KR20170044000A - A transfer paper for ceramic coated metal, the cooking container using the same and the manufacturing thereof - Google Patents

A transfer paper for ceramic coated metal, the cooking container using the same and the manufacturing thereof Download PDF

Info

Publication number
KR20170044000A
KR20170044000A KR1020160114967A KR20160114967A KR20170044000A KR 20170044000 A KR20170044000 A KR 20170044000A KR 1020160114967 A KR1020160114967 A KR 1020160114967A KR 20160114967 A KR20160114967 A KR 20160114967A KR 20170044000 A KR20170044000 A KR 20170044000A
Authority
KR
South Korea
Prior art keywords
transfer paper
ceramic coating
coating layer
layer
water
Prior art date
Application number
KR1020160114967A
Other languages
Korean (ko)
Other versions
KR101941747B1 (en
Inventor
박란수
박혜민
Original Assignee
박란수
박혜민
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박란수, 박혜민 filed Critical 박란수
Publication of KR20170044000A publication Critical patent/KR20170044000A/en
Application granted granted Critical
Publication of KR101941747B1 publication Critical patent/KR101941747B1/en

Abstract

The present invention relates to a transfer paper for ceramic coating, which includes: a transfer sheet; a pattern layer which is formed on the transfer sheet and includes a silicone resin and a heat resistant pigment; a water-soluble resin layer which is formed on the pattern layer; and a peeling type coating layer which is formed on the water-soluble resin layer, a cooking vessel using the same, and a manufacturing method thereof. If the transfer paper of the present invention is used in the cooking vessel, sufficient heat resistance and stain resistance required for the cooking vessel can be obtained.

Description

세라믹 코팅용 전사지, 이를 사용한 조리용기 및 조리용기의 제조방법{A TRANSFER PAPER FOR CERAMIC COATED METAL, THE COOKING CONTAINER USING THE SAME AND THE MANUFACTURING THEREOF}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a transfer sheet for ceramic coating, a cooking vessel using the same, and a manufacturing method of a cooking vessel,

본 발명은 세라믹 코팅용 전사지, 이를 사용한 조리용기 및 조리용기의 제조방법에 관한 것으로, 보다 자세하게는 조리용기의 세라믹 코팅층 상에 전사 인쇄를 통하여 무늬를 장식할 수 있는 세라믹 코팅용 전사지, 이를 사용한 조리용기 및 조리용기의 제조방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a transfer sheet for ceramic coating, a cooking vessel using the same, and a method of manufacturing a cooking vessel, and more particularly, to a transfer sheet for ceramic coating which can decorate patterns on a ceramic coating layer of a cooking vessel through transfer printing, And a method of manufacturing the container.

종래부터 알루미늄이나 철재의 표면에 세라믹 코팅을 하여 내식성을 향상시키고, 표면을 미려하게 처리하는 기술을 통하여, 알루미늄 조리기구나 난방용 난로등에 사용하여 왔다. Background Art [0002] Heretofore, the surface of aluminum or steel has been coated with a ceramic to improve the corrosion resistance, and has been used for an aluminum cooker, a heating furnace,

이러한 세라믹 코팅은 내열성, 내긁힘성 및 내오염성 등이 우수하고 다양한색상을 낼 수 있으며, 외관이 미려하므로 주방기구나 난로와 같은 열기구의 표면을 처리하는데 널리 이용되어 왔으나, 표면에 문양을 새겨 넣거나 계기판 등으로 나타낼 숫자를 새겨야 하는 경우, 내오염성이 너무 강하여 적당한 접착 방법이 없다는 문제점이 제기되고 있는 실정이다.These ceramic coatings are excellent in heat resistance, scratch resistance and stain resistance, can give various colors, and have been widely used to treat surfaces of hot air balloons such as kitchen utensils and stoves because of their beautiful appearance. However, When the number to be indicated by the instrument panel is to be inscribed, there is a problem that the stain resistance is too strong and there is no suitable bonding method.

특히, 종래의 방법으로 세라믹 코팅 상에 유기잉크를 사용하여 인쇄를 한 후, 소성을 하는 경우에는 유기잉크의 부착성이 나빠서 쉽게 벗겨지고, 인쇄된 잉크가 250℃ 이상의 고온에서 견딜 수가 없기 때문에 상용화되지 못한 문제점이 있다.Particularly, in the case of performing printing using an organic ink on a ceramic coating by a conventional method and then firing, since the adhesion of the organic ink is bad and peeling off easily, and the printed ink can not withstand a high temperature of 250 캜 or more, .

한국 공개 특허 제2011-0138400호Korea Patent Publication No. 2011-0138400

상기와 같은 종래기술의 문제점을 해결하고자, In order to solve the above problems of the prior art,

전사공정이 손쉽고, 세라믹 코팅층에 내열성, 내마모성, 내수성 및 내오염성이 우수하여 소비자가 요구하는 물성을 충족하는 세라믹코팅용 전사지 및 전사방법을 제공하는 것을 목적으로 한다.It is an object of the present invention to provide a transfer sheet for ceramic coating and a transfer method which is easy to transfer and has excellent heat resistance, abrasion resistance, water resistance and stain resistance on the ceramic coating layer and satisfies the property required by the consumer.

상기의 목적을 달성하기 위하여, In order to achieve the above object,

본 발명은 전사대지; 상기 전사대지 상에 형성되고, 실리콘 수지 및 내열성 안료를 포함하는 무늬층; 상기 무늬층 또는 전사대지 상에 형성되는 수용성 수지층; 및 상기 수용성 수지층 상에 형성되는 박리형 코팅층;을 포함하는 세라믹 코팅용 전사지를 제공한다.
The present invention relates to a transfer material; A pattern layer formed on the transferring material and including a silicone resin and a heat resistant pigment; A water-soluble resin layer formed on the pattern layer or transfer paper; And a peelable coating layer formed on the water-soluble resin layer.

또한, 본 발명은 a) 상기 전사지의 전사대지를 제거한 후, 세라믹 코팅층 상에 위치시킨 후, 전사지를 부착시키는 단계; b) 전사지의 박리형 코팅층을 제거하는 단계; c) 수용성 수지층을 물로 세척하는 단계; 및 d) 상기 세라믹 코팅층을 150 내지 400℃에서 소성하는 단계;를 포함하는 세라믹 코팅층이 형성된 조리용기의 제조방법을 제공한다.
Further, the present invention provides a method of manufacturing a transfer sheet, comprising the steps of: a) removing transfer paper, positioning the transfer paper on a ceramic coating layer, and attaching a transfer paper; b) removing the peelable coating layer of the transfer paper; c) washing the water-soluble resin layer with water; And d) firing the ceramic coating layer at 150 to 400 ° C.

또한, 본 발명은 상기 전사지가 인쇄된 후, 소성된 것을 특징으로 하는 조리용기를 제공한다.Further, the present invention provides a cooking container characterized in that the transfer sheet is printed and then baked.

본 발명의 세라믹 코팅용 전사지 에 따르면, According to the transfer sheet for ceramic coating of the present invention,

세라믹 코팅층에 잘 부착이 될 뿐만 아니라, 세라믹 코팅층에 손쉽게 전사 인쇄할 수 있고, 기존 인쇄잉크로 구현한 장식무늬보다 내오염성, 내열성, 내수성 및 내마모성이 우수하여 식기로 상용화해도 문제가 없다는 장점이 있다.It is not only adhered well to the ceramic coating layer but also can be easily transferred and printed on the ceramic coating layer and is excellent in resistance to staining, heat resistance, water resistance and abrasion resistance than that of the decorative pattern realized by conventional printing ink, .

도 1은 본 발명의 세라믹 코팅용 전사지의 모식도를 나타낸 그림이다.
도 2는 본 발명의 실시예 2에 따라 제조된 세라믹 코팅의 색상 손실 여부를 확인한 사진이다.
도 3은 본 발명의 비교예 2에 따라 제조된 세라믹 코팅의 색상 손실 여부를 확인한 사진이다.1 is a schematic view of a transfer sheet for ceramic coating according to the present invention.
FIG. 2 is a photograph showing the color loss of a ceramic coating prepared according to Example 2 of the present invention. FIG.
3 is a photograph showing the color loss of the ceramic coating prepared according to Comparative Example 2 of the present invention.

이하, 본 발명의 세라믹 코팅용 전사지, 이를 사용한 조리용기 및 조리용기의 제조방법에 대하여 상세하게 설명한다.
Hereinafter, a transfer sheet for ceramic coating of the present invention, a cooking vessel using the same, and a method of manufacturing a cooking vessel will be described in detail.

먼저, 본 발명의 세라믹 코팅용 전사지는, 도 1에 도시된 바와 같이, 전사대지(1); 상기 전사대지 상에 형성되고, 실리콘 수지 및 내열성 안료를 포함하는 무늬층(2); 상기 무늬층 또는 전사대지 상에 형성되는 수용성 수지층(3); 및 상기 수용성 수지층 상에 형성되는 박리형 코팅층(4)을 포함한다.
First, as shown in Fig. 1, the transfer sheet for ceramic coating of the present invention comprises a transfer paper 1; A pattern layer (2) formed on the transferring material and comprising a silicone resin and a heat resistant pigment; A water-soluble resin layer (3) formed on the pattern layer or transfer paper; And a peelable coating layer (4) formed on the water-soluble resin layer.

본 발명에 있어서, 세라믹 코팅이라 함은, 조리용기나 난방기구 등에 사용되는 금속의 표면에 알콕시 실란류와 내열성 안료의 혼합물이 코팅된 것을 말한다. 이러한 세라믹 코팅은 금속 표면에 유리질과 유사한 내화물의 피복을 하여 내식성, 내열성, 전기절연성 등을 갖게 하여, 금속의 내식성을 향상시키고, 표면의 질감을 향상시키기 위한 것으로서, 조리용기의 세라믹 코팅에는 특별한 제한은 없으나, 실리콘 오일 등을 혼용하여 비점착성(Non-Stick) 코팅으로 많이 이용되고 있다.
In the present invention, the term "ceramic coating" refers to a coating of a mixture of an alkoxysilane and a heat-resistant pigment on the surface of a metal used in a cooking vessel, a heating apparatus, or the like. Such a ceramic coating is intended to improve the corrosion resistance and the surface texture of the metal by coating the metal surface with a refractory similar to glass to have corrosion resistance, heat resistance, electrical insulation, and the like. But it is widely used as a non-stick coating by mixing silicone oil and the like.

본 발명의 세라믹 코팅용 전사지에 있어서, 상기 전사대지(1)은 본 발명의 전사지의 다른 구성요소를 지지해주는 것으로서, 대지 또는 시트지를 일정한 크기로 잘라서 사용할 수 있다. 상기 전사대지는 특별한 제한은 없으나, 예를 들어, 물 전사지용 대지를 사용할 수 있으며, 이러한 전사대지의 일면에는 수용성(水溶性) 분리면이 형성되어 있어, 후술하는 무늬층과 분리하는 것을 손쉽게 해 줄 수 있다. 이러한 수용성 분리면은, 특별한 제한은 없으나, 아라비안 검과 같은 고무, 전분, 알코올 및 물을 일정량 혼합하여 사용할 수 있으며, 이를 전사대지의 표면에 도포하여 막의 형태로 제공될 수 있다.
In the transfer sheet for ceramic coating according to the present invention, the transfer paper 1 supports other constituent elements of the transfer paper of the present invention, and the paper or paper sheet can be cut to a certain size. There is no particular limitation on the transfer site, but for example, a land for water transfer paper can be used. On one side of the transfer paper, a water-soluble separating surface is formed, which facilitates separation from the below- You can give. The water-soluble separating surface is not particularly limited, but may be a mixture of rubber, starch, alcohol and water, such as Arabian gum, and may be applied to the surface of the transfer paper to be provided in the form of a film.

본 발명의 세라믹 코팅용 전사지에 있어서, 상기 무늬층(2)은 상기 전사대지(1) 상에 형성되는 것이다. 상기 무늬층(2)은 본 발명의 전사지가 세라믹 상에 코팅될 때, 무늬를 형성할 수 있도록 하는 것으로서, 세라믹 코팅층 상에 대한 부착성이 좋아야 하며, 소성 및 사용시에 열에 의하여 훼손되지 않도록 내열성 역시 뛰어나야 한다. 이러한 무늬를 형성하기 위하여, 본 발명의 세라믹 코팅용 전사지의 무늬층(2)은 실리콘 수지 및 내열성 안료를 포함하여 사용자가 원하는 색상을 띄게 된다.
In the transfer sheet for ceramic coating of the present invention, the pattern layer (2) is formed on the transfer paper (1). The pattern layer 2 is a layer which can form a pattern when the transfer paper of the present invention is coated on a ceramic. The pattern layer 2 should have a good adhesion to the ceramic coating layer and have heat resistance so as not to be damaged by heat during firing and use. It should be excellent. In order to form such a pattern, the pattern layer 2 of the transfer sheet for ceramic coating of the present invention includes a silicone resin and a heat-resistant pigment, and has a color desired by a user.

본 발명에 있어서, 상기 무늬층(2)을 구성하는 상기 실리콘 수지는 순실리콘 수지, 실리콘폴리에스테르, 실리콘에폭시수지, 또는 메틸페닐폴리실록산 수지 등으로 이루어지는 군에서 선택되는 하나 이상인 것을 사용할 수 있으며, 바람직하게는 메틸페닐폴리실록산 수지를 사용할 수 있다. 또한, 상기 메틸페닐폴리실록산 수지를 사용하는 경우, 상기 실리콘 수지의 총중량 대비 80중량% 이상으로 메틸페닐폴리실록산 수지가 혼합된 것을 사용할 수 있다.
In the present invention, the silicone resin constituting the pattern layer (2) may be at least one selected from the group consisting of pure silicone resin, silicone polyester, silicone epoxy resin, methylphenyl polysiloxane resin and the like, A methylphenylpolysiloxane resin can be used. When the methylphenylpolysiloxane resin is used, a mixture of methylphenylpolysiloxane resin in an amount of 80% by weight or more based on the total weight of the silicone resin may be used.

또한, 상기 무늬층(2)을 구성하는 상기 내열성 안료는 착색 시에 색깔을 나타내는 역할을 하는 것으로서, 당업계에서 일반적으로 사용하는 내열성 안료라면 특별한 제한은 없으나, 바람직하게는 내열성이 300℃ 이상인 것을 사용할 수 있으며, 더 바람직하게는 인체에 유해한 중금속을 제외한 티탄 블랙, Cu, Fe, Mn, Cr, Co, Ni, V, Zn, Se, Mg, Ca, Sr, Ba, Ag, In, Sn, Sb, Bi, Ti, Si 및 Al로 이루어지는 군에서 선택되는 금속의 산화물, 상기 금속의 복합 산화물, 상기 금속의 황화물, 상기 금속의 황산염, 상기 금속의 탄산염, 또는 유기 내열성 안료를 사용할 수 있다.
The heat-resistant pigment constituting the pattern layer (2) has a role of exhibiting color upon coloring, and is not particularly limited as long as it is a heat-resistant pigment generally used in the art. Preferably, the heat- And more preferably titanium black, Cu, Fe, Mn, Cr, Co, Ni, V, Zn, Se, Mg, Ca, Sr, Ba, Ag, In, Sn, Sb except for heavy metals harmful to human body , An oxide of a metal selected from the group consisting of Bi, Ti, Si, and Al, a complex oxide of the metal, a sulfide of the metal, a sulfate of the metal, a carbonate of the metal, or an organic heat resistant pigment.

상기 실리콘 수지와 내열성 안료는 중량비 기준으로 색상의 구현도에 따라 임의의 혼합비율로 혼합될 수 있다.
The silicone resin and the heat-resistant pigment may be mixed at an arbitrary mixing ratio according to the degree of hue on the basis of the weight ratio.

상기 무늬층(2)은 상기 전사대지(1) 상에 형성할 수 있으며, 특별한 제한 없이 실크 스크린 인쇄를 하거나 직접 도포하여 다양한 색상 및 모양이 나타나도록 무늬층(2)을 형성할 수 있으며, 인쇄 또는 도포 후에 건조하여 경화시킬 수 있다.
The pattern layer 2 can be formed on the transfer paper 1 and can be formed by silk screen printing or directly applied without any particular limitation to form the pattern layer 2 in various colors and shapes, Or may be dried and cured after application.

본 발명의 세라믹 코팅용 전사지에 있어서, 도 1에서와 같이, 상기 수용성 수지층(3)은 무늬층(2) 상에 형성될 수 있으며, 무늬층(2) 형성되지 않은 전사대지 상에 형성될 수도 있다. 본 발명의 세라믹 코팅용 전사지는 상기 수용성 수지층(3)을 포함하기 때문에, 전사공정 시에 상기 무늬층(2)과 후술하는 박리형 코팅층(4)을 손쉽게 분리시킬 수 있을 뿐만 아니라, 물로 손쉽게 제거할 수 있게 된다. 이를 위하여, 상기 수용성 수지층은 PVA, 알긴산소다, CMC, Hydroxy, Ethyl Cellurose, 전분 등으로 이루어지는 군에서 선택되는 하나 이상을 포함할 수 있다.
1, the water-soluble resin layer 3 may be formed on the pattern layer 2, and may be formed on a transfer material that is not formed with the pattern layer 2 It is possible. Since the transfer sheet for ceramic coating of the present invention includes the water-soluble resin layer 3, not only can the pattern layer 2 and the peelable coating layer 4 described later be easily separated during the transfer process, Can be removed. For this, the water-soluble resin layer may include one or more selected from the group consisting of PVA, sodium alginate, CMC, Hydroxy, Ethyl Cellulose, starch, and the like.

본 발명의 세라믹 코팅용 전사지에 있어서, 상기 박리형 코팅층(4)은 상기 수용성 수지층(3) 상에 형성된다. 상기 박리형 코팅층(4)은 전사를 용이하게 하는 역할을 하는 층이며 상기 수용성 수지층 상에서, 이를 충격이나 마모와 같은 물리적인 훼손뿐만 아니라, 열에 의한 훼손 등을 보호하는 역할도 한다. 상기 박리형 코팅층(4)은 수용성 수지층(3)의 전체를 덮는 형태로 도포되어 형성할 수 있다. 상기 박리형 코팅층(4)의 재료로는 당업계에서 사용하는 통상의 아크릴수지 혹은 비닐수지를 사용할 수 있으나, 반드시 이에 한정되는 것은 아니며, 바람직하게는 특허공개 19921-0001484에 언급된 코팅층을 사용할 수 있다.
In the transfer sheet for ceramic coating of the present invention, the peelable coating layer (4) is formed on the water-soluble resin layer (3). The peelable coating layer 4 serves to facilitate the transfer, and protects the water-soluble resin layer from physical damage such as impact or abrasion, as well as thermal damage. The peelable coating layer 4 may be formed by coating the entire surface of the water-soluble resin layer 3. As the material of the peelable coating layer 4, an ordinary acrylic resin or a vinyl resin used in the related art can be used. However, the present invention is not limited thereto. Preferably, the coating layer described in Japanese Patent Application Laid-Open No. 19921-0001484 can be used have.

다음으로, 본 발명의 세라믹 코팅용 전사지를 사용하여, 세라믹 코팅층이 형성된 조리용기를 제조하는 방법은, Next, a method of manufacturing a cooking vessel in which a ceramic coating layer is formed using the transfer sheet for ceramic coating of the present invention,

a) 본 발명의 전사지의 전사대지를 제거한 후, 세라믹 코팅층 상에 위치시킨 후, 50 내지 100℃로 승온한 후, 30분 내지 4 시간 유지하여 전사지를 부착시키는 단계; b) 전사지의 박리형 코팅층을 제거하는 단계; c) 수용성 수지층을 물로 세척하는 단계; 및 d) 상기 세라믹 코팅층을 200 내지 400℃에서 소성하는 단계;를 포함한다.
a) removing the transfer paper of the transfer paper of the present invention, placing the paper on the ceramic coating layer, raising the temperature to 50 to 100 캜, holding the paper for 30 minutes to 4 hours, and attaching the transfer paper; b) removing the peelable coating layer of the transfer paper; c) washing the water-soluble resin layer with water; And d) firing the ceramic coating layer at 200 to 400 캜.

먼저, 본 발명의 세라믹 코팅층이 형성된 조리용기의 제조방법은 a) 단계에서, 앞서 살펴본 본 발명의 세라믹 코팅용 전사지의 전사대지를 제거한 후, 세라믹 코팅층 상에 위치시킨 후, 전사지를 부착시킨다.First, in the method of manufacturing a cooking vessel in which the ceramic coating layer of the present invention is formed, the transfer ground of the ceramic coating transfer sheet of the present invention is removed, and then the ceramic coating layer is placed on the ceramic coating layer.

상기 전사대지의 제거는 세라믹 코팅용 전사지 전체를 물에 일정시간 이상 담근 후, 전사대지 상에 형성된 수용성 분리면이 용해되면서, 전사대지가 분리가 된다. 이렇게 전사대지가 제거된 전사지를 무늬를 형성하려는 세라믹 코팅층 상에 위치시킨 후, 상온에서 2~4시간 자연건조시켜 전사지를 부착시키거나, 또는 50 내지 100℃로 승온한 후, 30분 내지 4 시간 유지하는 것이 바람직하다.
In the removal of the transfer paper, the entire transfer paper for ceramic coating is immersed in water for a certain period of time, and the water-soluble separating surface formed on the transfer paper is dissolved, and the transfer paper is separated. The transfer paper on which the transfer paper has been removed is placed on the ceramic coating layer to be patterned and then naturally dried at room temperature for 2 to 4 hours to adhere the transfer paper or heated to 50 to 100 ° C for 30 minutes to 4 hours .

또한, 상기 a) 단계에서, 세라믹 코팅층의 표면을 코로나 화염 처리 또는 플라즈마 방전 처리로 전처리 한 후, 전사지를 부착할 수 있다. 이러한 전처리를 하는 경우, 전사지의 무늬층과 세라믹 코팅층의 접착강도가 강해져서, 조리용기 제조시 또는 조리용기 사용시에 무늬층이 쉽게 벗겨지지 않게 되는 장점이 있다.
Also, in the step a), the surface of the ceramic coating layer may be pretreated with a corona flame treatment or a plasma discharge treatment, and then a transfer sheet may be attached. In such a pretreatment, the adhesive strength between the pattern layer of the transfer paper and the ceramic coating layer becomes strong, so that the pattern layer is not easily peeled off when the cooking container is used or when the cooking container is used.

이 후, 본 발명의 세라믹 코팅층이 형성된 조리용기의 제조방법은 b) 단계에서, 전사지의 박리형 코팅층을 제거한다. 상기 박리형 코팅층의 제거방법은, 당업계의 통상적인 방법으로 진행할 수 있으며, 구체적으로는 긁어서 벗겨내거나 접착테이프로 벗겨낼 수 있다.
Thereafter, in the method for producing a cooking container in which the ceramic coating layer of the present invention is formed, in step b), the peelable coating layer of the transfer paper is removed. The removal method of the peelable coating layer can be carried out by a conventional method in the art, and can be specifically scraped off or peeled off with an adhesive tape.

이 후, 본 발명의 세라믹 코팅층이 형성된 조리용기의 제조방법은 c) 단계에서, 수용성 수지층을 물로 세척한다. 상기 수용성 수지층은 앞서 살펴본 바와 같이 물에 잘 용해되는 것이기 때문에, 물수건으로 세척하거나, 물을 분사하는 방식으로 손쉽게 제거할 수 있다.
Thereafter, in the manufacturing method of the cooking vessel in which the ceramic coating layer of the present invention is formed, in the step c), the water-soluble resin layer is washed with water. Since the water-soluble resin layer is dissolved in water as described above, the water-soluble resin layer can be easily removed by washing with water or spraying water.

이 후, 본 발명의 세라믹 코팅층이 형성된 조리용기의 제조방법은 d) 단계에서, 상기 세라믹 코팅층을 150 내지 400℃에서 소성한다.Thereafter, in the method of manufacturing the cooking vessel in which the ceramic coating layer of the present invention is formed, the ceramic coating layer is baked at 150 to 400 캜 in step d).

상기 소성 온도가 150℃ 미만이면, 부착강도에 문제가 있으며, 400℃ 보다 높으면 피착물의 팽창계수 관계로 변형될 수 있다는 문제점이 있다.
If the firing temperature is less than 150 ° C, there is a problem in the adhesion strength. If the firing temperature is higher than 400 ° C, there is a problem that the firing temperature can be deformed in relation to the expansion coefficient of the adherend.

상기에서와 같이, 본 발명의 세라믹 코팅용 전사지를 전사한 후 이를 소성하여 제조된 조리용기는, 세라믹 코팅층 상에 무늬를 형성할 수 없었던 종래 기술과는 달리, 다양한 무늬층, 예를 들어 다색도 무늬가 인쇄된 것을 세라믹 코팅층 상에 형성할 수 있다. As described above, unlike the prior art in which a pattern can not be formed on the ceramic coating layer, the cooking container manufactured by transferring the transfer sheet for ceramic coating of the present invention and firing the transfer sheet has various pattern layers, A printed pattern can be formed on the ceramic coating layer.

이하 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변경 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope and spirit of the invention as disclosed in the accompanying claims. Changes and modifications may fall within the scope of the appended claims.

실시예Example

세라믹 코팅용 For ceramic coating 전사지의Transfer 제조  Produce

[실시예 1][Example 1]

전사지의 제조에 있어서, 본 출원인의 이전 발명인 특허공개 1992-0001484를 참조하였다. In the manufacture of transfer paper, reference has been made to the prior application of the present applicant, Patent Publication No. 1992-0001484.

먼저, 메틸페닐폴리실록산 수지(Dow Corning 社, 805 Resin) 10 중량부와 Ti02 5중량부를 혼합한 후, 트리플 롤러 밀(triple roller mill)로 혼합하여 백색 잉크를 제조하였다. 이 후, 상기 백색잉크 10중량부에 Co2O3 (cobalt oxide) 3중량부를 혼합하여 청색 잉크를 제조하였다.First, 10 parts by weight of methylphenylpolysiloxane resin (Dow Corning, 805 Resin) and 5 parts by weight of TiO 2 were mixed and mixed with a triple roller mill to prepare a white ink. Thereafter, 10 parts by weight of the white ink was mixed with 3 parts by weight of Co 2 O 3 (cobalt oxide) to prepare a blue ink.

이후, 툴리스러셀 전사대지(150g/m2) 상에, 상기 제조된 백색 잉크를 사용하여 300Mesh 실크 스크린으로 인쇄를 한 후 건조하였다. 그 위에 다시 상기 제조된 청색 잉크를 사용하여 350Mesh 실크 스크린으로 문양을 만들어 인쇄한 후 건조하였다. 이 후, 상기 인쇄층 상에 폴리비닐알콜(쿠라레사제)을 150Mesh로 도포한 후, 건조하였다. 이 후, 상기 폴리비닐알콜 층 상에 박리형 코팅층으로서 아크릴 수지(특허Thereafter, the resulting white ink was printed on a 300 mesh silk screen on a Toolless Russell transfer paper (150 g / m 2 ) and dried. The patterned blue ink was again printed on a 350Mesh silk screen to be printed and dried. Thereafter, polyvinyl alcohol (manufactured by Kuraray Co., Ltd.) was coated on the printing layer at 150 Mesh and dried. Thereafter, on the polyvinyl alcohol layer, an acrylic resin as a peelable coating layer

공개 1992-10001484에서 사용한 수지와 동일)를 60Mesh로 도포한 후, 건조하여 전사지를 제조하였다. Open No. 1992-10001484) was applied at 60 Mesh, and then dried to prepare a transfer paper.

[비교예 1] [Comparative Example 1]

실리콘 폴리에스테르수지 10중량부와 Ti02 5중량부를 혼합한 백색 잉크를 제조하였따. 이 후 상기 백색잉크 10 중량부에 Co2O3 (cobalt oxide) 3중량부를 혼합하여 청색 잉크를 제조하였다. 이 후, 상기 제조된 백색 잉크를 사용하여 300Mesh 실크 스크린으로 인쇄를 한 후 건조하였다. 그 위에 다시 상기 제조된 청색 잉크를 사용하여 350Mesh 실크 스크린으로 문양을 만들어 인쇄한 후 건조하여 전사지를 제조하였다.
A white ink was prepared by mixing 10 parts by weight of silicone polyester resin and 5 parts by weight of TiO 2 . Thereafter, 10 parts by weight of the white ink was mixed with 3 parts by weight of Co 2 O 3 (cobalt oxide) to prepare a blue ink. Thereafter, the white ink prepared above was printed on a 300 Mesh silkscreen and dried. A pattern was formed on a 350Mesh silk screen using the above-prepared blue ink, followed by printing and drying to prepare a transfer paper.

세라믹 코팅 조리용기의 제조 Manufacture of Ceramic Coated Cooking Container

[실시예 2][Example 2]

상기 실시예 1에서 제조한 전사지를 상온의 물에 담근 후, 전사대지를 제거하였다. 이 후, 시중에 판매되는 세라믹층이 형성된 알루미늄 용기를 준비한 후, 전사지의 무늬층과 세라믹층이 마주치도록 위치시킨 후, 60℃로 승온한 후, 1시간 동안 유지한 후 박리형 코팅을 벗겨내었다. 이 후, 상온의 물에 침지시켜 수용성 수지를 제거하였다. 이 후, 다시 250℃로 10분간 소성하여 세라믹층 상에 무늬층이 형성된 알루미늄 금속을 제조하였다.The transfer paper prepared in Example 1 was immersed in water at room temperature, and the transfer paper was removed. Thereafter, an aluminum container on which a commercially available ceramic layer was formed was prepared. After positioning the patterned layer of the transfer paper and the ceramic layer so as to face each other, the temperature was raised to 60 캜 and maintained for 1 hour. I got it. Thereafter, it was immersed in water at room temperature to remove the water-soluble resin. Thereafter, the resultant was further baked at 250 DEG C for 10 minutes to produce an aluminum metal having a patterned layer formed on the ceramic layer.

[비교예 2][Comparative Example 2]

상기 비교예 1의 전사지를 사용하는 것을 제외하고는 실시예 2와 동일한 방법으로 무늬층을 형성하였다.
A pattern layer was formed in the same manner as in Example 2, except that the transfer paper of Comparative Example 1 was used.

실험예Experimental Example 1: 세라믹 코팅된 알루미늄 상의 착색 실험  1: Color experiment on ceramic coated aluminum

상기 실시예 2 및 비교예 2에서 제조한 금속에 대하여, 알루미늄의 세라믹층 상의 착색 부분의 외관, 연필경도 및 내열성을 각각 비교하여 하기 표 1에 나타내었다.
The appearance, pencil hardness and heat resistance of the colored portion on the aluminum ceramic layer were compared with the metals prepared in Example 2 and Comparative Example 2, and the results are shown in Table 1 below.

[연필 경도 평가][Pencil hardness evaluation]

ASTM D 3363 에 따라 세라믹 코팅 표면에 부착된 전사 필름의 표면 경도를 측정하여 평가하였다. The surface hardness of the transferred film adhering to the ceramic coating surface in accordance with ASTM D 3363 was measured and evaluated.

[Cross-cut Adhesion Test][Cross-cut Adhesion Test]

ASTM D 3359에 따라 테스트 하였다Tested according to ASTM D 3359

[내열성 평가][Heat resistance evaluation]

세라믹층의 착색 부분을 촬영하여, 착색된 부분의 색상이 손실(변화)되었는지를 확인하여 하기 표 1 및 도 2 내지 도 3에 나타내었다.The colored portion of the ceramic layer was photographed to confirm whether the color of the colored portion was lost (changed). The results are shown in Table 1 and Figs. 2 to 3.

[외관][Exterior]

250℃로 가열 후, 육안으로 관찰하여, 착색된 부분이 전체적으로 이상이 없는지를 확인하여 하기 표 1에 나타내었다.After heating to 250 ° C, the sample was observed with naked eyes to confirm whether or not the colored part was totally abnormal. The results are shown in Table 1 below.

실시예 2Example 2 비교예 2Comparative Example 2 표면경도
(연필경도)Surface hardness
(Pencil hardness) 5H5H HH Cross-cut Adhesion TestCross-cut Adhesion Test 100/100100/100 5/100이하5/100 or less 내열성Heat resistance 250℃ PassPass 250 ° C 250℃에서 변질됨Deteriorated at 250 ° C 외관Exterior 이상 없음clear 황변Yellow

상기 표 1에서와 같이, 본 발명의 세라믹 코팅용 전사지를 이용한 경우, 종래 기술에 의하여 제조된 제품에서는 구현할 수 없었던 세라믹 코팅층 상에 대한 부착성 및 내열성이 확보되는 것을 알 수 있었다. As shown in Table 1, when the transfer sheet for ceramic coating of the present invention was used, adhesion and heat resistance to the ceramic coating layer, which could not be realized by the conventional products, were secured.

1: 전사대지
2: 무늬층
3: 수용성 수지층
4: 박리형 코팅층1: Warrior Earth
2: pattern layer
3: Water-soluble resin layer
4: Peelable coating layer

Claims (10)

전사대지;
상기 전사대지 상에 형성되고, 실리콘 수지 및 내열성 안료를 포함하는 무늬층;
상기 무늬층 또는 전사대지 상에 형성되는 수용성 수지층; 및
상기 수용성 수지층 상에 형성되는 박리형 코팅층;
을 포함하는 세라믹 코팅용 전사지.Warrior land;
A pattern layer formed on the transferring material and including a silicone resin and a heat resistant pigment;
A water-soluble resin layer formed on the pattern layer or transfer paper; And
A peelable coating layer formed on the water-soluble resin layer;
≪ / RTI > 청구항 1에 있어서,
상기 실리콘 수지는 순실리콘 수지, 실리콘폴리에스테르, 실리콘에폭시수지 및 메틸페닐폴리실록산 수지로 이루어지는 군에서 선택되는 하나 이상인 것을 특징으로 하는 세라믹 코팅용 전사지.The method according to claim 1,
Wherein the silicone resin is at least one selected from the group consisting of pure silicone resin, silicone polyester, silicone epoxy resin and methylphenyl polysiloxane resin. 청구항 2에 있어서,
상기 실리콘 수지는 실리콘 수지의 총중량 대비 80중량% 이상으로 메틸페닐폴리실록산 수지가 혼합된 것을 특징으로 하는 세라믹 코팅용 전사지.The method of claim 2,
Wherein the silicone resin is mixed with methylphenyl polysiloxane resin in an amount of 80% by weight or more based on the total weight of the silicone resin. 청구항 1에 있어서,
상기 내열성 안료는 티탄 블랙; Cu, Fe, Mn, Cr, Co, Ni, V, Zn, Se, Mg, Ca, Sr, Ba, Ag, In, Sn, Sb, Bi, Ti, Si 및 Al로 이루어지는 군에서 선택되는 금속의 산화물; 상기 금속의 복합 산화물; 상기 금속의 황화물; 상기 금속의 황산염; 상기 금속의 탄산염; 및 유기 내열성 안료로 이루어지는 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는 세라믹 코팅용 전사지.The method according to claim 1,
The heat resistant pigment is titanium black; An oxide of a metal selected from the group consisting of Cu, Fe, Mn, Cr, Co, Ni, V, Zn, Se, Mg, Ca, Sr, Ba, Ag, In, Sn, Sb, Bi, ; A composite oxide of the metal; A sulfide of the metal; A sulfate of the metal; A carbonate of the metal; And an organic heat-resistant pigment. The transfer sheet for a ceramic coating according to claim 1, 청구항 1에 있어서,
상기 수용성 수지층은 PVA, 알긴산소다, CMC(carboxymethyl cellulose), Hydroxy, Ethyl Cellurose 및 전분으로 이루어지는 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는 세라믹 코팅용 전사지.The method according to claim 1,
Wherein the water-soluble resin layer comprises at least one selected from the group consisting of PVA, sodium alginate, carboxymethyl cellulose (CMC), hydroxy, ethylcellulose and starch. 청구항 1에 있어서,
상기 박리형 코팅층은 아크릴 수지 및 비닐수지 중 어느 하나 이상을 포함하는 것을 특징으로 하는 세라믹 코팅용 전사지.The method according to claim 1,
Wherein the peelable coating layer comprises at least one of an acrylic resin and a vinyl resin. a) 청구항 1의 전사지의 전사대지를 제거한 후, 세라믹 코팅층 상에 위치시킨 후, 전사지를 부착시키는 단계;
b) 전사지의 박리형 코팅층을 제거하는 단계;
c) 수용성 수지층을 물로 세척하는 단계; 및
d) 상기 세라믹 코팅층을 150 내지 400℃에서 소성하는 단계;
를 포함하는 세라믹 코팅층이 형성된 조리용기의 제조방법.a) removing the transfer paper of the transfer paper of claim 1, placing the transfer paper on the ceramic coating layer, and attaching the transfer paper;
b) removing the peelable coating layer of the transfer paper;
c) washing the water-soluble resin layer with water; And
d) firing the ceramic coating layer at 150-400 占 폚;
And a ceramic coating layer formed on the ceramic coating layer. 청구항 1에 있어서,
상기 a) 단계에서, 세라믹 코팅층의 표면을 코로나 화염 처리 또는 플라즈마 방전 처리로 전처리 한 후, 전사지를 부착시키는 것을 특징으로 하는 세라믹 코팅층이 형성된 조리용기의 제조방법.The method according to claim 1,
Wherein a surface of the ceramic coating layer is pretreated with a corona flame treatment or a plasma discharge treatment in the step a), and then a transfer paper is adhered to the surface of the ceramic coating layer. 청구항 1의 전사지가 인쇄된 후, 이를 이용하여 다색도 무늬가 인쇄된 것을 특징으로 하는 세라믹 코팅층이 형성된 조리용기.The method of claim 1, wherein the ceramic coating layer is formed by printing a transfer paper of claim 1 and printing a polychromatic pattern thereon. 청구항 11에 있어서, 상기 조리용기의 세라믹 코팅 상에 상기 전사지가 전사된 후, 소성된 것을 특징으로 하는 조리용기.

12. The cooking vessel according to claim 11, wherein the transfer paper is transferred onto the ceramic coating of the cooking vessel and then fired.

KR1020160114967A 2015-10-14 2016-09-07 A transfer paper for ceramic coated metal, the cooking container using the same and the manufacturing thereof KR101941747B1 (en)