KR20190013039A - Manufacturing method of anti-wrinkle transparent solid paste - Google Patents

Manufacturing method of anti-wrinkle transparent solid paste Download PDF

Info

Publication number
KR20190013039A
KR20190013039A KR1020170096966A KR20170096966A KR20190013039A KR 20190013039 A KR20190013039 A KR 20190013039A KR 1020170096966 A KR1020170096966 A KR 1020170096966A KR 20170096966 A KR20170096966 A KR 20170096966A KR 20190013039 A KR20190013039 A KR 20190013039A
Authority
KR
South Korea
Prior art keywords
transparent solid
solid paste
weight
parts
added
Prior art date
Application number
KR1020170096966A
Other languages
Korean (ko)
Other versions
KR101946158B1 (en
Inventor
남명석
Original Assignee
주식회사 문교오엔에스
남명석
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 문교오엔에스, 남명석 filed Critical 주식회사 문교오엔에스
Priority to KR1020170096966A priority Critical patent/KR101946158B1/en
Publication of KR20190013039A publication Critical patent/KR20190013039A/en
Application granted granted Critical
Publication of KR101946158B1 publication Critical patent/KR101946158B1/en

Abstract

The present invention relates to a method for manufacturing anti-wrinkle transparent solid paste. The paste contains water and sucrose. Therefore, according to the method for manufacturing the anti-wrinkle transparent solid paste of the present invention, the anti-wrinkle transparent solid paste has excellent adhesion and storage properties, and wrinkles are barely made at a portion to which the solid paste is applied.

Description

주름이 방지되는 투명 고형풀 제조방법{Manufacturing method of anti-wrinkle transparent solid paste}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a transparent solid paste for wrinkle-

본 발명은 주름이 방지되는 투명 고형풀 제조방법에 관한 것으로, 더욱 상세하게는 물, 수크로즈(sucrose), 에탄올, 소포제, 표백제인 Longalite, 가성소다, 글리세린(Glycerin), 동결방지제인 Propylene Glycol, 계면활성제인 Polyoxyethylene Laureth, 고형화제인 Lauric Acid와 Sodium Steatate, 접착제인 PVP(poly vinyl pyrrolidone), 고형화제인 방부제, 살균제, 향을 포함하는 주름이 방지되는 투명 고형풀 제조방법에 관한 것이다.More particularly, the present invention relates to a method for producing a transparent solid paste in which wrinkles are prevented, and more particularly, to a method for producing a transparent solid paste which is free from wrinkles, The present invention relates to a method for producing a transparent solid paste which contains a surfactant Polyoxyethylene Laureth, a solidifying agent such as Lauric Acid and Sodium Steatate, an adhesive polyvinyl pyrrolidone (PVP), a preservative which is a solidifying agent, a disinfectant and fragrance.

일반적으로 문구용이나 사무용에 쓰는 풀은 옛날에는 곡물류를 원료로 한 녹말풀이 대부분이었으나, 오늘날에는 전분 풀에 향료나 방부제를 첨가하거나 화학적인 재료를 사용한 것 등 많은 종류(예컨대 녹말풀, 해조풀, 합성풀 등)가 있음은 이미 주지된 사실이다.Generally, grasses used for stationary or office use are mostly pasta grasses made from grains. Today, starch grasses have many kinds (for example, starch paste, seaweed grass, Synthetic pools, etc.) are already known.

그리고 액체풀의 사용에 따른 누액, 건조에 의한 출구 막힘 현상, 건조시 종이의 습윤 팽창 현상 등의 단점을 보완하기 위하여 고체 풀을 생산하기 시작하였고, 고체 풀은 시장에서 차지하는 비중이 70%이상 되며, 점차 수요가 증가하고 있는 추세이다.In order to compensate for the drawbacks of liquid leakage due to the use of liquid pool, clogging of the outlet due to drying, wet swelling of paper during drying, and so on, solid paste has begun to be produced, and the solid paste has more than 70% , And demand is gradually increasing.

그러나 고체 풀의 주성분인 PVP(poly vinyl pyrrolidone)는 세계적으로 몇몇 회사에서만 생산되고 있고, 국내 업체들은 이 원료를 수입하여 생산하다 보니 제품의 원가에서 풀 원료비(주성분인 PVP)가 차지하는 비율이 상당히 높아 업체에서는 인건비를 줄여 채산성을 고려할 형편에 이르러 가격과 수출경쟁에서도 뒤지는 양상을 보이고 있다.However, polyvinyl pyrrolidone (PVP), which is a main component of solid paste, is produced only in a few companies globally. Domestic companies are importing and producing these raw materials. As a result, the ratio of raw material cost (main component, PVP) In the case of companies, labor costs are reduced and profitability is taken into account.

상술한 경제적인 어려움을 해소하기 위하여, PVA(polyvinyl alcohol, 폴리비닐알콜)을 접착 성분으로 사용하기도 하였으나, PVA는 가격이 저렴하나 냄새가 좋지 않고 안정성이 떨어져 유통기한이 짧아진다는 단점이 있었다.PVA (polyvinyl alcohol) has been used as an adhesive component in order to solve the economic difficulties described above. However, PVA has a disadvantage that the price is low, the smell is not good, the stability is poor, and the shelf life is shortened.

또한, 상기 폴리비닐피롤리돈을 대체할 수 있는 다양한 재료들에 대한 연구가 진행되어왔지만 실질적으로 우수한 접착력을 보장하면서도 경제성, 보관성이 우수한 재료가 개발되지 못한 문제점이 있다.In addition, various materials capable of replacing the polyvinylpyrrolidone have been studied, but materials having excellent economical and storage properties can not be developed while ensuring excellent adhesive strength.

한편, 이와 같은 문제점을 해결하기 위해서 종래기술로서 등록특허공보 제10-0555226호에 PVAc와 PVP를 중량비 20:27로 혼합한 합성수지 접착제40∼50wt%, 전분(starch) 30∼40wt%, 수용성 접착제(methyl cellulose) 10∼20wt%의 비율로 혼합기에서 섞는 과정과, 보습제(glcerine)를 전체 중량의 1∼5wt% 첨가하는 과정과, 상기 총 시료와 동일한 양의 물을 첨가하는 과정과, 상기의 전체 혼합물을 60-70℃의 온도에서 2시간 정도 가열하는 중에 교반되도록 하는 과정과, 상기의 가열 온도를 유지시킨 상태에서 중합완료 30분 전에 에스테르(drying agent)를 접착시료 전 중량의 10wt%-15wt% 정도 중합 중인 접착제에 혼합하여(blending) 고형화하는 과정과, 혼화제(builder)로 점도 증가를 위해 광물인 wax(canderillia wax)도 천연에서 생산되는 고상 파우더를 사용하여 반응 온도인 60-70℃에서 전처리 후 접착제 시료의 축합 중합 마지막 단계에 5wt%-10wt% 반응 시간 종료 직전 혼화하는 과정과, 상기의 기열시간이 완료된 전체 시료를 상온에서 냉각하는 과정들에 의해 제조됨을 특징으로 하는 고체 풀의 제조방법이 기재되어 있다.In order to solve such problems, Patent Document 10-0555226 discloses that 40 to 50 wt% of a synthetic resin adhesive in which PVAc and PVP are mixed at a weight ratio of 20:27, 30 to 40 wt% of a starch, (methyl cellulose) in a mixer at a ratio of 10 to 20 wt%, adding glutenine to 1 wt% to 5 wt% of the total weight, adding the same amount of water as the total sample, And stirring the entire mixture at 60-70 ° C for 2 hours. In the state where the heating temperature is maintained, a drying agent is added at a concentration of 10 wt% The wax (canderillia wax), which is a mineral for the purpose of increasing the viscosity with a builder, is prepared by mixing the binder in a polymerization state of about 15 wt% After pre-treatment in A step of blending the adhesive sample immediately before the end of the reaction time of 5 wt% to 10 wt% at the final stage of the condensation polymerization, and a step of cooling the entire sample at the room temperature, .

또한, 등록특허공보 등록번호 제10-1650668호에 기재된 바에 의하면, 플라스크에 이온교환수와 계면활성제를 투입한 후 가온하며 교반함으로써 상기 계면활성제를 모두 용해시켜 계면활성액을 제조하는 계면 활성 단계;이온교환수에 촉매제를 넣고 용해시킨 촉매 용액을 제조하여 이를 상기 계면활성액에 혼합함으로써 기초반응액을 생성하는 촉매 투입 단계; 메틸렌 비스 아크릴 아마이드를 포함하는 둘 이상의 아크릴계 모노머와 계면활성제, 에탄올 및 연쇄이동제를 첨가 및 혼합하여 프리 에멀젼액을 형성하는 모노머 믹스 형성 단계와, 상기 기초 반응액에 총중량 대비 4 내지 6퍼센트의 상기 프리 에멀젼액을 투입하여 교반함으로써 초기 입자가 형성된 초기 혼합액을 생성하는 초기 입자 형성 단계 및, 상기 초기 혼합액에 나머지 프리 에멀젼액을 일정한 속도로 투입하여 중합 반응을 유도하여 1차 반응액을 형성하는 전체 반응 진행 단계를 포함하는 중합 단계; 상기 1차 반응액을 숙성시키는 숙성 단계; 상기 숙성 단계를 거친 1차 반응액을 냉각시킨 후 잔여반응 촉매제를 투입하여 교반함으로써 상기 중합 단계에서 반응되지 않은 미반응 모노머들을 반응시켜 최종 반응물을 생성하는 후처리 단계; 상기 최종 반응물을 상온으로 냉각시키는 냉각 단계를 포함하는 아크릴 중합체 제조 단계;를 포함하되, 상기 잔여반응 촉매제는 소디움 포름알데히드 술폭시레이트(SFS) 수용액이되, 상기 소디움 포름알데히드 술폭시레이트(SFS) 수용액의 용매는 편백나무 및 편백잎 중 어느 하나로부터 증류법으로 추출한 편백수인 것을 특징으로 하는, 아크릴 중합체를 포함하는 고체풀 제조 방법이 등록공개되어 있다.In addition, according to Patent Document No. 10-1650668, a surfactant step for preparing a surfactant solution by adding ion-exchanged water and a surfactant to a flask and then heating and stirring to dissolve all of the surfactant; A catalyst adding step of preparing a base solution by mixing a catalyst solution prepared by dissolving a catalyst in an exchange water and mixing the catalyst solution with the surfactant; A monomer mix forming step of adding and mixing at least two acrylic monomers including methylene bisacrylamide, a surfactant, ethanol and a chain transfer agent to form a pre-emulsion liquid, and a monomer mix forming step of adding 4 to 6% An initial particle formation step of adding an emulsion liquid and stirring to produce an initial mixed liquid in which initial particles have been formed, and an initial particle formation step of adding the remaining pre-emulsion liquid to the initial mixed liquid at a constant rate to induce a polymerization reaction, A polymerization step comprising an advancing step; An aging step of aging the primary reaction solution; A post-treatment step of cooling the first reaction solution after the aging step and then adding the remaining reaction catalyst and stirring to react the unreacted monomers in the polymerization step to produce a final reaction product; (SFS), wherein the residual reaction catalyst is an aqueous solution of sodium formaldehyde sulfoxylate (SFS), wherein the residual reaction catalyst is an aqueous solution of sodium formaldehyde sulfoxylate (SFS) A method for producing a solid paste including an acrylic polymer is disclosed, wherein the solvent of the aqueous solution is a fraction extracted from either the unplasticized or unbleached leaves by distillation.

그러나 상기와 같은 종래의 고체풀 제조방법은 접착력과 보관성이 떨어지거나, 고체풀 접착면이 불투명하고 PVP의 함량이 높아 경제성이 떨어지는 등의 문제점이 있었다.However, the conventional method of producing a solid paste as described above has problems such as poor adhesive strength and storage property, opaque solid adhesive surface, high PVP content, and poor economical efficiency.

따라서, 본 발명은 상기와 같은 문제점을 해결하고자 안출된 것으로, 접착력과 보관성이 우수하며, 상기 고형풀을 종이 등에 칠한 후에는 칠한 부분에 주름이 잘 생기지 않는 주름이 방지되는 투명 고형풀 제조방법을 제공하고자 한다.SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a transparent solid paste manufacturing method which is excellent in adhesion and storage property and which prevents wrinkles, .

본 발명은 주름이 방지되는 투명 고형풀 제조방법에 관한 것으로, 물 및 수크로즈(sucrose)를 포함하는 것을 특징으로 한다.The present invention relates to a method for producing a transparent solid paste in which wrinkles are prevented, and is characterized by including water and sucrose.

또한, 상기 주름이 방지되는 투명 고형풀의 원료는 에탄올, 소포제, 표백제, 가성소다, 글리세린(Glycerin), 동결방지제, 계면활성제, 고형화제, 접착제, 방부제, 살균제, 향을 더 포함하는 것을 특징으로 한다.In addition, the raw material of the transparent solid paste to prevent wrinkles may further include ethanol, a defoaming agent, a bleaching agent, caustic soda, glycerin, a cryoprotectant, a surfactant, a solidifying agent, an adhesive, a preservative, do.

또한, 상기 표백제는 Longalite, 상기 동결방지제는 Propylene Glycol, 상기 계면활성제는 Polyoxyethylene Laureth, 상기 고형화제는 Lauric Acid와 Sodium Steatate, 상기 접착제는 PVP인 것을 특징으로 한다.The bleaching agent is Longalite, the cryoprotectant is propylene glycol, the surfactant is polyoxyethylene laureth, the solidifying agent is lauric acid and sodium stearate, and the adhesive is PVP.

따라서, 본 발명인 주름이 방지되는 투명 고형풀 제조방법은 접착력과 보관성이 우수하며, 상기 고형풀을 종이 등에 칠한 후에는 칠한 부분에 주름이 잘 생기지 않는 등의 현저한 효과가 있다.Therefore, the method of manufacturing a transparent solid paste in which wrinkles are prevented according to the present invention is excellent in adhesion force and storage property, and has a remarkable effect such that wrinkles are not easily formed on a painted portion after the solid paste is coated on paper.

도 1은 본 발명인 주름이 방지되는 투명 고형풀 제조방법의 공정도FIG. 1 is a process diagram of a method for producing a transparent solid pool in which wrinkles are prevented according to the present invention

본 발명은 주름이 방지되는 투명 고형풀 제조방법에 관한 것으로, 물 및 수크로즈(Sucrose)를 포함하는 것을 특징으로 한다.The present invention relates to a method for producing a transparent solid paste in which wrinkles are prevented, and is characterized by including water and sucrose.

또한, 상기 주름이 방지되는 투명 고형풀의 원료는 에탄올, 소포제, 표백제, 가성소다, 글리세린(Glycerin), 동결방지제, 계면활성제, 고형화제, 접착제, 방부제, 살균제, 향을 더 포함하는 것을 특징으로 한다.In addition, the raw material of the transparent solid paste to prevent wrinkles may further include ethanol, a defoaming agent, a bleaching agent, caustic soda, glycerin, a cryoprotectant, a surfactant, a solidifying agent, an adhesive, a preservative, do.

또한, 상기 표백제는 Longalite, 상기 동결방지제는 Propylene Glycol, 상기 계면활성제는 Polyoxyethylene Laureth, 상기 고형화제는 Lauric Acid와 Sodium Steatate, 상기 접착제는 PVP인 것을 특징으로 한다.The bleaching agent is Longalite, the cryoprotectant is propylene glycol, the surfactant is polyoxyethylene laureth, the solidifying agent is lauric acid and sodium stearate, and the adhesive is PVP.

또한, 상기 물 370중량부에 대하여 수크로즈(sucrose) 265~325중량부, 에탄올 72~88중량부, 소포제 1~3중량부, 표백제인 Longalite 1~2중량부, 가성소다 1~3중량부, 글리세린(Glycerin) 38~46중량부, 동결방지제인 Propylene Glycol 11~15중량부, 계면활성제인 Polyoxyethylene Laureth 4~6중량부, 고형화제인 Lauric Acid 3~5중량부, 접착제인 PVP(poly vinyl pyrrolidone) 126~154중량부, 고형화제인 Sodium Steatate 36~44중량부, 방부제 2~4중량부, 살균제 1~2중량부, 향 1~3중량부를 첨가한 후 교반하여 혼합물을 제조하는 단계; 상기 제조된 혼합물을 65-75℃의 온도에서 1~3시간 가열교반하는 단계; 상기 가열교반된 혼합물을 용기에 넣고 굳히는 냉각성형단계;로 구성되는 것을 특징으로 한다.In addition, 265 to 325 parts by weight of sucrose, 72 to 88 parts by weight of ethanol, 1 to 3 parts by weight of a defoamer, 1 to 2 parts by weight of longalite as a bleaching agent, 1 to 3 parts by weight of caustic soda, 38 to 46 parts by weight of glycerin, 11 to 15 parts by weight of Propylene Glycol as a cryoprotectant, 4 to 6 parts by weight of Polyoxyethylene Laureth as a surfactant, 3 to 5 parts by weight of Lauric Acid as a solidifying agent, polyvinyl pyrrolidone ), 126 to 154 parts by weight of a solidifying agent, 36 to 44 parts by weight of sodium steatate, 2 to 4 parts by weight of a preservative, 1 to 2 parts by weight of a germicide, and 1 to 3 parts by weight of an incense. Stirring the prepared mixture at a temperature of 65 to 75 DEG C for 1 to 3 hours; And a cooling and molding step in which the heated and stirred mixture is placed in a container and solidified.

본 발명을 첨부도면에 의해 상세히 설명하면 다음과 같다.The present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명인 주름이 방지되는 투명 고형풀 제조방법의 공정도이다.Fig. 1 is a process diagram of a method for manufacturing a transparent solid paste in which wrinkles are prevented according to the present invention.

본 발명인 주름이 방지되는 투명 고형풀 제조방법은 물 370중량부에 대하여 수크로즈(sucrose) 265~325중량부, 에탄올 72~88중량부, 소포제 1~3중량부, 표백제인 Longalite 1~2중량부, 가성소다 1~3중량부, 글리세린(Glycerin) 38~46중량부, 동결방지제인 Propylene Glycol 11~15중량부, 계면활성제인 Polyoxyethylene Laureth 4~6중량부, 고형화제인 Lauric Acid 3~5중량부, 접착제인 PVP(poly vinyl pyrrolidone) 126~154중량부, 고형화제인 Sodium Steatate 36~44중량부, 방부제 2~4중량부, 살균제 1~2중량부, 향 1~3중량부를 첨가한 후 교반하여 혼합물을 제조하는 단계; 상기 제조된 혼합물을 65-75℃의 온도에서 1~3시간 가열교반하는 단계; 상기 가열교반된 혼합물을 용기에 넣고 굳히는 냉각성형단계;로 구성되는 것을 특징으로 한다.The method for producing a transparent solid paste of the present invention is characterized by comprising 265 to 325 parts by weight of sucrose, 72 to 88 parts by weight of ethanol, 1 to 3 parts by weight of an antifoaming agent, 1 to 2 parts by weight of a bleaching agent Longalite 1 to 3 parts by weight of caustic soda, 38 to 46 parts by weight of glycerin, 11 to 15 parts by weight of Propylene Glycol as a cryoprotectant, 4 to 6 parts by weight of Polyoxyethylene Laureth as a surfactant, 3 to 5 by weight of Lauric Acid as a solidifying agent 126 to 154 parts by weight of polyvinyl pyrrolidone (PVP) as an adhesive, 36 to 44 parts by weight of sodium stearate as a solidifying agent, 2 to 4 parts by weight of a preservative, 1 to 2 parts by weight of a bactericide and 1 to 3 parts by weight of an incense, To prepare a mixture; Stirring the prepared mixture at a temperature of 65 to 75 DEG C for 1 to 3 hours; And a cooling and molding step in which the heated and stirred mixture is placed in a container and solidified.

본 발명인 주름이 방지되는 투명 고형풀 제조방법에서 첨가되는 수크로즈(sucrose)는 물에 녹아 고형풀의 색깔을 투명하게 하며, 가열교반되면서 점성과 끈기를 가지게 되어 접착력을 증대시키므로 상기 투명 고형풀 제조 시 첨가되는 PVP(poly vinyl pyrrolidone)의 양을 줄일 수 있다.The sucrose added in the wrinkle-free transparent solid paste manufacturing method of the present invention is soluble in water to make the color of the solid paste transparent and has viscosity and stickiness while being heated and agitated, The amount of polyvinyl pyrrolidone (PVP) added can be reduced.

상기 수크로즈(sucrose)가 265중량부 미만으로 첨가되면 제조되는 투명 고형풀의 접착력이 떨어지며, 상기 수크로즈(sucrose)이 325중량부를 초과하여 첨가되면 상기 냉각성형단계에서 수크로즈(sucrose)가 재결정을 이루어 석출되고 이로 인해 접착력이 떨어지는 현상이 나타날 수 있다.When the sucrose is added in an amount of less than 265 parts by weight, the adhesive strength of the transparent solid paste to be produced is low. When the sucrose is added in an amount exceeding 325 parts by weight, sucrose is recrystallized So that the adhesive strength is lowered.

상기 에탄올은 고형풀의 색깔을 투명하게 하며, 상기 투명 고형풀 제조 시 첨가되는 첨가물 중 물에 녹지 않는 첨가물들을 녹이는 용매 역할을 한다.The ethanol makes the color of the solid paste transparent and serves as a solvent for dissolving the water-insoluble additives in the additive added in the production of the transparent solid paste.

그리고, 상기 에탄올이 72중량부 미만으로 첨가되면 상기 투명 고형풀 제조 시 첨가되는 첨가물 중 물에 녹지 않는 첨가물들이 잘 녹지 않으며, 88중량부를 초과하여 첨가되면 고형화제인 상기 투명 고형풀 제조 시 첨가되는 첨가물 중 물에 녹지 않는 첨가물들은 다 녹으나 남는 에탄올이 있어 에탄올이 낭비가 된다.When the ethanol is added in an amount of less than 72 parts by weight, the water-insoluble additives are insufficiently dissolved in the additive to be added in the production of the transparent solid paste. When the additive is added in an amount exceeding 88 parts by weight, All of the water-insoluble additives dissolve, but there is ethanol remaining, which is a waste of ethanol.

상기 소포제가 하는 역할은 물에 발생되는 거품을 없애는 역할을 한다.The role of the defoaming agent is to remove the bubbles generated in the water.

그리고, 상기 소포제가 1중량부 미만으로 첨가되면 거품이 제거되지 않아 가열교반하는 단계에서 게속 거품이 발생하고, 3중량부를 초과하여 첨가되면 소포제의 양이 과다하여 잔존하는 소포제가 있어 낭비가 된다.When the defoaming agent is added in an amount of less than 1 part by weight, the foam is not removed and the defoaming agent is generated in the heating and stirring step. If the defoaming agent is added in an amount exceeding 3 parts by weight, the amount of defoaming agent is excessive.

상기 표백제인 Longalite가 1중량부 미만으로 첨가되면 표백작용이 올바르게 이루어지지 않아 제조되는 투명 고형풀에 얼룩이나 유색 물질이 생길 수 있으며, 2중량부를 초과하여 첨가되면 잔존하는 표백제가 있을 수 있어 사용자의 피부건강에 유해한 영향을 미칠 수 있다.When the bleaching agent Longalite is added in an amount of less than 1 part by weight, the bleaching action is not properly performed, so that stain or colored materials may be formed in the transparent solid paste to be produced. If the bleaching agent is added in an amount exceeding 2 parts by weight, It can have a detrimental effect on skin health.

상기 가성소다가 1중량부 미만으로 첨가되면 비누화 반응이 잘 일어나지 않아 제조되는 투명 고형풀이 일정한 크기로 부풀지 않으며, 3중량부를 초과하여 첨가되면 잔존하는 가성소다가 있을 수 있어 사용자의 피부건강에 유해한 영향을 미칠 수 있다.When the amount of the caustic soda is less than 1 part by weight, the saponification reaction does not occur well, and the transparent solid paste to be prepared does not inflate to a certain size. If the caustic soda is added in an amount exceeding 3 parts by weight, residual caustic soda may be present, It can have an impact.

상기 글리세린(Glycerin)은 제조되는 투명 고형풀이 투명한 색깔을 띄게 하고, 상기 투명 고형풀을 접착면에 바를 때 부드럽게 발리게 하는 역할을 한다.The glycerin serves to make the transparent solid pool to be produced have a transparent color and soften the transparent solid pool when the transparent solid pool is applied to the adhesive surface.

그리고, 상기 글리세린(Glycerin)이 38중량부 미만으로 첨가되면 제조되는 투명 고형풀의 보습력이 떨어져 접착면에 바를 때 부드럽게 발리지 않으며, 46중량부를 초과하여 첨가되면 제조되는 투명 고형풀이 강도가 약해지고 물러진다.When the glycerin is added in an amount of less than 38 parts by weight, the transparency of the transparent solid paste is lowered, and when it is added to the adhesive surface, the transparent solid paste is not softened. When the added amount is more than 46 parts by weight, Loses.

상기 동결방지제인 Propylene Glycol이 11중량부 미만으로 첨가되면 제조된 투명 고형풀이 동절기에 얼고 녹은 다음 급격히 강도가 약해지고 물러지는 현상이 발생하며, 15중량부를 초과하여 첨가되면 제조되는 투명 고형풀이 강도가 약해지고 물러진다.When the above-mentioned cryoprotectant, Propylene Glycol, is added in an amount of less than 11 parts by weight, the resulting transparent solid solution is frozen and melted in the winter season and rapidly weakens and shrinks. When more than 15 parts by weight of the transparent solid solution is added, Back off.

상기 계면활성제인 Polyoxyethylene Laureth가 4중량부 미만으로 첨가되면 첨가물들이 서로 잘 섞이지 않고, 6중량부를 초과하여 첨가되면 제조되는 투명 고형풀이 강도가 약해지고 물러진다.If less than 4 parts by weight of the surfactant Polyoxyethylene Laureth is added, the additives do not mix well, and if more than 6 parts by weight of the additive is added, the transparent solid paste is weakened and retards.

상기 고형화제 중 하나인 Lauric Acid가 3중량부 미만으로 첨가되면 첨가된 수크로즈(sucrose)으로 인하여 습기를 흡수하여 제조된 투명 고형풀이 물러져 상기 투명 고형풀을 접착면에 바를 때 너무 많이 발라지거나 모양이 쉽게 변형될 수 있으며, 5중량부를 초과하여 첨가되면 상기 투명 고형풀의 강도가 딱딱해져 상기 투명 고형풀을 접착면에 바를 때 부드럽게 발리지 않게 된다.When Lauric Acid, which is one of the solidifying agents, is added in an amount of less than 3 parts by weight, moisture is absorbed due to the added sucrose, so that the transparent solid paste obtained by backing up the transparent solid paste is applied to the adhesive surface, If the content of the transparent solid paste is more than 5 parts by weight, the strength of the transparent solid paste becomes hard and the transparent solid paste does not smooth smoothly when the transparent solid paste is applied on the adhesive surface.

그리고, 상기 고형화제 중 다른 하나인 Sodium Steatate가 36중량부 미만으로 첨가되면 제조된 투명 고형풀이 물러져 상기 투명 고형풀을 접착면에 바를 때 너무 많이 발라지거나 모양이 쉽게 변형될 수 있으며, 44중량부를 초과하여 첨가되면 상기 투명 고형풀의 강도가 딱딱해져 상기 투명 고형풀을 접착면에 바를 때 부드럽게 발리지 않게 된다.When sodium stearate, which is another one of the solidifying agents, is added in an amount of less than 36 parts by weight, the prepared transparent solid paste is reclaimed, and when the transparent solid paste is applied on the adhesive surface, The strength of the transparent solid paste is hardened so that the transparent solid paste does not soften when the transparent solid paste is applied on the adhesive surface.

상기 접착제인 PVP(poly vinyl pyrrolidone)가 126중량부 미만으로 첨가되면 제조된 투명 고형풀의 접착력이 떨어지며, 154중량부를 초과하여 첨가되면 상기 투명 고형풀을 접착면에 바를 때 많이 달라붙으며 부드럽게 발리지 않게 된다. If the amount of polyvinyl pyrrolidone (PVP) added is less than 126 parts by weight, the adhesive strength of the prepared transparent solid paste deteriorates. If the adhesive is added in an amount exceeding 154 parts by weight, the transparent solid paste adheres to the adhesive surface much, .

상기 방부제가 2중량부 미만으로 첨가되면 제조된 투명 고형풀이 무덥고 습한 하절기에 변질될 수 있으며, 4중량부를 초과하여 첨가되면 잔존하는 방부제가 사용자의 피부건강에 유해한 영향을 미칠 수 있다.If the preservative is added in an amount of less than 2 parts by weight, the prepared transparent solid paste may deteriorate in a hot and humid summer season. If the preservative is added in an amount of more than 4 parts by weight, the preservative may adversely affect the skin health of the user.

상기 살균제가 1중량부 미만으로 첨가되면 제조된 투명 고형풀에 세균이 서식할 수 있어 사용자의 건강에 좋지 않으며, 2중량부를 초과하여 첨가되면 살균제가 잔존할 수 있어 살균제가 낭비된다.If less than 1 part by weight of the sterilizing agent is added, the sterilizing agent may be left in the transparent solid paste, and if the sterilizing agent is added in an amount of more than 2 parts by weight, the sterilizing agent may be wasted.

상기 향이 1중량부 미만으로 첨가되면 제조된 투명 고형풀에서 이상한 냄새가 나며, 3중량부를 초과하여 첨가되면 향이 강하여 사용자가 거부감을 느낄 수 있다.When the fragrance is added in an amount of less than 1 part by weight, odorous odor is produced in the transparent solid paste. If the fragrance is added in more than 3 parts by weight, the fragrance is strong.

상기 제조된 혼합물을 가열교반할 때 65℃ 미만의 온도로 가열되면 상기 고형화제인 Sodium Steatate이 잘 녹지 않으며, 75℃를 초과하는 온도로 가열되면 에탄올, 방부제, 살균제, 향 등이 변성되거나 기화되어 제조되는 투명 고형풀의 품질이 떨어진다.When the mixture is heated and stirred at a temperature of less than 65 ° C., the solidifying agent, sodium steatate, is not dissolved sufficiently. When the mixture is heated to a temperature exceeding 75 ° C., ethanol, preservative, bactericide, The quality of the transparent solid paste is deteriorated.

그리고, 상기 제조된 혼합물을 가열교반할 때 1시간 미만으로 가열되면 첨가물들이 제대로 반응이 일어나지 않아 제조되는 투명 고형풀의 품질이 떨어지며, 3시간을 초과하여 가열되면 제조되는 투명 고형풀의 색상이 탁해지고 강도가 딱딱해져 상기 투명 고형풀을 접착면에 바를 때 부드럽게 발리지 않게 된다.When the prepared mixture is heated under stirring for less than 1 hour, the additives do not react properly and the quality of the transparent solid paste to be produced deteriorates. If the transparent solid paste is heated for more than 3 hours, So that the transparent solid paste does not soften when the transparent solid paste is applied to the adhesive surface.

따라서, 본 발명인 주름이 방지되는 투명 고형풀 제조방법은 접착력과 보관성이 우수하며, 상기 고형풀을 종이 등에 칠한 후에는 칠한 부분에 주름이 잘 생기지 않는 등의 현저한 효과가 있다.Therefore, the method of manufacturing a transparent solid paste in which wrinkles are prevented according to the present invention is excellent in adhesion force and storage property, and has a remarkable effect such that wrinkles are not easily formed on a painted portion after the solid paste is coated on paper.

Claims (3)

물 및 수크로즈(Sucrose)를 포함하는 것을 특징으로 하는 주름이 방지되는 투명 고형풀 제조방법
A method for producing a wrinkle-free transparent solid paste characterized by comprising water and sucrose
제1항에 있어서, 상기 주름이 방지되는 투명 고형풀의 원료는 에탄올, 소포제, 표백제, 가성소다, 글리세린(Glycerin), 동결방지제, 계면활성제, 고형화제, 접착제, 방부제, 살균제, 향을 더 포함하는 것을 특징으로 하는 주름이 방지되는 투명 고형풀 제조방법
The method of claim 1, wherein the wrinkle-free transparent solid pool material further comprises ethanol, an antifoaming agent, a bleach, caustic soda, glycerin, a cryoprotectant, a surfactant, a solidifying agent, an adhesive, a preservative, A method for manufacturing a transparent solid paste which prevents wrinkles
제2항에 있어서, 상기 표백제는 Longalite, 상기 동결방지제는 Propylene Glycol, 상기 계면활성제는 Polyoxyethylene Laureth, 상기 고형화제는 Lauric Acid와 Sodium Steatate, 상기 접착제는 PVP인 것을 특징으로 하는 주름이 방지되는 투명 고형풀 제조방법


[3] The method according to claim 2, wherein the bleaching agent is Longalite, the cryoprotectant is Propylene Glycol, the surfactant is Polyoxyethylene Laureth, the solidifying agent is Lauric Acid and Sodium Steatate, and the adhesive is PVP. Pool Manufacturing Method


KR1020170096966A 2017-07-31 2017-07-31 Manufacturing method of anti-wrinkle transparent solid paste KR101946158B1 (en)