KR20160054959A - Polyketone cable box - Google Patents

Abstract

The present invention relates to a bracket for fastening a polyketone power cable manufactured by injection molding of a linear alternating polyketone formed of carbon dioxide and at least one kind of ethylenically unsaturated hydrocarbon, and more particularly, to a bracket for fastening a polyketone power cable, which have improved impact strength and dimensional stability of the bracket.

Description

Polyketone power line braiding {Polyketone cable box}

TECHNICAL FIELD The present invention relates to a polyketone used in a power line binding cable box (cable box), and more particularly to a power line binding bracket obtained by injection-molding a linear alternating polyketone composed of carbon monoxide and at least one ethylenically unsaturated hydrocarbon.

The industrial line, also known as a power line tying bracket, aka cable box, is used to organize power lines (cables) that are tangled together. Conventionally, high-impact PBT was used for the brackets for power line binding. However, the impact resistance is insufficient for long use, and injection molding takes a comparatively long injection time.

Therefore, it was necessary to study a material capable of manufacturing a power line binding bracket through a short injection time while ensuring sufficient impact resistance.

On the other hand, Polyketone (PK) is an inexpensive material of raw material and polymerization process ratio compared with general engineering plastic materials such as polyamide, polyester and polycarbonate. It has excellent properties such as heat resistance, chemical resistance, fuel permeability and abrasion resistance It is widely applied to various industries.

For this reason, there is a growing interest in a family of linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon, known as polyketones or polyketone polymers. U.S. Patent No. 4,880,903 discloses a linear alternating polyketone terpolymer consisting of carbon monoxide, ethylene and terephthalic unsaturated hydrocarbons such as propylene. The process for preparing the polyketone polymer is generally carried out by reacting a compound of a Group VIII metal selected from among palladium, cobalt or nickel with an anion of a strong halogen-hydrohalogentic acid, , Phosphorus, arsenic, or antimony (Antimon). U.S. Patent No. 4,843,144 discloses a method for producing a polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon using a palladium compound, an anion of a nonhydrohalogen acid having a pKa of less than 6, and a catalyst that is a bidentate ligand Lt; / RTI >

Korean Patent No. 1004453540000 Korean Patent No. 1008108650000

In order to solve the above problems, it is an object of the present invention to obtain a power line binding bracket which is characterized by sufficient impact resistance and dimensional stability using polyketone.

In order to accomplish the above object, the present invention provides a power line binding bracket, which is manufactured by injection molding a linear alternating polyketone composed of carbon monoxide and at least one ethylenic unsaturated hydrocarbon.

Specifically, the bracket for power line binding has an impact strength of 8 kJ / m 2 or more, the polyketone has a molar ratio of ethylene to propylene in the range of 9: 1 to 24: 1, and the inherent viscosity of the polyketone is 1.0 to 2.0 dl / g, and the polyketone has a molecular weight distribution of 1.5 to 2.5.

In addition, in the polyketone used in the power line binding bracket of the present invention, the ligand of the catalyst composition used in the polymerization is ((2,2-dimethyl-1,3-dioxane-5,5- ) Bis (bis (2-methoxyphenyl) phosphine).

The power line binding brackets of the present invention have the effect of shortening the impact strength and cycle time as compared with the conventional high impact polybutylene terephthalate (high impact PBT) material. Therefore, a bracket for power line bonding improved in impact resistance and dimensional stability by polyketone injection molding can be obtained.

1. Polyketone polymer composition

The polyketone polymer of the present invention is a linear alternating structure and substantially contains carbon monoxide per one molecule of unsaturated hydrocarbon. Ethylenically unsaturated hydrocarbons suitable for use as precursors of polyketone polymers have up to 20 carbon atoms, preferably up to 10 carbon atoms. Ethylenically unsaturated hydrocarbons can also be selected from the group consisting of ethene and alpha-olefins such as propene, 1-butene, iso-butene, 1- hexene, 1- octene, , Or an aryl aliphatic group containing an aryl substituent on another aliphatic molecule, particularly containing an aryl substituent on an ethylenically unsaturated carbon atom. Examples of aryl aliphatic hydrocarbons in ethylenically unsaturated hydrocarbons include styrene, p-methyl styrene, p-ethyl styrene and m-isopropyl styrene. The polyketone polymer preferably used in the present invention is a copolymer of carbon monoxide and ethene or a second ethylenically unsaturated hydrocarbon having carbon monoxide, ethene and at least three carbon atoms, in particular alpha-olefins such as propene Is a terpolymer.

When the polyketone terpolymer is used as the main polymer component of the blend of the present invention, there are at least two units containing an ethylene moiety in each unit containing the second hydrocarbon moiety in the terpolymer. It is preferable that the number of units containing the second hydrocarbon moiety is from 10 to 100.

Preferred polymeric rings of the polyketone polymers in the present invention can be represented by the following formula (1).

[Chemical Formula 1]

- [CO- (-CH2-CH2-)] x- [CO- (G)] y-

In the above formula (1), G is an ethylenically unsaturated hydrocarbon, particularly an ethylenically unsaturated hydrocarbon having at least three carbon atoms, and x: y is preferably at least 1: 0.01.

In another embodiment, the polyketone polymer is a copolymer comprising repeating units represented by the general formulas (1) and (2), and y / x is preferably 0.03 to 0.3. When the value of the y / x value is less than 0.03, there is a limit in that the meltability and processability are inferior. When the value of y / x is more than 0.3, the mechanical properties are poor. Further, y / x is more preferably 0.03 to 0.1.

- [- CH2CH2-CO] x- (1)

- [- CH2 --CH (CH3) - CO] y - (2)

In addition, the melting point of the polymer can be controlled by controlling the ratio of ethylene to propylene in the polyketone polymer. For example, when the molar ratio of ethylene: propylene: carbon monoxide is adjusted to 46: 4: 50, the melting point is about 220 ° C, while the melting point is adjusted to 235 ° C when the molar ratio is adjusted to 47.3: 2.7: 50.

Particularly preferred are polyketone polymers having a number average molecular weight of from 100 to 200,000, especially from 20,000 to 90,000, as measured by gel permeation chromatography. The physical properties of the polymer are determined according to the molecular weight, depending on whether the polymer is a copolymer or a terpolymer and, in the case of a terpolymer, the properties of the second hydrocarbon part. The melting point of the total of the polymers used in the present invention is 175 ° C to 300 ° C, and generally 210 ° C to 270 ° C. The intrinsic viscosity (LVN) of the polymer measured by HFIP (hexafluoroisopropyl alcohol) at 60 DEG C using a standard tubular viscosity measuring apparatus is 0.5 dl / g to 10 dl / g, preferably 0.8 dl / g to 4 dl / g, And more preferably 1.0 dl / g to 2.0 dl / g. If the intrinsic viscosity is less than 0.5 dl / g, the mechanical properties are deteriorated. If the intrinsic viscosity exceeds 10 dl / g, the workability is deteriorated.

On the other hand, the molecular weight distribution of the polyketone is preferably 1.5 to 2.5, more preferably 1.8 to 2.2. When the ratio is less than 1.5, the polymerization yield decreases. When the ratio is 2.5 or more, the moldability is poor. In order to control the molecular weight distribution, it is possible to adjust proportionally according to the amount of the palladium catalyst and the polymerization temperature. That is, when the amount of the palladium catalyst is increased or when the polymerization temperature is 100 ° C or higher, the molecular weight distribution becomes larger.

 A preferred process for producing a polyketone polymer is disclosed in U.S. Patent No. 4,843,144. In the presence of a catalyst composition suitably produced from an anion of a non-hydrohalogenic acid having a pKa of less than 6 or preferably less than pKa < 2 > and a bidentate ligand of phosphorus (measured in water at 18 DEG C), carbon monoxide and a hydrocarbon monomer Is contacted under polymerization conditions to prepare a polyketone polymer.

A preferred process for producing a polyketone polymer is disclosed in U.S. Patent No. 4,843,144. The carbon monoxide and the hydrocarbon monomer are brought into contact under polymerization conditions in the presence of a catalyst composition suitably produced from a palladium compound, an anion of a hydrohalogenic acid having a pKa of 6 or less, preferably less than pKa 2, and a bidentate two-coordinate ligand, to produce a polyketone polymer.

As the production method of the polyketone resin, liquid phase polymerization in which carbon monoxide and olefin are carried out in an alcohol solvent through a catalyst composition composed of a palladium compound, an acid having 6 or less of PKa, and a ligand compound of phosphorus can be employed. The polymerization temperature is preferably from 50 to 100 ° C. and the reaction pressure is from 40 to 60 bar. The polymer is recovered through filtration and purification processes after polymerization, and the remaining catalyst composition is removed with a solvent such as alcohol or acetone.

This is preferred as palladium acetate and a palladium compound in the amount of 10 ^-3 to ^10-2 1mole preferred. Specific examples of the acid having a pKa value of 6 or less include trifluoroacetic acid, p-toluenesulfonic acid, sulfuric acid, and sulfonic acid. In the present invention, trifluoroacetic acid is used and its amount is preferably 6 to 20 equivalents based on palladium. ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene)) bis (bis (2-methoxyphenyl) phosphine) is preferable as the two- , And the amount to be used is preferably 1 to 1.2 equivalents based on palladium.

2. Polyketone polymerization process

Hereinafter, the polymerization process of the polyketone resin will be described in detail.

The repeating unit derived from carbon monoxide, an ethylenically unsaturated compound and one or more olefinically unsaturated hydrocarbon compounds, three or more copolymers, particularly repeating units derived from carbon monoxide, and ethylenically unsaturated compounds and repeating units derived from propylenically unsaturated compounds are substantially Are excellent in mechanical properties and thermal properties, excellent in processability, high in abrasion resistance, chemical resistance and gas barrier property, and thus are useful materials for various applications. It is considered that the high molecular weight product of the copolymerized polyketone having three or more members is more useful as an engineering plastic material having higher workability and thermal properties and having excellent economy. Particularly, it has high abrasion resistance and can be used in light gasoline tanks because of high gas barrier properties such as parts of gears of automobiles, high chemical resistance, and lining materials of chemical transport pipes. In the case of using an ultrahigh molecular weight polyketone having an intrinsic viscosity of 2 or more as the fiber, it is possible to conduct stretching at a high magnification and to have a high strength and a high modulus of elasticity oriented in the stretching direction as belts, reinforcements of rubber hoses, tire cords, And is suitable for use in building materials and industrial materials.

The production method of polyketone is carried out in the presence of an organometallic complex catalyst comprising (a) a Group 9, 10 or 11 transition metal compound, and (b) a ligand having an element of Group 15 elements, Wherein the carbon monoxide, ethylene and propylene are subjected to liquid phase polymerization in a mixed solvent of an alcohol (e.g., methanol) and water to produce a linear terpolymer, As the solvent, a mixture of 100 parts by weight of methanol and 2 to 10 parts by weight of water may be used. If the content of water in the mixed solvent is less than 2 parts by weight, a ketal may be formed to lower the heat stability in the process. If the amount is more than 10 parts by weight, the mechanical properties of the product may be deteriorated.

Wherein the catalyst comprises (a) a Group 9, 10 or 11 transition metal compound of the Periodic Table of the Elements (IUPAC Inorganic Chemical Nomenclature, 1989) and (b) a ligand having an element of Group 15 elements.

Examples of the Group 9 transition metal compound in the ninth, tenth, or eleventh group transition metal compound (a) include complexes of cobalt or ruthenium, carbonates, phosphates, carbamates, and sulfonates, Specific examples thereof include cobalt acetate, cobalt acetylacetate, ruthenium acetate, ruthenium trifluoroacetate, ruthenium acetylacetate, and ruthenium trifluoromethanesulfonate.

 Examples of the Group 10 transition metal compounds include complexes of nickel or palladium, carbonates, phosphates, carbamates, sulfonates and the like. Specific examples thereof include nickel acetate, nickel acetylacetate, palladium acetate, palladium trifluoroacetate , Palladium acetylacetate, palladium chloride, bis (N, N-diethylcarbamate) bis (diethylamine) palladium and palladium sulfate.

 Examples of the Group 11 transition metal compound include copper or silver complexes, carbonates, phosphates, carbamates, and sulfonates, and specific examples thereof include copper acetate, copper trifluoroacetate, copper acetylacetate, Examples of the fluoroacetic acid include silver acetyl acetate, trifluoromethanesulfonic acid and the like.

 Of these, the transition metal compound (a), which is preferable inexpensively and economically, is nickel and copper compounds, and the preferable transition metal compound (a) in terms of the yield of the polyketone and the molecular weight is the palladium compound, It is most preferable to use palladium acetate.

  Examples of the ligands (b) having an atom of Group XIII include 2,2'-bipyridyl, 4,4'-dimethyl-2,2'-bipyridyl, 2,2'- Bis (diphenylphosphino) ethane, 1,3-bis (diphenylphosphino) propane, 1,4-bis (diphenylphosphino) (2-methoxyphenyl) propane, 1,3-bis [di (2-isopropyl) Bis (diphenylphosphino) cyclohexane, 1,2-bis (diphenylphosphino) phosphine] propane, (Diphenylphosphino) methyl] benzene, 1,2-bis [[di (2-methoxyphenyl) (Diphenylphosphino) ferrocene, 2-hydroxy-1,3-bis [di (2-methoxy- (2-methoxyphenyl) phosphino] propane, 2,2-dimethyl-1,3-bis [di (2- Spinosyns; there may be mentioned a ligand, such as propane.

 Among these ligands, preferred ligands (b) having a Group 15 element are phosphorus ligands having an atom of Group 15, and particularly preferred ligands in terms of yield of polyketone are 1,3-bis [di (2- Methoxyphenyl) phosphino] propane and 1,2-bis [[di (2-methoxyphenyl) phosphino] methyl] benzene, Di (2-methoxyphenyl) phosphino] propane, and it is safe in that it does not require an organic solvent. Soluble sodium salts such as 1,3-bis [di (2-methoxy-4-sulfonic acid sodium-phenyl) phosphino] propane, 1,2- ] Methyl] benzene, and 1,3-bis (diphenylphosphino) propane and 1,4-bis (diphenylphosphino) butane are preferred for ease of synthesis and availability in large quantities and economically. The preferred ligand (b) having a Group 15 atom is 1,3-bis [di (2-methoxyphenyl) phosphino] propane or 1,3-bis (diphenylphosphino) Bis (di (2-methoxyphenyl) phosphino] propane or ((2,2-dimethyl-1,3-dioxane-5,5- -Methoxyphenyl) phosphine).

(2)

Bis (bis (2-methoxyphenyl) phosphine) bis ((2,2-dimethyl-1,3-dioxane-5,5- Activity equivalent to that of 3,3-bis- [bis- (2-methoxyphenyl) phosphanylmethyl] -1,5-dioxa-spiro [5,5] undecane, which is known to exhibit the highest activity among polymerization catalysts The structure is simpler and has a lower molecular weight. As a result, the present invention has been able to provide a novel polyketone polymerization catalyst having the highest activity as a polyketone polymerization catalyst of the present invention, while further reducing its manufacturing cost and cost. A method for producing a ligand for a polyketone polymerization catalyst is as follows. ((2,2-dimethyl) -2,3-dioxolane was obtained by using bis (2-methoxyphenyl) phosphine, 5,5-bis (bromomethyl) Bis (bis (methylene)) bis (bis (2-methoxyphenyl) phosphine) is obtained by reacting a bis (methylene) . The process for preparing a ligand for a polyketone polymerization catalyst according to the present invention is a process for producing a ligand for a polyketone polymerization catalyst which comprises reacting 3,3-bis- [bis- (2-methoxyphenyl) phosphanylmethyl] -1,5-dioxa-spiro [5,5] ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene)) bis (bis (2- Methoxyphenyl) phosphine) can be commercially synthesized in a large amount.

      In a preferred embodiment, the process for preparing a ligand for a polyketone polymerization catalyst of the present invention comprises: (a) introducing bis (2-methoxyphenyl) phosphine and dimethylsulfoxide (DMSO) into a reaction vessel under nitrogen atmosphere, Adding sodium and stirring; (b) adding 5,5-bis (bromomethyl) -2,2-dimethyl-1,3-dioxane and dimethylsulfoxide to the resulting mixture, followed by stirring and reacting; (c) adding methanol and stirring after completion of the reaction; (d) adding toluene and water, separating the layers, washing the oil layer with water, drying with anhydrous sodium sulfate, filtering under reduced pressure, and concentrating under reduced pressure; And (e) the residue was recrystallized from methanol to obtain ((2,2-dimethyl-1,3-dioxane-5,5- diyl) bis (methylene)) bis (bis (2- methoxyphenyl) And a step of acquiring the image data.

 The amount of the Group 9, Group 10 or Group 11 transition metal compound (a) to be used varies depending on the kinds of the ethylenic and propylenically unsaturated compounds to be selected and other polymerization conditions. Therefore, But it is usually from 0.01 to 100 mmol, preferably from 0.01 to 10 mmol, per 1 liter of the reaction zone. The capacity of the reaction zone means the liquid phase capacity of the reactor. The amount of the ligand (b) to be used is not particularly limited, but is usually 0.1 to 3 mol, preferably 1 to 3 mol, per 1 mol of the transition metal compound (a).

Further, the addition of benzophenone in the polymerization of the polyketone is another characteristic. In the present invention, an effect of improving the intrinsic viscosity of the polyketone can be achieved by adding benzophenone in the polymerization of the polyketone. The molar ratio of (a) the ninth, tenth or eleventh transition metal compound to benzophenone is 1: 5-100, preferably 1:40-60. If the molar ratio of the transition metal to the benzophenone is less than 1: 5, the effect of improving the intrinsic viscosity of the produced polyketone is unsatisfactory. If the molar ratio of the transition metal to the benzophenone exceeds 1: 100, It is not preferable because it tends to decrease

Examples of the ethylenically unsaturated compound copolymerized with carbon monoxide include ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, 1-octene, -Olefins such as hexadecene and vinylcyclohexane; Alkenyl aromatic compounds such as styrene and? -Methylstyrene; But are not limited to, cyclopentene, norbornene, 5-methylnorbornene, 5-phenylnorbornene, tetracyclododecene, tricyclododecene, tricyclo undecene, pentacyclopentadecene, pentacyclohexadecene, Cyclic olefins such as cyclododecene; Vinyl halides such as vinyl chloride; Ethyl acrylate, and acrylates such as methyl acrylate. Of these, preferred ethylenically unsaturated compounds are? -Olefins, more preferably? -Olefins having 2 to 4 carbon atoms, and most preferably ethylene.

  Wherein the carbon monoxide and the ethylenically unsaturated compound and the propylenically unsaturated compound are copolymerized with an organometallic complex comprising a ligand (b) having an element of group 9, group 10 or group 11 transition metal compound (a) or group 15 Catalyzed, the catalyst is produced by contacting the two components. Any method may be employed as the method of contacting. That is, the solution may be prepared as a solution in which two components are premixed in a suitable solvent, or the two components may be supplied separately to the polymerization system and contacted in the polymerization system. In this case, the molar ratio of the ethylenic unsaturated compound and the propylenic unsaturated compound is preferably 9: 1 to 24: 1, but is not limited thereto.

 As the polymerization method, a solution polymerization method using a liquid medium, a suspension polymerization method, a vapor phase polymerization method in which a small amount of a polymer is impregnated with a high concentration catalyst solution, and the like are used. The polymerization may be either batchwise or continuous. The reactor used in the polymerization can be used as it is or in a known manner. The polymerization temperature is not particularly limited, and is generally 40 to 180 占 폚, preferably 50 to 120 占 폚. The pressure at the time of polymerization is not particularly limited, but is generally from normal pressure to 20 MPa, preferably from 4 to 15 MPa.

A linear alternating polyketone is formed by the polymerization method as described above.

3. Examples and Comparative Examples

Hereinafter, the present invention will be described in detail by way of examples. However, these examples are provided only for the understanding of the present invention, and the scope of the present invention is not limited to these examples in any sense.

Example 1

The linear alternating polyketone terpolymer of carbon monoxide and ethylene and propene is prepared by reacting palladium acetate, trifluoroacetic acid and ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene) Bis (2-methoxyphenyl) phosphine). In the above, the content of trifluoroacetic acid with respect to palladium is 11 times the molar ratio, and the two stages of the first stage at a polymerization temperature of 80 ° C and the second stage at 84 ° C are carried out. The molar ratio of ethylene to propene in the polyketone terpolymer prepared above was 46 to 4. The melting point of the polyketone terpolymer was 220 占 폚, the LVN measured at 25 占 폚 by HFIP (hexa-fluoroisopropano) was 1.2 dl / g, the MI index was 60 g / 10 min and the MWD was 2.0. The polyketone terpolymer prepared above was molded into a pellet on an extruder using a twin screw having a diameter of 40 mm and L / D = 32, which was operated at 250 rpm, and then injection molded to manufacture a power line binding bracket specimen Respectively.

Example 2

The linear alternating polyketone terpolymer of carbon monoxide and ethylene and propene is prepared by reacting palladium acetate, trifluoroacetic acid and ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene) Bis (2-methoxyphenyl) phosphine). In the above, the content of trifluoroacetic acid with respect to palladium is 10 times the molar ratio, and the two stages of the first stage at a polymerization temperature of 78 占 폚 and 84 占 폚 are carried out. The molar ratio of ethylene to propene in the polyketone terpolymer prepared above was 46 to 4. The melting point of the polyketone terpolymer was 220 占 폚, the LVN measured at 25 占 폚 by HFIP (hexa-fluoroisopropano) was 1.4 dl / g, the MI index was 60 g / 10 min and the MWD was 2.0. The polyketone terpolymer prepared above was molded into a pellet on an extruder using a twin screw having a diameter of 40 mm and L / D = 32, which was operated at 250 rpm, and injection molded to produce a power line bracket specimen .

Example 3

The linear alternating polyketone terpolymer of carbon monoxide and ethylene and propene is prepared by reacting palladium acetate, trifluoroacetic acid and ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene) Bis (2-methoxyphenyl) phosphine). In the above, the content of trifluoroacetic acid with respect to palladium is 9 times the molar ratio, and the two stages of the first stage at a polymerization temperature of 74 deg. C and the second stage at 84 deg. The molar ratio of ethylene to propene in the polyketone terpolymer prepared above was 46 to 4. The melting point of the polyketone terpolymer was 220 占 폚, the LVN measured at 25 占 폚 by HFIP (hexa-fluoroisopropano) was 1.6 dl / g, the MI index was 60 g / 10 min and the MWD was 2.0. The polyketone terpolymer prepared above was molded into a pellet on an extruder using a twin screw having a diameter of 40 mm and L / D = 32, which was operated at 250 rpm, and injection molded to produce a power line bracket specimen .

Example 4

The linear alternating polyketone terpolymer of carbon monoxide and ethylene and propene is prepared by reacting palladium acetate, trifluoroacetic acid and ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene) Bis (2-methoxyphenyl) phosphine). In the above, the content of trifluoroacetic acid with respect to palladium is 10 times the molar ratio, and the two stages of the first stage at a polymerization temperature of 78 占 폚 and 84 占 폚 are carried out. The molar ratio of ethylene to propene in the polyketone terpolymer prepared above was 46 to 4. The melting point of the polyketone terpolymer was 220 占 폚, the LVN measured at 25 占 폚 by HFIP (hexa-fluoroisopropano) was 1.4 dl / g, the MI index was 60 g / 10 min and the MWD was 1.8. The polyketone terpolymer prepared above was molded into a pellet on an extruder using a twin screw having a diameter of 40 mm and L / D = 32, which was operated at 250 rpm, and injection molded to produce a power line bracket specimen .

Example 5

The linear alternating polyketone terpolymer of carbon monoxide and ethylene and propene is prepared by reacting palladium acetate, trifluoroacetic acid and ((2,2-dimethyl-1,3-dioxane-5,5-diyl) bis (methylene) Bis (2-methoxyphenyl) phosphine). In the above, the content of trifluoroacetic acid with respect to palladium is 10 times the molar ratio, and the two stages of the first stage at a polymerization temperature of 78 占 폚 and 84 占 폚 are carried out. The molar ratio of ethylene to propene in the polyketone terpolymer prepared above was 46 to 4. The melting point of the polyketone terpolymer was 220 占 폚, the LVN measured at 25 占 폚 by HFIP (hexa-fluoroisopropano) was 1.4 dl / g, the MI index was 60 g / 10 min and the MWD was 2.2. The polyketone terpolymer prepared above was molded into a pellet on an extruder using a twin screw having a diameter of 40 mm and L / D = 32, which was operated at 250 rpm, and injection molded to produce a power line bracket specimen .

Comparative Example 1

The same as Example 1 except that high impact PBT was used instead of the polyketone of Example 1.

Property evaluation

The polyketone resin composition pellets of the above-mentioned examples were (injection molded) to produce power line binding bracket specimens. The properties of the bracket specimens were evaluated in the following manner in comparison with the products of the comparative examples, and the results are shown in Table 1 below.

1. Izod Impact Strength: Performed according to ASTM D256.

2. Cycle time (injection moldability evaluation sec): The time until the pellets prepared in the Example or Comparative Example were crystallized after melting was measured in sec.

3. Evaluation of dimensional change rate

Treated at 300 캜 for 2 hours by ASTM D-638, and the width of the parallel portion of the specimen for bobbin before and after the treatment was measured by a slide caliper to observe a dimensional change.

Example 1 Example 2 Example 3 Example 4 Example 5 Comparative Example 1 Properties IV: 1.2
MWD: 2.0 IV: 1.4
MWD: 2.0 IV: 1.6
MWD: 2.0 IV: 1.4
MWD: 1.8 IV: 1.4
MWD: 2.2 High impact PBT Impact strength
(kJ / m2) 9 10 11 9.5 9.7 6.5 cycle time (sec) 14 15 17 16 16 25 Dimensional change rate 1.3% 1.2% 1.2% 1.4% 1.3% 5.2%

According to Table 1, the impact strength of the Examples was higher than that of Comparative Example 1, and the impact resistance was more excellent. In addition, the cycle time was shortened and the productivity was improved. In addition, it was evaluated that dimensional stability was excellent because of low dimensional change rate. Therefore, it was found that the embodiment is more excellent for use as a power line binding bracket.

Claims (6)

Which is produced by injection molding a linear alternating polyketone composed of carbon monoxide and at least one ethylenically unsaturated hydrocarbon.
The method according to claim 1,
Wherein the power line binding bracket has an impact strength of 8 kJ / m 2 or more.
The method according to claim 1,
Wherein the polyketone has a molar ratio of ethylene to propylene of 9 to 24: 1.
The method according to claim 1,
Wherein the polyketone has an intrinsic viscosity of 1.0 to 2.0 dl / g.
The method according to claim 1,
Wherein the polyketone has a molecular weight distribution of 1.5 to 2.5.
The method according to claim 1,
The ligand of the catalyst composition used in the polymerization of the polyketone is bis (methylene) bis (bis (2-methoxyphenyl) phosphine Pin) for connecting the power line.