KR20170084494A - Fabrics for clothing and clothing including the same - Google Patents
Fabrics for clothing and clothing including the same Download PDFInfo
- Publication number
- KR20170084494A KR20170084494A KR1020160003590A KR20160003590A KR20170084494A KR 20170084494 A KR20170084494 A KR 20170084494A KR 1020160003590 A KR1020160003590 A KR 1020160003590A KR 20160003590 A KR20160003590 A KR 20160003590A KR 20170084494 A KR20170084494 A KR 20170084494A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- garment
- riblet
- cloth
- clothing
- Prior art date
Abstract
본 발명은 리블렛이 적용된 의류용 천 및 이를 포함하는 의류에 관한 것이다. 리블렛이 적용된 의류용 천은 기저층; 상기 기저층 상면에 적층되는 투습 방수층; 상기 투습 방수층 상면에 적층되는 접착층 및 상기 접착층 상면에 리블렛(riblets)이 형성된 배리어 층이 적층된 것을 포함하는 것일 수 있다.
본 발명에 따른 리블렛이 적용된 의류용 천은 리블렛 효과를 나타내는 것이어서 외풍에 의해 갖혀있는 공기층이 생김으로서 보온성이 향상되고 외부의 찬 공기와의 마찰감소로 대류효과가 저하되면서 방한성이 향상되는 의류 즉, 보온성 의류 또는 방한용 의류를 제조할 수 있게 한다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a garment cloth to which a levlet is applied and a garment including the same. The garment cloth to which the riblet is applied comprises a base layer; A moisture permeable waterproof layer laminated on the upper surface of the base layer; And an adhesive layer laminated on the moisture permeable and waterproof layer and a barrier layer having riblets formed on the adhesive layer.
The garment cloth to which the riblet according to the present invention is applied exhibits the Librett effect, so that an air layer formed by the draft is formed, thereby improving the warmth and reducing the friction with the outside cold air, , A warm-up garment or a winter garment.
Description
본 발명은 의류용 천 및 이를 포함하는 의류에 관한 것으로 상세하게는 리블렛(riblets)이 적용된 의류용 천 및 이를 포함하는 의류에 관한 것이다. 보다 상세하게는 리블렛 형상을 적용하여 공기저항을 감소시켜 방한성 또는 보온성을 높일 수 있는 의류용 천과 상기 보온성이 향상된 의류용 천을 포함하여 제작된 방한성 또는 보온성이 향상된 의류에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a garment cloth and a garment including the same, and more particularly, to a garment cloth to which riblets are applied and a garment including the garment cloth. More particularly, the present invention relates to a garment having improved warmth or warmth, comprising a garment cloth and a garment cloth having improved warmth and / or warmth by reducing the air resistance by applying a riblet shape.
최근 의류 시장은 패션상품으로서의 의류뿐만 아니라 다기능성을 가진 의류에 대한 수요가 높아지고 있다. 즉, 의류 제품 군이 세분화 되면서 단순한 기능성뿐만 아니라 다양한 소재 및 패턴의 개발로 다양한 개성을 표현할 수 있는 제품 군으로 발전하고 있다.In recent years, there has been an increasing demand for the apparel market as well as apparel as a fashion product as well as multi-functional apparel. That is, as the clothing product group is divided, the product group is developed as a product group that can express various characteristics by developing not only simple functionality but also various materials and patterns.
한편, 동절기에 작업 또는 산행하는 사람에 있어 방한용 의류는 매우 필요한 의복 중 하나이다. 이러한 방한용 의류는 통상적으로 외부에서 불어오는 바람을 막아주고, 몸에서 발생되는 땀을 배출하는 기능을 가지며, 방한용 의류의 내부에는 체온을 유지할 수 있도록 보온재가 채워져 있다.On the other hand, cold weather clothing is one of the most necessary clothes for people working or hiking in winter. Such cold clothing generally has a function of preventing wind blowing from the outside and discharging sweat generated from the body, and the inside of the cold weather garment is filled with a heat insulating material to maintain the body temperature.
이러한 방한용 의류의 경우 작업 또는 산행하는 사람뿐만 아니라 일상생활에서도 널리 보급되고 있으며, 최근에는 하나의 겨울철 패션상품으로 인식되고 있는 실정이다.Such winter clothes are widely used not only for people working or hiking, but also for everyday life, and recently, they are recognized as a fashion item for winter.
따라서 종래 보다 더 높은 보온 효과를 나타내면서도 패션적인 연출이 용이한 다양한 소재의 개발이 요구되고 있다.Therefore, it is required to develop various materials that exhibit a warming effect that is higher than that of the prior art, but are easily fashionable.
이와 관련된 선행기술을 보면, 선행기술 1은 자동보온가변식 방안점퍼에 관한 것으로 전기에 의해 발열되는 발열패드를 포함하는 방한 점퍼에 관한 것으로 이는 방한효과를 높이는 장점이 있으나 점퍼 자체의 방한성 향상 등에 관한 것은 아니다.The prior art 1 relates to an automatic warming variable jumper, which is related to a warming jumper including a heat generating pad which is generated by electricity, which has an advantage of improving a cold effect, It is not.
선행기술 2는 방한 점퍼에 관한 것으로 안감에 서로 이격되게 부착된 복수개의 충전재가 포함되는 것으로 보온성과 쾌적함을 증진시키는 것을 효과로 하고 있다. 상기 선행기술 2에 의하는 경우 상기 다수개의 충전재를 통해 방한성을 높이는 장점이 될 수 있다.Prior art 2 relates to a warm-up jumper, in which a plurality of fillers are attached to a lining so as to be spaced apart from each other, thereby improving warmth and comfort. According to the prior art 2, it is advantageous to increase the cold resistance through the plurality of fillers.
상기 선행기술을 볼 때 방한성을 향상시킨 의류 제작을 위한 다양한 시도가 활발하게 이루어지고 있다는 것을 알 수 있다. 다만, 최근 다양한 소재가 적용되어 의류 자체의 방한성 또는 보온성을 높이면서도 다양한 패션연출이 용이하게 이루어질 수 있는 의류 시장의 경향을 고려할 때, 보다 많은 소재 또는 외피 형상을 갖춘 의류용 천이 제공될 필요가 있다.It can be seen from the above-mentioned prior art that various attempts have been actively made to manufacture garments having improved cold resistance. However, in view of the tendency of the apparel market where various kinds of materials are applied to increase the warmth or warmth of the garment itself and can easily produce a variety of fashion displays, it is necessary to provide clothing cloths having more materials or shell shapes .
따라서 상기 적용되는 천의 다양성을 통해 상기 천을 포함하는 의류의 기능성과 가공성을 향상시킬 수 있고, 패션적인 연출이 가능하게 함으로서 다양한 상품의 제공이 가능할 수 있도록 하는 연구가 필요하다.Therefore, it is necessary to study the diversity of the cloth to improve the functionality and workability of the garment including the cloth, and to provide a variety of products by enabling fashionable production.
본 발명의 목적은 바람의 유동저항을 감소시켜 보온성 및 방한성을 향상시키고 바람에 의한 낙상 등의 사고를 방지할 수 있는 리블렛이 적용된 의류용 천을 제공하는 것이다.It is an object of the present invention to provide a garment cloth to which a levlet is applied that can reduce wind flow resistance to improve warmth and cold resistance and prevent accidents such as falling due to wind.
본 발명의 다른 목적은 상기 리블렛이 적용된 의류용 천을 이용하여 제조한 의류를 제공하는 것이다.Another object of the present invention is to provide a garment manufactured using the garment cloth to which the above-mentioned levlet is applied.
상기 목적을 달성하기 위하여, 본 발명의 일 실시예에 따른 리블렛이 적용된 의류용 천은 기저층; 상기 기저층 상면에 적층되는 투습 방수층; 상기 투습 방수층 상면에 적층되는 접착층 및 상기 접착층 상면에 리블렛(riblets)이 형성된 배리어 층이 적층된 것을 포함하는 것일 수 있다.In order to achieve the above object, a garment cloth to which a riblet is applied according to an embodiment of the present invention includes a base layer; A moisture permeable waterproof layer laminated on the upper surface of the base layer; And an adhesive layer laminated on the moisture permeable and waterproof layer and a barrier layer having riblets formed on the adhesive layer.
상기 리블렛이 적용된 의류용 천은 상기 배리어 층 상면에 상기 PVC, ABS, PET 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나를 코팅층으로 더 포함하고, 상기 접착층 및 배리어 층 사이에 일면 이상이 코팅된 필름 층을 더 포함하는 필름층을 더 포함하는 것일 수 있다.The garment cloth to which the levelet is applied may further comprise at least one selected from the group consisting of PVC, ABS, PET, and a mixture thereof on the upper surface of the barrier layer, and a film And a film layer further comprising a layer.
본 발명의 다른 일 실시예에 따른 상기 리블렛이 적용된 의류용 천을 포함하는 의류는 상기 리블렛이 적용된 의류용 천을 외피의 전면 또는 일부분 이상에 포함하는 것일 수 있다.The garment including the garment cloth to which the riblet is applied may include the garment cloth to which the riblet is applied in at least a part or whole of the envelope according to another embodiment of the present invention.
상기 리블렛이 적용된 의류용 천을 포함하는 의류는 아웃도어 의류인 것일 수 있다.The garment including the garment cloth to which the levlet is applied may be an outdoor garment.
이하, 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
상기 목적을 달성하기 위하여, 본 발명의 일 실시예에 따른 리블렛이 적용된 의류용 천은 기저층; 상기 기저층 상면에 적층되는 투습 방수층; 상기 투습 방수층 상면에 적층되는 접착층 및 상기 접착층 상면에 리블렛(riblets)이 형성된 배리어 층이 적층된 것을 포함하는 것일 수 있다.In order to achieve the above object, a garment cloth to which a riblet is applied according to an embodiment of the present invention includes a base layer; A moisture permeable waterproof layer laminated on the upper surface of the base layer; And an adhesive layer laminated on the moisture permeable and waterproof layer and a barrier layer having riblets formed on the adhesive layer.
상기 기저층은 기본천을 구성하는 층을 말하며, 상기 기저층은 천연섬유, 합성섬유(合成纖維), 인조섬유(人造纖維) 및 이들의 혼합물을 포함하는 천 기타 의류 등에 사용할 수 있는 기재를 모두 포함하는 것으로 본다.The base layer refers to a layer constituting the base fabric, and the base layer includes all the base materials which can be used for natural fibers, synthetic fibers (synthetic fibers), man-made fibers, see.
상기 투습 방수층은 투습효과를 가지면서도 방수효과를 가지는 합성천일 수 있다. 투습성이 높으면 착용감과 쾌적함을 높일 수 있고 방수효과를 통해 외부의 물이 상기 기저층으로 유입되는 것을 방지할 수 있다. 바람직하게 상기 투습 방수층은 폴리테트라플루오로에틸렌 (polytetrafluoroethylene; PTFE)을 포함하는 것일 수 있다. 이 경우 방수 및 방습성이 우수할 뿐만 아니라 기계적 내구성이 우수할 수 있고 나아가 투습 효과가 우수하여 인체에서 배출된 땀 등을 쉽게 배출할 수 있다는 장점을 가진다.The breathable waterproof layer may be a synthetic fabric having a waterproof effect and a waterproof effect. If the moisture permeability is high, the feeling of comfort and comfort can be increased, and water from outside can be prevented from flowing into the base layer through the waterproof effect. Preferably, the moisture permeable waterproof layer comprises polytetrafluoroethylene (PTFE). In this case, it has an advantage of being excellent in waterproof and moisture-proof property, excellent in mechanical durability, and further excellent in moisture permeability, so that sweat discharged from the human body can be easily discharged.
상기 접착층은 기본적으로 상기 투습 방수층과 상기 리블렛층 사이에 접착 및 투습 및 보온효과를 유지하기 위한 것으로 바람직하게 상기 접착층은 발포 우레탄 수지 100 중량부에 대하여 실리콘 수지 30 내지 80 중량부 및 에폭시 수지 40 내지 130 중량부가 포함된 혼합 접착제를 사용할 것일 수 있다. 상기 혼합 접착제를 사용하는 경우 상기 투습 방수층이 기계적 마모 등으로 손상되는 경우에도 일정시간 동안 방수효과를 나타냄으로서 기저층을 보호할 수 있다. 또한, 단열효과와 기계적 내구성이 높아지는 장점을 가진다.The adhesive layer is basically used to maintain adhesion, moisture permeability and warming effect between the moisture permeable and waterproof layer and the above-mentioned levlet layer. Preferably, the adhesive layer is composed of 30 to 80 parts by weight of silicone resin and 40 to 80 parts by weight of epoxy resin per 100 parts by weight of the foamed urethane resin. 130 parts by weight may be used. When the mixed adhesive is used, even when the moisture permeable and waterproof layer is damaged due to mechanical wear or the like, the waterproof effect is exhibited for a certain period of time, so that the base layer can be protected. In addition, it has an advantage of increasing the adiabatic effect and mechanical durability.
더 바람직하게 상기 접착층은 상기 발포 우레탄 수지 100 중량부에 대하여 하이드라진 하이드레이트(HYDRAZINE HYDRATE) 0.1 내지 0.01 중량부가 더 포함되는 것일 수 있다. 상기 하이드라진 하이드레이트(HYDRAZINE HYDRATE)가 상기 범위로 포함되는 경우 접착력과 내구성을 저하시키지 않으면서도 접착층에 일정한 간격으로 발포기공이 형성되기 때문에 상기 접착층의 방수효과가 유지될 수 있고 보온성 향상에 보다 적합할 수 있다.More preferably, the adhesive layer may further contain 0.1 to 0.01 parts by weight of hydrazine hydrate (HYDRAZINE HYDRATE) relative to 100 parts by weight of the foamed urethane resin. When the hydrazine hydrate is contained in the above range, since the foamed pores are formed at a constant interval in the adhesive layer without deteriorating the adhesive strength and durability, the waterproof effect of the adhesive layer can be maintained and it is more suitable for improving warmth have.
특히 상기 접착층은 상기 투습 방수층 위에 위치하여 상기 투습 방수층을 통해 배출된 습기가 상기 접착층에 발포기공으로 이동하여 방수효과와 방습효과를 유지하게 할 수 있다. 따라서 상기 리블렛이 적용된 의류용 천으로 의류를 제조하는 경우 착용자로부터 배출된 습기가 상기 투습 방지층을 통해 접착층의 발포기공에 이동하여 상기 착용자의 쾌적함을 유지할 수 있게 할 수 있다.Particularly, the adhesive layer is located on the moisture permeable and waterproof layer, and the moisture discharged through the moisture permeable and waterproof layer can move to the foamed pores in the adhesive layer to maintain a waterproof effect and a moisture-proof effect. Therefore, when the garment is manufactured from the garment cloth to which the levret is applied, the moisture discharged from the wearer moves to the foam pores of the adhesive layer through the moisture permeation preventive layer, so that the comfort of the wearer can be maintained.
상기 배리어 층은 상기 접착층 상면에 적층되면서 상기 접착층과 반대되는 면에 리블렛(riblets)이 형성된 것이다.The barrier layer is formed on the upper surface of the adhesive layer, and riblets are formed on a surface opposite to the adhesive layer.
리블렛이란 주 유동방향을 따라 홈이 파진 표면구조를 말하며, 하기의 도 3과 같은 형상이 이에 해당한다. 상기 리블렛은 리블렛 현상을 유도한다. 리블렛 구조는 상어 비늘 표면의 작은 돌기에서 발견되어 현재 MRF(Micro Riblet Film)와 같은 형태로 수영복이나 비행기 표면 등에 사용되고 있다. 상기 리블렛 현상이란 상기 리블렛이 표면 주변의 유동구조를 변화시킴으로써 물체에 작용하는 항력을 줄여주는 현상을 말한다.The riblet is a surface structure in which grooves are formed along the main flow direction, and corresponds to the shape shown in FIG. 3 below. The levlet induces a levlet phenomenon. The riblet structure is found in small projections on the surface of shark scales and is currently used in the form of MRF (Micro Riblet Film) for swimwear and airplane surfaces. The Librett phenomenon refers to a phenomenon in which the Librett reduces the drag acting on an object by changing the flow structure around the surface.
즉 상기 리블렛의 현상을 흐름방향과 동일하게 물체의 표면에 1mm 내외의 미세한 홈을 촘촘하게 설치하면 상기 물체 주위의 흐름이 원활하게 증가되어 표면 마찰항력이 감소된다. 상기 리블렛의 대표적인 형상으로 원형(○), 사각형(□), 삼각형(△)이 사용되고 있다.That is, if the development of the libretto is finely provided with fine grooves of about 1 mm on the surface of the object in the same direction as the flow direction, the flow around the object smoothly increases and the surface frictional drag decreases. (∘), a square (□), and a triangle (△) are used as a typical shape of the above-mentioned levlet.
상기 리블렛은 천연 또는 합성천에 가공을 통하여 일면에 상기 리블렛이 형성된 것일 수 있다. 상기 리블렛을 형성하는 방법은 코팅 또는 압출성형 등을 사용할 수 있으며, 해당 분야에서 통상의 지식을 가진 자가 사용할 수 있는 방법을 모두 포함하는 것으로 해석한다.The above-mentioned lyblet may be a natural or synthetic fabric which is processed to have the above-mentioned levlet formed on one side thereof. The method of forming the above-described liget may be coating or extrusion molding, and is interpreted to include all methods that can be used by those having ordinary knowledge in the field.
상기 천의 표면에 상기 리블렛 구조가 포함됨에 따라 상기 천의 표면을 유동하는 바람 기타 외풍의 저항감소로 외풍과 대류현상에 의한 열손실을 방지할 수 있으며, 상기 외풍과 상기 리블렛 구조 사이에 공기층이 형성되어 보온효과가 더 높아질 수 있는 장점이 있다.As the riblet structure is included on the surface of the cloth, it is possible to prevent the heat loss due to the draft and the convection due to the decrease in the resistance of the wind or other wind flowing on the cloth surface, An air layer is formed and the warming effect can be further enhanced.
바람직하게 상기 리블렛은 원형, 반구형 또는 구형으로 형성된 것일 수 있다. 일반적으로 삼각형이 마찰항력 감소를 위해 많이 사용되는 것이지만 보온성 및 방한성을 높이기 위한 구성으로서는 원형, 반구형 또는 구형이 적합할 수 있다.Preferably, the riblet may be circular, hemispherical or spherical. Generally, triangles are widely used for reducing friction drag, but circular, hemispherical or spherical shapes may be suitable for the construction for enhancing warmth and warmth.
따라서 상기 리블렛은 천연 또는 PVC 등의 합성천 위에 구형 실리카(silica)가 일정한 간격으로 배열되고, 상기 구형 실리카는 평균직경이 0.1 내지 5mm인 것이고, 비표면적인 50 내지 300(m2/g)인 것일 수 있다. 나아가 상기 구형 실리카는 콜로이달 실리카 및 제2인산나트륨을 100 : 0.1 내지 100 : 0.01 중량비로 혼합된 혼합물을 포함하는 함침액에 함침된 후 건조된 것일 수 있다. The spherical silica has an average diameter of 0.1 to 5 mm and a specific surface area of 50 to 300 (m 2 / g). The spherical silica has an average diameter of 0.1 to 5 mm, Lt; / RTI > Furthermore, the spherical silica may be impregnated with impregnation solution containing a mixture of colloidal silica and dibasic sodium phosphate in a weight ratio of 100: 0.1 to 100: 0.01 and dried.
이 경우 상기 구형 실리카는 기공이 상기 콜로이달 실리카 반응물에 의해 채워지면서 기계적인 내구성이 급격히 높아지므로 외부 충격에 의해 깨지지 않게 된다. 특히 상기 범위에 의하는 경우 상기 제2인산나트륨이 포함되면서 상기 구형 실리카 내부의 함침액의 경도가 증가하여 기계적 내구성이 급격히 높아질 수 있다. 상기 함침액에서 제2인산나트륨이 상기 범위보다 적게 포함되는 경우 기계적 내구성 향상 효과가 저하되고 상기 범위를 초과하여 포함되는 경우 상기 콜로이달 실리카가 경화되지 않을 수 있다.In this case, since the spherical silica is filled with the colloidal silica reaction product, the mechanical durability of the spherical silica is rapidly increased, so that the spherical silica is not broken by the external impact. Particularly in the above-mentioned range, the hardness of the impregnation solution in the spherical silica increases due to the inclusion of the second sodium phosphate, and the mechanical durability can be drastically increased. If the impregnating solution contains less than the above range of sodium phosphate, the effect of improving the mechanical durability is deteriorated. If the impregnating solution is contained in excess of the above range, the colloidal silica may not be cured.
상기 구형 실리카를 사용하여 구형의 리블렛 구조를 형성하는 경우 구형 실리카의 사용으로 천을 리블렛 구조로 성형하는 경우에 비하여 보온효과가 더 높아질 수 있다. 나아가 상기 함침액에 색소를 사용하여 다양한 디자인의 연출이 가능하다는 장점이 있다. 대류에 의한 열손실 방지와 방한 또는 보온효과가 높아지는 장점을 가진다.When the spherical silica is used to form a spherical lyblet structure, the use of spherical silica may provide a greater effect of heat retention than the case of forming the cloth into a riblet structure. Furthermore, there is an advantage that a variety of designs can be produced by using a dye in the impregnation solution. It has the advantage of preventing heat loss due to convection and increasing the effect of cold or warming.
상기 리블렛이 적용된 의류용 천은 상기 배리어 층 상면에 상기 PVC, ABS, PET 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나를 코팅층으로 더 포함하고, 상기 접착층 및 배리어 층 사이에 일면 이상이 코팅된 필름 층을 더 포함하는 필름층을 더 포함하는 것일 수 있다.The garment cloth to which the levelet is applied may further comprise at least one selected from the group consisting of PVC, ABS, PET, and a mixture thereof on the upper surface of the barrier layer, and a film And a film layer further comprising a layer.
상기 리블렛 층이 상기 구형 실리카에 의해 형성되는 경우 상기 코팅층을 포함하여 상기 리블렛 층이 외부에 의한 충격으로 손상되는 일을 방지할 수 있다.When the riblet layer is formed of the spherical silica, it is possible to prevent the riblet layer including the coating layer from being damaged by external impact.
상기 필름층은 기본적으로 배리어 층 밖의 수분이 안쪽으로 통과하지 못하도록 하는 방수층의 역할을 하며, 일정한 탄성을 가지면서 상기 리블렛에 외부로부터 기계적 충격이 가해진 경우 이를 완화시켜 상기 리블렛 형상에 대한 내구성을 높일 수 있다. 따라서 상기 필름은 우레탄 필름인 것일 수 있다.The film layer basically serves as a waterproof layer that prevents moisture from passing outside the barrier layer. When the mechanical impact is exerted on the lyblet from the outside with a certain elasticity, durability against the shape of the lyblet is improved . Therefore, the film may be a urethane film.
상기 코팅은 방수기능을 할 수 있는 코팅이 이루어진 것이며, 라미네이팅 기타 해당 분야에서 통상의 지식을 가진 자가 사용하는 코팅방법을 모두 포함하는 것으로 본다.The coating is a coating capable of waterproofing, and is considered to include all coating methods used by those skilled in the art, such as laminating.
본 발명의 다른 일 실시예에 따른 상기 리블렛이 적용된 의류용 천을 포함하는 의류는 상기 리블렛이 적용된 의류용 천을 외피의 전면 또는 일부분 이상에 포함하는 것일 수 있다.The garment including the garment cloth to which the riblet is applied may include the garment cloth to which the riblet is applied in at least a part or whole of the envelope according to another embodiment of the present invention.
상기 일부분은 공기저항이 많은 부분에 사용하는 것이 바람직하다. 따라서 자켓이나 점퍼 등과 같은 상의의 경우 어깨, 팔꿈치, 가슴 부위에 상기 리블렛이 적용된 의류용 천이 포함되는 것일 수 있다.It is preferable that the part is used for a part having a large air resistance. Accordingly, in the case of a jacket, a jumper, or the like, a shoulder, an elbow, or a chest may include a garment cloth to which the above-mentioned levlet is applied.
상기 리블렛이 적용된 의류용 천을 포함하는 의류는 아웃도어 의류인 것일 수 있다.The garment including the garment cloth to which the levlet is applied may be an outdoor garment.
상기 리블렛이 적용된 의류용 천을 포함하는 의류는 상기 리블렛이 적용된 의류용 천의 사용으로 방한성 및 보온성이 우수할 뿐만 아니라 투습성이 좋고 방수성이 우수하여 기능성 아웃도어용 의류에 사용할 수 있다.The garment including the garment cloth to which the levelet is applied is excellent in the cold and warmth due to the use of the garment cloth to which the riblet is applied, and is also excellent in moisture permeability and waterproof property, so that it can be used in clothes for functional outdoor wear.
나아가 상기 리블렛이 적용됨에 따라 공기저항이 감소할 수 있으므로 산악 등반 등 등산용 아웃도어용 의류에 있어 강풍에 의해 넘어지는 사고를 방지할 수 있다는 장점을 가진다.Furthermore, since the air resistance can be reduced as the above-mentioned levlet is applied, it has an advantage of being able to prevent an accident that falls due to strong winds in outdoor clothing for mountain climbing and other mountain climbing.
본 발명 전반에 걸쳐 기재한 상기 아웃도어용 의류란 옥외나 야외에서 입을 수 있는 의류를 말하며, 등산, 캠핑, 레저 등의 활동을 하는데 있어 주로 입는 의류를 포함하는 것으로 정의한다.The outdoor clothing described throughout the present invention refers to clothing that can be worn outdoors or outdoors and is defined to include clothing mainly worn for activities such as climbing, camping, and leisure.
상기 리블렛이 적용된 의류용 천을 포함하는 의류는 소매 부분이 스판텍스(spandex)로 이루어진 것일 수 있다.The garment including the garment cloth to which the levelet is applied may be one in which the sleeve portion is made of spandex.
본 발명에 따른 리블렛이 적용된 의류용 천은 리블렛 효과를 나타내는 것이어서 외풍에 의해 갖혀있는 공기층이 생김으로서 보온성이 향상되고 외부의 찬 공기와의 마찰감소로 대류효과가 저하되면서 방한성이 향상되는 의류 즉, 보온성 의류 또는 방한용 의류를 제조할 수 있게 한다.The garment cloth to which the riblet according to the present invention is applied exhibits the Librett effect, so that an air layer formed by the draft is formed, thereby improving the warmth and reducing the friction with the outside cold air, , A warm-up garment or a winter garment.
또한 상기 리블렛은 외부 공기와의 유동마찰 감소로 강풍에 의한 낙상 등의 사고를 방지할 수 있어 상기 리블렛이 적용된 의류용 천을 사용하여 등산복, 야외복 등의 아웃도어용 의류에 사용할 수 있다.In addition, the riblet can prevent accidents such as falling due to strong winds due to reduction of the flow friction with the outside air, and thus can be used for clothes for outdoor wear such as climbing clothes, outdoor clothes and the like using the clothing cloth to which the riblet is applied.
본 발명의 따른 리블렛이 적용된 의류용 천을 이용하여 제조된 의류의 경우 보온성 및 방한성이 높아질 수 있으며, 상기 천을 다양한 디자인의 패턴으로서 사용할 수 있어 고기능성과 함께 다양한 패턴 및 디자인을 연출할 수 있는 의류 특히 아웃도어용 의류에 적용할 수 있다.The clothing manufactured using the garment cloth to which the riblet according to the present invention is applied can be improved in heat retention and cold resistance, and the cloth can be used as a pattern of various designs, so that a garment capable of producing various patterns and designs, It can be applied to clothes for door.
도 1은 본 발명의 일 실시예에 따른 리블렛이 적용된 의류용 천의 구성에 관한 것이다.
도 2는 본 발명의 일 실시예에 따른 리블렛이 적용된 의류용 천의 구성에 관한 것이다.
도 3은 리블렛 형상에 관한 그림이다.FIG. 1 is a view illustrating a configuration of a garment cloth to which a levlet is applied according to an embodiment of the present invention.
FIG. 2 is a view illustrating a configuration of a garment cloth to which a levlet is applied according to an embodiment of the present invention.
Fig. 3 is a diagram relating to the shape of the rivlet.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, embodiments of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.
[[ 제조예Manufacturing example : : 실시예Example 및 And 비교예Comparative Example 제조] Produce]
본 발명에 따른 리블렛이 적용된 의류용 천의 보온성을 평가하기 위해 실시예 1 내지 4와 비교예 1 및 2를 하기의 표 1과 같이 구성으로 적층된 천을 제조하였다.In order to evaluate the warmth of the garment cloth to which the riblet according to the present invention was applied, the laminated cloths of Examples 1 to 4 and Comparative Examples 1 and 2 were prepared as shown in Table 1 below.
- 기저층: 폴리에스테르 천- Base layer: polyester cloth
- 투습방수층: 고어텍스- Waterproof breathable layer: Gore-Tex
- 접착층 A: 우레탄 수지, 실리콘 수지 및 에폭시 수지 2: 0.9: 1.2 중량비로 혼합된 접착조성물을 도포하여 형성- Adhesive layer A: urethane resin, silicone resin and epoxy resin 2: 0.9: 1.2 by weight
- 접착층 B: 접착층 A의 조성물에 하이드라진 하이드레이트(HYDRAZINE HYDRATE) 첨가- Adhesive layer B: HYDRAZINE HYDRATE added to the composition of the adhesive layer A
- 배리어 층 A: PVC에 삼각형의 리블렛이 형성되도록 성형- Barrier Layer A: Molded to form a triplet of riblets on PVC
- 배리어 층 B: PVC에 원형의 리블렛이 형성되도록 성형- Barrier layer B: Molded to form a circular riblet on PVC
- 배리어 층 C: PVC에 콜로이달 실리카가 함침된 구형 실리카를 건조한 뒤 PVC에 일정한 간격으로 배치하여 리블렛을 형성.- Barrier layer C: Dry a spherical silica impregnated with colloidal silica in PVC and place it at regular intervals in PVC to form a rivet.
[[ 실험예Experimental Example : : 실시예Example 및 And 비교예의Comparative example 평가] evaluation]
상기 실시예 1 내지 4와 비교예 1 및 2를 점퍼의 어깨, 팔꿈치, 가슴 및 배부분에 부착하였고, 이에 따라 보온성, 공기에 대한 저항, 촉감, 내구성 및 디자인 구현성을 평가하였다. 평가된 사항은 실시예 1을 기준지수 50로 설정하였고, 상기 기준지수를 기준으로 상기 실시예 2 내지 4와 비교예 1 및 2에 대한 평가결과를 비교하여 1 내지 100으로 지수화 하여 표현하였다. 상기 지수는 높을수록 그 성능이 우수한 것이다.The above Examples 1 to 4 and Comparative Examples 1 and 2 were attached to the shoulder, elbow, chest and abdomen of the jumper, thereby evaluating warmth, resistance to air, touch, durability and designability. The evaluation items were set to a reference index of 50 in Example 1, and the evaluation results for Examples 2 to 4 and Comparative Examples 1 and 2 were compared based on the reference index, and indexed from 1 to 100. The higher the index, the better the performance.
또한 객관성을 높이기 위해 실시예 및 비교예의 구성을 알지 못하는 10인이 반복적으로 평가한 뒤 상기 지수에 대한 평균으로 나타낸 값을 표 2에 나타내었다.Table 2 shows values obtained by repeatedly evaluating 10 persons who did not know the composition of the examples and comparative examples to improve the objectivity, and the average value of the indexes.
보온성은 외부 온도에 비해 착용자가 느끼는 온기를 지수로 평가하여 판단하였고, 공기에 대한 저항은 같은 바람의 저항을 받았을 때 움직이거나 서있는데 편한 정도를 지수화 하여 평가하였다. 또한 촉감은 상기 실시예 부분을 손을 만져보면서 종래의 천재질과 비교하면서 촉감에 대한 선호도를 지수화 하여 평가하였다. 내구성은 상기 실시예 및 비교예에 대하여 기계적 충격을 가하면서 재질이 마모되는지 여부를 평가하고 이를 지수로 나타내었다. 디자인 구현성을 겉표면을 보면서 무늬나 패턴의 부가 등으로 다양한 디자인이 연출될 수 있는 정도를 평가하여 지수로 표현하였다.The warmth was assessed by evaluating the warmth felt by the wearer compared to the external temperature, and the resistance to air was assessed by indexing the degree of comfort when moving or standing while receiving the same wind resistance. In addition, the tactile sensation was evaluated by indexing the preference for the tactile sensation while comparing with the conventional tinnitus while touching the hand portion of the above embodiment. The durability was evaluated by evaluating whether or not the material is worn while applying a mechanical impact to the examples and the comparative examples and exposing it as an index. The degree to which various designs can be produced by adding patterns or patterns while looking at the surface of the design is evaluated and expressed as an index.
이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, Of the right.
Claims (4)
상기 배리어 층은 리블렛이 형성된 의류용 천.
상기 기저층 상면에 적층되는 투습 방수층;
상기 투습 방수층 상면에 적층되는 접착층 및
상기 접착층 상면에 리블렛이 형성된 배리어 층이 적층된 것을 포함하는
의류용 천천.A moisture permeable and waterproof layer disposed on the base layer, an adhesive layer disposed on the moisture permeable and waterproof layer, and a barrier layer disposed on the adhesive layer,
Wherein the barrier layer is formed of a riblet.
A moisture permeable waterproof layer laminated on the upper surface of the base layer;
An adhesive layer laminated on the moisture permeable waterproof layer and
And a barrier layer in which a riblet is formed on the upper surface of the adhesive layer
Thousands of clothes.
상기 배리어 층 상면에 상기 PVC(polyvinyl chloride), ABS(Acrylonitrile butadiene styrene), PET(Polyethylene terephthalate) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나를 코팅층으로 더 포함하고,
상기 접착층 및 배리어 층 사이에 일면 이상이 코팅된 필름층을 더 포함하는
의류용 천천.The method of claim 1, wherein
Wherein the barrier layer further comprises a coating layer selected from the group consisting of polyvinyl chloride (PVC), acrylonitrile butadiene styrene (ABS), polyethylene terephthalate (PET), and mixtures thereof,
Further comprising a film layer coated on at least one side between the adhesive layer and the barrier layer
Thousands of clothes.
의류용 천천을 포함하는 의류.A garment for a garment comprising a ribbing according to any one of claims 1 or 2,
Clothes containing clothing garments.
상기 리블렛이 적용된 의류용 천천을 포함하는 의류는
아웃도어 의류인 것인
의류용 천천을 포함하는 의류.The method of claim 3,
A garment comprising a clothing garment to which said levlet is applied
Outdoor clothing
Clothes containing clothing garments.