KR20160121831A - Egg packing container with Eco-friendly biodegradable materials - Google Patents

Egg packing container with Eco-friendly biodegradable materials Download PDF

Info

Publication number
KR20160121831A
KR20160121831A KR1020150051531A KR20150051531A KR20160121831A KR 20160121831 A KR20160121831 A KR 20160121831A KR 1020150051531 A KR1020150051531 A KR 1020150051531A KR 20150051531 A KR20150051531 A KR 20150051531A KR 20160121831 A KR20160121831 A KR 20160121831A
Authority
KR
South Korea
Prior art keywords
egg
packing container
resin
present
weight
Prior art date
Application number
KR1020150051531A
Other languages
Korean (ko)
Inventor
김성현
Original Assignee
김성현
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김성현 filed Critical 김성현
Priority to KR1020150051531A priority Critical patent/KR20160121831A/en
Publication of KR20160121831A publication Critical patent/KR20160121831A/en

Abstract

The present invention relates to an environmentally friendly packing container for packing eggs. The environmentally friendly egg packing container is composed of a composite containing a biodegradable resin or a biomass resin. According to an embodiment of the present invention, the composite contains: a mixture containing 50-80 wt% of PP, PS, or PE synthetic resin, 10-20 wt% of the biomass resin, and 1-10 wt% of a surfactant; 50-80 wt% of the biodegradable resin; and 3-15 wt% of PBAT. The composite is manufactured by injection molding. Also, the egg packing container has a structure in which an egg accommodating unit is continuously formed on the left and right sides, and an elevated unit is formed on the bottom of the egg accommodating unit. The elevated unit enables the eggs to be easily mounted thereon.

Description

친환경 식물성 수지 조성물을 이용한 달걀 포장용기 {Egg packing container with Eco-friendly biodegradable materials} [0001] The present invention relates to an egg-packing container with an eco-friendly biodegradable material,

본 발명은 친환경 수지 조성물을 이용한 달걀 포장용기에 관한 것으로서, 보다 구체적으로는 식물성 옥수수 전분을 이용한 PLA(Polylatic Acid) 수지를 이용하여 시트를 금형으로 달걀용기를 제조한다. 오목 및 볼록 형태로 달걀을 사방에서 견고하게 잡아주어 외부 충격으로부터 달걀을 안전하게 보호함을 목적으로 하는 친환경 달걀 포장용기를 제공코자 하는 것이다.   The present invention relates to an egg packing container using an eco-friendly resin composition, and more specifically, an egg container is manufactured from a PLA (Polylatic Acid) resin using vegetable corn starch as a sheet. The present invention provides an eco-friendly egg packing container for holding eggs securely in a concave and convex form in all directions to safely protect eggs from external impacts.

본 발명은 친환경 생분해성 수지 조성물을 이용한 달걀 포장용기에 관한 것이다. 더 상세하게는, 생분해성 수지 조성물을 이용하여 포장재를 성형함으로써, 폐기에 따른 환경 부담을 줄이고, 인체에 유해한 환경 호르몬이 발생하지 않도록 하며 또한 제작이 편리하고, 외부 충격으로부터 제품을 보호할 수 있는 달걀 포장용기에 관한 것이다.The present invention relates to an egg packing container using an environmentally friendly biodegradable resin composition. More particularly, the present invention relates to a biodegradable resin composition for molding a packaging material using a biodegradable resin composition, which can reduce environmental burden due to disposal, prevent the generation of harmful environmental hormones, Egg packing containers.

본 발명은 이와 같은 종래의 문제점을 감안하여 이루어진 것으로, 그 목적은 분해 속도가 빠른 생분해성 수지조성물을 이용하고, 프레스 금형을 통한 대량 생산이 가능하도록 하며, 폐기에 따른 환경 오염에 대한 부담을 크게 줄일 수 있는 생분해성 조성물을 이용한 달걀 포장용기를 제공하는 데 있다. 본 발명의 다른 목적은, 달걀의 상부를 감싸는 보호대를 구비하여 제품 상부에 별도의 포장이 불필요하도록 한 달걀 포장용기를 제공하는 데 있다. 본 발명의 또 다른 목적은, 베이스 부재의 하부 또는 상부에 설치되는 완충부를 구비하여 달걀의 운반 및 보관 시 외부 충격으로 달걀을 보호할 수 있는 포장재를 제공하는 데 있다.DISCLOSURE OF THE INVENTION The present invention has been made in view of such conventional problems, and it is an object of the present invention to provide a biodegradable resin composition having a high decomposition speed, capable of mass production through a press die, And an egg packing container using the biodegradable composition. Another object of the present invention is to provide an egg packing container having a protector for covering an upper portion of an egg so that no separate packaging is required in the upper portion of the product. It is a further object of the present invention to provide a packaging material which is provided at a lower portion or an upper portion of a base member to protect eggs from external shocks when the eggs are transported and stored.

상기 목적을 달성하기 위하여, 달걀 포장용기는 달걀 수납부가 좌우로 연속된 구성으로, 이 수납부의 저면에 융기부가 마련된다. In order to attain the above object, the egg packing container has a structure in which the egg storage portion is continuous from side to side, and a ridge is provided on the bottom surface of the storage portion.

본 발명의 특징이라 할 수 있는 이 융기부는 달걀이 잘 안착되도록 하는 구성이다.The protuberance, which is a characteristic feature of the present invention, is a constitution in which the egg is seated well.

본 발명은 달걀 포장용 친환경 포장 용기 및 이 포장 용기의 제조 방법에 관한 것이다. 일반적으로 달걀은 PP, PE 또는 종이재를 압축 성형하여 마련된 반원형의 수납부에 달걀을 끼워 포장 판매하고 있다. 그런데, 종이재는 자원 낭비기 심하고, 합성수지 플라스틱은 소각 처리는 물론 매립이 불가능하고, 따라서 환경오염의 원인이 되는 문제가 있다. 또한, 폐기물 처리 시에도 막대한 비용이 소요되어 기업은 물론 사회적으로도 크나큰 문제가 아닐 수 없다.The present invention relates to an eco-friendly packaging container for egg packing and a method of manufacturing the packaging container. Generally, eggs are packed in eggs in a semicircular compartment formed by compression molding of PP, PE or paper. However, paper materials are wasted resources, and synthetic plastic plastics are incapable of incineration as well as incapable of being buried, thus causing environmental pollution. In addition, waste disposal costs are very high, which can be a big problem for both companies and society.

본 발명은 달걀 포장용 친환경 포장 용기에 관한 것으로, 생분해성 수지 또는 바이오매스 수지를 포함하는 조성물로 이루어진다. 하나의 실 시예로, 상기 조성물은 PP, PS 또는 PE 합성수지 50-80중량%, 바이오매스수지 10-20 중량%, 계면활성제 1-10중량%를 포함하는 혼합물과, 이 혼합물 100중량%를 기준으로 생분해성수지 PLA 50-80% 중량%, PBAT 3-15 중량%가 포함되며, 이 조성물은 사출 성형을 통해 제작된다. 또한 본 발명의 포장 용기는 달걀 수납부가 좌우로 연속된 구성으로, 이 수납부의 저면에 융기부가 마련된 구성으로, 이 융기부는 달걀이 잘 안착되도록 하는 구성이다.The present invention relates to an eco-friendly packaging container for egg packing comprising a biodegradable resin or a composition comprising a biomass resin. In one embodiment, the composition comprises a mixture comprising 50-80 wt.% PP, PS or PE synthetic resin, 10-20 wt.% Biomass resin, 1-10 wt.% Surfactant, 50 to 80% by weight of a biodegradable resin PLA, and 3 to 15% by weight of PBAT, and the composition is prepared by injection molding. In addition, the packaging container of the present invention is constituted such that the egg storage portion is continuous to the left and right, and the ridge portion is provided on the bottom surface of the storage portion.

상기 베이스 부재는, 생분해성 수지 조성물을 기본으로 하되, 바이오매스 수지가 이용될 수도 있으며, 본 발명에서는 상기 생분해성 수지 조성물 또는 바이오매스 수지가 폐기되었을 때 소각처리되지 않고 단순히 매립처리하도록 함으로써, 이들이 생분해성, 광분해성 중 1가지 이상의 분해 기능에 의해서 수개월 내지 수년 이내에 물, 이산화탄소, 메탄가스, 바이오매스 등으로 분해되어 1차 및 2차 환경 오염을 줄일 수 있도록 한 것이다.In the present invention, when the biodegradable resin composition or biomass resin is discarded, the base member is merely buried without being incinerated, so that the biodegradable resin composition or biomass resin Carbon dioxide, methane gas and biomass within a period of several months to several years by one or more decomposing functions among the biodegradable and photodegradable materials, thereby reducing primary and secondary environmental pollution.

한편, 본 발명에 따른 생분해성 수지는 지방족 폴리에스테르계 고분자 80-94중량%, 물성 계량제 5-10중량% 및 윤활제 1-10중량%로 이루어지거나, 또는 지방족 폴리에스테르계 고분자 75-93중량%, 물성 계량제 5-10중량%, 윤활제 15중량% 및 무기 연마제 1-10중량%를 포함한다. 상기 지방족 폴리에스테르계 고분자로는 폴리유산 혹은 폴리락타이드가 적합하다. On the other hand, the biodegradable resin according to the present invention comprises 80-94% by weight of an aliphatic polyester polymer, 5-10% by weight of a physical property measuring agent and 1-10% by weight of a lubricant, or 75-93% by weight of an aliphatic polyester polymer %, A physical property measuring agent 5-10% by weight, a lubricant 15% by weight and an inorganic abrasive agent 1-10% by weight. The aliphatic polyester-based polymer is preferably polylactic acid or polylactide.

물성 계량제는 지방족 폴리에스테르계 고분자로 사용되는 폴리유산 혹은 폴리락타이드의 문제점인 낮은 인성 즉, 강도는 높지만 신장률이 부족해 쉽게 파단되는 특성을 보완하기 위해 사용된 것으로서, 디에틸렌 글리콜로 얻어지는 2가 알콜 혹은 글리세롤, 트리메틸올 프로판으로부터 얻어지는 3가 알콜과 숙신산, 아디핀산으로부터 얻어지는 2가 산 혹은 2가 산의 무수물 형태로부터 축중합에 의해 제조되는 것을 사용함이 바람직하고, 중량 평균 분자량이 50,000150,000이며, 용융지수 2030g/10min인 것이 적합하다.The physical property metering agent is used to compensate for the properties of polylactide or polylactide used as an aliphatic polyester-based polymer, that is, low toughness, that is, high fracture toughness due to insufficient elongation. It is preferable to use a product obtained by polycondensation from a trihydric alcohol obtained from alcohol, glycerol or trimethylolpropane and a divalent acid obtained from succinic acid or adipic acid or an anhydride form of divalent acid, and preferably has a weight average molecular weight of 50,000, 000, and a melt index of 2030 g / 10 min.

또한, 폴리카프로락톤을 사용할 수 있는데, 이는 분자량이 30,00060,000 정도이며, 용융지수 2030g/10min, 융점 5860인 것을 사용함이 바람직하다.In addition, polycaprolactone can be used, and it is preferable to use a polymer having a molecular weight of about 30,000 to 60,000, a melt index of 2030 g / 10 min, and a melting point of 5860.

윤활제는 장시간 방사시 친유성 성분이 증가하기 때문에 분자내 친수성 성분과 친유성 성분의 비율을 나타내는 HLB값이 7.016.0의 범위인 지방산 에스테르를 선택하여 사용함이 바람직하다.It is preferable to use a fatty acid ester having an HLB value in the range of 7.016.0, which indicates the ratio of the hydrophilic component to the lipophilic component in the molecule, since the lipophilic component increases during prolonged spinning of the lubricant.

무기 연마제는 강성도와 굴곡복원률 특성을 개선함과 동시에 세정력을 향상시킨다. 이로는 치약 구성 성분으로 통상 사용하는 이산화규산(실리카), 인산칼슘, 탄산칼슘, 무수규산, 수산화알루미늄 등이 있으며, 일반적으로 입자크기 10-1,000의 나노 입자 혹은 1-100의 마이크로 입자가 모두 사용 가능하다.The inorganic abrasive improves the stiffness and flexural restoration characteristics and improves the cleaning power. These include silica dioxide (silica), calcium phosphate, calcium carbonate, silicic acid anhydride, and aluminum hydroxide, which are commonly used as toothpaste components. In general, nanoparticles having a particle size of 10-1,000 or 1-100 microparticles are used It is possible.

상기 PBAT는 제품의 유연성 즉 신율을 향상시킴과 아울러 강도를 증가시키는 것으로, 계면활성제가 추가적으로 포함된다.The PBAT improves the flexibility, i.e., elongation, and increases the strength of the product, and further includes a surfactant.

상기 계면 활성제는 양이온성, 음이온성, 비이온성을 포함한다.The surfactant includes cationic, anionic, and nonionic.

양이온성 계면활성제로는, 긴 알킬 사슬 (예를 들어, 4 가 암모니아, 포스포늄 또는 솔포늄 염), 또는 고리 (즉, 이미다졸린) 의 일부일 수 있는 4가 기를 함유하는 벌키한 양이온으로 이루어질 수 있다.Cationic surfactants include bulky cations containing quadrivalent groups that can be part of long alkyl chains (e.g., tetravalent ammonia, phosphonium or sulfonium salts) or rings (i.e., imidazolines) .

음이온성 계면활성제는 알킬 술포네이트, 술페이트, 포스페이트, 포스포네이트, 디티오카르바메이트가 포함될 수 있으며, 일반적으로는 알칼리 금속 또는 알칼리 토류로 중성화된 카르복실라제가 사용된다.Anionic surfactants may include alkyl sulfonates, sulfates, phosphates, phosphonates, dithiocarbamates, and in general, carboxylates which are neutralized with an alkali metal or alkaline earth are used.

비이온성 대전방지제는, 폴리에톡실레이트 에스테르 및 에테르, 지방산의 에스테르 또는 아미드, 지방 아민의 모노 및 디글리세리드를 포함하는 중성 계면활성제가 사용될 수 있다.Nonionic antistatic agents may be neutral surfactants including polyethoxylate esters and ethers, esters or amides of fatty acids, mono- and diglycerides of fatty amines.

또한 본 발명은 경우에 따라서, 티타늄 이산화물, 점토, 구리 프탈로시아닌, 칼슘 카르보네이트, 탈크, 운모, 실리카, 실리케이트, 철 산화물 및 수산화물, 카본 블랙 및 마그네슘 산화물과 같은 안료 및 염료 또는 색 안정제가 포함될 수 있으며, 이들은 상기 생분해성 수지 조성물 100중량%에 대하여 0.13중량%가 혼합됨이 바람직하다.The present invention may also optionally include pigments and dyes or color stabilizers such as titanium dioxide, clay, copper phthalocyanine, calcium carbonate, talc, mica, silica, silicates, iron oxides and hydroxides, carbon black and magnesium oxide And they are preferably mixed with 0.13% by weight based on 100% by weight of the biodegradable resin composition.

또 본 발명은 상용화제가 포함될 수 있다. 이 상용화제는 에폭시기(에폭시 그룹; epoxy group)을 포함한 물질로서, 그 예로는 styrene-acrylic multi-functional oligomeric chain extenders이 있다.The present invention can also include a compatibilizer. This compatibilizer is a material containing an epoxy group, for example, styrene-acrylic multi-functional oligomeric chain extenders.

본 발명은 상기 상용화제와 함께, 또는 상용화제를 제외하고 가소제가 사용될 수도 있다.The present invention may employ a plasticizer with or without the compatibilizing agent.

즉 가소제(plasticizer)를 이용하여 가소화시킨 것을 사용할 수 있으며, 가소제로 트리아세틴(TA), 트리에틸 시트레이트(TEC), 또는 글리세린 등을 단독 또는 2종 이상 사용할 수 있다. 바람직한 가소제는 트리아세틴이다.(TA), triethyl citrate (TEC), glycerin or the like may be used alone or in combination of two or more thereof as a plasticizer. A preferred plasticizer is triacetin.

본 발명에서 상기 상용화제는 상기 생분해성 수지 조성물 100중량%에 대하여 15 중량%가 첨가될 수 있으며, 가소제는 0.11중량%가 첨가될 수 있다.In the present invention, the compatibilizer may be added in an amount of 15% by weight based on 100% by weight of the biodegradable resin composition, and 0.11% by weight of a plasticizer may be added.

한편, 본 발명은 생분해성 수지 조성물 이외에 바이오매스 수지가 이용될 수 있다.On the other hand, in the present invention, a biomass resin may be used in addition to the biodegradable resin composition.

상기 바이오매스 수지는 곡물 또는 식물에서 추출된 바이오매스 수지 원료 80중량%와, PE, PP 등에서 선택된 일반 플라스틱 20중량%가 혼합된 바이오매스 플라스틱을 사용하거나, 상기 바이오매스 수지 원료 25중량%와 PLA, PCL 등에서 선택된 생분해성 플라스틱이 75중량%가 혼합된 바이오매스 플라스틱이 사용될 수 있다.The biomass resin may be prepared by using biomass plastic in which 80% by weight of raw material of biomass resin extracted from grains or plants and 20% by weight of general plastic selected from PE, PP or the like is mixed or 25% by weight of the biomass resin raw material and PLA , PCL, etc., may be used as the biomass plastic.

상기 바이오매스 수지 원료는 25중량% 이상 포함되는 것이 바람직하다.It is preferable that the biomass resin material is contained in an amount of 25 wt% or more.

본 발명에 적용되는 바이오매스 수지의 일 예로는 자연 원료인 옥수수, 코코넛을 활용하는 PTT(폴리트리메틸렌, 테레프탈산) 재질이 사용될 수 있다.As an example of the biomass resin to be applied to the present invention, PTT (polytrimethylene, terephthalic acid) materials using corn and coconut which are natural raw materials can be used.

이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the spirit and scope of the present invention as defined by the appended claims and their equivalents.

Claims (3)

달걀 포장용기 몸체와
상기 몸체에 설치되어 복수개의 달걀을 수용하는 수용부와
상기 수용부를 구분하여 달걀의 측면부를 지지하는 측면 지지부와
상기 수용부에 수용되는 복수개의 달걀의 저면을 지지하는 저면부와
상기 저면부에 설치되고 상기 수용부에 수용되는 달걀의 하단부를 상향 지지하는록 일정높이로 돌출된 돌출부와
상기 저면부 돌출부 사이 소정의 공간이 설치되는 공기통로를 포함하는 것을 특징으로 하는 친환경 수지 조성물을 이용한 달걀 포장용기.
Egg packing container body
A receiving portion provided on the body for receiving a plurality of eggs;
A side support portion for supporting the side portion of the egg by dividing the accommodating portion;
A bottom portion for supporting a bottom surface of a plurality of eggs housed in the accommodating portion;
A protruding portion provided at the bottom portion and protruding at a predetermined height to support a lower end portion of the egg accommodated in the accommodating portion upward;
And an air passage in which a predetermined space is provided between the bottom surface protrusions.
제1항에 있어서,
상기 달걀 포장용기 몸체의 재질은 식물성 생분해성 수지 또는 바이오매스 수지로 제조하는 것을 특징으로 하는 친환경 수지 조성물을 이용한 달걀 포장용기.
The method according to claim 1,
Wherein the egg packing container body is made of vegetable biodegradable resin or biomass resin.
제1항에 있어서,
상기 달걀 포장용기 몸체의 조성물은 PP, PS 또는 PE 합성수지 50-80중량%, 바이오매스수지 10-20 중량%, 계면활성제 1-10중량%를 포함하는 혼합물과 이 혼합물 100중량%를 기준으로 식물성 생분해성수지 PLA 50-80% 중량%, PBAT 3-15 중량%가 포함되며, 이 조성물은 사출 성형을 통해 제조하는 하는 것을 특징으로 하는 친환경 수지 조성물을 이용한 달걀 포장용기.
The method according to claim 1,
Wherein the composition of the egg packing container body comprises a mixture comprising 50-80 wt.% Of PP, PS or PE synthetic resin, 10-20 wt.% Of biomass resin, 1-10 wt.% Of a surfactant and 100 wt. Wherein the composition comprises 50-80% by weight of biodegradable resin PLA and 3-15% by weight of PBAT, and the composition is prepared by injection molding.
KR1020150051531A 2015-04-13 2015-04-13 Egg packing container with Eco-friendly biodegradable materials KR20160121831A (en)