KR20160051514A - Manufacturing method of curling stone - Google Patents

Manufacturing method of curling stone Download PDF

Info

Publication number
KR20160051514A
KR20160051514A KR1020150021173A KR20150021173A KR20160051514A KR 20160051514 A KR20160051514 A KR 20160051514A KR 1020150021173 A KR1020150021173 A KR 1020150021173A KR 20150021173 A KR20150021173 A KR 20150021173A KR 20160051514 A KR20160051514 A KR 20160051514A
Authority
KR
South Korea
Prior art keywords
curling stone
curling
weight
stone body
mold
Prior art date
Application number
KR1020150021173A
Other languages
Korean (ko)
Other versions
KR101735293B1 (en
Inventor
김동현
Original Assignee
김동현
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김동현 filed Critical 김동현
Publication of KR20160051514A publication Critical patent/KR20160051514A/en
Application granted granted Critical
Publication of KR101735293B1 publication Critical patent/KR101735293B1/en

Abstract

The present invention relates to a method for producing a curling stone. According to the present invention, the method can create the same effects and shape as an actual curling stone, and allows anyone to enjoy curling conveniently by altering the weight thereof. In addition, the method enables the production of direction-convertible curling stone as well. To this end, the method comprises the following steps: producing a frame (10) in a shape of a curling stone body (20); inserting a synthetic resin into the frame (10); separating the curling stone body (20) made of the cured synthetic resin from the frame (10); and attaching a handle (30) to an upper end of the curling stone body (20).

Description

컬링스톤의 제작방법{MANUFACTURING METHOD OF CURLING STONE}{MANUFACTURING METHOD OF CURLING STONE}

본 발명은 컬링스톤의 제작방법에 관한 것으로, 보다 상세하게는, 실제 컬링스톤과 같은 모양과 느낌을 구현할 수 있고, 중량을 달리하여 남녀노소 편리하게 컬링 경기를 즐길 수 있으며, 컬링스톤의 방향 전환이 가능하게 하는 컬링스톤의 제작방법을 제공하는 데 있다.The present invention relates to a method of manufacturing a curling stone, and more particularly, to a curling stone having a shape and feel similar to actual curling stone, And to provide a manufacturing method of a curling stone which enables the curling stone to be produced.

일반적으로 컬링이란 빙상에서 평면으로 된 돌[磨石]을 브룸(Broom, 빗 모양을 한 것)으로 미끄러지게 하여 표적에 넣어 득점을 겨루는 경기를 말한다.In general, curling refers to a game in which an ice sheet slides a flat stone [boulder] into a broom (comb), and puts it into the target to compete for scoring.

경기의 발상지는 스코틀랜드이며, 16세기경에 성행하였다고 한다.The birthplace of the game was Scotland, and it was said to have been active around the 16th century.

초기의 돌은 손가락으로 쥐기 위해 구멍이 뚫린 큰 돌이었으나, 1800년대에는 돌 대신 철이 사용된 적도 있다. 한때는 100 lb(45.4kg) 이상이나 되는 것도 사용되었고 한다. 1838년 그랜드(현재는 로열) 칼레도니언 컬링 클럽이 스코틀랜드에 설립되어 이것이 국제적 컬링클럽으로 합병될 때의 기초가 되었다.The earliest stone was a large stone with a hole to hold it with a finger, but iron was used instead of stone in the 1800s. At one time, more than 100 lb (45.4 kg) was used and is done. In 1838, the Grand (currently the Royal) Caledonian Curling Club was founded in Scotland and became the foundation upon which it was merged into an international curling club.

캐나다는 일찍이 컬링을 받아들인 나라로서, 1807년 로열몬트리올클럽을 결성하였다.Canada was an early adopter of curling, and in 1807 formed the Royal Montreal Club.

1927년 캐나다 선수권대회가 시작되었으며, 1959년부터 세계 선수권대회가 매년 개최된다. 캐나다를 비롯하여 북아메리카, 유럽, 뉴질랜드 등에서 성행한다.The 1927 Canadian Championships began, and the World Championships are held annually since 1959. Canada, North America, Europe, and New Zealand.

컬링의 경기방식은 1팀 4명씩 2개조로 구성되어 길이 42.1m, 너비 4.3m의 링크 내에서, 하우스라고 하는 원 속의 표적에 2개의 돌을 상대 팀과 교대로 미끄러지게 하여 표적에 어느 편이 가까이 갔는가에 따라 점수를 겨룬다.The curling method is composed of two teams of four teams each. In the link of 42.1m in length and 4.3m in width, two stones are alternately slid on the target in the circle called the house, Compete for points depending on whether you went.

돌은 무게 20kg 이하, 둘레 91.4cm 이하, 높이 11.4cm이다. 16회를 1엔드로 하여 10엔드 또는 12엔드를 1게임으로 하고, 득점의 다소에 따라 승부를 가린다.The stone is 20kg or less in weight, 91.4cm or less in circumference, and 11.4cm in height. Sixteen rounds are used as one end, and 10 or 12 rounds are used as one game, and the game is blocked depending on the score somewhat.

그러나 우리나라는 컬링의 발생지인 스코틀랜드나 컬링을 일찍 받아들인 캐나다와는 달리 겨울이 길지않고, 또한 아이스링크를 갖춘 실내경기장이 적은 관계로 컬링을 대중적으로 즐길 수 없는 여건이다.However, unlike Canada, which is an origin of curling, Scotland, which is an early adopter of curling, there is not a long winter, and there are few indoor arenas with ice rinks.

이를 위해 컬링을 대중적으로 즐길 수 있는 에어컬링 유닛(실용신안등록 제20-0436642호)이 등록된 바 있다.To this end, an air curling unit (Utility Model Registration No. 20-0436642) has been registered in which curling can be popularly enjoyed.

하지만 이러한 에어컬링 유닛은 실재 컬링스톤의 모양을 구현하기 어렵고, 또한 실제 컬링스톤과 같은 무게로 하면 부양력을 얻기 어렵게 되어 적은 무게로밖에 제작될 수 없으며, 컬링스톤의 방향 전환을 위한 수단이 구비되지 않아 경기의 재미가 떨어질 뿐만 아니라 실전 감각을 익힐 수 없는 문제점이 있었다.However, such an air curling unit is difficult to realize the shape of the actual curling stone, and if it is the same weight as the actual curling stone, it is difficult to obtain a floating force, so that it can be manufactured only with a small weight, There was a problem that not only the fun of the game fell but also it was not able to learn the sense of real.

또한 종래에는 컬링스톤이 고가일 뿐만 아니라 구입하기 어려워 컬링 경기가 쉽게 보급되지 못하는 실정이었다. In addition, in the past, curling stones are not only expensive but also difficult to purchase, so that the curling game can not be easily spread.

본 발명은 상기와 같은 문제점을 감안하여 안출된 것으로, 본 발명의 목적은, 실제 컬링스톤과 같은 모양과 느낌을 구현할 수 있는 컬링스톤의 제작방법을 제공하는 데 있다.SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and an object of the present invention is to provide a method of manufacturing a curling stone capable of realizing the same shape and feel as a curling stone.

본 발명의 다른 목적은 중량을 달리하여 남녀노소 편리하게 컬링 경기를 즐길 수 있는 컬링스톤의 제작방법을 제공하는 데 있다.Another object of the present invention is to provide a method of manufacturing a curling stone capable of enjoying a curling game at a young age and with a different weight.

본 발명의 또 다른 목적은, 컬링스톤의 방향 전환이 가능하게 하는 컬링스톤의 제작방법을 제공하는 데 있다.It is still another object of the present invention to provide a method of manufacturing a curling stone which enables the curling stone to change direction.

본 발명은 상기한 바와 같은 목적을 달성하기 위한 특징에 따르면, 본 발명은 컬링스톤의 제작방법에 관한 것으로, 컬링스톤 몸체의 형상으로 틀을 제작하는 단계; 상기 틀에 합성수지를 투입하는 단계; 경화된 합성수지에 의한 컬링스톤 몸체를 상기 틀로부터 분리하는 단계; 및 상기 컬링스톤 몸체의 상단에 손잡이를 결합하는 단계;를 포함한다.According to an aspect of the present invention, there is provided a method of manufacturing a curling stone, the method comprising: fabricating a mold in a shape of a curling stone body; Injecting a synthetic resin into the mold; Separating the curling stone body from the mold by the cured synthetic resin; And engaging a handle on the top of the curling stone body.

그리고 상기 틀 제작단계에서 상기 틀에는 상부에 내부로 볼록한 돌기를 형성하고, 상기 결합단계에서는, 상기 돌기로 인해 상기 컬링스톤 몸체 상단에 형성된 홈에 손잡이를 삽입하여 고정한다.In the mold making step, convex protrusions are formed in the upper part of the mold, and in the engaging step, the handle is inserted and fixed in the groove formed on the upper side of the curling stone body by the protrusions.

또한 상기 투입단계에서는, 상기 합성수지 100중량부에 대하여 안료 0.01~20중량부를 더 혼합할 수 있다.Further, in the above-mentioned charging step, 0.01 to 20 parts by weight of pigment may be further mixed with 100 parts by weight of the synthetic resin.

그리고 상기 투입단계에서는, 상기 컬링스톤 몸체의 중량을 증가시키기 위하여 중량증가체를 더 첨가할 수 있으며, 상기 중량증가체는, 제강슬래그, 금속체, 제강슬래그, 금속체, 골재, 규사 중 하나이거나 2종 이상 혼합되는 것이 바람직하다.In addition, the weight increasing body may be added to increase the weight of the curling stone body, and the weight increasing body may be one of steelmaking slag, metal body, steel making slag, metal body, aggregate, It is preferable to mix two or more kinds.

또는, 상기 투입단계에서는, 상기 컬링스톤 몸체의 중량을 감소시키기 위하여 중량감소체를 더 첨가할 수 있으며, 상기 중량감소체는, 고무칩과 질석 중 하나 이상인 것이 바람직하다.Alternatively, in the applying step, a weight sensitive body may be further added to reduce the weight of the curling stone body, and the weight sensitive body is preferably at least one of rubber chips and vermiculite.

또한 상기 투입단계 이전에는, 상기 합성수지에 규사를 혼합하여 상기 틀에 투입하여 양생하는 단계가 더 추가되고, 상기 분리단계 이후에는, 상기 컬링스톤 몸체의 표면에 노출된 규사를 매끈하게 연마하는 단계가 더 추가될 수 있다.Further, before the step of injecting, a step of adding silica sand to the synthetic resin and curing it by adding it to the mold is further added, and after the separating step, smooth polishing the silica sand exposed on the surface of the curling stone body More can be added.

이때 상기 틀은 상부와 하부의 2조로 구성되고, 상기 양생단계에서 상기 규사에 의한 층을 상기 틀 중 하부에만 형성하거나 상부 및 하부에 형성한다.At this time, the frame is composed of two parts, upper part and lower part. In the curing step, the layer formed by the sandpaper is formed only at the lower part of the frame or at the upper part and the lower part.

그리고 상기 분리단계 이후에, 상기 컬링스톤 몸체의 저면에 바닥판을 부착하는 단계가 더 추가될 수 있다. 이때 상기 바닥판에는 표면과의 마찰력을 줄이기 위한 돌기가 형성된다.And after the separating step, a step of attaching a bottom plate to the bottom surface of the curling stone body may be further added. At this time, a protrusion is formed on the bottom plate to reduce frictional force with the surface.

또한 상기 바닥판은 상기 컬링스톤 몸체의 저면에 홈을 형성시키고 상기 홈에 삽입되어 장착될 수도 있다. Further, the bottom plate may be formed by forming grooves on the bottom surface of the curling stone body and inserted into the grooves.

또는 상기 틀에는 상기 컬링스톤 몸체의 저면에 홈이 형성되도록 돌기가 형성되고, 상기 분리단계 이후에, 상기 컬링스톤 몸체의 저면에 형성된 홈에 바닥판을 삽입하여 장착할 수도 있다. Alternatively, protrusions may be formed on the bottom surface of the curling stone body so that grooves are formed on the bottom surface of the curling stone body. After the separation step, a bottom plate may be inserted into the grooves formed on the bottom surface of the curling stone body.

이러한 경우에 상기 바닥판은 화강암으로 제작될 수 있다.In this case, the bottom plate may be made of granite.

아울러, 상기 틀 제작단계에서는, 상기 틀의 측면에서 내부로 돌출된 장착부를 등간격으로 형성하고, 상기 분리단계 이후에는, 상기 장착부에 의해 상기 컬링스톤의 몸체에 형성된 장착홈에 자성체 또는 금속을 삽입한다.In addition, in the mold making step, the mounting portions protruding inward from the side surface of the mold are formed at equal intervals, and after the removing step, a magnetic substance or metal is inserted into the mounting recess formed in the body of the curling stone by the mounting portion do.

본 발명에 따른 컬링스톤의 제작방법에 따르면, 실제 컬링스톤과 같은 모양과 느낌을 구현할 수 있어 실제 컬링 경기와 같은 느낌을 줄 수 있는 장점이 있다.According to the method of manufacturing a curling stone according to the present invention, it is possible to realize the same shape and feel as a curling stone in actuality, thereby providing an effect similar to a real curling game.

그리고 본 발명에 의하면, 중량을 달리하여 남녀노소 편리하게 컬링 경기를 즐길 수 있어 컬링 경기의 대중화에 기여할 수 있는 이점이 있다.According to the present invention, it is possible to enjoy a curling game for a man or woman, a man, woman, and a woman in a different weight, thereby contributing to popularization of a curling game.

또한 본 발명에 의하면, 컬링스톤의 방향 전환이 가능하게 하여 컬링 경기의 재미 및 실전 감각을 향상시킬 수 있는 효과가 있다. Further, according to the present invention, it is possible to change the direction of the curling stone, thereby improving the fun and practical sense of the curling game.

도 1은 본 발명에 따른 컬링스톤의 제작방법을 도시한 순서도,
도 2는 본 발명에 따른 손잡이 결합구조를 설명하는 도면,
도 3은 본 발명에 따른 규사에 의한 층의 형성을 설명하는 도면,
도 4는 본 발명에 따른 자성체 삽입을 위한 구성을 설명하는 도면,
도 5는 본 발명에 따른 바닥판의 구성을 설명하는 도면,
도 6은 본 발명에 따른 바닥판의 다른 구성을 설명하는 도면이다.1 is a flow chart showing a method of manufacturing a curling stone according to the present invention,
2 is a view for explaining a handle coupling structure according to the present invention,
3 is a view for explaining the formation of a layer by sandpaper according to the present invention,
4 is a view for explaining a configuration for insertion of a magnetic body according to the present invention,
5 is a view for explaining a configuration of a bottom plate according to the present invention,
6 is a view for explaining another configuration of a bottom plate according to the present invention.

이하에서는 본 발명에 따른 컬링스톤의 제작방법에 관하여 상세히 설명하기로 한다.
Hereinafter, a method of manufacturing a curling stone according to the present invention will be described in detail.

도 1은 본 발명에 따른 컬링스톤의 제작방법을 도시한 순서도이다.1 is a flowchart showing a method of manufacturing a curling stone according to the present invention.

도시된 바와 같이, 본 발명에 따른 컬링스톤의 제작방법은 컬링스톤 몸체(20)의 형상으로 이루어지는 틀(10)을 제작하는 단계로부터 개시된다. 상기 틀(10)은 2개 부분으로 분리되어 2개가 1조를 이루게 제작된다. 즉 상기 틀(10)은 도 2의 (a)에 도시된 바와 같이, 상부 틀(10a)과 하부 틀(10b)로 구성된다.As shown in the drawing, the method of manufacturing a curling stone according to the present invention starts from the step of manufacturing the frame 10 having the shape of the curling stone body 20. The frame 10 is divided into two parts so that two pieces of the frame 10 are formed. That is, the frame 10 is composed of an upper frame 10a and a lower frame 10b, as shown in FIG. 2 (a).

그리고 상기 틀(10)에는 내부로 합성수지 등을 투입할 수 있는 투입구(11)가 별도로 마련될 수도 있으나, 도 2의 (a)에 도시된 바와 같이, 컬링스톤의 손잡이 위치에 대응되게 형성되는 돌기(13)를 투입구 용도로 활용할 수도 있다. 이러한 돌기(13)는 상기 틀(10)의 상부에서 내부로 볼록한 형상으로 구성된다.In addition, the mold 10 may be provided with a charging port 11 through which a synthetic resin or the like can be inserted therein. Alternatively, as shown in FIG. 2 (a), a protrusion (13) may be used as an inlet port. The protrusions 13 are formed in a convex shape from the upper portion of the frame 10 to the inside.

또한 상기 틀(10)에는, 측면에서 내부로 돌출된 장착부(15)가 등간격으로 형성될 수도 있다. 상기 장착부(15)를 형성하기 위하여 본 실시예에서는 도 4의 (a)에 도시된 바와 같이, 하부 틀(10)에 관통공(17)을 등간격으로 형성하고 상기 관통공(17)에 장착부(15)를 삽입하여 상기 틀(10) 내부로 돌출되게 한다. 이러한 장착부(15)는 컬링스톤 몸체(20)에 장착홈(25)을 형성하기 위한 것으로, 다른 방법에 의해 장착홈(25)을 형성할 수 있다면 장착부(15)는 생략 가능하다.In addition, the frame 10 may be provided with mounting portions 15 protruding inward from a side surface thereof at regular intervals. In order to form the mounting portion 15, as shown in FIG. 4A, through holes 17 are formed at equal intervals in the lower frame 10, (15) to protrude into the frame (10). The mounting portion 15 is for forming the mounting groove 25 in the curling stone body 20 and the mounting portion 15 can be omitted if the mounting groove 25 can be formed by another method.

아울러, 도 6에 도시된 바와 같이, 컬링스톤 몸체(20)에 홈(29)을 형성하고 그 홈에 바닥판(40)을 삽입하여 장착하는 경우에는, 상기 틀(10)에는 상기 컬링스톤 몸체(20)의 저면에 홈(29)이 형성되도록 돌기(미도시)를 마련하는 것이 바람직하다(단계 S10). 6, when the grooves 29 are formed in the curling stone body 20 and the bottom plate 40 is inserted into the grooves 29, the frame 10 is provided with the curling stone body 20, (Not shown) so that the groove 29 is formed on the bottom surface of the base 20 (step S10).

다음으로 상기 틀(10) 내부로 합성수지를 투입하여 양생한다. 합성수지에는 경화제가 혼합될 수 있고, 색상 발현을 위하여 상기 합성수지 100중량부에 대하여 0.01~20중량부의 안료가 첨가될 수도 있다. Next, synthetic resin is injected into the mold 10 to cure it. The hardener may be mixed with the synthetic resin, and 0.01 to 20 parts by weight of the pigment may be added to 100 parts by weight of the synthetic resin for color development.

또한 컬링 경기에 사용되는 컬링스톤의 무게가 대략 19~19.9㎏이므로, 이러한 무게 또는 연령별 적정 무게가 될 수 있도록 상기 합성수지에는 중량증가체 또는 중량감소체가 더 첨가될 수 있다. 상기 중량증가체는 제강슬래그, 금속체, 제강슬래그, 금속체, 골재, 규사 중 하나이거나 2종 이상 혼합될 수 있고, 사용되는 중량증가체의 단위중량을 토대로 합성수지에 대한 중량증가체의 혼합비율을 결정할 수 있다.In addition, since the weight of the curling stone used in the curling game is approximately 19 to 19.9 kg, weight increase bodies or weight bodies may be further added to the synthetic resin so as to be appropriate weight or age-specific weight. The weight increasing body may be one or more of steelmaking slag, metal body, steelmaking slag, metal body, aggregate, and silica sand. The weight increasing body may be mixed with the weight increasing body Can be determined.

이때 중량증가체를 합성수지와 혼합하여 양생하면 중량증가체는 그 하중에 의해 컬링스톤 몸체(20)의 하부로 몰리게 되어 무게중심이 하부에 위치하게 된다. 이러한 현상을 방지하기 위하여 하부에 다리가 부착된 판재(미도시)를 구비할 수 있다. 이러한 판재의 중앙에는 관통공이 형성되거나 상기 판재의 측면이 틀의 내면에 이격되게 형성되어 중량증가체가 상기 판재에 막혀 이동이 제한되므로 중량증가체의 침강을 방지할 수 있다. 그리고 이러한 판재는 복수 개로 구비하여 컬링스톤이 의도하는 무게중심을 갖도록 할 수 있다.At this time, when the weight-increasing body is cured by mixing with the synthetic resin, the weight-increasing body is pushed to the lower side of the curling stone body 20 by the load, and the center of gravity is located at the bottom. In order to prevent such a phenomenon, a plate (not shown) having a leg attached thereto may be provided. A through hole is formed at the center of the plate material or a side surface of the plate material is spaced apart from the inner surface of the frame so that the weight increasing body is blocked by the plate material, thereby preventing the weight increasing body from sinking. A plurality of such plates may be provided so that the curling stone has an intended center of gravity.

반대로, 컬링스톤의 중량을 감소시키기 위하여 첨가되는 중량감소체는 고무칩과 질석 중 하나 이상으로 이루어지고, 사용되는 중량감소체의 단위중량을 토대로 합성수지에 대한 중량감소체의 혼합비율을 결정할 수 있다.On the contrary, the weight sensitive body added to reduce the weight of the curling stone is made of at least one of rubber chips and vermiculite, and the mixing ratio of the weight sensitive bodies to the synthetic resin can be determined based on the unit weight of the used heavy weight body.

이러한 중량증가체 및 중량감소체로서 소개된 제강슬래그나 고무칩 등은 그 일례일 뿐 그에 한정되는 것은 아니므로, 중량의 증가 및 감소를 위해 주변 환경과 필요에 따라 그 소재는 변경될 수 있다.The steel-making slag and the rubber chip, which are introduced as the weight-increasing body and the weight-sensitive body, are merely examples, but the material is not limited thereto.

또한 컬링 경기에 사용되는 컬링스톤은 화강암으로 제작되므로, 본 발명에 따른 컬링스톤에서도 암석과 같은 느낌을 연출하기 위하여 상기 틀(10)에 합성수지를 투입하기 이전에 먼저 규사를 투입하여 컬링스톤 몸체(20)의 외형을 형성하는 규사층(21)을 이루게 할 수 있다. 이때 규사에는 합성수지가 바인더로서 첨가되고, 그 비율은 규사 80~90중량%와 합성수지 10~20중량%로 구성된다. In addition, since the curling stone used in the curling game is made of granite, the curling stone according to the present invention may be provided with a curling stone body (not shown) before putting the synthetic resin into the frame 10, 20 can be formed. In this case, synthetic resin is added to silica sand as a binder, and the ratio thereof is 80 to 90% by weight of silica sand and 10 to 20% by weight of synthetic resin.

이러한 규사층(21)은 상부 틀(10a)과 하부 틀(10b) 전체에 형성될 수도 있지만, 도 3에 도시된 바와 같이, 하부 틀(10b)에만 형성할 수도 있다.The sand layer 21 may be formed on the entire upper frame 10a and the lower frame 10b but may be formed only on the lower frame 10b as shown in FIG.

이렇게 규사층(21)을 형성한 이후에 틀(10) 내부로 합성수지를 투입하면 양생된 합성수지 외면에 규사가 덮여있는 컬링스톤 몸체(20)가 생성될 수 있다(단계 S20).When the synthetic resin is injected into the mold 10 after the silica layer 21 is formed, a curling stone body 20 having silica sand on the outer surface of the cured synthetic resin may be produced (step S20).

다음으로, 합성수지가 틀(10) 내부에서 경화되면 상기 틀(10)을 분해하여 컬링스톤 몸체(20)를 틀(10)로부터 분리한다. Next, when the synthetic resin is hardened in the mold 10, the mold 10 is disassembled to separate the curling stone body 20 from the mold 10.

분리된 컬링스톤 몸체(20)의 외부가 규사로 이루어진 경우에는, 노출된 규사를 매끈하게 연마하여 암석과 같은 느낌이 나도록 연출한다.When the outside of the separated curling stone body 20 is made of silica sand, the exposed silica sand is smoothly polished to produce a feeling like a rock.

그리고 분리된 컬링스톤 몸체(20)의 상단에는 손잡이(30)를 결합하는데, 상술한 바와 같이, 틀(10) 내부로 볼록한 돌기(13)가 형성된 상태로 합성수지가 양생되면 컬링스톤 몸체(20)의 상부에는 홈(23)이 형성되므로, 상기 홈(23)에 손잡이(30)를 삽입할 수 있게 된다. 이때 도 2의 (b)에 도시된 바와 같이, 상기 손잡이(30)가 홈(23)에 삽입되는 부분에는 나사산(31)을 형성하여 합성수지로 이루어지는 홈(23)에 회전하면서 삽입하여 고정할 수 있다.When the synthetic resin is cured in a state where convex protrusions 13 are formed in the mold 10 as described above, the curling stone body 20 is joined to the upper end of the separated curling stone body 20, The handle 30 can be inserted into the groove 23 because the groove 23 is formed in the upper portion of the groove 23. 2 (b), a thread 31 is formed at a portion where the handle 30 is inserted into the groove 23, and the thread 31 is inserted into and fixed to the groove 23 made of synthetic resin have.

또한 틀(10)에 장착부(15)를 형성하여 컬링스톤 몸체(20)를 제작하면, 컬링스톤 몸체(20)에는 장착부(15)에 의한 장착홈(25)이 형성된다. 이때 형성된 장착홈(25)에는, 도 4의 (b)에 도시된 바와 같이, 자성체(27) 또는 금속을 삽입한다. When the curling stone body 20 is formed by forming the mounting portion 15 on the frame 10, the curling stone body 20 is formed with the mounting groove 25 formed by the mounting portion 15. As shown in Fig. 4 (b), a magnetic substance 27 or a metal is inserted into the mounting groove 25 formed at this time.

즉, 상기 컬링스톤 몸체(20)는 바닥에서 활주 시 브룸(미도시)의 빗질에 의해 방향을 조향시킬 수 있도록 자성체(27) 또는 금속을 이용하는 것이다. 예를 들면, 도 4의 (b)에 도시된 바와 같이, 컬링스톤 몸체(20)에는 자성체(27)를 상기 장착홈(25)에 삽입하고, 상기 브롬의 측면에는 금속판을 외장시킬 수 있다. That is, the curling stone body 20 uses the magnetic body 27 or metal so as to steer the direction by combing the broom (not shown) when sliding from the bottom. For example, as shown in FIG. 4 (b), a magnetic substance 27 may be inserted into the mounting groove 25 in the curling stone body 20, and a metal plate may be mounted on the side surface of the bromine.

또한 상기 컬링스톤 몸체(20)의 저면에는 바닥판(40)을 부착할 수 있다. 상기 바닥판(40)에는, 도 5에 도시된 바와 같이, 표면과의 마찰력을 줄이기 위한 돌기(41)가 형성될 수 있다. 그리고 장기간의 사용으로 인하여 상기 돌기(41)는 마모될 수 있기 때문에 상기 바닥판(40)은 상기 컬링스톤 몸체(20)로부터 분리가능하게 부착되는 것이 바람직하다.A bottom plate 40 may be attached to the bottom surface of the curling stone body 20. As shown in Fig. 5, the bottom plate 40 may be provided with a projection 41 for reducing frictional force with the surface. It is preferable that the bottom plate 40 is detachably attached to the curling stone body 20 because the protrusion 41 may be worn due to long-term use.

한편, 도 6에 도시된 바와 같이, 합성수지제의 컬링스톤 몸체(20) 저면에 홈(29)을 형성시키고 상기 홈(29)에 바닥판(40)을 삽입하여 장착할 수도 있다. 이러한 바닥판의 삽입방법은, 틀(10)에 상기 홈(29)에 대응하는 돌기를 미리 형성시켜 컬링스톤 몸체(20)를 제작한 후에 바닥판(40)을 삽입하여 장착하는 방법으로도 구현될 수 있다.6, grooves 29 may be formed in the bottom surface of the curling stone body 20 made of synthetic resin, and the bottom plate 40 may be inserted into the grooves 29 to be mounted. Such a method of inserting the bottom plate may also be embodied by a method in which a protrusion corresponding to the groove 29 is formed in the mold 10 in advance to manufacture the curling stone body 20 and then the bottom plate 40 is inserted and mounted .

이때 바닥판(40)은 실제 컬링스톤과 동일한 재질인 화강암으로 제작하여 얼음판에서 실제 컬링스톤과 동일한 마찰력으로 미끌리게 한다. 따라서 본 발명에 따른 컬링스톤을 사용하여도 실제 컬링스톤과 거의 동일한 느낌으로 컬링 경기를 할 수 있게 된다.
At this time, the bottom plate 40 is made of granite which is the same material as the actual curling stone, and is not attracted to the ice plate with the same frictional force as the actual curling stone. Therefore, even if the curling stone according to the present invention is used, the curling game can be performed with almost the same feeling as the actual curling stone.

비록 본 발명이 상기에서 언급한 바람직한 실시예와 관련하여 설명되어졌지만, 본 발명의 요지와 범위로부터 벗어남이 없이 다른 다양한 수정 및 변형이 가능할 것이다. 따라서, 첨부된 청구의 범위는 본 발명의 진정한 범위 내에 속하는 그러한 수정 및 변형을 포함할 것이라고 여겨진다.Although the present invention has been described in connection with the preferred embodiments mentioned above, various other modifications and variations will be possible without departing from the spirit and scope of the invention. It is, therefore, to be understood that the appended claims are intended to cover such modifications and changes as fall within the true scope of the invention.

10 : 틀 11 : 투입구
13 : 돌기 15 : 장착부
17 : 관통공 20 : 컬링스톤 몸체
21 : 규사층 23 : 홈
25 : 장착홈 27 : 자성체
30 : 손잡이 31 : 나사산
40 : 바닥판 41 : 돌기10: Frame 11: Inlet
13: projection 15:
17: Through hole 20: Curling stone body
21: Silica layer 23: Home
25: mounting groove 27: magnetic body
30: handle 31: thread
40: bottom plate 41: projection

Claims (15)

컬링스톤 몸체(20)의 형상으로 틀(10)을 제작하는 단계;
상기 틀(10)에 합성수지를 투입하는 단계;
경화된 합성수지에 의한 컬링스톤 몸체(20)를 상기 틀(10)로부터 분리하는 단계; 및
상기 컬링스톤 몸체(20)의 상단에 손잡이(30)를 결합하는 단계;를 포함하는 것을 특징으로 하는 컬링스톤의 제작방법.(10) in the shape of a curling stone body (20);
Applying synthetic resin to the frame (10);
Separating the curling stone body (20) from the mold (10) by cured synthetic resin; And
And engaging a handle (30) on an upper end of the curling stone body (20). 제1항에 있어서,
상기 틀(10) 제작단계에서 상기 틀(10)에는 상부에 내부로 볼록한 돌기(13)를 형성하고,
상기 결합단계에서는, 상기 돌기(13)로 인해 상기 컬링스톤 몸체(20) 상단에 형성된 홈에 손잡이(30)를 삽입하여 고정하는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
In the mold 10, the mold 10 is formed with a convex protrusion 13 at its upper portion,
Wherein the engaging step comprises inserting the knob (30) into the groove formed in the upper end of the curling stone body (20) by the protrusion (13) and fixing the knob (30). 제1항에 있어서,
상기 투입단계에서는, 상기 합성수지 100중량부에 대하여 안료 0.01~20중량부를 더 혼합하는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
Wherein the mixing step further comprises mixing 0.01 to 20 parts by weight of pigment with respect to 100 parts by weight of the synthetic resin. 제1항에 있어서,
상기 투입단계에서는, 상기 컬링스톤 몸체(20)의 중량을 증가시키기 위하여 중량증가체를 더 첨가하는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
Wherein the weight of the curling stone body (20) is increased in order to increase the weight of the curling stone body (20). 제4항에 있어서,
상기 중량증가체는, 제강슬래그, 금속체, 제강슬래그, 금속체, 골재, 규사 중 하나이거나 2종 이상 혼합되는 특징으로 하는 컬링스톤의 제작방법.5. The method of claim 4,
Wherein the weight increasing body is one of steel making slag, metal body, steel making slag, metal body, aggregate, and silica sand, or a mixture of two or more thereof. 제1항에 있어서,
상기 투입단계에서는, 상기 컬링스톤 몸체(20)의 중량을 감소시키기 위하여 중량감소체를 더 첨가하는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
Wherein the weighting body is further added in order to reduce the weight of the curling stone body (20). 제6항에 있어서,
상기 중량감소체는, 고무칩과 질석 중 하나 이상인 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 6,
Wherein the weight sensitive element is at least one of rubber chips and vermiculite. 제1항에 있어서,
상기 투입단계 이전에는,
상기 합성수지에 규사를 혼합하여 상기 틀(10)에 투입하여 양생하는 단계가 더 추가되고,
상기 분리단계 이후에는,
상기 컬링스톤 몸체(20)의 표면에 노출된 규사를 매끈하게 연마하는 단계가 더 추가되는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
Prior to the step of injecting,
Mixing the synthetic resin with silica sand, and curing the mixture by filling it into the mold (10)
After the separating step,
The method of manufacturing a curling stone according to claim 1, further comprising the step of smoothly grinding the sanding yarn exposed on the surface of the curling stone body (20). 제8항에 있어서,
상기 틀(10)은 상부와 하부의 2조로 구성되고,
상기 양생단계에서 상기 규사에 의한 층을 상기 틀(10) 중 하부에만 형성하거나 상부 및 하부에 형성하는 것을 특징으로 하는 컬링스톤의 제작방법.9. The method of claim 8,
The frame (10) consists of two parts, upper and lower,
Wherein the layer of the sandpaper is formed only in the lower part of the frame (10) or formed on the upper part and the lower part in the curing step. 제1항에 있어서,
상기 분리단계 이후에, 상기 컬링스톤 몸체(20)의 저면에 바닥판(40)을 부착하는 단계가 더 추가되는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
Wherein the step of attaching a bottom plate (40) to the bottom surface of the curling stone body (20) is further added after the separating step. 제10항에 있어서,
상기 바닥판(40)에는 표면과의 마찰력을 줄이기 위한 돌기(41)가 형성되는 것을 특징으로 하는 컬링스톤의 제작방법.11. The method of claim 10,
Wherein the bottom plate (40) is provided with a projection (41) for reducing frictional force with the surface. 제10항에 있어서,
상기 바닥판(40)은 상기 컬링스톤 몸체(20)의 저면에 홈(29)을 형성시키고 상기 홈(29)에 삽입되어 장착되는 것을 특징으로 하는 컬링스톤의 제작방법.11. The method of claim 10,
Wherein the bottom plate (40) is formed by forming a groove (29) on the bottom surface of the curling stone body (20) and inserted into the groove (29). 제1항에 있어서,
상기 틀(10)에는 상기 컬링스톤 몸체(20)의 저면에 홈(29)이 형성되도록 돌기가 형성되고,
상기 분리단계 이후에, 상기 컬링스톤 몸체(20)의 저면에 형성된 홈(29)에 바닥판(40)을 삽입하여 장착하는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
A protrusion is formed in the frame 10 so that a groove 29 is formed on a bottom surface of the curling stone body 20,
Wherein the bottom plate (40) is inserted into the groove (29) formed in the bottom surface of the curling stone body (20) after the separating step. 제12항 또는 제13항에 있어서,
상기 바닥판(40)은 화강암으로 제작되는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 12 or 13,
Wherein the bottom plate (40) is made of granite. 제1항에 있어서,
상기 틀 제작단계에서는, 상기 틀(10)의 측면에서 내부로 돌출된 장착부(15)를 등간격으로 형성하고,
상기 분리단계 이후에는, 상기 장착부(15)에 의해 상기 컬링스톤의 몸체에 형성된 장착홈(25)에 자성체(27) 또는 금속을 삽입하는 것을 특징으로 하는 컬링스톤의 제작방법.The method according to claim 1,
In the mold making step, the mounting portions 15 protruding from the side surface of the mold 10 are formed at equal intervals,
Wherein the magnetic member (27) or metal is inserted into the mounting groove (25) formed in the body of the curling stone by the mounting portion (15) after the separating step.
KR1020150021173A 2014-10-31 2015-02-11 Manufacturing method of curling stone KR101735293B1 (en)