KR20170112558A - Pressure-sensitive adhesive composition - Google Patents

Abstract

The present application provides a pressure-sensitive adhesive composition capable of effectively blocking water or oxygen introduced into the organic electronic device from the outside and capable of realizing not only durability reliability under harsh conditions such as high temperature and high humidity but also excellent optical characteristics and an adhesive film comprising the same .

Description

[0001] PRESSURE-SENSITIVE ADHESIVE COMPOSITION [0002]

The present application relates to a pressure-sensitive adhesive composition, an adhesive film comprising the same, and an organic electronic device including the same.

An organic electronic device (OED) refers to an apparatus that includes an organic material layer that generates holes and electrons to generate an alternating current. Examples thereof include a photovoltaic device, a rectifier, A transmitter and an organic light emitting diode (OLED).

Organic light emitting diodes (OLEDs) among the above organic electronic devices have a lower power consumption and a faster response speed than conventional light sources, and are advantageous for thinning display devices or illumination. In addition, OLEDs are expected to be applied in various fields covering various portable devices, monitors, notebooks, and televisions because of their excellent space utilization.

In commercialization of OLEDs and expansion of applications, the main problem is durability. Organic materials and metal electrodes contained in OLEDs are very easily oxidized by external factors such as moisture. Thus, products containing OLEDs are highly sensitive to environmental factors. Accordingly, various methods have been proposed to effectively block penetration of oxygen or moisture from the outside into organic electronic devices such as OLEDs.

In recent years, attempts have been made to use a PIB (polyisobutylene) resin as a pressure-sensitive adhesive composition for sealing. PIB (polyisobutylene) resin is superior to acrylic resin in blocking ability to prevent the influence of moisture and active oxygen, and is transparent and has almost no effect of corrosion. However, it causes problems such as restriction of the hardener content due to compatibility problems and consequent reduction of the water barrier effect due to the problem of lowering the crosslink density.

Patent Document 1 is a film of an adhesive encapsulating composition and an organic electroluminescent device, which is an adhesive based on PIB (polyisobutylene) and has poor processability and poor reliability under high temperature and high humidity conditions.

Therefore, it is required to develop an encapsulant that can maintain the reliability at high temperature and high humidity conditions and has excellent optical characteristics, while securing the required lifetime in the organic electronic device and effectively blocking the penetration of moisture.

Korean Patent Publication No. 2008-0088606

The present application provides a pressure-sensitive adhesive composition which is capable of effectively blocking moisture or oxygen introduced into an organic electronic device from the outside, has excellent durability and optical characteristics, and an adhesive film containing the pressure-sensitive adhesive composition.

The present application relates to a pressure-sensitive adhesive composition. The pressure-sensitive adhesive composition can be applied to encapsulating or encapsulating organic electronic devices such as, for example, OLEDs. For example, the pressure-sensitive adhesive composition may be applied to encapsulate the front surface of an organic electronic device, or may be applied to a surface of the substrate on which the device is formed, to be located on the opposite side of the surface on which the device is formed.

As used herein, the term " organic electronic device " refers to an article or apparatus having a structure including an organic material layer that generates alternating electric charges using holes and electrons between a pair of electrodes facing each other, But are not limited to, photovoltaic devices, rectifiers, transmitters, and organic light emitting diodes (OLEDs). In one example of the present invention, the organic electronic device may be an OLED.

In the present application, the pressure-sensitive adhesive composition may include a base resin containing an olefin-based compound as a polymerization unit and at least one unsaturated group being epoxidized and a curable resin. The base resin may be a homopolymer derived from an olefinic compound or a copolymer obtained by polymerizing other polymerizable monomer. The polymer may have at least one unsaturated group, and the base resin of the present application may be epoxidized with at least one unsaturated group. The unsaturated group may be, for example, a carbon-carbon double bond. In one example, the epoxidation may refer to a reaction in which one atom of oxygen is added to the ethylene bond to produce the 1,2-epoxide. The application of the present application increases the compatibility of the two resins by using the epoxidized base resin together with the curable resin, thereby achieving excellent moisture barrier properties and maintaining heat resistance and durability at high temperature and high humidity.

In embodiments of the present application, the base resin comprises a resin derived from a mixture of monomers, and the mixture may comprise olefinic compounds. The olefin-based compound may have an isoolefin monomer component or a multi-olefin monomer component having at least 4 to 7 carbon atoms. The isoolefin may be present, for example, in an amount ranging from 0.5 to 50% by weight, from 5 to 40% by weight or from 10 to 30% by weight, based on the total monomer weight. The multi-olefin-derived component may be present in the range of 60 to 100 wt%, or 70 to 90 wt%. The present application can control the degree of epoxidation modification by controlling the content of the monomer.

Examples of the isoolefin include isobutylene, 2-methyl-1-butene, 3-methyl-1-butene, Vinyltrimethylsilane, hexene, or 4-methyl-1-pentene. The multi-olefins may have from 4 to 14 carbon atoms and include, for example, isoprene, butadiene, 2,3-dimethyl-1,3-butadiene, myrcene, 6,6-dimethyl-fulvene, hexadiene, cyclopentadiene, or Piperylene may be exemplified. Other polymerizable monomers such as styrene and dichlorostyrene can also be homopolymerized or copolymerized.

The base resin in the present application may comprise an olefinic compound homopolymer or copolymer. As mentioned above, the isobutylene-based olefinic resin or polymer may refer to an olefinic resin or polymer comprising isobutylene repeat units and at least one other polymerizable unit.

In the present application, the base resin may be a butyl rubber or a branched butyl rubber. Exemplary base resins are unsaturated butyl rubbers such as olefins or copolymers of isoolefins and multi olefins. Examples of the base resin to be contained in the pressure-sensitive adhesive composition of the present invention include styrene-isoprene-styrene copolymer, poly (isobutylene-co-isoprene), polyisoprene, polybutadiene, polyisobutylene, Natural rubbers, butyl rubbers, and mixtures thereof. Base resins useful in the present application may be prepared by any suitable means known in the art and the present invention is not limited by the method of making base resins here.

In one example, the base resin may have an epoxy equivalent of from 100 g / eq to 2000 g / eq, or from 500 g / eq to 2000 g / eq. As described above, the base resin may be epoxidized and may have an epoxy functional group in the main chain of the base resin due to epoxidation. By controlling the epoxy equivalent of the base resin within the above range, the present application provides a highly reliable encapsulation material by maintaining compatibility with a curable resin and forming a dense cross-linked density to increase internal stress and realize excellent transparency.

In the present application, the base resin may have a number average molecular weight to such an extent that the pressure-sensitive adhesive composition can be formed into a film. For example, the base resin may have a number average molecular weight of 10,000 to 1,000,000 50,000 to 900,000, 100,000 to 800,000, or 150,000 to 700,000. By controlling the number average molecular weight of the base resin in the above range, the present application can maintain excellent heat resistance, endurance reliability and optical characteristics at high temperature and high humidity simultaneously after being applied as an encapsulating material.

In embodiments of the present application, the pressure sensitive adhesive composition may comprise a curable resin. In one example, the curable resin may have, but is not limited to, a cyclic structure in which the ring constituent atoms within the molecular structure are in the range of 3 to 10 or 4 to 9. Further, the curable resin may have the annular structure even after the pressure-sensitive adhesive is cured. The annular structure may be alicyclic. The curable resin of the above structure can realize a stable crosslinking structure against external factors such as shrinkage and expansion even after the pressure-sensitive adhesive is crosslinked or cured.

In embodiments of the present application, the curable resin may be UV curable, but it is not limited thereto and may be thermosetting. The curable resin may include at least one curable functional group. The curable functional group may be at least one selected from, for example, a glycidyl group, an isocyanate group, a hydroxyl group, a carboxyl group, an amide group, an epoxide group, a cyclic ether group, a sulfide group, an acetal group and a lactone group. The curable resin realizes excellent heat resistance at high temperature and high humidity by realizing a degree of crosslinking suitable for the pressure-sensitive adhesive.

In one example, the curable resin may be an alicyclic epoxy compound or a curable oligomer comprising at least one cyclic ether group.

Examples of alicyclic epoxy compounds include 3,4-epoxycyclohexylmethyl 3 ', 4'-epoxycyclohexanecarboxylate (EEC) and derivatives, dicyclopentadiene dioxide and derivatives, vinylcyclohexyldioxide and derivatives, 1, 4-cyclohexanedimethanol bis (3,4-epoxycyclohexanecarboxylate) and derivatives, but are not limited thereto.

The curable oligomer may have a weight average molecular weight ranging from 1,000 to 100,000, from 2,000 to 90,000, from 3,000 to 80,000, from 4,000 to 70,000, or from 5,000 to 60,000. Within the above-mentioned molecular weight range, the pressure-sensitive adhesive composition of the present application is cured to have excellent water barrier properties, and excellent heat resistance and adhesiveness can be realized.

Examples of the curable oligomer include commercially available products such as EHPE3150, GT401, PB3600, and PB4700 manufactured by DAICEL. Also included are ether group-containing monomers such as M100 (7-oxabicyclo [4.1.0] heptan-3-yl) methyl methacrylate) or celloxide 2000 (4-vinyl-1-cyclohexene 1,2- Cationically-curable oligomers prepared by radical polymerization or the like using an ether group-containing monomer having a cyclic structure.

The curable resin may be contained in an amount of 20 to 50 parts by weight, 25 to 45 parts by weight or 30 to 40 parts by weight based on 100 parts by weight of the base resin. Within the above-mentioned weight range, the present application can be applied to encapsulating an organic electronic device to realize an endurance reliability at high temperature and high humidity together with excellent moisture barrier properties.

In one example, the pressure sensitive adhesive composition of the present application may further comprise a tackifier. The tackifier may be a resin produced by reacting a terpene compound with an aromatic compound. When the tackifier has an aromatic group in the molecular structure, the compatibility between the base resin having a low polarity and the curable resin having a high polarity can be improved. The aromatic compound may include a reactive functional group. Examples of the functional group include a hydroxyl group, a carboxyl group, and an amine group. In the present application, the cross-linking density of the whole pressure-sensitive adhesive can be improved due to the reactive functional group. Specifically, the aromatic compound may be phenol, and the tackifier may be a terpene phenolic resin. The present application provides a pressure-sensitive adhesive excellent in adhesive strength as well as superior compatibility with a base resin and a curable resin by using the terpene phenolic resin as a tackifier, thereby improving crosslink density and durability .

The tackifier may be a resin produced by reacting a terpene compound with a phenolic compound. Terpene compound may represent a compound having a basic skeleton n (C ₅ H ₈₎ is 2 or more isoprene (C ₅ H ₈₎ combination. In the above, n may be two or more. In the above, the terpene compound may be at least one selected from the group consisting of? -Pinene,? -Pinene,? -Carenylene, 3-carene, D-limonene and dipentene. The phenolic compound may also be selected from the group consisting of phenol, para-tert-butylphenol (PTBP), 4-t-octylphenol (PTOP), 4- -pentyl phenol (PNPP), and para-n-hexyl phenol (PNHP).

The tackifier may be included in an amount of 30 to 90 parts by weight, 30 to 80 parts by weight, 35 to 70 parts by weight, 35 to 60 parts by weight or 38 to 50 parts by weight based on 100 parts by weight of the base resin. Within the above weight range, the pressure-sensitive adhesive can excellently realize compatibility between the base resin and the curable resin.

In the embodiments of the present application, the pressure-sensitive adhesive composition may further include a curing agent or an initiator depending on the kind of the base resin and the curable resin. For example, a curing agent capable of reacting with the aforementioned base resin and the curable resin to form a crosslinked structure or the like or a cationic initiator capable of initiating a curing reaction may be further included. As the cationic initiator, a cationic photopolymerization initiator or a cationic thermal initiator may be used.

As the curing agent, there can be used one or more kinds of epoxy curing agents known in the art, such as amine curing agents, imidazole curing agents, phenol curing agents, phosphorus curing agents and acid anhydride curing agents, but not limited thereto .

In one example, as the curing agent, an imidazole compound which is solid at room temperature and has a melting point or a decomposition temperature of 80 ° C or higher can be used. Such compounds include, for example, 2-methylimidazole, 2-heptadecylimidazole, 2-phenylimidazole, 2-phenyl-4-methylimidazole or 1-cyanoethyl- For example, but not limited to,

The content of the curing agent may be selected depending on the composition of the composition, for example, the type and ratio of the base resin and the curable resin. For example, the curing agent may be contained in an amount of 1 to 20 parts by weight, 1 to 10 parts by weight, or 1 to 5 parts by weight based on 100 parts by weight of the curable resin. However, the weight ratio may be changed depending on the types and ratios of the functional groups of the base resin and the curable resin or the compound, the crosslinking density to be implemented, and the like.

In one example, when the curable resin is a resin that can be cured by irradiation with active energy rays, for example, a cationic photopolymerization initiator may be used as the initiator.

As the cationic photopolymerization initiator, an ionized cationic initiator or an organic silane or latent sulfonic acid series based onium salt or organometallic salt series or a nonionic ionic cationic photopolymerization initiator can be used. As the initiator of the onium salt series, diaryliodonium salt, triarylsulfonium salt or aryldiazonium salt can be exemplified, and the initiation of the organometallic salt series Examples of the initiator of the organosilane series include o-nitrobenzyl triaryl silyl ether, triaryl silyl peroxide, and the like. Or an acyl silane, and examples of the initiator of the latent sulfuric acid series include, but are not limited to,? -Sulfonyloxy ketone or? -Hydroxymethylbenzoin sulfonate, and the like .

In one example, an ionized cationic photopolymerization initiator may be used as the cationic initiator.

In one example, the initiator may be included in an amount of 0.1 to 10 parts by weight, 0.1 to 7 parts by weight, or 0.1 to 6 parts by weight based on 100 parts by weight of the curable resin.

In the present specification, unless otherwise specified, the unit " weight part " means a weight ratio between the respective components.

The pressure-sensitive adhesive composition according to the present application may contain various additives in addition to the above-mentioned composition, in addition to the effects of the above-mentioned invention, depending on the application, the kind of the resin component and the process for producing the pressure-sensitive adhesive layer described later. For example, the pressure-sensitive adhesive composition may be contained in an appropriate range depending on the intended properties of a moisture adsorbent, an inorganic filler, a coupling agent, a crosslinking agent, a curing substance, a UV stabilizer or an antioxidant.

In one example, the pressure-sensitive adhesive composition may satisfy the following general formula (1).

[Formula 1]

DELTA X ≤ 1000 mu m

After △ X in the general formula 1, form a crosslinked product of the pressure-sensitive adhesive composition as a pressure-sensitive adhesive layer having a thickness of 30 ㎛, and attached to a glass plate to stand for 24 hours to a base film to form the pressure-sensitive adhesive layer on one side with an adhesive area 1cm ² , And the pushing distance of the pressure-sensitive adhesive layer when the load of 1.5 kg was applied at 25 DEG C for 1000 seconds. The pushing distance represented by the general formula 1 may be 1000 mu m or less, and may be 10 to 900 mu m, 100 to 880 mu m, or 200 to 850 mu m. That is, the present application secures an appropriate range of crosslinking structure and degree of crosslinking, thereby controlling the pushing distance to 1000 占 퐉 or less. In particular, when the adhesive film is applied to an organic electronic device, excellent moisture barrier properties, And optical characteristics.

Further, the pressure-sensitive adhesive composition according to the present application may have a gel content of 30% or more according to the following general formula (2).

[Formula 2]

Gel content (% by weight) = B / A x 100

In the general formula 2, A represents the mass of the pressure-sensitive adhesive composition, and B represents the mass of the pressure-sensitive adhesive composition. The pressure-sensitive adhesive composition is immersed in toluene at 25 ° C for 24 hours, filtered through a mesh of 200 mesh (pore size 74 μm) The dry mass of the insoluble component of the pressure-sensitive adhesive composition.

The gel content represented by the general formula 2 may be 30% to 70%, 35% to 65%, or 40% to 60%. That is, the present invention can provide a pressure-sensitive adhesive having excellent cross-linking structure and degree of crosslinking by controlling the gel content within the above range.

The present application also relates to an adhesive film. The pressure-sensitive adhesive film may include a pressure-sensitive adhesive layer containing the pressure-sensitive adhesive composition described above. The structure of the pressure-sensitive adhesive film of the present application is not particularly limited, but may be, for example, a base film or a release film (hereinafter sometimes referred to as " first film "); And a pressure-sensitive adhesive layer formed on the base film or the release film.

The pressure-sensitive adhesive film of the present application may further include a base film or a release film (hereinafter sometimes referred to as " second film ") formed on the pressure-sensitive adhesive layer.

The specific kind of the first film that can be used in the present application is not particularly limited. In the present application, for example, a general polymer film in this field can be used as the first film. In the present application, for example, the base material or the release film may be a polyethylene terephthalate film, a polytetrafluoroethylene film, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a polyvinyl chloride film, , An ethylene-vinyl acetate film, an ethylene-propylene copolymer film, an ethylene-ethyl acrylate copolymer film, an ethylene-methyl acrylate copolymer film, or a polyimide film. In addition, a suitable mold release treatment may be performed on one or both surfaces of the base film or release film of the present application. Examples of the releasing agent used in the releasing treatment of the base film include an alkyd type, a silicone type, a fluorine type, an unsaturated ester type, a polyolefin type, a wax type and the like. Among them, the use of an alkyd type, a silicone type or a fluorine type releasing agent But is not limited thereto.

Also, the kind of the second film (hereinafter sometimes referred to as " cover film ") that can be used in the present application is not particularly limited either. For example, in the present application, as the second film, the same or a different kind as the first film may be used within the scope exemplified in the first film described above. In the present application, the second film may also be subjected to appropriate mold release treatment.

The thickness of the pressure-sensitive adhesive layer included in the pressure-sensitive adhesive film of the present application is not particularly limited and may be appropriately selected in accordance with the following conditions in consideration of the application to which the film is applied. The thickness of the pressure-sensitive adhesive layer included in the pressure-sensitive adhesive film of the present application may be about 5 占 퐉 to 200 占 퐉, preferably about 10 占 퐉 to 150 占 퐉.

In addition, the pressure-sensitive adhesive film may have excellent light transmittance with respect to the visible light region. In one example, the pressure-sensitive adhesive film of the present application can exhibit a light transmittance of 90% or more with respect to the visible light region. For example, the adhesive film may have a light transmittance of 92% or more or 95% or more with respect to the visible light region. Further, the pressure-sensitive adhesive film of the present application can exhibit low haze with excellent light transmittance. In one example, the adhesive film may exhibit a haze of 10% or less, 8% or less, 7% or less, 6% or less, 5% or less, 4% or less, or 3% or less. The optical characteristics may be measured at 550 nm using a UV-Vis spectrometer.

The present application also includes a substrate 21; An organic electronic device 23 formed on one surface of the substrate 21; And the above-described adhesive film (24) formed on the other surface of the substrate (21). Further, the sealing member 12 sealing the organic electronic device 23 may be further included. The sealing material may include, but is not limited to, the above-described pressure-sensitive adhesive composition.

The organic electronic device in the present application may be an organic light emitting diode.

The organic electronic device may further include a protective film for protecting the device on the organic electronic device.

The organic electronic device may further include a cover substrate 22 covering the top of the encapsulant 12.

The present application also relates to a method of manufacturing an organic electronic device, comprising the step of forming an adhesive film on the other side of a substrate on which an organic electronic element is formed, the adhesive film comprising the above-described adhesive composition. In one example, the manufacturing method may further include a step of crosslinking or curing the adhesive film.

In addition, the adhesive film exhibits excellent transparency and can be formed as a stable adhesive film regardless of the form of the organic electronic device such as top emission or bottom emission.

As used herein, the term " curing " means that the adhesive composition of the present invention forms a cross-linked structure through heating or UV irradiation, etc., and is produced in the form of a pressure-sensitive adhesive.

Specifically, a transparent electrode is formed on a glass or polymer film used as a substrate by a method such as vacuum deposition or sputtering. On the transparent electrode, a light-emitting organic material composed of a hole transporting layer, a light- And then an electrode layer is further formed on the electrode layer to form an organic electronic device.

Then, the adhesive film is placed on the other surface of the substrate, and the adhesive film is heated using a laminate or the like to press the adhesive film in a state of imparting fluidity, and the resin in the adhesive film can be crosslinked.

The present application provides a pressure-sensitive adhesive composition which is capable of effectively blocking moisture or oxygen introduced into an organic electronic device from the outside, has excellent durability and optical characteristics, and an adhesive film containing the pressure-sensitive adhesive composition.

1 is a cross-sectional view showing an organic electronic device according to one example of the present invention.

Hereinafter, the present invention will be described in more detail with reference to the following examples and comparative examples, but the scope of the present invention is not limited by the following examples.

Example  One

90 parts by weight of cyclohexane, 10 parts by weight of styrene-isoprene-styrene copolymer (SIS Zeon Quintac 3421, 14% by weight of styrene content, 3.3 parts by weight of formic acid and 7 parts by weight of hydrogen peroxide) , And an epoxidation reaction was carried out for 1 hour in a state where the temperature of the reaction vessel was maintained at 65 DEG C. Subsequently, the modified base resin 1 was obtained by precipitating in isopropyl alcohol.

100 g of the obtained base resin 1 was put in a mixing container and 35 parts by weight of an alicyclic epoxy compound (Celloxide 2021P, DAICEL) as a curable resin was added to the vessel in an amount of 100 parts by weight based on 100 parts by weight of the base resin. Further, a terpene phenol-based tackifier (DERTOPHENE T 115, manufactured by DRT) was added to the container in an amount of 40 parts by weight based on 100 parts by weight of the base resin. 1.8 parts by weight of a photoinitiator (Triarylsulfonium hexafluoroantimonate, Aldrich) based on 100 parts by weight of solid content of the curable resin was further added to the container.

A homogeneous pressure-sensitive adhesive composition solution (solvent: toluene) was prepared using a conventional mechanical stirrer as the mixing container.

The prepared solution was coated on the releasing surface of the releasing PET and dried (5 atm) in an oven at 70 캜 for 30 minutes to produce an adhesive film comprising a pressure-sensitive adhesive layer having a thickness of 30 탆. The properties of the produced film were measured for a sample irradiated with 2 J / cm ² (100 mW / cm ^{2 on the} A region basis) of ultraviolet rays under a nitrogen atmosphere.

Example  2

hydrogen peroxide was added in an amount of 3.5 parts by weight, and a pressure-sensitive adhesive film was prepared.

Example  3

A base resin was prepared in the same manner as in Example 1 except that SIS Zeon Quintac 3280 (styrene content: 25 wt%) was used as a styrene-isoprene-styrene copolymer, and an adhesive film was produced.

Comparative Example  One

hydrogen peroxide was added in an amount of 0.5 part by weight, to prepare a base resin and an adhesive film.

Comparative Example  2

An adhesive film was prepared in the same manner as in Example 1, except that a styrene-isoprene-styrene copolymer (SIS Zeon Quintac 3421 (styrene content: 14 wt%) was used instead of the base resin 1.

The pressure-sensitive adhesive compositions and pressure-sensitive adhesive films prepared in Examples and Comparative Examples were measured for physical properties as described below.

One. Gel content

Gel content (% by weight) = B / A x 100

B represents the mass of the pressure-sensitive adhesive composition; and B represents the mass of the pressure-sensitive adhesive composition obtained by immersing the pressure-sensitive adhesive composition in toluene at 25 ° C for 24 hours, filtering it with a mesh of 200 mesh (pore size 74 μm) It represents the dry weight of the insoluble fraction of the composition.

2. Creep

A substrate film having a thickness of 30 占 퐉 and a pressure-sensitive adhesive layer (width 1 cm, length 12 cm) formed on one side thereof, which was formed using the pressure-sensitive adhesive compositions of Examples and Comparative Examples, was attached to a glass plate at an adhesion area of 1 cm ² , aged for 24 hours, C, the pushing distance of the pressure-sensitive adhesive layer was measured when a load of 1.5 kg was applied for 1000 seconds. The base film used was a polyethylene terephthalate (PET) film.

3. Light transmittance  And Hayes

The adhesive films according to Examples and Comparative Examples were aged at 70 ° C for 5 minutes under a pressure of 5 atm, and haze and light transmittance were measured using Hazemeter (COH-400, Nippon Denshoku).

The above measurement results are summarized in Table 1 below.

Gel (%) Creep (탆) Haze (%) Light transmittance (%) Example 1 77.1 282 4.31 90.47 Example 2 72.97 308 7.72 90.89 Example 3 77.6 292 5.67 90.14 Comparative Example 1 33.2 Fail 6.52 91.13 Comparative Example 2 28 Fail 13.4 90.7

21: substrate
22: Cover substrate
23: Organic electronic device
24: Adhesive film
12: Encapsulation material

Claims (18)

A pressure-sensitive adhesive composition comprising an olefin-based compound as a polymerization unit, wherein at least one or more unsaturated groups are epoxidized and comprises a base resin and a curable resin. The pressure-sensitive adhesive composition according to claim 1, wherein the base resin has an epoxy equivalent of 100 g / eq to 2000 g / eq. The pressure-sensitive adhesive composition according to claim 1, wherein the base resin has a number-average molecular weight in the range of 10,000 to 1,000,000. The pressure-sensitive adhesive composition according to claim 1, wherein the curable resin is contained in an amount of 20 to 50 parts by weight based on 100 parts by weight of the base resin. The pressure-sensitive adhesive composition according to claim 1, wherein the curable resin has a cyclic structure having a ring-constituting atom within the molecular structure within a range of 3 to 10. The pressure-sensitive adhesive composition according to claim 1, wherein the curable resin has a cyclic structure after curing of the pressure-sensitive adhesive. The pressure-sensitive adhesive composition according to claim 1, wherein the curable resin comprises at least one curable functional group. The pressure-sensitive adhesive composition according to claim 7, wherein the curable functional group is at least one selected from a glycidyl group, an isocyanate group, a hydroxyl group, a carboxyl group, an amide group, an epoxide group, a cyclic ether group, a sulfide group, an acetal group and a lactone group. The pressure-sensitive adhesive composition according to claim 1, wherein the curable resin comprises an alicyclic epoxy compound. The pressure-sensitive adhesive composition according to claim 1, wherein the curable resin is UV-curable. The pressure-sensitive adhesive composition according to claim 1, further comprising a tackifier. The pressure-sensitive adhesive composition according to claim 11, wherein the tackifier is contained in an amount of 30 to 90 parts by weight based on 100 parts by weight of the base resin. The pressure-sensitive adhesive composition according to claim 1, further comprising a curing agent or an initiator. A pressure-sensitive adhesive film having a pressure-sensitive adhesive layer comprising the pressure-sensitive adhesive composition according to claim 1. 15. The adhesive film according to claim 14, wherein the adhesive film exhibits a haze of 10% or less. 15. The adhesive film according to claim 14, wherein the adhesive film exhibits a light transmittance of 90% or more with respect to the visible light region. Board; An organic electronic device formed on one surface of the substrate; And an adhesive film according to claim 14 formed on the other surface of the substrate. Forming an adhesive film according to claim 14 on another surface of a substrate on which an organic electronic element is formed on one surface; And a step of curing the adhesive film.