KR20180012045A - VFP 3D printing system, and method thereof - Google Patents

Abstract

The present invention relates to a vacuum film process (VFP) three-dimensional printing system and a VFP three-dimensional printing method. More specifically, the present invention relates to the VFP three-dimensional printing system which molds a roll-to-roll film into a preset shape by repeating a process of enabling a heat press to fuse and cut the roll-to-roll film continuously supplied under vacuum, and the VFP three-dimensional printing method. Further, the VFP three-dimensional printing system of the present invention includes: a film supply unit for continuously supplying a film in the form of roll-to-roll; a vacuum sealing unit for vacuum sealing the film supplied through the film supply unit; a bed which is disposed at a lower side within the vacuum sealing unit, and on which a sculpture is stacked; a heat press unit which is disposed in an upper side within the vacuum sealing unit and heats and pressurizes the supplied film to fuse the film onto a top portion of the bed or the stacked sculpture; and a cutting unit for cutting the film fused by the heat press unit into the preset shape.

Description

[0001] VFP 3D printing system and method [0002]

[0001] The present invention relates to a VFP 3D printing system and a method thereof, and more particularly, to a VFP 3D printing system and a method thereof. More particularly, the present invention relates to a VFP 3D printing system and a method thereof, Vaccum Film Process (VFP) 3D printing system and method thereof.

The production process, which is mainly used when manufacturing products of the shape set in the manufacturing process, is a process of cutting or cutting large raw materials and joining or assembling the processed parts. However, As the tendency is changed not to mass production but to multi-product small quantity production, a new processing method is required.

3D (Three Dimension) printing is a technique for producing a three-dimensional three-dimensional object by sintering and laminating plastics, metals and composite materials thereof based on a three-dimensional CAD model (modeling data) of a predetermined sculpture. Unlike the process of joining or assembling the processed parts and the assembled parts, it is possible to greatly reduce the assembly cost, and it is possible to replace mass production based on the conventional manufacturing process, which is mainly for cutting, .

In the early days of 3D printing technology, it was mainly applied to the mold industry. However, nowadays, products using 3D printing technology are being released in almost all fields of industries ranging from industrial application to bio, food and fashion. 3D printing technology is emerging as a technology that will lead the tertiary manufacturing revolution.

The types of 3D printing technology include Selective Laser Sintering (SLS), Laser Fusion Deposition Modeling (FDM), sintering of metal powders by laser, (Direct Metal Laser Sintering, DMLS), Electron Beam Melting (EBM) through electron beam, and Stereo Lithography Apparatus (SLA) by selectively emitting laser light. Numerous studies are continuing to maximize process efficiency.

In Korean Patent No. 10-1523692, a head capable of moving in the X, Y, and Z axes discharges thermoplastic filaments to laminate a working material having the same shape as a printing object on a working plate, Dimensional printers that can be used in a variety of applications.

Korean Patent No. 10-1524362 discloses that a first carrier module and a second carrier module which support the head module on both sides of a head module provided with nozzles and move up and down along the Z axis direction are connected to a single motor Dimensional stereoscopic printer apparatus in which a feed control section for controlling the feed of the filament fed to the head module is not provided in the head module itself but is attached to another part of the printer apparatus .

Korean Patent No. 10-1510137 discloses an ink jet printer having a chamber in which a hollow portion is formed in a longitudinal direction and a jet nozzle is formed in a lower portion of the hollow portion, a chamber connected to an inlet port formed at one side of the hollow portion, A three-dimensional printer including a syringe for introducing a substance (solid filament or liquid metal), a rotating member rotating in one direction located in the hollow portion, and an operating member for applying a driving force to rotate the rotating member .

Korean Patent Laid-Open Publication No. 10-2016-0059726 discloses a method of floating a powdered material using a powder capable of performing rapid fabrication and further manufacture after manufacturing by controlling the powder material to be located in an arbitrary space and curing through a plurality of lasers Dimensional printer.

In the 3D printing technology, a method of laminating filaments or sintering powder materials is used as a form in which raw materials are injected and applied.

However, the above methods have a problem in that the time required for forming the laminate and the molding material has a long time because the raw materials of the point unit and the line unit are successively laminated and laminated on the surface unit and the three-dimensional unit.

Further, it is difficult to keep the lamination thickness of each layer constant, and there is a problem that the height of the laminate to be formed through the three-dimensional CAD model of the preformed molding is not constant or inclined.

Particularly, there is a problem that it is difficult to correct the shrinkage degree depending on the area of each layer position.

Korean Patent No. 10-1523692 Three-dimensional printer Korean Patent No. 10-1524362 A three-dimensional stereoscopic printer apparatus Korean Patent No. 10-1510137 Three-dimensional printer Korean Patent Publication No. 10-2016-0059726 Floating-type three-dimensional

In order to solve the above problems, an object of the present invention is to provide a VFP 3D printing system and a method for rapidly forming a predetermined shape by repeating a process of fusing and cutting a continuously supplied roll- .

That is, the present invention provides a VFP 3D printing system and method for rapidly forming a three-dimensional molding through a Vaccum Film Process (VFP).

According to an aspect of the present invention, there is provided a VFP 3D printing system including a film feeder for continuously feeding a film in a roll-to-roll fashion, a vacuum seal for vacuum sealing the film supplied through the film feeder, A heat press portion for heating and pressing the film placed on the upper side in the vacuum hermetic portion and fusing the film to the upper portion of the bed or the laminated molding, And a cutting portion for cutting the cut-out portion into a predetermined shape.

The bed may further include a vertical conveying portion that can be lowered by a height corresponding to the height of the laminated molding so that the film to be supplied next can be moved and stacked on the upper side of the laminated building.

Further, the film supply part is constituted of a plurality of films for supplying a film having a plurality of different colors or thicknesses, and the bed is selectively transported to the lower side of the film supplied through any one of the plurality of film supply parts by the horizontal transfer part So that it is possible to control the color or thickness of the laminated film.

The apparatus further includes an adhesive applying unit for applying a thermosetting adhesive to a lower portion of the film supplied through the film supplying unit.

In addition, the VFP 3D printing method of the present invention includes a primary film supplying step (S100) for supplying a film continuously supplied in roll-to-roll form to a vacuum closing part provided with a hot press, A primary cutting step S300 of cutting a film fused to the bed to a predetermined shape by using a cutting part to form a first layer, and a film moving step A first peeling step (S400) of peeling off the remaining portion excluding the cut first layer from the bed (S400), and a film continuously fed again in a roll-to-roll form is disposed on the upper portion of the first layer, A second heat press step (S500) for fusing the re-supplied film to the upper part of the first layer, and a second heat press step (S500) for re- And a second peeling step (S700) for peeling off the remaining portion excluding the cut second layer from the first layer (S700) by moving the re-fed film and forming a predetermined lamination (S600) The second heat pressing step, the second cutting step, and the second peeling step are repeatedly performed according to the number of times of pressing the second heat pressing step, the second heat pressing step, the second cutting step and the second peeling step.

Further, the method further includes an adhesive applying step of applying a thermosetting adhesive to the lower part of the film continuously fed in roll-to-roll form prior to the primary film supplying step (S100).

As described above, according to the VFP 3D printing system and method of the present invention, the layers of the film material are formed at one time by fusing and cutting the raw material on the film continuously supplied by a hot press to form a three-dimensional molding It is possible to greatly reduce the time required for the operation.

BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a block diagram showing a vacuum film processor 3D printing system according to the present invention; FIG.
FIG. 2 is a flow chart showing a vacuum film processor 3D printing method of the present invention. FIG.
3 is a schematic diagram showing a bed horizontal conveying step according to the present invention.
4 is a schematic diagram showing a primary heat pressing step (S200) according to the present invention.
5 is a schematic diagram showing a first cutting step S300 according to an embodiment of the present invention;
6 is a schematic diagram showing a first cutting step (S300) according to another embodiment of the present invention;
7 is a schematic diagram showing a first peeling step (S400) according to the present invention.
8 is a schematic diagram showing a secondary heat pressing step (S500) according to the present invention.
9 is a schematic diagram showing (A) a second cutting step (S600) and (B) a second peeling step (S700) according to the present invention.

Specific features and advantages of the present invention will be described in detail below with reference to the accompanying drawings. The detailed description of the functions and configurations of the present invention will be omitted if it is determined that the gist of the present invention may be unnecessarily blurred.

The present invention relates to a VFP 3D printing system and a method thereof, and more particularly, to a VFP 3D printing system and a VFP 3D printing system in which a process of fusing and cutting a continuously supplied roll- It is about the method.

1 is a block diagram illustrating a vacuum film processor 3D printing system according to the present invention.

The vacuum film processor 3D printing system according to the present invention includes a film supply unit 10 for continuously supplying a film in a roll-to-roll fashion, a vacuum hermetic sealing unit 20 for vacuum-sealing the film supplied through the film supply unit 10, A bed 32 disposed on the lower side of the vacuum hermetically sealed part 20 and stacked with a molding material and a heating part 32 disposed on the upper side in the vacuum hermetically sealed part 20 to heat and press the supplied film to form a bed 32, And a cutting section 40 for cutting the film welded by the hot press section 31 into a predetermined shape.

The film supply unit 10 continuously supplies the film to the vacuum hermetically sealed part 20 in a roll-to-roll fashion in order to construct a 3D laminate (molding product) to be finally produced. When the film is supplied to the vacuum seal part 20 and the hot press part 31 by a predetermined length, the film supply part 10 stops the supply and movement so that a subsequent process can be performed.

The vacuum hermetically sealed part 20 may be opened or closed as shown in (1-I) or (1-II) When the film is supplied in the open state and the supply of the film supplied through the film supply unit 20 is completed, the vacuum hermetically sealed part 20 is lowered and the vacuum hermetically sealed do.

Further, in the present invention, the supplied film is heated and pressed to fuse the interface between the laminated films. In order to prevent bubbles from being generated in the molten film due to high temperature, the vacuum hermetically sealed part (20) .

The vacuum enclosure 20 includes a heating unit (not shown) for heating the inside of the vacuum enclosure 20. The vacuum enclosure 20 is further exposed to a high temperature environment after the hot pressing process to partially melt the side surface of the laminated film, To prevent staircase phenomena.

The hot press part 31 is provided inside the vacuum hermetic part 20 and the hot press 31 for heating and pressing the film supplied from the upper side in a roll-to-roll form is vertically transportable, And a heater (not shown) is provided to heat the supplied film, and the heater is maintained for 1 second to 10 seconds in a state where the hot press is heated to a temperature equal to or higher than the melting point of the film to melt the lower surface of the supplied film .

In addition, the bed 32 in which the film is firstly laminated and on which the laminate by the repetitive layer of the film is placed, is disposed below the film supplied in the form of a roll-to-roll form, and is provided so as not to interfere with the movement of the supplied film. It is preferable to be located at a height lower than the height of the lower surface, and it is preferable that the film is vertically movable considering the height of the layered body to be changed every time the film is repeatedly laminated.

That is, as the height of the continuously supplied film is always constant, the bed 32 needs to be lowered above the height of the laminated film so that the next film can be laminated successively on top of the laminated film after the films are laminated .

The cut portion 40 is for cutting the uppermost sheet into a predetermined shape after the fusion is completed and is disposed outside so as to enter the vacuum hermetically sealed portion 20 when the vacuum hermetic portion 20 is opened Or may be disposed inside the vacuum hermetic seal 20.

The cutting unit 40 may be a laser cutting machine capable of minimizing branching due to cutting. However, a blade, a saw blade, a rotary cutting tool, or the like may be used.

Also, at least one of the cut portions 40 (see 40 'in FIG. 5) may be provided so as to be capable of cutting at a plurality of positions at the same time.

In the 3D printing system of the present invention, the film is supplied to the vacuum hermetically sealed part 20 in a roll-to-roll form through the film supply part 10, and when the film is placed on the bed 32, And the hot press part 31 heats and presses the film under a vacuum environment.

The heated and pressurized film is fused and fixed on the bed 32 and the cut portion 40 cuts the fused film into a predetermined shape based on the information (predetermined modeling data) stored in the 3D printer control unit.

At this time, the fused film is divided into a portion (a first layer, which will be described below) which is to be a 3D sculpture and a portion which is not. When the film supply portion 10 is operated again after the cutting is completed, The portion (first layer) which is cut to become a 3D sculpture remains fixed to the bed 32, and the remaining portion temporarily fused by heating and pressing is peeled and discharged together with the movement of the film.

As described above, the bed 32 needs to be arranged at a height below the supplied film so as not to interfere with the movement of the film. To this end, the bed 32 is moved to the upper side of the laminated film And a vertically conveying part (not shown) capable of lowering the bed 32 by a height corresponding to the height of the stacked sculpture so that the bed 32 can be stacked.

In addition, the film cut in the fused state by lowering the bed 32 through the vertical transfer part is primarily peeled off from the remaining part (first layer) to be a 3D sculpture, And the like.

On the other hand, when the spacing between the bed 32 and the supplied film is equal to or greater than the thickness of the supplied film, or when the film is fused to the bed 32 as the film is stretched and lowered by the pressing of the hot press, It is not necessary to separately raise and lower the bed 32 in order to peel off the remaining portion of the film. However, when the bed 32 is raised, It is preferable that the height of the film 32 is changed by the vertical transfer unit whenever the laminated film is laminated so as not to affect the film supplied to form a new layer and finally the laminated film.

More specifically, once the film has been deposited on the bed 32, a new film has to be placed on top of the previously laminated film, with a space between the previously deposited film and the newly disposed film thereon Otherwise, there may occur defects such as crushing and breakage in the film laminated by the moving film.

Therefore, in order to solve this problem, the uppermost layer of the laminated film (the film to be a 3D printing molding) moves and is not influenced by the newly supplied film as the film is laminated, It is preferable to move the bed 32 downward by the height of the finally laminated film.

The film is moved and a first layer, which is cut into a predetermined shape by the cut portion 40, is left on the bed 32, and a new film is continuously supplied again in a roll-to-roll form on the layer, The supplied film is heated and pressurized by the hot press 20, and is laminated on the first layer. The film is repeatedly cut and peeled a plurality of times to form a predetermined 3D laminate (molding).

In addition, the vacuum film processor 3D printing system according to the present invention may further include a control unit (not shown) to control the operation of the 3D printing system.

In addition, the film may be selected in consideration of the material characteristics required of the final 3D sculpture to be produced, and a thin film including a plastic resin and an inorganic material may be used.

Examples of the plastic resin include polyethylene, polypropylene, polystyrene (PS), polyamide (PA), polyimide (PI), polyimide (PP), polyphthalamide ), Polycarbonate (PC), polyoxymethylene (POM), polysulfone (PS), polybutylene terephthalate (PBT), polyvinyl chloride (PTFE), polymethyl methacylate (PMMA), acrylonitrile butadiene (ABS), and the like, as well as polytetrafluoroethylene (PET) Styrene, styrene acrylonitrile copolymer (SAN), thermoplastic polyurethane (TPU), modified polyphenylene oxide (PPO), and epoxy resin.

The inorganic material may include, but is not limited to, iron, copper, zinc, aluminum, nickel, titanium, magnesium, stainless steel and alloys, calcium carbonate and silica.

In addition, it may include a laminate and a prepreg made of a mixture of the resin material and an inorganic material, or a film in which a resin material is disposed on one side and an inorganic material is disposed on the other side.

Also, it is preferable that the thickness of the supplied film has a thickness of 5 to 5,000 mu m in consideration of excellent appearance and processability.

More specifically, when the thickness is less than the above-mentioned thickness, the process time is prolonged when the laminate and the molding are manufactured in an excessively thin film, and it becomes difficult to adhere to the hot press during hot press. It is preferable that the heat and pressure of the means are not transmitted to the surface or inside of the film and the adhesiveness between the film interface is deteriorated.

The thickness of the film can be selected in consideration of the curvature of curvature of the outer shape of the 3D sculpture to be finally produced. If the curvature of the sculpture of the 3D sculpture is small (if finer surface treatment is not required), a thick film is supplied, The film can be supplied with a thinner film and the efficiency of the process can be increased.

In addition, the process may be automatically changed.

That is, as the film is supplied in a roll-to-roll fashion, the film supply portion is composed of a plurality of films to supply a film having a plurality of different colors or thicknesses, The bed may be configured to be selectively transportable to a lower side of the film fed through any one of the plurality of film supply portions by a horizontal transfer portion.

Accordingly, it is possible to stack the films of different colors or thicknesses while transporting the bed through the horizontal transfer part according to the color or thickness of the film to be laminated.

The 3D printing method of the vacuum film processor according to the present invention uses the above-described vacuum film processor 3D printing system. Hereinafter, a vacuum film processor 3D printing method using the vacuum film processor 3D printing system will be described.

FIG. 2 is a flow chart showing the 3D film printing method of the vacuum film processor of the present invention.

The vacuum film processor 3D printing method of the present invention includes a first film feeding step (S100) of feeding a film continuously supplied in a roll-to-roll form to a vacuum closing part provided with a hot press, A primary cutting step S300 of cutting a film fused to the bed to a predetermined shape by using a cutting part to form a first layer, and a film moving step A first peeling step (S400) of peeling off the remaining portion excluding the cut first layer from the bed (S400), and a film continuously fed again in a roll-to-roll form is disposed on the upper portion of the first layer, (S500) for fusing the re-supplied film to the upper portion of the first layer (S500), and a step of cutting the thermally pressed film into a predetermined shape by using the cut portion (S600) for forming a second layer (S600), and a second peeling step (S700) for peeling off the remaining portion excluding the cut second layer from the first layer by moving the re-supplied film, The second thermal pressing step, the second cutting step and the second peeling step are repeatedly performed according to the predetermined number of times of lamination to form a laminate having a predetermined shape.

3, depending on the color, thickness, and material of the films 101 and 102 to be laminated before the primary film supplying step S100 or before the secondary heat pressing step S500, 101, and 102. In this case, the bed 32 may be horizontally conveyed to a lower side of the bed 32,

For example, the bed may be transported to the lower part of the film of different materials through the bed horizontal transporting step, and one of the films of different materials may be selectively laminated.

That is, as described above, it is not necessary to use a film in which a metal material is disposed on one surface and a resin material is disposed on the other surface, or a film composed of another material is supplied while the feeding of the film is stopped And selectively laminating any one of films made of different materials.

For example, a plurality of supply lines are formed in such a manner that a film 101 made of a metal material is supplied to one side and a film 102 made of resin is supplied to the other side, A film 101 made of a metal material and a film 102 made of a resin are selectively laminated by selectively transporting the bed 32 and stacking the films, or a film 101 made of a metal and a resin The film 102 may be alternately stacked.

FIG. 4 shows a film supply step (S100) and a primary heat pressing step (S200) according to the present invention.

The film supply step S100 supplies the film 100 in a roll-to-roll fashion to the vacuum sealing part provided inside the hot press part 31. When the film 100 is disposed on the upper part of the bed 32, Thereby stopping the supply and movement of the battery 100.

The primary heat pressing step (S200) presses and feeds the supplied film (100) by the hot press part (31) and fuses it to the bed (32).

When the film 100 is a general thermoplastic material, the interface of the film is melted and laminated through the hot press part 31, so that a separate adhesive application step is not required. However, a higher adhesive force may be formed, Or an adhesive applying step of applying a thermosetting adhesive to the lower part of the film continuously fed in roll-to-roll form prior to the primary film supplying step (S100), in the case of laminating different kinds of films which are not fused by heating or pressurization And may be configured to cure the thermosetting adhesive applied through the hot press.

Pressurization and heating by the hot press part 31 proceed in a vacuum environment of 5 to 15 bar so as not to generate bubbles when the films are laminated.

At this time, it is preferable that the hot press is performed at a pressure of 50,000 to 150,000 bar and a temperature of 80 to 500 ° C. When the pressure and the temperature are lower than this temperature, the supplied film hardly softens and melts and adhesion between the interfaces is difficult. If the temperature is exceeded, it is difficult to keep the preset range because it is too melted to maintain the predetermined shape.

5 shows a first cutting step S300 according to the present invention.

In the first cutting step S300, the film 100 fused to the bed 32 is cut into a predetermined shape using the cut portion 40 to form the first layer 100 '.

As shown in FIG. 6, it is also possible to form one or more 3D sculptures at the same time by providing one or more cut portions 40.

7 shows the first peeling step S400 according to the present invention. In the first peeling step S400, the remaining film 100B excluding the cut first layer 100 'is peeled from the bed 32, .

More specifically, the film fused to the bed 32 by the primary thermal pressing step S200 is divided into a part (first layer, 100 ') to be a 3D molding material by the first cutting step S300 And separation of the film 100 is performed by moving the film 100 or lowering the bed 32. When the film 100 is moved, One layer 100 'remains fixed to the bed 32 and the remaining portion 100B temporarily attached by heating and softening is peeled and moved and discharged together with the movement of the film 100. [

8 shows a second thermal pressing step S500 according to the present invention. In the second thermal pressing step S500, the film 200 continuously fed again in a roll-to- And then pressurized and heated by the hot press part 31 to be fused to the upper part of the first layer 100 '.

The secondary heat pressing step (S500) May be performed in the same manner as in the primary heat pressing step (S200), or by further increasing the hot press temperature and pressure.

remind In the first thermal pressing step S200, the film is heated and pressed on the bed 32 for the first time. Therefore, when the thermal press is performed at a high temperature, the film is excessively melted and adhesion with the bed is too strong, 400 is formed at a relatively low temperature since the remaining portion to be peeled off from the first layer can not be peeled off with the movement of the film.

However, in the secondary heat press step S500 after the first layer 100 'is formed, the film 200 re-supplied to the upper part of the first layer 100' is separated from the bed 32 It is possible to form the hot pressing condition relatively high.

In the primary heat pressing step (S200) and the secondary heat pressing step (S500), the hot press part for pressing the fed film is maintained at a temperature equal to or higher than the melting point of the supplied film for 1 second to 10 seconds, And a cooling step of curing the fused film by maintaining the hot press part fused with the film to a temperature not higher than the melting point of the supplied film for 1 second to 10 seconds have.

At this time, the fusing step is performed by heating the hot press part at a temperature equal to or higher than the melting point of the supplied film and holding the hot press part for 1 second to 10 seconds. It is preferable to expose for a short time of 1 second to 10 seconds since it is exposed for a long time at a temperature equal to or higher than the melting point or when the high temperature process is continuously repeated, deformation of the final 3D formed product may occur.

In addition, in order to perform the cooling step, the cooling passage passing through the hot press part may be formed, and the cooling water may be supplied to the cooling passage to lower the temperature of the hot press part.

9 shows (A) the second cutting step (S600) and (B) the second peeling step (S700) according to the present invention.

In the second cutting step S600, the laminated film 200 is cut into a predetermined shape using the cut portion 40 to form the second layer 200 '.

In the second peeling step S700, the re-supplied film is moved to peel off the remaining film 200 except for the cut second layer 200 ', and the second layer 200' Two layers 200 'exist in a laminated state.

The final molding of 3D printing is repeatedly performed in the second heat pressing step, the second cutting step and the second peeling step according to the predetermined number of times of lamination to form a predetermined shape to produce a molding.

While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is clearly understood that the same is by way of illustration and example only and is not to be taken as limiting the scope of the present invention. The present invention can be variously modified or modified. The scope of the invention should, therefore, be construed in light of the claims set forth to cover many of such variations.

10: Film supply part
20: vacuum sealing part
31: Heat Press
32: Bed
40:
100: film
100 ': first layer
200: Re-fed film
200 ': Second layer

Claims (6)

A film supply unit for continuously supplying the film in a roll-to-roll form;
A vacuum enclosure for vacuum sealing the film supplied through the film supply unit;
A bed disposed on the lower side of the vacuum hermetic sealing part and stacked with a molding;
A hot press part disposed on the upper side of the vacuum hermetically sealed part for heating and pressing the supplied film to fuse the upper part of the bed or the laminated molding;
And a cutting portion for cutting the film fused by the hot press portion into a predetermined shape.
VFP 3D printing system.
The method according to claim 1,
The bed
Further comprising a vertical transfer section capable of being lowered by a height corresponding to the height of the laminated molding so that the next supplied film can be moved and stacked on the upper side of the laminated molding
VFP 3D printing system.
The method according to claim 1,
Wherein the film supply part is constituted of a plurality of films for supplying a film having a plurality of different colors or thicknesses,
Wherein the bed is configured to be selectively transported to a lower side of a film fed through any one of the plurality of film supply units by a horizontal transfer unit to control the color or thickness of the laminated film
VFP 3D printing system.
The method according to claim 1,
And an adhesive applying unit for applying a thermosetting adhesive to the lower part of the film supplied through the film supplying unit
VFP 3D printing system.
A primary film supplying step (SlOO) for supplying a film continuously fed in roll-to-roll form to a vacuum sealing part provided inside the hot press;
A primary heat pressing step (S200) of pressing the supplied film to a hot press part and fusing the heated film to the bed;
A first cutting step (S300) of forming a first layer by cutting a film welded to the bed into a predetermined shape using a cut portion;
A first peeling step (S400) of peeling off the remaining portion of the film other than the first layer cut off from the bed by moving the film;
A second heat pressing step (S500) of placing a film, which is continuously fed in a roll-to-roll fashion, on the first layer and pressing and heating the same with a hot press to fuse the re-supplied film to the top of the first layer;
A second cutting step (S600) of forming a second layer by cutting the hot-pressed film into a predetermined shape using a cut portion;
And a second peeling step (S700) in which the re-supplied film is moved to peel off the remaining portion excluding the cut second layer from the first layer,
The second heat pressing step, the second cutting step and the second peeling step are repeatedly performed in accordance with the predetermined number of times of lamination to form a laminate having a predetermined shape
VFP 3D printing method.
6. The method of claim 5,
Before the primary film supply step (S100)
Characterized by further comprising an adhesive applying step of applying a thermosetting adhesive to the lower part of the film continuously fed in roll to roll form
VFP 3D printing method.