KR20160070614A - Cable type secondary battery using Vanadium redox couple and method for charging and discharging the same - Google Patents

Cable type secondary battery using Vanadium redox couple and method for charging and discharging the same Download PDF

Info

Publication number
KR20160070614A
KR20160070614A KR1020140177799A KR20140177799A KR20160070614A KR 20160070614 A KR20160070614 A KR 20160070614A KR 1020140177799 A KR1020140177799 A KR 1020140177799A KR 20140177799 A KR20140177799 A KR 20140177799A KR 20160070614 A KR20160070614 A KR 20160070614A
Authority
KR
South Korea
Prior art keywords
secondary battery
type secondary
redox couple
charging
cable type
Prior art date
Application number
KR1020140177799A
Other languages
Korean (ko)
Other versions
KR101802569B1 (en
Inventor
정봉현
변수진
노태근
민근기
문식원
이정배
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020140177799A priority Critical patent/KR101802569B1/en
Publication of KR20160070614A publication Critical patent/KR20160070614A/en
Application granted granted Critical
Publication of KR101802569B1 publication Critical patent/KR101802569B1/en

Abstract

The present invention relates to a cable-type secondary battery using vanadium redox couple and a method for charging and discharging the same. According to the present invention, first and second cathode terminals are provided on one and the other sides of a cathode current collector configured to pass through a cathode battery of a cable-type secondary battery using vanadium redox couple, first and second anode terminals are provided on one and the other sides of an anode current collector configured to pass through an anode battery surrounding the cathode battery, and charging and discharging are performed by the use of the first anode terminal and the second cathode terminal or the second anode terminal and the first cathode terminal.

Description

바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법{Cable type secondary battery using Vanadium redox couple and method for charging and discharging the same}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cable type secondary battery using a vanadium redox couple, and a charging /

본 발명은 바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법에 관한 것으로서, 보다 상세하게는, 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 음극 전극 내부를 관통하도록 구성되는 음극 집전체에 제1 및 제2 음극 단자를 각각 일측과 타측에 구비하고, 음극 전지의 외측을 감싸는 양극 전극의 내부를 관통하도록 구성되는 양극 집전체에 제1 및 제2 양극 단자를 각각 일측과 타측에 구비하며, 제1 양극 단자와 제2 음극 단자 또는 제2 양극 단자와 제1 음극 단자를 이용하여 충방전을 수행하는 바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법에 관한 것이다.
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cable type secondary battery using a vanadium redox couple and a charging / discharging method thereof, and more particularly, to a cable type secondary battery using a vanadium redox couple, A first positive electrode terminal and a second positive electrode terminal are provided on one side and the other side, respectively, of the positive electrode current collector provided on one side and the other side of the positive and negative electrode terminals, respectively, The present invention relates to a cable type secondary battery using a vanadium redox couple which performs charge and discharge by using a first positive electrode terminal and a second negative electrode terminal, or a second positive electrode terminal and a first negative electrode terminal, and a charging and discharging method thereof.

비디오 카메라, 휴대용 전화, 휴대용 PC 등의 휴대용 전기 제품 사용이 활성화됨에 따라 그 구동 전원으로서 주로 사용되는 이차 전지에 대한 중요성이 증가되고 있다. 일반적으로, 이차 전지는 단위 중량 당 에너지 밀도가 높고 급속 충전이 가능한 니켈-카드뮴 전지, 니켈-수소 전지, 니켈-아연전지 등이 사용되며, 최근에는 대용량화 및 상온 작동이 가능하고, 용량과 출력을 각기 독립적으로 설계할 수 있는 레독스 플로우 배터리(RFB, redox flow battery)가 각광받고 있는 실정이다.As the use of portable electric appliances such as video cameras, portable phones, and portable PCs is being activated, the importance of secondary batteries, which are mainly used as driving power sources, is increasing. In general, a secondary battery uses a nickel-cadmium battery, a nickel-hydrogen battery, and a nickel-zinc battery, which have high energy density per unit weight and can be rapidly charged. Recently, Redundant flow batteries (RFBs), which can be designed independently of each other, are in the spotlight.

이러한, 이차전지는 음극, 양극 및 분리막으로 구성된 전극조립체를 원통형 또는 각형의 금속캔이나 알루미늄 라미네이트 시트의 파우치형 케이스 내부에 장착하고, 상기 전극 조립체에 전해질을 주입시켜 제조하므로 그 형태가 한정되어 다양한 형태로 제조되는 휴대용 장치의 전력원으로 사용하기 어려운 문제점을 가진다. The secondary battery is manufactured by inserting an electrode assembly composed of a cathode, an anode and a separator into a pouch-shaped case of a cylindrical or rectangular metal can or an aluminum laminate sheet, and injecting an electrolyte into the electrode assembly, It is difficult to use it as a power source for a portable device manufactured in the form of a wire.

이에 따라, 형태의 변형이 용이하고 단면적 직경에 대하여 길이의 비가 매우 큰 케이블형 이차 전지에 대한 연구 개발이 이뤄지고 있으나, 전지의 체적에 비해 표면적이 큰 전극 및 집전체로 인해 전자의 원활한 흐름이 불가능한 문제점을 가진다.Thus, research and development have been conducted on a cable type secondary battery which is easy to deform in shape and has a large length-to-sectional diameter ratio. However, it is difficult to smoothly flow electrons due to electrodes and a current collector having a surface area larger than the volume of the battery I have a problem.

보다 구체적으로, 종래의 케이블형 이차 전지는 전지 내부의 전극 전체에 균일한 충방전이 이뤄지지 않고 외부 도선과 집전체의 접촉부위에 국한되어 충방전이 일어나 전지의 용량, 쿨롱 효율 및 수명의 저하가 발생하는 문제점을 가진다.More specifically, the conventional cable type secondary battery is not uniformly charged and discharged over the entire electrode in the battery, but is charged and discharged only at the contact portion between the external conductor and the current collector, so that the capacity of the battery, the coulomb efficiency, .

본 발명은 바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법에 관한 것으로서, 보다 상세하게는, 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 음극 전지 내부를 관통하도록 구성되는 음극 집전체에 제1 및 제2 음극 단자를 각각 일측과 타측에 구비하고, 음극 전지의 외측을 감싸는 양극 전지의 내부를 관통하도록 구성되는 양극 집전체에 제1 및 제2 양극 단자를 각각 일측과 타측에 구비하며, 제1 양극 단자와 제2 음극 단자 또는 제2 양극 단자와 제1 음극 단자를 이용하여 충방전을 수행하는 바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cable type secondary battery using a vanadium redox couple and a charging / discharging method thereof, and more particularly, to a cable type secondary battery using a vanadium redox couple, A first positive electrode terminal and a second negative electrode terminal are provided on one side and the other side of the positive electrode current collector which is provided on one side and the other side of the first and second negative electrode terminals and penetrates the inside of the positive electrode cell surrounding the negative electrode cell, The present invention relates to a cable type secondary battery using a vanadium redox couple which performs charge and discharge by using a first positive electrode terminal and a second negative electrode terminal, or a second positive electrode terminal and a first negative electrode terminal, and a charging and discharging method thereof.

이에, 본 발명자는, 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 음극 전극 내부를 관통하도록 구성되는 음극 집전체에 제1 및 제2 음극 단자를 각각 일측과 타측에 구비하고, 음극 전지의 외측을 감싸는 양극 전극의 내부를 관통하도록 구성되는 양극 집전체에 제1 및 제2 양극 단자를 각각 일측과 타측에 구비하며, 제1 양극 단자와 제2 음극 단자 또는 제2 양극 단자와 제1 음극 단자를 이용하여 충방전을 수행하는 바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법을 발명하기에 이르렀다.
The present inventors have found that a negative electrode current collector constructed to penetrate the inside of a negative electrode of a cable type secondary battery using a vanadium redox couple has first and second negative electrode terminals on one side and the other side respectively, A first positive electrode terminal and a second negative electrode terminal, and a first positive electrode terminal and a second negative electrode terminal are provided on one side and the other side, respectively, of a positive electrode current collector passing through the inside of the wrapping positive electrode, The present invention relates to a cable type secondary battery using a vanadium redox couple which performs charging / discharging by using the vanadium redox couple, and a charging / discharging method thereof.

한국공개특허 제10- 2005-0099903호Korean Patent Publication No. 10- 2005-0099903

본 발명은 상술된 문제점을 해결하기 위해 안출된 것으로, 본 발명의 목적은, 양극 전극의 내부를 관통하는 양극 집전체의 일측에 구비된 제1 양극 단자와 음극 전극의 내부를 관통하는 음극 집전체의 타측에 구비된 제2 음극 단자를 이용하거나, 상술된 양극 집전체의 타측에 구비된 제2 양극 단자와 상술된 음극 집전체의 일측에 구비된 제1 음극 단자를 이용하여 케이블형 이차 전지를 충방전하는 바나듐 레독스 커플을 이용한 케이블형 이차 전지 및 이의 충방전 방법에 관한 것이다.
SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-described problems, and an object of the present invention is to provide a positive electrode collector, which has a first positive electrode terminal provided on one side of a positive electrode collector passing through the inside of a positive electrode, Type secondary battery provided on the other side of the above-described positive electrode current collector and the above-described first negative electrode terminal provided on the other side of the above-described negative electrode current collector, The present invention relates to a cable type secondary battery using a vanadium redox couple to charge and discharge and a charging and discharging method therefor.

본 발명에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지는, 음극 전극의 내부를 관통하도록 구성되는 음극 집전체; 상기 음극 전극의 외측을 감싸는 양극 전극의 내부를 관통하도록 구성되는 양극 집전체;를 포함하고, 상기 양극 집전체는 제1 양극 단자 및 제2 양극 단자를 각각 일측 및 타측에 구비한다.A cable type secondary battery using a vanadium redox couple according to the present invention comprises: an anode current collector configured to pass through a cathode electrode; And a cathode current collector configured to pass through the inside of the anode electrode surrounding the cathode electrode, wherein the cathode current collector has a first anode terminal and a second anode terminal on one side and the other side, respectively.

상기 음극 집전체는 제1 음극 단자 및 제2 음극 단자를 각각 일측 및 타측에 구비하고, 그리고 상기 제1 양극 단자와 상기 제2 음극 단자 또는 제2 양극 단자와 제1 음극 단자를 이용하여 충방전을 수행할 수 있다.The negative electrode current collector includes a first negative terminal and a second negative terminal at one side and the other, respectively, and the first positive terminal and the second negative terminal, or the second positive terminal and the first negative terminal, Can be performed.

상기 음극 집전체는, 상기 음극 전극의 양측면으로부터 길이 방향으로 돌출되어 구성될 수 있다.The anode current collector may be configured to protrude in the longitudinal direction from both side surfaces of the cathode electrode.

상기 양극 집전체는, 상기 양극 전극의 양측면으로부터 길이 방향으로 돌출되어 구성될 수 있다. The cathode current collector may be configured to protrude in the longitudinal direction from both side surfaces of the anode electrode.

상기 양극 전극과 상기 음극 전극 사이에 이온 교환 수지가 함침된 중공섬유를 포함하는 분리막을 구비할 수 있다.And a separation membrane including a hollow fiber impregnated with an ion exchange resin between the anode electrode and the cathode electrode.

상기 양극 전극 및 상기 음극 전극은, 카본 펠트를 포함할 수 있다. The anode electrode and the cathode electrode may include carbon felt.

상기 양극 전극은, 바나듐 5가 양이온 및 바나듐 4가 양이온이 용해된 양극 전해액을 포함할 수 있다.The positive electrode may include a positive electrode electrolyte in which vanadium pentavalent cation and vanadium tetravalent cation are dissolved.

상기 음극 전극은, 바나듐 3가 양이온 및 바나듐 2가 양이온이 용해된 음극 전해액을 포함할 수 있다. The cathode electrode may include a cathode electrolyte in which vanadium trivalent cations and vanadium divalent cations are dissolved.

본 발명에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법은 상기 케이블형 이차 전지에 전력을 충전하는 충전 장치를 이용하여 충전을 수행하는 단계; 및 상기 케이블형 이차 전지의 전력을 전력 소비 장치로 공급하여 상기 케이블형 이차 전지의 방전을 수행하는 단계;를 포함하여 구성된다.A method of charging and discharging a cable type secondary battery using a vanadium redox couple according to the present invention comprises the steps of: charging the cable type secondary battery using a charging device for charging electric power; And supplying power of the cable type secondary battery to the power consumption device to perform discharging of the cable type secondary battery.

상기 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법은 상기 케이블형 이차 전지의 제1 양극 단자 및 제2 음극 단자를 이용하여 상기 케이블형 이차 전지의 충방전을 수행하는 단계;를 포함할 수 있다.The charging and discharging method of the cable type secondary battery using the vanadium redox couple includes charging and discharging the cable type secondary battery using the first positive terminal and the second negative terminal of the cable type secondary battery .

바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법은 상기 케이블형 이차 전지의 제2 양극 단자 및 제1 음극 단자를 이용하여 상기 케이블형 이차 전지의 충방전을 수행하는 단계;를 더 포함할 수 있다.The charging and discharging method of the cable type secondary battery using the vanadium redox couple may further include charging and discharging the cable type secondary battery using the second positive terminal and the first negative terminal of the cable type secondary battery .

도 1은 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 내부를 개략적으로 도시한 도면이다.
도 2는 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 측면을 개략적으로 도시한 도면이다.
도 3은 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법을 통해 충방전되는 케이블형 이차 전지의 방전 용량을 도시한 도시한 그래프이다.
도 4는 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법을 통해 충방전되는 케이블형 이차 전지의 콜롱 효율을 도시한 도시한 그래프이다.1 is a schematic view showing the inside of a cable type secondary battery using a vanadium redox couple according to an embodiment of the present invention.
2 is a schematic view illustrating a side view of a cable type secondary battery using a vanadium redox couple according to an embodiment of the present invention.
3 is a graph showing a discharge capacity of a cable type secondary battery charged and discharged through a charging / discharging method of a cable type secondary battery using a vanadium redox couple according to an embodiment of the present invention.
FIG. 4 is a graph illustrating the Coulomb efficiency of a cable-type secondary battery that is charged and discharged through a charging / discharging method of a cable-type secondary battery using a vanadium redox couple according to an embodiment of the present invention.

본 발명을 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다. 여기서, 반복되는 설명, 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능, 및 구성에 대한 상세한 설명은 생략한다. 본 발명의 실시형태는 당 업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다. 따라서, 도면에서의 요소들의 형상 및 크기 등은 보다 명확한 설명을 위하여 과장될 수 있다.The present invention will now be described in detail with reference to the accompanying drawings. Hereinafter, a repeated description, a known function that may obscure the gist of the present invention, and a detailed description of the configuration will be omitted. Embodiments of the present invention are provided to more fully describe the present invention to those skilled in the art. Accordingly, the shapes and sizes of the elements in the drawings and the like can be exaggerated for clarity.

명세서 전체에서, 어떤 부분이 어떤 구성 요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.
Throughout the specification, when an element is referred to as "comprising ", it means that it can include other elements as well, without excluding other elements unless specifically stated otherwise.

도 1은 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 내부를 개략적으로 도시한 도면이고, 도 2는 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 측면을 개략적으로 도시한 도면이다.FIG. 1 is a schematic view showing the inside of a cable type secondary battery using a vanadium redox couple according to an embodiment of the present invention. FIG. 2 is a schematic view showing a cable type using a vanadium redox couple according to an embodiment of the present invention. And schematically showing a side surface of the secondary battery.

도 1 및 도 2를 참조하면, 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)는 음극 전극(110), 음극 집전체(120), 양극 전극(130), 양극 집전체(140) 및 분리막(150)을 포함할 수 있다. 또한, 음극 집전체(120)는 제1 및 제2 음극 단자(121, 122)를 포함할 수 있으며, 양극 집전체(140)는 제1 및 제2 양극 단자(141, 142)를 포함할 수 있다.Referring to FIGS. 1 and 2, a cable-type secondary battery 100 using a vanadium redox couple according to an embodiment of the present invention includes a cathode electrode 110, an anode current collector 120, an anode electrode 130, A cathode current collector 140, and a separator 150. The anode current collector 120 may include first and second cathode terminals 121 and 122 and the cathode current collector 140 may include first and second cathode terminals 141 and 142. [ have.

본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)는 가늘고 긴 형태로 구성되어 길이 방향으로 신축 가능한 케이블형 구조일 수 있으며, 이에 따라, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)에 포함된 상술된 구성 또한 케이블형 구조일 수 있다.The cable type secondary battery 100 using the vanadium redox couples according to an embodiment of the present invention may have a cable-type structure that is formed in an elongated shape and can be stretched in the longitudinal direction. Thus, a cable using a vanadium redox couple The above-described configuration included in the rechargeable battery 100 may also be a cable-like structure.

또한, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)는 외부로부터 공급된 전기 에너지를 화학 에너지로 변환하여 저장하고, 저장된 화학 에너지를 전기 에너지로 변환하여 외부로 공급하기 위한 구성을 포함할 수 있다.In addition, the cable-type secondary battery 100 using the vanadium redox couple may include a structure for converting the electrical energy supplied from the outside into chemical energy and storing the converted chemical energy into electrical energy for external supply have.

음극 전극(110)은 바나듐 3가 양이온 및 바나듐 2가 양이온이 용해된 음극 전해액을 포함할 수 있다. The cathode electrode 110 may include a cathode electrolyte in which vanadium trivalent cations and vanadium divalent cations are dissolved.

이러한, 음극 전극(110)에서는 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충전 반응시 바나듐 3가 양이온이 전자를 받아들여 바나듐 2가 양이온으로 변환되는 환원반응이 일어나게 되고, 방전 반응시에는 상술된 충전 반응과 반대로 바나듐 양이온의 산화수가 변화되는 산화/환원 반응이 일어남으로써 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전이 수행된다.In the cathode electrode 110, during the charging reaction of the cable-type secondary battery 100 using the vanadium redox couple, the vanadium trivalent cation accepts electrons to cause a reduction reaction in which the vanadium divalent cation is converted, An oxidation / reduction reaction occurs in which the oxidation number of the vanadium cation is changed as opposed to the charging reaction described above, so that the charging and discharging of the cable-type secondary battery 100 using the vanadium redox couple is performed.

음극 전극(110)은 구부러질 수 있으며, 음극 전해액을 저장할 수 있는 공간이 내부에 형성될 수 있다.The cathode electrode 110 may be bent and a space capable of storing the cathode electrolyte may be formed therein.

음극 전극(110)은 카본 펠트를 포함하는 소재일 수 있으나, 구부러질 수 있는 한 그 소재의 종류는 한정되지 않으며 당 기술분야에서 일반적으로 사용되는 소재가 사용될 수 있음을 유의한다.The cathode electrode 110 may be a material containing carbon felt, but it should be noted that the kind of the material is not limited as long as it can be bent, and a material commonly used in the art can be used.

음극 전극(110)의 직경은 0.1μm 내지 500μm일 수 있다.The diameter of the cathode electrode 110 may be between 0.1 μm and 500 μm.

이때, 음극 전해액의 용매는 황산 수용액(HSSO4)일 수 있다.At this time, the solvent of the negative electrode electrolyte may be an aqueous sulfuric acid solution (H 2 SO 4 ).

음극 집전체(120)는 음극 전극(110)의 내부를 관통하도록 구성될 수 있다. 보다 구체적으로, 음극 집전체(120)는 음극 전극(110)의 길이 방향으로 연장된 와이어 형태일 수 있으며, 음극 전극(110)의 양단으로 돌출될 수 있다.The anode current collector 120 may be configured to penetrate the inside of the cathode electrode 110. More specifically, the anode current collector 120 may be in the form of a wire extending in the longitudinal direction of the cathode electrode 110, and may protrude from both ends of the cathode electrode 110.

이러한, 음극 집전체(120)는 충방전에 필요한 산화환원 반응시 전자의 이동 경로 역할을 수행할 수 있다.The anode current collector 120 may serve as a path for electrons to flow during the redox reaction required for charging and discharging.

음극 집전체(120)는 스테인리스 스틸(Steel Use Stainless; SUS)을 포함하는 소재일 수 있으나, 강산의 음극 전해액에 내구성이 있는 한 그 소재의 종류는 한정되지 않으며 당 기술분야에서 일반적으로 사용되는 소재가 사용될 수 있음을 유의한다.The anode current collector 120 may be a material including stainless steel (Stainless Use Stainless (SUS)). However, the anode current collector 120 may be made of any material that is generally used in the related art May be used.

일 실시예에서, 음극 집전체(120)는 알루미늄, 니켈, 티탄, 소성탄소 및 구리를 포함하는 소재일 수 있으며, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 가요성 및 경량성을 향상시키기 위하여 폴리피롤(Polypyrrole)과 같은 전도성 고분자를 포함하는 소재일 수 있다.In one embodiment, the anode current collector 120 may be made of a material including aluminum, nickel, titanium, sintered carbon, and copper. The flexibility and light weight of the cable-type secondary battery 100 using the vanadium redox couple It may be a material containing a conductive polymer such as polypyrrole.

음극 집전체(120)의 직경은 0.1μm 내지 500μm일 수 있으나, 음극 전극(110)의 직경 보다 작음을 유의한다.Note that the diameter of the anode current collector 120 may be between 0.1 μm and 500 μm, but smaller than the diameter of the cathode electrode 110.

한편, 음극 집전체(120)는 제1 및 제2 음극 단자(121, 122)를 각각 일측 및 타측에 구비할 수 있다. 보다 구체적으로, 음극 집전체(120)의 양끝단에는 음극 집전체(120)의 길이 방향으로 제1 및 제2 음극 단자(121, 122)가 돌출되어 형성될 수 있다.On the other hand, the anode current collector 120 may include first and second cathode terminals 121 and 122 on one side and the other side, respectively. More specifically, the first and second negative electrode terminals 121 and 122 may protrude from both ends of the negative electrode current collector 120 in the longitudinal direction of the negative electrode current collector 120.

이때, 제 1 또는 제2 음극 단자(121)는 외부로부터 전력을 공급받거나 외부로 전력을 공급하는 외부 도선과 연결되어 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행할 수 있다. At this time, the first or second negative terminal 121 is connected to an external conductor which is supplied with electric power from the outside or supplies electric power to the outside, so that the charging or discharging of the cable type secondary battery 100 using the vanadium redox couple can be performed have.

음극 집전체(120)는 활물질의 전기화학 반응에 의해 생성된 전자를 모으거나 전기화학 반응에 필요한 전자를 공급하는 역할을 하는 것으로, 일반적으로 구리나 알루미늄 등의 금속을 사용한다. The anode current collector 120 collects electrons generated by the electrochemical reaction of the active material and supplies electrons necessary for the electrochemical reaction. In general, a metal such as copper or aluminum is used.

양극 전극(130)은 바나듐 5가 양이온 및 바나듐 4가 양이온이 용해된 양극 전해액을 포함할 수 있다. 이러한, 양극 전극(130)에서는 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충전 반응시 바나듐 4가 양이온이 산화되어 바나듐 5가 양이온으로 변환되는 산화반응이 일어나게 되고, 방전 반응시에는 상술된 충전 반응과 반대로 바나듐 양이온의 산화수가 변화되는 산화/환원 반응이 일어남으로써 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전이 수행된다.The anode electrode 130 may include a cathode electrolyte in which vanadium pentavalent cations and vanadium tetravalent cations are dissolved. During the charging reaction of the cable-type secondary battery 100 using the vanadium redox couple, the oxidation reaction in which vanadium tetravalent cations are oxidized and vanadium 5 is converted into cations takes place in the anode electrode 130, The oxidation / reduction reaction in which the oxidation number of the vanadium cation is changed is performed as opposed to the charging reaction in which the vanadium redox couple is used to charge and discharge the cable type secondary battery 100 using the vanadium redox couple.

양극 전극(130)은 구부러질 수 있으며, 양극 전해액을 저장할 수 있는 공간이 내부에 형성될 수 있다.The anode electrode 130 may be bent and a space capable of storing the anode electrolyte may be formed therein.

양극 전극(130)은 카본 펠트를 포함하는 소재일 수 있으나, 구부러질 수 있는 한 그 소재의 종류는 한정되지 않으며 당 기술분야에서 일반적으로 사용되는 소재가 사용될 수 있음을 유의한다.The anode electrode 130 may be a material containing carbon felt, but the material is not limited as long as it can be bent, and it is noted that a material generally used in the art can be used.

이때, 양극 전해액의 용매는 황산 수용액(HSSO4)일 수 있다.At this time, the solvent of the positive electrode electrolyte may be an aqueous solution of sulfuric acid (H 2 SO 4 ).

양극 집전체(140)는 양극 전극(130)의 내부를 관통하도록 구성될 수 있다. 보다 구체적으로, 양극 집전체(140)는 양극 전극(130)의 길이 방향으로 연장된 와이어 형태일 수 있으며, 양극 전극(130)의 양단으로 돌출될 수 있다.The anode current collector 140 may be configured to penetrate the inside of the anode electrode 130. More specifically, the cathode current collector 140 may be in the form of a wire extending in the longitudinal direction of the anode electrode 130, and may protrude from both ends of the anode electrode 130.

이러한, 양극 집전체(140)는 충방전에 필요한 산화환원 반응시 전자의 이동 경로 역할을 수행할 수 있다.The cathode current collector 140 may serve as a path for transferring electrons during a redox reaction required for charging and discharging.

양극 집전체(140)는 스테인리스 스틸을 포함하는 소재일 수 있으나, 강산의 양극 전해액에 내구성이 있는 한 그 소재의 종류는 한정되지 않으며 당 기술분야에서 일반적으로 사용되는 소재가 사용될 수 있음을 유의한다.The anode current collector 140 may be a material including stainless steel, but it is noted that the type of the anode current collector 140 is not limited as long as the cathode electrolyte of the strong acid is durable, and a material commonly used in the art can be used .

일 실시예에서, 양극 집전체(140)는 알루미늄, 니켈, 티탄, 소성탄소 및 구리를 포함하는 소재일 수 있으며, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 가요성 및 경량성을 향상시키기 위하여 폴리피롤과 같은 전도성 고분자를 포함하는 소재일 수 있다.In one embodiment, the cathode current collector 140 may be made of a material including aluminum, nickel, titanium, sintered carbon, and copper. The flexibility and light weight of the cable-type secondary battery 100 using the vanadium redox couple It may be a material including a conductive polymer such as polypyrrole.

양극 집전체(140)의 직경은 0.1μm 내지 500μm일 수 있다.The diameter of the cathode current collector 140 may be 0.1 to 500 mu m.

한편, 양극 집전체(140)는 제1 및 제2 양극 단자(141, 142)를 각각 일측 및 타측에 구비할 수 있다. 보다 구체적으로, 양극 집전체(140)의 양끝단에는 양극 집전체(140)의 길이 방향으로 제1 및 제2 양극 단자(141, 142)가 돌출되어 형성될 수 있다.Meanwhile, the positive electrode current collector 140 may include first and second positive electrode terminals 141 and 142 on one side and the other side, respectively. More specifically, at both ends of the positive electrode current collector 140, first and second positive electrode terminals 141 and 142 may protrude in the longitudinal direction of the positive electrode current collector 140.

이때, 제 1 또는 제2 양극 단자(121)는 외부로부터 전력을 공급받거나 외부로 전력을 공급하는 외부 도선과 연결되어 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행할 수 있다. At this time, the first or second cathode terminal 121 is connected to an external conductor which is supplied with electric power from the outside or supplies electric power to the outside, so that the charging or discharging of the cable type secondary battery 100 using the vanadium redox couple can be performed have.

분리막(150)은 음극 전극(110) 및 양극 전극(130) 간에 수소 이온은 전달시키고, 음극 및 양극 전해액의 양이온이 상대극으로 이동하는 것은 차단시키는 역할을 수행할 수 있다.The separation membrane 150 may transfer hydrogen ions between the cathode electrode 110 and the anode electrode 130 and may block the movement of the cathodes and cathodes of the anode electrolyte to the counter electrode.

이러한, 분리막(150)은 이온 교환 수지가 함침된 중공 섬유(Hollow Fiber)로 구성될 수 있다.The separation membrane 150 may be formed of a hollow fiber impregnated with an ion exchange resin.

분리막(150)의 중공 섬유의 구조 및 소재는 한정되지 않으며 당 기술분야에서 일반적으로 사용되는 소재가 사용될 수 있음을 유의한다.It is noted that the structure and material of the hollow fibers of the separation membrane 150 are not limited, and that materials generally used in the art can be used.

예를 들어, 중공 섬유는 폴리 이미드(Polyimide; PI), 나일론, 폴리에틸렌테레프탈레이트(Polyethyleneterephtalate; PET), 폴리테트라플루오로 에틸렌(Polytetrafluoro Ethylene; PTFE), 폴리에틸렌(Polyethylene; PE), 폴리프로필렌(Polypropylene; PP), 폴리아릴렌에테르술폰(Poly(arylene ethersulfone); PAES), 폴리에테르에테르케톤(Polyetheretherketone; PEEK) 중 적어도 하나 이상을 포함할 수 있다.For example, the hollow fiber may be made of a material selected from the group consisting of polyimide (PI), nylon, polyethylene terephthalate (PET), polytetrafluoroethylene (PTFE), polyethylene (PE), polypropylene (PP), poly (arylene ethersulfone) (PAES), and polyetheretherketone (PEEK).

분리막(150)의 중공 섬유의 기공에 함침되는 이온 교환 수지는 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전시 이온 교환을 수행할 수 있는 물질이라면 한정되지 않으며 당 기술분야에서 일반적으로 사용되는 소재가 사용될 수 있음을 유의한다.The ion exchange resin impregnated into the pores of the hollow fiber of the separation membrane 150 is not limited as long as it is a material capable of performing ion exchange when charging and discharging the cable type secondary battery 100 using the vanadium redox couple, May be used.

예를 들어, 이온 교환 수지는 나피온(Nafion), 술폰화 폴리에테르에테르케톤(PEEK, Polyetheretherketone), 술폰화 폴리에테르케톤 (sPEK, Sulfonated(polyetherketone)), 폴리비닐리덴 플로라이드-그라프트-폴리스티렌 술폰산(Poly(vinylidene fluoride)-graft-poly(styrene sulfonic acid), PVDF-g-PSSA) 및 술폰화 폴리플루로레닐 에테르케톤(Sulfonated poly (fluorenyl ether ketone)) 중 적어도 하나 이상을 포함할 수 있다. For example, ion exchange resins include Nafion, sulfonated polyetheretherketone (PEEK), sulfonated polyetherketone (sPEK), polyvinylidene fluoride-graft-polystyrene (Vinylidene fluoride) -graft-poly (styrene sulfonic acid), PVDF-g-PSSA), and sulfonated poly (fluorenyl ether ketone) .

분리막(150)의 두께는 0.1μm 내지 500μm일 수 있다.
The thickness of the separation membrane 150 may be between 0.1 μm and 500 μm.

본 발명의 일 실시예에 따른, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)는 제1 음극 단자(121)과 제2 양극 단자(142) 또는 제2 음극 단자(122)와 제1 양극 단자(141)를 이용하여 충방전을 수행할 수 있다.A cable type secondary battery 100 using a vanadium redox couple according to an embodiment of the present invention includes a first negative electrode terminal 121 and a second positive electrode terminal 142 or a second negative electrode terminal 122, Charging and discharging can be performed using the terminal 141.

즉, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 일측에 구비된 전극 단자(121, 141) 중 어느 하나를 선택하여 외부로부터 전력을 공급 받거나 외부로 전력을 공급하는 외부 도선과 연결하는 경우, 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 타측에 구비된 전극 단자(122, 142) 중 일측에서 선택된 전극 단자와 극성이 반대인 전극 단자를 외부 도선과 연결하여 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행할 수 있다.That is, any one of the electrode terminals 121 and 141 provided on one side of the cable-type secondary battery 100 using the vanadium redox couple may be selected and connected to an external conductor for receiving power from the outside or supplying power to the outside Electrode terminals 122 and 142 provided on the other side of the cable-type secondary battery 100 using the vanadium redox couple are connected to the external leads at the opposite polarity to the electrode terminals selected at one side, It is possible to perform charging and discharging of the cable-type secondary battery 100 using the battery.

이를 통해, 체적에 비해 표면적이 큰 음극 및 양극 전극(110, 130)과 음극 및 양극 집전체(120, 140)로 인해 전극 전체에 균일한 충방전이 이뤄지지 않고 외부 도선과 음극 및 양극 집전체(120, 140)의 접촉부위에 국한되어 충방전이 일어남으로써, 전지의 용량, 쿨롱 효율 및 수명의 저하가 발생하는 문제점을 해소할 수 있다.
As a result, the cathode and the anode electrodes 110 and 130 having a larger surface area than the volume, the cathode and the anode current collectors 120 and 140 do not uniformly charge and discharge the entire electrode, 120, and 140, thereby preventing the problem of deterioration of battery capacity, coulomb efficiency, and service life.

다음으로, 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법의 실험예에 대해 설명하도록 한다.Next, an experimental example of a charging / discharging method of a cable type secondary battery using a vanadium redox couple according to an embodiment of the present invention will be described.

바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법의 실험예 1, 2, 비교예 1 및 2에서 제1 음극 단자, 제2 음극 단자, 제1 양극 단자 및 제2 양극 단자(121, 122, 141, 142)와 외부 도선의 연결 모드는 하기의 표 1과 같다.The first negative electrode terminal, the second negative electrode terminal, the first positive electrode terminal, and the second positive electrode terminal 121, 122 in the Experimental Examples 1, 2, and Comparative Examples 1 and 2 of the charging and discharging method of the cable type secondary battery using the vanadium redox couple , 141, 142) and the outer conductor are shown in Table 1 below.

연결 모드Connection mode 단자 연결Terminal connection 실험예 1(제1 모드)Experimental Example 1 (first mode) 제1 음극 단자(121)The first negative electrode terminal 121, 제2 양극 단자(141)The second positive electrode terminal 141, 실험예 2(제2 모드)Experimental Example 2 (Second Mode) 제2 음극 단자(122)The second negative terminal 122, 제1 양극 단자(142)The first positive electrode terminal 142, 비교예 1(제3 모드)Comparative Example 1 (third mode) 제1 음극 단자(121)The first negative electrode terminal 121, 제1 양극 단자(141)The first positive electrode terminal 141, 비교예 2(제4 모드)Comparative Example 2 (fourth mode) 제2 음극 단자(122)The second negative terminal 122, 제2 양극 단자(142)The second positive electrode terminal 142,

<실험예 1><Experimental Example 1>

실험예 1은 제1 음극 단자(121)와 제2 양극 단자(142)를 외부 도선의 양단과 연결한 제1 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행하여 전지의 방전 용량 및 콜롱 효율을 측정하였다.In Experimental Example 1, the charging and discharging of the cable-type secondary battery 100 using the vanadium redox couple in the first mode in which the first anode terminal 121 and the second anode terminal 142 are connected to both ends of the outer conductor were performed The discharge capacity and the cologen efficiency of the battery were measured.

<실험예 2><Experimental Example 2>

실험예 2는 제2 음극 단자(122)와 제1 양극 단자(141)를 외부 도선의 양단과 연결한 제2 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행하여 전지의 방전 용량 및 콜롱 효율을 측정하였다.In Experimental Example 2, the charging and discharging of the cable-type secondary battery 100 using the vanadium redox couple in the second mode in which the second negative terminal 122 and the first positive terminal 141 are connected to both ends of the outer conductor are performed The discharge capacity and the cologen efficiency of the battery were measured.

<비교예 1>&Lt; Comparative Example 1 &

비교예 1은 제1 음극 단자(121)와 제1 양극 단자(141)를 외부 도선의 양단과 연결한 제1 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행하여 전지의 방전 용량 및 콜롱 효율을 측정하였다.In Comparative Example 1, the charging and discharging of the cable-type secondary battery 100 using the vanadium redox couple in the first mode in which the first negative electrode terminal 121 and the first positive electrode terminal 141 were connected to both ends of the outer conductor were performed The discharge capacity and the cologen efficiency of the battery were measured.

<비교예 2>&Lt; Comparative Example 2 &

비교예 2는 제2 음극 단자(122)와 제2 양극 단자(142)를 외부 도선의 양단과 연결한 제1 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전을 수행하여 전지의 방전 용량 및 콜롱 효율을 측정하였다.
In Comparative Example 2, the charging and discharging of the cable-type secondary battery 100 using the vanadium redox couple in the first mode in which the second negative electrode terminal 122 and the second positive electrode terminal 142 are connected to both ends of the outer conductor were performed The discharge capacity and the cologen efficiency of the battery were measured.

도 3은 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법을 통해 충방전되는 케이블형 이차 전지의 방전 용량을 도시한 도시한 그래프이다.3 is a graph showing a discharge capacity of a cable type secondary battery charged and discharged through a charging / discharging method of a cable type secondary battery using a vanadium redox couple according to an embodiment of the present invention.

도 3을 참조하면, 제1 및 제2 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전 수행 시 측정된 방전 용량의 편차에 비해, 제3 및 제4 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전 수행 시 측정된 방전 용량의 편차는 매우 큼을 알 수 있다.Referring to FIG. 3, in comparison with the deviation of the discharge capacity measured in the charging and discharging of the cable-type secondary battery 100 using the vanadium redox couple in the first and second modes, in the third and fourth modes, It can be seen that the deviation of the measured discharge capacity during charging and discharging of the cable-type secondary battery 100 using a couple is very large.

이는, 직경 대비 길이가 긴 형태의 특성을 갖는 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)가 길이 방향으로 충전 상태(State Of Charge; SOC) 및 전극의 저항이 상이하여 발생하는 현상임을 알 수 있다.It is known that the cable type secondary battery 100 using the vanadium redox couple having the shape of a length-to-diameter-length shape is a phenomenon that occurs due to the difference in the state of charge (SOC) and electrode resistance in the longitudinal direction .

이에 따라, 본 발명의 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법 통해 충방전을 수행하는 경우, 전지의 용량 편차를 감소시켜 전지의 용량 저하를 방지하고, 전지의 수명을 연장시킬 수 있다.
Accordingly, when charging / discharging the cable type secondary battery using the vanadium redox couples according to the present invention, it is possible to reduce the capacity variation of the battery to prevent a decrease in the capacity of the battery and to prolong the life of the battery have.

도 4는 본 발명의 일 실시예에 따른 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법을 통해 충방전되는 케이블형 이차 전지의 콜롱 효율을 도시한 도시한 그래프이다.FIG. 4 is a graph illustrating the Coulomb efficiency of a cable-type secondary battery that is charged and discharged through a charging / discharging method of a cable-type secondary battery using a vanadium redox couple according to an embodiment of the present invention.

도 4를 참조하면, 제1 및 제2 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전 수행 시 측정된 콜롱 효율에 비해, 제3 및 제4 모드에서 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 충방전 수행 시 측정된 콜롱 효율이 낮음을 알 수 있다.Referring to FIG. 4, it can be seen that, in the third and fourth modes, the vanadium redox couples are significantly lower in the first and second modes than in the culong efficiency measured in the charging and discharging of the cable type secondary battery 100 using the vanadium redox couple. It can be seen that the measured coulomb efficiency is low when the rechargeable battery of the cable type secondary battery 100 is used.

이는, 상술한 바와 같이, 직경 대비 길이가 긴 형태의 특성을 갖는 바나듐 레독스 커플을 이용한 케이블형 이차 전지(100)의 전극에 길이 방향으로 저항 편차를 가짐으로써 발생하는 현상으로, 본 발명의 바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법 통해 충방전을 수행하는 경우, 전지의 콜롱 효율의 저하를 방지할 수 있다.
This is a phenomenon that occurs when a resistance variation in the longitudinal direction is applied to the electrode of the cable-type secondary battery 100 using the vanadium redox couple having the characteristics of a shape having a length to length ratio with respect to the diameter, When charging / discharging is performed through the charging / discharging method of the cable type secondary battery using the redox couple, deterioration of the colun efficiency of the battery can be prevented.

상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention as defined by the following claims It can be understood that

100 : 바나듐 레독스 커플을 이용한 케이블형 이차 전지
110 : 음극 전극
120 : 음극 집전체
121 : 제1 음극 단자 122 : 제2 음극 단자
130 : 양극 전극
140 : 양극 집전체
141 : 제2 양극 단자 142 : 제2 양극 단자
150 : 분리막
100: Cable type secondary battery using vanadium redox couple
110: cathode electrode
120: cathode collector
121: first negative terminal 122: second negative terminal
130: anode electrode
140: positive current collector
141: second positive electrode terminal 142: second positive electrode terminal
150: membrane

Claims (10)

바나듐 레독스 커플을 이용한 케이블형 이차 전지에 있어서,
음극 전극의 내부를 관통하도록 구성되는 음극 집전체;
상기 음극 전극의 외측을 감싸는 양극 전극의 내부를 관통하도록 구성되는 양극 집전체;를 포함하고,
상기 양극 집전체는 제1 및 제2 양극 단자를 각각 일측 및 타측에 구비하고,
상기 음극 집전체는 제1 및 제2 음극 단자를 각각 일측 및 타측에 구비하고, 그리고
상기 제1 양극 단자와 상기 제2 음극 단자 또는 제2 양극 단자와 제1 음극 단자를 이용하여 충방전을 수행하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
In a cable-type secondary battery using a vanadium redox couple,
An anode current collector configured to penetrate the inside of the cathode electrode;
And a cathode current collector configured to penetrate the inside of the anode electrode that surrounds the outside of the cathode electrode,
Wherein the positive electrode collector has first and second positive electrode terminals on one side and the other side, respectively,
The negative electrode current collector has first and second negative electrode terminals on one side and the other side, respectively, and
Wherein the charge / discharge is performed using the first positive electrode terminal, the second negative electrode terminal, the second positive electrode terminal, and the first negative electrode terminal.
A cable type secondary battery using a vanadium redox couple.
제1항에 있어서,
상기 음극 집전체는,
상기 음극 전극의 양측면으로부터 길이 방향으로 돌출되어 구성되는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
The method according to claim 1,
The anode current collector
Wherein the cathode electrode is protruded in the longitudinal direction from both side surfaces of the cathode electrode.
A cable type secondary battery using a vanadium redox couple.
제1항에 있어서,
상기 양극 집전체는,
상기 양극 전극의 양측면으로부터 길이 방향으로 돌출되어 구성되는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
The method according to claim 1,
The positive electrode current collector
Wherein the anode electrode is protruded in the longitudinal direction from both side surfaces of the anode electrode.
A cable type secondary battery using a vanadium redox couple.
제1항에 있어서,
상기 양극 전극과 상기 음극 전극 사이에 이온 교환 수지가 함침된 중공섬유를 포함하는 분리막을 구비하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
The method according to claim 1,
And a separation membrane including a hollow fiber impregnated with an ion exchange resin between the anode electrode and the cathode electrode.
A cable type secondary battery using a vanadium redox couple.
제1항에 있어서,
상기 양극 전극 및 상기 음극 전극은,
카본 펠트를 포함하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
The method according to claim 1,
Wherein the anode electrode and the cathode electrode are made of a metal,
Characterized in that it comprises carbon felt.
A cable type secondary battery using a vanadium redox couple.
제1항에 있어서,
상기 양극 전극은,
바나듐 5가 양이온 및 바나듐 4가 양이온이 용해된 양극 전해액을 포함하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
The method according to claim 1,
The positive electrode includes:
Characterized in that it comprises a positive electrode electrolytic solution in which vanadium pentavalent cation and vanadium tetravalent cation are dissolved.
A cable type secondary battery using a vanadium redox couple.
제1항에 있어서,
상기 음극 전극은,
바나듐 3가 양이온 및 바나듐 2가 양이온이 용해된 음극 전해액을 포함하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지.
The method according to claim 1,
The cathode electrode
Characterized in that it comprises a negative electrode electrolyte in which vanadium trivalent cations and vanadium divalent cations are dissolved.
A cable type secondary battery using a vanadium redox couple.
제1항 내지 제7항 중 어느 한 항에 따른 케이블형 이차 전지에 전력을 충전하는 충전 장치를 이용하여 충전을 수행하는 단계; 및
상기 케이블형 이차 전지의 전력을 전력 소비 장치로 공급하여 상기 케이블형 이차 전지의 방전을 수행하는 단계;를 포함하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법.
A method of charging a cable rechargeable battery, comprising: charging a cable type secondary battery according to any one of claims 1 to 7 using a charging device for charging electric power; And
And supplying power of the cable type secondary battery to the power consumption device to perform discharging of the cable type secondary battery.
A method for charging and discharging a cable type secondary battery using a vanadium redox couple.
제8항에 있어서,
상기 케이블형 이차 전지의 제1 양극 단자 및 제2 음극 단자를 이용하여 상기 케이블형 이차 전지의 충방전을 수행하는 단계;를 포함하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법.
9. The method of claim 8,
And charging and discharging the cable-type secondary battery using the first positive terminal and the second negative terminal of the cable-type secondary battery.
A method for charging and discharging a cable type secondary battery using a vanadium redox couple.
제8항에 있어서,
상기 케이블형 이차 전지의 제2 양극 단자 및 제1 음극 단자를 이용하여 상기 케이블형 이차 전지의 충방전을 수행하는 단계;를 더 포함하는 것을 특징으로 하는,
바나듐 레독스 커플을 이용한 케이블형 이차 전지의 충방전 방법.9. The method of claim 8,
Further comprising the step of charging / discharging the cable type secondary battery using the second positive terminal and the first negative terminal of the cable type secondary battery,
A method for charging and discharging a cable type secondary battery using a vanadium redox couple.
KR1020140177799A 2014-12-10 2014-12-10 Cable type secondary battery using Vanadium redox couple and method for charging and discharging the same KR101802569B1 (en)