KR20170054000A

KR20170054000A - Eco-friendly surface finishing material sheet and manufacture method thereof

Info

Publication number: KR20170054000A
Application number: KR1020150156642A
Authority: KR
Inventors: 장영환
Original assignee: (주)아이.씨.씨; (주) 모드온
Priority date: 2015-11-09
Filing date: 2015-11-09
Publication date: 2017-05-17
Also published as: KR101792129B1

Abstract

The present invention relates to a surface finishing sheet comprising: paper impregnated with a urethane resin; a coating layer which is formed on one side of the paper, and is capable of re-painting; a UV paint film formed on the coating layer; and a PET layer formed on the paint film. The surface finishing foil of the present invention has an excellent effect of being clean, as if texture of the surface were painted, and improves surface smoothness of a product. Moreover, the surface finishing foil of the present invention enhances gloss and hardness as well as has excellent properties, compared to any other finishing sheets, such as abrasion resistance, scratch resistance, acid resistance, water resistance, and the like.

Description

TECHNICAL FIELD [0001] The present invention relates to a PET UV foil using an environmentally friendly finishing foil,

The present invention relates to a PET UV foil for introducing PET laminating and UV coating technology into an environmentally friendly finishing foil impregnated with urethane and exhibiting the effect of high gloss and matte paint texture, and a manufacturing method thereof .

In general, the surface materials used for furniture, interior and interior and exterior materials are dominated by natural veneer, PVC, coated paper, HPM, LPM and finishing foil. The double finishing foil has a high environmental friendliness by using paper as a base material, and has excellent textured surface and excellent workability. Finishing foil, which is mainly used nowadays, is generally used to impregnate strongly pressed paper with acrylic or urethane resin, then coat with lacquer, then dry and overlay onto PB or MDF, In order to enhance the hardness and physical properties while making the texture of the surface cleaner, it is necessary to carry out a secondary process such as UV coating and polyurethane coating on the board.

There is no problem when the general finishing foil manufactured only by impregnation and coating process is overlayed on PB or MDF and then used directly as furniture or interior and exterior materials. However, there is no problem in overlay adhesion on PB or MDF or UV coating on top of general finishing foil. A problem of coating failure occurs in the process. In addition, for UV coating and high gloss rendering, additional transportation costs for secondary processing and cost of raw materials due to the use of UV coatings and polyol are additionally incurred.

Especially unsaturated polyester resin used for paint coating contains a strong chemical substance, which is very odorous during operation. There is a problem that the gloss of the product is poor and it is not environmentally friendly and the process cost is expensive.

The present invention relates to a method for producing a finish finishing foil for re-coating to prevent the problem of poor coating in a secondary addition process through urethane impregnation and coating with a lacquer coating using all impregnating paper and printing paper, PET UV foil.

In order to achieve the above object, the present invention is characterized by comprising a paper impregnated with a urethane resin, a coating layer formed on one side of the paper, a UV paint film formed on the coating layer, and a PET layer laminated on the paint film And a surface finish sheet.

The PET to be laminated on the UV paint film is preferably biaxially stretched O-PET.

PET or O-PET is superior in scratch resistance, stain resistance and abrasion resistance to conventional resin products. O-PET is an amorphous resin copolymerized with terephthalic acid, ethylene glycol and cyclohexanedimethanol, Good workability, abrasion resistance and tensile strength.

The present invention also relates to a method of making a primary impregnating composition comprising impregnating paper with a primary impregnating composition; Drying the impregnated paper primarily; Impregnating and coating one side of the dried paper with a secondary coating composition comprising a water-soluble lacquer, water and a lacquer curing agent; Drying and cooling the coated paper to produce a finishing foil; Coating a coating surface of the finishing foil with a UV paint to form a UV paint film; A step of raising and laminating PET on the coating film of the finishing foil; Pressing the PET-bonded finishing foil through a roller device, and irradiating UV onto the roller-pressed finishing foil.

The primary impregnating composition is characterized by containing 70 to 85 wt% of a water-dispersible urethane resin, 14 to 25 wt% of water, 1.0 to 1.5 wt% of a plasticizer, and 0.5 to 1.0 wt% of a release agent, From 66 to 70 wt% of a water-soluble lacquer, from 26 to 28 wt% of water, and from 3 to 5 wt% of a lacquer curing agent.

In addition, the method may further include removing foreign substances on the coated surface before applying the UV paint on the coated surface of the finishing foil in the manufacturing process.

It is more preferable that the PET is O-PET (biaxially stretched) having higher strength than G-PET.

It is preferable that the UV irradiation is performed at 80 to 100 ° C for 2 to 7 seconds.

The surface finishing material sheet of the present invention is excellent in clean and excellent effect as if the surface of the surface is painted, improves smoothness of the product designation, improves gloss and hardness, And has better physical properties.

In addition, conventional conventional finishing foil or LPM sheet is bonded or laminated to the board, and then the existing troublesome processes such as polyurethane coating or UV coating are eliminated. Instead, the final surface finish is solved in the sheet manufacturing process, Machining and molding construction is possible.

In addition, for the purpose of manufacturing eco-friendly products based on paper and reducing the existing transportation costs and expenses for UV coating and polyurethane coating by pre-directing the glossiness through paper, PET lamination and UV coating in the production of the initial finishing foil do.

1 is a sectional view of a surface finishing sheet according to the present invention.
2 is a manufacturing process diagram showing a method of manufacturing a surface finishing sheet according to the present invention.
3 is a photograph of a surface finish sheet according to an embodiment of the present invention.
4 is a photograph of a case where PET is laminated on a general finishing material sheet.
5 to 8 are test report records of the indoor surface pollutants of the surface finishing material sheet according to the present invention.

The surface finishing sheet 100 of the present invention comprises a general printing paper 80, a paper 110 impregnated with a urethane resin, a coating layer 120 formed on one side of the paper, a UV coating film 130, and a PET layer 140 laminated on the paint film. (Fig. 1)

Wherein the surface finishing sheet comprises:

Impregnating the paper with the primary impregnating composition;

Drying the impregnated paper primarily;

Impregnating and coating one side of the dried paper with a secondary coating composition comprising a water-soluble lacquer, water and a lacquer curing agent;

Drying and cooling the coated paper to produce a finishing foil;

Coating a coating surface of the finishing foil with a UV paint to form a UV paint film;

A step of raising and laminating PET on the coating film of the finishing foil;

Passing the PET laminated finishing foil through a roller device to pressurize;

And irradiating the roller-pressed finishing foil with UV light.

The paper of the present invention uses an unprinted plain paper or an ordinary paper (70 to 80 g / m 2, printed) that has absorbency, and uses white paper, a wood grain pattern, It is possible.

Hereinafter, the manufacturing process of the surface finishing sheet of the present invention will be described in detail with reference to FIG.

1. First of origin Impregnation

The paper is impregnated with the primary impregnating composition. At this time, the type of paper is irrelevant, and a print paper may be used.

The primary impregnating composition comprises 70 to 85 wt% of a water dispersible urethane resin, 14 to 25 wt% of water, 10. 1 to 1.5 wt% of a plasticizer, and 0.5 to 1.0 wt% of a release agent. In the first impregnating composition, the water-dispersible urethane resin has a nonvolatile content of 34 to 36% and a viscosity of 20 CPS (at 25 캜), which is more effective in improving the adhesion, tensile strength and flexibility of the finish sheet than conventional acrylic resins.

The water content in the impregnating composition is preferably 14 to 25 wt%, and if the compounding ratio of water is too large, the impregnated paper has a small amount of solid content, so that adhesion at the time of hot pressing may not be properly performed. The plasticizer serves to further increase the flexibility and is preferably polyoxyethylene glycol (CAS-No.25322-68-3) and glycerine, and the releasing agent is preferably a release agent in which the roll- And serves to prevent sticking.

2. Drying

The primary impregnated paper is dried through an oven at 125-135 < 0 > C.

3. Secondary Impregnation And Coating

The primary dried paper is again impregnated and coated with the secondary impregnation and coating composition.

The secondary coating composition may comprise from 66 to 70 wt% of a water soluble lacquer, from 26 to 28 wt% of water, and from 3 to 5 wt% of a lacquer curing agent. When coating with a secondary coating composition containing water-soluble lacquer, the finishing foil becomes re-coatable, the UV paint film is applied, and after the curing, the close contact between the finishing foil and the paint film is improved, There is a good advantage. Water in the composition serves to adjust viscosity so that the coated surface can be spread evenly.

4. Secondary drying

The paper impregnated with the second impregnating composition is dried by passing through an oven at 140 to 160 ° C.

5. Cooling

The dried paper becomes a finishing foil that can be cooled and repainted.

6. Rewinding And Unwinding

The finishing foil is rewound and then unwound ready.

7. UV paint application

A UV paint is applied to the coated surface of the finishing foil to form a UV paint film. At this time, a step of removing foreign matter on the upper surface of the finishing foil may be added.

A coating film can be formed by coating a UV paint on the upper surface of the finishing foil in a uniform and uniform thickness by a roll method. According to this method, there is an advantage that the operation is easier than the curtain coater method, and the cost is also reduced.

8. PET Lyo

PET is laminated on the UV paint film.

PET is transparent and light, has no taste and odor, harmless to the human body, and has excellent physical properties such as abrasion resistance, scratch resistance, impact resistance, weather resistance, and chemical resistance, so that the physical properties of post-joint finishing foil can be improved.

The PET is preferably O-PET excellent in moldability, processability, abrasion resistance and tensile strength, and can be made into a transparent product.

9. Roller press

After the PET laminate is passed through the roller device, the roller is pressurized to flatten the surface to maintain the smoothness of the product surface, to make the product thickness uniform, and to prevent the foil from being easily deformed or peeled in the subsequent process.

10. UV irradiation

The finishing foil after the roller pressing is passed through the inside of the UV irradiator and irradiated with ultraviolet rays from the UV lamp to be dried and cured. The UV irradiation is preferably performed at 80 to 100 ° C for 2 to 7 seconds. When the irradiation temperature is less than 100 ° C or the irradiation time is less than 2 seconds, the curing treatment and the drying effect are lowered. When the irradiation temperature exceeds 150 ° C If the time exceeds 7 seconds, the shape of the foil may be deformed due to excessive heat treatment and the smoothness of the top surface of the PET may be deteriorated.

When the UV paint is cured and dried, it has a smooth surface with high gloss and has various physical properties such as durability, chemical resistance, fire resistance and acid resistance.

Hereinafter, the present invention will be described in more detail by way of examples.

Example 1: PET Lyo And UV coated surface finishes

(70 g / m < 2 >) in a state of being printed with aqueous ink was impregnated with a primary impregnation composition composed of 80% by weight of water-dispersible urethane resin, 17% of water, 1.2% by weight of plasticizer and 0.8% by weight of a release agent. The primary impregnated paper was dried in an oven at 130 캜. The dried paper was coated with a secondary coating composition consisting of 69 wt% water soluble lacquer, 27 wt% water and 4 wt% lacquer curing agent. The coated paper was again passed through an oven at 150 ° C. and then dried to produce a finishing foil capable of being repainted.

The finishing foil was subjected to rewinding and unwinding, and after removal of foreign substances on the upper surface, UV coating was uniformly applied on the coated surface in a roll manner to form a UV coating film.

Then, the PET was laminated on the UV paint film, the roller was pressurized to flatten the surface, the finishing foil was passed through the inside of the UV irradiator, and the UV lamp was irradiated with ultraviolet rays at 120 ° C to be dried and cured.

The finished surface finish sheet was clean as if the surface texture had been coated, the surface smoothness, gloss and hardness of the product were high, and it showed better physical properties than any finish sheet such as abrasion resistance, scratch resistance, acid resistance and water resistance . As shown in FIG. 3 (a), it was confirmed that the surface finishing sheet of Example 1 was not lifted or separated after it became a PET laminate.

When tested according to the analytical conditions of Figs. 6 and 7, as can be seen from the test results of Fig. 5 and Fig. 8, when the surface material of the present invention was used, the benzene, toluene, ethylbenzene, xylene, styrene, Formaldehyde was not detected and the amount of total volatile organic compounds detected was small. Therefore, it can be seen that the surface finishing material of the present invention is an eco-friendly product.

Example 2: PET Lyo And UV coated surface finishes

Except that the color of the paper of Example 1 and the color of the paper was brown. As shown in Fig. 3 (b), it was confirmed that the surface finishing material sheet was not lifted or separated after PET lamination.

Comparative Example One

(70 g / m < 2 >) printed with water-based ink was impregnated with an impregnation composition containing an acrylic resin. The impregnated paper was dried in an oven at 130 캜.

A UV paint film was uniformly coated on the coated surface of the finishing foil in a roll manner to form a UV paint film.

The finished surface finish sheet was lifted and separated as shown in Fig. 4, in which the finishing foil and the PET were not bonded together at all.

110: paper 120: coating layer
130: UV paint film 140: PET

Claims

A paper layer impregnated with a urethane resin, a coating layer formed on one side of the paper, a UV coating layer formed on the coating layer, and a PET layer laminated on the coating layer.

The surface finishing sheet according to claim 1, wherein the PET is O-PET.

Impregnating the paper with the primary impregnating composition;
Drying the impregnated paper primarily;
Impregnating and coating one side of the dried paper with a secondary coating composition comprising a water-soluble lacquer, water and a lacquer curing agent;
Drying and cooling the coated paper to produce a finishing foil;
Coating a coating surface of the finishing foil with a UV paint to form a UV paint film;
A step of raising and laminating PET on the coating film of the finishing foil;
Passing the PET laminated finishing foil through a roller device to pressurize;
And irradiating the roller-pressed finishing foil with UV light.

The method according to claim 3, wherein the primary impregnating composition is a water dispersible urethane resin 70 to 85 , 14 to 25 wt% of water, 1.0 to 1.5 wt% of a plasticizer, and 0.5 to 1.0 wt% of a release agent.

4. The method of claim 3, wherein the secondary coating composition comprises 66 to 70 wt% of a water soluble lacquer, 26 to 28 wt% of water, and 3 to 5 wt% of a lacquer curing agent.

4. The method of claim 3, further comprising removing foreign matter on the coated surface before applying the UV paint on the coated surface of the finishing foil.

The method of manufacturing a surface finishing sheet according to claim 3, wherein the PET is O-PET.

4. The method according to claim 3, wherein the UV irradiation is performed at 80 to 100 DEG C for 2 to 7 seconds.