람직하게는, 길이 방향과 폭 방향의 길이비가 1.5 내지 3:1을 갖는 긴 형상을 갖는 것을 사용한다. The tourmaline pellet may have a granular shape having an average particle diameter of 1500 to 5000 nm, or may have a columnar shape and a long shape. More preferably, the length ratio of the tourmaline pellet is 1.5 to 3: 1 Having a long shape is used.

보다 상세하게는, 표면층(400)은 긴 형상을 갖는 토르말린 펠렛을 수직으로 배열시켜 외부의 열을 피부로 더욱 효과적으로 전달시킬 수 있게 된다.More specifically, the surface layer 400 may vertically arrange the long-shaped tourmaline pellets so as to more effectively transfer the external heat to the skin.

제 2실시예에 따른 표면층(400)은 상기 열전도성 실리콘 베이스에 긴 형상을 갖는 토르말린 펠렛을 혼합 및 분산시킨 후 제 2실시예에 따른 열전도성 실리콘 조성물의 제조한 후, 박판에 제 2실시예에 따른 열전도 실리콘 조성물을 도포한 후 건조되기 전 상기 박판의 하부에 0.05 내지 3kG의 자기장을 인가하여 제 2실시예에 따른 열전도성 실리콘 조성물 내부에 긴 형상을 갖는 토르말린 펠렛을 수직으로 배열시키게 된다.The surface layer 400 according to the second embodiment is obtained by mixing and dispersing the long-form tourmaline pellets in the thermally conductive silicone base, preparing the thermally conductive silicone composition according to the second embodiment, , A magnetic field of 0.05 to 3 kG is applied to the lower portion of the thin plate to form a long-shaped tourmaline pellet vertically in the thermally conductive silicone composition according to the second embodiment.

상기 토르말린 펠렛은 상기 열전도성 실리콘 베이스에 투입하기에 앞서, 150 내지 700℃에서 가열처리하는 것이 바람직한데, 가열처리공정을 거침으로써 토르말린 펠렛의 양단이 대전 특성이 더욱 강해져 자기장 인가시 수직 배열성이 더욱 우수하게 된다. It is preferable that the tourmaline pellet is heated at 150 to 700 ° C prior to the introduction into the thermally conductive silicon base. By subjecting the tourmaline pellet to a heat treatment process, both ends of the tourmaline pellet become more strongly charged, And more excellent.

디자인 형성층(300)은 마스크 시트(1)에 디자인적 요소를 부가함과 동시에 내구성을 향상시키기 위한 층으로서, 이미지 인쇄물 또는 레이스를 포함할 수 있다. The design forming layer 300 may include an image print or a lace as a layer for enhancing durability while adding a design element to the mask sheet 1.

상기 이미지 인쇄물은 고분자 수지, 종이, 펄프, 부직포, 직물 등의 베이스 기재에 캐릭터, 동물, 식물, 기하학 패턴, 사진 등의 이미지를 인쇄하여 형성되며, 상기 이미지는 잉크를 이용하여 베이스 기재에 인쇄될 수 있다.The image print is formed by printing an image such as a character, an animal, a plant, a geometric pattern, or a photograph on a base substrate such as a polymer resin, a paper, a pulp, a nonwoven fabric or a fabric, .

상기 고분자 수지는 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리에스테르(PS), 나일론, 폴리프로필렌(PP), 방향성 폴리프로필렌(Oriented Poly Propylene, OPP), 캐스팅 폴리프로필렌(casting poly propylene CPP), 고밀도 폴리에틸렌(High Density Polyethylene, HDPE), 저밀도 폴리레틸렌(Low Density Polyethylene, LDPE), 선형저밀도 폴리에틸렌(Linear Low Density Polyethylene, LLDPE), 폴리비닐클로라이드, 폴리아크릴로니트릴, 폴리우레탄으로 이루어진 그룹으로부터 선택될 수 있다.The polymer resin may be selected from the group consisting of polyethylene terephthalate (PET), polyethylene (PE), polyester (PS), nylon, polypropylene (PP), aromatic polypropylene (OPP), casting polypropylene (HDPE), Low Density Polyethylene (LDPE), Linear Low Density Polyethylene (LLDPE), polyvinyl chloride, polyacrylonitrile, and polyurethane. Can be selected.

보다 바람직하게는, 베이스 기재로서 상기 고분자 수지를 전기 방사하여 제조된 나노섬유에 이미지를 인쇄하여, 이미지의 선명도를 향상시킬 수 있다. More preferably, the image can be printed on the nanofibers produced by electrospinning the polymer resin as the base substrate, thereby improving the sharpness of the image.

지지층(200)은 마스크 시트(1)에 내구성을 부여하여 찢어짐을 방지함과 동시에 신축성을 부여하여 상기 마스크 시트의 부착 및 탈착시 용이함 및 피부 적용시 리프팅 효과를 부여할 수 있다.The support layer 200 imparts durability to the mask sheet 1 to prevent tearing, and at the same time provides elasticity to facilitate attachment and detachment of the mask sheet and lifting effect when applying the skin.

상기 지지층(200)은 내구성 및 신축성을 부여하는 재질 및 방법이라면 한정하지 않지만, 구체적인 예로는 편성이 있을 수 있다. The supporting layer 200 is not limited as long as it is a material and a method for imparting durability and stretchability, but specific examples thereof may be combinations.

편성은 실섬유로 편환을 만들어 편환과 편환을 연결하여 원단을 제조하는 방법으로서, 크게 경방향으로 루프와 루프가 연결된 경편과 위방향으로 루프와 루프가 연결된 위편으로 분류된다. 편성으로 제조된 원단은 다른 방법에 비해 보다 신축성 및 유연성을 부여할 수 있다.Knitting is a method of manufacturing a fabric by connecting a circular and a circular ring by making a circular ring with thread fibers, and it is classified into a thread piece connected with a loop and a loop in a radial direction and an upper piece connected with a loop and a loop in an upward direction. Fabrics made by knitting can give more elasticity and flexibility than other methods.

편성을 통한 구체적인 조직 형성 방법은 트리코트(Tricot), 랏셀(Rachel), 말라네즈(Milanese), 자카드, 평편(Plain Stitch), 펄편(Purl Stritch), 고무편(Rib Stitch), 파일편(Pile Stitch), 테리편(Knitted Stitch), 터크편(Tuck Stitch) 등이 있다.Specific tissue formation methods through knitting include Tricot, Rachel, Milanese, Jacquard, Plain Stitch, Purl Stritch, Rib Stitch, Pile Stitch, Knitted Stitch, and Tuck Stitch.

보다 바람직하게는, 트리코트 방법을 사용할 수 있는데, 트리코트(Tricot)는 경편의 일종으로 실을 안내하는 가이드 바가 셋으로 이루어진 경편기를 이용하여 편성한 것으로서, 섬세하고 치밀한 조직 형성이 가능하면서 신축성을 갖기 때문에 본 발명의 마스크 시트의 부착 및 탈착시 얼굴 형상 및 굴곡에 따라 용이하게 신장 및 수축이 가능하다.More preferably, the tricot method can be used. Tricot is a kind of warp knitting yarn, which is knitted using a warp knitting machine consisting of three guide bars for guiding yarn, and it is possible to form a delicate and dense structure, It is possible to easily stretch and shrink the mask sheet according to the shape and the shape of the face when attaching and detaching the mask sheet of the present invention.

상기 지지층(200)의 재질은 셀룰로오스, 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리에스테르(PS), 나일론, 폴리프로필렌(PP), 방향성 폴리프로필렌(Oriented Poly Propylene, OPP), 캐스팅 폴리프로필렌(casting poly propylene CPP), 고밀도 폴리에틸렌(High Density Polyethylene, HDPE), 저밀도 폴리레틸렌(Low Density Polyethylene, LDPE), 선형저밀도 폴리에틸렌(Linear Low Density Polyethylene, LLDPE), 폴리비닐클로라이드, 폴리아크릴로니트릴, 폴리우레탄으로 이루어진 그룹으로부터 선택될 수 있다.The material of the support layer 200 may be selected from the group consisting of cellulose, polyethylene terephthalate (PET), polyethylene (PE), polyester (PS), nylon, polypropylene (PP), Oriented Polypropylene casting polypropylene CPP, high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), polyvinyl chloride, polyacrylonitrile, &Lt; / RTI > polyurethane.

상기 지지층(200)의 섬도는 3 내지 20 데니어(denier)이고, 메쉬 크기는 20 내지 100 mesh 인 것이 바람직한데, 섬도가 3 데니어 미만이면, 내구성이 저하되고, 20데니어를 초과하는 경우 유연성이 저하되고, 마스크 시트(1)의 두께가 두껍게 형성되기 때문에 사용시 답답함을 초래할 수 있다.The support layer 200 preferably has a fineness of 3 to 20 denier and a mesh size of 20 to 100 mesh. When the fineness is less than 3 denier, the durability is degraded. When the fineness is more than 20 denier, And the thickness of the mask sheet 1 is formed to be thick, so that it may cause difficulty in use.

또한, 메쉬 크기가 20 mesh 미만이면 내구성이 저하되고, 피부 리프팅 효과를 부여하기 힘들며, 100 mesh를 초과하면 너무 촘촘하게 형성되어 신축성 부여 효과가 미미하고, 불충분한 신축성으로 인하여 피부 적용시 답답함을 유발할 수 있다.In addition, if the mesh size is less than 20 mesh, durability is lowered, skin lifting effect is hardly given, and when it is more than 100 mesh, the effect of imparting elasticity is insignificant and insufficient elasticity may cause stiffness have.

이때, 상기 디자인 형성층(300)과 상기 지지층(200)은 열 압착되어 형성되며, 열 압착시 온도와 압력은 상기 디자인 형성층과 상기 지지층의 재질에 따라 설계될 수 있다. At this time, the design forming layer 300 and the supporting layer 200 are formed by thermocompression, and the temperature and pressure during the thermocompression bonding may be designed according to the material of the design forming layer and the supporting layer.

상기 열 압착 조건은 1 내지 20 kgf/㎠, 온도 80 내지 250℃에서 3초 내지 20초간 수행될 수 있다. The thermo-compression bonding conditions may be 1 to 20 kgf / cm 2 and a temperature of 80 to 250 ° C for 3 seconds to 20 seconds.

열 압착성을 더욱 향상시키기 위하여서는, 상기 디자인 형성층(300)과 상기 지지층(200)을 동일한 재질로 형성하거나, 동일한 특성을 갖는 것을 사용한다.In order to further improve the thermal compression property, the design forming layer 300 and the supporting layer 200 are formed of the same material or have the same characteristics.

예를 들어, 상기 디자인 형성층의 재질이 소수성을 가지면, 상기 지지층 또한 소수성을 갖는 재질로 형성됨으로써 열 압착시 서로 간의 상호 친화성을 가져 열 압착 효과를 더욱 향상시킬 수 있다.For example, if the material of the design forming layer is hydrophobic, the supporting layer is also formed of a material having hydrophobicity, so that mutual affinity between the materials can be improved during thermocompression, thereby further improving the thermocompression effect.

피부 점착층(100)은 피부 점착 조성물로 형성되어 사용시 피부에 점착 고정시키고, 물을 이용하여 세척 가능한 재질로 형성되어 반영구적으로 사용할 수 있게 한다.The skin adhesive layer 100 is formed of a skin adhesive composition, is fixed to the skin during use, and is made of a washable material using water, so that it can be used semi-permanently.

제 1실시예에 따른 피부 점착 조성물은 폴리우레탄 수지, 아크릴 수지, 천연고무 수지, 합성고무 수지, 실리콘 수지 및 이들의 조합으로 이루어지는 베이스 수지 중 어느 하나를 사용할 수 있으며, 유기용매 및 첨가제를 더 포함하여 제조될 수 있다. The skin adhesive composition according to the first embodiment can use any one of a polyurethane resin, an acrylic resin, a natural rubber resin, a synthetic rubber resin, a silicone resin, and a base resin composed of a combination of these, and further includes an organic solvent and an additive .

보다 바람직하게는, 상기 베이스 수지는 PSA(Pressure Sensitive Adhesive)용 실리콘 수지, PSA(Pressure Sensitive Adhesive)용 아크릴계 수지 및 이들의 조합 중 어느 하나일 수 있다. More preferably, the base resin may be any one of a silicone resin for PSA (Pressure Sensitive Adhesive), an acrylic resin for PSA (Pressure Sensitive Adhesive), and a combination thereof.

유기용매로는 예를 들면, 디클로로메탄, 디메틸 포름아미드, 디메틸설폭시드, 디메틸아세트아미드, 메틸에틸케톤, 클로로포름, 아세톤, 물, 포름산, 아세트산, 부틸 아세테이트, 시클로헥산, THF 및 이들의 조합으로 이루어지는 용매를 사용할 수 있으나 이에 한정하는 것은 아니다.Examples of the organic solvent include organic solvents such as dichloromethane, dimethylformamide, dimethylsulfoxide, dimethylacetamide, methylethylketone, chloroform, acetone, water, formic acid, acetic acid, butyl acetate, cyclohexane, THF, Solvents may be used, but are not limited thereto.

첨가제로는 경화제, 노화방지제, 소포제, 증점제, 레벨링제, 대전방지제 및 이들의 조합 중 어느 하나의 더 포함하여 제조될 수 있으며, 이에 한정하지 않는다.The additive may be manufactured by including, but not limited to, a curing agent, an antioxidant, a defoaming agent, a thickener, a leveling agent, an antistatic agent, and a combination thereof.

제 2실시예에 따른 피부 점착 조성물은 상기 제 1실시예에 따른 피부 점착 조성물을 베이스로 하여, 상기 베이스 100중량부에 대하여 아로마 캡슐 조성물을 0.5 내지 3중량부 더 포함하여 피부 적용시 아로마 테라피 효과를 발현시킬 수 있다. The skin adhesive composition according to the second embodiment, based on the skin adhesive composition according to the first embodiment, further comprises 0.5 to 3 parts by weight of an aromatic capsule composition based on 100 parts by weight of the base to provide an aromatherapy effect Can be expressed.

상기 아로마 캡슐 조성물은 천연 식물 오일이 젤라틴 및 실리카 담체에 담지된 것으로서, 평균 입도 10 내지 100 ㎛ 를 갖는 것을 사용할 수 있다. 상기 천연 식물 오일은 카모마일 오일, 올리브유, 라벤더에센셜 오일, 아보카도유, 동백유, 아몬드유, 포도씨유, 마카다미아 오일, 로즈힙 오일, 일랑일랑 오일, 티트리 오일, 로즈마리 오일, 레몬오일, 자몽오일 및 이들의 조합 중 어느 하나를 포함할 수 있으나, 아로마 테라피 효과를 발현할 수 있는 것이라면 이에 한정하지 않는다.The above-mentioned aromatic capsule composition may be a natural plant oil supported on gelatin and a silica carrier and having an average particle size of 10 to 100 mu m. The natural plant oils are selected from the group consisting of chamomile oil, olive oil, lavender essential oil, avocado oil, camellia oil, almond oil, grape seed oil, macadamia oil, rosehip oil, ylang ylang oil, tea tree oil, rosemary oil, lemon oil, And combinations thereof, but it is not limited thereto as long as it can manifest the aromatherapy effect.

제 3실시예에 따른 피부 점착 조성물은 상기 제 1실시예 또는 상기 제 2실시예에 따른 피부 점착 조성물을 베이스로 하여, 상기 베이스 100중량부에 대하여 상술된 토르말린 펠렛을 5 내지 30중량부 더 포함할 수 있다. The skin adhesive composition according to the third embodiment further comprises 5 to 30 parts by weight of the tourmaline pellet described above relative to 100 parts by weight of the base on the basis of the skin adhesive composition according to the first or second embodiment can do.

제 4실시예에 따른 피부 점착 조성물은 폴리우레탄 수지, 아크릴 수지, 천연고무 수지, 합성고무 수지, 실리콘 수지 및 이들의 조합으로 이루어지는 베이스 수지 100중량부에 대하여, 아로마 캡슐 조성물 0.3 내지 3중량부, 토르말린 펠렛 5 내지 30중량부, 광물 나노 입자 5 내지 10중량부를 혼합하여 제조될 수 있다.The skin adhesive composition according to the fourth embodiment is prepared by mixing 0.3 to 3 parts by weight of an aromatic capsule composition with 100 parts by weight of a base resin comprising a polyurethane resin, an acrylic resin, a natural rubber resin, a synthetic rubber resin, a silicone resin, 5 to 30 parts by weight of tourmaline pellets, and 5 to 10 parts by weight of mineral nanoparticles.

상기 광물 나노 입자는 100 내지 500nm의 크기로 나노화된 스코리아, 게르마늄, 맥반석, 벤토나이트, 일라이트 및 이들의 조합으로 이루어지는 나노화 광물을 피톤치드 조성물로 코팅 처리하여 제조될 수 있다.The mineral nanoparticles may be prepared by coating nanoparticles of nano-sized scoria, germanium, elvanite, bentonite, ilite, and combinations thereof with a phytoncide composition to a size of 100 to 500 nm.

상기 피톤치드 조성물은 증류수 100중량부에 대하여, 피톤치드 원액 5 내지 20 중량부와 5 내지 50nm의 평균입도를 갖는 나노 숯분말 0.5 내지 10중량부를 150 내지 300rpm에서 5분 내지 20분간 교반하여 제조된다. 상기 피톤치드 조성물은 피톤치드 원액 및 나노 숯 분말의 첨가량을 달리하여, 1.5 내지 10 cP (20℃ 기준)를 갖는 제 1피톤치드 조성물과 15 내지 25 cP를 갖는 제 2피톤치드 조성물로 준비될 수 있다.The phytoncide composition is prepared by stirring 5 to 20 parts by weight of a phytoncide stock solution and 0.5 to 10 parts by weight of nano charcoal powder having an average particle size of 5 to 50 nm at 150 to 300 rpm for 5 to 20 minutes with respect to 100 parts by weight of distilled water. The phytoncide composition may be prepared with a first phytoncide composition having a concentration of 1.5 to 10 cP (based on 20 ° C) and a second phytonchide composition having 15 to 25 cP, the amounts of the phytoncide stock solution and the nanoconchar powder being different.

상기 광물 나노 입자는 제1피톤치드 조성물 100 중량부에 대하여, 나노화 광물을 30 내지 60 중량부 첨가하여, 상기 나노화 광물의 공극에 제 1피톤치드 조성물을 흡수시키는 제 1혼합단계와 상기 제 1피톤치드 조성물이 흡수된 나노화 광물을 50 내지 120℃에서 30분 내지 5시간 건조시키는 제 1건조단계와 제 2피톤치드 조성물 100중량부에 대하여, 제 1건조단계에 의해 건조된 나노화 광물을 30 내지 60중량부 첨가하여, 제 2피톤치드 조성물을 흡수시키는 제 2혼합단계 및 상기 제 2피톤치드 조성물을 흡수된 나노화 광물을 80 내지 150 에서 30분 내지 5시간 건조시키는 제 2건조단계를 포함하여 제조된다.Wherein the mineral nanoparticles comprise a first mixing step of adding 30 to 60 parts by weight of a nanoparticle mineral to 100 parts by weight of the first phytoncide composition to absorb the first phytoncide composition into the pores of the nanoparticle mineral, 30 to 60 parts by weight of the nano-mineralized material dried by the first drying step is added to 100 parts by weight of the second phytoncide composition by drying the absorbed nanoparticles at 50 to 120 DEG C for 30 minutes to 5 hours , A second mixing step of absorbing the second phytoncide composition, and a second drying step of drying the absorbed nanoparticles at 80 to 150 for 30 minutes to 5 hours.

상기와 같이, 1차로 저점도의 피톤치드 조성물을 이용함으로써 나노화 광물의 공극에 원활하게 침투될 수 있도록 하고, 2차로 고점도의 피톤치드 조성물을 이용함으로써 1차에서 흡수 및 고정된 피톤치드 조성물이 용출되지 않도록 하고, 보다 고정력 및 코팅력을 향상시킬 수 있게 된다.As described above, by using the first low-viscosity phytoncide composition, it is possible to smoothly penetrate the pores of the nano-minerals, and by using the second high-viscosity phytoncide composition, the first-order absorbed and fixed phytoncide composition is prevented from being eluted , The fixing force and the coating force can be more improved.

이때, 제 3실시예에 따른 피부 점착 조성물 및 제 4실시예에 따른 피부 점착 조성물을 이용하여 피부 점착층을 형성할 경우, 토르말린 펠렛을 수평으로 배열시켜, 외부 및 상기 표면층으로부터 전달된 열이 피부 점착층의 면 방향을 따라 균일하게 분산될 수 있도록 한다.At this time, when the skin adhesive layer is formed using the skin adhesive composition according to the third embodiment and the skin adhesive composition according to the fourth embodiment, the tourmaline pellets are arranged horizontally, So that they can be uniformly dispersed along the surface direction of the adhesive layer.

이로써, 상기 열에 의해 토르말린, 광물이 갖는 원적외선 방사능 및 음이온발생을 촉진하고, 피톤치드가 갖는 항균성, 면역력 개선 및 아로마 테라피 효과가 극대화될 수 있게 된다.As a result, it is possible to promote far-infrared radiation activity and anion generation of tourmaline and minerals by the heat, thereby maximizing antimicrobial activity, immunity and aromatherapy effect of phytoncide.

제 3실시예에 따른 피부 점착 조성물 및 제 4실시예에 따른 피부 점착 조성물에 의해 제조되는 피부 점착층 내에서 토르말린 펠렛을 수평으로 배열시키는 방법은 박판 또는 지지층의 상부에 제 3실시예에 따른 피부 점착 조성물 및 제 4실시예에 따른 피부 점착 조성물을 도포한 후, 완전히 건조되기 전 롤러 및 압착 장치를 이용하여 상부에 압력을 가하거나 측면에서 0.5 내지 10kG의 자기장을 인가하여 상기 피부 점착 조성물 내부의 토르말린 펠렛을 수평으로 배열하는 방법을 사용할 수 있다.The method of horizontally arranging the tourmaline pellets in the skin adhesive layer produced by the skin adhesive composition according to the third embodiment and the skin adhesive composition according to the fourth embodiment is the same as the method according to the third embodiment, After applying the adhesive composition and the skin adhesive composition according to the fourth embodiment, a pressure is applied to the upper part using a roller and a compression device before being completely dried, or a magnetic field of 0.5 to 10 kG is applied on the side, A method of horizontally arranging the tourmaline pellets can be used.

이로써, 상기 표면층은 수직으로 배열된 토르말린 펠렛을 포함하여 외부로부터 전달된 열을 효율적으로 집중적으로 내부로 전달하고, 상기 피부 점착층은 수평으로 배열된 토르말린 펠렛을 포함하여 열을 보다 효율적으로 분산시킴과 동시에 상기 피부 점착 조성물이 갖는 음이온 및 원적외선 발산 효과, 피톤치드 발산 효과를 극대화할 수 있게 되는 것이다.As a result, the surface layer includes the vertically arranged tourmaline pellets to efficiently and intensively transfer the heat transmitted from the outside, and the skin adhesive layer includes the horizontally arranged tourmaline pellets to more efficiently disperse the heat And at the same time, the anionic and far-infrared radiation effect and the phytoncide dissipation effect of the skin adhesive composition can be maximized.

본 발명은 따른 피부 점착층의 형성을 위한 실시예로서, 점착성을 얼굴 영역에 따라 다르게 형성하여 리프팅 효과를 극대화하는 것도 가능하다.As an embodiment for forming a skin adhesive layer according to the present invention, it is also possible to maximize the lifting effect by forming adhesiveness differently depending on the face region.

예를 들어, 마스크의 형태가 얼굴 형상으로 형성될 경우, 주름이 많이 발생하는 부위인 팔자 주름부, 눈가 주름부, 미간, 이마 영역 등의 주변부의 점착성을 나머지 영역보다 더욱 높게 형성하여 리프팅 효과를 향상시킬 수 있다.For example, when the shape of the mask is formed into a face shape, the peripheral portions such as the wrinkles, the wrinkles, the eyes, and the forehead regions of the wrinkles are formed to have a higher tackiness than the remaining regions. Can be improved.

도 2에 도시된 바와 같이, 팔자 주름부 영역(A)에는 피부 점착력을 0 내지 1.2 kgf/25mm 로 형성하고, 팔자 주름부의 주변부 영역(B)에는 1.2 kgf/25m를 초과하게 형성하여, 팔자 주름부의 주변부의 점착력으로 팔자 주름부를 리프팅할 수 있게 된다. As shown in Fig. 2, the skin adhesion force is formed to be in the range of 0 to 1.2 kgf / 25 mm in the wrinkle crease region A and in the peripheral region B of the wrinkle crease portion in excess of 1.2 kgf / 25 m, The wrinkle portion can be lifted by the adhesive force of the peripheral portion of the portion.

이를 위해 최소 팔자 주름부를 기준으로 좌측(B')과 우측(B") 방향, 즉 대응되는 두 지점에서 주름을 당길 수 있도록 높은 점착력을 형성하는 것이 바람직할 것이다.For this purpose, it is desirable to form a high adhesive force so that the wrinkles can be pulled in the left side (B ') and the right side (B') direction, that is, at the corresponding two points based on the minimum wrinkle portion.

본 발명에 따른 점착성 미용 마스크 시트는 표면층, 디자인 형성층, 지지층 및 표면층 각각을 별도로 제조한 후 최종적으로 접착제 및 열압착을 통하여 적층 처리하거나, 표면층을 먼저 형성하고, 상기 표면층 위에 디자인 형성층, 지지층 및 표면층을 순차적으로 형성해나가며 적층하는 것도 가능하다. The viscous cosmetic mask sheet according to the present invention can be produced by separately preparing a surface layer, a design forming layer, a support layer and a surface layer, and finally laminating them through an adhesive and thermocompression bonding or by forming a surface layer first, It is also possible to laminate them sequentially.

열압착을 통한 접합시, 15 내지 35 kgf/㎠, 온도 80 내지 250℃ 하에서 3초 내지 10초간 수행될 수 있다. At the time of joining through thermocompression, 15 to 35 kgf / cm 2, at a temperature of 80 to 250 ° C for 3 seconds to 10 seconds.

본 발명에 따른 점착성 미용 마스크 시트의 피부 점착층은 1 내지 5mm의 두께로 형성되며, 지지층과 디자인 형성층은 각각 0.1 내지 0.5mm로 형성되며, 표면층의 두께는 3 내지 8mm로 형성될 수 있으나, 이에 한정하는 것은 아니다. The skin adhesive layer of the viscous cosmetic mask sheet according to the present invention is formed to a thickness of 1 to 5 mm and the support layer and the design forming layer are each formed to be 0.1 to 0.5 mm and the thickness of the surface layer is 3 to 8 mm, But is not limited to.

도 3은 본 발명에 따른 점착성 미용 마스크 시트(2)의 적층구조의 다른 실시예를 보여준다. Fig. 3 shows another embodiment of the laminated structure of the viscous cosmetic mask sheet 2 according to the present invention.

본 발명의 점착성 미용 마스크 시트(2)는 열전도 실리콘 조성물로 형성되는 표면층(400)과 이미지 인쇄물 또는 레이스를 포함하는 디자인 형성층(300)과 표면층보다 경도가 낮은 열전도성 실리콘 조성물로 형성되는 중간층(250)과 트리코트 방법으로 형성된 메쉬 구조를 갖는 지지층(200)과 피부 점착 조성물로 형성되어 피부에 점착고정되는 피부 점착층(100)이 순차적으로 적층된다. The viscous cosmetic mask sheet 2 of the present invention comprises a surface layer 400 formed from a thermally conductive silicone composition, a design forming layer 300 comprising an image print or a lace and an intermediate layer 250 formed from a thermally conductive silicone composition having a lower hardness than the surface layer A support layer 200 having a mesh structure formed by a tricot method and a skin adhesive layer 100 formed of a skin adhesive composition and fixed to the skin are sequentially laminated.

본 발명의 점착성 미용 마스크 시트(2)는 상기 디자인 형성층(300)과 상기 지지층(200)을 열접합하지 않고, 상기 디자인 형성층(300)과 상기 지지층(200) 사이에 열전도성 실리콘 조성물로 형성되는 중간층을 더 포함하여, 상기 디자인 형성층과 상기 지지층이 마스크 시트(2) 내에서 안정적으로 적층될 수 있도록 하며, 디자인 형성층과 지지층이 이격시켜 입체감을 더욱 향상시킬 수 있다. The viscous cosmetic mask sheet 2 of the present invention is formed by thermally bonding the design forming layer 300 and the supporting layer 200 to each other without thermally bonding the supporting layer 200 with the thermally conductive silicone composition between the design forming layer 300 and the supporting layer 200 Forming layer and the support layer can be stably stacked in the mask sheet 2, and the design-forming layer and the support layer are separated from each other, thereby further enhancing the three-dimensional effect.

이때, 상기 중간층(250)은 표면층(400)보다 경도가 낮은 열전도성 실리콘 조성물로 형성되거나, 두께를 1/3~1/2 정도로 얇게 형성하여 상기 중간층의 삽입에 의해 마스크 시트(2)의 유연성이 떨어지는 것을 방지할 수 있게 된다. At this time, the intermediate layer 250 may be formed of a thermoconductive silicone composition having a lower hardness than the surface layer 400, or may be formed to have a thickness of about 1/3 to 1/2 of the thickness of the intermediate layer 250 so that the flexibility of the mask sheet 2 It is possible to prevent the dropout from occurring.

또한, 상기 중간층(250)의 다른 실시예로서, 수직 배열된 토르말린 펠렛을 더 포함하여 상기 표면층(400)으로부터 전달받은 열을 상기 피부 점착층(100)으로 더욱 원활히 전달할 수 있도록 하는 것도 가능하다. 상기 중간층(250)에서 토르말린 펠렛을 수직배열시키기는 방법은 상술된 바와 동일한 바 생략하도록 한다.As another embodiment of the intermediate layer 250, it is possible to further transmit the heat transferred from the surface layer 400 to the skin adhesive layer 100 by further including vertically arranged tourmaline pellets. The method of vertically arranging the tourmaline pellets in the intermediate layer 250 is the same as described above.

1. 점착성 미용 마스크 시트의 제조1. Manufacture of adhesive cosmetic mask sheet

1-1. 표면층 형성1-1. Surface layer formation

열전도실리콘 Dow Corning SE4485 1000g에 토르말린 펠렛 150g을 첨가하여 150~200rpm으로 약 10분간 교반처리하였다.Heat transfer Silicone 150 g of tourmaline pellets were added to 1000 g of Dow Corning SE4485 and stirred at 150-200 rpm for about 10 minutes.

토르말린 펠렛은 약 100nm를 평균입경을 갖는 토르말린 분말과 은 분말을 3:2의 중량비로 혼합하여 고온에서 소성 및 성형처리하였으며, The tourmaline pellet was obtained by mixing and calcining tourmaline powder having a mean particle diameter of about 100 nm and silver powder at a weight ratio of 3: 2,

길이 방향의 길이가 약 2800nm, 폭 방향의 길이가 약 1500nm 을 갖는 토르말린 펠렛이 준비되었다. A tourmaline pellet having a length in the longitudinal direction of about 2800 nm and a length in the width direction of about 1500 nm was prepared.

박판에 토르말린 펠렛을 첨가한 열전도 실리콘이 건조되기 전에 약 3mm로 두께로 도포한 후 박판 하단에 3kG의 자기장을 인가하여 토르말린 펠렛을 수직으로 배열하였다.The thermally conductive silicone with the tourmaline pellet added to the thin plate was applied to a thickness of about 3 mm before drying and the tourmaline pellet was arranged vertically by applying a magnetic field of 3 kG to the bottom of the thin plate.

1-2. 디자인 형성층 및 지지층의 준비1-2. Preparation of Design Shapes and Support Layers

폴리에스테르 수지를 전계방사하여 제조된 베이스 메쉬망에 잉크로 캐릭터 형상을 인쇄하여 디자인 형성층을 준비하였다.A design forming layer was prepared by printing a character shape with ink on a base mesh net produced by electrospinning a polyester resin.

지지층은 섬도 20 데니어를 갖는 폴리에스테르 섬유사를 이용하여 트리코트 방법으로 제조되었다.The support layer was made by tricot method using polyester fiber yarn having a fineness of 20 denier.

제조된 디자인 형성층과 지지층을 8 kgf/㎠, 온도 120℃에서 5초간 열압착하였다.The prepared formed layer and the supporting layer were thermocompression bonded at 8 kgf / cm 2 and 120 ° C for 5 seconds.

1-3. 1-3. 피부점착층의Of the skin adhesive layer 준비 Ready

Dow Corning 의 7-9800 Soft Skin Adhesive Kit(Part A & B) 를 베이스 수지로 준비하고, 라벤더오일이 함유된 평균입도 80㎛의 아로마 캡슐 조성물을 준비하였다.A 7-9800 Soft Skin Adhesive Kit (Part A & B) from Dow Corning was prepared as a base resin and an aroma capsule composition with an average particle size of 80 μm containing lavender oil was prepared.

토르말린 펠렛은 상술된 바와 동일한 것을 사용하였으며, 피톤치드 조성물은 증류수 200g에 피톤치드 원액(순수아로마 사의 편백수) 20g, 평균입도 30nm의 나노 숯분말 10g 혼합하여 200rpm에서 10분간 교반처리하여 준비되었으며, 광물 나노입자는 약 300nm의 평균입도를 갖는 스코리아 분말을 피톤치드 조성물에 침지 후 약 80℃에서 1시간 건조시켜 준비되었다. The tourmaline pellet used was the same as that described above. The phytoncide composition was prepared by mixing 200 g of distilled water with 20 g of phytoncide stock solution (pure water of pure Aroma Co., Ltd.) and 10 g of nano charcoal powder having an average particle size of 30 nm and stirring at 200 rpm for 10 minutes. The particles were prepared by dipping a scoria powder having an average particle size of about 300 nm into the phononchide composition and drying at about 80 DEG C for one hour.

베이스 수지 1000g에 아로마 캡슐 10g, 토르말린 펠렛 50g, 광물 나노 입자 50g을 150rpm에서 10분간 교반처리하여 피부 점착 조성물을 준비하였다.10 g of the aromatic capsule, 50 g of the tourmaline pellet and 50 g of the mineral nanoparticles were stirred at 150 rpm for 10 minutes to prepare a skin adhesive composition.

박판에 상기 피부 점착 조성물을 약 10mm 두께로 도포한 후, 25℃에서 30분간 건조시킨 후 압착기를 이용하여 압착처리하여 토르말린 펠렛을 수평으로 배열시켰다.The skin adhesive composition was coated on the thin plate to a thickness of about 10 mm, and then dried at 25 DEG C for 30 minutes, followed by compression using a press to arrange the tourmaline pellets horizontally.

1-4. 적층1-4. Lamination

준비된 표면층, 디자인 형성층, 지지층 및 피부 점착층을 차례대로 적층하여 20 kgf/㎠, 110℃에서 5초간 열압착하였다.The prepared surface layer, the design forming layer, the supporting layer and the skin adhesive layer were laminated in order and thermocompression bonded at 20 kgf / cm 2 and 110 ° C for 5 seconds.

2. 열전도 특성의 비교2. Comparison of Thermal Conductivity

실시예 1)상기 1에 의해 제조된 점착성 미용 마스크 시트를 준비하였다. Example 1) The viscous cosmetic mask sheet prepared in the above-mentioned 1 was prepared.

실시예 2) 토르말린 펠렛을 별도 배열처리하지 않았으며, 나머지 조건은 실시예 1과 동일하게 실시하였다. Example 2) Tourmaline pellets were not treated separately, and the other conditions were the same as in Example 1. [

비교예 1) 표면층으로 열전도실리콘 Dow Corning SE4485 을 시트상으로 제조하고, 디자인 형성층 및 지지층은 실시예 1과 동일하게 준비하였으며, 피부 점착층으로 Dow Corning 의 7-9800 Soft Skin Adhesive Kit(Part A & B)를 베이스 수지로 준비하였다. 각 층의 두께는 실시예 1과 동일하게 형성하였다.Comparative Example 1 A thermally conductive silicone Dow Corning SE4485 as a surface layer was prepared in the form of a sheet. The design forming layer and the support layer were prepared in the same manner as in Example 1. As the skin adhesive layer, Dow Corning's 7-9800 Soft Skin Adhesive Kit (Part A & B) was prepared as a base resin. The thickness of each layer was formed in the same manner as in Example 1.

열전도 특성을 비교하기 위하여, 표면층에 약 80 ℃의 스팀을 3분간 가한 후, 피부 점착층의 온도를 확인하였다.In order to compare the heat conduction characteristics, steam was applied to the surface layer at about 80 DEG C for 3 minutes, and then the temperature of the skin adhesive layer was confirmed.

표 1은 피부 점착층의 측정 온도를 보여준다.Table 1 shows the measurement temperature of the skin adhesive layer.

실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 피부 점착층의 온도The temperature of the skin adhesive layer 46℃46 ° C 41℃41 C 36℃36 ℃

실시예 1과 실시예 2 모두 비교예 1에 비하여 표면층의 온도가 높게 측정되었으며, 실시예 1의 경우, 실시예 2에 비하여 표면층의 온도가 더 높게 측정된 것을 보아, 이는 토르말린 펠렛을 배열에 방향성을 부여하여 상기 결과가 도출된 것으로 판단할 수 있었다.In both Example 1 and Example 2, the temperature of the surface layer was measured higher than that of Comparative Example 1, and in Example 1, the temperature of the surface layer was measured to be higher than that of Example 2, indicating that the tourmaline pellet was oriented It can be judged that the above result is derived.

또한, 실시예 1과 실시예 2의 부착성 테스트 결과 모두 피부에 견고하게 부착되었으며, 세척 후 사용시에도 동일한 부착성을 유지하였다.In addition, both of the adhesion test results of Example 1 and Example 2 were firmly attached to the skin, and the same adhesion was maintained even after washing.

본 발명에 따른 점착성 미용 마스크 시트에 의하면, 피부에 점착고정되어 움직임의 제한을 받지 않고, 세척하여 반영구적으로 사용할 수 있으며, 건식으로 화장료 제제가 흐르는 불편함이 없는 효과가 있다. The viscous cosmetic mask sheet according to the present invention has the effect of being free from the inconvenience that the cosmetic preparation flows in a dry manner without being restricted by movement, and can be used semi-permanently.

또한, 토르말린 펠렛이 방향성을 가지고 배열되어 외부 열을 내부로 피부 점착층으로 집중적으로 잘 전달함에 따라 피부 점착층의 음이온, 원적외선 발산 효과 및 피톤치드의 효과를 극대화할 수 있는 효과가 있다. In addition, since the tourmaline pellet is arranged with directionality to intensively transmit the external heat intensively to the skin adhesive layer, the effect of the anion, the far-infrared radiation and the phytoncide of the skin adhesive layer can be maximized.

본 발명에 따른 점착성 미용 마스크 시트는 피지제거 전 모공을 열어주기 위한 용도나 마사지 전 피부 혈액 순환을 위한 용도나 외출 중 리프팅이 필요할 때나 화장료 제제가 흘러내리지 않는 건식 마스크가 필요할 때 사용할 수 있으며, 이에 한정하지 않는다.The cosmetic beauty mask sheet according to the present invention can be used for the purpose of opening the pores before removing the sebum, the skin blood circulation before the massage, the dry mask requiring no lifting or lifting of the cosmetic agent, and the like Not limited.

이상과 같이 본 발명은 첨부된 도면을 참조하여 바람직한 실시예를 중심으로 설명하였지만 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 본 발명의 특허청구범위에 기재된 기술적 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 또는 변형하여 실시할 수 있다. 따라서 본 발명의 범주는 이러한 많은 변형의 예들을 포함하도록 기술된 청구범위에 의해서 해석되어야 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is clearly understood that the same is by way of illustration and example only and is not to be taken as limiting the scope of the present invention. The present invention can be variously modified or modified. The scope of the invention should, therefore, be construed in light of the claims set forth to cover many of such variations.

1, 2: 점착성 미용 마스크 시트
100 : 피부 점착층
200 : 지지층
300 : 디자인 형성층
400 : 표면층1, 2: Adhesive beauty mask sheet
100: skin adhesive layer
200: support layer
300: Design formation layer
400: surface layer

Claims

In a viscous cosmetic mask sheet excellent in external heat transfer and semi-permanently usable,
A surface layer formed of a thermally conductive silicone composition;
A design formation layer including an image print or a race;
A support layer having a mesh structure formed by a tricot method;
A skin adhesive layer formed of a skin adhesive composition and fixed to the skin and fixed to the skin;
Adhesive beauty mask sheet.

The method according to claim 1,
The surface layer
Characterized in that it comprises a vertically arranged tourmaline pellet
Adhesive beauty mask sheet.

The method according to claim 1,
The skin-
0.5 to 3 parts by weight of an aromatic capsule, 5 to 30 parts by weight of an aromatic capsule, 5 to 30 parts by weight of a tourmaline pellet, 100 parts by weight of a phthalic acid composition, And 5 to 10 parts by weight of the coated mineral nanoparticles.
Adhesive beauty mask sheet.

The method of claim 3,
The skin-
Characterized in that it comprises a horizontally arranged tourmaline pellet
Adhesive beauty mask sheet.

The method according to claim 1,
The design forming layer and the supporting layer
Characterized in that it is thermocompression bonded
Adhesive beauty mask sheet.

The method according to claim 1,
Between the design forming layer and the supporting layer
And an intermediate layer formed of a thermoconductive silicone composition having a hardness lower than that of the surface layer
Adhesive beauty mask sheet.