KR20180010043A - Process for making sticker - Google Patents

Process for making sticker Download PDF

Info

Publication number
KR20180010043A
KR20180010043A KR1020160092127A KR20160092127A KR20180010043A KR 20180010043 A KR20180010043 A KR 20180010043A KR 1020160092127 A KR1020160092127 A KR 1020160092127A KR 20160092127 A KR20160092127 A KR 20160092127A KR 20180010043 A KR20180010043 A KR 20180010043A
Authority
KR
South Korea
Prior art keywords
layer
forming step
sticker
forming
casting
Prior art date
Application number
KR1020160092127A
Other languages
Korean (ko)
Inventor
고경열
Original Assignee
고경열
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 고경열 filed Critical 고경열
Priority to KR1020160092127A priority Critical patent/KR20180010043A/en
Publication of KR20180010043A publication Critical patent/KR20180010043A/en

Abstract

The present invention relates to a method for manufacturing stickers for entertainment which improves adhesive force to attach, for a long time, a sticker which is used by being attached on a blackboard or the like when infants or children play. The method comprises: a release film preparing step (S100) which prepares PET of 100 in a form of a roll or sheet paper; a silicone layer forming step (S200) which coats silicone (200) on the top part of the release film to form a silicone layer (200); a livable layer forming step (S300) which forms a livable layer (300, an adhesive layer) to attach stickers to a blackboard or the like; a casting layer forming step (S400) which forms a casting providing a cushion effect to the top part of the livable layer, and coats the casting at the thickness of 1 m/, then irradiates ultraviolet rays for curing; a printing layer forming step (S500) which prints various designs on the top part of the casting layer; a transparent film layer forming step (S600) which forms a transparent film layer for preventing the printed printing from being damaged by peeling or the like, and adheres transparent films at 0.2 to the top part of the printing; a sticker forming step (S700) which uses a punch to form a sticker in order to detach the sticker from the release film layer with designs.

Description

유희용 스티커 제작방법{PROCESS FOR MAKING STICKER}{PROCESS FOR MAKING STICKER}

본 발명은 유희용 스티커 제작방법에 관한 것으로, 더욱 상세하게는 유아나 어린이들이 칠판 등에 붙여 놀이를 하는 스티커를 장시간 점착할 수 있도록 접착력을 향상시킨 유희용 스티커 제작방법에 관한 것이다. More particularly, the present invention relates to a method for manufacturing a sticker for a chef, which improves the sticking ability of a child or a child to stick a play sticking to a chalkboard or the like for a long time.

일반적으로, 스티커는 가방, 다이어 리노트, 핸드폰, 학용품, 손톱 등과 같은 다양한 대상에 점착되는 장식물 혹은 선전 광고, 상표, 표지 등과 같은 인쇄물을 포하는 포괄적인 개념이다.Generally, a sticker is a comprehensive concept that includes prints such as ornaments adverted to various objects such as bags, diary notes, cell phones, school supplies, nails, or advertising, trademarks, and signs.

이러한 스티커는 이형지, 이형지의 상면에 점착되어 그림이나 글 등과 같은 문양이 도안됨은 물론 저면에 접착력을 갖는 인쇄부로 구성되고, 인쇄부에 분리가능하게 결합되는 적어도 하나 이상의 문양부를 구비하여 이형지에 점착된 인쇄부에서 문양부를 떼어내어 사용하도록 구성된 것이 보통이다.Such a sticker is composed of a release paper sheet and a printing unit which is attached to the upper surface of the release paper sheet and has a pattern such as a picture or a letter and has an adhesive force on the bottom surface thereof and has at least one or more patterned parts detachably coupled to the printing unit, It is common to use the print unit to remove the pattern.

하지만, 종래 스티커는 평면적 형상과 모양 혹은 도안, 글씨 등으로 인쇄부가 이루어짐으로 인해 볼륨감, 특히 질감 표현이 없어 밋밋하고, 장식효과가 현저히 떨어지는 단점이 있었다.However, the conventional sticker has a disadvantage in that it has a flatness, a shape, a pattern, a letter, a letter, and the like, and therefore has a volume feeling,

이에, 인쇄부의 형상과 모양을 입체감 있게 표현함으로써 장식미, 유희성 등을 향상시키려는 노력들이 경주되어 왔으며, 그 일예들은 하기한 선행기술문헌을 포함한 다수의 특허 기술들에 나타나 있다.Accordingly, efforts have been made to improve the decorative effect and playability by expressing the shape and the shape of the printing part in a three-dimensional manner, and examples thereof are shown in a number of patent technologies including the above-mentioned prior art documents.

한편, 이형성과 두께, 쿠션감 등 제조상, 외형상 여러가지 잇점으로 인해 발포 스티커가 시판되고 있는데, 발포스티커는 기저시트 위에 PVC 폼으로 발포층을 형성하고, 발포층 위에 인쇄층을 구현한 스티커를 말한다.On the other hand, foaming stickers are sold on the market due to various advantages such as mold releasability, thickness, and cushioning feeling. The foaming sticker refers to a sticker that forms a foam layer with a PVC foam on a base sheet and implements a print layer on the foam layer .

그런데, 시판 중인 입체 발포 스티커는 입체감을 주기 위해 발포층을 두껍게 올린 다음 무늬 등을 인쇄하여 인쇄층을 형성하고, 일부를 눌러 볼록하게 보이게 하는 단순한 형태로 제조하였기 때문에 스티커를 접었다 펼칠 경우 인쇄층이 벗겨지거나 탈락되거나 혹은 깨지는 등의 문제가 발생하여 품질이 저하됨은 물론 입체감도 질감을 느낄 수 있는 수준이 아니라 단순히 눌러 준 형태에 불과하여 입체감을 주는 부분이 전체적으로 두께만 높아진 형태로서 매우 저급하였다.However, the commercially available three-dimensional foamed sticker is manufactured in a simple form in which a foaming layer is thickly raised to give a three-dimensional effect, and then a pattern or the like is printed to form a printed layer and a portion is pressed to be convex. Not only the quality is deteriorated due to peeling, dropping, or cracking, but also the level of the three-dimensional feeling is very low.

때문에, 고급스러움을 연출할 수 있고, 두께감이 좋아 질감 표현력이 우수하면서 소수성으로 인해 물기에 강한 에폭시수지를 인쇄층을 사용한다면 매우 좋다. 그렇지만, 에폭시는 발포층인 PVC와의 물성이 달라 비친화적이기 때문에 마치 기름기 있는 부분에 인쇄한 것 같이 인쇄용 잉크가 번져 원하는 형상과 모양의 무늬를 구현할 수 없을 뿐만 아니라, 충분한 접착력을 얻을 수 없어 쉽게 박리되거나 분리 이탈 또는 인쇄층 깨짐 등의 단점이 있다.Therefore, it is very good if you can use the printing layer of epoxy resin which is able to produce a high quality and is resistant to water due to hydrophobicity because of its excellent thickness and texture. However, the epoxy is inexpensive because it is different in physical properties from the foamed layer of PVC. As a result, the printing ink spreads as if it were printed on a greasy portion, so that the desired shape and shape of the pattern can not be realized. There is a drawback such as separation or separation or breakage of the print layer.

더구나, 수차례에 걸쳐 반복 인쇄함으로써 일정한 형상과 모양의 무늬를 형성한다고 하더라도 쉽게 탈락되어 버리기 때문에 입체 발포 스티커의 품질이 급격히 떨어지는 한계를 가진다.Moreover, even if a pattern of a certain shape and shape is formed by repeatedly printing a number of times, the stencil foam sticker is detached easily, so that the quality of the stencil foam sticker is rapidly deteriorated.

대한민국 등록특허 제0928393호(2009.11.17)Korean Patent No. 0928393 (November 17, 2009)

본 발명은 상술한 종래기술의 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 유아나 어린이들이 칠판 등에 붙여 놀이를 하는 스티커를 장시간 점착할 수 있도록 접착력을 향상시킨 유희용 스티커 제작방법을 제공함에 있다.It is an object of the present invention to provide a method of manufacturing a sticker for a chef, which improves the adhesive force so that a sticker for playing and pasting a child or a child on a chalkboard can be adhered for a long period of time.

상기 목적을 달성하기 위한 본 발명의 일 실시 예에 따른 본 발명은 접착력을 향상시킨 유희용 스티커 제작방법은In order to accomplish the above object, according to one embodiment of the present invention,

100μ의 페트(PET)를 롤 또는 시트지 형태로 준비하는 이형필름 준비단계(S100);A release film preparation step (S100) of preparing 100 占 퐉 PET (PET) in the form of a roll or a sheet paper;

이형필름 상부에 실리콘(200)을 도포하여 실리콘층(200)을 형성하는 실리콘층 형성단계(S200);A silicon layer forming step (S200) of forming a silicon layer (200) by applying silicon (200) on the release film;

칠판 등에 스티커를 점착할 수 있도록 리버블층(300, 점착층)을 형성하는리버블층 형성단계(S300);A rebubbing layer forming step (S300) of forming a rebubbing layer (300, adhesive layer) so that a sticker can be adhered to a blackboard or the like;

리버블층 상부에 쿠션효과를 주는 캐스팅을 형성하는 단계로, 캐스팅을 1m/μ 두께로 도포한 후 자외선을 조사하여 경화시키는 캐스팅층 형성단계(S400);Forming a casting for imparting a cushioning effect to an upper portion of the rebubbed layer, the casting layer forming step (S400) of applying a casting to a thickness of 1 m / 占 퐉 and curing by irradiating ultraviolet rays;

캐스팅층 상부에 각종 디자인을 인쇄하는 인쇄층 형성단계(S500);A printing layer forming step (S500) of printing various designs on the casting layer;

인쇄된 인쇄물이 박피 등으로 회손되는 것을 방지하기 위하여 투명필름층을 형성하는 것으로, 0.2의 투명필름을 인쇄물 상부에 접착하는 투명필름층 형성단계(S600);A transparent film layer forming step (S600) of forming a transparent film layer so as to prevent printed printed matter from being peeled off by peeling or the like, and adhering 0.2 transparent film to the top of the printed material;

디자인에 맞춰 스티커를 이형필름층에서 탈거할 수 있도록 펀치를 이용하여 도무송을 형성하는 도무송 형성단계(S700)를 포함하는 것을 특징으로 한다.(S700) for forming an envelope using a punch so that the sticker can be removed from the release film layer in accordance with the design.

그리고 이형필름(100)을 준비하는 단계(S100)와; 이형필름 상부에 스티커의 탈착을 용이하게 하는 실리콘(200)을 도포하여 실리콘층(200)을 형성하는 실리콘층 형성단계(S200)와; 칠판 등에 점착할 수 있도록 하는 리버블층(300)을 형성하는 리버블층(300) 형성단계(S300)와; 쿠션효과를 주는 캐스팅 층을 형성하는 캐스팅 층 형성단계(S400)와; 각종 디자인을 인쇄하는 인쇄층 형성단계(S500)와; 인쇄물을 보호하는 투명필름층을 형성하는 투명필름층 형성단계(S600)와; 디자인에 맞취 스티커를 이형필름층에서 탈거할 수 있도록 도무송을 형성하는 도무송 형성단계(S700)로 제작되는 것을 특징으로 한다.And preparing a release film (100) (S100); A silicon layer forming step (S200) of forming a silicon layer (200) by applying silicon (200) on the release film to facilitate detachment of the sticker; (S300) of forming a rebubled layer (300) to be adhered to a blackboard or the like; A casting layer forming step (S400) of forming a casting layer which gives a cushioning effect; A printing layer forming step (S500) of printing various designs; A transparent film layer forming step (S600) of forming a transparent film layer for protecting the printed matter; (S700) for forming an adhesive film so that the sticker can be removed from the release film layer according to the design.

본 발명에 따르면, 본 발명 유희용 스티커 제작방법은 유아나 어린이들이 칠판 등에 붙여 놀이를 하는 스티커를 장시간 점착할 수 있는 효과가 있다.According to the present invention, the method for manufacturing a sticker for amusement according to the present invention has an effect that an infant or a child sticks a sticker to play on a blackboard for a long time.

그리고 부분적으로 볼륨감을 갖도록 볼록한 두께 편차를 갖는 입체 형상의 질감 표현이 가능하고, 점착력을 높일 수 있어 쉽게 분리 이탈되지 않아 고급스러움은 물론 품질이 향상되며, 물기에 강하고, 원하는 형상과 모양의 무늬를 자유롭게 연출할 수 있는 효과가 있다.And it is possible to express texture of three-dimensional shape with convex thickness deviation so that it has a volume feeling in part, and it can increase adhesion and can not easily separate and separated. Therefore, quality is improved as well as quality. There is an effect that can be produced freely.

또한, 자석식 스티커의 자석을 대신하여 리버블로 점착할 수 있도록 함으로써 제작비용을 절감할 수 있는 효과가 있다.In addition, it is possible to re-adhere to the magnetic sticker in place of the magnets, thereby reducing manufacturing costs.

도 1은 본 발명에 따른 스티커를 나타낸 단면도,
도 2는 본 발명에 따른 스티커를 나타낸 사시도,
도 3은 본 발명에 따른 스티커의 제조과정을 나타낸 블록도.1 is a sectional view showing a sticker according to the present invention,
2 is a perspective view showing a sticker according to the present invention,
3 is a block diagram illustrating a process of manufacturing a sticker according to the present invention.

본 명세서 및 청구범위에서 사용하는 용어나 단어는, 통상적이거나 사전적인 의미로 한정하여 해석될 것이 아니라, '발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다.'라는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms and words used in the present specification and claims should not be construed to be limited to ordinary or dictionary meanings, but the inventor may appropriately define the concept of the term to describe its invention in the best way Can be interpreted as a meaning and a concept consistent with the technical idea of the present invention.

또한, 본 명세서에 기재된 실시 예와 도면에 도시한 구성은, 본 발명의 바람직한 실시 예에 불과한 것일 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어 이들을 대체할 수 있는 다양한 균등물과 변형 예들이 있을 수 있음을 이해해야 한다.It should be noted that the embodiments described in the present specification and the configurations shown in the drawings are merely preferred embodiments of the present invention and do not represent all the technical ideas of the present invention, It should be understood that various equivalents and modifications may be present.

이하, 첨부한 도면을 참조하여 본 발명의 바람직한 실시 예를 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명은 도 1 ~ 도 3에 도시한 바와 같이, 스티커는 페트(PET)로 이루어진 이형필름층(100)과; 이형필름층에서 스티커의 탈착을 용이하게 하는 실리콘층(200)과; 칠판 등에 점착할 수 있도록 하는 리버블층(300)과; 쿠션효과를 주는 캐스팅 층과(400); 각종 디자인이 인쇄된 인쇄층(500)과; 인쇄물을 보호하는 투명필름층(600)으로 구성된다.1 to 3, the sticker includes a release film layer 100 made of PET; A silicone layer (200) that facilitates removal of the sticker from the release film layer; A rebubbed layer 300 for adhering to a blackboard or the like; A casting layer (400) providing a cushioning effect; A printed layer 500 on which various designs are printed; And a transparent film layer 600 for protecting the printed matter.

상기에 따른 스티커는 이형필름(100)을 준비하는 단계(S100)와; 이형필름 상부에 스티커의 탈착을 용이하게 하는 실리콘(200)을 도포하여 실리콘층(200)을 형성하는 실리콘층 형성단계(S200)와; 칠판 등에 점착할 수 있도록 하는 리버블층(300)을 형성하는 리버블층(300) 형성단계(S300)와; 쿠션효과를 주는 캐스팅 층을 형성하는 캐스팅 층 형성단계(S400)와; 각종 디자인을 인쇄하는 인쇄층 형성단계(S500)와; 인쇄물을 보호하는 투명필름층을 형성하는 투명필름층 형성단계(S600)와; 디자인에 맞취 스티커를 이형필름층에서 탈거할 수 있도록 도무송을 형성하는 도무송 형성단계(S700)로 제작된다.The sticker according to the present invention includes a step (S100) of preparing a release film (100); A silicon layer forming step (S200) of forming a silicon layer (200) by applying silicon (200) on the release film to facilitate detachment of the sticker; (S300) of forming a rebubled layer (300) to be adhered to a blackboard or the like; A casting layer forming step (S400) of forming a casting layer which gives a cushioning effect; A printing layer forming step (S500) of printing various designs; A transparent film layer forming step (S600) of forming a transparent film layer for protecting the printed matter; (S700) for forming an adhesive film so that the sticker can be removed from the release film layer in accordance with the design.

이형필름 준비단계(S100)는 100μ의 페트(PET)를 롤 또는 시트지 형태로 준비하는 단계이다.The release film preparing step (S100) is a step of preparing PET (PET) in the form of a roll or a sheet.

실리콘층 형성단계(S200)는 이형필름 상부에 실리콘(200)을 도포하여 실리콘층(200)을 형성하는 단계로, 스티커를 이형필름에서 탈착을 용이하게 하기 위한 것이다.The silicon layer forming step (S200) is a step for forming the silicon layer (200) by applying the silicone (200) on the release film to facilitate detachment of the sticker from the release film.

리버블층 형성단계(S300)는 칠판 등에 스티커를 점착할 수 있도록 리버블층(300, 점착층)을 형성하는 단계로, 리버블을 0.1mm로 도포하여 형성한다.In the rebubbing layer formation step (S300), a rebubbing layer (300, adhesive layer) is formed so that a sticker can be adhered to a blackboard.

리버블층은 이후 형성되는 캐스팅층을 고정하는 가교역할을 한다.The rebubbed layer serves as a bridge for fixing the casting layer to be formed later.

캐스팅층 형성단계(S400)는 리버블층 상부에 쿠션효과를 주는 캐스팅을 형성하는 단계로, 캐스팅을 1m/μ 두께로 도포한 후 자외선을 조사하여 경화시킨다.The casting layer forming step (S400) is a step of forming a casting which gives a cushioning effect to the upper part of the rebubbed layer. The casting is applied at a thickness of 1m / 占 퐉 and then cured by irradiating ultraviolet rays.

인쇄층 형성단계(S500)는 캐스팅층 상부에 각종 디자인을 인쇄하는 단계이다.The printing layer forming step (S500) is a step of printing various designs on the casting layer.

본 발명에 캐스팅에 디자인을 인쇄하는 작업이 종래의 전사지 없이도 이루어질 수 있기 때문에 공정 횟수가 종래에 비해 감소한다. In the present invention, since the operation of printing the design on the casting can be performed without the conventional transfer paper, the number of processes is reduced compared with the conventional method.

투명필름층 형성단계(S600)는 인쇄된 인쇄물이 박피 등으로 회손되는 것을 방지하기 위하여 투명필름층을 형성하는 것으로, 0.2의 투명필름을 인쇄물 상부에 접착하는 것이다. The transparent film layer forming step (S600) is to form a transparent film layer to prevent printed prints from being peeled off by peeling or the like.

도무송 형성단계(S700)는 디자인에 맞춰 스티커를 이형필름층에서 탈거할 수 있도록 펀치를 이용하여 도무송을 형성하는 단계이다.In step S700, the adhesive is formed by using a punch so that the sticker can be removed from the release film layer according to the design.

100 : 이형필름층 200 : 실리콘층
300 : 리버블층 400 : 캐스팅층
500 : 인쇄층 600 : 투명필름층
700 : 도무송100: release film layer 200: silicon layer
300: Rebible layer 400: Casting layer
500: printing layer 600: transparent film layer
700: Domou Song

Claims (2)

100μ의 페트(PET)를 롤 또는 시트지 형태로 준비하는 이형필름 준비단계(S100);
이형필름 상부에 실리콘(200)을 도포하여 실리콘층(200)을 형성하는 실리콘층 형성단계(S200);
칠판 등에 스티커를 점착할 수 있도록 리버블층(300, 점착층)을 형성하는리버블층 형성단계(S300);
리버블층 상부에 쿠션효과를 주는 캐스팅을 형성하는 단계로, 캐스팅을 1m/μ 두께로 도포한 후 자외선을 조사하여 경화시키는 캐스팅층 형성단계(S400);
캐스팅층 상부에 각종 디자인을 인쇄하는 인쇄층 형성단계(S500);
인쇄된 인쇄물이 박피 등으로 회손되는 것을 방지하기 위하여 투명필름층을 형성하는 것으로, 0.2의 투명필름을 인쇄물 상부에 접착하는 투명필름층 형성단계(S600);
디자인에 맞춰 스티커를 이형필름층에서 탈거할 수 있도록 펀치를 이용하여 도무송을 형성하는 도무송 형성단계(S700)를 포함하는 것을 특징으로 하는 유희용 스티커 제작방법.
A release film preparation step (S100) of preparing 100 占 퐉 PET (PET) in the form of a roll or a sheet paper;
A silicon layer forming step (S200) of forming a silicon layer (200) by applying silicon (200) on the release film;
A rebubbing layer forming step (S300) of forming a rebubbing layer (300, adhesive layer) so that a sticker can be adhered to a blackboard or the like;
Forming a casting for imparting a cushioning effect to the upper portion of the rebubbed layer, the casting layer forming step (S400) comprising coating a casting with a thickness of 1 m / 占 퐉 and curing by irradiating ultraviolet rays;
A printing layer forming step (S500) of printing various designs on the casting layer;
A transparent film layer forming step (S600) of forming a transparent film layer so as to prevent printed printed matter from being peeled off by peeling or the like, and adhering 0.2 transparent film to the top of the printed material;
(S700) for forming an envelope using a punch so that the sticker can be removed from the release film layer in accordance with the design.
이형필름(100)을 준비하는 단계(S100)와;
이형필름 상부에 스티커의 탈착을 용이하게 하는 실리콘(200)을 도포하여 실리콘층(200)을 형성하는 실리콘층 형성단계(S200)와;
칠판 등에 점착할 수 있도록 하는 리버블층(300)을 형성하는 리버블층(300) 형성단계(S300)와;
쿠션효과를 주는 캐스팅 층을 형성하는 캐스팅 층 형성단계(S400)와; 각종 디자인을 인쇄하는 인쇄층 형성단계(S500)와;
인쇄물을 보호하는 투명필름층을 형성하는 투명필름층 형성단계(S600)와;
디자인에 맞취 스티커를 이형필름층에서 탈거할 수 있도록 도무송을 형성하는 도무송 형성단계(S700)로 제작되는 것을 특징으로 하는 유희용 스티커.
Preparing a release film (100) (S100);
A silicon layer forming step (S200) of forming a silicon layer (200) by applying silicon (200) on the release film to facilitate detachment of the sticker;
(S300) of forming a rebubled layer (300) to be adhered to a blackboard or the like;
A casting layer forming step (S400) of forming a casting layer which gives a cushioning effect; A printing layer forming step (S500) of printing various designs;
A transparent film layer forming step (S600) of forming a transparent film layer for protecting the printed matter;
(S700) for forming an adhesive film so that the sticker can be removed from the release film layer in accordance with the design.
KR1020160092127A 2016-07-20 2016-07-20 Process for making sticker KR20180010043A (en)