KR20180113892A - Adhesive composition and adhesive film - Google Patents

Adhesive composition and adhesive film Download PDF

Info

Publication number
KR20180113892A
KR20180113892A KR1020170133826A KR20170133826A KR20180113892A KR 20180113892 A KR20180113892 A KR 20180113892A KR 1020170133826 A KR1020170133826 A KR 1020170133826A KR 20170133826 A KR20170133826 A KR 20170133826A KR 20180113892 A KR20180113892 A KR 20180113892A
Authority
KR
South Korea
Prior art keywords
pressure
sensitive adhesive
group
adhesive layer
meth
Prior art date
Application number
KR1020170133826A
Other languages
Korean (ko)
Other versions
KR102034512B1 (en
Inventor
타케시 나가쿠라
히로유키 요시다
후미에 스즈키
켄타로 오츠가
아키요 히시누마
Original Assignee
후지모리 고교 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 후지모리 고교 가부시키가이샤 filed Critical 후지모리 고교 가부시키가이샤
Publication of KR20180113892A publication Critical patent/KR20180113892A/en
Application granted granted Critical
Publication of KR102034512B1 publication Critical patent/KR102034512B1/en

Abstract

The present invention provides an adhesive composition and an adhesive film using the same in which the adhesive composition is extremely excellent in antistatic performance by having surface resistivity of an adhesive layer of 2.0×10^(+9)Ω/□ or less, and does not impede durability. According to the present invention, the adhesive composition comprises: an acrylic polymer which is a copolymer obtained by copolymerizing (A) n-butyl acrylate, (B) at least one selected from t-butyl acrylate, isobutyl acrylate, n-butyl methacrylate, and methyl acrylate, (C) a copolymerizable vinyl monomer containing a hydroxyl group and/or a carboxyl group, and (D) an aromatic group-containing copolymerizable vinyl monomer; (E) an ammonium-based antistatic agent having fluoro group-containing anions; and (F) a crosslinking agent consisting of an isocyanate compound having three or more functional groups or an epoxy compound having two or more functional groups. The adhesive composition further comprises (G) a silane coupling agent containing a functional group selected from an epoxy group, a mercapto group and an acid anhydride group.

Description

점착제 조성물 및 점착 필름{ADHESIVE COMPOSITION AND ADHESIVE FILM}[0001] ADHESIVE COMPOSITION AND ADHESIVE FILM [0002]

본 발명은 예를 들면, 피착체가 액정 패널이며, 터치 패널의 기능을 도입한 인셀 패널에 첩합하는 용도로 사용될 수 있는 점착제 조성물 및 점착 필름에 관한 것이다. The present invention relates to, for example, a pressure-sensitive adhesive composition and a pressure-sensitive adhesive film which can be used in applications where the adherend is a liquid crystal panel and is attached to an inshell panel incorporating a function of a touch panel.

특히, 점착제층의 표면 저항율이 종래 기술에서는 달성할 수 없는 2.0×10+9Ω/□ 이하인 지극히 우수한 대전 방지 성능을 갖는 점착제 조성물 및 이를 사용한 점착 필름에 관한 것이다.In particular, the surface resistivity of the adhesive layer directed to a pressure-sensitive adhesive composition and an adhesive film using the same having a 2.0 × 10 +9 Ω / □ or less very good antistatic property can not be achieved in the prior art.

편광판, 위상차판 등의 광학 부재를 점착제층을 개재하여 액정 셀 등의 피착체에 첩합하기 위한 다양한 점착 필름이 제안되어 있다(예를 들면, 특허문헌 1∼2참조). There have been proposed various adhesive films for bonding an optical member such as a polarizing plate and a retarder to an adherend such as a liquid crystal cell through a pressure-sensitive adhesive layer (see, for example, Patent Documents 1 and 2).

특허문헌 1에는 부틸아크릴레이트 등을 주성분의 모노머로 하고, 아크릴아미드 화합물 등을 공중합시킨 아크릴계 폴리머를 함유하는 광학용 점착제 조성물이 기재되어 있다. Patent Document 1 discloses a pressure-sensitive adhesive composition for optical purposes containing an acryl-based polymer obtained by copolymerizing an acrylamide compound or the like with butyl acrylate or the like as a main component monomer.

특허문헌 2에는 탄소수 4∼8의 알킬기를 갖는 (메타)아크릴레이트를 주성분의 모노머로 하고, 카르복실기 함유 모노머 및 질소 함유 비닐 모노머를 공중합시킨 아크릴계 폴리머를 함유하는 광학용 점착제 조성물이 기재되어 있다. Patent Document 2 discloses a pressure-sensitive adhesive composition for optical use which contains an acrylic polymer obtained by copolymerizing a carboxyl-containing monomer and a nitrogen-containing vinyl monomer with a (meth) acrylate having an alkyl group having 4 to 8 carbon atoms as a main component monomer.

일본 공개특허공보 2012-177022호Japanese Laid-Open Patent Publication No. 2012-177022 일본 공개특허공보 2012-201734호Japanese Laid-Open Patent Publication No. 2012-201734

그러나, 편광판과 액정 패널을 첩합하는 용도의 점착제층에 있어서는, 액정 패널이 터치 패널의 기능을 도입한 인셀 패널로 된 경우에는 당해 점착제층의 표면 저항율을 종래의 표면 저항율에 비해 낮은 값으로 하는 것이 요구되고 있다. However, in the pressure-sensitive adhesive layer for application of a polarizing plate and a liquid crystal panel, when the liquid crystal panel is made of an insulphone panel incorporating the function of a touch panel, the surface resistivity of the pressure-sensitive adhesive layer is made lower than that of the conventional surface resistivity Is required.

이 때문에, 편광판을 액정 패널에 첩합하는 용도의 점착제층은, 당해 점착제층의 표면 저항율을 2.0×10+9Ω/□ 이하로 하는 것이 요망되고 있다. 그러나, 종래 기술에 있어서는 이러한 고도의 대전 방지 성능을 발현시키는 것이 매우 어려운 상황이었다. For this reason, it is desired that the pressure-sensitive adhesive layer to be used for bonding the polarizing plate to the liquid crystal panel has a surface resistivity of 2.0 x 10 < + 9 > However, in the prior art, it has been very difficult to develop such a high antistatic performance.

또한, 이러한 고도의 대전 방지 성능이 발현된 경우에도, 동시에 점착제층의 내구성을 유지하는 것이 곤란하였다. Further, even when such a high antistatic property is exhibited, it is difficult to maintain the durability of the pressure-sensitive adhesive layer at the same time.

본 발명은 점착제층의 표면 저항율이 2.0×10+9Ω/□ 이하의 지극히 우수한 대전 방지 성능을 갖고, 또한 내구성을 저해하지 않는 점착제 조성물 및 이를 사용한 점착 필름을 제공하는 것을 과제로 한다.Disclosed is a pressure-sensitive adhesive composition which has an excellent antistatic property with a surface resistivity of 2.0 x 10 < + 9 > / & squ & / square or less and does not hinder durability.

이러한 고도의 대전 방지 성능과 내구성의 양쪽 모두를 동시에 달성한다고 하는 곤란한 과제를 해결하기 위해, 본 발명자들이 예의 검토하였다. 그 결과, 점착제 조성물의 아크릴계 폴리머를 구성하는 알킬(메타)아크릴레이트의 알킬기의 탄소수를 특정 범위로 한정하여, 특정 조합의 2종 이상의 알킬(메타)아크릴레이트를 공중합시킨 공중합체로 이루어지는 아크릴계 폴리머로 하고, 추가로 특정 대전 방지제를 함유시킨 점착제 조성물로 함으로써, 이 과제를 해결하는 것이 가능해졌다. In order to solve such a difficult problem that both of the high antistatic performance and the durability are simultaneously achieved, the present inventors have eagerly studied. As a result, an acrylic polymer comprising a copolymer in which a specific combination of two or more alkyl (meth) acrylates are copolymerized by limiting the number of carbon atoms in the alkyl group of the alkyl (meth) acrylate constituting the acrylic polymer of the pressure- , And further a specific antistatic agent is contained in the pressure-sensitive adhesive composition, it is possible to solve this problem.

본 발명자들은 상기 아크릴계 폴리머와, 상기 아크릴계 폴리머의 100중량부에 대해 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제를 15중량부를 초과하는 비율로 함유시킴으로써, 종래의 점착제 조성물과 비교하여 지극히 우수한 대전 방지 성능을 갖고, 또한 대전 방지제가 석출되지 않으며, 경시 열화되지 않고 우수한 내구성을 갖는 점착제 조성물이 얻어지는 것을 알아내어, 본 발명을 완성시켰다. The present inventors have found that by containing the acrylic polymer and the ammonium-based antistatic agent having a fluorine group-containing anion in an amount exceeding 15 parts by weight based on 100 parts by weight of the acrylic polymer, And that an antistatic agent is not precipitated, and that a pressure-sensitive adhesive composition having excellent durability without deterioration with time can be obtained, thereby completing the present invention.

본 발명에 따른 점착제 조성물은 점착제층의 표면 저항율을 2.0×10+9Ω/□ 이하의 지극히 우수한 대전 방지 성능으로 하기 위해, 아크릴계 폴리머의 100중량부에 대해 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제를 15중량부를 초과하는 비율로 함유시키고 있다. 이와 같이, 본 발명에서는 종래 기술에서는 달성할 수 없는 지극히 우수한 대전 방지 성능을 얻기 위해 대전 방지제의 함유량을 많게 하고 있다. The pressure-sensitive adhesive composition according to the present invention is characterized in that the pressure-sensitive adhesive layer has an excellent antistatic property with a surface resistivity of 2.0 x 10 < -9 > And contains an inhibitor in a proportion exceeding 15 parts by weight. As described above, in the present invention, the content of the antistatic agent is increased in order to obtain extremely excellent antistatic performance which can not be achieved by the prior art.

본 발명에 따른 점착제 조성물은 점착제층의 고온·고습도 환경하에 있어서의 내구성 시험 후에 있어서, 점착제층 중에 다량으로 포함되는 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제가 점착제층의 표면에 석출되지 않고, 내구성을 유지할 수 있는 점착제층으로 하기 위해, 점착제 조성물에 포함되는 아크릴계 폴리머가 n-부틸아크릴레이트(BA)를 주체로 하고, BA와 공중합성이 좋은 모노머를 선택하여 공중합시켜서 이루어지는 것을 기술 사상으로 하고 있다. The pressure-sensitive adhesive composition of the present invention does not precipitate on the surface of the pressure-sensitive adhesive layer the ammonium-based antistatic agent having a fluorine group-containing anion contained in a large amount in the pressure-sensitive adhesive layer after the durability test in a high- In order to obtain a pressure-sensitive adhesive layer capable of maintaining durability, the acrylic polymer contained in the pressure-sensitive adhesive composition is composed of n-butyl acrylate (BA) as a main component and a monomer having good copolymerization with BA is selected and copolymerized have.

또한, 상기의 과제를 해결하기 위해, 본 발명은 아크릴계 폴리머와, 대전 방지제와, 가교제를 함유하는 점착제 조성물로서, 상기 아크릴계 폴리머가 (A) n-부틸아크릴레이트와, (B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종과, (C) 수산기 및/또는 카르복실기를 함유하는 공중합성 비닐 모노머의 적어도 1종과, (D) 방향족기를 함유하는 공중합성 비닐 모노머의 적어도 1종을 공중합시킨 공중합체의 중량 평균 분자량이 100∼300만인 아크릴계 폴리머이며, 상기 (E) 대전 방지제로서 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제를 상기 아크릴계 폴리머의 100중량부에 대해 15중량부 초과 40중량부 이하의 비율로 함유하여 이루어지고, 상기 (F) 가교제로서 3관능 이상의 이소시아네이트 화합물, 2관능 이상의 에폭시 화합물로 이루어지는 군에서 선택된 적어도 1종 이상의 가교제를 함유하여 이루어지고, 상기 점착제 조성물이 (G) 에폭시기, 메르캅토기, 산무수물기에서 선택된 적어도 1종 이상의 관능기를 함유하는 모노머 타입 또는 올리고머 타입의 실란 커플링제를 추가로 함유하여 이루어지고, 상기 점착제 조성물을 가교시킨 점착제층의 표면 저항율이 2.0×10+9Ω/□ 이하이며, 상기 점착제층을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 또는 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 상기 점착제층의 표면에 상기 대전 방지제가 석출되어 있지 않는 것을 특징으로 하는 점착제 조성물을 제공한다. In order to solve the above problems, the present invention provides a pressure-sensitive adhesive composition containing an acrylic polymer, an antistatic agent and a crosslinking agent, wherein the acrylic polymer comprises (A) n-butyl acrylate, (B) (C) at least one copolymerizable vinyl monomer containing at least one member selected from the group consisting of isopropyl (meth) acrylate, isobutyl acrylate, n-butyl methacrylate and methyl acrylate, and (C) a hydroxyl group and / ) A copolymer obtained by copolymerizing at least one copolymerizable vinyl monomer containing an aromatic group is an acrylic polymer having a weight average molecular weight of 100 to 3,000,000, and the (E) ammonium-based antistatic agent having a fluorine group-containing anion as the antistatic agent Based on 100 parts by weight of the acryl-based polymer, in an amount of not less than 15 parts by weight and not more than 40 parts by weight, and (F) Isocyanate compound and at least one crosslinking agent selected from the group consisting of bifunctional or higher functional epoxy compounds, and the pressure-sensitive adhesive composition comprises (G) at least one functional group selected from the group consisting of an epoxy group, a mercapto group and an acid anhydride group a monomer type or is made to further contain a silane coupling agent, an oligomer type, the surface resistivity of the pressure-sensitive adhesive layer crosslinked with the pressure-sensitive adhesive composition is 2.0 × 10 +9 Ω / □ or less, the test of the pressure-sensitive adhesive layer 85 ℃ × 750hr Characterized in that the antistatic agent is not precipitated on the surface of the pressure-sensitive adhesive layer after the pressure-sensitive adhesive layer is provided in a durability test under an environment or in a durability test under a test environment of 60 캜 x 90% RH x 750 hr Sensitive adhesive composition.

또한, 상기 대전 방지제가 플루오로기 함유 음이온과 암모늄 양이온으로 이루어지는 융점이 25℃ 이상인 이온성 화합물이며, 상기 플루오로기 함유 음이온이 펜타플루오로벤젠술포네이트, 헥사플루오로포스페이트, 비스(트리플루오로메탄술포닐)이미드, 비스(플루오로술포닐)이미드, 트리플레이트로 이루어지는 군에서 선택된 1종인 것이 바람직하다. The antistatic agent is an ionic compound having a fluoro group-containing anion and an ammonium cation and having a melting point of 25 ° C or higher, and the fluoro group-containing anion is pentafluorobenzenesulfonate, hexafluorophosphate, bis (trifluoro Methanesulfonyl) imide, bis (fluorosulfonyl) imide, triflate, and the like.

상기 아크릴계 폴리머가 상기 아크릴계 폴리머의 100중량부에 대해, 상기 (A) n-부틸아크릴레이트를 40∼89중량부와, 상기 (B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종 이상의 합계를 5∼40중량부의 비율로 함유하여 이루어지고, 또한 (A)와 (B)의 비율((A)／(B))이 1.0∼17.8인 것이 바람직하다. (A) n-butylacrylate in an amount of 40 to 89 parts by weight based on 100 parts by weight of the acryl-based polymer, and (B) t-butyl acrylate, isobutyl acrylate, n-butyl (A) / (B) in a ratio of (A) / (B) is 1.0 or less, To 17.8.

상기 점착제 조성물을 가교시킨 두께 20㎛의 점착제층을 개재하여 총 두께 80㎛의 편광판을 무알칼리 유리에 첩합하였을 때, 상기 점착제층의 무알칼리 유리에 대한 점착력이 1.0∼6.0N/25㎜이며, 상기 점착제 조성물을 가교시킨 두께 20㎛의 점착제층을 개재하여 10㎝ 각의 총 두께 80㎛의 편광판을 무알칼리 유리에 첩합하여 이루어지는 시험편을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 또는 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 발포 및 박리가 없는 것이 바람직하다. The pressure-sensitive adhesive layer had an adhesive force of 1.0 to 6.0 N / 25 mm to a non-alkali glass when a polarizing plate having a total thickness of 80 占 퐉 was bonded to a non-alkali glass via a pressure-sensitive adhesive layer having a thickness of 20 占 퐉, A test piece consisting of a 10-cm square polarizing plate having a total thickness of 80 占 퐉 laminated to a non-alkali glass via a pressure-sensitive adhesive layer having a thickness of 20 占 퐉 bridged with the pressure-sensitive adhesive composition was provided in a durability test under a test environment of 85 占 폚 for 750 hours It is preferable that there is no foaming and peeling after it is provided in a durability test in a test environment of 60 占 폚 占 90% RH 占 占 750 hr.

상기 (C) 수산기 및/또는 카르복실기를 함유하는 공중합성 비닐 모노머가 수산기를 함유하는 공중합 가능한 모노머 및 카르복실기를 함유하는 공중합 가능한 모노머로 이루어지는 군에서 선택된 적어도 1종 이상이며, 상기 수산기를 함유하는 공중합 가능한 모노머가 8-히드록시옥틸(메타)아크릴레이트, 6-히드록시헥실(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 2-히드록시에틸(메타)아크릴레이트, N-히드록시(메타)아크릴아미드, N-히드록시메틸(메타)아크릴아미드, N-히드록시에틸(메타)아크릴아미드로 이루어지는 화합물군 중에서 선택된 적어도 1종 이상이며, 상기 카르복실기를 함유하는 공중합 가능한 모노머가 (메타)아크릴산, 카르복시에틸(메타)아크릴레이트, 카르복시펜틸(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸헥사히드로프탈산, 2-(메타)아크릴로일옥시프로필헥사히드로프탈산, 2-(메타)아크릴로일옥시에틸프탈산, 2-(메타)아크릴로일옥시에틸숙신산, 2-(메타)아크릴로일옥시에틸말레산, 카르복시폴리카프로락톤모노(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸테트라히드로프탈산으로 이루어지는 화합물군 중에서 선택된 적어도 1종 이상인 것이 바람직하다. (C) the copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group is at least one or more selected from the group consisting of a copolymerizable monomer containing a hydroxyl group and a copolymerizable monomer containing a carboxyl group, (Meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, N-hydroxy (Meth) acrylamide, N-hydroxymethyl (meth) acrylamide and N-hydroxyethyl (meth) acrylamide, wherein the copolymerizable monomer containing a carboxyl group is at least one selected from the group consisting of ) Acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, 2- (meth) acryloyloxyethylhexahydro (Meth) acryloyloxyethylphthalic acid, 2- (meth) acryloyloxyethylsuccinic acid, 2- (meth) acryloyloxyethyl At least one member selected from the group consisting of maleic acid, carboxypolycaprolactone mono (meth) acrylate, and 2- (meth) acryloyloxyethyltetrahydrophthalic acid is preferable.

상기 점착제층의 초기 표면 저항율 및 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후의 표면 저항율이 모두 2.0×10+9Ω/□ 이하인 것이 바람직하다. It is preferable that both the initial surface resistivity of the pressure-sensitive adhesive layer and the surface resistivity after being provided in the durability test under the test environment of 85 占 폚 占 750 hr are all 2.0 x 10 + 9 ? /? Or less.

또한, 본 발명은 수지 필름의 한쪽 면에 상기 점착제 조성물을 가교시킨 점착제층이 적층되어 이루어지는 것을 특징으로 하는 점착 필름을 제공한다. The present invention also provides an adhesive film comprising a resin film laminated on one side thereof with a pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition.

또한, 본 발명은 상기 점착 필름이 사용된 편광판용 점착 필름을 제공한다. The present invention also provides an adhesive film for a polarizing plate using the adhesive film.

또한, 본 발명은 편광판과 인셀 패널의 첩합에 사용되고 있는 것을 특징으로 하는 상기 편광판용 점착 필름을 제공한다. The present invention also provides a pressure-sensitive adhesive film for a polarizing plate, which is used for bonding a polarizing plate and an ink cell panel.

또한, 본 발명은 이형 필름의 한쪽 면에 상기 점착제 조성물을 가교시킨 점착제층이 1㎛∼25㎛의 두께로 형성된 이형 필름/점착제층/이형 필름의 구성인 것을 특징으로 하는 점착 필름을 제공한다. Further, the present invention provides an adhesive film characterized in that the pressure-sensitive adhesive layer in which the pressure-sensitive adhesive composition is crosslinked on one side of the release film is constituted of a release film / pressure-sensitive adhesive layer / release film formed to a thickness of 1 m to 25 m.

또한, 본 발명은 광학 필름의 적어도 한 면에 상기 점착제 조성물을 가교시킨 점착제층이 적층되어 이루어지는 것을 특징으로 하는 점착제층 부착 광학 필름을 제공한다. The present invention also provides an optical film with a pressure-sensitive adhesive layer, wherein a pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition on at least one surface of the optical film is laminated.

또한, 본 발명은 편광판의 한쪽 면에 상기 점착제 조성물을 가교시킨 점착제층이 적층되어 이루어지는 것을 특징으로 하는 점착제층 부착 편광판을 제공한다. The present invention also provides a polarizing plate with a pressure-sensitive adhesive layer, wherein a pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition on one side of the polarizing plate is laminated.

또한, 본 발명은 상기 점착제층 부착 편광판이 사용되고 있는 것을 특징으로 하는 액정 패널을 제공한다. Further, the present invention provides a liquid crystal panel characterized in that the polarizer with a pressure-sensitive adhesive layer is used.

또한, 본 발명은 상기 점착제층 부착 편광판이 사용되고 있는 것을 특징으로 하는 인셀형 액정 패널을 제공한다. Further, the present invention provides an in-cell liquid crystal panel characterized in that the polarizer with a pressure-sensitive adhesive layer is used.

본 발명에 의하면, 점착제층의 표면 저항율이 종래 기술에서는 달성할 수 없는 2.0×10+9Ω/□ 이하의 지극히 우수한 대전 방지 성능을 갖고, 또한 내구성을 저해하지 않는 점착제 조성물 및 이를 사용한 점착 필름을 제공할 수 있다.INDUSTRIAL APPLICABILITY According to the present invention, there is provided a pressure-sensitive adhesive composition which has an extremely excellent antistatic property of not higher than 2.0 x 10 < -9 > .

이하, 바람직한 실시형태를 기초로 본 발명을 설명한다. Hereinafter, the present invention will be described based on preferred embodiments.

본 실시형태의 점착제 조성물은 아크릴계 폴리머와, 대전 방지제와, 가교제를 함유하는 점착제 조성물로서, 상기 아크릴계 폴리머가 (A) n-부틸아크릴레이트와, (B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종과, (C) 수산기 및/또는 카르복실기를 함유하는 공중합성 비닐 모노머의 적어도 1종과, (D) 방향족기를 함유하는 공중합성 비닐 모노머의 적어도 1종을 공중합시킨 공중합체의 중량 평균 분자량이 100∼300만인 아크릴계 폴리머이며, 상기 (E) 대전 방지제로서 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제를 상기 아크릴계 폴리머의 100중량부에 대해 15중량부 초과 40중량부 이하의 비율로 함유하여 이루어지고, 상기 (F) 가교제로서 3관능 이상의 이소시아네이트 화합물, 2관능 이상의 에폭시 화합물로 이루어지는 군에서 선택된 적어도 1종 이상의 가교제를 함유하여 이루어지고, 상기 점착제 조성물이 (G) 에폭시기, 메르캅토기, 산무수물기에서 선택된 적어도 1종 이상의 관능기를 함유하는 모노머 타입 또는 올리고머 타입의 실란 커플링제를 추가로 함유하여 이루어지고, 상기 점착제 조성물을 가교시킨 점착제층의 표면 저항율이 2.0×10+9Ω/□ 이하이며, 상기 점착제층을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 또는 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 상기 점착제층의 표면에 상기 대전 방지제가 석출되어 있지 않는 것을 특징으로 한다. The pressure-sensitive adhesive composition of the present embodiment is a pressure-sensitive adhesive composition containing an acrylic polymer, an antistatic agent, and a crosslinking agent, wherein the acrylic polymer comprises (A) n-butyl acrylate, (B) at least one selected from the group consisting of n-butyl methacrylate and methyl acrylate, (C) at least one copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group, (D) (E) an ammonium-based antistatic agent having a fluorine group-containing anion as the antistatic agent (E) is added to 100 parts by weight of the acryl-based polymer (B) at a ratio of not less than 15 parts by weight and not more than 40 parts by weight based on 100 parts by weight of the (B) (G) a monomer containing at least one functional group selected from an epoxy group, a mercapto group and an acid anhydride group, wherein the pressure-sensitive adhesive composition contains at least one crosslinking agent selected from the group consisting of an epoxy compound, Type or oligomer type silane coupling agent, wherein the pressure-sensitive adhesive layer crosslinked with the pressure-sensitive adhesive composition has a surface resistivity of 2.0 x 10 < +9 & , Or the antistatic agent is not precipitated on the surface of the pressure-sensitive adhesive layer after the pressure-sensitive adhesive layer is provided in a durability test under a test environment of 60 캜 x 90% RH x 750 hr .

(A) n-부틸아크릴레이트 및 (B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종은 모두 알킬(메타)아크릴레이트 모노머에 해당한다. 본 실시형태의 점착제 조성물은 아크릴계 폴리머를 구성하는 알킬(메타)아크릴레이트의 모노머를 특정 2종 이상인 (A) 및 (B)의 조합으로 하는 것이 바람직하다. At least one member selected from the group consisting of (A) n-butyl acrylate and (B) t-butyl acrylate, isobutyl acrylate, n-butyl methacrylate and methyl acrylate is an alkyl (meth) acrylate monomer . The pressure-sensitive adhesive composition of the present embodiment is preferably a combination of (A) and (B) of two or more specific monomers of alkyl (meth) acrylate constituting the acrylic polymer.

본 실시형태의 아크릴계 폴리머는 (A) n-부틸아크릴레이트를 주체로 하고, 예를 들면, 아크릴계 폴리머의 100중량부에 대해 (A) n-부틸아크릴레이트를 40∼89중량부의 비율로 함유하여 이루어지는 것이 바람직하다. 또한, 아크릴계 폴리머가 (A) n-부틸아크릴레이트 이외의 알킬(메타)아크릴레이트 모노머로서 (B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종 이상의 합계를 5∼40중량부의 비율로 함유하여 이루어지는 것이 바람직하다. 또한 (A)와 (B)의 비율((A)／(B))이 중량비로서 1.0∼17.8인 것이 바람직하다. The acrylic polymer of the present embodiment mainly comprises (A) n-butyl acrylate and contains, for example, 40 to 89 parts by weight of (A) n-butyl acrylate per 100 parts by weight of the acrylic polymer . In the case where the acrylic polymer is an alkyl (meth) acrylate monomer other than (A) n-butyl acrylate, (B) a group consisting of t-butyl acrylate, isobutyl acrylate, n-butyl methacrylate and methyl acrylate In a proportion of 5 to 40 parts by weight. Further, it is preferable that the ratio of (A) to (B) ((A) / (B)) is 1.0 to 17.8 as a weight ratio.

(C) 수산기 및/또는 카르복실기를 함유하는 공중합성 비닐 모노머로는, 수산기를 함유하는 공중합 가능한 모노머(히드록실기 함유 모노머) 및 카르복실기를 함유하는 공중합 가능한 모노머(카르복실기 함유 모노머)로 이루어지는 군에서 선택된 적어도 1종 이상을 들 수 있다. 즉, 히드록실기 함유 모노머, 또는 카르복실기 함유 모노머 중 어느 하나만을 선택하여 공중합시켜도 되고, 히드록실기 함유 모노머 및 카르복실기 함유 모노머의 양쪽 모두를 공중합시켜도 된다. (C) a copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group is preferably selected from the group consisting of a copolymerizable monomer containing a hydroxyl group (a hydroxyl group-containing monomer) and a copolymerizable monomer containing a carboxyl group (a carboxyl group-containing monomer) At least one of them may be mentioned. That is, either one of the hydroxyl group-containing monomer and the carboxyl group-containing monomer may be selected and copolymerized, or both the hydroxyl group-containing monomer and the carboxyl group-containing monomer may be copolymerized.

히드록실기 함유 모노머로는, 예를 들면, 8-히드록시옥틸(메타)아크릴레이트, 6-히드록시헥실(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 2-히드록시에틸(메타)아크릴레이트 등의 히드록시알킬(메타)아크릴레이트류나, N-히드록시(메타)아크릴아미드, N-히드록시메틸(메타)아크릴아미드, N-히드록시에틸(메타)아크릴아미드 등의 히드록실기 함유 (메타)아크릴아미드류 등의 적어도 1종 이상을 들 수 있다. Examples of the hydroxyl group-containing monomer include 8-hydroxyoctyl (meth) acrylate, 6-hydroxyhexyl (meth) acrylate, 4-hydroxybutyl (Meth) acrylate, N-hydroxy (meth) acrylamide, N-hydroxymethyl (meth) acrylamide and N-hydroxyethyl Hydroxyl group-containing (meth) acrylamides, and the like.

또한, 본 실시형태에 따른 점착제 조성물에 함유시키는 히드록실기 함유 모노머는, 얻어지는 점착제층이 투명 도전성 필름의 ITO 표면 등의 부식되기 쉬운 피착체에 대한 부식성에 영향을 주는 카르복실기 함유 모노머의 함유량을 줄이기 위한 공중합성 모노머로서 사용할 수 있다. 이 때문에, 히드록실기 함유 모노머는 점착제층의 점착력을 향상시키고 또한 부식성을 저감시키는 것에 유용할 수 있다. 본 실시형태의 점착제 조성물에 함유시키는 히드록실기 함유 모노머의 비율은 아크릴계 폴리머의 100중량부에 대해 0.1∼5.0중량부의 비율인 것이 바람직하고, 0.1∼4.4중량부의 비율인 것이 보다 바람직하고, 0.1∼3.8중량부의 비율인 것이 특히 바람직하다. In addition, the hydroxyl group-containing monomer to be contained in the pressure-sensitive adhesive composition according to the present embodiment can be obtained by reducing the content of the carboxyl group-containing monomer which affects the corrosiveness of an adherend which is likely to corrode, such as the ITO surface of the transparent conductive film Can be used. Therefore, the hydroxyl group-containing monomer can be useful for improving the adhesive strength of the pressure-sensitive adhesive layer and also for reducing the corrosiveness. The ratio of the hydroxyl group-containing monomer to be contained in the pressure-sensitive adhesive composition of the present embodiment is preferably 0.1 to 5.0 parts by weight, more preferably 0.1 to 4.4 parts by weight, Particularly preferably 3.8 parts by weight.

카르복실기 함유 모노머로는, 예를 들면, (메타)아크릴산, 카르복시에틸(메타)아크릴레이트, 카르복시펜틸(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸헥사히드로프탈산, 2-(메타)아크릴로일옥시프로필헥사히드로프탈산, 2-(메타)아크릴로일옥시에틸프탈산, 2-(메타)아크릴로일옥시에틸숙신산, 2-(메타)아크릴로일옥시에틸말레산, 카르복시폴리카프로락톤모노(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸테트라히드로프탈산 등의 적어도 1종 이상을 들 수 있다. Examples of the carboxyl group-containing monomer include (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, 2- (meth) acryloyloxyethylhexahydrophthalic acid, 2- (Meth) acryloyloxyethylmaleic acid, 2- (meth) acryloyloxyethylphthalic acid, 2- (meth) acryloyloxyethylsuccinic acid, 2- (meth) acryloyloxyethylmaleic acid, carboxypolycaprolactone Mono (meth) acrylate, 2- (meth) acryloyloxyethyltetrahydrophthalic acid, and the like.

또한, 본 실시형태에 따른 점착제 조성물에 함유시키는 카르복실기 함유 모노머는, 얻어지는 점착제층에 대해 필요한 응집력을 부여시킬 수 있다. 본 실시형태에 따른 점착제 조성물에 있어서의 카르복실기 함유 모노머의 비율은, 아크릴계 폴리머의 100중량부에 대해 0∼5.0중량부인(카르복실기 함유 모노머를 공중합시키지 않는 경우도 허용된다) 것이 바람직하고, 카르복실기 함유 모노머를 공중합시키는 경우에는, 0.01∼5.0중량부의 비율인 것이 보다 바람직하고, 0.01∼3.3중량부의 비율인 것이 특히 바람직하고, 0.01∼2.8중량부의 비율인 것이 가장 바람직하다. Further, the carboxyl group-containing monomer contained in the pressure-sensitive adhesive composition according to the present embodiment can impart necessary cohesive force to the pressure-sensitive adhesive layer to be obtained. The proportion of the carboxyl group-containing monomer in the pressure-sensitive adhesive composition according to the present embodiment is preferably 0 to 5.0 parts by weight based on 100 parts by weight of the acrylic polymer (the case where the carboxyl group-containing monomer is not copolymerized) More preferably 0.01 to 3.3 parts by weight, and most preferably 0.01 to 2.8 parts by weight.

(D) 방향족기를 함유하는 공중합성 비닐 모노머로는, 예를 들면, 벤질(메타)아크릴레이트, 나프틸(메타)아크릴레이트, 페녹시에틸(메타)아크릴레이트, 페녹시부틸(메타)아크릴레이트, 2-(1-나프틸옥시)에틸(메타)아크릴레이트, 2-(2-나프틸옥시)에틸(메타)아크릴레이트, 6-(1-나프틸옥시)헥실(메타)아크릴레이트, 6-(2-나프틸옥시)헥실(메타)아크릴레이트, 8-(1-나프틸옥시)옥틸(메타)아크릴레이트, 8-(2-나프틸옥시)옥틸(메타)아크릴레이트 등의 적어도 1종 이상을 들 수 있다. (D) 방향족기를 함유하는 공중합성 비닐 모노머로서 방향족기를 함유하는 (메타)아크릴레이트 모노머를 함유하는 경우에는, (A) 및 (B)의 조합으로 이루어지는 알킬(메타)아크릴레이트 모노머와의 공중합성이 우수하기 때문에 바람직하다. Examples of the copolymerizable vinyl monomer containing (D) an aromatic group include benzyl (meth) acrylate, naphthyl (meth) acrylate, phenoxyethyl (meth) acrylate, phenoxybutyl (Meth) acrylate, 6 (1-naphthyloxy) ethyl (meth) acrylate, 2- At least one (meth) acrylate such as - (2-naphthyloxy) hexyl (meth) acrylate, 8- (1-naphthyloxy) More than species. (Meth) acrylate monomer containing an aromatic group as the copolymerizable vinyl monomer containing (D) an aromatic group, the copolymerization with the alkyl (meth) acrylate monomer comprising the combination of (A) and (B) Is preferable.

굴절률이 높은 점착제층을 얻기 위해서는 본 실시형태에 따른 점착제 조성물에 방향족기를 함유하는 (메타)아크릴레이트 모노머의 적어도 1종 이상을 배합하는 것이 바람직하다. 이들 방향족기를 함유하는 (메타)아크릴레이트 모노머를 아크릴계 폴리머에 공중합시킴으로써, 얻어지는 점착제층의 굴절률을 상승시켜 조정할 수 있고, 광학 부재 간의 굴절률 차이를 적게 하여 전반사를 저감시킴으로써, 전광선 투과율을 향상시킬 수 있다. 본 실시형태에 따른 점착제 조성물에 있어서, 방향족기를 함유하는 (메타)아크릴레이트 모노머는 아크릴계 폴리머의 100중량부에 대해 5∼30중량부의 비율로 함유시키는 것이 바람직하고, 6∼28중량부의 비율로 함유시키는 것이 보다 바람직하고, 6∼24중량부의 비율로 함유시키는 것이 특히 바람직하다. In order to obtain a pressure-sensitive adhesive layer having a high refractive index, it is preferable to blend at least one or more (meth) acrylate monomers containing an aromatic group in the pressure-sensitive adhesive composition according to the present embodiment. By copolymerizing these (meth) acrylate monomers containing an aromatic group with an acrylic polymer, the refractive index of the resulting pressure-sensitive adhesive layer can be adjusted and adjusted, and the difference in refractive index between the optical members can be reduced to reduce total reflection, thereby improving the total light transmittance . In the pressure-sensitive adhesive composition according to the present embodiment, the (meth) acrylate monomer containing an aromatic group is preferably contained in an amount of 5 to 30 parts by weight based on 100 parts by weight of the acrylic polymer, More preferably from 6 to 24 parts by weight.

본 실시형태에 따른 점착제 조성물에 함유시키는 아크릴계 폴리머의 제조 방법은 특별히 한정되는 것은 아니며, 용액 중합법, 유화 중합법 등 적절히 공지의 중합 방법이 사용 가능하다. 아크릴계 폴리머의 공중합체의 중량 평균 분자량은 100∼300만인 것이 바람직하다. The method of producing the acrylic polymer to be contained in the pressure-sensitive adhesive composition according to the present embodiment is not particularly limited, and a well-known polymerization method such as a solution polymerization method and an emulsion polymerization method can be used. The weight average molecular weight of the copolymer of the acrylic polymer is preferably from 100 to 3,000,000.

본 실시형태에 따른 점착제 조성물은 대전 방지 성능을 얻기 위해 (E) 대전 방지제를 함유한다. (E) 대전 방지제로서 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제를 아크릴계 폴리머의 100중량부에 대해 15중량부 초과 40중량부 이하의 비율로 함유하여 이루어지는 것이 바람직하고, 16∼40중량부의 비율로 함유하여 이루어지는 것이 보다 바람직하고, 16∼38중량부의 비율로 함유하여 이루어지는 것이 특히 바람직하다. 이 대전 방지제는 플루오로기 함유 음이온과 암모늄 양이온으로 이루어지는 이온성 화합물이다. 이 이온성 화합물은 융점이 25℃ 이상인 이온성 화합물이며, 상온(예를 들면 25℃)에서 고체인 것이 바람직하다. 또한, 이 이온성 화합물은 온도 25℃에서 고체인, 융점이 25℃∼80℃인 이온성 화합물인 것이 보다 바람직하다. The pressure-sensitive adhesive composition according to the present embodiment contains (E) an antistatic agent to obtain an antistatic property. (E) an antistatic agent containing an ammonium-based antistatic agent having a fluorine group-containing anion in an amount of not less than 15 parts by weight and not more than 40 parts by weight per 100 parts by weight of the acrylic polymer, More preferably 16 to 38 parts by weight, based on the total weight of the composition. This antistatic agent is an ionic compound comprising a fluoro group-containing anion and an ammonium cation. The ionic compound is an ionic compound having a melting point of 25 캜 or higher, and is preferably a solid at ordinary temperature (for example, 25 캜). The ionic compound is more preferably an ionic compound having a melting point of 25 占 폚 to 80 占 폚 which is a solid at a temperature of 25 占 폚.

(E) 대전 방지제에 함유되는 플루오로기 함유 음이온으로는 무기 또는 유기의 플루오로기 함유 음이온을 들 수 있다. 여기서 플루오로기란, 음이온을 구성하는 다른 원자에 결합된 불소 원자를 의미한다. 무기의 플루오로기 함유 음이온으로는, PF6 -, AsF6 -, SbF6 -, BF4 -, AlF4 -, (FSO2)2N-, FSO3 - 등을 들 수 있다. 유기의 플루오로기 함유 음이온으로는 플루오로기 함유의 술포네이트 음이온(RSO3 -), 플루오로기 함유의 카르복실레이트 음이온(RCOO-), 플루오로기 함유의 알콕시드 또는 페녹시드 음이온(RO-), 플루오로기 함유의 유기 이미드 음이온(R2N-), 플루오로기 함유의 메티드(R3C-) 음이온, 플루오로기 함유의 유기 보레이트(R4B-) 음이온 등으로, R이 적어도 1 이상으로서 플루오로기 함유의 유기기를 갖는 음이온을 들 수 있다. 유기기로는 알킬기, 알콕시기, 방향족기(아릴기, 아르알킬기 등), 알킬카르보닐기, 방향족 카르보닐기, 알킬술포닐기, 방향족 술포닐기 등의 1종 이상을 들 수 있다. 음이온이 2 이상의 R을 갖는 경우에는, 2 이상의 R 사이에 결합하여 환상으로 되어도 된다. 그 중에서도, 펜타플루오로벤젠술포네이트, 헥사플루오로포스페이트, 비스(트리플루오로메탄술포닐)이미드, 비스(플루오로술포닐)이미드, 트리플레이트로 이루어지는 군에서 선택된 1종인 것이 바람직하다. Examples of the fluoro group-containing anion contained in the antistatic agent (E) include inorganic or organic fluoro group-containing anions. Here, the fluoro group means a fluorine atom bonded to another atom constituting the anion. As an anion group-containing fluoropolymer of the weapon, PF 6 -, AsF 6 - , SbF 6 - , BF 4 - , AlF 4 - , (FSO 2 ) 2 N - , FSO 3 - and the like. Examples of the organic fluoro group-containing anion include a fluoro group-containing sulfonate anion (RSO 3 - ), a fluoro group-containing carboxylate anion (RCOO - ), a fluoro group-containing alkoxide or a phenoxide anion a) an anion such as -), organic imide anion group-containing fluoropolymer (R 2 N -), methide of group-containing fluoropolymer (R 3 C -) anions, organic borates of group-containing fluoropolymer (R 4 B , And an anion having at least one R group and a fluoro group-containing organic group. Examples of the organic group include an alkyl group, an alkoxy group, an aromatic group (aryl group, aralkyl group, etc.), an alkylcarbonyl group, an aromatic carbonyl group, an alkylsulfonyl group and an aromatic sulfonyl group. When the anion has 2 or more R, it may be bonded between two or more R to form a ring. Among them, one selected from the group consisting of pentafluorobenzene sulfonate, hexafluorophosphate, bis (trifluoromethanesulfonyl) imide, bis (fluorosulfonyl) imide and triflate is preferable.

(E) 대전 방지제에 함유되는 암모늄 양이온으로는 1∼4의 유기기를 갖는 유기 암모늄 양이온을 들 수 있고, 특히 4급 암모늄 양이온(R4N+)이 바람직하다. R로는 비환상 또는 환상의 알킬기, 방향족기(아릴기, 아르알킬기 등) 등의 탄화수소기를 들 수 있다. 양이온이 2 이상의 R을 갖는 경우에는, 2 이상의 R 사이에 결합하여 환상으로 되어도 된다. Examples of the ammonium cation to be contained in the antistatic agent (E) include an organic ammonium cation having 1 to 4 organic groups, and a quaternary ammonium cation (R 4 N + ) is particularly preferred. R may be a hydrocarbon group such as a non-cyclic or cyclic alkyl group, an aromatic group (aryl group, aralkyl group, etc.). When the cation has two or more R's, they may be bonded to each other between two or more R's to form a ring.

본 실시형태에 따른 점착제 조성물은 (F) 가교제로서 3관능 이상의 이소시아네이트 화합물, 2관능 이상의 에폭시 화합물로 이루어지는 군에서 선택된 적어도 1종 이상의 가교제를 추가로 함유한다. (F) 가교제의 비율로는, 예를 들면, 아크릴계 폴리머의 100중량부에 대해 0.01∼5중량부의 비율을 들 수 있다. The pressure-sensitive adhesive composition according to the present embodiment further comprises (F) at least one crosslinking agent selected from the group consisting of an isocyanate compound having three or more functional groups and an epoxy compound having two or more functional groups as the crosslinking agent. The proportion of the crosslinking agent (F) is, for example, from 0.01 to 5 parts by weight based on 100 parts by weight of the acrylic polymer.

3관능 이상의 이소시아네이트 화합물로는, 예를 들면, 헥사메틸렌디이소시아네이트, 이소포론디이소시아네이트, 디페닐메탄디이소시아네이트, 톨릴렌디이소시아네이트, 자일릴렌디이소시아네이트 등의 디이소시아네이트류의 뷰렛 변성체나 이소시아누레이트 변성체, 트리메틸올프로판이나, 글리세린 등의 3가 이상의 폴리올과의 어덕트체 등을 들 수 있다. Examples of the trifunctional or higher isocyanate compound include biuret-modified products of diisocyanates such as hexamethylene diisocyanate, isophorone diisocyanate, diphenylmethane diisocyanate, tolylene diisocyanate and xylylene diisocyanate, And adducts with tri- or higher-valent polyols such as trimethylolpropane and glycerin.

2관능 이상의 에폭시 화합물로는 글리콜류의 디글리시딜에테르, 비스페놀류의 디글리시딜에테르, 트리올류의 트리글리시딜에테르, 디카르복실산의 디글리시딜에스테르, 디글리시딜 치환의 아민류, 테트라글리시딜 치환의 디아민류 등을 들 수 있다. Examples of the epoxy compound having two or more functional groups include diglycidyl ether of glycols, diglycidyl ether of bisphenol, triglycidyl ether of triol, diglycidyl ester of dicarboxylic acid, Amines, diamines of tetraglycidyl substitution, and the like.

본 실시형태에 따른 점착제 조성물은 (G) 실란 커플링제를 추가로 함유한다. (G) 실란 커플링제로는 1분자 중에 적어도 1개의 유기 관능기와, 적어도 1개의 가수 분해성기를 갖고, 상기 가수 분해성기가 규소 원자에 결합된 알콕시기 등인 화합물을 들 수 있다. (G) 실란 커플링제는 에폭시기, 메르캅토기, 산무수물기에서 선택된 적어도 1종 이상의 관능기를 함유한다. (G) 실란 커플링제는 모노머 타입 또는 올리고머 타입의 한쪽 또는 양쪽을 적어도 1종 이상 사용할 수 있다. 실란 커플링제의 비율은, 예를 들면, 아크릴계 폴리머의 100중량부에 대해 0.01∼0.5중량부를 들 수 있다. The pressure-sensitive adhesive composition according to the present embodiment further contains (G) a silane coupling agent. (G) The silane coupling agent includes a compound having at least one organic functional group and at least one hydrolysable group in one molecule, and the hydrolyzable group is an alkoxy group bonded to a silicon atom. (G) The silane coupling agent contains at least one or more functional groups selected from an epoxy group, a mercapto group and an acid anhydride group. (G) The silane coupling agent may use one or both of a monomer type and an oligomer type. The proportion of the silane coupling agent is, for example, 0.01 to 0.5 parts by weight based on 100 parts by weight of the acrylic polymer.

에폭시기를 갖는 실란 커플링제로는, 예를 들면, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필메틸디에톡시실란, 3-글리시독시프로필메틸디메톡시실란, 3-글리시독시프로필트리에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란, 2-(3,4-에폭시시클로헥실)에틸메틸디메톡시실란, 2-(3,4-에폭시시클로헥실)에틸메틸디에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리에톡시실란, 5,6-에폭시헥실트리메톡시실란, 5,6-에폭시헥실메틸디메톡시실란, 5,6-에폭시헥실메틸디에톡시실란, 5,6-에폭시헥실트리에톡시실란 등을 들 수 있다. 메르캅토기를 갖는 실란 커플링제로는, 예를 들면, 3-메르캅토프로필메틸디메톡시실란, 3-메르캅토프로필트리메톡시실란, 3-메르캅토프로필메틸디에톡시실란, 3-메르캅토프로필트리에톡시실란 등을 들 수 있다. 산무수물기를 갖는 실란 커플링제로는, 예를 들면, 3-트리메톡시실릴프로필숙신산무수물, 3-트리에톡시실릴프로필숙신산무수물 등을 들 수 있다. 또한, 올리고머화한 알콕시 올리고머(실리콘알콕시올리고머) 등도 실란 커플링제로서 사용할 수 있다. Examples of the silane coupling agent having an epoxy group include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 3- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 2- (3,4-epoxycyclohexyl) ethylmethyldimethoxysilane, 2- (3,4-epoxycyclohexyl) Hexyl) ethylmethyldiethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltriethoxysilane, 5,6-epoxyhexyltrimethoxysilane, 5,6-epoxyhexylmethyldimethoxysilane, 5,6 -Epoxyhexylmethyldiethoxysilane, 5,6-epoxyhexyltriethoxysilane, and the like. Examples of the silane coupling agent having a mercapto group include 3-mercaptopropylmethyldimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-mercaptopropylmethyldiethoxysilane, 3-mercaptopropylsilane, Triethoxysilane, and the like. Examples of the silane coupling agent having an acid anhydride group include 3-trimethoxysilylpropylsuccinic anhydride and 3-triethoxysilylpropylsuccinic anhydride. In addition, oligomerized alkoxy oligomers (silicon alkoxy oligomers) and the like can also be used as a silane coupling agent.

본 실시형태의 점착제 조성물은 임의의 성분으로서 산화 방지제, 계면 활성제, 경화 촉진제, 가소제, 충전제, 가교 촉매, 가교 지연제, 경화 지연제, 가공 조제, 노화 방지제 등의 공지의 첨가제를 적절히 배합할 수 있다. 이들은 단독으로 사용해도 되고 혹은 2종 이상 병용하여 사용해도 된다. The pressure-sensitive adhesive composition of the present embodiment can appropriately contain, as optional components, known additives such as an antioxidant, a surfactant, a curing accelerator, a plasticizer, a filler, a crosslinking catalyst, a crosslinking retarder, a curing retarder, a processing aid, have. These may be used alone or in combination of two or more.

본 실시형태의 점착제 조성물을 가교시킨 점착제층의 표면 저항율은, 2.0×10+9Ω/□ 이하인 것이 바람직하고, 1.0×10+9Ω/□ 이하인 것이 보다 바람직하고, 8.0×10+8Ω/□ 이하인 것이 특히 바람직하다. 이 점착제층은 초기 표면 저항율 및 내구성 시험 후의 표면 저항율이 모두 2.0×10+9Ω/□ 이하인 것이 바람직하고, 1.0×10+9Ω/□ 이하인 것이 보다 바람직하고, 8.0×10+8Ω/□ 이하인 것이 특히 바람직하다. 여기서 초기 표면 저항율이란, 점착제층을 내구성 시험에 제공하기 전의 표면 저항율이다. 또한, 내구성 시험 후의 표면 저항율이란, 점착제층을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후의 표면 저항율이다. 여기서, 85℃×750hr의 시험 환경은 dry 조건이어도 된다. Surface resistivity of the pressure-sensitive adhesive layer in which a crosslinked pressure-sensitive adhesive composition of the present embodiment, 2.0 × 10 +9 Ω / □ or less is preferable, and, 1.0 × 10 +9 Ω / □ or less and is more preferably, 8.0 × 10 +8 Ω / □ or less. The pressure-sensitive adhesive layer preferably has an initial surface resistivity and a surface resistivity after the durability test of 2.0 × 10 + 9 Ω / □ or less, more preferably 1.0 × 10 + 9 Ω / □ or less and 8.0 × 10 + Or less. Here, the initial surface resistivity is the surface resistivity before the pressure-sensitive adhesive layer is provided in the durability test. The surface resistivity after the durability test is a surface resistivity after providing the pressure-sensitive adhesive layer in a durability test under a test environment of 85 캜 x 750 hr. Here, the test environment of 85 占 폚 占 750 hr may be a dry condition.

본 실시형태의 점착제 조성물을 가교시킨 점착제층은 85℃×750hr의 시험 환경하에 있어서의 내구성 시험 및 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 점착제층의 표면에 (E) 대전 방지제가 석출되어 있지 않는 것이 된다. 여기서, 85℃×750hr의 시험 환경은 dry 조건이어도 된다. The pressure-sensitive adhesive layer obtained by crosslinking the pressure-sensitive adhesive composition of the present embodiment was subjected to a durability test under a test environment of 85 占 폚 占 750 hours and a durability test under a test environment of 60 占 폚 占 90% RH 占 占 750 hours, The antistatic agent (E) is not precipitated. Here, the test environment of 85 占 폚 占 750 hr may be a dry condition.

본 실시형태의 점착제 조성물에 있어서의 (E) 대전 방지제의 석출 방지 성능은 동일한 점착제 조성물을 가교시킨 점착제층의 샘플을 2 이상 제작하고, 1개의 샘플을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, (E) 대전 방지제가 석출되지 않고, 또한 다른 샘플을 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, (E) 대전 방지제가 석출되어 있지 않는 것이어도 된다. In the pressure-sensitive adhesive composition of the present embodiment, two or more samples of the pressure-sensitive adhesive layer obtained by crosslinking the same pressure-sensitive adhesive composition were prepared, and one sample was durability under a test environment of 85 ° C. × 750 hr (E) an antistatic agent is not precipitated, and another sample is subjected to a durability test under a test environment of 60 ° C × 90% RH × 750 hr, (E) the antistatic agent is not precipitated It may not be.

본 실시형태의 점착제 조성물을 가교시킨 점착제층은 두께 20㎛의 점착제층을 개재하여 총 두께 80㎛의 편광판을 무알칼리 유리에 첩합하였을 때, 점착제층의 무알칼리 유리에 대한 점착력이 1.0∼6.0N/25㎜인 것이 바람직하다. The pressure-sensitive adhesive layer crosslinked with the pressure-sensitive adhesive composition of the present embodiment had a pressure-sensitive adhesive force of 1.0 to 6.0 N / m < 2 > / 25 mm.

또한, 두께 20㎛의 점착제층을 개재하여 10㎝ 각의 총 두께 80㎛의 편광판을 무알칼리 유리에 첩합하여 이루어지는 시험편을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험 및 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 발포 및 박리가 없는 것이 바람직하다. A test piece made of a 10-cm square polarizing plate having a total thickness of 80 占 퐉 laminated to an alkali-free glass through a pressure-sensitive adhesive layer having a thickness of 20 占 퐉 was durability tested under a test environment of 85 占 폚 for 750 hours, X 750 hours, it is preferable that there is no foaming and peeling.

본 실시형태의 점착제 조성물에 있어서의 발포 및 박리가 없는 성능은, 동일한 점착제 조성물을 이용해서 제작한 시험편을 2 이상 제작하고, 1개의 시험편을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 발포 및 박리가 없고, 또한 다른 시험편을 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 발포 및 박리가 없는 것이어도 된다. The performance without foaming and peeling in the pressure-sensitive adhesive composition of this embodiment can be obtained by preparing two or more test pieces prepared using the same pressure-sensitive adhesive composition and providing one test piece for the durability test under the test environment of 85 ° C. × 750 hr The test piece may be free from foaming and peeling, and may be free from foaming and peeling after another test piece is subjected to a durability test under a test environment of 60 캜 x 90% RH x 750 hr.

본 실시형태에 따른 점착제층은 본 실시형태의 점착제 조성물을 수지 필름이나 이형 필름 등의 기재에 도포한 후, 점착제 조성물을 가교함으로써 얻을 수 있다. The pressure-sensitive adhesive layer according to the present embodiment can be obtained by applying the pressure-sensitive adhesive composition of the present embodiment to a substrate such as a resin film or a release film, and then crosslinking the pressure-sensitive adhesive composition.

본 실시형태에 따른 점착제층을 광학 부재의 층간의 첩합 등에 사용하는 경우, 점착제층과 광학 부재의 계면에서의 광선의 반사를 저감시키기 위해 굴절률의 차이가 가능한 한 작은 것이 바람직하다. 이 때문에, 점착제층의 굴절률이 1.47∼1.50인 것이 바람직하다. When the pressure-sensitive adhesive layer according to the present embodiment is used for bonding the layers of the optical member or the like, it is preferable that the refractive index difference be as small as possible in order to reduce reflection of light rays at the interface between the pressure-sensitive adhesive layer and the optical member. Therefore, the refractive index of the pressure-sensitive adhesive layer is preferably 1.47 to 1.50.

본 실시형태에 따른 점착 필름은 본 실시형태에 따른 점착제층을 수지 필름이나 이형 필름 등의 기재의 한쪽 면 위에 형성함으로써 제조할 수 있다. 기재가 되는 수지 필름이나 이형 필름(세퍼레이터)으로는 폴리에스테르 필름 등의 수지 필름 등을 사용할 수 있다. 이형 필름에는 점착제층의 점착면과 합해지는 측의 면에 실리콘계, 불소계의 이형제 등에 의해 이형 처리가 실시되어도 된다. 기재가 되는 수지 필름에는 수지 필름의 점착제층이 형성된 측과는 반대면에 실리콘계, 불소계의 이형제나 코트제, 실리카 미립자 등에 의한 방오 처리, 대전 방지제의 도포나 혼입 등에 의한 대전 방지 처리를 실시할 수 있다. 점착제층의 두께로는, 예를 들면, 1㎛∼25㎛의 두께를 들 수 있다. The adhesive film according to the present embodiment can be produced by forming the pressure-sensitive adhesive layer according to the present embodiment on one side of a substrate such as a resin film or a release film. As a resin film or a release film (separator) to be a substrate, a resin film such as a polyester film and the like can be used. The releasing film may be subjected to releasing treatment by a silicone-based or fluorine-releasing agent or the like on the side of the pressure-sensitive adhesive layer to be combined with the pressure-sensitive adhesive surface. Antistatic treatment with an antifouling treatment with a silicone type or fluorine type releasing agent, a coating agent, fine silica particles or the like, application of an antistatic agent, or the like can be carried out on the resin film of the resin film as the base material opposite to the side on which the pressure- have. The thickness of the pressure-sensitive adhesive layer is, for example, 1 占 퐉 to 25 占 퐉.

1개의 점착제층의 양면에 각각 이형 필름의 이형 처리가 실시된 면을 맞춤으로써, 「이형 필름/점착제층/이형 필름」의 구성으로 할 수도 있다. 이 경우, 양측의 이형 필름을 순차적으로, 혹은 동시에 박리하여 점착면을 표출시킴으로써, 광학 필름 등의 광학 부재와 첩합 가능하게 된다. 광학 필름으로는 편광 필름, 위상차 필름, 반사 방지 필름, 방현(안티글레어) 필름, 자외선 흡수 필름, 적외선 흡수 필름, 광학 보상 필름, 휘도 향상 필름 등을 들 수 있다. 광학 부재가 적용되는 기기로는 액정 패널, 유기 EL 패널, 터치 패널, 인셀형 액정 패널 등을 들 수 있다. The release film, the pressure-sensitive adhesive layer, and the release film may be formed on both surfaces of one pressure-sensitive adhesive layer by aligning the surfaces subjected to the release treatment of the release film. In this case, the releasing films on both sides are sequentially or simultaneously peeled off to expose the adhesive surface, so that the releasing film can be bonded to an optical member such as an optical film. Examples of the optical film include a polarizing film, a retardation film, an antireflection film, an antiglare film, an ultraviolet absorbing film, an infrared absorbing film, an optical compensating film, and a brightness improving film. Examples of the device to which the optical member is applied include a liquid crystal panel, an organic EL panel, a touch panel, and an in-cell type liquid crystal panel.

본 실시형태의 점착 필름은 편광판용 점착 필름으로서 바람직하다. 특히, 편광판과 인셀 패널의 첩합에 사용되어도 된다. 또한, 상기 광학 필름의 적어도 한 면에 상기 점착제층이 적층되어 이루어지는 점착제층 부착 광학 필름으로 할 수 있다. 또한, 편광판의 한쪽 면에 상기 점착 필름을 사용함으로써, 점착제층 부착 편광판을 제공할 수 있다. 상기 점착제층 부착 편광판을 사용하여, 인셀형 액정 패널 등의 액정 패널을 제공할 수 있다. The pressure-sensitive adhesive film of the present embodiment is preferable as a pressure-sensitive adhesive film for a polarizing plate. In particular, it may be used for bonding the polarizing plate and the insulator panel. Further, an optical film with a pressure-sensitive adhesive layer in which the pressure-sensitive adhesive layer is laminated on at least one surface of the optical film may be used. Further, by using the above-mentioned pressure-sensitive adhesive film on one surface of the polarizing plate, a polarizing plate with a pressure-sensitive adhesive layer can be provided. A polarizing plate with a pressure-sensitive adhesive layer can be used to provide a liquid crystal panel such as a phosphor cell type liquid crystal panel.

이러한 점착제층 부착 광학 필름의 적층 구성의 구체예로는, 「이형 필름/점착제층/광학 필름」, 「이형 필름/점착제층/광학 필름/점착제층/이형 필름」, 「광학 필름/점착제층/광학 필름」, 「광학 필름/점착제층」, 「점착제층/광학 필름/점착제층」 등을 들 수 있다. 점착제층 부착 편광판의 적층 구성의 구체예로서, 「이형 필름/점착제층/편광판」, 「이형 필름/점착제층/편광판/점착제층/이형 필름」, 「편광판/점착제층」, 「점착제층/편광판/점착제층」 등을 들 수 있다. 액정 패널 등의 부분 구조로서, 이들 점착제층 부착 광학 필름, 또는 점착제층 부착 편광판이 도입되어도 된다. Specific examples of the lamination structure of the optical film with a pressure-sensitive adhesive layer include "release film / pressure-sensitive adhesive layer / optical film", "release film / pressure-sensitive adhesive layer / optical film / pressure-sensitive adhesive layer / release film" Quot; optical film ", " optical film / pressure sensitive adhesive layer ", and " pressure sensitive adhesive layer / optical film / pressure sensitive adhesive layer " Sensitive adhesive layer / polarizer / polarizer / pressure-sensitive adhesive layer / release film "," polarizer / pressure-sensitive adhesive layer "," pressure-sensitive adhesive layer / polarizer plate " / Pressure-sensitive adhesive layer " As a partial structure such as a liquid crystal panel, an optical film with a pressure-sensitive adhesive layer or a polarizer with a pressure-sensitive adhesive layer may be introduced.

한편, 「이형 필름/점착제층/광학 필름」, 「이형 필름/점착제층/편광판」등과 같이, 이형 필름을 적층 구성에 포함되는 경우에는, 이형 필름을 박리한 후, 점착제층을 개재하여 광학 필름 또는 편광판이 피착체에 첩합된다. On the other hand, when the releasing film is included in the lamination structure, such as "releasing film / pressure-sensitive adhesive layer / optical film", "releasing film / pressure-sensitive adhesive layer / polarizing plate", the release film is peeled off, Or the polarizing plate is bonded to the adherend.

실시예Example

이하, 실시예에 의해 본 발명을 구체적으로 설명한다. Hereinafter, the present invention will be described in detail by way of examples.

＜아크릴계 폴리머의 제조＞ ≪ Preparation of acrylic polymer &

[실시예 1] [Example 1]

교반기, 온도계, 환류 냉각기 및 질소 도입관을 구비한 반응 장치에 질소 가스를 도입하여, 반응 장치 내의 공기를 질소 가스로 치환하였다. 그 후, 반응 장치에 n-부틸아크릴레이트 70중량부, n-부틸메타크릴레이트 15중량부, 8-히드록시옥틸아크릴레이트 2.0중량부, 벤질아크릴레이트 15중량부와 함께, 용제(초산에틸)를 첨가하였다. 그 후, 중합 개시제로서 아조비스이소부티로니트릴 0.1중량부를 2시간에 걸쳐 적하시키고, 65℃에서 6시간 반응시켜, 실시예 1에 사용하는 아크릴계 폴리머 용액을 얻었다. Nitrogen gas was introduced into a reactor equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen introduction tube to replace the air in the reactor with nitrogen gas. Subsequently, 70 parts by weight of n-butyl acrylate, 15 parts by weight of n-butyl methacrylate, 2.0 parts by weight of 8-hydroxyoctyl acrylate and 15 parts by weight of benzyl acrylate were mixed with a solvent (ethyl acetate) Was added. Thereafter, 0.1 part by weight of azobisisobutyronitrile as a polymerization initiator was added dropwise over 2 hours, and the mixture was reacted at 65 DEG C for 6 hours to obtain an acrylic polymer solution used in Example 1. [

[실시예 2∼6 및 비교예 1∼3] [Examples 2 to 6 and Comparative Examples 1 to 3]

모노머의 조성을 각각 표 1의 (A)∼(D)의 기재와 같이 하는 것 이외에는 상기 실시예 1과 동일하게 하여, 실시예 2∼6 및 비교예 1∼3에 사용하는 아크릴계 폴리머 용액을 얻었다. The acrylic polymer solution used in Examples 2 to 6 and Comparative Examples 1 to 3 was obtained in the same manner as in Example 1 except that the composition of the monomers was changed as shown in Table 1 (A) to (D).

한편, 특별히 측정 결과를 나타내지 않지만, 실시예 1∼6 및 비교예 1∼3의 아크릴계 폴리머 용액에 포함되는 공중합체의 중량 평균 분자량은 100∼300만의 범위 내이다. On the other hand, although the measurement results are not particularly shown, the weight average molecular weights of the copolymers contained in the acrylic polymer solutions of Examples 1 to 6 and Comparative Examples 1 to 3 are in the range of 100 to 3 million.

＜점착 필름의 제조＞ ≪ Preparation of pressure-sensitive adhesive film &

[실시예 1] [Example 1]

상기와 같이 제조한 실시예 1의 아크릴계 폴리머 용액에 대해, 시클로헥실트리메틸암모늄비스(트리플루오로메탄술포닐)이미드를 20중량부와, 가교제(D-110N)를 0.1중량부와, 실란 커플링제(X-12-967C)를 0.05중량부의 비율로 첨가하고 교반 혼합하여 실시예 1의 점착제 조성물을 얻었다.20 parts by weight of cyclohexyltrimethylammonium bis (trifluoromethanesulfonyl) imide, 0.1 part by weight of a cross-linking agent (D-110N), 0.1 part by weight of a silane coupling agent (X-12-967C) was added in a ratio of 0.05 part by weight, and the mixture was stirred and mixed to obtain the pressure-sensitive adhesive composition of Example 1.

이 점착제 조성물을 실리콘 수지 코트된 폴리에틸렌테레프탈레이트(PET) 필름으로 이루어지는 이형 필름 위에 건조 후의 점착제층의 두께가 20㎛이 되도록 도포한 후, 90℃로 건조함으로써 용제를 제거하였다. 그 후, 23℃, 50% RH의 분위기하에서 7일간 에이징함으로써, 점착제 조성물을 가교시킨 점착제층을 이형 필름의 한쪽 면 위에 갖고, 이형 필름/점착제층/이형 필름의 구성인 실시예 1의 점착 필름을 얻었다. This pressure-sensitive adhesive composition was coated on a releasing film made of a polyethylene terephthalate (PET) film coated with silicone resin so that the thickness of the pressure-sensitive adhesive layer after drying was 20 占 퐉 and dried at 90 占 폚 to remove the solvent. Thereafter, the pressure-sensitive adhesive layer obtained by crosslinking the pressure-sensitive adhesive composition on one side of the release film was aged under an atmosphere of 23 ° C and 50% RH for 7 days to obtain a pressure-sensitive adhesive film of Example 1 which is a constitution of a release film / pressure- ≪ / RTI >

[실시예 2∼6 및 비교예 1∼3] [Examples 2 to 6 and Comparative Examples 1 to 3]

첨가제의 조성을 각각 표 1의 (E)∼(G)의 기재와 같이 한 것 이외에는 상기 실시예 1의 점착 필름과 동일하게 하여, 실시예 2∼6 및 비교예 1∼3의 점착 필름을 얻었다. The pressure-sensitive adhesive films of Examples 2 to 6 and Comparative Examples 1 to 3 were obtained in the same manner as in the pressure-sensitive adhesive films of Example 1 except that the compositions of the additives were changed as shown in (E) to (G)

Figure pat00001
Figure pat00001

표 1에 있어서 각 성분의 약기호의 뒤에 붙인 수치는 중량부를 나타낸다. 이 중량부는 (A)와 (B)와 (D)의 합계를 100중량부로 하여 구해진다. 또한, 표 1에 사용한 각 성분의 약기호의 화합물명을 표 2에 나타낸다. IOA는 편의상 (B)에 포함시켰다. (C)는 수산기를 함유하는 모노머를 「(C)OH」, 카르복실기를 함유하는 모노머를 「(C)COOH」와 같이 분류하였다. In Table 1, numerical values after the weak symbols of each component represent weight parts. This weight portion is obtained by setting the total of (A), (B) and (D) to 100 parts by weight. Table 2 shows the compound names of the weak symbols of the respective components used in Table 1. IOA is included in (B) for convenience. (C), the monomer containing a hydroxyl group is classified as "(C) OH", and the monomer containing a carboxyl group is classified as "(C) COOH".

Figure pat00002
Figure pat00002

표 2에 있어서 코로네이트(등록 상표) L은 토소 주식회사의 상품명이며, D-110N은 미츠이 화학 주식회사의 상품명이고, TETRAD(등록 상표)-X는 미츠비시 가스 화학 주식회사의 상품명이다. 또한, TDI는 톨릴렌디이소시아네이트를 의미하며, TMP는 트리메틸올프로판을 의미하고, XDI는 자일릴렌디이소시아네이트를 의미한다. 또한, KBM-403, X-12-967C, X-41-1805, KBM-503은 모두 신에츠 화학 공업 주식회사의 상품명이다. In Table 2, Coronate (registered trademark) L is a trade name of Tosoh Corporation, D-110N is a trade name of Mitsui Chemicals, Inc., and TETRAD (trade name) -X is a trade name of Mitsubishi Gas Chemical Co., Also, TDI means tolylene diisocyanate, TMP means trimethylol propane, and XDI means xylylene diisocyanate. KBM-403, X-12-967C, X-41-1805 and KBM-503 are trade names of Shin-Etsu Chemical Co.,

＜시험 방법 및 평가＞ <Test Method and Evaluation>

실시예 1∼6 및 비교예 1∼3에 있어서의 점착 필름으로부터, 이형 필름(실리콘 수지 코트된 PET 필름)을 박리하여, 상기 점착 필름의 점착제층의 한쪽 면을 표출시켰다. 그 후, 두께 80㎛의 편광판(수지 필름)의 한쪽 면에, 상기 점착제층을 개재하여 상기 점착 필름을 첩합하여 이형 필름/점착제층/편광판의 구성인 점착제층 부착 편광판을 얻었다. A release film (PET film coated with a silicone resin) was peeled from the pressure-sensitive adhesive films of Examples 1 to 6 and Comparative Examples 1 to 3 to expose one side of the pressure-sensitive adhesive layer of the pressure-sensitive adhesive film. Thereafter, the pressure-sensitive adhesive film was bonded to one side of a polarizing plate (resin film) having a thickness of 80 占 퐉 with the pressure-sensitive adhesive layer interposed therebetween to obtain a polarizer with a pressure-sensitive adhesive layer constituting a releasing film / pressure-sensitive adhesive layer / polarizing plate.

＜점착력의 측정 방법＞ &Lt; Measurement method of adhesive force &gt;

상기에서 얻어진 점착제층 부착 편광판의 이형 필름을 박리하고, 무알칼리 유리(코닝사 제조 이글 XG(등록 상표))의 아세톤으로 세정한 면에 상기 점착제층을 개재하여 점착제층 부착 편광판을 압착 롤로 첩합하여 시험편을 작성하였다. 그 후, 당해 시험편을 50℃, 0.5MPa×20분간의 조건으로 오토클레이브 처리하였다. 그 후, 23℃×50% RH의 분위기하로 되돌리고, 1시간 경과 후의 점착제층 부착 편광판의 박리 강도를 인장 시험기에 의해 JIS Z0237 「점착 테이프·점착 시트 시험 방법」에 준거하여 측정하고, 180° 방향으로 0.3m/min의 속도로 박리했을 때의 박리 강도를 무알칼리 유리에 대한 점착제층의 점착력으로 하였다. The release film of the polarizing plate with a pressure-sensitive adhesive layer thus obtained was peeled off, and a polarizing plate with a pressure-sensitive adhesive layer was bonded to the surface of the glass plate cleaned with acetone of an alkali-free glass (Eagle XG (registered trademark) Respectively. Thereafter, the test piece was autoclaved under the conditions of 50 占 폚 and 0.5 MPa 占 20 minutes. Thereafter, the film was returned to an atmosphere of 23 ° C × 50% RH and the peel strength of the polarizing plate with a pressure-sensitive adhesive layer after 1 hour was measured by a tensile tester in accordance with JIS Z0237 "Test method for pressure-sensitive adhesive tape and pressure- At a speed of 0.3 m / min as the adhesive strength of the pressure-sensitive adhesive layer to the alkali-free glass.

＜표면 저항율의 측정 방법＞ &Lt; Method of measuring surface resistivity &

상기에서 얻어진 점착제층 부착 편광판에 대해 저항율계 하이레스터(등록 상표) UP-HT450(미츠비시 화학 애널리텍크 제조)을 이용해 점착제층의 표면 저항율 (Ω/□)을 측정하여 초기 표면 저항율을 구하였다. 동일한 점착제층 부착 편광판을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험을 한 후, 동일하게 표면 저항율을 측정하여 내구성 시험 후의 표면 저항율을 구하였다. The surface resistivity (? /?) Of the pressure-sensitive adhesive layer was measured for the polarizer with a pressure-sensitive adhesive layer obtained above using a resistivity meter Hirester (registered trademark) UP-HT450 (manufactured by Mitsubishi Chemical Analytek) to obtain an initial surface resistivity. After the durability test under the test environment of 85 占 폚 占 750 hr was carried out on the same polarizer plate with the same pressure-sensitive adhesive layer, the surface resistivity was similarly measured and the surface resistivity after the durability test was determined.

＜내구성의 시험 방법＞ <Test method of durability>

점착력의 측정과 동일한 방법으로 10㎝ 각의 점착제층 부착 편광판의 이형 필름을 박리하고, 무알칼리 유리의 아세톤으로 세정한 면에 첩합하여 시험편을 작성하였다. 그 후, 당해 시험편에 대해 85℃×750hr의 시험 환경하에 있어서의 내구성 시험 및 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험을 한 후, 23℃×50% RH 분위기하로 꺼내고, 1시간 후에 점착제층의 상태를 육안으로 관찰하여 내구성을 판단하였다. The release film of the 10 cm-square pressure-sensitive adhesive layer polarizing plate was peeled off in the same manner as in the measurement of the adhesive force, and was attached to a surface cleaned with acetone of an alkali-free glass to prepare a test piece. Thereafter, the test piece was subjected to a durability test under a test environment of 85 占 폚 占 750 hours and a durability test under a test environment of 60 占 폚 占 90% RH 占 占 750 hours and then taken out under an atmosphere of 23 占 폚 占 50% RH, After 1 hour, the state of the pressure-sensitive adhesive layer was visually observed to determine durability.

○··점착제층의 발포 및 박리가 전혀 없다. No blowing or peeling of the pressure-sensitive adhesive layer.

△··점착제층의 일부에 발포, 박리가 발생되고 있다. DELTA ... A portion of the pressure-sensitive adhesive layer is foamed or peeled.

×··점착제층 전체에 발포, 박리가 발생되고 있다. X · · Foaming and peeling occur throughout the pressure-sensitive adhesive layer.

＜대전 방지제의 석출 상태의 평가 방법＞ &Lt; Evaluation method of precipitation state of antistatic agent &gt;

점착력의 측정과 동일한 방법으로 10㎝ 각의 점착제층 부착 편광판의 이형 필름을 박리하고, 무알칼리 유리의 아세톤으로 세정한 면에 첩합하여 시험편을 작성하였다. 그 후, 당해 시험편에 대해 85℃×750hr의 시험 환경하에 있어서의 내구성 시험 및 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험을 한 후, 23℃×50% RH 분위기하로 꺼내고, 1시간 후에 점착제층의 상태를 육안으로 관찰하여 점착제층의 표면에 대한 대전 방지제의 석출 상태를 판단하였다. The release film of the 10 cm-square pressure-sensitive adhesive layer polarizing plate was peeled off in the same manner as in the measurement of the adhesive force, and was attached to a surface cleaned with acetone of an alkali-free glass to prepare a test piece. Thereafter, the test piece was subjected to a durability test under a test environment of 85 占 폚 占 750 hours and a durability test under a test environment of 60 占 폚 占 90% RH 占 占 750 hours and then taken out under an atmosphere of 23 占 폚 占 50% RH, After 1 hour, the state of the pressure-sensitive adhesive layer was visually observed to determine the state of precipitation of the antistatic agent on the surface of the pressure-sensitive adhesive layer.

○··점착제층의 표면에 대전 방지제의 석출이 전혀 없다. No antistatic agent precipitates on the surface of the pressure-sensitive adhesive layer.

△··점착제층의 표면의 일부에 대전 방지제의 석출이 발생되고 있다. DELTA ... An antistatic agent is precipitated on a part of the surface of the pressure-sensitive adhesive layer.

×··점착제층의 표면 전체에 대전 방지제의 석출이 발생되고 있다. X Antistatic agent precipitation occurs on the entire surface of the pressure-sensitive adhesive layer.

표 3에 평가 결과를 나타낸다. Table 3 shows the evaluation results.

Figure pat00003
Figure pat00003

실시예 1∼6의 점착 필름은 무알칼리 유리에 대한 점착력이 1.0∼6.0N/25㎜이며, 점착제층의 초기 표면 저항율 및 85℃×750hr의 시험 환경하에 있어서의 내구성 시험 후의 표면 저항율이 모두 2.0×10+9Ω/□ 이하이며, 85℃×750hr의 시험 환경하에 있어서의 내구성 시험 및 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험 후에 발포 및 박리가 없고, 내구성을 갖고 있고, 또한 점착제층의 표면에 대전 방지제의 석출도 없었다. 즉, 실시예 1∼6의 점착 필름에 대한 평가 결과에서는 본 발명의 과제를 해결할 수 있었던 것이 실증되어 있다. The adhesive films of Examples 1 to 6 had an adhesive force of 1.0 to 6.0 N / 25 mm to the alkali-free glass, an initial surface resistivity of the pressure-sensitive adhesive layer, and a surface resistivity after the durability test under a test environment of 85 占 폚 占 750 hr were both 2.0 × 10 +9 Ω / □ or less, no durability test under a test environment of 85 ° C. × 750 hr and a durability test under a test environment of 60 ° C. × 90% RH × 750 hr, , And there was no precipitation of an antistatic agent on the surface of the pressure-sensitive adhesive layer. That is, the results of the evaluation of the adhesive films of Examples 1 to 6 demonstrate that the problems of the present invention can be solved.

비교예 1의 점착 필름은 아크릴계 폴리머에 공중합시킨 알킬(메타)아크릴레이트 모노머가 TBA, IBA, BMA, MA 중 어느 것도 아니며, 또한 (D) 방향족기를 함유하는 공중합성 비닐 모노머를 공중합시키지 않았다. 이 때문에, 비교예 1의 점착 필름은 내구성 시험 전의 점착제층의 점착력은 과대하지만, 내구성이 떨어져 있었다. 또한, 비교예 1의 점착 필름은 (E) 대전 방지제의 함유 비율을 많게 하고 있기 때문에 점착제층의 표면 저항율은 낮아졌지만, 내구성 시험 후에 대전 방지제가 점착제층의 표면에 전면적으로 석출되었다. In the pressure-sensitive adhesive film of Comparative Example 1, the alkyl (meth) acrylate monomer copolymerized with the acrylic polymer was not any of TBA, IBA, BMA, and MA, and the copolymerizable vinyl monomer containing the aromatic group (D) was not copolymerized. For this reason, the pressure-sensitive adhesive film of Comparative Example 1 had an excessively high adhesive strength before the durability test, but had poor durability. Further, since the content of the antistatic agent (E) in the pressure-sensitive adhesive film of Comparative Example 1 was increased, the surface resistivity of the pressure-sensitive adhesive layer was lowered, but after the endurance test, the antistatic agent was completely deposited on the surface of the pressure-

비교예 2의 점착 필름은 (G) 실란 커플링제를 함유하지만, 에폭시기, 메르캅토기, 산무수물기에서 선택된 적어도 1종 이상의 관능기를 함유하는 것이 아니다. 이 때문에, 비교예 2의 점착 필름은 점착제층의 내구성이 떨어지고, 내구성 시험 후에 대전 방지제가 점착제층의 표면에 부분적으로 석출되었다. The pressure-sensitive adhesive film of Comparative Example 2 contains (G) a silane coupling agent but does not contain at least one functional group selected from an epoxy group, a mercapto group and an acid anhydride group. Therefore, the durability of the pressure-sensitive adhesive layer of Comparative Example 2 was poor, and after the durability test, the antistatic agent partially precipitated on the surface of the pressure-sensitive adhesive layer.

비교예 3의 점착 필름은 아크릴계 폴리머에 공중합시킨 알킬(메타)아크릴레이트 모노머가 TBA, IBA, BMA, MA 중 어느 것도 아니며, 또한 (D) 방향족기를 함유하는 공중합성 비닐 모노머를 공중합시키지 않았다. 이 때문에, 비교예 3의 점착 필름은 (G) 실란 커플링제를 함유하고 있지 않아도, 내구성 시험 전의 점착제층의 점착력은 과대하지만, 내구성이 떨어져 있었다. 또한, 비교예 3의 점착 필름은 (E) 대전 방지제의 함유 비율이 적기 때문에, 내구성 시험 후의 대전 방지제의 점착제층의 표면에 대한 석출은 없었지만, 점착제층의 표면 저항율이 높아졌다. In the pressure-sensitive adhesive film of Comparative Example 3, the alkyl (meth) acrylate monomer copolymerized with the acrylic polymer was not any of TBA, IBA, BMA, and MA, and the copolymerizable vinyl monomer containing the aromatic group (D) was not copolymerized. For this reason, the pressure-sensitive adhesive film of Comparative Example 3 did not contain the silane coupling agent (G), the pressure-sensitive adhesive layer before the durability test had an excessive adhesive force, but the durability was poor. Further, since the content of the antistatic agent (E) in the pressure-sensitive adhesive film of Comparative Example 3 was small, there was no precipitation of the antistatic agent on the surface of the pressure-sensitive adhesive layer after the durability test, but the surface resistivity of the pressure-

이와 같이, 비교예 1∼3의 점착 필름에서는 본 발명의 과제를 해결할 수 없었다. As described above, the problems of the present invention were not solved in the adhesive films of Comparative Examples 1 to 3.

본 발명에 의하면, 점착제층의 표면 저항율이 종래 기술에서는 달성할 수 없는 2.0×10+9Ω/□ 이하의 지극히 우수한 대전 방지 성능을 갖고, 또한 내구성을 저해하지 않는 점착제 조성물 및 이를 사용한 점착 필름을 제공할 수 있다. 이 때문에, 본 발명에 따른 점착제 조성물 및 이를 사용한 점착 필름은 편광판과 액정 패널을 첩합하는 용도의 점착제 조성물 및 이를 사용한 점착 필름으로서 지극히 우수한 대전 방지 성능을 갖고, 또한 내구성을 갖는다는 점에서 산업상의 이용 가치가 크다.INDUSTRIAL APPLICABILITY According to the present invention, there is provided a pressure-sensitive adhesive composition which has an extremely excellent antistatic property of not higher than 2.0 x 10 &lt; -9 &gt; . Therefore, the pressure-sensitive adhesive composition and the pressure-sensitive adhesive film using the pressure-sensitive adhesive composition according to the present invention are excellent in antistatic performance and durability as a pressure-sensitive adhesive composition for use with a polarizing plate and a liquid- Great value.

Claims (14)

아크릴계 폴리머와, 대전 방지제와, 가교제를 함유하는 점착제 조성물로서,
상기 아크릴계 폴리머가,
(A) n-부틸아크릴레이트와,
(B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종과,
(C) 수산기 및/또는 카르복실기를 함유하는 공중합성 비닐 모노머의 적어도 1종과,
(D) 방향족기를 함유하는 공중합성 비닐 모노머의 적어도 1종을 공중합시킨 공중합체의 중량 평균 분자량이 100∼300만인 아크릴계 폴리머이며,
상기 (E) 대전 방지제로서, 플루오로기 함유 음이온을 갖는 암모늄계 대전 방지제를 상기 아크릴계 폴리머의 100중량부에 대해 15중량부 초과 40중량부 이하의 비율로 함유하여 이루어지고,
상기 (F) 가교제로서, 3관능 이상의 이소시아네이트 화합물, 2관능 이상의 에폭시 화합물로 이루어지는 군에서 선택된 적어도 1종 이상의 가교제를 함유하여 이루어지고,
상기 점착제 조성물이 (G) 에폭시기, 메르캅토기, 산무수물기에서 선택된 적어도 1종 이상의 관능기를 함유하는 모노머 타입 또는 올리고머 타입의 실란 커플링제를 추가로 함유하여 이루어지고,
상기 점착제 조성물을 가교시킨 점착제층의 표면 저항율이 2.0×10+9Ω/□ 이하이며,
상기 점착제층을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 또는 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 상기 점착제층의 표면에 상기 대전 방지제가 석출되어 있지 않는 것을 특징으로 하는 점착제 조성물. A pressure-sensitive adhesive composition containing an acrylic polymer, an antistatic agent, and a crosslinking agent,
Wherein the acryl-
(A) n-butyl acrylate,
(B) at least one member selected from the group consisting of t-butyl acrylate, isobutyl acrylate, n-butyl methacrylate and methyl acrylate,
(C) at least one copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group,
(D) a copolymer obtained by copolymerizing at least one copolymerizable vinyl monomer containing an aromatic group, the acrylic polymer having a weight average molecular weight of 100 to 3,000,000,
(E) an antistatic agent containing an ammonium-based antistatic agent having a fluorine group-containing anion in an amount of not less than 15 parts by weight and not more than 40 parts by weight per 100 parts by weight of the acrylic polymer,
(F) at least one crosslinking agent selected from the group consisting of an isocyanate compound having three or more functional groups and an epoxy compound having two or more functional groups,
Wherein the pressure-sensitive adhesive composition further comprises (G) a monomer type or oligomer type silane coupling agent containing at least one functional group selected from an epoxy group, a mercapto group and an acid anhydride group,
Wherein the pressure-sensitive adhesive layer crosslinked with the pressure-sensitive adhesive composition has a surface resistivity of 2.0 x 10 &lt; + 9 &
The pressure-sensitive adhesive layer was provided in a durability test under a test environment of 85 占 폚 占 750 hours or after it was provided in a durability test under a test environment of 60 占 폚 占 90% RH 占 750 hr. Wherein an antistatic agent is not precipitated. 제 1 항에 있어서,
상기 대전 방지제가 플루오로기 함유 음이온과 암모늄 양이온으로 이루어지는 융점이 25℃ 이상인 이온성 화합물이며,
상기 플루오로기 함유 음이온이 펜타플루오로벤젠술포네이트, 헥사플루오로포스페이트, 비스(트리플루오로메탄술포닐)이미드, 비스(플루오로술포닐)이미드, 트리플레이트로 이루어지는 군에서 선택된 1종인 것을 특징으로 하는 점착제 조성물. The method according to claim 1,
Wherein the antistatic agent is an ionic compound having a fluoro group-containing anion and an ammonium cation and having a melting point of 25 ° C or higher,
Wherein the fluorine group-containing anion is at least one selected from the group consisting of pentafluorobenzene sulfonate, hexafluorophosphate, bis (trifluoromethanesulfonyl) imide, bis (fluorosulfonyl) &Lt; / RTI &gt; 제 1 항 또는 제 2 항에 있어서,
상기 아크릴계 폴리머가 상기 아크릴계 폴리머의 100중량부에 대해 상기 (A) n-부틸아크릴레이트를 40∼89중량부와, 상기 (B) t-부틸아크릴레이트, 이소부틸아크릴레이트, n-부틸메타크릴레이트, 메틸아크릴레이트로 이루어지는 군에서 선택된 적어도 1종 이상의 합계를 5∼40중량부의 비율로 함유하여 이루어지고, 또한 (A)와 (B)의 비율((A)／(B))이 1.0∼17.8인 것을 특징으로 하는 점착제 조성물. 3. The method according to claim 1 or 2,
(A) n-butyl acrylate in an amount of 40 to 89 parts by weight based on 100 parts by weight of the acryl-based polymer, and (B) t-butyl acrylate, isobutyl acrylate, n- (A) / (B) in a ratio of (A) to (B) of from 1.0 to 10 parts by weight based on 100 parts by weight of the total amount of at least one selected from the group consisting of 17.8. &Lt; / RTI &gt; 제 1 항 또는 제 2 항에 있어서,
상기 점착제 조성물을 가교시킨 두께 20㎛의 점착제층을 개재하여 총 두께 80㎛의 편광판을 무알칼리 유리에 첩합하였을 때, 상기 점착제층의 무알칼리 유리에 대한 점착력이 1.0∼6.0N/25㎜이며,
상기 점착제 조성물을 가교시킨 두께 20㎛의 점착제층을 개재하여 10㎝ 각의 총 두께 80㎛의 편광판을 무알칼리 유리에 첩합하여 이루어지는 시험편을 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 또는 60℃×90% RH×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후에, 발포 및 박리가 없는 것을 특징으로 하는 점착제 조성물.3. The method according to claim 1 or 2,
The pressure-sensitive adhesive layer had an adhesive force of 1.0 to 6.0 N / 25 mm to a non-alkali glass when a polarizing plate having a total thickness of 80 占 퐉 was bonded to a non-alkali glass via a pressure-sensitive adhesive layer having a thickness of 20 占 퐉,
A test piece consisting of a 10-cm square polarizing plate having a total thickness of 80 占 퐉 laminated to a non-alkali glass via a pressure-sensitive adhesive layer having a thickness of 20 占 퐉 bridged with the pressure-sensitive adhesive composition was provided in a durability test under a test environment of 85 占 폚 for 750 hours By weight or less, or after subjected to a durability test under a test environment of 60 캜 x 90% RH x 750 hours, there is no foaming and peeling. 제 1 항 또는 제 2 항에 있어서,
상기 (C) 수산기 및/또는 카르복실기를 함유하는 공중합성 비닐 모노머가 수산기를 함유하는 공중합 가능한 모노머 및 카르복실기를 함유하는 공중합 가능한 모노머로 이루어지는 군에서 선택된 적어도 1종 이상이며,
상기 수산기를 함유하는 공중합 가능한 모노머가 8-히드록시옥틸(메타)아크릴레이트, 6-히드록시헥실(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 2-히드록시에틸(메타)아크릴레이트, N-히드록시(메타)아크릴아미드, N-히드록시메틸(메타)아크릴아미드, N-히드록시에틸(메타)아크릴아미드로 이루어지는 화합물군 중에서 선택된 적어도 1종 이상이며,
상기 카르복실기를 함유하는 공중합 가능한 모노머가 (메타)아크릴산, 카르복시에틸(메타)아크릴레이트, 카르복시펜틸(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸헥사히드로프탈산, 2-(메타)아크릴로일옥시프로필헥사히드로프탈산, 2-(메타)아크릴로일옥시에틸프탈산, 2-(메타)아크릴로일옥시에틸숙신산, 2-(메타)아크릴로일옥시에틸말레산, 카르복시폴리카프로락톤모노(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸테트라히드로프탈산으로 이루어지는 화합물군 중에서 선택된 적어도 1종 이상인 것을 특징으로 하는 점착제 조성물.3. The method according to claim 1 or 2,
Wherein the copolymerizable vinyl monomer containing (C) a hydroxyl group and / or a carboxyl group is at least one or more selected from the group consisting of a copolymerizable monomer containing a hydroxyl group and a copolymerizable monomer containing a carboxyl group,
(Meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 4-hydroxybutyl (Meth) acrylate, N-hydroxy (meth) acrylamide, N-hydroxymethyl (meth) acrylamide and N-hydroxyethyl
Wherein the copolymerizable monomer containing a carboxyl group is selected from the group consisting of (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, 2- (meth) acryloyloxyethylhexahydrophthalic acid, 2- (Meth) acryloyloxyethylmaleic acid, 2- (meth) acryloyloxyethylphthalic acid, 2- (meth) acryloyloxyethylsuccinic acid, carboxypolycaprolactone mono (Meth) acrylate, and 2- (meth) acryloyloxyethyl tetrahydrophthalic acid. The pressure-sensitive adhesive composition according to claim 1, 제 1 항 또는 제 2 항에 있어서,
상기 점착제층의 초기 표면 저항율 및 85℃×750hr의 시험 환경하에 있어서의 내구성 시험에 제공한 후의 표면 저항율이 모두 2.0×10+9Ω/□ 이하인 것을 특징으로 하는 점착제 조성물.3. The method according to claim 1 or 2,
Wherein the initial surface resistivity of the pressure-sensitive adhesive layer and the surface resistivity after being provided in the durability test under a test environment of 85 占 폚 占 750 hr are both 2.0 占 10 + 9 ? /? Or less. 수지 필름의 한쪽 면에 제 1 항 또는 제 2 항의 점착제 조성물을 가교시킨 점착제층이 적층되어 이루어지는 것을 특징으로 하는 점착 필름. Wherein a pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition of claim 1 or 2 is laminated on one side of the resin film. 제 7 항의 점착 필름이 사용된 편광판용 점착 필름.A pressure-sensitive adhesive film for a polarizing plate, wherein the pressure-sensitive adhesive film of claim 7 is used. 제 8 항에 있어서,
편광판과 인셀 패널의 첩합에 사용되고 있는 것을 특징으로 하는 편광판용 점착 필름.9. The method of claim 8,
Wherein the pressure-sensitive adhesive layer is used for bonding the polarizing plate and the insole panel. 이형 필름의 한쪽 면에 제 1 항 또는 제 2 항의 점착제 조성물을 가교시킨 점착제층이 1㎛∼25㎛의 두께로 형성된 이형 필름/점착제층/이형 필름의 구성인 것을 특징으로 하는 점착 필름.Wherein the pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition of claim 1 or 2 on one side of the release film has a configuration of a release film / pressure-sensitive adhesive layer / release film formed to a thickness of 1 m to 25 m. 광학 필름의 적어도 한 면에 제 1 항 또는 제 2 항의 점착제 조성물을 가교시킨 점착제층이 적층되어 이루어지는 것을 특징으로 하는 점착제층 부착 광학 필름.The optical film with a pressure-sensitive adhesive layer, wherein a pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition of claim 1 or 2 is laminated on at least one surface of the optical film. 편광판의 한쪽 면에 제 1 항 또는 제 2 항의 점착제 조성물을 가교시킨 점착제층이 적층되어 이루어지는 것을 특징으로 하는 점착제층 부착 편광판.A pressure-sensitive adhesive sheet with a pressure-sensitive adhesive layer, wherein a pressure-sensitive adhesive layer formed by crosslinking the pressure-sensitive adhesive composition of claim 1 or 2 is laminated on one side of the polarizing plate. 제 12 항의 점착제층 부착 편광판이 사용되고 있는 것을 특징으로 하는 액정 패널.A liquid crystal panel characterized by using the polarizer with a pressure-sensitive adhesive layer according to claim 12. 제 12 항의 점착제층 부착 편광판이 사용되고 있는 것을 특징으로 하는 인셀형 액정 패널.An in-cell liquid crystal panel, wherein the polarizing plate with a pressure-sensitive adhesive layer according to claim 12 is used.
KR1020170133826A 2017-04-07 2017-10-16 Adhesive composition and adhesive film KR102034512B1 (en)